TY - JOUR A1 - Zaghdoudi, Maha A1 - Kömmling, Anja A1 - Jaunich, Matthias A1 - Wolff, Dietmar T1 - Understanding the recovery behaviour and the degradative processes of EPDM during ageing JF - Polymer Testing N2 - Recovery is an important measure for seal applications representing to which extent the elastomer regains its initial shape after deformation and release of an applied force. Compression set (CS) indicates the degree of recovery. Ethylene propylene diene rubber (EPDM) was aged at 75 ◦C, 100 ◦C, 125 ◦C and 150 ◦C for different ageing times up to five years and compression set measurements were performed at different times after disassembly and after additional tempering. Short- and long-term recovery up to one year after release for samples aged at 125 ◦C and 150 ◦C was also studied. To assess the curvature in the Arrhenius diagram that may occur due to non-sufficiently aged specimens, a degradation-rate based model was fitted to the CS data after tempering. For each ageing temperature, two decay fit functions were proposed, each with an activation energy and a corresponding degradative process. The influence of ageing on the leak-tightness after fast small partial release is investigated and estimated through the analysis of the shift factors from time temperature superposition (TTS) of CS measurements at different times after disassembly. Shift factors of CS measurement after 1 s and after additional tempering are in good agreement. KW - Compression set KW - Ageing KW - Recovery KW - Degradative processes KW - Leakage rate PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-573699 DO - https://doi.org/10.1016/j.polymertesting.2023.107987 SN - 0142-9418 VL - 121 SP - 107987 PB - Elsevier Ltd. AN - OPUS4-57369 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wolff, Dietmar A1 - Jaunich, Matthias A1 - Probst, Ulrich A1 - Nagelschmidt, Sven T1 - Understanding the long-term behavior of sealing systems and neutron shielding material for extended dry cask storage T2 - PSAM 12 - Probabilistic safety assessment and management (Proceedings) N2 - In Germany, the concept of dry interim storage in dual purpose metal casks before disposal is being pursued for spent nuclear fuel (SF) and high active waste (HAW) management. However, since there is no repository available today, the initially planned and established dry interim storage license duration of up to 40 years will be too short and its extension will become necessary. For such a storage license extension it is required to assess the long-term performance of SF and all safety related storage system components in order to confirm the viability of extended storage. The main safety relevant components are the thick-walled dual purpose metal casks. These casks consist of a monolithic cask body with integrated neutron shielding components (polymers, e.g. polyethylene) and a monitored double lid barrier system with metal and elastomeric seals. The metal seals of this bolted closure system guarantee the required leak-tightness whereas the elastomeric seals allow for leakage rate measurement of the metal seals. This paper presents an update on running long-term tests on metal seals at different temperatures under static conditions over longer periods of time. In addition, first results of our approach to understand the aging behavior of different elastomeric seals and neutron radiation shielding material polyethylene are discussed. T2 - PSAM 12 - Probabilistic safety assessment and management CY - Honolulu, Hawaii, USA DA - 22.06.2014 KW - Extended storage KW - Dual purpose casks KW - Metal seals KW - Elastomeric seals KW - Neutron shielding material PY - 2014 SP - 1 EP - 9 AN - OPUS4-32072 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beckmann, Jörg A1 - Schade, U. A1 - von der Ehe, Kerstin A1 - Jaunich, Matthias A1 - Wolff, Dietmar A1 - Aziz, E. F. T1 - THz and Mid IR Fourier transform spectroscopy on polyethylene irradiated with Gamma- Co60 radiation T2 - IRMMW-THz 2014 - 39th International conference on infrared, millimeter, and terahertz waves N2 - THz and mid IR spectroscopy of high molecular PE (HMW) and ultra high molecular PE (UHMW) reveals modifications of the molecular structure induced by γ-Co60 radiation. UHMW-PE and HMW-PE can be distinguished. The integral absorption in the B1u THz-region can quantitatively describe the amorphization of crystallinity. The formation of trans vinylene unsaturations and the decay of vinyl can be followed by mid IR spectroscopy T2 - IRMMW-THz 2014 - 39th International conference on infrared, millimeter, and terahertz waves CY - Tucson, Arizona, USA DA - 14.09.2014 KW - Thz and Mid IR Fourier transform spectroscopy KW - Polyethylene KW - Gamma-Co-60 radiation KW - Fourier transform spectroscopy KW - Infrared spectroscopy KW - Light absorption KW - Molecular electronic states KW - Polymers KW - MidIR Fourier transform spectroscopy KW - Terahertz spectroscopy KW - THz spectroscopy KW - γ-Co60radiation KW - HMW KW - High molecular PE KW - Ultrahigh molecular PE KW - Molecular structure modifications KW - UHMW-PE KW - HMW-PE KW - Integral absorption KW - B1uTHz-region KW - Crystallinity amorphization KW - Transvinylene unsaturation formation KW - Vinyl decay KW - Absorption KW - Radiation effects KW - Temperature measurement KW - Spectroscopy PY - 2014 UR - http://ieeexplore.ieee.org/stamp/stamp.jsp?tp=&arnumber=6956355&isnumber=6955975 SN - 978-1-4799-3877-3 DO - https://doi.org/10.1109/IRMMW-THz.2014.6956355 IS - IEEE Catalog No.: CFP14IMM-ART SP - 1 EP - 2 AN - OPUS4-32699 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kömmling, Anja A1 - Grelle, Tobias A1 - Jaunich, Matthias A1 - Goral, Milan A1 - Wolff, Dietmar T1 - Three-dimensional thermal expansion of neat and irradiated (U)HMWPE materials at elevated temperatures JF - Polymer Testing N2 - The thermal expansion of polymeric parts can be an issue in many applications where the available space is limited, or exact dimensions of the part are required. For this study, a device was designed and built that allowed measuring the thermal expansion simultaneously in all three spatial directions on cubic samples with real-scale dimensions (78 mm edge length). The results are shown between 25 °C and 125 °C for two PE materials, one HMWPE and one tempered UHMWPE, for non-irradiated samples as well as cubes that have been irradiated with 100 and 400 kGy. The results measured with the new device were very similar to those measured with conventional thermo-mechanical analysis equipment and to literature data of UHMWPE. The HMWPE material shows a much larger thermal expansion coefficient in one direction compared to the other two directions during the first heating due to frozen stresses from the pressing step during material manufacturing. These stresses are mostly released by the expansion during the first heating, so that the expansion during the second heating is more uniform. The overall volumetric expansion is the same for both heating runs. By contrast, the tempered UHMWPE material shows no significant difference between first and second heating run, as the stresses from processing could already relax in the tempering step. The irradiation treatment does not affect the values significantly for the given test set-up. KW - Lupolen KW - Ultra high molecular weight polyethylene KW - GUR KW - Coefficient of thermal expansion KW - High temperature PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-563987 DO - https://doi.org/10.1016/j.polymertesting.2022.107841 SN - 0142-9418 VL - 117 SP - 1 EP - 8 PB - Elsevier Ltd. AN - OPUS4-56398 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Mike A1 - Kömmling, Anja A1 - Jaunich, Matthias A1 - Wolff, Dietmar A1 - Zencker, Uwe A1 - Völzke, Holger A1 - Schulze, Dietmar A1 - Probst, Ulrich T1 - Testing and Numerical Simulation of Elastomers - From Specimen Tests to Simulation of Seal Behavior under Assembly Conditions T2 - Proceedings-CD, ASME 2017 Pressure Vessels & Piping Conference (PVP2017) N2 - Due to delays in the siting procedure to establish a deep geological repository for spent nuclear fuel and high level radioactive waste as well as in construction of the already licensed Konrad repository for low and intermediate level radioactive waste, extended periods of interim storage become more relevant in Germany. BAM is involved in most of the cask licensing procedures and especially responsible for the evaluation of cask-related long-term safety issues. The long-term performance of elastomer seals for lid systems of transport and storage casks, whether used as auxiliary seals in spent fuel casks or as primary seals for low and intermediate level waste packages, is an important issue in this context. The polymeric structure of these seals causes a complex mechanical behavior with time-dependent sealing force reduction. The results of a comprehensive purpose-designed test program consisting of basic compression and tension tests as well as relaxation tests on unaged specimens of representative types of elastomers (fluorocarbon rubber (FKM) and ethylene propylene diene rubber (EPDM)) at different temperatures and strain rates are presented. They were used to identify the constitutive behavior and to obtain parameters for finite element material models provided by the computer code ABAQUS®. After estimating the influence of uncertainties such as Poisson’s ratio and friction coefficient by sensitivity analyses, the chosen parameters had to prove their suitability for the finite element simulation of the specimen tests themselves. Based on this preliminary work the simulation of a specific laboratory test configuration containing a typical elastomer seal with circular cross section is presented. The chosen finite element material model and the implemented parameters had to show that they are able to represent not only the specimen behavior under predominantly uniaxial load but also the more complex stress states in real components. Deviations between the measured and calculated results are pointed out and discussed. For the consideration of long-term effects in the simulation of elastomer behavior, test results of aged specimens are needed. First information about a new test program, started recently and planned to provide these data, are given. T2 - ASME 2017 Pressure Vessels & Piping Conference (PVP2017) CY - Waikoloa, Hawaii, USA DA - 16.07.2017 KW - Time dependent effects KW - Low temperature behavior KW - Elastomeric seals KW - Aging KW - Simulation KW - Testing PY - 2017 SN - 978-0-7918-5802-8 VL - 7 SP - Article UNSP V007T07A035, 1 EP - 8 AN - OPUS4-41841 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Mike A1 - Kömmling, Anja A1 - Jaunich, Matthias A1 - Wolff, Dietmar A1 - Zencker, Uwe A1 - Völzke, Holger A1 - Schulze, Dietmar T1 - Testing and numerical simulation of elastomeric seals under consideration of time dependent effects T2 - Proceedings-CD, ASME 2016 Pressure Vessels & Piping Conference (PVP2016) N2 - Due to delays in the siting procedure to establish a deep geological repository for spent nuclear fuel and high level waste and in construction of the already licensed Konrad repository for low and intermediate level waste, extended periods of interim storage will become more relevant in Germany. BAM is involved in most of the cask licensing procedures and is responsible for the evaluation of cask-related long-term safety issues. Elastomeric seals are widely used as barrier seals for containers for low and intermediate level radioactive waste. In addition they are also used as auxiliary seals in spent fuel storage and transportation casks (dual purpose casks (DPC)). To address the complex requirements resulting from the described applications, BAM has initiated several test programs for investigating the behavior of elastomeric seals. These include experiments concerning the hyperelastic and viscoelastic behavior at different temperatures and strain rates, the low temperature performance down to -40°C, the influence of gamma irradiation and the aging behavior. The first part of the paper gives an overview of these tests, their relevant results and their possible impact on BAM’s work as a consultant in the framework of approval and licensing procedures. The second part presents an approach of the development of a finite element model using the finite element code ABAQUS®. The long-term goal is to simulate the complex elastomeric behavior in a complete lid closure system under specific operation and accident conditions. T2 - ASME 2016 Pressure Vessels & Piping Conference (PVP2016) CY - Vancouver, BC, Canada DA - 17.07.2016 KW - Elastomeric seals KW - Testing KW - Low temperature behavior KW - Aging KW - Simulation KW - Time dependent effects PY - 2016 SN - 978-0-7918-5045-9 VL - 7 SP - Paper 63192, 1 EP - 10 AN - OPUS4-37046 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Grelle, Tobias A1 - Wolff, Dietmar A1 - Jaunich, Matthias T1 - Temperature-dependent leak tightness of elastomer seals after partial and rapid release of compression JF - Polymer Testing N2 - A device has been designed, built and tested that allows the investigation of effects of dynamic loads on the leak tightness of elastomer seals at low temperatures. With the test setup, the compression of the tested seal can be reduced by a defined degree in a time period of less than 1 s. For the evaluation of the leak tightness, leakage rates can be determined. It was shown that the rapid partial release of an elastomer seal leads to its failure already at the beginning of the rubber–glass transition and, therefore, at significantly higher temperatures than the loss of leak tightness observed under static conditions. KW - Sealing material KW - Elastomer KW - Dynamic loading KW - Low temperature behaviour KW - Leakage rate PY - 2015 DO - https://doi.org/10.1016/j.polymertesting.2015.09.009 SN - 0142-9418 VL - 48 SP - 44 EP - 49 PB - Elsevier Ltd. CY - Amsterdam [u.a.] AN - OPUS4-34445 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zaghdoudi, Maha A1 - Kömmling, Anja A1 - Jaunich, Matthias A1 - Wolff, Dietmar T1 - Scission, cross-linking, and physical relaxation during thermal degradation of elastomers JF - Polymers N2 - Elastomers are susceptible to chemical ageing, i.e., scission and cross-linking, at high temperatures. This thermally driven ageing process affects their mechanical properties and leads to limited operating time. Continuous and intermittent stress Relaxation measurements were conducted on ethylene propylene diene rubber (EPDM) and hydrogenated nitrile butadiene rubber (HNBR) samples for different ageing times and an ageing temperature of 125 °C. The contributions of chain scission and cross-linking were analysed for both materials at different ageing states, elucidating the respective ageing mechanisms. Furthermore, compression set experiments were performed under various test conditions. Adopting the two-network model, compression set values were calculated and compared to the measured data. The additional effect of physical processes to scission and cross-linking during a long-term thermal exposure is quantified through the compression set analysis. The characteristic times relative to the degradation processes are also determined. KW - Ageing KW - Scission KW - Cross-linking KW - Compression set KW - Physical relaxation PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-486091 DO - https://doi.org/10.3390/polym11081280 SN - 2073-4360 VL - 11 IS - 8 SP - 1280, 1 EP - 12 PB - MDPI AN - OPUS4-48609 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völzke, Holger A1 - Wolff, Dietmar T1 - Safety aspects of long dry interim cask storage of spent fuel in Germany T2 - IHLRWM 2011 - International high-level radioactive waste management conference (Proceedings) N2 - Dry cask storage of spent fuel and high active waste front reprocessing is licensed and established in Germany for up to 40years so far. About 10years ago, the strategy has been shifted from centralized storage using facilities in Ahaus and Gorleben to cit-site storage facilities in Order to avoid immediate cask shipping from nuclear power plants. At present, several hundred casks are stored safeiy and without any major problem. BAM is highly involved in cask specific safety evaluations within the scope of licensing procedures as well as of quality assurance procedures during cask fabrication, loading and storage. A major prerequisite for any cask storage license is a valid transport Type B license. Subsequently, cask transportability has to be ensured at any point during the entire storage period. So far, this requirement is met by continuous maintenance of the Type B license. Anyhow, IAEA Type B regulations do not consider permanently loaded storage casks that have the sole purpose of being finally shipped öfter decades of storage inducing ageing effects. No transport safety demonstration has to be performed on aged cask components. T2 - International high-level radioactive waste management conference (IHLRWMC 2011) CY - Albuquerque, NM, USA DA - 10.04.2011 KW - Safety KW - Cask KW - Interim storage KW - Spent fuel PY - 2011 SP - 712 EP - 719 AN - OPUS4-23651 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kömmling, Anja A1 - Jaunich, Matthias A1 - Wolff, Dietmar T1 - Revealing effects of chain scission during ageing of EPDM rubber using relaxation and recovery experiment JF - Polymer Testing N2 - Both chain scission and crosslinking reactions occur during ageing of EPDM rubber. However, with many conventional polymer analysis methods such as hardness and DMA, it is hardly possible to obtain information about the contribution of each reaction type to the measured data. For example, hardness and Tg both increase during ageing of EPDM, indicating crosslinking during ageing, but it is not clear whether this is partly counterbalanced by chain scission reactions which would lower hardness and Tg. An indication that chain scission reactions probably counteract the hardness or Tg increase by crosslinking is given by Compression Set (CS) measurements. CS exhibits a higher change than hardness or Tg, as CS increases additively through both chain scission and crosslinking reactions. In order to elucidate the share of chain scission reactions in the total degradation, a method testing relaxation and recovery behaviour using DMA equipment was applied. The method revealed the strong influence of chain scissions, leading to more pronounced relaxation and higher residual strain after compression. KW - Compression set KW - DMA KW - Nnetwork KW - Crosslinking PY - 2016 DO - https://doi.org/10.1016/j.polymertesting.2016.10.026 SN - 0142-9418 SN - 1873-2348 IS - 56 SP - 261 EP - 268 PB - Elsevier Ltd. AN - OPUS4-38012 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -