TY - CONF A1 - Weltschev, Margit T1 - Compatibility of sealing materials with biofuels and biodiesel-heating oil blends T2 - CORROSION 2015 CY - Dallas, USA DA - 2015-03-15 PY - 2015 AN - OPUS4-32909 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Beständigkeit von metallischen Werkstoffen und polymeren Dichtungswerkstoffen unter dem Einfluss von Biokraftstoffen T2 - 14. netinforum Gewässer- und Explosionsschutz CY - Ludwigsburg, Germnany DA - 2014-07-01 PY - 2014 AN - OPUS4-30947 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Compatibility of sealing materials with biofuels, biodiesel-heating oil blends and premium grade fuel at different temperatures T2 - EUROCORR 2014 CY - Pisa, Italy DA - 2014-09-08 PY - 2014 AN - OPUS4-31418 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Bewertung der Beständigkeit von metallischen Behälterwerkstoffen und polymeren Dichtungswerkstoffen unter dem Einfluss von Biokraftstoffen und Bioheizöl T2 - Seminarvorträge zu ausgewählten Kapiteln der Werkstofftechnik CY - Wuppertal, Germany DA - 2014-01-17 PY - 2014 AN - OPUS4-30024 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Werkstoffverträglichkeit von Behältern für die Beförderung gefährlicher Güter N2 - Die BAM-Liste - Anforderungen an Tanks für die Beförderung gefährlicher Güter – mit den Beständigkeitsbewertungen metallischer und polymerer Werkstoffe ist Grundlage für die stoffbezogenen Baumusterzulassungen für Tankcontainer und ortsbewegliche Tanks zur Beförderung gefährlicher Güter durch die BAM seit der Herausgabe der 1. Auflage 1989. Diese Beständigkeitsbewertungen werden nicht nur bundesweit, sondern weltweit als Erkenntnisquelle genutzt. Für die Zulassung von Kesselwagen und Tankfahrzeugen werden diese Daten auch herangezogen. Die Werkstoffbeständigkeitsdaten und der damit verbundene Informationsservice der BAM haben mit Sicherheit dazu beigetragen, Leckagen von Tanks aufgrund des Einsatzes von Tanks/Kesselwagen aus einem gegenüber dem Füllgut unbeständigem Tankwerkstoff oder Dichtungswerkstoff zu vermeiden. T2 - Ausgewählte Kapitel der Werkstofftechnik - Werkstoffe und Fertigungstechnik CY - Wuppertal, Germany DA - 13.01.2017 KW - Werkstoffbeständigkeit KW - Tankwerkstoffe KW - Dichtungswerkstoffe KW - BAM-Liste KW - Datenbank Gefahrgut PY - 2017 AN - OPUS4-38974 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Compatibility Evaluations of Sealing Materials with Aged Biofuels N2 - The objective of this research was to determine the resistance of frequently used sealing materials such as EPDM, FKM, FVMQ, CR, CSM, IIR, NBR, PA, PUR and VMQ in aged biodiesel and heating oil B10 with 10 % biodiesel. The mass, tensile strength, breaking elongation and Shore hardnesses of the test specimens were determined before and after exposure in non-aged, one-year, two-year, three-year and four-year aged biodiesel and B10 at 20 °C, 40 °C and 70 °C. A threshold for the reduction in tensile properties and Shore hardness is not set in the international standards. Therefore, a threshold of 15 % was set for the evaluation of the compatibility. The decrease in tensile properties and Shore hardness increased with the age and the temperature of the biodiesel and the heating oil. The age of the biodiesel was not relevant for the sealing materials CR, CSM, EPDM, IIR and NBR, which were generally not resistant to biodiesel and B10. FKM and PA showed high compatibility in non-aged and aged biodiesel. FVMQ and PA could be evaluated as resistant in non-aged and aged B10 at 20°C and 40°C, whereas FKM was resistant up to 70°C despite of the age of B10. T2 - CORROSION 2017 CY - New Orleans, LA, USA DA - 26.03.2017 KW - Sealing materials KW - Compatibility KW - Aged biodiesel KW - Aged heating oil with 10% biodiesel (B10) KW - Tensile properties KW - Shore hardness PY - 2017 AN - OPUS4-39640 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Change in properties of sealing materials in biofuels, biodiesel-heating oil blends, diesel and premium grade fuel at different temperatures T2 - EUROCORR 2015 CY - Graz, Österreich DA - 2015-09-06 PY - 2015 AN - OPUS4-34547 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Compability of polyethylene grades with biofuels and biodiesel-heating oil blends T2 - EUROCORR 2015 CY - Graz, Östereich DA - 2015-09-06 PY - 2015 AN - OPUS4-34551 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Investigations on the degree of damage of polyethylene grades of heating oil storage tanks after a service life in excess of 25 years N2 - Plastic storage tanks for heating oil have been on the market since the early 1970s in Germany, mainly made from polyethylene grades. Tank manufacturers and experts examining the tanks recommend the replacement of the tanks to ensure the safety after a period of 30 years. The tank manufacturer is legally obliged to specify the service life of the tanks. Polyethylene is subject to ageing by alteration of the properties during its life cycle. A distinction is made between internal and external ageing processes. The internal ageing, such as the breakdown of internal stresses, post-crystallization, phase sepa-ration of multicomponent systems and plasticizer migration is attributed to thermodynamically instable conditions of the plastic material. The external ageing in form of stress cracking, fatigue cracking, thermooxidative degradation or swelling is based on physical or chemical effects of the environment of the polyethylene grade. The degree of ageing and the nature of the degradation process mainly depend on the chemical degradation of the polyethylene, the wall thickness of the tank and the environmental conditions. There are no results available on the long-term behaviour of the polyethylene grades used as materials for heating oil storage tanks, especially after a service life of more than 25 years. The aim of this investigation was the determination of the factual degree of damage in comparison to the uncontaminated polyethylene grades. Data on the melt flow rate (MFR) and density of the used polyethylene grades are available because the BAM was the competent authority for the approval of the plastic heating oil storage tanks until the end of the 1980s. The technical service of specialist companies for fuel tank disposal supplied tank sections from the bottom, the shell and the roof of 8 segregated heating oil storage tanks. Some of the tanks had been in service for more than 30 years. Two polyethylene grades mainly were used as materials for these tanks over this time. The determination of the MFR according to EN ISO 1133 and the FTIR spectroscopy followed standard test methods. The highest average percentage increase in the MFR was determined as 31- 43 % for the bottom section of the tanks, for both the inner shell and the outer shell. The lowest increase in MFR was measured for the top of the tank, with 6 - 12 % for the inner shell and 0 - 8 % for the outer shell. The tank shell sections had an average percentage increase in MFR of 10 - 33 % for the inner shell and of 14 - 40 % for the outer shell. The oxidative damage of the polyethylene grades was highest in the bottom area due to the permanent contact with the heating oil and degradation products. The microtome cuttings were analyzed with image-guided infrared microscopy in the transmission mode and confirmed the results obtained with the MFR measurements. In summary it can be concluded that the oxidative damage of the polyethylene grades after long-term contact with heating oil is relative low. T2 - EUROCORR 2017 CY - Prag, Czech Republic DA - 03.09.2017 KW - Polyethylene KW - Heating oil tanks KW - Service life KW - Degree of degradation PY - 2017 AN - OPUS4-41907 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Beständigkeitsbewertungen von Tank- und Behälterwerkstoffen in der Datenbank Gefahrgut und in der BAM-Liste T2 - Vortrag an der Bergischen Universität Wuppertal im FB Sicherheitstechnik im Seminar, ausgewählte Kapitel der Sicherheitstechnik/Materialkunde: Werkstoffe und Fertigungstechnik CY - Wuppertal, Germany DA - 2008-07-17 PY - 2008 AN - OPUS4-17739 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -