TY - CONF A1 - Woydt, Mathias A1 - Mohrbacher, H. T1 - The background for the use of hardmetals and MMCs based on niobium carbide (NbC) as cutting tools and for wear resistant tribosystems N2 - In this present study, the mechanical properties (strength, hardness, moduli) and the dry sliding properties of stoichiometric and sub-stoichiometric NbC were compared. Microhardness and elastic properties of NbC depend from the C/Nb ratio, because the binary phase diagram Nb-C shows a region of homogeneity of NbCx of 0,72≤ x ≤1.0. At RT, hard metals of stoichiometric NbC have an elastic modulus E of ~440 GPa, those of substochiometric NbC0,88 an E of 405 GPa. The hot hardness of sub-stoichiometric NbC is above 600°C higher than of WC. The dry sliding wear resistance (0,1-7/10 m/s) of the present Fe3Al-NbC0,94 with ~61 vol.-% NbC as hard phase was close to those known of NbC-based hard metals. No grain pull-outs or fragmentations of the NbC grains were seen in the wear tracks of the Fe3Al-NbC composite (MMC), as a metallurgical interphase was formed between matrix and NbC grains. Stoichiometric and sub-stoichiometric niobium carbides have at RT and 400°C under dry sliding a prone intrinsic wear resistance more or less independent from sliding speed, either as hardmetal or as hard phase in metal matrix composite, associated with an exceptional high load carrying capacity. T2 - 3rd International Conference on Stone and Concrete Machining (ICSCM) CY - Bochum, Germany DA - 02.11.2015 KW - NbC KW - Niobium carbide KW - Cobalt KW - Fe3Al KW - Hardmetals KW - Metal matrix composite KW - Wear resistance KW - Cutting KW - Milling PY - 2015 SN - 978-3-943063-20-2 SP - 199 EP - 207 PB - Ruhr-Universität Bochum CY - Bochum AN - OPUS4-34846 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias T1 - Tailoring the functional properties of niobium carbide N2 - Several phases, like Nb₄C₃, Nb₆C₅ and other short and long range ordered phases occur in the region of homogeneity of NbCₓ (0,75≤ x ≤1.0) in the binary phase diagram. Properties, like micro-hardness, hot hardness, sliding wear resistance, elastic modulus and toughness can be tailored by the C/Nb ratio, the addition of secondary carbides and the type of binder. Supporting results from different grades with varying C/Nb ratio or binder types were illuminated. Thus, the NbC system offers to producers a wider process window, than WC. The impact of These tailored properties on sliding wear and cutting performance was illuminated by tribological and machining results. Niobium is today largely available. NbC can be synthesized by carbothermal conversion of Nb₂O₅ or be metallurgically grown and leached out, provides comparably low friction in many relevant tribo-contacts and displays low wear. NbC and Nb₂O₅ have so far no REACH classification related to human toxicology and are not listed as substances of very high concern contrary to WO₃ and Co₃O₄. T2 - 40th International Conference and Exposition on Advanced Ceramics and Composites CY - Daytona Beach, FL, USA DA - 24.01.2016 KW - Niobium carbide KW - Hard metal KW - Wear KW - Friction KW - Machining KW - Cutting KW - Metal matrix composite PY - 2016 SP - Paper: 2347292, 1 EP - 13 AN - OPUS4-35640 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Mohrbacher, H. T1 - The use of niobium carbide (Nbc) for wear resistant tribosystems and the tribological backgrounds as cutting tools N2 - The tribological profile of rotating disks made in binder-less niobium Carbide (hot-pressed NbC) and cobalt-bonded NbCs (NbC-8Co and NbC-12Co) mated against alumina (99.7%) were determined under unidirectional sliding tests (0.1 m/s to 8.0 m/s; 22°C and 400°C) as well as in oscillation tests (f= 20 Hz, Ax= 0.2 mm, 2/50/98% rel. humidity, n= 105/l 06 cycles) under unlubricated (dry) conditions. In addition, the microstructure and mechanical properties of HPNbCl and NbC bonded with 8 vol.-% and 12 vol.-% cobalt were determined as well. The tribological data obtained were benchmarked with different ceramics, cermets, hard metals and thermally sprayed coatings, where the NbCs bonded with 8% and 12% Co presented above 7 m/s the lowest wear rates so far in such a bench mark. HP-NbCl, NbC-8Co and NbC-12Co exhibited low wear rates under dry sliding associated with PV high load carrying capacities. The tribological profile established revealed a strong position of NbC bearing materials under tribological considerations and for closed tribo-systems against traditional references. T2 - 9th International conference on tungsten, refractory & hardmaterials CY - Orlando, FL, USA DA - 18.05.2014 KW - Friction KW - Wear KW - Ceramic KW - Oscillation KW - NbC KW - Niobium carbide KW - Cobalt KW - Hard metal KW - Strength KW - Sliding KW - Modulus KW - High temperatures PY - 2014 SN - 978-0-9853397-7-7 SP - 222 EP - 232 AN - OPUS4-31630 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Woydt, Mathias A1 - Mohrbacher, H. T1 - The tribological and mechanical properties of niobium carbides (NbC) bonded with cobalt of Fe3Al N2 - The tribological and mechanical properties of niobium carbide bonded with 8 vol.-% (NbC-8Co), 12 vol.-% of cobalt (NbC-12Co) or 12 vol.-% of Fe3Al (NbC-12Fe3Al) are presented. Rotating discs made of metal-bonded niobium carbide were mated against alumina (99.7%) under unlubricated (dry) unidirectional sliding tests (0.1 m/s to 12.0 m/s; 22 °C and 400 C) as well as in oscillation tests (f=20 Hz, Δx=0.2 mm, 2/50/98% rel. humidity, n=105/106 cycles). Microstructure and phase compositions were determined as well. The tribological data obtained were benchmarked with different ceramics, cermets, hard metals and thermally sprayed coatings, where NbC bonded with 8% and 12% Co presented above 7 m/s the lowest wear rates so far in such a benchmark. Binderless NbC (HP-NbC1) and the metal-bonded NbCs exhibited low wear rates under dry sliding associated with P·V high load carrying capacities. NbC-based hard metal bonded with 12 vol.-% of Fe3Al resulted in a higher hardness level than for 12 vol.-% cobalt. The tribological profile established revealed a strong position of NbC-bearing materials under tribological considerations and for closed tribosystems against established reference tribo-couples. KW - Sliding KW - Ceramic KW - Oscillation KW - Strength KW - Modulus KW - High temperatures KW - Friction KW - Wear KW - NbC KW - Niobium carbide KW - Cobalt KW - Fe3Al KW - Hard metal PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-316129 DO - https://doi.org/10.1016/j.wear.2014.09.007 SN - 0043-1648 VL - 321 SP - 1 EP - 7 PB - Elsevier CY - Amsterdam AN - OPUS4-31612 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias T1 - Adjusting the functional properties of niobium carbide N2 - The process window and range of functional properties of NbC is wide, because micro-hardness, hot hardness, sliding wear resistance, elastic modulus and toughness can be tailored by the C/Nb ratio, because Nb4C3, Nb6C5 and other short and long range ordered phases occur in the region of homogeneity of NbCx (0,75≤ x ≤1.0) in the binary Phase diagram, and by the type of binder. Further improvements enable the addition of secondary carbides. Supporting results from literature and different grades with varying C/Nb ratio or binder types were illuminated. Thus, the NbC system offers to producers a wider process window, than WC. The impact of these tailored properties on sliding wear and cutting performance was illuminated by tribological and machining results. NbC can be synthesized by carbothermal conversion of Nb2O5 or be metallurgically grown in melts and leached out as coarse NbC cubes. NbC provides comparably lower friction in many relevant tribo-contacts and displays low wear. NbC and Nb2O5 have so far no REACH classification related to human toxicology and are not listed as substances of very high concern contrary to WO3 and Co3O4. T2 - 2016 International Conference on Powder Metallurgy & Particulate Materials CY - Boston, MA, USA DA - 05.06.2016 KW - Niobium carbide KW - NbC KW - Wear KW - Friction PY - 2016 AN - OPUS4-36497 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Genga, R. M. A1 - Rokebrand, P. A1 - Cornish, L. A. A1 - Nelwalani, N. A1 - Brandt, Guido A1 - Kelling, Norbert A1 - Woydt, Mathias A1 - Janse van Vuuren, A. A1 - Polese, C. T1 - High-temperature sliding wear, elastic modulus and transverse rupture strength of Ni bonded NbC and WC cermets N2 - The effects of rapid pulse electric current sintering (PECS), substitution of WC by NbC and Co by Ni, and carbide additives (TiC and Mo2C) on the microstructure, elastic modulus, B3B transverse rupture strength (TRS) and high temperature sliding wear on WC-Co, WC-Ni, NbC-Co and NbC-Ni cermets were studied. High temperature sliding wear tests were carried out using a ball-on-disk tribometer, with a 10 N force, at a sliding speed of 1.34 m/s for 0.8 km (10 min) and 2.4 km (30 min), using 100Cr6 (AISI 52100) steel balls at 400 °C and 0% humidity. Additions of TiC and Mo2C to NbC-12Ni improved the sliding wear resistance, with TiC having the greater effect, reducing the sample wear rate by over 30% from 15.1×10−6mm3/N·m to 9.4×10−6mm3/N·m after sliding distance of 2.4 km. Generally, the LPS samples had lower wear volumes than the corresponding SPS samples, due to higher K1c and TRS. KW - Pulse electric current sintering KW - Niobium carbide KW - Nickel KW - Molybdenum carbide KW - Titanium carbide PY - 2020 DO - https://doi.org/10.1016/j.ijrmhm.2019.105143 SN - 0263-4368 VL - 87 SP - 105143 PB - Elsevier Ltd. AN - OPUS4-51473 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Woydt, Mathias A1 - Huang, S. A1 - Vleugels, J. A1 - Mohrbacher, H. A1 - Cannizza, E. T1 - Potentials of niobium carbide (NbC) as cutting tools and for wear protection N2 - Research and development of WC grades is 90 years ahead of niobium carbide-based hard materials, which showed already as light-weight and unexplored material a very high potential for many technical applications, especially for wear protection and machining. NbC evoluted recently from lab scale to pilot scale, especially in areas where established WC-based materials are causing economic, environmental or technical concerns. Benchmark trials of NbC-based hard metals indicated already a favorable performance in machining of steel components. KW - Niobium carbide KW - Friction KW - Wear KW - NbC KW - Hard metals KW - Machining KW - Nickel PY - 2018 DO - https://doi.org/10.1016/j.ijrmhm.2018.01.009 SN - 0263-4368 VL - 72 SP - 380 EP - 387 PB - Elsevier Ltd. AN - OPUS4-44166 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Mohrbacher, H. T1 - The tribological property profile of hard metals and metal matrix composites based on niobium carbide N2 - This work is focused on the tribological profile of NbC-based material, as well as their potential applications and environmental implications. T2 - International Symposium on Wear Resistant Alloys for the Mining and Processing Industry CY - Sao Paulo, Brazil DA - 04.05.2015 KW - Niobium carbide KW - Metal KW - Binder KW - Metal matrix composite KW - Friction KW - Wear KW - Hardness KW - Solubility KW - Toughness KW - Abrasion PY - 2018 SN - 978-0-692-05382-9 SP - 427 EP - 461 AN - OPUS4-44201 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Huang, S. G. A1 - Vleugels, J. A1 - Mohrbacher, H. A1 - Woydt, Mathias T1 - NbC-based cermets: influence of secondary carbide addition and metal binder N2 - Full densification of Fe, Co and Ni bonded NbC based cermet’s was achieved by pressure less liquid phase sintering in vacuum for one hour at 1420°C. The hardness and toughness of the NbC matrix cermet’s can be mainly tailored by the binder composition and secondary carbide additions. Ni binder based NbC cermet’s allow the combination of high hardness and improved toughness. The addition of lesser amounts of VC/Cr3C2 in a NbC partially substituted WC-Co cemented carbide increased significantly the hardness in combination with a moderate fracture toughness. T2 - International Symposium on Wear Resistant Alloys for the Mining and Processing Industry CY - Sao Paulo, Brazil DA - 04.05.2015 KW - Niobium carbide KW - Hardmetal KW - Cemented carbide KW - Sintering KW - Grain growth KW - Microstructure KW - Hardness KW - Fracture toughness PY - 2018 SN - 978-0-692-05382-9 SP - 521 EP - 534 AN - OPUS4-44206 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Le Quilliec, G. A1 - Leroy, R. A1 - Richard, C. A1 - Woydt, Mathias A1 - Morandeau, A. T1 - Comparison of the life-span of NbC-Co and WC-Co inserts during different machining operations on 100Cr6 (SAE 52100) bearing steel N2 - The aim of the study presented in this paper is to highlight the potential of niobium carbide cutting tool inserts for machining and to compare their performance to commercially available tungsten carbide inserts. In this work, a comparison between a conventional Wc-Co insert and NbC-Co inserts was carried out under hard machining conditions on specimens made of 100Cr6 bearing steel grade (SAE 52100). T2 - International Symposium on Wear Resistant Alloys for the Mining and Processing Industry CY - Sao Paulo, Brazil DA - 04.05.2015 KW - Niobium carbide KW - Cobalt KW - Fe3Al KW - Inserts KW - Cutting tools KW - Wear KW - Turning PY - 2018 SN - 978-0-692-05382-9 SP - 535 EP - 545 AN - OPUS4-44207 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -