TY - JOUR A1 - Kricheldorf, Hans R. A1 - Weidner, Steffen A1 - Meyer, Andreas T1 - Poly(butylene terephthalate): About condensation, cyclization, degradation and elimination reactions in the solid state, and the role of smooth crystal surfaces N2 - Three commercial poly(butylene terephthalate) (PBT) samples - Pocan B1300 (B13), Pocan B1600 (B16), and Addigy P 1210 (AP121) - served as the starting materials for the annealing experiments, which were conducted with and without the addition of esterification and transesterification catalysts. The catalysts used were Sn(II) 2-ethylhexanoate (SnOct₂), Zr(IV) acetylacetonate, and 4-toluene sulfonic acid (TSA). Temperatures varied between 150 and 210 °C. The PBT samples were characterized using differential scanning calorimetry (DSC), gel permeation chromatography (GPC), small-angle X-ray scattering (SAXS), and matrix-assisted laser desorption/ionization time-of-flight (MALDI TOF) mass spectrometry. The MALDI mass spectra of all three samples differed greatly but displayed mass peaks of cycles. Similar results were produced by annealing with SnOct₂ or Zr(acac)₄, which favored the formation of even-numbered cycles within the mass range below m/z 5000, along with slow degradation. TSA favored a more intensive degradation without the formation of cycles or even with the destruction of cycles. PBT chains with two carboxylic (COOH) end groups were the most stable species under all circumstances. The origin of the extremely high melting point of AP121 (241–242 °C) can be explained by the smoothing of crystallite surfaces via transesterification. The results suggest that combining MALDI mass spectrometry and SAXS measurements provides a new way to better understand the solid-state chemistry of PBT and related polyesters. KW - MALDI-TOF MS KW - Polybutylene Terephthalate KW - Crystallization KW - solid state KW - cyclization PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-652844 DO - https://doi.org/10.1016/j.polymdegradstab.2025.111862 SN - 0141-3910 VL - 245 SP - 1 EP - 11 PB - Elsevier Ltd. AN - OPUS4-65284 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dalgic, Mete‐Sungur A1 - Kumar, Sourabh A1 - Weidner, Steffen T1 - Quantitative Analysis of Polymers by MALDI‐TOF Mass Spectrometry: Correlation Between Signal Intensity and Arm Number N2 - The signal intensities of linear and star‐shaped poly(L‐lactides) (PLA) and poly (ethylene oxides) (PEO) were compared to determine the influence of the number of arms on the ionization in matrix‐assisted laser desorption/ionization time‐of‐flight (MALDI‐TOF) mass spectrometry. In this study, a variety of blends were prepared and investigated, including binary and ternary combinations of linear and star‐shaped polymers with similar molecular masses. The focus was on examining their intensity ratios. In equimolar binary PLA blends, polymer stars were observed to exhibit higher intensities than their linear counterparts. This result was supported by experiments with equimolar ternary PLA blends, which clearly demonstrated an intensity dependence on the number of polymer arms. It was observed that four‐arm PLA exhibited higher intensities than three‐arm PLA. A similar trend was observed in investigations involving acetylated polymer end groups, suggesting that differences in ionization are primarily influenced by polymer architecture rather than end groups. In order to validate this assumption, the binding energies for [polymer‐K] + adduct ions utilizing the most stable geometry obtained from GOAT (Global Optimizer Algorithm) were calculated, revealing that star‐shaped lower mass oligomers have slightly higher binding energies. KW - MALDI-TOF MS KW - Starlike polymers KW - Quantification KW - Topology PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-653401 DO - https://doi.org/10.1002/jms.70023 SN - 1076-5174 VL - 61 IS - 1 SP - 1 EP - 12 PB - John Wiley & Sons Ltd. AN - OPUS4-65340 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weidner, Steffen A1 - Meyer, Andreas A1 - Falkenhagen, Jana A1 - Kricheldorf, Hans R. T1 - Cyclic polyglycolide by means of metal acetylacetonates N2 - Glycolide was polymerized in bulk at 160 °C using various metal acetylacetonates as catalysts. Zirconium acetylacetonate was particularly efficient, enabling rapid polymerization even at 130 °C. The formation of cyclic poly(glycolic acid) (PGA), most likely via a ring-expansion polymerization (REP) mechanism, was proven by matrix-assisted laser desorption/ionization time-of-flight (MALDI-TOF) mass spectrometry. Depending on the polymerization conditions, the formation of even-numbered cycles was favored to varying degrees. Number-average molecular weights (Mn) in the range of 2000–3500 g mol−1 were achieved with dispersities below 2.0. Wide-angle X-ray scattering (WAXS) powder patterns showed that the crystal lattice was the same as that of known linear PGAs, regardless of the Mn values. These patterns enabled a comparison of crystallinities with values derived from DSC measurements. KW - MALDI-TOF MS KW - Polyglycolide KW - Crystallization KW - Small-angle X-ray scattering KW - Cyclization PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-653731 DO - https://doi.org/10.1039/d5ra07961f SN - 2046-2069 VL - 16 IS - 2 SP - 1757 EP - 1764 PB - Royal Society of Chemistry (RSC) AN - OPUS4-65373 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Jlalia, I. A1 - Gomri, M. A1 - Chabbah, T. A1 - Chatti, S. A1 - Weidner, Steffen A1 - Abderrazak, H. A1 - Marestin, C. A1 - Mercier, R. A1 - Ben Halima, H. A1 - Lakard, B. A1 - Jaffrezic Renault, N. T1 - Design of Fluorinated Poly(Ether-Pyridine) Films for Impedimetric Detection of Heavy Metal Ions N2 - A series of fluorinated poly(ether-pyridine)s were synthesized via polycondensation of bis-perfluoropyridine with either bisphe-nol A (BPA) or isosorbide, a bio-sourced diol. The polymers were characterized using 1 H and 19 F NMR spectroscopy, and their molecular weights were determined using GPC. Thermal properties were assessed using thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). The presence of isosorbide in polymer P2 increases the glass transition temperature and results in a lower molecular weight and a higher hydrophilicity. On the other hand, polymer P3, based on BPA, shows the best thermal stability, the highest molecular weight, and the most pronounced hydrophobic character. Electrochemical impedance spectroscopy (EIS) was used to evaluate the modified gold electrodes for the selective detection of metal ions. Among the four target ions (Ni 2+, Cd 2+, Pb2+, and Hg 2+), defined by the European Water Framework Directive, Pb2+ was selectively detected on the hydrophilic polymer P2, while Cd 2+ was selectively detected on the hydrophobic polymer P3. The achieved detection limits were 5 × 10−11 M, corresponding to 10 ng/L for Pb2+ and 5.6 ng/L for Cd 2+, respectively. KW - Cadmium KW - Electrochemical impedance spectroscopy KW - Fluorinated polyether pyridines KW - Isosorbide KW - Lead PY - 2025 DO - https://doi.org/10.1002/pat.70038 SN - 1099-1581 VL - 36 IS - 1 SP - 1 EP - 14 PB - John Wiley & Sons Ltd. AN - OPUS4-62384 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, Hans. R. A1 - Weidner, Steffen T1 - About the Toxicity of Polymerization Catalysts and Polymer Additives Based on Tin(II) Salts and Tin(IV) Compounds N2 - This article reviews and discusses information on the toxicity of numerous tin-based catalysts used in academic research and industrial production for the synthesis of various polymers, such as polyesters, polyurethanes, and polysiloxanes. Tin(IV) compounds used as additives and as PVC stabilizers are also considered. Emphasis is put on the differentiation between tin(II) salts on the one hand and tin(IV) compounds on the other hand. In the first chapter, historical facts about human contact with stannous ions are discussed, along with toxicity studies of canned foods and beverages. In the second part, toxicity tests based on cell cultures and medical applications of tin(II)-containing films or implants are described. The third part focuses on alkyl and aryl tin(IV) compounds. KW - Tin KW - Toxicity KW - Environment KW - Polymer catalysts KW - Polymer additives PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-642877 DO - https://doi.org/10.1021/acs.chas.5c00105 SN - 1871-5532 SP - 1 EP - 13 PB - American Chemical Society (ACS) AN - OPUS4-64287 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Meyer, Andreas A1 - Weidner, Steffen A1 - Kricheldorf, Hans R. T1 - Star-shaped poly(l-lactide)s based on pentaerythritol: About crystallization and polycondensation plus disproportionation and ring formation in the solid state N2 - Star-shaped poly( L-lactide)s (s-PLAs), were prepared by ring-opening polymerization of with pentaerythritol and catalyzed by tin(II) 2-ethylhyexanoate (SnOct out in bulk at either 120 ◦ C or 160 ◦ L-lactide (LA) initiated 2 ). Two small series of ROPs were carried C with variation of the LA/initiator ratio. Matrix-assisted laser desorption/ ionization time-of-flight (MALDI-TOF) mass spectra revealed traces of cycles in 120 ◦ C samples only at low initiator/catalyst ratios. In contrast, higher fractions of cycles were detected in samples prepared at 160 C, suggesting a "back-biting" origin. The influence of arm length and thermal history on crystallinity was investigated by differential scanning calorimetry (DSC) and wide-angle x-ray scattering (WAXS). It was shown that annealing increased the melting temperature (T ◦ ◦ m ) and crystallinity. However, annealing at 140 ◦ C for 14 d also caused significant solid-state transesterification. In addition, crystallites composed of s-PLAs with extended arms and, simultaneously, crystallites composed exclusively of extended rings were formed, identified by their typical "sawtooth" pattern in the MALDI mass spectra. Small angle x-ray scattering (SAXS) indicated that the crystal thickness was lower than that of linear PLAs annealed under identical conditions, but increased upon annealing at 140 C. KW - MALDI-TOF MS KW - Polylactide KW - Crystallisation KW - AStar-shaped polymers PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-636832 DO - https://doi.org/10.1016/j.polymer.2025.128709 SN - 0032-3861 VL - 334 SP - 1 EP - 11 PB - Elsevier Ltd. AN - OPUS4-63683 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, Hans R. A1 - Weidner, Steffen T1 - H2O-Initiated Polymerization of L-Lactide N2 - Water-initiated ring-opening polymerizations (ROPs) of L-lactide (LA) were performed in bulk at 140 °C, whereupon 11 different salts or complexes of low-toxic metal ions such as tin (II), Zn(II), Zr(IV), and Bi(III) were used as catalysts. Only four catalysts gave satisfactory results despite a long reaction time (24 h). The influence of the temperature was studied with tin (II) 2-ethylhexanoate (SnOct2), dibutyltin oxide (Bu2SnO), and zinc bis-acetylacetonate (Zn(acac)2) and zirconium acetylacetonate (Zr(acac)4). With SnOct2, Bu2SnO and Zr(acac)4 the time was varied at 140 °C to compare their reactivity. Furthermore, two series of ROPs were carried out with variation of the LA/H2O ratio to verify the control of the molecular weight by the monomer-initiator ratio. Bi- or tri-modal molecular weight distributions (MWD) were found for most of the ROPs and bimodal melting endotherms in the differential scanning calorimetry (DSC) heating traces. The thickness and dependence of the 3D packing of the crystallites were monitored by small-angle X-ray scattering (SAXS) measurements. KW - MALDI-TOF MS KW - Polylactide KW - Ring-opening polymerization KW - Crystallization PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-628761 DO - https://doi.org/10.1007/s10924-025-03565-w SN - 1572-8919 VL - 33 IS - 6 SP - 2843 EP - 2857 PB - Springer Science and Business Media LLC CY - New York, NY AN - OPUS4-62876 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Falkenhagen, Jana A1 - Dalgic, Mete-Sungur A1 - Weidner, Steffen T1 - Quantitative MALDI-TOF Mass Spectrometry of Star-Shaped Polylactides Based on Chromatographic Hyphenation N2 - The end groups of three- and four-arm star-shaped polylactides (PLA) with trimethylolpropane and pentaerythritol core structures were functionalized with acetic acid. Reaction products with different degrees of functionalization were analyzed by matrix-assisted laser desorption/ionization time-of-flight (MALDI-TOF) mass spectrometry. Additional gradient elution liquid adsorption chromatography (GELAC) measurements were performed to determine the degree of functionalization. This technique enabled clear separation and sufficient quantification of the formed species. These chromatographic data could be used inversely to quantify mass spectrometric results, which are usually biased by the unknown ionization probabilities of different polymer end group structures. Our results showed that, in this particular case, the peak intensity in the MALDITOF mass spectra can be used to semiquantitatively determine the degree of functionalization in incompletely functionalized multiarm PLA. KW - Polylactides KW - MALDI-TOF-MS KW - Gradient elution liquid adsorption chromatography PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-625292 DO - https://doi.org/10.1021/jasms.4c00491 SN - 1879-1123 SP - 1 EP - 9 PB - American Chemical Society (ACS) AN - OPUS4-62529 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, Hans R. A1 - Weidner, Steffen A1 - Scheliga, Felix T1 - Polycondensation of L-lactic acid: a deeper look into solid state polycondensation N2 - L-Lactic acid (LA) was condensed in the presence of SnCl2 or 4-toluenesulfonic acid (TSA) at 140 °C, and chain growth without cyclization was observed. In addition, poly(L-lactic acid)s (PLAs) with a degree of polymerization (DP) of 25, 50 or 100 were prepared by water-initiated ring-opening polymerization (ROP). These PLAs were annealed in the solid state at 140 °C and 160 °C in the presence of tin(II) 2-ethylhexanoate (SnOct2, SnCl2 or TSA). The changes in the molar mass distribution and in the topology were characterized by means of matrix-assisted laser desorption/ionization time-of-flight (MALDI-TOF) mass spectrometry and size exclusion chromatography (SEC). With increasing time, fewer side reactions caused higher molar masses and increasing fractions of cyclic polylactides (cPLA) were obtained. Their “saw tooth” pattern in the MALDI-TOF mass spectra indicated the formation of extended ring crystallites in the solid state. TSA was the most active catalyst and caused fewer side reactions than SnCl2, which was the least reactive catalyst. Acetylation of the CH-OH end groups hindered polycondensation and prevented the formation of cPLAs. Reaction mechanisms will be discussed. KW - MALDI-TOF MS KW - Polycondensation KW - Polylaktide KW - Solid state PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-625271 DO - https://doi.org/10.1039/d4py01191k SN - 1759-9962 SP - 1 EP - 9 PB - Royal Society of Chemistry (RSC) AN - OPUS4-62527 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rösler, Alexander A1 - Weidner, Steffen A1 - Klamroth, Tillmann A1 - Müller, Axel HE A1 - Schlaad, Helmut T1 - Kinetics of anionic polymerization of β‐myrcene in hydrocarbon solvents N2 - AbstractThe kinetics of anionic polymerization of β‐myrcene initiated by sec‐butyllithium were examined in saturated and unsaturated hydrocarbon solvents, i.e. cyclohexane, cyclohexene, 4‐vinylcyclohexene and dl‐limonene. Polymerizations usually proceeded in a living manner, i.e. in the absence of termination and chain transfer reactions, in all solvents, to produce well‐defined polymyrcenes with high content (85%) of cis‐1,4 units. However, polymyrcenyllithium chains exhibited limited long‐term stability in 4‐vinylcyclohexene solution, most probably due to chain transfer to solvent. Reaction orders with respect to the concentration of active chains were found to be one‐quarter in cyclohexane increasing to one‐half in unsaturated solvents, indicating that the polymyrcenyllithium chains are present as tetrameric or dimeric associates, respectively. Apparent activation energies were found to be 81 kJ mol−1 in cyclohexane and 77 kJ mol−1 in dl‐limonene solution, which are close to the values obtained by quantum chemical calculations. © 2025 The Author(s). Polymer International published by John Wiley & Sons Ltd on behalf of Society of Chemical Industry. KW - Myrcene KW - Anionic polymerization KW - Reaction order KW - Activation energy KW - Microstructure KW - Quantum chemical calculation PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-636840 DO - https://doi.org/10.1002/pi.6772 SN - 0959-8103 SP - 1 EP - 8 PB - Wiley AN - OPUS4-63684 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -