TY - CONF A1 - Weltschev, Margit T1 - Evaluation of the resistance of metallic and polymeric materials used for tanks for the transport of dangerous goods T2 - ACHEMA CY - Frankfurt am Main, Germany DA - 2012-06-20 PY - 2012 AN - OPUS4-26089 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Evaluation of the resistance of metallic materials under the influence of biofuels N2 - Changes in fuel composition and the introduction of alternative fuels often create problems of corrosion and degradation in materials. The objective of this research was to determine the corrosion behaviour of commercial metallic tank materials (unalloyed steels, austenitic CrNi- and CrNiMo-steels, aluminium and its alloys) in fuels and heating oil with admixtures of biogenic sources, such as gasoline with addition of ethanol (E10, E85), pure biodiesel and heating oil with 10 % biodiesel (B10). Metallic tank materials were evaluated as resistant in a liquid if the annual corrosion rate due to uniform corrosion did not exceed 0.1 mm/year, and localized corrosion effects in the form of pitting corrosion, stress corrosion cracking and crevice corrosion did not occur. The corrosion rates of the tank materials after exposure to E10, E85, non-aged and two-year aged pure biodiesel, and non-aged and one-year aged heating oil B10 for four weeks at 50 °C, according to DIN 50905/4, were well below the limit of 0.1 mm/year. For the unalloyed steels, the formation of rust was observed independently of the biofuels amount of ageing. U-bend specimens made of unalloyed steel were not damaged in form of stress corrosion cracking in all test fuels at this test temperature. T2 - CORROSION 2017 CY - New Orleans, LA, USA DA - 26.03.2017 KW - Biodiesel KW - Bioethanol KW - Tank materials KW - Corrosion resistance KW - Stress corrosion cracking PY - 2017 AN - OPUS4-39642 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Comparison of the Corrosion Resistance to Dangerous Goods of Austenitic CrNiMo and Duplex Steels T2 - CORROSION 2014 CY - San Antonio, TX, USA DA - 2014-03-09 PY - 2014 AN - OPUS4-30429 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - DGMK-Projekt 780: Entwicklung einer Prüfmethode zur Bewertung der Materialbeständigkeit von Bauteilen in Mitteldestillatanwendungen N2 - Für Bauteile (Komponenten) von Versorgungsanlagen für flüssige Brenn- und Kraftstoffe muss die Beständigkeit der metallenen Werkstoffe und Polymere nachgewiesen werden. Im Anwendungsfall von Heizöl mit 20 % biogenen Anteilen in Form von Rapsölfettsäuremethylester (FAME, Biodiesel) ist es für eine konservative Beurteilung des Korrosionssystems Werkstoff/Medium/Umgebung wichtig, die Alterungseffekte des Mediums einzubeziehen. Entwicklung eines Prüfverfahrens für die Untersuchung der Beständigkeit von metallenen Werkstoffen und Polymeren in Heizöl und Heizöl-FAME-Blends, das für eine Vorauswahl der Werkstoffe und zum Nachweis der Beständigkeit im Hinblick auf die bauaufsichtlichen Zulassungsverfahren geeignet ist. Ein Schwerpunkt wird bei den metallenen Werkstoffen auf der Erprobung von Messmethoden liegen, mit denen sich in kurzer Versuchszeit ein Korrosionsangriff detektieren lässt. Die untersuchten Werkstoffe Aluminium, Stahl 1.0037, 1.4301, Kupfer, Messing (CuZn40Pb) und Zink (ZP0410) sind in B0, B20, B100 und in 6 Jahre altem B100 beständig. Auch in einem Jahr alten B20 und in einem Jahr alten B100 sind die Werkstoffe beständig. Bei Kupfer blieb die Korrosionsrate in der Flüssigphase sowohl in B20 (0 μ m/ a) als auch in B100 (4 μ m/ a) nach einem Jahr unverändert. Für das 6 Jahre alte B100 stieg die Korrosionsrate des Kupfers an (16 μ m/a). Im Gegensatz dazu sank bei Messing die Korrosionsrate in der Flüssigphase mit dem Alter des Brennstoffs, nach einem Jahr für B20 von 4 μ m/ a auf 1 μ m/a und für B100 von 36 μ m/ a auf 6 μ m/ a, im 6 Jahre alten B100 lag die Korrosionsrate des Messings bei 0 μ m/ a. In 8 Jahre altem B10 trat bei Zink in der Flüssigphase Flächenkorrosion auf, es ist in dem Medium demnach nicht beständig. Messing zeigte örtliche Korrosion in der Gasphase, es ist folglich unbeständig und für den Einsatz in stark gealterten B10 nicht geeignet. Aluminium, 1.0037, 1.4301 und Kupfer sind in dem 8 Jahre alten B10 beständig. Die Änderung der Zugfestigkeit und der Reißdehnung von ACM, HNBR und FKM in Heizöl, B20 und gealterten B10 beträgt < 15 %. Diese Werkstoffe sind in Heizöl, B20 und in gealterten B10 unter Berücksichtigung des von der BAM zur Beurteilung der Beständigkeit festgelegten Grenzwertes von 15 % bei 40 °C als beständig zu bewerten. PUR ist bei 40 °C nicht beständig in B20 und in gealtertem B10. Bei 70 °C ist HNBR nicht in B20 beständig aufgrund der Verringerung der Zugfestigkeit (40 %) und der Reißdehnung (50 %). FKM ist bei 70 °C in Heizöl und in B20 beständig. T2 - Sitzung AK Prüfstellen CY - Berlin, Germany DA - 18.09.2019 KW - Heizöl mit 20% Biodiesel (B20) KW - Beständigkeit KW - Metallene Werkstoffe KW - Polymere Werkstoffe KW - Zugeigenschaften KW - Shore-Härte PY - 2019 AN - OPUS4-50188 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Compatibility of polymers with aged heating oil containing 10 % and 20 % biodiesel under static conditions N2 - Biodiesel is viewed as a major source of energy. In areas such as the European Un-ion, where 80 % of the oil-based fuel is imported, there is also the desire to reduce dependence on external oil supplies. Materials compatibility is a major concern whenever the fuel composition is changed. The question arises of whether polymeric materials are resistant to heating oil with 20 % biodiesel (B20) in comparison to pure heating oil. The polarity of biodiesel increases its solvency and facilitates permeation and extrac-tion. Solvation, swelling and/or extraction lead to changes in the physical properties. Extraction alters the fuel chemistry. These chemical changes could also accelerate the degradation (hydrolysis and oxidation) of the polymeric material with the loss of additives and stabilizers. Exposure tests to determine the resistance of polymers frequently used for compo-nents in middle distillate facilities, such as ACM, FKM, HNBR, PA, PE, POM, PUR and PVC in heating oil and a blend of heating oil and 20 % biodiesel (B20) were al-ready performed. The objective of this research was to determine the resistance of these polymers in 8-year aged heating oil blend B10 and 1-year aged blend B20 at 40 °C. Mass, tensile strength, breaking elongation and Shore hardness A (D) of the test specimens were determined before and after exposure for 84 (42) days in the test fuels under static conditions. There is not determined a threshold for the reduction in tensile properties and Shore hardness in the international standards. Therefore, a threshold of 15 % was deter-mined for the evaluation of the compatibility. A significant reduction in Shore hardness was determined after exposure of ACM and PUR test specimens in 1-year aged B20. The tensile strength of PUR test specimens in 1-year aged B20 was reduced by more than 50 %, and the breaking elongation by more than 30 %. A decrease in breaking elongation was measured for POM test specimens after ex-posure to 1-year aged B20 by 25 % (limited resistance). 8-year aged B10 had a stronger effect than 1-year aged B20 on the polymers. ACM test specimens were softened by B10 resulting in a drop of Shore hardness by over 20 %. B10 reduced tensile strength and breaking elongation of PUR test specimens by over 50 %. In contrast, the breaking elongation of POM was increased by over 270 %. It can be concluded that the polymers HNBR, FKM, PA6, PE and PVC are resistant in 1-year aged B20 whereas ACM and POM are limited resistant. PUR is not re-sistant. HNBR, FKM, PA6, PE and PVC are resistant in 8-year aged B10, whereas PUR and POM are not resistant, and ACM just limited resistant. T2 - EUROCORR 2020 CY - Online meeting DA - 07.09.2020 KW - Aged heating oil with 10% and 20% biodiesel KW - Resistance of polymers KW - Tensile properties KW - Shore hardness PY - 2020 AN - OPUS4-51240 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Bewertung de Beständigkeit von metallischen Werkstoffen und polymeren Dichtungswerkstoffen unter dem Einfluss von Biokraftstoffen T2 - Beiratssitzung des Normenausschusses Tankanlagen im DIN CY - DIN Berlin DA - 2014-11-06 PY - 2014 AN - OPUS4-31924 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Compatibility of polymers with heating oil with 20 % biodiesel at different temperatures under static and compressed conditions N2 - Biodiesel is viewed as a major source of energy. In areas such as the European Union, where 80 % of the oil-based fuel is imported, there is also the desire to reduce dependence on external oil supplies. Materials compatibility is a major concern whenever the fuel composition is changed. The question arises of whether polymeric materials are resistant to heating oil with 20 % biodiesel (B20) in comparison to pure heating oil. The polarity of biodiesel increases its solvency and facilitates permeation and extraction. Solvation, swelling and/or extraction lead to changes in the physical properties. Extraction alters the fuel chemistry. These chemical changes could also accelerate the degradation (hydrolysis and oxidation) of the polymeric material with the loss of additives and stabilizers. The objective of this research was to determine the resistance of frequently used materials for components in middle distillate facilities such as ACM, FKM, HNBR, PA, PE, POM, PUR and PVC in heating oil and heating oil blend B20 for 84 days at 40 °C, and FKM, HNBR, PA, POM, PUR and PVC at 70 °C. Mass, tensile strength, breaking elongation and Shore hardness A (D) of the test specimens were determined before and after exposure for 84 (42) days in the test fuels under static conditions. For the investigations under compressed conditions, the mass and the compression set of FKM test specimens were determined before and after exposure for 3, 7, 14, 28, 56 and 90 days in B20 at 40 °C and 70 °C according to ISO 815-1 “Rubber, vul-canized or thermoplastic - determination of compression set – Part 1: At ambient or elevated temperatures”. There is not determined a threshold for the reduction in tensile properties and Shore hardness in the international standards. Therefore, a threshold of 15 % was determined for the evaluation of the compatibility. The change of tensile strength and breaking elongation of test specimens made of ACM, FKM, HNBR, PA, PE, POM, PUR and PVC exposed to heating oil and the blend B20 was less than 15 % at 40 °C. A maximum reduction in Shore hardness A of 14 % was determined for ACM at 40 °C and for HNBR of 15 % at 70 °C. It can be concluded that ACM, FKM, HNBR, PA, PE, POM, PVC and PUR were resistant in B20 at 40°C. FKM, PA, POM and PVC were evaluated as resistant in heat-ing oil and B20 at 70 °C, HNBR and PUR were not resistant in these fuels at 70°C. Based on the mass increase and compression set values of FKM test specimens it can be stated that FKM is resistant in B20 under compressed conditions at 40 °C and 70 °C. T2 - EUROCORR 2019 CY - Sevilla, Spain DA - 09.09.2019 KW - Heating oil - biodiesel - blend KW - Polymeric materials KW - Compatibility KW - Tensile properties KW - Shore Hardness PY - 2019 AN - OPUS4-49002 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Use of Higher Alloyed Metallic Materials and Duplex Steels for Transport Tanks of Dangerous Goods T2 - Steels in Cars and Trucks (SCT 2011) CY - Salzburg, Austria DA - 2011-06-06 PY - 2011 AN - OPUS4-23801 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Compatibility of metallic tank and polymeric sealing materials with biofuels T2 - ACHEMA CY - Frankfurt am Main DA - 2015-06-15 PY - 2015 AN - OPUS4-33534 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -