TY - CONF A1 - Weltschev, Margit A1 - Werner, Jan A1 - Heming, Frank A1 - Jochems, Frank T1 - Impact of biocomponents in the fuel and heating oil on the compatibility of sealing materials N2 - The objective of this research was to determine the resistance of frequently used sealing materials such as FKM, FVMQ, VMQ, EPDM, CR, CSM, IIR, PA, NBR and PUR in fuels and heating oil with and without admixtures of biogenic sources such as E10, diesel fuel with 5 % biodiesel, non-aged and 2 year aged B10 (heating oil with 10 % biodiesel), pure diesel, standard heating oil and premium grade fuel Super plus at 20 °C, 40 °C and 70 °C. Mass, tensile strength and breaking elongation of the test specimens were determined before and after the exposure for 84 days in the fuels. The visual examination of some elastomer test specimens clearly showed the great volume increase until break or partial dissolution. Shore hardness A and D (for PA) were determined before and after exposure of the test specimens in the biofuels for 42 days. There is not determined a threshold for the reduction in tensile properties and Shore hardness in the international standards. Therefore a threshold of 15 % was determined for the evaluation of the compatibility. In summary, it can be therefore stated that the chemical resistance of the fluoropolymers FKM and FVMQ in fuels and biofuels is the best one. T2 - CORROSION 2016 CY - Vancouver, Kanada DA - 06.03.2016 KW - sealing materials KW - compatibility KW - biofuels PY - 2016 SP - Paper No. 7307, 1 EP - 12 PB - NACE INTERNATIONAL, Publications Division CY - Houston, Texas 77084 (USA) AN - OPUS4-35622 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Werner, Jan A1 - Heming, Frank A1 - Jochems, Frank T1 - Impact of biocomponents in the fuel and heating oil on the compatibility of sealing materials N2 - The objective of this research was to determine the resistance of frequently used sealing materials such as FKM, FVMQ, VMQ, EPDM, CR, CSM, IIR, PA, NBR and PUR in fuels and heating oil with and without admixtures of biogenic sources such as E10, diesel fuel with 5 % biodiesel, non-aged and 2 year aged B10 (heating oil with 10 % biodiesel), pure diesel, standard heating oil and premium grade fuel Super plus at 20 °C, 40 °C and 70 °C. Mass, tensile strength and breaking elongation of the test specimens were determined before and after the exposure for 84 days in the fuels. The visual examination of some elastomer test specimens clearly showed the great volume increase until break or partial dissolution. Shore hardness A and D (for PA) were determined before and after exposure of the test specimens in the biofuels for 42 days. There is not determined a threshold for the reduction in tensile properties and Shore hardness in the international standards. Therefore a threshold of 15 % was determined for the evaluation of the compatibility. In summary, it can be therefore stated that the chemical resistance of the fluoropolymers FKM and FVMQ in fuels and biofuels is the best one. T2 - CORROSION 2016 CY - Vancouver, Kanada DA - 06.03.2016 KW - compatibility KW - sealing materials KW - biofuels PY - 2016 AN - OPUS4-35623 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Hoffmann, Gabi T1 - Schadensursachen an Rohrleitungen N2 - Das Gefährdungspotential von Rohrleitungen hängt primär von den Eigenschaften des durchfließenden Stoffes, den Betriebsbedingungen und den äußeren Beanspruchungen ab. Zu den Hauptschadensursachen an Rohrleitungen zählen Korrosion, Druckstöße und Kavitationsschläge, Zeitstandbeanspruchung, struktur- und fluidmechanische Schwingungen, Fremdberührungen, elektrische Fremdbeeinflussung und geologische Besonderheiten im Bereich des Rohrleitungsverlaufes. T2 - Workshop:Anwendung der verteilten akustischen und faseroptischen Sensorik zur kontinuierlichen Überwachung von Rohrleitungen CY - Berlin DA - 01.03.2016 KW - Korrosion KW - Zeitstandbeanspruchung KW - Struktur- und fluidmechanische Schwingungen KW - Elektrische Fremdbeeinflussung PY - 2016 AN - OPUS4-35624 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Werner, Jan A1 - Heming, Frank T1 - Compatibility of elastomers with biofuels N2 - Biofuels represent an important renewable fuel alternative to petroleum-derived transport fuels. Materials compatibility is a major concern whenever the fuel composition is changed. The aim of this work is to study the interaction of the elastomers: FKM, EPDM, CR, CSM, NBR, IIR, VMQ and FVMQ and biofuels such as biodiesel (FAME), E85 (fuel with 85% ethanol) and B10 (heating oil with 10% biodiesel). Exposure tests were performed with test specimens at 40°C (104°F) and 70°C (158°F) for 84 days to document the changes in mass, volume and tensile properties according to ISO 1817. The exposure tests in E85 showed that the weight gain caused by swelling was in the range up to 12%. The lowest decrease in the tensile properties was determined for FKM, VMQ and IIR. The weight gain of the elastomers in biodiesel varied between 10% (FKM) and 126% (CSM) and the loss of tensile strength between 16% (FKM) and 100% (CSM) at 70°C (158°F). FKM and FVMQ absorbed much less B10 and swelled less. NBR, EPDM, CR, CSM, IIR and VMQ were not resistant to B10 at all as the decrease in the tensile properties was significantly over 50%. Among all of the elastomers FKM showed high compatibility with these biofuels up to 70°C (158°F). T2 - Corrosion 2014 CY - San Antonio, TX, USA DA - 09.03.2014 KW - Biofuels KW - Elastomers KW - Compatibility KW - Change in tensile properties KW - Change in mass KW - Sealing materials KW - Biodiesel KW - E85 KW - B10 KW - Mass loss KW - Tensile properties PY - 2014 SP - Paper 3745, 1 EP - 9 AN - OPUS4-30411 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Comparison of the Corrosion Resistance to Dangerous Goods of Austenitic CrNiMo and Duplex Steels T2 - CORROSION 2014 CY - San Antonio, TX, USA DA - 2014-03-09 PY - 2014 AN - OPUS4-30429 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Compatibility of Elastomers with Biofuels T2 - CORROSION 2014 CY - San Antonio, TX, USA DA - 2014-03-09 PY - 2014 AN - OPUS4-30430 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bäßler, Ralph A1 - Weltschev, Margit ED - Wieland, H.-J. ED - Brockmann, S. T1 - Duplex steel's corrosion resistance compared to the austenite containing molybdenum KW - Duplexsteel KW - Dangerous goods PY - 2014 SN - 978-3-514-00813-7 SP - 316 EP - 323 PB - Verl. Stahleisen GmbH CY - Düsseldorf AN - OPUS4-31035 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Niebergall, Ute T1 - Comparison of the stress crack resistance of polyethylene grades with the test performance behaviour of packagings for the transport of dangerous goods N2 - Technically high-quality hollow articles made of polyethylene have proved many times their value as dangerous goods packagings. Design type tests according to the international regulations for the transport of dangerous goods - drop test, stacking test, hydraulic pressure test and leakproofness test must be performed for every design type and manufacturer. The properties melt flow rate (MFR), relative density (D), low temperature notched Impact strength (N.I.S.) at -30 °C, environmental stress crack resistance (FNCT) and resistance to oxidative degradation Ox by nitric acid (determined by the increase of MFR) have been selected together with the corresponding test methods and tolerances for a comparison of polyethylene grades of one design type in the procedural rule on suitability proof for alternative plastic resins used for dangerous goods packagings and intermediate bulk containers (IBCs) – EN 15507. We wanted to proof the practical relevance of this standard by comparing the relationship between the results of the FNCT and the times to failure of design types in stacking tests with wetting solution and normal butyl acetate saturated wetting solution. T2 - EUROCORR 2010 CY - Moscow, Russia DA - 13.09.2010 KW - Drop test KW - Stacking test KW - Hydraulic pressure test KW - Leakproofness test PY - 2010 AN - OPUS4-35843 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Compatibility of metallic tank and polymeric sealing materials with biofuels T2 - ACHEMA CY - Frankfurt am Main DA - 2015-06-15 PY - 2015 AN - OPUS4-33534 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Kohl, Anka A1 - Haufe, Manuela T1 - Compatibility of polyethylene grades with biofuels and biodiesel-heating oil blends N2 - 8iofuels including ethanol and biodiesel (fatty acid methyl ester) represent an important renewable fuel alternative to petroleum-derived transport fuels. lncreasing biofuels use would bring some benefits, such as a reduction in oil demands and greenhause gas emissions, and an improvement in air quality. T2 - EUROCORR 2015 - European corrosion congress CY - Graz, Austria DA - 06.09.2015 KW - Compatibility KW - Polyethylene grades KW - Biofuels KW - Change in MFR and tensile properties PY - 2015 SP - Paper 16_1074, 1 EP - 11 AN - OPUS4-34203 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -