TY - JOUR A1 - Domonov, D.P. A1 - Pechenyuk, S.I. A1 - Semushina, Y.P. A1 - Yusenko, Kirill T1 - Solid state transformation in inner coordination sphere of [Co(NH3)6][Fe(C2O4)3]·3H2O as a route to access catalytically active Co-Fe materials JF - Materials N2 - Thermal decomposition of [Co(NH₃)₆][Fe(C₂O₄)₃]∙3H₂O in argon atmosphere, at a low heating rate (3°/min), and in large amounts of the initial complex (~0.1 mole), has been studied. It was possible to distinguish four decomposition steps upon heating: In the temperature range of 50⁻100 °C-the loss of crystal water; 100⁻190 °C-stability region of dehydrated complex; 230⁻270 °C-the range of stability of intermediate phase with the formula CoFe(NH₃)₂(C₂O₄)₂; 270⁻350 °C-thermal decomposition of the intermediate with the formation of metallic products and further air oxidation with the formation of Co1.5Fe1.5O₄. Catalytic properties of thermolysis products were tested in the decomposition reaction of H₂O₂ (inactive), oxidation of acetone (average activity), and decomposition of ammonium perchlorate (highly active). KW - Double complex salts KW - Catalysts KW - Single-source precursors PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-474014 DO - https://doi.org/10.3390/ma12020221 SN - 1996-1944 VL - 12 IS - 2 SP - 221, 1 EP - 10 PB - mdpi CY - Zürich AN - OPUS4-47401 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Yusenko, Kirill T1 - Single-source precursors strategy to access refractory high-entropy alloys for electrocatalytic applications N2 - High-entropy alloys containing up to 6 platinum group metals can be prepared by thermal decomposition of single-source precursors non requiring high temperature. We prepare the first example of a single-phase hexagonal high-entropy alloy. Heat treat- ment up to 1500 K and compression up to 45 GPa do not result in phase changes, a record temperature and pres- sure stability for a single-phase high-entropy alloy. The alloys show pronounced electrocatalytic activity in methanol oxidation, which opens a route for the use of high-entropy alloys as materials for sustainable energy conversion. T2 - HEA2020: first international virtual workshop on high-entropy alloy and complex solid solution nanoparticles for electrocatalysis CY - Online meeting DA - 06.10.2020 KW - High-entropy alloys KW - Single-source precursors PY - 2020 AN - OPUS4-54013 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pechenyuk, S A1 - Vikulova, E A1 - Semushina, Y A1 - Baidina, I A1 - Filatov, E A1 - Yusenko, Kirill T1 - Isostructurality and Thermal Properties in the Series of Double Complex Salts [M-1(NH3)(6)][M-2(C2O4)(3)]center dot 3H(2)O (M-1 = Co, Ir, M-2 = Fe, Cr) T1 - ИЗОСТРУКТУРНОСТЬ И ТЕРМИЧЕСКИЕ СВОЙСТВА В РЯДУ ДВОЙНЫХ КОМПЛЕКСНЫХ СОЛЕЙ СОСТАВА JF - Journal of Structural Chemistry N2 - Preparation of new bimetallic compounds, including double complex salts (DCSs), containing both a platinumgroup metal and a transition metal of the fourth period is of great interest since these compounds can act as precursors of bimetallic materials. One example of using such compounds is the preparation of ultrafine particles of solid solutions of metals or intermetallic compounds on various supports to fabricate highly efficient catalysts with a low content of noble metals. Compounds containing coordinated oxalate anions are important objects of synthetic chemistry and interesting precursors. For example, a lot of attention is given to salts with [M(C2O4)2]2– anions, where M = Co, Ni, Cu, Pt, Pd. On the one hand, the uniqueness of oxalate coordinated anions is due to the fact that they are easily obtained and are stable both in aqueous solutions and in the solid phase; on the other hand, they are thermally decomposed at relatively low temperatures, which makes them promising precursors for the fabrication of metallic and oxide materials. N2 - Синтезирован ряд из четырех изоструктурных двойных комплексных солей, построенных на основе катионов [М1(NH3)6]3+ и анионов [M2(C2O4)3]3-, где M1 = Co, Ir, M2 = Fe, Cr. Соли кристаллизуются в гексагональной пространственной группе симметрии P`3c1. Согласно данным термического анализа в атмосфере аргона, термическая устойчивость (температуры начала разложения обезвоженных продуктов) изучаемых соединений зависит от природы комплексного трисоксалатного аниона и увеличивается в рядах [Ir(NH3)6][Co(C2O4)3] < [Ir(NH3)6][Fe(C2O4)3] < [Ir(NH3)6][Cr(C2O4)3] < [Ir(NH3)6][Ir(C2O4)3] и [Co(NH3)6][Co(C2O4)3] < [Co(NH3)6][Fe(C2O4)3] < [Co(NH3)6][Cr(C2O4)3] < [Co(NH3)6][Ir(C2O4)]. При этом при одинаковом анионе соли гексаммина иридия(III) более устойчивы по сравнению с солями кобальта(III)). При термическом разложении солей [Co(NH3)6][Fe(C2O4)3]·3H2O и [Ir(NH3)6][Fe(C2O4)3] 3H2O в атмосфере водорода образуются твердые растворы Co0,5Fe0,5 и Ir0,5Fe0,5 соответственно. KW - Single-source precursors KW - Double complex salts KW - Catalysts PY - 2019 UR - https://doi.org/10.1134/S0022476619070060 DO - https://doi.org/10.26902/JSC_id42958 VL - 60 IS - 7 SP - 1110 EP - 1119 PB - Springer AN - OPUS4-48925 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yusenko, Kirill A1 - Khandarkhaeva, S. A1 - Bykov, M. A1 - Fedotenko, T. A1 - Hanfland, M. A1 - Sukhikh, A. A1 - Gromilov, S. A1 - Dubrovinsky, L. T1 - Face-centered cubic refractory alloys prepared from single-source precursors JF - Material N2 - Three binary fcc-structured alloys (fcc–Ir0.50Pt0.50, fcc Rh0.66Pt0.33 and fcc–Rh0.50Pd0.50) were 14 prepared from [Ir(NH3)5Cl][PtCl6], [Ir(NH3)5Cl][PtBr6], [Rh(NH3)5Cl]2[PtCl6]Cl2 and 15 [Rh(NH3)5Cl][PdCl4]·H2O, respectively, as single-source precursors. All alloys were prepared by 16 thermal decomposition in gaseous hydrogen flow below 800 °C. Fcc–Ir0.50Pt0.50 and fcc–Rh0.50Pd0.50 17 correspond to miscibility gaps on binary metallic phase diagrams and can be considered as 18 metastable alloys. Detailed comparison of [Ir(NH3)5Cl][PtCl6] and [Ir(NH3)5Cl][PtBr6] crystal 19 structures suggests that two isoformular salts are not isostructural. In [Ir(NH3)5Cl][PtBr6], specific 20 Br…Br interactions are responsible for crystal structure arrangement. Room temperature 21 compressibility of fcc–Ir0.50Pt0.50, fcc–Rh0.66Pt0.33 and fcc–Rh0.50Pd0.50 has been investigated up to 50 GPa 22 in diamond anvil cells. All investigated fcc-structured binary alloys are stable under compression. 23 Atomic volumes and bulk moduli show good agreement with ideal solutions model. For fcc–24 Ir0.50Pt0.50, V0/Z = 14.597(6) Å3·atom-1, B0 = 321(6) GPa, B0' = 6(1); for fcc–Rh0.66Pt0.33, V0/Z = 14.211(3) 25 Å3·atom-1, B0 =259(1) GPa, B0' = 6.66(9); for fcc–Rh0.50Pd0.50, V0/Z = 14.18(2) Å3·atom-1, B0 =223(4) GPa, 26 B0' = 5.0(3). KW - High-pressure KW - Refractory alloys KW - Platinum group metals KW - Single-source precursors PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-508176 DO - https://doi.org/10.3390/ma13061418 VL - 13 IS - 6 SP - 1418 PB - MDPI CY - Basel AN - OPUS4-50817 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yusenko, Kirill A1 - Spektor, K. A1 - Khandarkhaeva, S. A1 - Fedotenko, T. A1 - Pakhomova, A. A1 - Kupenko, I. A1 - Rohrbach, A. A1 - Klemme, S. A1 - Crichton, W. A. A1 - Dyachkova, T. V. A1 - Tyutyunnik, A. P. A1 - Zainulin, Y. G. A1 - Gramilov, S. A. A1 - Dubrovinsky, L. S. T1 - Decomposition of single-source precursors under high-temperature highpressure to access osmium–platinum refractory alloys JF - Journal of alloys compounds N2 - Thermal decomposition of (NH4)2[OsxPt1-xCl6] as single-source precursors for Os-Pt binary alloys has been investigated under ambient and high pressure up to 40 GPa. Thermal decomposition of mixed-metal (NH4)2[OsxPt1-xCl6] precursor in hydrogen atmosphere (reductive environment) under ambient pressure results in formation of β-trans[Pt(NH3)2Cl2] and α-trans-[Pt(NH3)2Cl2] crystalline intermediates as well as single and twophase Os—Pt binary alloys. For the first time, direct thermal decomposition of coordination compound under pressure has been investigated. A formation of pure metallic alloys from single-source precursors under pressure has been shown. Miscibility between fcc- and hcpstructured alloys has been probed up to 50 GPa by in situ high-pressure X-ray diffraction. Miscibility gap between fcc- and hcp-structured alloys does not change its positions with pressure up to at least 50 GPa. KW - High-pressure high-temperature KW - Osmium KW - Platinum KW - Phase diagrams KW - Alloys KW - Single-source precursors PY - 2020 DO - https://doi.org/10.1016/j.jallcom.2019.152121 VL - 813 SP - 152121 PB - Elsevier AN - OPUS4-50019 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -