TY - CONF A1 - Weltschev, Margit A1 - Pötzsch, Sina T1 - Compatibility of polymeric sealing materials with biodiesel heating oil blends at different temperatures N2 - Biodiesel is subject to degradation processes like oil and grease. The oxidative degradation products of vegetable oil esters in biodiesel particularly lead to enhanced sedimentation in blended fuels. The polarity of biodiesel increases its solvency and facilitates permeation and extraction. Solvation, swelling and/or extraction lead to changes in the physical properties and chemical changes of polymeric materials. It also accelerates the degradation (hydrolysis and oxidation) of these materials with the loss of additives and stabilizers. The objective of this research was to determine the resistance of frequently used polymeric materials such as ACM, EPDM, FKM, FVMQ, CR, CSM, IIR, HNBR, NBR, PA, PE; POM, PUR, PVC and VMQ in biodiesel and heating oil with 10 %/20 % biodiesel (B10/B20) at 40°C and 70°C. Mass, tensile strength and breaking elongation of the test specimens were determined before and after the exposure for 84 days in the biodiesel heating oil blends. The visual examination of some elastomer test specimens clearly showed the great volume increase until break or partial dissolution. Shore hardness A and D were determined before and after exposure of the test specimens in the biofuels for 42 days. The elastomers CR, CSM, EPDM, IIR, NBR and VMQ were generally not resistant to biodiesel and B10 at 40°C and 70°C. FKM, ACM, HNBR, PA, PE, POM, and PVC showed high compatibility in B10/B20 at 40°C. A lower compatibility was determined for ACM in biodiesel. ACM and HNBR were not resistant in B20 at 70°C. T2 - Biofuels & Bioenergy CY - Rome, Italy DA - 14.10.2019 KW - Heating oil-Biodiesel-Blend KW - Compatibility evaluations KW - Tensile properties KW - Shore hardness PY - 2019 AN - OPUS4-49306 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Pötzsch, Sina A1 - Bäßler, Ralph T1 - Compatibility of polymers with heating oil with 20 % biodiesel at different temperatures under static and compressed conditions N2 - Biodiesel is viewed as a major source of energy. In areas such as the European Union, where 80 % of the oil-based fuel is imported, there is also the desire to reduce dependence on external oil supplies. Materials compatibility is a major concern whenever the fuel composition is changed. The question arises of whether polymeric materials are resistant to heating oil with 20 % biodiesel (B20) in comparison to pure heating oil. The polarity of biodiesel increases its solvency and facilitates permeation and extraction. Solvation, swelling and/or extraction lead to changes in the physical properties. Extraction alters the fuel chemistry. These chemical changes could also accelerate the degradation (hydrolysis and oxidation) of the polymeric material with the loss of additives and stabilizers. The objective of this research was to determine the resistance of frequently used materials for components in middle distillate facilities such as ACM, FKM, HNBR, PA, PE, POM, PUR and PVC in heating oil and heating oil blend B20 for 84 days at 40 °C, and FKM, HNBR, PA, POM, PUR and PVC at 70 °C. Mass, tensile strength, breaking elongation and Shore hardness A (D) of the test specimens were determined before and after exposure for 84 (42) days in the test fuels under static conditions. For the investigations under compressed conditions, the mass and the compression set of FKM test specimens were determined before and after exposure for 3, 7, 14, 28, 56 and 90 days in B20 at 40 °C and 70 °C according to ISO 815-1 “Rubber, vul-canized or thermoplastic - determination of compression set – Part 1: At ambient or elevated temperatures”. There is not determined a threshold for the reduction in tensile properties and Shore hardness in the international standards. Therefore, a threshold of 15 % was determined for the evaluation of the compatibility. The change of tensile strength and breaking elongation of test specimens made of ACM, FKM, HNBR, PA, PE, POM, PUR and PVC exposed to heating oil and the blend B20 was less than 15 % at 40 °C. A maximum reduction in Shore hardness A of 14 % was determined for ACM at 40 °C and for HNBR of 15 % at 70 °C. It can be concluded that ACM, FKM, HNBR, PA, PE, POM, PVC and PUR were resistant in B20 at 40°C. FKM, PA, POM and PVC were evaluated as resistant in heat-ing oil and B20 at 70 °C, HNBR and PUR were not resistant in these fuels at 70°C. Based on the mass increase and compression set values of FKM test specimens it can be stated that FKM is resistant in B20 under compressed conditions at 40 °C and 70 °C. T2 - EUROCORR 2019 CY - Sevilla, Spain DA - 09.09.2019 KW - Heating oil - biodiesel - blend KW - Polymeric materials KW - Compatibility KW - Tensile properties KW - Shore Hardness PY - 2019 AN - OPUS4-49002 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Beständigkeit von Fluorkautschuk in Kraftstoffen und Heizöl mit biogenen Anteilen unter Druckbeanspruchung N2 - Die Bewertung der Werkstoffbeständigkeit ist von großer Bedeutung bei Änderung der Zusammensetzung der Kraftstoffe und des Heizöls, insbesondere die Frage nach der Beständigkeit der Dichtungswerkstoffe bei Zusätzen von Bioethanol und Biodiesel (Rapsölfettsäuremethylester). Vorhergehende Untersuchungen (Messungen der Veränderungen der Masse, der Zugeigenschaften und der Härte) bezogen sich auf die Bewertung der Beständigkeit häufig verwendeter Dichtungswerkstoffe wie FKM, FVMQ, VMQ, EPDM, CR, CSM, IIR, PA, NBR und PUR in Kraftstoffen und Heizöl mit 10 % Biodiesel (nicht gealtert und bis zu 5 Jahre gealtert) unter statischen Bedingungen. Ziel der Untersuchungen war die Bewertung der Beständigkeit von Fluorkautschuk unter verpressten Bedingungen in Analogie zu den Einsatzbedingungen in der Praxis. Die Masse und der Druckverformungsrest von Prüfkörpern aus FKM wurden vor und nach der Auslagerung über einen Zeitraum von 3, 7, 14, 28, 56 und 90 Tagen in E10 (Kraftstoff mit max. 10 % Ethanol), E85 (Kraftstoff mit 85 % Ethanol), Biodiesel (Rapsölfettsäuremethylester), Super (Kraftstoff mit max. 5 % Ethanol), Dieselkraftstoff mit max. 5 % Biodiesel, Super Plus (Kraftstoff ohne Ethanolzusatz) und Heizöl mit 10 % Biodiesel (B10) bei 40 °C gemäß ISO 815-1 bestimmt. Die Druckverformungsrestprüfung zählt neben der Messung der Härte, der Dichte und der Zugeigenschaften zu den wichtigsten Grundprüfverfahren der Elastomerindustrie. Nach Ende der Auslagerung in den Kraftstoffen und der Aufhebung der Verpressung wur-de der Druckverformungsrest der Prüfkörper in regelmäßigen Zeitabständen bis zu einer Rücktrocknung > 90 Tage bestimmt. Zum Vergleich wurden Prüfkörper aus FKM ohne Kraftstoff oder Heizöl unter Verpressung bei 40 °C ausgelagert. Die Masseänderung der Prüfkörper aus FKM betrug nach 90 Tagen Auslagerung in E10 9 %, in Super 8 %, in E85 4% und 0,6 % in Biodiesel. Die Erhöhung der Masse und die damit verbundene Quellung der Prüfkörper in E10 und Super mit 5 – 10% Ethanolzusatz hatte einen Einfluss auf den Druckverformungsrest, der sprunghaften Veränderungen unterlag im Vergleich zu den Werten nach Auslagerung in Biodiesel, Dieselkraftstoff und Heizöl B10 bei 40 °C. Zum Vergleich, unter statischen Bedingungen verringerte sich die Zugfestigkeit der Prüfkörper aus FKM nach Auslagerung in E10 bei 40 °C um 31 % und die Reißdehnung um 18 %. T2 - Gastvortrag im Rahmen des Seminars: Ausgewählte Kapitel der Werkstofftechnik an der Bergischen Universität Wuppertal CY - Wuppertal, Germany DA - 11.01.2019 KW - Dichtungswerkstoffe KW - Beständigkeit in Biokraftstoffen KW - Biodiesel KW - Heizöl mit 10% Biodiesel KW - E10 (Kraftstoff mit bis zu 10% Ethanol) PY - 2019 AN - OPUS4-47222 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Pötzsch, Sina A1 - Bäßler, Ralph T1 - Entwicklung einer Prüfmethode zur Bewertung der Materialbeständigkeit von Bauteilen in Mitteldestillatanwendungen N2 - Für Bauteile (Komponenten) von Versorgungsanlagen für flüssige Brenn- und Kraftstoffe muss die Beständigkeit der metallenen Werkstoffe und Polymere nachgewiesen werden. Im Anwendungsfall von Heizöl mit 20 % biogenen Anteilen in Form von Rapsölfettsäuremethylester (FAME, Biodiesel) ist es für eine konservative Beurteilung des Korrosionssystems Werkstoff/Medium/Umgebung wichtig, die Alterungs­effekte des Mediums einzubeziehen. Entwicklung eines Prüfverfahrens für die Untersuchung der Beständigkeit von metallenen Werkstoffen und Polymeren in Heizöl und Heizöl-FAME-Blends, das für eine Vorauswahl der Werkstoffe und zum Nachweis der Beständigkeit im Hinblick auf die bauaufsichtlichen Zulassungsverfahren geeignet ist. Ein Schwerpunkt wird bei den metallenen Werkstoffen auf der Erprobung von Messmethoden liegen, mit denen sich in kurzer Versuchszeit ein Korrosionsangriff detektieren lässt. Metallene Werkstoffe: Weder örtliche Korrosion noch erhöhte Flächenkorrosion (Korrosionsrate:< 0,1 m/Jahr) sind bei den bisher geprüften Werkstoffen: Aluminium, C-Stahl 1.0037, austenitischer CrNi-Stahl 1.4301, Kupfer und Messing in Heizöl und B20 (Heizöl mit 20% Biodiesel) aufgetreten. Diese Werkstoffe sind in den Prüfmedien Heizöl und B20 als beständig zu bewerten. Es wurde keine signifikante Veränderung des pH-Wertes der Prüfmedien gemessen. Polymere: Massebestimmung: Die Prüfkörper der Elastomere ACM, HNBR und PUR sowie in geringerem Maße PE neigten zur Quellung in Heizöl und B20 nach 42 d und 84 d Auslagerung; für PA 6, POM und PVC wurde keine Masseänderung gemessen. Die Masseänderung der Prüfkörper in Heizöl und B20 ist mit Ausnahme von PUR vergleichbar. Bei PE traten Verfärbungen durch die Brennstoffe auf. Zugeigenschaften: ACM, HNBR, PE und PVC sind in Heizöl und B20 beständig, da die Änderung der Zugfestigkeit und der Reißdehnung < 15 % beträgt. PA und POM sind bedingt beständig, da die Änderung der Zugfestigkeit und der Reißdehnung < 30% beträgt. T2 - DGMK-Projekttreffen CY - Rostock, Germany DA - 28.03.2019 KW - Beständigkeitsbewertung KW - Metallene Werkstoffe KW - Polymere KW - Heizöl KW - Heizöl-FAME-Blends PY - 2019 AN - OPUS4-47841 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Pötzsch, Sina A1 - Bäßler, Ralph T1 - DGMK-Projekt 780: Entwicklung einer Prüfmethode zur Bewertung der Materialbeständigkeit von Bauteilen in Mitteldestillatanwendungen N2 - Für Bauteile (Komponenten) von Versorgungsanlagen für flüssige Brenn- und Kraftstoffe muss die Beständigkeit der metallenen Werkstoffe und Polymere nachgewiesen werden. Im Anwendungsfall von Heizöl mit 20 % biogenen Anteilen in Form von Rapsölfettsäuremethylester (FAME, Biodiesel) ist es für eine konservative Beurteilung des Korrosionssystems Werkstoff/Medium/Umgebung wichtig, die Alterungseffekte des Mediums einzubeziehen. Entwicklung eines Prüfverfahrens für die Untersuchung der Beständigkeit von metallenen Werkstoffen und Polymeren in Heizöl und Heizöl-FAME-Blends, das für eine Vorauswahl der Werkstoffe und zum Nachweis der Beständigkeit im Hinblick auf die bauaufsichtlichen Zulassungsverfahren geeignet ist. Ein Schwerpunkt wird bei den metallenen Werkstoffen auf der Erprobung von Messmethoden liegen, mit denen sich in kurzer Versuchszeit ein Korrosionsangriff detektieren lässt. Die untersuchten Werkstoffe Aluminium, Stahl 1.0037, 1.4301, Kupfer, Messing (CuZn40Pb) und Zink (ZP0410) sind in B0, B20, B100 und in 6 Jahre altem B100 beständig. Auch in einem Jahr alten B20 und in einem Jahr alten B100 sind die Werkstoffe beständig. Bei Kupfer blieb die Korrosionsrate in der Flüssigphase sowohl in B20 (0 μ m/ a) als auch in B100 (4 μ m/ a) nach einem Jahr unverändert. Für das 6 Jahre alte B100 stieg die Korrosionsrate des Kupfers an (16 μ m/a). Im Gegensatz dazu sank bei Messing die Korrosionsrate in der Flüssigphase mit dem Alter des Brennstoffs, nach einem Jahr für B20 von 4 μ m/ a auf 1 μ m/a und für B100 von 36 μ m/ a auf 6 μ m/ a, im 6 Jahre alten B100 lag die Korrosionsrate des Messings bei 0 μ m/ a. In 8 Jahre altem B10 trat bei Zink in der Flüssigphase Flächenkorrosion auf, es ist in dem Medium demnach nicht beständig. Messing zeigte örtliche Korrosion in der Gasphase, es ist folglich unbeständig und für den Einsatz in stark gealterten B10 nicht geeignet. Aluminium, 1.0037, 1.4301 und Kupfer sind in dem 8 Jahre alten B10 beständig. Die Änderung der Zugfestigkeit und der Reißdehnung von ACM, HNBR und FKM in Heizöl, B20 und gealterten B10 beträgt < 15 %. Diese Werkstoffe sind in Heizöl, B20 und in gealterten B10 unter Berücksichtigung des von der BAM zur Beurteilung der Beständigkeit festgelegten Grenzwertes von 15 % bei 40 °C als beständig zu bewerten. PUR ist bei 40 °C nicht beständig in B20 und in gealtertem B10. Bei 70 °C ist HNBR nicht in B20 beständig aufgrund der Verringerung der Zugfestigkeit (40 %) und der Reißdehnung (50 %). FKM ist bei 70 °C in Heizöl und in B20 beständig. T2 - Sitzung AK Prüfstellen CY - Berlin, Germany DA - 18.09.2019 KW - Heizöl mit 20% Biodiesel (B20) KW - Beständigkeit KW - Metallene Werkstoffe KW - Polymere Werkstoffe KW - Zugeigenschaften KW - Shore-Härte PY - 2019 AN - OPUS4-50188 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hennersdorf, Felix A1 - Weltschev, Margit A1 - Hertwig, Andreas T1 - ATR Investigations into the effect of ageing on HD-PE heating oil storage tanks after a service life of more than 30 years N2 - Heating oil storage tanks made of polyethylene grades have been on the market in Germany since the early 1970s. To ensure safety, their replacement is recommended by tank manufacturers after a period of 30 years. Polyethylene is subject to ageing by alteration of the properties during its life cycle. The degree of degradation and the nature of the process mainly depend on the chemical alteration of the polyethylene, the wall thickness of the tank and the environmental conditions. There are no data available on the long-term behaviour of the polyethylene grades, especially after a service life of more than 30 years. The aim of this investigation was to find a suitable test method to determine the factual degree of damage in comparison to the uncontaminated polyethylene grades. Material data of the used polyethylene grades are available because the BAM was the competent authority for the tests and expert reports for the approval of these tanks until the middle of the 1990s. Therefore, tank sections from the bottom, the shell and the roof of 22 individual storage tanks produced of polyethylene grades A and B have been examined by Melt Flow Rate (MFR) and Attenuated Total Reflectance (ATR). Their service life was in the range between 20 and 41 years. The MFR measurements of the tank sections showed differences in the values depending on the weight which was used (5 kg or 21.6 kg). An increase of the MFR was determined for the samples of polyethylene grade A, whereas a reduction of the MFR values was measured for most samples of polyethylene grade B. This grade is mainly subject to the internal ageing by cross-linkages, increased degree of branched molecules and loss of the plasticizer. ATR analysis exhibits an absorption band at 909 cm‒1 predominantly in samples of polyethylene grade A indicating chain scission and concomitantly formed terminal vinyl groups. This absorption band can be used for the characterization of the ageing of the polyethylene grades. T2 - EUROCORR 2019 CY - Sevilla, Spain DA - 09.09.2019 KW - Heating oil tanks KW - Polyethylene KW - Ageing KW - Service life PY - 2019 AN - OPUS4-49000 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Ackermann, H. A1 - Pötzsch, Sina A1 - Weltschev, Margit A1 - Bäßler, Ralph A1 - Plum, W. T1 - Entwicklung einer Prüfmethode zur Bewertung der Materialbeständigkeit von Bauteilen in Mitteldestillatanwendungen N2 - Im Vorhaben wurde eine forcierte Prüfmethode zur Bestimmung der Beständigkeit von metallenen Werkstoffen gegenüber Brennstoffen aus Mitteldestillaten und Gemischen aus Mitteldestillat und paraffinischen Kohlenwasserstoffen, die jeweils Fettsäuremethylester (FAME) als biogene Komponente enthalten, entwickelt. Bei der Prüfmethode werden Prüfkörper des jeweiligen Werkstoffes in speziellen Prüfmedien ausgelagert. Die Zusammensetzung von zwei Prüfmedien wurde im Vorhaben erarbeitet. Diese Prüfmedien erfassen die Effekte der Alterung des FAME, die zu erwarten sind, wenn der Brennstoff länger als 2 Jahre im Feld lagert. Sie decken den Bereich bis 20 % (V/V) FAME-Anteil ab. Die Auslagerung kann bei geringem Aufwand unter Atmosphärendruck durchgeführt werden. Die Eignung einer Auswahl von metallenen Werkstoffen und Polymerwerkstoffen, die für Versorgungsanlagen für Mitteldestillat relevant sind, wurde durch Auslagerung in folgenden nicht gealterten Brennstoffen bestimmt: Heizöl EL schwefelarm (B0), Heizöl EL schwefelarm mit 20 % (V/V) FAME (B20), FAME (B100) und hydriertes Pflanzenöl (HVO). Die Werkstoffe wurden auch in einem 1 Jahr gealterten B20 und einem 8 Jahre gealtertem B10 ausgelagert. Die Temperatur bei der Auslagerung betrug 50 °C für die metallenen Werkstoffe und 40 °C und 70 °C für die Polymerwerkstoffe. Die Ergebnisse der Beständigkeitsbewertung wurden in Beständigkeitslisten zusammengefasst. Die mit B20 erhaltenen Bewertungen gelten generell für Gemische aus Heizöl EL schwefelarm und FAME mit einem FAME-Gehalt bis 20 % (V/V). Sie sind auch auf Gemische aus Dieselkraftstoff und FAME mit einem FAME-Gehalt bis 20 %(V/V) übertragbar. Die forcierte Prüfmethode kann insbesondere KMUs bei der Weiterentwicklung von bestehenden Produkten und der Entwicklung von neuen Produkten als ein kostengünstiger Schnelltest zur Überprüfung der Werkstoff- und Bauteilbeständigkeit gegenüber Mitteldestillaten mit hohem FAME-Anteil dienen. Sie kann für die Hersteller die Sicherheit erhöhen, dass Bauteile die Freigabeprüfungen der Bauaufsicht bestehen, wobei die Freigabe jedoch nur für Deutschland gültig ist. Die Erkenntnisse des Forschungsvorhabens können in eine harmonisierte Europäische Norm für alternative Brenn- und Kraftstoffe einfließen. Diese ist für die Bauteilhersteller die Voraussetzung für die Erschließung des europäischen Marktes.   N2 - Within this project, a forced test method was developed to determine the resistance of metallic materials to middle distillate fuels and mixtures of middle distillate and paraffinic hydrocarbons both with fatty acid methyl ester (FAME) as a biogenic component. In the method, specimens of the material are immersed in special test media. The compositions of two test media were developed within the project. These test media include the influence of aging of the FAME which is to be expected after a storage of the fuel exceeding 2 years in the field. They cover a range of up to 20 % (v/v) FAME content. The exposure test can be carried out at ambient pressure with little effort. Suitability of selected metallic and polymer materials relevant for middle distillate supply systems was determined by exposure to the following non-aged fuels: low-sulfur light fuel oil (B0), low-sulfur light fuel oil with 20 % (v/v) FAME (B20), FAME (B100) and hydrogenated vegetable oil (HVO). The materials were also exposed in the 1-year-aged B20 and 8-year-aged B10. Test temperature was 50 °C for metallic materials and 40 °C and 70 °C for polymers. Resulting materials resistances were summarized in resistance tables. Resistances obtained in B20 are valid for any mixture of low-sulfur light fuel oil and FAME containing up to 20 % (v/v) FAME. They are also transferable to mixtures of diesel and FAME having a FAME content of up to 20 % (v/v). This method with special test media is a cost-effective rapid test for checking resistance of materials to middle distillates having a high FAME content. It can support SMEs manufacturing components for supply systems in further development of existing and new products. It increases the manufacturers' certainty that components will pass approval tests of authorities. Results of this research project can be incorporated into a harmonized European standard for alternative fuels. This is the prerequisite for component manufacturers to access the European market. KW - Heizöl KW - FAME KW - Biobrennstoff PY - 2020 UR - https://dgmk.de/publikationen/ SN - 978-3-947716-14-2 SN - 0937-9762 SP - 1 EP - 153 PB - DGMK CY - Hamburg AN - OPUS4-51110 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Pötzsch, Sina A1 - Bäßler, Ralph T1 - Bewertung der Beständigkeit von metallenen und polymeren Werkstoffen in Mitteldestillatanwendungen mit Zusatz von Biodiesel N2 - Für Bauteile (Komponenten) von Versorgungsanlagen für flüssige Brenn- und Kraftstoffe muss die Beständigkeit der metallenen Werkstoffe und Polymere nachgewiesen werden. Im Anwendungsfall von Heizöl mit 20 % biogenen Anteilen in Form von Rapsölfettsäuremethylester (FAME, Biodiesel) ist es für eine konservative Beurteilung des Korrosionssystems Werkstoff/Medium/Umgebung wichtig, die Alterungseffekte des Mediums einzubeziehen. Entwicklung eines Prüfverfahrens für die Untersuchung der Beständigkeit von metallenen Werkstoffen und Polymeren in Heizöl und Heizöl-Biodiesel-Blends, das für eine Vorauswahl der Werkstoffe und zum Nachweis der Beständigkeit im Hinblick auf die bauaufsichtlichen Zulassungsverfahren geeignet ist. Ein Schwerpunkt wird bei den metallenen Werkstoffen auf der Erprobung von Messmethoden liegen, mit denen sich in kurzer Versuchszeit ein Korrosionsangriff detektieren lässt. T2 - Seminar: Ausgewählte Kapitel der Werkstofftechnik an der Bergischen Universität Wuppertal CY - Wuppertal, Germany DA - 24.01.2020 KW - Heizöl-20% Biodiesel-Blend KW - Beständigkeitsuntersuchungen KW - Metallene Werkstoffe KW - Polymerwerkstoffe PY - 2020 AN - OPUS4-50298 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Pötzsch, S. A1 - Bäßler, Ralph T1 - Compatibility of polymers with aged heating oil containing 10 % and 20 % biodiesel under static conditions N2 - Biodiesel is viewed as a major source of energy. In areas such as the European Un-ion, where 80 % of the oil-based fuel is imported, there is also the desire to reduce dependence on external oil supplies. Materials compatibility is a major concern whenever the fuel composition is changed. The question arises of whether polymeric materials are resistant to heating oil with 20 % biodiesel (B20) in comparison to pure heating oil. The polarity of biodiesel increases its solvency and facilitates permeation and extrac-tion. Solvation, swelling and/or extraction lead to changes in the physical properties. Extraction alters the fuel chemistry. These chemical changes could also accelerate the degradation (hydrolysis and oxidation) of the polymeric material with the loss of additives and stabilizers. Exposure tests to determine the resistance of polymers frequently used for compo-nents in middle distillate facilities, such as ACM, FKM, HNBR, PA, PE, POM, PUR and PVC in heating oil and a blend of heating oil and 20 % biodiesel (B20) were al-ready performed. The objective of this research was to determine the resistance of these polymers in 8-year aged heating oil blend B10 and 1-year aged blend B20 at 40 °C. Mass, tensile strength, breaking elongation and Shore hardness A (D) of the test specimens were determined before and after exposure for 84 (42) days in the test fuels under static conditions. There is not determined a threshold for the reduction in tensile properties and Shore hardness in the international standards. Therefore, a threshold of 15 % was deter-mined for the evaluation of the compatibility. A significant reduction in Shore hardness was determined after exposure of ACM and PUR test specimens in 1-year aged B20. The tensile strength of PUR test specimens in 1-year aged B20 was reduced by more than 50 %, and the breaking elongation by more than 30 %. A decrease in breaking elongation was measured for POM test specimens after ex-posure to 1-year aged B20 by 25 % (limited resistance). 8-year aged B10 had a stronger effect than 1-year aged B20 on the polymers. ACM test specimens were softened by B10 resulting in a drop of Shore hardness by over 20 %. B10 reduced tensile strength and breaking elongation of PUR test specimens by over 50 %. In contrast, the breaking elongation of POM was increased by over 270 %. It can be concluded that the polymers HNBR, FKM, PA6, PE and PVC are resistant in 1-year aged B20 whereas ACM and POM are limited resistant. PUR is not re-sistant. HNBR, FKM, PA6, PE and PVC are resistant in 8-year aged B10, whereas PUR and POM are not resistant, and ACM just limited resistant. T2 - EUROCORR 2020 CY - Online meeting DA - 07.09.2020 KW - Aged heating oil with 10% and 20% biodiesel KW - Resistance of polymers KW - Tensile properties KW - Shore hardness PY - 2020 AN - OPUS4-51240 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pötzsch, Sina A1 - Weltschev, Margit A1 - Bäßler, Ralph T1 - Compatibility of polymers exposed to heating oil blends with 10 % and 20 % biodiesel (FAME) N2 - Biodiesel (FAME) from rapeseed is an environmentally friendly alternative to common fossil fuels. It is also suitable to serve as blending component to fuels like heating oil. If the fuel composition is changed, materials compatibility must be guaranteed. Adding polar biodiesel to nonpolar heating oil, changes the blend’s solvency and might cause swelling, extraction and solvation of polymers. The objective of this research was to investigate the compatibility of polymeric materials, which are commonly used for components in middle distillate facilities, along with blends of heating oil and 20 % biodiesel (B20). For this propose, ACM, HNBR, FKM, PE, PA 6, POM, PUR and PVC were exposed to heating oil and B20 for 42 and 84 days at 40 °C. In addition, the polymers HNBR, FKM, PA, POM and PVC were also exposed at 70 °C. Furthermore, the resistance of polymers in eight-year aged B10 at 40 °C was evaluated. Ageing of biodiesel increases acidity which might propagate polymer corrosion. The materials were evaluated as resistant, if the loss in tensile properties (tensile strength and elongation at break) and Shore hardness remained under 15 % compared to the initial unexposed material values. For investigations under compressed conditions, the compression set was determined for specimens of ACM, FKM and HNBR after exposure in heating oil B0 and B20 for 3,7,14, 28, 56 and 90 days at 40 °C according to ISO 815-1. It was found that the resistance in B20 at 40 °C was given for all tested polymers except PUR. In the 8 years aged B10, PUR and POM were not compatible and ACM just conditionally compatible. At 70 °C, FKM and PVC were resistant in B20, whereas HNBR and PA 6 were not compatible. Swelling occurred for the elastomers ACM, HNBR and PUR. T2 - AMPP Annual International Corrosion Conference 2021 CY - Online Meeting DA - 19.04.2021 KW - Biodiesel KW - FAME KW - RME KW - Polymer in fuels PY - 2021 SP - 16222-01 EP - 16222-12 CY - Houston AN - OPUS4-52499 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -