TY - CONF A1 - Weltschev, Margit A1 - Hoffmann, Gabi A1 - Haufe, Manuela A1 - Kohl, Anka T1 - Investigations on the degree of damage of polyethylene grades of heating oil storage tanks after a service life in excess of 25 years N2 - Plastic storage tanks for heating oil have been on the market since the early 1970s in Germany, mainly made from polyethylene grades. Tank manufacturers and experts examining the tanks recommend the replacement of the tanks to ensure the safety after a period of 30 years. The tank manufacturer is legally obliged to specify the service life of the tanks. Polyethylene is subject to ageing by alteration of the properties during its life cycle. A distinction is made between internal and external ageing processes. The internal ageing, such as the breakdown of internal stresses, post-crystallization, phase sepa-ration of multicomponent systems and plasticizer migration is attributed to thermodynamically instable conditions of the plastic material. The external ageing in form of stress cracking, fatigue cracking, thermooxidative degradation or swelling is based on physical or chemical effects of the environment of the polyethylene grade. The degree of ageing and the nature of the degradation process mainly depend on the chemical degradation of the polyethylene, the wall thickness of the tank and the environmental conditions. There are no results available on the long-term behaviour of the polyethylene grades used as materials for heating oil storage tanks, especially after a service life of more than 25 years. The aim of this investigation was the determination of the factual degree of damage in comparison to the uncontaminated polyethylene grades. Data on the melt flow rate (MFR) and density of the used polyethylene grades are available because the BAM was the competent authority for the approval of the plastic heating oil storage tanks until the end of the 1980s. The technical service of specialist companies for fuel tank disposal supplied tank sections from the bottom, the shell and the roof of 8 segregated heating oil storage tanks. Some of the tanks had been in service for more than 30 years. Two polyethylene grades mainly were used as materials for these tanks over this time. The determination of the MFR according to EN ISO 1133 and the FTIR spectroscopy followed standard test methods. The highest average percentage increase in the MFR was determined as 31- 43 % for the bottom section of the tanks, for both the inner shell and the outer shell. The lowest increase in MFR was measured for the top of the tank, with 6 - 12 % for the inner shell and 0 - 8 % for the outer shell. The tank shell sections had an average percentage increase in MFR of 10 - 33 % for the inner shell and of 14 - 40 % for the outer shell. The oxidative damage of the polyethylene grades was highest in the bottom area due to the permanent contact with the heating oil and degradation products. The microtome cuttings were analyzed with image-guided infrared microscopy in the transmission mode and confirmed the results obtained with the MFR measurements. In summary it can be concluded that the oxidative damage of the polyethylene grades after long-term contact with heating oil is relative low. T2 - EUROCORR 2017 CY - Prag, Czech Republic DA - 03.09.2017 KW - Polyethylene KW - Heating oil tanks KW - Service life KW - Degree of degradation PY - 2017 AN - OPUS4-41907 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Bäßler, Ralph T1 - Evaluation of the Resistance of Metallic Materials under the Influence of Biofuels N2 - Changes in fuel composition and the introduction of alternative fuels often create problems of corrosion and degradation in materials. The objective of this research was to determine the corrosion behaviour of commercial metallic tank materials (unalloyed steels, austenitic CrNi- and CrNiMo-steels, aluminium and its alloys) in fuels and heating oil with admixtures of biogenic sources, such as gasoline with addition of ethanol (E10, E85), pure biodiesel and heating oil with 10 % biodiesel (B10). Metallic tank materials were evaluated as resistant in a liquid if the annual corrosion rate due to uniform corrosion did not exceed 0.1 mm/year, and localized corrosion effects in the form of pitting corrosion, stress corrosion cracking and crevice corrosion did not occur. The corrosion rates of the tank materials after exposure to E10, E85, non-aged and two-year aged pure biodiesel, and non-aged and one-year aged heating oil B10 for four weeks at 50 °C, according to DIN 50905/4, were well below the limit of 0.1 mm/year. For the unalloyed steels, the formation of rust was observed independently of the biofuels amount of ageing. U-bend specimens made of unalloyed steel were not damaged in form of stress corrosion cracking in all test fuels at this test temperature. T2 - CORROSION 2017 CY - New Orleans, LA, USA DA - 26.03.2017 KW - Biodiesel KW - Bioethanol KW - Tank materials KW - Corrosion resistance KW - Stress corrosion cracking PY - 2017 SP - Paper No 8854, 1 EP - 12 PB - NACE International Publications Division CY - Houston, Texas, USA AN - OPUS4-39638 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Bäßler, Ralph T1 - Evaluation of the resistance of metallic materials under the influence of biofuels N2 - Changes in fuel composition and the introduction of alternative fuels often create problems of corrosion and degradation in materials. The objective of this research was to determine the corrosion behaviour of commercial metallic tank materials (unalloyed steels, austenitic CrNi- and CrNiMo-steels, aluminium and its alloys) in fuels and heating oil with admixtures of biogenic sources, such as gasoline with addition of ethanol (E10, E85), pure biodiesel and heating oil with 10 % biodiesel (B10). Metallic tank materials were evaluated as resistant in a liquid if the annual corrosion rate due to uniform corrosion did not exceed 0.1 mm/year, and localized corrosion effects in the form of pitting corrosion, stress corrosion cracking and crevice corrosion did not occur. The corrosion rates of the tank materials after exposure to E10, E85, non-aged and two-year aged pure biodiesel, and non-aged and one-year aged heating oil B10 for four weeks at 50 °C, according to DIN 50905/4, were well below the limit of 0.1 mm/year. For the unalloyed steels, the formation of rust was observed independently of the biofuels amount of ageing. U-bend specimens made of unalloyed steel were not damaged in form of stress corrosion cracking in all test fuels at this test temperature. T2 - CORROSION 2017 CY - New Orleans, LA, USA DA - 26.03.2017 KW - Biodiesel KW - Bioethanol KW - Tank materials KW - Corrosion resistance KW - Stress corrosion cracking PY - 2017 AN - OPUS4-39642 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Hoffmann, Gabi A1 - Kohl, Anka A1 - Haufe, Manuela T1 - Untersuchungen des Schädigungsgrades von Kunststoffen als Werkstoffe von Heizöllagerbehältern nach einer Nutzungsdauer > 25 Jahre N2 - Heizöllagerbehälter aus Kunststoffen (z.B. Polyethylen) sind für einen sicheren Betrieb von 30 Jahren, dem Zeitraum der Produkthaftung, ausgelegt. Die Tankhersteller empfehlen zur Gewährleistung der Sicherheit nach Ablauf von 30 Jahren den Ersatz dieser Behälter. Kunststoffe unterliegen im Laufe ihrer Nutzungsdauer der Alterung durch die Veränderung ihrer Eigenschaften. Das Ausmaß der Alterung und die Art des Abbauvorganges hängen im Wesentlichen vom chemischen Abbau des Kunststoffes, der Wanddicke des Behälters und den Umgebungsbedingungen ab. Aufgrund der Komplexität der Alterungsvorgänge sind Aussagen zum Langzeitverhalten bzw. zur Lebensdauer der Heizöllagerbehälter ohne geeignete Langzeitprüfungen problematisch. Bisher liegen keine Untersuchungen zum Langzeitverhalten der Kunststoffe vor, insbesondere nach einer Nutzungsdauer über 20 Jahre. In der BDH-Broschüre: Effiziente Systeme und erneuerbare Energien wird darauf hingewiesen, dass ca. 45 % der Heizöllagerbehälter aus Kunststoffen in Deutschland 26 Jahre und älter sind. Viele dieser Tankanlagen sind zudem noch nie von einem Sachverständigen überprüft worden. Schätzungen gehen davon aus, dass mehr als 10.000.000 Tankanlagen aus Kunststoffen in Deutschland vor 1987 errichtet wurden. Ziel der Untersuchungen ist, den Schädigungsgrad der Kunststoffe im Vergleich zu den unbelasteten Werkstoffen zu ermitteln. Da die BAM bis Ende der 80-iger Jahre für die Zulassung dieser Behälter zuständig war, sind die Daten über den eingesetzten Werkstoff für den Vergleich noch vorhanden. Der Bundesverband Lagerbehälter e.V. und das Institut für Wärme und Oeltechnik (IWO) befürworten diese Untersuchungen, um eine Überalterung der Tankanlagen zu vermeiden. Diese Überalterung könnte die zukünftige Gefahr für die Heizöltankanlage sein, nicht der Wettbewerb mit anderen Energieformen. T2 - BUW - Ausgewählte Kapitel der Werkstoffkunde CY - Wuppertal, Germany DA - 12.01.2018 KW - Heizöllagerbehälter KW - Polyethylen KW - Schädigung KW - Lebensdauer PY - 2018 AN - OPUS4-44191 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Haufe, Manuela A1 - Kohl, Anka A1 - Rehfeldt, Rainer T1 - Resistance of polyethylene grades with permeation barriers in biofuels N2 - Biofuels including ethanol and biodiesel (FAME) represent a renewable fuel alternative to petroleum-derived transport fuels. The aim of this work was to study the interaction between high density polyethylene (HDPE) with permeation barriers in form of polyamide (PA) and fluorination, and biofuels such as E85 (fuel with 85 % ethanol), biodiesel and B10 (heating oil with 10 % biodiesel). 10 l jerrycans made of polyethylene with permeation barrier of PA were filled with E85 and biodiesel and exposed to temperatures of 20 °C and 40 °C for 5 years. Half of the 20 l jerrycans of HDPE for filling with B10 were fluorinated at the inner layer to prevent permeation before the exposure. Tensile properties were determined once a year, and FTIR-spectroscopy was used to evaluate possible changes. The tensile properties tensile strength and breaking elongation of HDPE jerrycan cuttings with permeation barrier decreased, but not significantly, after immersion in E85, biodiesel and B10. The elasticity modulus of the polyethylene grades was especially reduced during exposure to E85. The FTIR spectra of HDPE jerrycan cuttings with permeation barrier showed that immersion tests for five years with the test fuels at 20 °C and 40 °C did not lead to a decomposition of the permeation barriers. T2 - CORROSION 2018 CY - Phönix, Arizona, USA DA - 16.04.2018 KW - Polyethylene grades KW - Biofuels KW - Permeation barriers KW - FTIR spectra PY - 2018 SP - Paper 10543, 1 EP - Paper 10543, 12 PB - NACE International CY - Houston, Texas, USA AN - OPUS4-44768 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Haufe, Manuela A1 - Kohl, Anka A1 - Rehfeldt, Rainer T1 - Resistance of polyethylene grades with permeation barriers in biofuels N2 - Biofuels including ethanol and biodiesel (FAME) represent a renewable fuel alternative to petroleum-derived transport fuels. The aim of this work was to study the interaction between high density polyethylene (HDPE) with permeation barriers in form of polyamide (PA) and fluorination, and biofuels such as E85 (fuel with 85 % ethanol), biodiesel and B10 (heating oil with 10 % biodiesel). 10 l jerrycans made of polyethylene with permeation barrier of PA were filled with E85 and biodiesel and exposed to temperatures of 20 °C and 40 °C for 5 years. Half of the 20 l jerrycans of HDPE for filling with B10 were fluorinated at the inner layer to prevent permeation before the exposure. Tensile properties were determined once a year, and FTIR-spectroscopy was used to evaluate possible changes. The tensile properties tensile strength and breaking elongation of HDPE jerrycan cuttings with permeation barrier decreased, but not significantly, after immersion in E85, biodiesel and B10. The elasticity modulus of the polyethylene grades was especially reduced during exposure to E85. The FTIR spectra of HDPE jerrycan cuttings with permeation barrier showed that immersion tests for five years with the test fuels at 20 °C and 40 °C did not lead to a decomposition of the permeation barriers. T2 - CORROSION 2018 CY - Phönix, Arizona, USA DA - 16.04.2018 KW - Polyethylene grades KW - Biofuels KW - Permeation barriers KW - FTIR spectra PY - 2018 AN - OPUS4-44758 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stajanca, Pavol A1 - Baensch, Franziska A1 - Baer, Wolfram A1 - Chruscicki, Sebastian A1 - Homann, Tobias A1 - Seifert, Stefan A1 - Schmidt, Dirk A1 - Weltschev, Margit A1 - Wossidlo, Peter A1 - Habib, Abdel Karim T1 - Monitoring of pipes by distributed acoustic fibre optic sensors – A large-scale test on a pipeline under realistic operation condition N2 - The monitoring of oil and gas pipelines by means of distributed fibre optic sensors is becoming common. The most recent development in the field of fibre optic sensing is the distributed acoustic sensing (DAS), which allows to detect and to localize third party threats to pipelines. For this purpose, fibre optic telecommunication cables located close to the pipelines are usually used. However, DAS carries a far greater potential for continuous condition monitoring of pipelines. The interdisciplinary research project AGIFAMOR (Ageing Infrastructures – Fibre Optic Monitoring of Pipes) at BAM investigates a new technical approach to extend the application field of DAS towards the detection and localization of acoustic signals that indicate critical alterations and certain damage scenarios originated from within the pipeline or the pipe wall. Therefore, the optical fibre sensors are applied onto the pipe itself and the application procedure towards an optimal acoustic signal transduction is optimized. A number of laboratory scale experiments were performed focusing on the signal transmission of acoustic signals as well as the detection of damages in the pipe wall by means of DAS. Furthermore, real-scale tests on a pipeline DN100 of 38m length have been carried out at the BAM test site for technical safety (BAM-TTS) to study the detection and localization of leaks and of changing flow profiles due to corrosion or sedimentation processes. T2 - 13th Pipeline Technology Conference CY - Berlin, Germany DA - 12.03.2018 KW - Pipeline monitoring KW - Distributed acoustic sensing KW - Fiber optic sensing PY - 2018 SN - 2198-428X SP - Poster session, paper 9, 1 EP - 8 PB - EITEP (Euro Institute for Information and Technology Transfer in Environmental Protection) CY - Hannover AN - OPUS4-44519 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Baensch, Franziska A1 - Baer, Wolfram A1 - Chruscicki, Sebastian A1 - Homann, Tobias A1 - Prager, Jens A1 - Schmidt, Dirk A1 - Stajanca, Pavol A1 - Weltschev, Margit A1 - Wossidlo, Peter A1 - Habib, Abdel Karim T1 - AGIFAMOR: Anwendung der verteilten akustischen und faseroptischen Sensorik zur kontinuierlichen Überwachung von Rohrleitungen - Teil 2: Technische Hintergründe - Schadensursachen und Prüfeinrichtungen N2 - Schäden an Rohrleitungen können zu hohen Umweltbelastungen und wirtschaftlichen Schäden führen. Um die dauerhafte Verfügbarkeit der Infrastruktur zu gewährleisten, wird im Rahmen des Projekts AGIFAMOR an der Bundesanstalt für Materialforschung und -prüfung (BAM) erprobt, inwiefern das Verfahren der verteilten akustischen faseroptischen Sensorik (Distributed acoustic sensing – DAS) zur kontinuierlichen Überwachung von Rohrleitungen eingesetzt werden kann. Neben der DAS werden erprobte Verfahren der zerstörungsfreien Prüfung wie Schallemissionsanalyse (SEA) und Beschleunigungssensoren eingesetzt. An dieser Stelle soll detailliert auf die Hauptschadensursachen an Rohrleitungen, den Versuchsstand zur mechanischen Belastung von Rohren sowie die Möglichkeiten zu Untersuchungen im Realmaßstab eingegangen werden. KW - Schadensursachen an Rohrleitungen KW - Monitoring von Rohrleitungen KW - Verteilte Faseroptische Sensorik KW - Rohrbiegeprüfstand KW - Leckage PY - 2018 SN - 2191-0073 VL - 8 IS - 3 SP - 24 EP - 29 PB - Springer VDI-Verlag GmbH & Co. KG CY - Düsseldorf AN - OPUS4-44507 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Untersuchungen des Schädigungsgrades von Kunststoffen als Werkstoffe von Heizöllagerbehältern nach einer Nutzungsdauer > 25 Jahre N2 - Heizöllagerbehälter aus Polyethylenformstoffen werden seit Beginn der 70-iger Jahre in Deutschland hergestellt. Die Hersteller empfehlen zur Gewährleistung der Sicherheit nach Ablauf von 30 Jahren den Ersatz dieser Behälter. Polyethylenformstoffe unterliegen im Laufe ihrer Nutzungsdauer der Alterung durch die Veränderung ihrer Eigenschaften. Das Ausmaß der Alterung und die Art des Abbauvorganges hängen im Wesentlichen vom chemischen Abbau des Polyethylens, der Wanddicke des Behälters und den Umgebungsbedingungen ab. Bisher lagen keine Untersuchungen zum Langzeitverhalten der Polyethylenformstoffe vor, insbesondere nach einer Nutzungsdauer der Tanks über 30 Jahre. Ziel der Untersu-chungen war, den tatsächlichen Schädigungsgrad der Polyethylenformstoffe im Vergleich zu den unbelasteten Formstoffen zu ermitteln. Da die BAM bis Mitte der 90-iger Jahre für die Prüfungen und Gutachten zur Zulassung dieser Behälter zuständig war, sind die Werkstoffdaten noch vorhanden. Als Untersuchungsmethoden wurden die Bestimmung der Schmelze-Masse-Fließrate (MFR) und die Fourier-Transformation-IR-Spektroskopie (FTIR) von Tankausschnitten aus dem Bereich des Bodens, des Mantels und des Daches von 10 ausgesonderten Behältern aus den Polyethylenformstoffen A und B herangezogen. Die Messungen der MFR der Tankaus-schnitte aus diesen Bereichen zeigten Unterschiede in den Werten in Abhängigkeit vom Ge-wicht (5 kg oder 21,6 kg), welches eingesetzt wurde. Eine Abnahme der MFR-Werte wurde für die größere Anzahl der Tankwandungsausschnitte aus dem Formstoff B nach einer Lebensdauer der Tanks > 30 Jahre gemessen. Dieser Formstoff wurde hauptsächlich durch innere Alterung infolge Vernetzungen, Verzweigungen und Weichmacherverlust und weniger durch oxidativen Abbau geschädigt. Die FTIR-Messungen der Proben aus dem Bereich des Bodens und des Mantels der Tanks zeigten, dass die Intensität der asymmetrischen/symmetrischen CH2 -Streckschwingungen im Bereich: 2800 - 2900 cm-1 und der CH2 -Biegeverformungsschwingung bei 1400 cm-1 aufgrund von Kettenspaltungen zugenommen haben. Die Intensität der Carbonylstreckschwingung C=O bei 1740 cm-1 ist niedrig. Sie ist ein Maß für die Oxidation des Polymerwerkstoffes. T2 - Behördenerfahrungsaustausch 2018 CY - Berlin, Germany DA - 04.06.2018 KW - Polyethylen KW - Heizöllagerbehälter KW - Schädigungsgrad PY - 2018 AN - OPUS4-45138 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Otremba, Frank A1 - Sklorz, Christian A1 - Rehfeldt, Rainer T1 - Impact of biocomponents in the fuel and heating oil on the compatibility of fluorocarbon rubber under compressed conditions N2 - Materials compatibility is a major concern whenever the fuel composition is changed. The question arises of whether sealing materials are resistant to fuels with bioethanol and biodiesel (rapeseed oil fatty acid methyl ester). Previous research considered the resistance of frequently used sealing materials such as FKM (fluorocarbon rubber), FVMQ (methyl-fluoro-silicone rubber), VMQ (methyl-vinyl-silicone rubber), EPDM (ethylene-propylene-diene rubber), CR (chloroprene rubber), CSM (chlorosulfonated polyethylene), IIR (butyl rubber), PA (polyamides), NBR (acrylonitrile-butadiene rubber) and PUR (polyester urethane rubber) in fuels and heating oil with admixtures of biogenic substances such as biodiesel and B10 (heating oil with 10 % biodiesel) under purely static conditions. The aim of this study was to evaluate the fluorocarbon rubber performance under compressed conditions. For the investigations, the mass and the compression set of the FKM test specimens were determined before and after exposure for 3, 7, 14, 28, 56 and 90 days in E10 (fuel with 10 % ethanol), E85 (fuel with 85 % ethanol), biodiesel (fatty acid methyl ester, FAME), Super (fuel with max. 5 % ethanol), diesel fuel with max. 5 % biodiesel, pure diesel fuel, Super Plus (fuel without ethanol) and heating oil with 10 % biodiesel (B10) at 40 °C according to ISO 815-1 “Rubber, vulcanized or thermoplastic - determination of compression set – Part 1: At ambient or elevated temperatures”. The compression set test belongs beside the determination of the Shore hardness, the density and the tensile properties to the basic test methods for elastomers. It was measured in regular time intervals up to a re-drying of more than 90 days after relaxation of test specimens. For comparison, FKM test specimens were exposed without fuel under compressed conditions at 40 °C. The highest mass increase of FKM test specimens was measured after 90 days exposure in E10 by 9 %, followed by 8 % in Super fuel, by 4 % in E85 and by 0.6 % in biodiesel. Mass increase and swelling of the test specimens in E10 and Super fuel with max. 5 % ethanol had an influence on the compression set values which were subject to high fluctuations in comparison to the values obtained after exposure to other fuels such as biodiesel, diesel fuel and B10. The results of the present work confirmed the higher swelling of the elastomers such as FKM in E10 obtained under static condition. It can be concluded on the basis of the mass increase and compression set values that FKM is resistant in all fuels under compressed conditions at 40 °C. T2 - EUROCORR 2018 CY - Krakow, Poland DA - 09.09.2018 KW - Sealing materials KW - Compression set KW - Compatibility KW - Fuels KW - Heating oil KW - Biodiesel KW - Bioethanol PY - 2018 AN - OPUS4-45935 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Hoffmann, Gabi A1 - Rehfeldt, Rainer A1 - Kohl, Anka T1 - Investigations on the degree of damage of polyethylene grades as materials of heating oil storage tanks after a service life of more than 30 years N2 - Tanks for heating oil made of polyethylene grades have been on the market since the early 1970s in Germany. Tank manufacturers recommend the replacement of the tanks after a period of 30 years due to guarantee safety. Polyethylene grades are subject to ageing by alteration of the properties during their life cycle. The degree of ageing and the nature of the degradation process mainly depend on the chemical degradation of the polyethylene, the wall thickness of the tank and the environmental conditions. There are no results available on the long-term behavior of the polyethylene grades, especially after a service life of more than 30 years. The aim of this investigation was the determination of the factual degree of damage in comparison to the uncontaminated polyethylene grades. Material data of the used polyethylene grades are available because the BAM was the competent authority for the tests and expert reports for the approval of these tanks until the middle of the 1990s. The determination of the Melt Flow Rate (MFR) and the Fourier Transmission IR Spectroscopy (FTIR) of tank sections from the bottom, the shell and the roof of 10 segregated heating oil storage tanks produced of polyethylene grades A and B were used as tests methods. The MFR measurements of the tank sections showed differences in the values depending on the weight which was used (5 kg or 21.6 kg). A reduction of the MFR values was measured for most of the sections of tanks made of polyethylene grade B after a service life of the tanks of more than 30 years. This grade is mainly subject to the internal ageing by cross-linkages, increased degree of branched molecules and loss of the plasticizer, and to a lesser extent by oxidative degradation. The FTIR analysis, especially of tank sections of the bottom and the shell showed that the intensity of the CH2 asymmetric and symmetric stretching vibrations in the range: 2800 - 2900 cm-1 and the CH2 bending deformation vibration at 1400 cm-1 increased due chain scissions. The intensity of the carbonyl stretching vibration C=O at 1740 cm-1 is low. The carbonyl index characterizes the degree of oxidation. T2 - EUROCORR 2018 CY - Krakow, Poland DA - 09.09.2018 KW - Heating oil storage tanks KW - Polyethylene KW - Degree of damage KW - Melt Flow Rate (MFR) KW - FTIR PY - 2018 AN - OPUS4-45939 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baensch, Franziska A1 - Baer, Wolfram A1 - Chruscicki, Sebastian A1 - Habib, Abdel Karim A1 - Homann, Tobias A1 - Hussels, Maria-Teresa A1 - Prager, Jens A1 - Schmidt, Dirk A1 - Stajanca, Pavol A1 - Weltschev, Margit A1 - Wossidlo, Peter T1 - Feasibility study - Continuous monitoring of pipes using distributed acoustic and fibre optic sensors N2 - The feasibility study „AGIFAMOR. Ageing infrastructures – distributed acoustic monitoring of pipes” is an interdisciplinary research project at BAM internally financed from 2015 to 2018. Therefore, the quite young fibre optic sensing technology of distributed acoustic sensing (DAS) was investigated to possibly be extended towards a global condition monitoring system for pipelines operating in real time. DAS is a highly dynamic fibre optic sensing technology based on the method of coherent optical time domain reflectometry (C-OTDR). DAS allows capturing strain changes in the range of kHz. For the experimental work, the most suitable application yielding an optimum sensitivity was proven by wrapping a standard single-mode silica fibre around the pipe. The DAS sensitivity was investigated regarding the detection of 1) incidents that initiate propagation of acoustic waves in the pipe wall, 2) changes inside the pipeline causing altered flow and 3) damage development in the pipe wall. Therefore, several testing setups in laboratory as well as in real scale were realized. For comparison purposes, experiments were accompanied by acoustic emission analyses and by measurements with accelerometers. DAS was found to be very sensitive to gas ignition and its propagation across the pipe. Furthermore, the ability of DAS to detect and localize acoustic signals associated with pipeline leakage was demonstrated. The detection of crack formation and propagation within the pipe wall by means of DAS was studied during bending tests on several pipe segments, but was not proven so far with certainty. As expected, these studies turned out as the most difficult challenge due to the random occurrence and transient nature of microscopic damage phenomena. T2 - Proceedings of the International Symposium on Structural Health Monitoring and Nondestructive Testing CY - Saarbrücken, Germany DA - 04.10.2018 KW - Accelerometers KW - Acoustic emission KW - Fibre optic acoustic sensing KW - Continous monitoring KW - Bending tests on pipe segments KW - Leak detection PY - 2018 SP - Paper 21 AN - OPUS4-46375 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Compatibility of sealing materials with biofuels and biodiesel heating oil blends at different temperatures N2 - The objective of this research was to determine the resistance of frequently used sealing materials such as FKM (fluorocarbon rubber), FVMQ (methyl-fluoro-silicone rubber), VMQ (methyl-vinyl-silicone rubber), EPDM (ethylene-propylene-diene rubber), CR (chloroprene rubber), CSM (chlorosulfonated polyethylene), IIR (butyl rubber), PA (polyamides), NBR (acrylonitrile-butadiene rubber) and PUR (polyester urethane rubber) in fuels and heating oil with admixtures of biogenic sources such as E10 (fuel with 10 % ethanol), E85 (fuel with 85 % ethanol), non-aged and aged biodiesel, diesel fuel with 5 % biodiesel, non-aged and aged B10 (heating oil with 10 % biodiesel) at 20 °C, 40 °C and 70 °C. Mass, tensile strength and breaking elongation of the test specimens were determined before and after the exposure for 84 days in the fuels. The visual examination of some elastomer test specimens clearly showed the great volume increase until break or partial dissolution. Shore hardness A and D (for PA) were determined before and after exposure of the test specimens in the biofuels for 42 days. There is not determined a threshold for the reduction in tensile properties and Shore hardness in the international standards. Therefore a threshold of 15 % was determined for the evaluation of the compatibility. In summary, it can be therefore stated that the chemical resistance of the fluoropolymers FKM and FVMQ in fuels and biofuels is the best one. T2 - 13th International Congress on Biofuels & Bioenergy CY - Ottawa, Canada DA - 18.10.2018 KW - Sealing materials KW - Biodiesel KW - Diesel fuel KW - Heating oil with 10 % biodiesel KW - Tensile properties KW - Shore hardness KW - Fuel with 10 % ethanol PY - 2018 AN - OPUS4-46358 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Langzeitschäden an Heizöllagerbehältern N2 - Heizöllagerbehälter aus Polyethylenformstoffen werden seit Beginn der 70-iger Jahre in Deutschland hergestellt. Die Hersteller empfehlen zur Gewährleistung der Sicherheit nach Ablauf von 30 Jahren den Ersatz dieser Behälter. Polyethylenformstoffe unterliegen im Laufe ihrer Nutzungsdauer der Alterung durch die Veränderung ihrer Eigenschaften. Das Ausmaß der Alterung und die Art des Abbauvorganges hängen im Wesentlichen vom chemischen Abbau des Polyethylens, der Wanddicke des Behälters und den Umgebungsbedingungen ab. Bisher lagen keine Untersuchungen zum Langzeitverhalten der Polyethylenformstoffe vor, insbesondere nach einer Nutzungsdauer der Tanks über 30 Jahre. Ziel der Untersu-chungen war, den tatsächlichen Schädigungsgrad der Polyethylenformstoffe im Vergleich zu den unbelasteten Formstoffen zu ermitteln. Da die BAM bis Mitte der 90-iger Jahre für die Prüfungen und Gutachten zur Zulassung dieser Behälter zuständig war, sind die Werkstoffdaten noch vorhanden. Als Untersuchungsmethoden wurden die Bestimmung der Schmelze-Masse-Fließrate (MFR) und die Fourier-Transformation-IR-Spektroskopie (FTIR) von Tankausschnitten aus dem Bereich des Bodens, des Mantels und des Daches von 10 ausgesonderten Behältern aus den Polyethylenformstoffen A und B herangezogen. Die Messungen der MFR der Tankaus-schnitte aus diesen Bereichen zeigten Unterschiede in den Werten in Abhängigkeit vom Ge-wicht (5 kg oder 21,6 kg), welches eingesetzt wurde. Eine Abnahme der MFR-Werte wurde für die größere Anzahl der Tankwandungsausschnitte aus dem Formstoff B nach einer Lebensdauer der Tanks > 30 Jahre gemessen. Dieser Formstoff wurde hauptsächlich durch innere Alterung infolge Vernetzungen, Verzweigungen und Weichmacherverlust und weniger durch oxidativen Abbau geschädigt. Die FTIR-Messungen der Proben aus dem Bereich des Bodens und des Mantels der Tanks zeigten, dass die Intensität der asymmetrischen/symmetrischen CH2 -Streckschwingungen im Bereich: 2800 - 2900 cm-1 und der CH2 -Biegeverformungsschwingung bei 1400 cm-1 aufgrund von Kettenspaltungen zugenommen haben. Die Intensität der Carbonylstreckschwingung C=O bei 1740 cm-1 ist niedrig. Sie ist ein Maß für die Oxidation des Polymerwerkstoffes. T2 - 14. Hildesheimer Forum zum anlagenbezogenen Gewässerschutz CY - Hildesheim, Germany DA - 04.12.2018 KW - Polyethylenformstoffe KW - Heizöllagerbehälter KW - Schädigungsgrad PY - 2018 AN - OPUS4-46886 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Einfluss von Biokomponenten in Kraftstoffen und Heizöl auf die Beständigkeit von Fluorkautschuk unter Praxisbedingungen N2 - Die Bewertung der Werkstoffbeständigkeit ist von großer Bedeutung bei Änderung der Zusammensetzung der Kraftstoffe und des Heizöls, insbesondere die Frage nach der Beständigkeit der Dichtungswerkstoffe bei Zusätzen von Bioethanol und Biodiesel (Rapsölfettsäuremethylester). Vorhergehende Untersuchungen (Messungen der Veränderungen der Masse, der Zugeigenschaften und der Härte) bezogen sich auf die Bewertung der Beständigkeit häufig verwendeter Dichtungswerkstoffe wie FKM, FVMQ, VMQ, EPDM, CR, CSM, IIR, PA, NBR und PUR in Kraftstoffen und Heizöl mit 10 % Biodiesel (nicht gealtert und bis zu 5 Jahre gealtert) unter statischen Bedingungen. Ziel der Untersuchungen war die Bewertung der Beständigkeit von Fluorkautschuk unter verpressten Bedingungen in Analogie zu den Einsatzbedingungen in der Praxis. Die Masse und der Druckverformungsrest von Prüfkörpern aus FKM wurden vor und nach der Auslagerung über einen Zeitraum von 3, 7, 14, 28, 56 und 90 Tagen in E10 (Kraftstoff mit max. 10 % Ethanol), E85 (Kraftstoff mit 85 % Ethanol), Biodiesel (Rapsölfettsäuremethylester), Super (Kraftstoff mit max. 5 % Ethanol), Dieselkraftstoff mit max. 5 % Biodiesel, Super Plus (Kraftstoff ohne Ethanolzusatz) und Heizöl mit 10 % Biodiesel (B10) bei 40 °C gemäß ISO 815-1 bestimmt. Die Druckverformungsrestprüfung zählt neben der Messung der Härte, der Dichte und der Zugeigenschaften zu den wichtigsten Grundprüfverfahren der Elastomerindustrie. Nach Ende der Auslagerung in den Kraftstoffen und der Aufhebung der Verpressung wurde der Druckverformungsrest der Prüfkörper in regelmäßigen Zeitabständen bis zu einer Rücktrocknung > 90 Tage bestimmt. Zum Vergleich wurden Prüfkörper aus FKM ohne Kraftstoff oder Heizöl unter Verpressung bei 40 °C ausgelagert. Die Masseänderung der Prüfkörper aus FKM betrug nach 90 Tagen Auslagerung in E10 9 %, in Super 8 %, in E85 4% und 0,6 % in Biodiesel. Die Erhöhung der Masse und die damit verbundene Quellung der Prüfkörper in E10 und Super mit 5 – 10% Ethanolzusatz hatte einen Einfluss auf den Druckverformungsrest, der sprunghaften Veränderungen unterlag im Vergleich zu den Werten nach Auslagerung in Biodiesel, Dieselkraftstoff und Heizöl B10 bei 40 °C. Zum Vergleich, unter statischen Bedingungen verringerte sich die Zugfestigkeit der Prüfkörper aus FKM nach Auslagerung in E10 bei 40 °C um 31 % und die Reißdehnung um 18 %. T2 - BAM-Abteilungskolloquium CY - Berlin, Germany DA - 22.11.2018 KW - Fluorkautschuk (FKM) KW - Kraftstoffe mit biogenen Anteilen KW - Druckverformungsrestprüfung PY - 2018 AN - OPUS4-46887 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weltschev, Margit A1 - Hoffmann, Gabi T1 - Untersuchungen des Schädigungsgrades von Polyethylenformstoffen als Werkstoffe von Heizöllagerbehältern nach einer Nutzungsdauer > 30 Jahre T1 - Investigations on the degree of damage of polyethylene grades of heating oil storage tanks after a service life in excess of 30 years N2 - Heizöllagerbehälter aus Polyethylenformstoffen werden seit Beginn der 70-iger Jahre in Deutschland hergestellt. Die Hersteller empfehlen zur Gewährleistung der Sicherheit nach Ablauf von 30 Jahren den Ersatz dieser Behälter. Polyethylenformstoffe unterliegen im Laufe ihrer Nutzungsdauer der Alterung durch die Veränderung ihrer Eigenschaften. Das Ausmaß der Alterung und die Art des Abbauvorganges hängen im Wesentlichen vom chemischen Abbau des Polyethylens, der Wanddicke des Behälters und den Umgebungsbedingungen ab. Bisher lagen keine Untersuchungen zum Langzeitverhalten der Polyethylenformstoffe vor, insbesondere nach einer Nutzungsdauer der Tanks über 30 Jahre. Ziel der Untersu-chungen war, den tatsächlichen Schädigungsgrad der Polyethylenformstoffe im Vergleich zu den unbelasteten Formstoffen zu ermitteln. Da die BAM bis Mitte der 90-iger Jahre für die Prüfungen und Gutachten zur Zulassung dieser Behälter zuständig war, sind die Werkstoffdaten noch vorhanden. Als Untersuchungsmethoden wurden die Bestimmung der Schmelze-Masse-Fließrate (MFR) und die Fourier-Transformation-IR-Spektroskopie (FTIR) von Tankausschnitten aus dem Bereich des Bodens, des Mantels und des Daches von 10 ausgesonderten Behältern aus den Polyethylenformstoffen A und B herangezogen. Die Messungen der MFR der Tankaus-schnitte aus diesen Bereichen zeigten Unterschiede in den Werten in Abhängigkeit vom Ge-wicht (5 kg oder 21,6 kg), welches eingesetzt wurde. Eine Abnahme der MFR-Werte wurde für die größere Anzahl der Tankwandungsausschnitte aus dem Formstoff B nach einer Lebensdauer der Tanks > 30 Jahre gemessen. Dieser Formstoff wurde hauptsächlich durch innere Alterung infolge Vernetzungen, Verzweigungen und Weichmacherverlust und weniger durch oxidativen Abbau geschädigt. Die FTIR-Messungen der Proben aus dem Bereich des Bodens und des Mantels der Tanks zeigten, dass die Intensität der asymmetrischen/symmetrischen CH2 -Streckschwingungen im Bereich: 2800 - 2900 cm-1 und der CH2 -Biegeverformungsschwingung bei 1400 cm-1 aufgrund von Kettenspaltungen zugenommen haben. Die Intensität der Carbonylstreckschwingung C=O bei 1740 cm-1 ist niedrig. Sie ist ein Maß für die Oxidation des Polymerwerkstoffes. KW - Heizöllagerbehälter KW - Polyethylen KW - Schädigungsgrad KW - Schmelze-Masse-Fließrate KW - FTIR PY - 2018 DO - https://doi.org/10.3139/120.111231 SN - 0025-5300 VL - 60 IS - 10 SP - 1013 EP - 1020 PB - Carl Hanser Verlag GmbH & Co. KG CY - München AN - OPUS4-46167 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Weltschev, Margit T1 - Physical test methods for elastomers (Book review) N2 - The book is primarely intended as a reference for those directly concerned with testing elastomers or for those indirectly involved in testing such as design engineers. KW - Elastomer PY - 2018 UR - https://doi.org/10.1002/maco.201870074 DO - https://doi.org/10.1002/maco.201870074 SN - 0947-5117 VL - 69 IS - 7 SP - 953 EP - 953 PB - WILEY-VCH Verlag GmbH & Co. KGaA CY - Weinheim AN - OPUS4-46746 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Pötzsch, Sina A1 - Rehfeldt, Rainer T1 - Compatibility of polymeric materials with heating oil/biodiesel blends at different temperatures N2 - Materials compatibility is a major concern whenever the fuel composition is changed. The question arises of whether polymeric materials are resistant to heating oil with admixtures of 10 % biodiesel (B10) and 20 % biodiesel (B20). The polarity of biodiesel increases its solvency and facilitates permeation and extrac-tion. Solvation, swelling and/or extraction lead to changes in the physical properties and chemical changes of polymeric materials. The objective of this research was to determine the resistance of frequently used sealing materials such as FKM, EPDM, CR, CSM, NBR, IIR, VMQ, FVMQ, PA and PUR in up to four-year aged B10 for 84 days at 20 °C, 40 °C and 70 °C. The polymeric materials: ACM, FKM, HNBR, PA, PE; POM, PUR and PVC were ex-posed to B20 for 84 days at 40°C and 70°C in another research project. Mass, tensile strength, breaking elongation and Shore hardness A (D) of the test specimens were determined before and after the exposure for 84 (42) days in the heating oil blends B10 and B20. There is not determined a threshold for the reduction in tensile properties and Shore hardness in the international standards. Therefore, a threshold of 15 % was deter-mined for the evaluation of the compatibility. Measurements of the variations in mass, tensile properties and Shore hardness after exposure of the polymers in non-aged and aged heating oil B10 showed clearly that FKM, FVMQ and PA were the most resistant materials in B10. The elastomers CR, CSM, EPDM, IIR, NBR and VMQ were generally not resistant to B10. Damage to the materials increased with higher test temperatures and the age of B10. FKM, POM and PVC showed high compatibility in B20 at 40°C and 70 °C. ACM, HNBR and PA were evaluated as resistant in B20 at 40 °C but not at 70°C. T2 - Corrosion 2019 CY - Warsaw, Poland DA - 27.09.2019 KW - Polymers KW - Compatibility evaluations KW - Heating oil with 10% biodiesel KW - Heating oil with 20% biodiesel KW - Tensile properties KW - Shore hardness PY - 2019 AN - OPUS4-48146 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weltschev, Margit T1 - Compatibility of sealing materials with biofuels and biodiesel heating oil blends at different temperatures N2 - Biofuels including ethanol and biodiesel (fatty acid methyl ester, FAME) represent an important renewable fuel alternative to petroleum-derived transport fuels. Increasing biofuels use would bring some benefits, such as a reduction in oil demands and greenhouse gas emissions, and an improvement in air quality. Materials compatibility is a major concern whenever the fuel composition is changed in a fuel system. The objective of this research was to determine the resistance of frequently used sealing materials such as CR (chloroprene rubber), CSM (chlorosulfonated polyethylene), EPDM (ethylene-propylene-diene rubber), FKM (fluorocarbon rubber), FVMQ (methyl-fluorosilicone rubber), IIR (butyl rubber), NBR (acrylonitrile-butadiene rubber), PA (polyamides), PUR (polyester urethane rubber) and VMQ (methyl-vinyl-silicone rubber), in heating oil with admixtures of biogenic sources such as E10 (fuel with max. 10 % ethanol), E85 (fuel with 85 % ethanol), non-aged and aged biodiesel, diesel fuel with 5 % biodiesel, non-aged and aged B10 (heating oil with 10 % biodiesel) at 20 °C, 40 °C and 70 °C. Mass, tensile strength and breaking elongation of the test specimens were determined before and after the exposure for 84 days in the fuels. The visual examination of some elastomer test specimens clearly showed the great volume increase until break or partial dissolution. Shore hardness A and D (for PA) were determined before and after exposure of the test specimens in the biofuels for 42 days. There is not determined a threshold for the reduction in tensile properties and Shore hardness in the international standards. Therefore, a threshold of 15 % was set for the evaluation of the compatibility. The sealing materials CR, CSM, EPDM, IIR and NBR were generally not resistant to biodiesel and B10. In summary, it can be therefore stated that the chemical resistance of the fluoropolymers FKM and FVMQ in fuels and biofuels is the best one. KW - Compatibility evaluation KW - Polymers KW - FAME KW - Heating oil with 10 % FAME PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-479722 DO - https://doi.org/10.15344/2456-351X/2019/165 SN - 2456-351X VL - 4 IS - 165 SP - 4 EP - 9 PB - Graphyonline Publications Pvt. Ltd. CY - Bangalore, Karnataka, Indien AN - OPUS4-47972 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Bewertung der Beständigkeit von metallischen und polymeren Werkstoffen für Behälter zur Lagerung und Beförderung von Chemikalien N2 - In der Bundesrepublik Deutschland werden über 400 Mio.t Gefahrgüter jährlich in Tankfahrzeugen, Aufsetztanks, Batteriefahrzeugen, Eisenbahnkesselwagen und Tankcontainern befördert, davon etwa 150 Millionen Tonnen im Straßengüterverkehr. Zu den Hauptschadensursachen zählt die Korrosion, wobei die gleichmäßige und ungleichmäßige Flächenkorrosion die Korrosionsart ist, die beim Chemikalientransport in Tanks am häufigsten auftritt. Viele Schäden durch Lochkorrosion entstehen beim Transport von chloridhaltigen Medien bei Anwesenheit von Feuchtigkeit. Die BAM-Liste - Anforderungen an Tanks für die Beförderung gefährlicher Güter - ist Grundlage für die stoffbezogenen Baumusterzulassungen für Tankcontainer und ortsbewegliche Tanks zur Beförderung gefährlicher Güter durch die BAM seit der Herausgabe der 1. Auflage 1989. In die BAM-Liste wurden vorrangig solche gefährlichen Güter aufgenommen, die potenziell in Tanks befördert werden können. Die Beständigkeitsbewertungen gebräuchlicher metallischer Tankwerkstoffe und polymerer Dichtungs-, Beschichtungs- und Auskleidungswerkstoffe werden auch bei der Zulassung von Kesselwagen und Tankfahrzeugen als Erkenntnisquelle verwendet. Diese Daten sind aber unter sorgfältiger Überprüfung der Übertragbarkeit auch für andere praktische Anwendungen und unter Berücksichtigung der jeweiligen Praxisbedingungen auch als Ratgeber für Verpackungen, IBC, Lagerbehälter, Rohrleitungen usw. aus metallischen Werkstoffen anwendbar. In den internationalen Gefahrgutverordnungen ADR, RID und IMDG-Code wird nach einer vorgegebenen Prüffrist eine innere Besichtigung der Tanks gefordert. Bei Tankcontainern beträgt diese Prüffrist im ADR/RID, Kap. 6.8 , fünf Jahre (bei der Beförderung von ortsbeweglichen Tanks nach ADR/RID, Kap. 6.7, und nach dem IMDG-Code 2½ Jahre) und bei Tankfahrzeugen sechs Jahre. Im RID wird für Eisenbahnkesselwagen eine Prüffrist von acht Jahren für die Innenbesichtigung vorgeschrieben. Für die Dauer der Prüfintervalle muss die Werkstoffbeständigkeit der Tankwerkstoffe gewährleistet sein. T2 - 28. Fachtagung BUKO, Workshop: DD/Ex/AwSV CY - Berlin, Kiwa GmbH, Germany DA - 04.10.2019 KW - Korrosionsschäden KW - Beständigkeitsbewertungen KW - BAM-Liste KW - Transport und Lagerung von Chemikalien PY - 2019 AN - OPUS4-49206 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -