TY - JOUR A1 - Kricheldorf, Hans R. A1 - Weidner, Steffen A1 - Meyer, Andreas T1 - Poly(butylene terephthalate): About condensation, cyclization, degradation and elimination reactions in the solid state, and the role of smooth crystal surfaces N2 - Three commercial poly(butylene terephthalate) (PBT) samples - Pocan B1300 (B13), Pocan B1600 (B16), and Addigy P 1210 (AP121) - served as the starting materials for the annealing experiments, which were conducted with and without the addition of esterification and transesterification catalysts. The catalysts used were Sn(II) 2-ethylhexanoate (SnOct₂), Zr(IV) acetylacetonate, and 4-toluene sulfonic acid (TSA). Temperatures varied between 150 and 210 °C. The PBT samples were characterized using differential scanning calorimetry (DSC), gel permeation chromatography (GPC), small-angle X-ray scattering (SAXS), and matrix-assisted laser desorption/ionization time-of-flight (MALDI TOF) mass spectrometry. The MALDI mass spectra of all three samples differed greatly but displayed mass peaks of cycles. Similar results were produced by annealing with SnOct₂ or Zr(acac)₄, which favored the formation of even-numbered cycles within the mass range below m/z 5000, along with slow degradation. TSA favored a more intensive degradation without the formation of cycles or even with the destruction of cycles. PBT chains with two carboxylic (COOH) end groups were the most stable species under all circumstances. The origin of the extremely high melting point of AP121 (241–242 °C) can be explained by the smoothing of crystallite surfaces via transesterification. The results suggest that combining MALDI mass spectrometry and SAXS measurements provides a new way to better understand the solid-state chemistry of PBT and related polyesters. KW - MALDI-TOF MS KW - Polybutylene Terephthalate KW - Crystallization KW - solid state KW - cyclization PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-652844 DO - https://doi.org/10.1016/j.polymdegradstab.2025.111862 SN - 0141-3910 VL - 245 SP - 1 EP - 11 PB - Elsevier Ltd. AN - OPUS4-65284 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dalgic, Mete‐Sungur A1 - Kumar, Sourabh A1 - Weidner, Steffen T1 - Quantitative Analysis of Polymers by MALDI‐TOF Mass Spectrometry: Correlation Between Signal Intensity and Arm Number N2 - The signal intensities of linear and star‐shaped poly(L‐lactides) (PLA) and poly (ethylene oxides) (PEO) were compared to determine the influence of the number of arms on the ionization in matrix‐assisted laser desorption/ionization time‐of‐flight (MALDI‐TOF) mass spectrometry. In this study, a variety of blends were prepared and investigated, including binary and ternary combinations of linear and star‐shaped polymers with similar molecular masses. The focus was on examining their intensity ratios. In equimolar binary PLA blends, polymer stars were observed to exhibit higher intensities than their linear counterparts. This result was supported by experiments with equimolar ternary PLA blends, which clearly demonstrated an intensity dependence on the number of polymer arms. It was observed that four‐arm PLA exhibited higher intensities than three‐arm PLA. A similar trend was observed in investigations involving acetylated polymer end groups, suggesting that differences in ionization are primarily influenced by polymer architecture rather than end groups. In order to validate this assumption, the binding energies for [polymer‐K] + adduct ions utilizing the most stable geometry obtained from GOAT (Global Optimizer Algorithm) were calculated, revealing that star‐shaped lower mass oligomers have slightly higher binding energies. KW - MALDI-TOF MS KW - Starlike polymers KW - Quantification KW - Topology PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-653401 DO - https://doi.org/10.1002/jms.70023 SN - 1076-5174 VL - 61 IS - 1 SP - 1 EP - 12 PB - John Wiley & Sons Ltd. AN - OPUS4-65340 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weidner, Steffen A1 - Meyer, Andreas A1 - Falkenhagen, Jana A1 - Kricheldorf, Hans R. T1 - Cyclic polyglycolide by means of metal acetylacetonates N2 - Glycolide was polymerized in bulk at 160 °C using various metal acetylacetonates as catalysts. Zirconium acetylacetonate was particularly efficient, enabling rapid polymerization even at 130 °C. The formation of cyclic poly(glycolic acid) (PGA), most likely via a ring-expansion polymerization (REP) mechanism, was proven by matrix-assisted laser desorption/ionization time-of-flight (MALDI-TOF) mass spectrometry. Depending on the polymerization conditions, the formation of even-numbered cycles was favored to varying degrees. Number-average molecular weights (Mn) in the range of 2000–3500 g mol−1 were achieved with dispersities below 2.0. Wide-angle X-ray scattering (WAXS) powder patterns showed that the crystal lattice was the same as that of known linear PGAs, regardless of the Mn values. These patterns enabled a comparison of crystallinities with values derived from DSC measurements. KW - MALDI-TOF MS KW - Polyglycolide KW - Crystallization KW - Small-angle X-ray scattering KW - Cyclization PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-653731 DO - https://doi.org/10.1039/d5ra07961f SN - 2046-2069 VL - 16 IS - 2 SP - 1757 EP - 1764 PB - Royal Society of Chemistry (RSC) AN - OPUS4-65373 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Meyer, Andreas A1 - Weidner, Steffen A1 - Kricheldorf, Hans R. T1 - Star-shaped poly(l-lactide)s based on pentaerythritol: About crystallization and polycondensation plus disproportionation and ring formation in the solid state N2 - Star-shaped poly( L-lactide)s (s-PLAs), were prepared by ring-opening polymerization of with pentaerythritol and catalyzed by tin(II) 2-ethylhyexanoate (SnOct out in bulk at either 120 ◦ C or 160 ◦ L-lactide (LA) initiated 2 ). Two small series of ROPs were carried C with variation of the LA/initiator ratio. Matrix-assisted laser desorption/ ionization time-of-flight (MALDI-TOF) mass spectra revealed traces of cycles in 120 ◦ C samples only at low initiator/catalyst ratios. In contrast, higher fractions of cycles were detected in samples prepared at 160 C, suggesting a "back-biting" origin. The influence of arm length and thermal history on crystallinity was investigated by differential scanning calorimetry (DSC) and wide-angle x-ray scattering (WAXS). It was shown that annealing increased the melting temperature (T ◦ ◦ m ) and crystallinity. However, annealing at 140 ◦ C for 14 d also caused significant solid-state transesterification. In addition, crystallites composed of s-PLAs with extended arms and, simultaneously, crystallites composed exclusively of extended rings were formed, identified by their typical "sawtooth" pattern in the MALDI mass spectra. Small angle x-ray scattering (SAXS) indicated that the crystal thickness was lower than that of linear PLAs annealed under identical conditions, but increased upon annealing at 140 C. KW - MALDI-TOF MS KW - Polylactide KW - Crystallisation KW - AStar-shaped polymers PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-636832 DO - https://doi.org/10.1016/j.polymer.2025.128709 SN - 0032-3861 VL - 334 SP - 1 EP - 11 PB - Elsevier Ltd. AN - OPUS4-63683 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, Hans R. A1 - Weidner, Steffen T1 - H2O-Initiated Polymerization of L-Lactide N2 - Water-initiated ring-opening polymerizations (ROPs) of L-lactide (LA) were performed in bulk at 140 °C, whereupon 11 different salts or complexes of low-toxic metal ions such as tin (II), Zn(II), Zr(IV), and Bi(III) were used as catalysts. Only four catalysts gave satisfactory results despite a long reaction time (24 h). The influence of the temperature was studied with tin (II) 2-ethylhexanoate (SnOct2), dibutyltin oxide (Bu2SnO), and zinc bis-acetylacetonate (Zn(acac)2) and zirconium acetylacetonate (Zr(acac)4). With SnOct2, Bu2SnO and Zr(acac)4 the time was varied at 140 °C to compare their reactivity. Furthermore, two series of ROPs were carried out with variation of the LA/H2O ratio to verify the control of the molecular weight by the monomer-initiator ratio. Bi- or tri-modal molecular weight distributions (MWD) were found for most of the ROPs and bimodal melting endotherms in the differential scanning calorimetry (DSC) heating traces. The thickness and dependence of the 3D packing of the crystallites were monitored by small-angle X-ray scattering (SAXS) measurements. KW - MALDI-TOF MS KW - Polylactide KW - Ring-opening polymerization KW - Crystallization PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-628761 DO - https://doi.org/10.1007/s10924-025-03565-w SN - 1572-8919 VL - 33 IS - 6 SP - 2843 EP - 2857 PB - Springer Science and Business Media LLC CY - New York, NY AN - OPUS4-62876 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, Hans R. A1 - Weidner, Steffen A1 - Scheliga, Felix T1 - Polycondensation of L-lactic acid: a deeper look into solid state polycondensation N2 - L-Lactic acid (LA) was condensed in the presence of SnCl2 or 4-toluenesulfonic acid (TSA) at 140 °C, and chain growth without cyclization was observed. In addition, poly(L-lactic acid)s (PLAs) with a degree of polymerization (DP) of 25, 50 or 100 were prepared by water-initiated ring-opening polymerization (ROP). These PLAs were annealed in the solid state at 140 °C and 160 °C in the presence of tin(II) 2-ethylhexanoate (SnOct2, SnCl2 or TSA). The changes in the molar mass distribution and in the topology were characterized by means of matrix-assisted laser desorption/ionization time-of-flight (MALDI-TOF) mass spectrometry and size exclusion chromatography (SEC). With increasing time, fewer side reactions caused higher molar masses and increasing fractions of cyclic polylactides (cPLA) were obtained. Their “saw tooth” pattern in the MALDI-TOF mass spectra indicated the formation of extended ring crystallites in the solid state. TSA was the most active catalyst and caused fewer side reactions than SnCl2, which was the least reactive catalyst. Acetylation of the CH-OH end groups hindered polycondensation and prevented the formation of cPLAs. Reaction mechanisms will be discussed. KW - MALDI-TOF MS KW - Polycondensation KW - Polylaktide KW - Solid state PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-625271 DO - https://doi.org/10.1039/d4py01191k SN - 1759-9962 SP - 1 EP - 9 PB - Royal Society of Chemistry (RSC) AN - OPUS4-62527 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H. R. A1 - Weidner, Steffen T1 - Syntheses of cyclic polylactides and the problem of catenane formation N2 - Cyclic poly(L-lactide)s (PLAs) were prepared in bulk either by ring-expansion polymerization (REP) or by ring-opening polymerization (ROP) with simultaneous polycondensation (ROPPOC). In contrast to REP the latter method involves formation of linear chains and thus, may involve formation of polydisperse catenanes that affect crystallization. The reprecipitated PLAs were annealed at 120 °C and compared with regard to melting temperature (Tm) and melting enthalpy (ΔHm). For similar molar masses the PLAs prepared by REP and ROPPOC had almost identical Tm's and crystallinities. Furthermore, the influence of REP and ROPPOC catalysts on the morphology of the virgin reaction products was compared. KW - MALDI-TOF MS KW - Catenane KW - Polylactide PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-625061 DO - https://doi.org/10.1039/d4ra08683j VL - 15 IS - 5 SP - 3686 EP - 3692 PB - RSC AN - OPUS4-62506 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rösler, Alexander A1 - Weidner, Steffen A1 - Klamroth, Tillmann A1 - Müller, Axel H. E. A1 - Schlaad, Helmut T1 - Kinetics of anionic polymerization of β‐myrcene in hydrocarbon solvents N2 - The kinetics of anionic polymerization of β‐myrcene initiated by sec‐butyllithium were examined in saturated and unsaturated hydrocarbon solvents, i.e. cyclohexane, cyclohexene, 4‐vinylcyclohexene and dl‐limonene. Polymerizations usually proceeded in a living manner, i.e. in the absence of termination and chain transfer reactions, in all solvents, to produce well‐defined polymyrcenes with high content (85%) of cis‐1,4 units. However, polymyrcenyllithium chains exhibited limited long‐term stability in 4‐vinylcyclohexene solution, most probably due to chain transfer to solvent. Reaction orders with respect to the concentration of active chains were found to be one‐quarter in cyclohexane increasing to one‐half in unsaturated solvents, indicating that the polymyrcenyllithium chains are present as tetrameric or dimeric associates, respectively. Apparent activation energies were found to be 81 kJ mol−1 in cyclohexane and 77 kJ mol−1 in dl‐limonene solution, which are close to the values obtained by quantum chemical calculations. KW - MALDI-TOF MS KW - Anionic polymerization KW - β‐myrcene KW - Kinetics KW - Reaction order KW - Activation energy KW - Microstructure KW - Quantum chemical calculations PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-630900 DO - https://doi.org/10.1002/pi.6772 SN - 1097-0126 SP - 1 EP - 8 PB - Wiley CY - New York, NY AN - OPUS4-63090 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, Hans R. A1 - Weidner, Steffen T1 - Zwitterionic polymerization of glycolide catalyzed by pyridine N2 - The usefulness of various N- and P-based catalysts for syntheses of cyclic polyglycolide via zwitterionic polymerization of glycolide was examined. Most catalysts produced discolored, largely insoluble polyglycolides consisting of cycles and unidentified byproducts. Soluble, cyclic polyglycolides were obtained using neat pyridine as catalyst at 120 °C, 100 °C, 80 °C, and even at 60 °C. The number-average molecular weights were extremely low and depended slightly on the glycolide-to-pyridine ratio. Three different mass distributions of the cycles were detected by mass spectrometry, depending on the reaction conditions. The cyclic polyglycolides were also characterized by differential scanning calorimetry (DSC) and small-angle X-ray scattering (SAXS) measurements. The SAXS data in combination with the mass spectra indicate that the majority of the cycles form extended-ring crystallites KW - MALDI-TOF MS KW - Polylactide KW - Polymerization KW - Zitterions PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-639748 DO - https://doi.org/10.1039/d5py00762c SN - 1759-9954 SP - 1 EP - 9 PB - Royal Society of Chemistry (RSC) AN - OPUS4-63974 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, Hans R. A1 - Weidner, Steffen T1 - Polymerization of L‐Lactide Catalyzed by Metal Acetylacetonate Complexes N2 - ABSTRACTRing‐opening polymerizations (ROPs) of l‐lactide (LA) were performed at 120°C, 140°C, 150°C, and 180°C in bulk catalyzed by acetylacetonate (acac) complexes of manganese(II), nickel(II), copper(II), zirconium(IV), dibutyltin(IV), and vanadyl(V). These experiments revealed that only the acac complexes of Zr and Bu2Sn were reactive enough to enable quantitative polymerization within a few hours. Further ROPs with Bu2Sn(acac)2 and Zr(acac)4 showed that Bu2Sn(acac)2 had a slightly lower reactivity than the Zr complex. The ROPs catalyzed with Zr(acac)4 yielded number average molecular weights (Mn) up to 70,000 g mol−1. The matrix‐assisted laser desorption/ionization time‐of‐flight (MALDI‐TOF) mass spectra indicated an exclusive formation of cycles in the mass range of up to m/z 13,000 for Zr(acac)4 and up to m/z 18,000 for Bu2Sn(acac)2. Unusually high melting temperatures (187°C–192°C) were also achieved along with high crystallinities. Furthermore, four lactide/glycolide copolymerizations catalyzed by Zr(acac)4 were performed, and the topology and the extent of transesterification were characterized by MALDI‐TOF mass spectrometry and 13C NMR spectroscopy. KW - MALDI-TOF MS KW - Polycondensation KW - Acetylacetonate PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-639754 DO - https://doi.org/10.1002/pol.20250788 SN - 2642-4150 SP - 1 EP - 9 PB - Wiley Periodicals LLC. AN - OPUS4-63975 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -