TY - JOUR A1 - Kricheldorf, H.R. A1 - Weidner, Steffen A1 - Scheliga, F. A1 - Lahcini, M. T1 - Poly(epsilon-caprolactone) by combined ring-opening polymerization and polycondensation N2 - Numerous water-initiated polymerizations of εCL are conducted in bulk with variation of catalyst, reaction time, and temperature. The conversions are determined by 1H NMR and the molar masses by SEC measurements. For polymerizations at 100 °C, Bi triflate and Hf triflate are used as catalysts, whereas at 140 °C, Al triflate, Sn(II) triflate, SnCl2, HfCl4, BiCl3, and LaCl3 are used. In addition to a closed reaction vessel, experiments are also performed with stirring in a vacuum. Under these conditions, the best catalyst (SnCl2) yields 2–3 times higher molar masses and mass spectra indicate a significant higher fraction of cyclic polymers. The results prove that a modification of the procedure may stimulate a polycondesation process without change of catalyst, time, and temperature. KW - Epsilon-Caprolactone KW - Cyclization KW - MALDI-TOF mass spectrometry KW - Polycondensations KW - Ring-opening polymerizations PY - 2012 DO - https://doi.org/10.1002/macp.201200061 SN - 1022-1352 SN - 1521-3935 VL - 213 IS - 14 SP - 1482 EP - 1488 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-26273 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Trimpin, S. A1 - Weidner, Steffen A1 - Falkenhagen, Jana A1 - McEwen, C.N. T1 - Fractionation and Solvent-Free MALDI-MS Analysis of Polymers Using Liquid Adsorption Chromatography at Critical Conditions in Combination with a Multisample On-Target Homogenization/Transfer Sample Preparation Method N2 - A solvent-free homogenization/transfer matrix-assisted laser desorption/ionization (MALDI) mass spectrometry (MS) method is described for the preparation and precise transfer of up to 100 samples simultaneously on a single MALDI plate. This method is demonstrated using a poly(ethylene oxide) (PEO) mixture consisting of different molecular weights (500-6000) and end groups (PEO, dimethoxy-PEO, monomethoxy monomethacrylate-PEO, and dimethacrylate-PEO) that was fractionated using liquid adsorption chromatography at critical conditions. Off-line fractionation is performed prior to the on-target homogenization/transfer solvent-free sample preparation and MALDI mass analysis. The miniaturization of the solvent-free MALDI approach allowed analysis of less than 2 g per PEO component per fraction corresponding to ~200 pmol for PEO 6000. The amounts of polymer sample used for LC separation and the quality of the MS results are equivalent to the "dry spray" method; however, three times more fractions were collected and analyzed with the newly developed hyphenated approach. The off-line method eliminates optimization of, for example, spray conditions or spreading of organic solvents on the MALDI plate that occurs with droplet deposition methods. The widespread applications of MALDI make this solvent-free, multisample method particularly important as it expands the capabilities for obtaining mass measurements with great efficiencies in areas with increased sample numbers. In addition, the solvent-free method is well suited for automated MALDI analysis as it virtually eliminates the "dead-spot" phenomenon. PY - 2007 DO - https://doi.org/10.1021/ac070986w SN - 0003-2700 SN - 1520-6882 VL - 79 IS - 19 SP - 7565 EP - 7570 PB - American Chemical Society CY - Washington, DC AN - OPUS4-17737 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weidner, Steffen A1 - Trimpin, S. T1 - Mass Spectrometry of Synthetic Polymers KW - Mass Spectrometry KW - Polymers KW - Application PY - 2008 DO - https://doi.org/10.1021/ac8006413 SN - 0003-2700 SN - 1520-6882 VL - 80 IS - 12 SP - 4349 EP - 4361 PB - American Chemical Society CY - Washington, DC AN - OPUS4-17718 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weidner, Steffen A1 - Falkenhagen, Jana A1 - Krüger, Ralph-Peter A1 - Just, Ulrich T1 - Principle of Two-Dimensional Characterization of Copolymers N2 - Two-dimensional polymer characterization is used for a simultaneous analysis of molar masses and chemical heterogeneities (e.g., end groups, copolymer composition, etc.). This principle is based on coupling of two different chromatographic modes. Liquid adsorption chromatography at critical conditions (LACCC) is applied for a separation according to the chemical heterogeneity, whereas in the second-dimension fractions are analyzed with regard to their molar mass distribution by means of size exclusion chromatography (SEC). Because appropriate standards for a calibration of the SEC are seldom available, matrix-assisted laser desorption/ionization-time-of-flight mass spectrometry (MALDI-TOF MS) was used to substitute the SEC. The LACCC-MALDI MS coupling enables acquiring additional structural information on copolymer composition, which can considerably enhance the performance of this coupled method. KW - MALDI-TOF MS KW - Chromatographie KW - Kopplung PY - 2007 DO - https://doi.org/10.1021/ac062145f SN - 0003-2700 SN - 1520-6882 VL - 79 IS - 13 SP - 4814 EP - 4819 PB - American Chemical Society CY - Washington, DC AN - OPUS4-17722 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H.R. A1 - Weidner, Steffen T1 - High Tg copolyesters of lactide, isosorbide and isophthalic acid N2 - Using SnCl2, ZnCl2, Zn-lactate or Zr-acetylacetonate as catalysts ʟ-lactide was oligomerized in bulk with isosorbide as initiator. The ratio isosorbide/lactide was varied from 8/2 to 2/8. The resulting oligomers were in situ polycondensed with isophthaloyl chloride in various aromatic solvents. In chlorobenzene homogeneous reaction mixtures were obtained, whereas molten copolyesters precipitated from toluene and xylene. The obtained average molecular weights indicated high polydispersities. According to MALDI-TOF MS the low molar mass reaction products (<4 kDa) almost exclusively consisted of cyclics with a composition depending on the feed ratio. The glass-transition temperatures (Tg) varied between the values of poly(ʟ-lactide (64 °C) and poly(isosorbide isophthalate) (180 °C). Four polyesters prepared from 5-tert-butyl isophthalic acid displayed higher Tg values. Differential thermoanalysis evidenced that the thermostability decreases with higher fractions of lactide, but processing from the melt seems to be feasible up to temperatures of 260 °C without risking degradation. KW - Lactide KW - Isosorbide KW - Ring-opening polymerization KW - Polycondensation KW - Cyclization PY - 2013 DO - https://doi.org/10.1016/j.eurpolymj.2013.05.007 SN - 0014-3057 SN - 1873-1945 VL - 49 IS - 8 SP - 2293 EP - 2302 PB - Elsevier CY - Oxford AN - OPUS4-29014 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weidner, Steffen A1 - Scheliga, F. A1 - Kricheldorf, H.R. T1 - Low-temperature polymerization of epsilon-caprolactone catalyzed by cerium triflates N2 - Using 22 metal triflates as catalysts, ε-caprolactone is polymerized at 22 °C in bulk. Only five relatively acidic triflates prove active. Three triflates, including the neutral Sm3+, are active using water as initiator. A very low content of cyclics is found in all the experiments. With Ce3+ and Ce4+, polymerizations are performed in CH2Cl2 and in bulk at 2 °C and 22 °C. Low dispersities (down to 1.1) are obtained. At 22 °C, Ce4+ and, even better, Ce3+ also catalyze syntheses of CO2H- and CH2OH-terminated polycaprolactones, whereby higher dispersities and larger fractions of cyclics are obtained. Further polymerizations and polycondensations are catalyzed with protic acids. The results can be explained by a proton-catalyzed activated monomer mechanism. KW - Epsilon-caprolactone KW - Cyclization KW - Metal triflates KW - Polycondensation KW - Ring-opening polymerization PY - 2013 DO - https://doi.org/10.1002/macp.201300279 SN - 1022-1352 SN - 1521-3935 VL - 214 IS - 18 SP - 2043 EP - 2053 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-29219 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Garaleh, M. A1 - Lahcini, M. A1 - Kricheldorf, H.R. A1 - Weidner, Steffen T1 - Syntheses of aliphatic polyesters catalyzed by lanthanide triflates N2 - Polycondensations of 1,6-hexane diol and sebacic acid were conducted in bulk with addition of a lanthanide triflate as acidic catalyst. With exception of promethium triflate all lanthanide triflates were studied. A particularly low molecular weight was obtained with neodym triflate and the best results with samarium triflate. With Sm(OTf)3 weight average (Mw) values up to 65 kDa (uncorrected SEC data) were achieved after optimization of the reaction conditions. Comparison of these results with those obtained from bismuth, magnesium, and zinc triflates, on the one hand, and comparison with the acidities of all catalysts, on the other, indicates that the esterification mechanism involves complexation of monomer by metal ions. Preparation of multiblock copoly(ether ester)s failed due to insufficient incorporation of poly(tetrahydrofuran) diols. KW - Biodegradable polyesters KW - Lanthanide ions KW - Macrocycles KW - MALDI-TOF KW - Polycondensation PY - 2009 DO - https://doi.org/10.1002/pola.23136 SN - 0360-6376 SN - 0887-624X VL - 47 IS - 1 SP - 170 EP - 177 PB - Wiley CY - Hoboken, NJ AN - OPUS4-19626 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Appelhans, Dietmar A1 - Oertel, U. A1 - Mazzeo, R. A1 - Komber, H. A1 - Hoffmann, J. A1 - Weidner, Steffen A1 - Brutschy, B. A1 - Voit, B. A1 - Ottaviani, M.F. T1 - Dense-shell glycodendrimers: UV/Vis and electron paramagnetic resonance study of metal ion complexation N2 - The development of dendritic metal ion carrier systems for use in a biological environment is a challenging task as the carrier system must possess multiple features (e.g. a protective shell for metal decomplexation, targeting functions, metal-intradendrimer complexes, etc.) to substitute for the function of metal proteins in processes such as copper metabolism. Thus, Cu(II) complexation by a series of poly(propyleneimine) glycodendrimers ranging up to the fifth generation that have either a dense maltose or maltotriose shell was investigated by UV/Vis spectroscopy and electron paramagnetic resonance (EPR). As a necessary step towards potential biological application, we elucidated the complexation capacity, location of the Cu(II)-dendrimer complexes and the Cu(II) coordination sphere in the dendritic environment. A generation-dependent Cu(II) complexation was found. Furthermore, analysis of the EPR spectra revealed that internal and external Cu(II) coordination and the symmetry (axial and rhombic) of the generated complexes depend on the oligosaccharide shell, dendrimer generation and the relative concentrations of Cu(II) and the dendrimers. Both axial and rhombic symmetries are generation dependent, but also distort with increasing generation number. External coordination of Cu(II) is supported by sugar groups and water molecules. Finally, a third-generation dendrimer with a maltose shell was used to explore the general complexation behaviour of the dendritic poly(propyleneimine) scaffold towards different metal ions [Cu(II), Ag(I), VO(IV), Ni(II), Eu(III) and UO2(VI)]. KW - Glycodendrimers KW - Metal ion complexation KW - Metal ion-intradendrimer complexes KW - Electron paramagnetic resonance study PY - 2010 DO - https://doi.org/10.1098/rspa.2009.0107 SN - 1364-5021 SN - 0962-8444 SN - 0080-4630 SN - 0950-1207 SN - 1471-2946 VL - 466 SP - 1489 EP - 1513 CY - London, UK AN - OPUS4-21622 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weidner, Steffen A1 - Trimpin, s. T1 - Mass Spectrometry of Synthetic Polymers KW - Polymere KW - Massenspektrometrie KW - MALDI PY - 2010 DO - https://doi.org/10.1021/ac101080n SN - 0003-2700 SN - 1520-6882 VL - 82 IS - 12 SP - 4811 EP - 4829 PB - American Chemical Society CY - Washington, DC AN - OPUS4-21623 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lahcini, M. A1 - Qayouh, H. A1 - Yashiro, T. A1 - Weidner, Steffen A1 - Kricheldorf, H.R. T1 - Bismuth-triflate-catalyzed polymerizations of epsilon-caprolactone N2 - εCL was polymerized using the triflates of lanthanum, samarium, magnesium, aluminum, scandium, and bismuth as catalysts. Bismuth triflate proved to be extraordinarily reactive, and catalyzed polymerizations of εCL even at 20 °C. Adding DTBMP reduced the polymerization rate only slightly. Furthermore, no evidence of a cationic mechanism was found by end‐group analyses. Polymerization at 20 °C either in bulk or in solution only yielded polyesters of low or medium molecular weights. Yet addition of alcohols allowed for a proper control of molecular weight and end‐groups. Additionally, low catalyst concentrations and low temperature resulted in narrow molecular weight distributions and polylactones almost free of cyclic compounds. KW - Bismuth KW - Epsilon-caprolactone KW - Ring-opening polymerization KW - Telechelic polyesters PY - 2011 DO - https://doi.org/10.1002/macp.201000517 SN - 1022-1352 SN - 1521-3935 VL - 212 IS - 6 SP - 583 EP - 591 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-23514 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H.R. A1 - Yashiro, T. A1 - Weidner, Steffen T1 - Isomerization-free polycondensations of maleic anhydride with alpha,omega-alkanediols KW - Polymerisation KW - Polykondensation KW - MALDI Massenspektrometrie PY - 2009 DO - https://doi.org/10.1021/ma9009356 SN - 0024-9297 SN - 1520-5835 VL - 42 IS - 17 SP - 6433 EP - 6439 PB - American Chemical Society CY - Washington, DC AN - OPUS4-20930 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H.R. A1 - Weidner, Steffen A1 - Scheliga, F. T1 - Poly(Epsilon-caprolactone) by combined ring-opening polymerization and azeotropic polycondensation - the role of cyclization and equilibration N2 - Using three different catalysts, water-initiated polymerizations of ε-caprolactone were conducted in bulk with variation of the monomer/water ratio. The resulting CH2OH and CO2H- terminated polylactones were subjected in situ to azeotropic polycondensations. With Bi-triflate and temperatures, the polycondensations were not much successful and involved side reactions. With ZnCl2, and especially SnCl2, considerably higher molar masses were achieved. The substitution of toluene for chlorobenzene for refluxing gave better results. The polycondensations broadened the molar mass distribution of the ROP-based prepolymers, and polydispersities between 1.4–1.8 were obtained. The MALDI–TOF mass spectra revealed that the polycondensations significantly enhanced the fraction of rings due to efficient 'end-biting' reactions. By comparison with copolymerization experiments and Sn methoxide-initiated polymerizations, it was demonstrated that equilibration reactions, such as the formation of rings by 'back-biting,' did not occur. KW - Ring-opening polymerization KW - Epsilon-caprolactone (e-CL) KW - Cyclization KW - MALDI-TOF mass spectrometry KW - Polycondensation KW - Polyesters PY - 2012 DO - https://doi.org/10.1002/pola.26222 SN - 0360-6376 SN - 0887-624X VL - 50 IS - 20 SP - 4206 EP - 4214 PB - Wiley CY - Hoboken, NJ AN - OPUS4-26500 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Soulis, S. A1 - Triantou, D. A1 - Weidner, Steffen A1 - Falkenhagen, Jana A1 - Simitzis, J. T1 - Structural analysis of biodegradable low-molecular mass copolyesters based on glycolic acid, adipic acid and 1,4 butanediol and correlation with their hydrolytic degradation N2 - Copolyesters of glycolic acid combined with adipic acid and 1,4 butanediol were synthesized, their in vitro hydrolytic degradation was studied and correlated with their structure. The hydrolytic degradation of the copolyesters was directly related with the degree of crystallinity and the diameter of the crystallites. It was found that glycolate units disturb the ordering of the butylene adipate units, which results in a decrease of the crystallinity. By comparing the hydrolysis parameters of synthesized copolyesters with those of similar aliphatic copolyesters a hydrolysis mechanism was proposed. According to this mechanism, the degradation takes place not only by the loss of end units, but also through the removal of larger segments. MALDI-TOF MS data showed that the possibility of a copolyester macromolecule forming cyclic structures correlates with the arrangement of ester groups in the macromolecules and the structure of the linear segments. KW - Biodegradable KW - Biopolymers KW - Hydrolytic degradation KW - Ft-IR KW - Matrix-assisted laser desorption/ionization-time-of-flight-mass spectrometry KW - MALDI-TOF-MS PY - 2012 DO - https://doi.org/10.1016/j.polymdegradstab.2012.09.002 SN - 0141-3910 SN - 1873-2321 VL - 97 IS - 11 SP - 2091 EP - 2103 PB - Applied Science Publ. CY - London AN - OPUS4-26723 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Enthaler, S. A1 - Krackl, S. A1 - Epping, J.D. A1 - Eckhardt, B. A1 - Weidner, Steffen A1 - Fischer, A. T1 - Iron-based pre-catalyst supported on polyformamidine for C-C bond formation N2 - In the present study the incorporation of iron into an organic polymer, composed of formamidine subunits [R–N=C(H)–NH–R], has been examined. The catalytic ability of the recyclable material was investigated in the iron-catalyzed formation of C–C bonds. After optimization of the reaction conditions, excellent yields and chemoselectivities were feasible. KW - Polyforamidine KW - Synthesis KW - Catalytic ability PY - 2012 DO - https://doi.org/10.1039/c2py00540a SN - 1759-9954 SN - 1759-9962 VL - 3 IS - 3 SP - 751 EP - 756 AN - OPUS4-25461 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yu, Z. A1 - Weidner, Steffen A1 - Risse, T. A1 - Hecht, S. T1 - The role of statistics and microenvironment for the photoresponse in multi-switch architectures: The case of photoswitchable oligoazobenzene foldamers N2 - Systems containing multiple photochromic units possibly display a synergistic interplay of individual switching events and hence potentially give rise to unprecedented photoresponsive behavior. Among such systems photoswitchable foldamers are attractive as the photoisomerization events are coupled to the helix–coil conformational transition. To gain comprehensive insight into the role of the number of switching units (statistics) as well as their specific location and relative orientation in the helix backbone, several series of foldamers have been synthesized and characterized. In these series of foldamers, the local environment of the photoswitchable units was precisely tuned as π,π-stacking interactions were enforced to occur between specific pairs, i.e. azobenzene–azobenzene, azobenzene–tolane, or phenylene–phenylene units. These particular arrangements are reflected not only in the stability of the helical conformation, but also affect the photoresponsive behavior, i.e. the rate of photoisomerization and extent of denaturation. Furthermore, determining the intramolecular spin–spin distance in a series of TEMPO-labeled foldamers with variable chain lengths and different spatial locations of the spin-labels deduced an independent verification of the photoinduced helix–coil transition by ESR spectroscopy. Quantitative analysis of the corresponding ESR spectra shows an excellent correlation of the extent of intramolecular spin–spin coupling and the intensity of the Cotton effect in CD spectroscopy. From all of these results an unusual relationship between the rate of photoisomerization and the extent of photoinduced denaturation could be unraveled, as they are not going hand-in-hand but compete with each other, i.e. the easier the individual switching event is, the harder it becomes to achieve a high degree of unfolding. This insight into the effect of microenvironment on the ease of individual switching events and the role of statistics on the resulting degree of the overall conformational transition is of general interest for the design of multi-switch architectures with improved photoresponse. KW - Polymers KW - Photoswitchable KW - Oligoazobenzene KW - Foldamers PY - 2013 DO - https://doi.org/10.1039/c3sc51664d SN - 2041-6520 SN - 2041-6539 VL - 4 IS - 11 SP - 4156 EP - 4167 PB - RSC CY - Cambridge AN - OPUS4-29814 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weidner, Steffen A1 - Meyer, A. A1 - Kricheldorf, H. R. T1 - Sn(II)2-ethylhexanoate-catalyzed polymerizations of L-lactide in solution – Solution grown crystals of cyclic Poly(L-Lactide)s N2 - L-lactide (LA) was polymerized in toluene by means of neat tin(II) 2-ethylhexanoate (SnOct2). Concentration, time and temperature were varied. The isothermally crystallized polyLAs (PLA) were characterized in the virgin state with regard to topology, molar mass, melting temperature (Tm), crystal modification, high or low Tm morphology, crystallinity and crystal thickness. Even a small amount of solvent favored cyclization relative to polymerization in bulk, so that cyclic polylactides were obtained at 115 ◦C and even at 95 ◦C. At all temperatures the α-modification of PLA was obtained along with crystallinities up to 90%. With 6 M solution the high Tm morphology with Tm’s > 190 ◦C was obtained at 115 ◦C. The crystal thickness of crystallites grown from solution at 115 ◦C was on the average 10–20% higher than that of PLA polymerized in bulk. At a polymerization temperature of 75 ◦C cyclization was incomplete and fewer perfect crystallites were formed. A new hypothesis for the crystal growth of cyclic polyLAs is proposed. KW - Polylactide KW - MALDI-TOF MS KW - Crystalinity KW - Polymerization PY - 2022 DO - https://doi.org/10.1016/j.polymer.2022.125142 SN - 0032-3861 VL - 255 SP - 1 EP - 9 PB - Elsevier CY - Oxford AN - OPUS4-55283 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Chabbah, T. A1 - Chatti, S. A1 - Zouaoui, F. A1 - Jlalia, A. A1 - Gaiji, H. A1 - Abderrazak, H. A1 - Casablanca, H. A1 - Mercier, R. A1 - Weidner, Steffen A1 - Errachid, A. A1 - Marestin, C. A1 - Jaffrezic-Renault, N. T1 - New poly(ether-phosphoramide)s sulfides based on green resources as sensitive films for the specific impedimetric detection of nickel ions N2 - For the development of selective and sensitive chemical sensors, we have developed a new family of poly(etherphosphoramide) polymers. These polymers were obtained with satisfactory yields by nucleophilic aromatic polycondensation using isosorbide as green resources, and bisphenol A with two novel difluoro phosphinothioic amide monomers. Unprecedented, the thiophosphorylated aminoheterocycles monomers, functionalized with two heterocyclic amine, N-methylpiperazine and morpholine were successfully obtained by nucleophilic substitution reaction of P(S)–Cl compound. The resulting polymers were characterized by different analytical techniques (NMR, MALDI–ToF MS, GPC, DSC, and ATG). The resulting partially green polymers, having tertiary phosphine sulfide with P–N side chain functionalities along the main chain of polymers are the sensitive film at the surface of a gold electrode for the impedimetric detection of Cd, Ni, Pb and Hg. The bio-based poly(etherphosphoramide) functionalized with N-methylpiperazine modified sensor showed better analytical performance than petrochemical based polymers for the detection of Ni2+. A detection limit of 50 pM was obtained which is very low compared to the previously published electrochemical sensors for nickel detection. KW - Poly(ether-phosphoramide)s sulfides KW - Green chemistry KW - Polymer film KW - MALDI TOF MS PY - 2022 DO - https://doi.org/10.1016/j.talanta.2022.123550 VL - 247 IS - 123550 SP - 1 EP - 9 PB - Elsevier B.V. AN - OPUS4-54980 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H. A1 - Weidner, Steffen A1 - Meyer, A. T1 - Ring-expansion polymerization (REP) of L-lactide with cyclic tin catalysts – About formation of extended ring crystals and optimization of Tm and ΔHm N2 - L-Lactide was polymerized in bulk at 140 °C with three different cyclic tin catalysts and the time was varied from 1 d up to 14 d. The MALDI TOF spectra confirmed the formation of cyclic polylactides (PLAs) and displayed a characteristic change of peak intensity distribution with formation of a “saw tooth pattern”. This pattern confirms a previous hypothesis that cyclic PLAs tend to form crystallites with extended ring conformation and relatively smooth surface. This type of crystallites is formed under thermodynamic control by transesterification on the surface of the crystallites. In this way PLAs with extraordinarily high melting temperatures (Tm's up to 200.6 °C) and extraordinarily high melting enthalpy were obtained (ΔHm's up to 105 J g−1). These ΔHm values require a revision of the maximum ΔHm value calculated in the literature for ideal PLA crystals. KW - Polylactide KW - MALDI-TOF MS KW - ring-expansion polymerization PY - 2022 DO - https://doi.org/10.1016/j.polymer.2022.125516 SN - 0032-3861 VL - 263 SP - 125516 PB - Elsevier Ltd. AN - OPUS4-56338 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H. R. A1 - Weidner, Steffen A1 - Meyer, A. T1 - About the Influence of (Non-)Solvents on the Ring Expansion Polymerization of l-Lactide and the Formation of Extended Ring Crystals N2 - Ring-expansion polymerizations (REPs) catalyzed by two cyclic tin catalysts(2-stanna-1.3-dioxa-4,5,6,7-dibenzazepine [SnBiph] and 2,2-dibutyl-2-stanna-1,3-dithiolane [DSTL) are performed at 140 °C in bulk. Small amounts (4 vol%) of chlorobenzene or other solvents are added to facilitate transesterification reactions (ring–ring equilibration) in the solid poly(l-lactide)s. In the mass range up to m/z 13 000 crystalline PLAs displaying a so-called saw-tooth pattern in the MALDI-TOF mass spectra are obtained indicating the formation of extended-ring crystals. The characteristics of extended-ring crystallites and folded-ring crystallites are discussed. Furthermore, extremely high melting temperatures (Tm’s up to 201.2 °C) and melting enthalpies (𝚫Hm’s up to 106 J g−1)) are found confirming that 𝚫Hmmax, the 𝚫Hm of a perfect crystal, is around or above 115 J g−1 in contrast to literature data. KW - Polylactide KW - MALDI-TOF MS KW - Ring-expansion polymerization KW - Crystals PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-565038 DO - https://doi.org/10.1002/macp.202200385 SN - 1022-1352 SP - 1 EP - 8 PB - Wiley VHC-Verlag AN - OPUS4-56503 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H. R. A1 - Weidner, Steffen T1 - Synthesis of polylactides by means of tin catalysts N2 - This article reviews the usefulness of tin(II) and tin(IV) salts and compounds as catalysts for the polymerization of lactides. The text is subdivided into nine parts mainly reflecting different polymerization strategies, such as ring-opening polymerization (ROP), ring-expansion polymerization (REP), ROP combined with simultaneous polycondensation (ROPPOC), various catalysts with unknown polymerization mechanisms, and polycondensation of lactic acid. Since the toxicity of tin salts and compounds is a matter of concern and frequently mentioned in numerous publications, the first section deals with facts instead of myths about the toxicity of tin salts and compounds. KW - Polylactide KW - MALDI-TOF MS KW - Tin catalysts PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-545050 DO - https://doi.org/10.1039/d2py00092j SP - 1 EP - 30 PB - Royal Society for Chemistry AN - OPUS4-54505 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Martins, Ines A1 - Al-Sabbagh, Dominik A1 - Bentrup, U. A1 - Marquardt, Julien A1 - Schmid, Thomas A1 - Scoppola, E. A1 - Kraus, Werner A1 - Stawski, Tomasz A1 - de Oliveira Guilherme Buzanich, Ana A1 - Yusenko, Kirill A1 - Weidner, Steffen A1 - Emmerling, Franziska T1 - Formation Mechanism of a Nano-Ring of Bismuth Cations and Mono-Lacunary Keggin-Type Phosphomolybdate N2 - A new hetero-bimetallic polyoxometalate (POM) nano-ring was synthesized in a one-pot procedure. The structure consists of tetrameric units containing four bismuth-substituted monolacunary Keggin anions including distorted [BiO8] cubes. The nano-ring is formed via self-assembly from metal precursors in aqueous acidic medium. The compound (NH4)16[(BiPMo11O39)4] ⋅ 22 H2O; (P4Bi4Mo44) was characterized by single-crystal X-ray diffraction, extended X-ray absorption fine structure spectroscopy (EXAFS), Raman spectroscopy, matrix-assisted laser desorption/ionisation-time of flight mass spectrometry (MALDI-TOF), and thermogravimetry/differential scanning calorimetry mass spectrometry (TG-DSC-MS). The formation of the nano-ring in solution was studied by time-resolved in situ small- and wide-angle X-ray scattering (SAXS/WAXS) and in situ EXAFS measurements at the Mo−K and the Bi−L3 edge indicating a two-step process consisting of condensation of Mo-anions and formation of Bi−Mo-units followed by a rapid self-assembly to yield the final tetrameric ring structure. KW - Bismuth KW - In situ EXAFS KW - In situ SAXS/WAXS KW - Lacunary Keggin ion KW - Polyoxometalates KW - Self-assembly PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-546823 DO - https://doi.org/10.1002/chem.202200079 SN - 0947-6539 VL - 28 IS - 27 SP - 1 EP - 7 PB - Wiley-VCH CY - Weinheim AN - OPUS4-54682 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H. R. A1 - Weidner, Steffen A1 - Scheliga, F. T1 - Ring-Expansion Polymerization of 𝝐-Caprolactone, Glycolide, and l-lactide with a Spirocyclic Tin(IV) Catalyst Derived from or 2,2′-Dihydroxy-1,1′-Binaphthyl – New Results and a Revision N2 - In contrast to other cyclic tin bisphenoxides, polymerizations of glycolide and l-lactide with the spirocyclic tin(IV) bis-1,1′-bisnapthoxide yield linear chains having a 1,1′-bisnapthol end group and no cycles. In the case of l-lactide, LA/Cat ratio and temperature are varied and at 160 °C or below, all polylactides mainly consist of even-numbered chains. A total predominance of even-numbered chains is also found for homopolymerization of glycolide, or the copolymerization of glycolide and l-lactide, when conducted <120 °C. Linear chains having a bisnaphthol end group are again the main reaction products of ring-expansion polymerizations (REP) of 𝝐-caprolactone, but above 150 °C cycles are also formed. KW - Polylactide KW - MALDI-TOF MS KW - Polymerization PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-541931 DO - https://doi.org/10.1002/macp.202100308 VL - 222 IS - 24 SP - 1 EP - 10 PB - Wiley VCH GmbH AN - OPUS4-54193 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H. R. A1 - Weidner, Steffen A1 - Scheliga, F. T1 - SnOct2-catalyzed and alcohol-initiated ROPS of L-lactide - Control of the molecular weight and the role of cyclization N2 - Ring-opening polymerizations (ROP) of l-lactide (LA) are conducted in bulk at 130, 160, or 180 °C and are initiated with two different alcohols at 160 °C. The lactide/initiator ratio (LA/In) is varied from 50/1 (20/1 at 180 °C) to 900/1 and the lactide/catalyst ratio (LA/Cat) between 2000/1 and 8000/1. At all temperatures a nearly perfect control of number average molecular weight (Mn) via the LA/In ratio is feasible up to LA/In = 200/1, but at higher ratios the Mn value lags behind the theoretical values and the discrepancy increases with higher LA/Cat ratios. Variation of the LA/Cat ratio influences the formation of cycles but does not significantly influence Mn, when the LA/In ratio is kept constant. The formation of cycles is favored by lower In/Cat ratios and is the main reason for the unsatisfactory control of Mn at high LA/In ratios. The results also suggest that the cycles are mainly or exclusively formed by end-to-end cyclization and not, as believed previously, by back-biting. KW - Polylactide KW - MALDI-TOF MS KW - Cyclization KW - Ring-opening polymerization PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-543066 DO - https://doi.org/10.1002/macp.202100464 SN - 1521-3935 SP - 1 EP - 10 PB - Wiley-VCH CY - Weinheim AN - OPUS4-54306 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weidner, Steffen A1 - Kricheldorf, H. R. T1 - SnOct2-catalyzed ROPs of L-lactide initiated by acidic OH- compounds: Switching from ROP to polycondensation and cyclization N2 - Ring-opening polymerizations (ROPs) of L-lactide are performed in bulk at 130°C with tin(II) 2-ethylhexanoate as catalyst and various phenols of differentacidity as initiators. Crystalline polylactides having phenyl ester end groups are isolated, which are almost free of cyclics. The dispersities and molecular weights are higher than those obtained from alcohol-initiated ROPs under identical conditions. Polymerizations at 160°C yield higher molecular weights than expected from the monomer/initiator ratio and a considerable fraction of cycles. The fraction of cycles increases with higher reactivity of the ester end group indicating that the cycles are formed by end-to-end cyclization. KW - Polylactide KW - MALDI-TOF MS KW - Polymerization PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-540250 DO - https://doi.org/10.1002/pol.20210823 SN - 2642-4150 VL - 60 IS - 5 SP - 785 EP - 793 PB - Wiley AN - OPUS4-54025 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Jlalia, I. A1 - Chabbah, T. A1 - Chatti, S. A1 - Schiets, F. A1 - Casabianca, H. A1 - Marestin, C. A1 - Mercier, R. A1 - Weidner, Steffen A1 - Kricheldorf, H. R. A1 - Errachid, A. A1 - Vulliet, E. A1 - Hammani, M. A1 - Jaffrezic-Renault, N. T1 - Alternating bio-based pyridinic copolymers modified with hydrophilic and hydrophobic spacers as sorbents of aromatic pollutants N2 - The main objective of this work was to design new advanced sorbent phases, alternating copolymers, derived from isosorbide and 2,6-difluorpyridine, to be used for the removal of aromatic organic pollutants present in water at low concentrations. Six different monomers, dianhydrohexitols isomers and bisphenol derivatives, weresynthesized in order to make it possible to study their hydrophilic and hydrophobiceffect on the sorption efficiency of the resulting polymeric phases. Before this study, we have confirmed the chemicals structures, molecular weights, and thermal properties of the obtained polymeric phases. Sorption results show a higher adsorption efficiency of P6 co-poly(ether-pyridine) based on bisphenol substituted with pyridineunits, for all tested pollutants, hydrophobic and hydrophilic ones, due to its less compact structure. Two aromatic organic pollutants, p-hydroxybenzoic acid and toluicacid, were selected as sorbates to study the adsorption characteristic, kinetics and isotherms of the copoly(ether pyridine) P6. Langmuir model led to a better fitting of the sorption isotherms; the sorption of toluic acid is easier than of that p-hydroxybenzoic acid. Comparing 1/n values for benzoic acid was two time lower for P6 compared to that for biochar and for crosslinked methacrylate resin, showing a higher efficiency KW - Alternating co-poly(ether pyridine)s KW - Aromatic organic compounds, KW - Biosourced isosorbide KW - Sorption isotherm KW - Sorption mechanism PY - 2021 DO - https://doi.org/10.1002/pat.5578 VL - 33 IS - 4 SP - 1057 EP - 1068 PB - Wiley Online Library AN - OPUS4-54031 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H. R. A1 - Meyer, A. A1 - Weidner, Steffen T1 - High Tm Poly(l-lactide)s by Means of Bismuth Catalysts? N2 - One series of BiSub-catalyzed ring-opening polymerizations (ROPs) is per-formed at 160 °C for 3 days with addition of difunctional cocatalysts to find out, if poly(l-lactide) crystallizes directly from the reaction mixture. An analogous series is performed with monofunctional cocatalysts. High Tm crystal-lites (Tm > 190 °C) are obtained from all bifunctional cocatalysts, but not from all monofunctional ones. It is shown by means of SAXS measurements that the high Tm values are mainly a consequence of a transesterification–homogenization process across the lamellar surfaces resulting in thickness and smoothing of the surfaces. An unusual enthalpy-driven modification of the molecular weight distribution is found for samples that have crystallized during the polymerization. A third series of ROPs is performed at 170 °C for 2 h followed by annealing at 120 °C (2 h) to induce crystallization. Complete transformation of the resulting low Tm crystallites (Tm < 180 °C) into the high Tm crystallites by annealing at 170 °C for 1 d is not achieved, despite variation of the cocatalyst. KW - Polylactide KW - MALDI-TOF MS KW - Crystallization PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-522777 DO - https://doi.org/10.1002/macp.202100019 SN - 1022-1352 VL - 222 IS - 8 SP - 19 PB - Wiley AN - OPUS4-52277 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H. R. A1 - Weidner, Steffen T1 - Polymerization of L-lactide with SnCl2: A Low Toxic and Eco-friendly Catalyst N2 - Polymerizations of L-lactide catalyzed either by neat SnCl2 or by SnCl2 + difunctional cocatalysts were conducted in bulk at 180, 160 and 140 °C with variation of the Lac/Cat ratio and time. With neat SnCl2 poly(L-lactide) having weight average molecular weights (uncorrected Mw’s) up to 190 000 g mol−1 were obtained mainly consisting of linear chains. Addition of salicylic acid or 1,1-bisphenol yielded a higher fraction of cyclic polylactides but lower molecular weights. Furthermore, SnCl2 was compared with Bu2SnCl2 and various other metal chlorides and the best results were obtained with SnCl2. With ethyl L-lactate as initiator SnCl2-catalyzed ROPs were performed at 120 °C and the lac/initiator ratio was varied. All these experiments were conducted under conditions allowing for comparison with ROPs catalyzed with neat Sn(II)-2-ethyhexanoate. Such a comparison was also performed with ε-caprolactone as monomer. KW - Catalyst KW - Polylactide KW - MALDI-TOF MS KW - Polycondensation PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-520517 DO - https://doi.org/10.1007/s10924-020-02042-w SN - 1566-2543 SP - 1 EP - 13 PB - Springer Nature AN - OPUS4-52051 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Meyer, A. A1 - Kricheldorf, H. R. A1 - Weidner, Steffen T1 - ROPs of L-lactide catalyzed by neat Tin(II)2-ethylhexanoate - Influence of the reaction conditions on Tm and ΔHm N2 - L-Lactide was polymerized by means of neat SnOct2 with variation of LA/Cat ratio, temperature and time. The resulting cyclic polylactides crystallized spontaneously at 160 °C or below, but needed nucleation via mechanical stress at 165 or 170 °C. All the crystalline polylactides obtained directly from ROP above 120 °C had melting temperatures (Tm) above 189 °C (up to 194.5 °C). SnOct2 also enabled transformation of low Tm poly(L-lactide)s (Tm <180 °C) into the high Tm m1odification by annealing, due to the impact of transesterification reactions in the interphase between the crystallites. The influence of crystallization temperature and annealing time on the crystal thickness was studied via SAXS measurements. A comparison with the crystallization and annealing experiments reported by Pennings and coworkers and Tsuji and Ikada is discussed, and a satisfactory agreement has been found, because those authors also studied polyLA samples containing SnOct2 in its active form. It is also demonstrated in this work that the high Tm modification cannot be obtained when the catalyst is removed or poisoned as it is true for commercial polylactides. KW - Polylactide KW - MALDI-TOF MS KW - Crystallization PY - 2021 DO - https://doi.org/10.1016/j.polymer.2021.124122 SN - 0032-3861 VL - 231 SP - 1 EP - 10 PB - Elsevier CY - Oxford AN - OPUS4-53194 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Brirmi, M A1 - Chabbah, T. A1 - Chatti, S. A1 - Schiets, F. A1 - Casabianca, H. A1 - Marestin, C. A1 - Mercier, R. A1 - Weidner, Steffen A1 - Errachid, A. A1 - Jaffrezic-Renault, N. A1 - Ben Romdhane, H. T1 - Effect of the pendent groups on biobased polymers, obtained from click chemistry suitable, for the adsorption of organic pollutants from water N2 - In this work, four triazole-based poly(ether-pyridine)s polymers were synthesized and used as an adsorbent for the removal of phenolic compounds from aqueous solutions. For this purpose, new fluoromonomers containing 1,2,3-triazole units were prepared by the Cu(I)-catalyzed 1,3-dipolar cycloaddition reaction and then used for the elaboration of novel poly(ether-pyridine-triazole)s (PEPTs) by direct polyconden-sation with isosorbide and bisphenol A. Chemical structure of fluorinated pyridinicmonomers as well as resulting polymers was confirmed by 1H and 19F NMR spectroscopic methods. The thermal behavior of the obtained PEPTs was characterized using differential scanning calorimetry and thermogravimetric analysis. Results of sorption showed that polymers can be effectively used as a sorbent for the removal of polarorganic pollutants. The isosorbide-based poly(ether-pyridine-triazole) which contains hydrophilic hydroxyl groups as pendants chains (P4) exhibited the highest sorption efficiencies (78%–100% after 1 h). In order to explain the results an adsorption mech-anism mainly based on π–π interactions and hydrogen bonding with the pendent groups is proposed. KW - Adsorption KW - Biobased polymers KW - Cycloaddition KW - Pentafluoropyridine KW - Phenolic compounds PY - 2022 DO - https://doi.org/10.1002/pat.5809 SN - 1042-7147 SP - 1 EP - 21 PB - Wiley online library AN - OPUS4-55389 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mechichi, R. A1 - Chabbah, T. A1 - Chatti, S. A1 - Jlalia, I. A1 - Sanglar, Corinne A1 - Casablanca, H. A1 - Vulliet, E. A1 - Marestin, C. A1 - Mercier, R. A1 - Weidner, Steffen A1 - Errachid, A. A1 - Hammani, M. A1 - Jaffrezic-Renault, N. A1 - Abderrazak, H. T1 - Semi‑interpenetrating Network‑Coated Silica Gel Based on Green Resources for the Efcient Adsorption of Aromatic Pollutants from Waters N2 - In the framework of the development of green analytical chemistry, a silica gel (SG) coated with a semi-penetrating network based on the partially biosourced poly(ethersulfone) is studied for a greener extraction process of aromatic organic pollutants. An optimized composition of the semi-penetrating network (80% of the linear polymer (LP): isosorbide-based poly(ethersulfone) and 20% cross-linking agent (XP) type bismaleimide) leads to a total adsorption of the selected aromatic pollutants, whatever their hydrophilicity. Adsorption characteristic, kinetics and isotherms of the SG-semi-INP LP80/XP20 for p-hydroxybenzoic acid and for toluic acid were studied. Langmuir model led to a better ftting of the adsorption isotherms; the adsorption of toluic acid is easier than that of p-hydroxybenzoic acid. 1/n values of benzoic acid was lower for SGsemi-INP LP80/XP20 compared to biochar and to cross-linked methacrylate resin, showing a higher adsorption efciency. KW - Isosorbide KW - Semi-interpenetrating networks KW - Silica gel modification KW - Aromatic pollutants KW - Adsorption PY - 2022 DO - https://doi.org/10.1007/s42250-022-00463 SN - 2522-5758 SP - 1 EP - 18 PB - Springer AN - OPUS4-55720 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H. R. A1 - Weidner, Steffen A1 - Scheliga, F. T1 - Ring-opening polymerizations of L-Lactide catalyzed by zinc caprylate: Syntheses of cyclic and linear poly(L-lactide)s N2 - Alcohol-initiated ring-opening polymerizations (ROPs) of L-Lactide (LA) were conducted in bulk at 130 °C catalyzed by Zn acetate (ZnAc2), lactate (ZnLac2), or caprylate (ZnCap2). 11-undecenol (UND), 1-hydroxymethylnaphtalene (HMN), and 4-nitrobenzylalcohol (4NB) were used as alcohols. Whereas variation of the alcohols had little effect, the usefulness of the catalysts increased in the order: acetate < lactate < caprylate. Hence, further alcohol-initiated polymerizations were performed with ZnCap2 alone and with variation of the lactide/catalyst (LA/Cat) ratio. With increasing LA/Cat ratio higher fractions of cyclic poly(L-lactide) (PLA) were found, so that the measured degree of polymerization (DP) is considerably lower than the theoretical value (i.e., 2 x LA/alcohol). With neat ZnCap2 cyclic PLAs were the largely prevailing reaction products. For these cyclic PLAs weight average molar masses (Mw) up to 134,000 were obtained and an optical purity around 99% was indicated by 13C NMR spectroscopy and DSC measurements even after 48 h at 150 or 160 °C. KW - Cyclization KW - Lactide KW - Ring opening polymerization KW - Transesterification KW - Zinc catalyst KW - MALDI PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-557565 DO - https://doi.org/10.1002/pol.20220328 SN - 2642-4150 SP - 1 EP - 10 PB - Wiley AN - OPUS4-55756 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H. R. A1 - Weidner, Steffen T1 - Alcohol-Initiated and SnOct2-Catalyzed Ring-Opening Polymerization (ROP) of L-Lactide in Solution: A Re-investigation N2 - Alcohol-initiated ring-opening polymerizations (ROP) of L-lactide (LA) were studied in solution at 70 °C, whereupon the nature of the alcohol, the LA/initiator ratio, the LA/SnOct2 ratio and the time were varied. In contrast to literature, neat SnOct2 is catalytically active in THF and several aromatic but donor solvents, such as 1,3-dioxolane, dimethylformamide (DMF) or N-methyl pyrrolidone (NMP), strongly reduce the activity of SnOct2. In agreement with literature, no cycles were formed by neat SnOct2 at 70 °C in toluene, whereas almost complete cyclization occurs at 115 °C. This finding is attributed to strongly reduced mobility of the initially formed linear chains having one Sn-O-CH and one anhydride end group. Due to better solvation and enhanced mobility cyclization occurs in THF at 70 °C. KW - Polylactide KW - Ring-opening polymerization KW - MALDI-TOF MS KW - Transesterification PY - 2023 DO - https://doi.org/10.1016/j.eurpolymj.2023.111822 SN - 0014-3057 SP - 1 EP - 18 PB - Elsevier CY - New York, NY [u.a.] AN - OPUS4-56818 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H. R. A1 - Weidner, Steffen T1 - Dispersities of Polyesters of Various Diphenols Prepared by Irreversible Polycondensations N2 - Polyesters of bisphenol-A, bisphenol-P, catechol, and sebacic acid are prepared and different synthetic methods are compared. The diphenols are condensed with sebacoyl chloride either in dichloromethane/pyridine or in refl uxing chlorobenzene without HCl-acceptor. Further- more, bisphenol-A acetate is polycondensed with sebacic acid in bulk. All experiments are worked up so that fractionation is avoided. The extent of cyclization is estimated by matrix-assisted laser desorption/ionization mass spectrometry (MALDI MS) and the molar mass distribution by size exclusion chromatography (SEC). Polycondensations in solution yield larger fractions of cyclics and higher dispersities (up to 11). Polycondensations in bulk give lower fractions of cycles and dispersities from 4.6 to 6.3 for high molar mass polyesters or 2.8 to 3.5 for low molar mass products. Characteristic curves describing the dependence of the dispersity on the initial monomer concentration are elaborated. KW - cyclization KW - dispersity KW - mass spectra KW - polycondensation KW - polyesters PY - 2016 DO - https://doi.org/10.1002/macp.201600004 IS - 217 SP - 1361 EP - 1369 PB - Wiley-VCH Verlag CY - Weinheim AN - OPUS4-37120 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H.R. A1 - Mix, Renate A1 - Weidner, Steffen T1 - Poly(ester urethane)s derived from lactide, isosorbide, terephthalic acidm abd various diisocyanates N2 - Isosorbide-initiated oligomerizations of ʟ-lactide were preformed in bulk using SnCl2 as catalyst. The resulting telechelic OH-terminated oligoesters were in situ subjected to simultaneous polycondensation and polyaddition with mixtures of terephthaloyl chloride and diisocyanates. Most polymerizations were conducted with 4,4'-diisocyanatodiphenyl methane and 2,4-diisocyanato toluene. The consequences of excess diisocyanate and four different catalysts were studied. The isosorbide/lactide ratio and the terephthalic acid/diisocyanate ratio were varied. Number average molecular weights up to 15 kDa with polydispersities around 3–5 were obtained. Depending on the chemical structure of the copolyester and on the feed ratio, incorporation of urethane groups may reduce or enhance the glass-transition temperature, but the thermal stability decreases dramatically regardless of composition. KW - Cyclization KW - Isosorbide KW - Lactide KW - Polyaddition KW - Polycondensation KW - Polyesters KW - Polyurethanes PY - 2014 DO - https://doi.org/10.1002/pola.27069 SN - 0360-6376 SN - 0887-624X VL - 52 IS - 6 SP - 867 EP - 875 PB - Wiley CY - Hoboken, NJ AN - OPUS4-30299 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Garaleh, M. A1 - Kricheldorf, H.R. A1 - Weidner, Steffen A1 - Yashiro, T. T1 - Hafnium chloride catalyzed polycondensation of Alpha, Omega-alkanediol with dicarboxylic acids or succinic anhydride KW - Polyester KW - Polycondensation KW - Hafnium KW - Cyclization PY - 2010 DO - https://doi.org/10.1080/10601320903539199 SN - 1060-1325 SN - 1520-5738 VL - 47 IS - 4 SP - 303 EP - 308 PB - Taylor & Francis CY - Philadelphia, PA AN - OPUS4-22953 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lahcini, M. A1 - Weidner, Steffen A1 - Oumayama, J. A1 - Scheliga, F. A1 - Kricheldorf, H. R. T1 - Unsaturated Copolyesters of Lactide N2 - Four classes of unsaturated copolyesters of L-lactide were prepared either from isosorbide or bis(hydroxymethyl)tricyclodecane in combination with fumaric acid or from 1,4-butenediol or 1,4- butynediol with terephthalic acid. All syntheses were performed in such a way that lactide was oligomerized with a diol as the initiator and the resulting oligomers were polycondensed with a dicarboxylic acid dichloride either in a one-pot synthesis or in a two-step procedure. For most copolyesters the SEC measurements gave weight average molecular weights in the range of 30–60 kg mol⁻1 and dispersities in the range of 4.2–6.2. The MALDI-TOF mass spectra displayed a high content of cycles and indicated an irreversible kinetic course of all polycondensations. Glass-transition temperatures (Tg) above 90 °C were only found for two copolyesters of isosorbide. Addition of bromine to copolyesters of 1,4-butenediol yielded flame retarding biodegradable polymers. KW - Copolyester KW - MALDI-TOF MS KW - SEC KW - Lactide PY - 2016 DO - https://doi.org/10.1039/c6ra16008e VL - 2016/6 IS - 96 SP - 93496 EP - 93504 PB - Royal Society of Chemistry AN - OPUS4-37913 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Koshkina, Olga A1 - Lang, Thomas A1 - Thiermann, R. A1 - Docter, D. A1 - Stauber, R.H. A1 - Secker, C. A1 - Schlaad, H. A1 - Weidner, Steffen A1 - Mohr, B. A1 - Maskos, M. A1 - Bertin, Annabelle T1 - Temperature-triggered protein adsorption on polymer-coated nanoparticles in serum N2 - The protein corona, which forms on the nanoparticle's surface in most biological media, determines the nanoparticle’s physicochemical characteristics. The formation of the protein corona has a significant impact on the biodistribution and clearance of nanoparticles in vivo. Therefore, the ability to influence the formation of the protein corona is essential to most biomedical applications, including drug delivery and imaging. In this study, we investigate the protein adsorption on nanoparticles with a hydrodynamic radius of 30 nm and a coating of thermoresponsive poly(2-isopropyl-2-oxazoline) in serum. Using multiangle dynamic light scattering (DLS) we demonstrate that heating of the nanoparticles above their phase separation temperature induces the formation of agglomerates, with a hydrodynamic radius of 1 µm. In serum, noticeably stronger agglomeration occurs at lower temperatures compared to serum-free conditions. Cryogenic transmission electron microscopy (cryo-TEM) revealed a high packing density of agglomerates when serum was not present. In contrast, in the presence of serum, agglomerated nanoparticles were loosely packed, indicating that proteins are intercalated between them. Moreover, an increase in protein content is observed upon heating, confirming that protein adsorption is induced by the alteration of the surface during phase separation. After cooling and switching the surface back, most of the agglomerates were dissolved and the main fraction returned to the original size of approximately 30 nm as shown by asymmetrical flow-field flow fractionation (AF-FFF) and DLS. Furthermore, the amounts of adsorbed proteins are similar before and after heating the nanoparticles to above their phase-separation temperature. Overall, our results demonstrate that the thermoresponsivity of the polymer coating enables turning the corona formation on nanoparticles on and off in situ. As the local heating of body areas can be easily done in vivo, the thermoresponsive coating could potentially be used to induce the agglomeration of nanoparticles and proteins and the accumulation of nanoparticles in a targeted body region. PY - 2015 DO - https://doi.org/10.1021/acs.langmuir.5b00537 SN - 0743-7463 SN - 1520-5827 VL - 31 IS - 32 SP - 8873 EP - 8881 PB - American Chemical Society CY - Washington, DC AN - OPUS4-34163 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wettmarshausen, Sascha A1 - Friedrich, Jörg Florian A1 - Meyer-Plath, Asmus A1 - Kalinka, Gerhard A1 - Hidde, Gundula A1 - Weidner, Steffen T1 - Coating of carbon fibers with adhesion-promoting thin poly(acrylic acid) and poly(hydroxyethylmethacrylate) layers using electrospray ionization N2 - Thin coatings of poly(acrylic acid) (PAA) and poly(hydroxyethylmethacrylate) (PHEMA) were deposited onto carbon fibers by means of the electrospray ionization (ESI) technique in ambient air. These high-molecular weight polymer layers were used as adhesion promoters in carbon fiber–epoxy resin composites. Within the ESI process, the carbon fibers were completely enwrapped with polymer in the upper 10 plies of a carbon fiber roving. As identified with scanning electron microscopy also shadowed fibers in a bundle as well as backsides of fiber rovings were pinhole-free coated with polymers (‘electrophoretic effect'). Under the conditions used, the layers have a granular structure. Residual solvent was absent in the deposit. PAA and PHEMA films did not show any changes in composition and structure in comparison with the original polymers as analyzed by X-ray photo-electron spectroscopy and matrix-assisted laser desorption/ionization time-of-flight mass spectrometry. Single-fiber pullout tests of coated fibers embedded in epoxy resin showed significantly increased interfacial shear strength. It is assumed that chemical bonds between carbon fiber poly(acrylic acid) and epoxy resin contribute significantly to the improved interactions. KW - Adhesion promotion KW - Thin polymer layers KW - Electrospray ionization (ESI) KW - Carbon fiber–epoxy resin laminates KW - Layer topography PY - 2015 DO - https://doi.org/10.1080/01694243.2015.1040980 SN - 0169-4243 SN - 1568-5616 VL - 29 IS - 15 SP - 1628 EP - 1650 PB - VNU Science Press CY - Utrecht AN - OPUS4-34564 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weidner, Steffen A1 - Kricheldorf, H.R. A1 - Scheliga, F. T1 - Cyclization and dispersity of poly(alkylene isophthalate)s N2 - Poly(alkylene isophthalate)s were prepared by different methods, either in solution or in bulk. The SEC measurements were evaluated in such a way that all oligomers were included. In solution (monomer conc. 0.1–0.7 mol/L) large fractions of rings were formed and high dispersities (up to 12) were obtained, which disagree with theoretical predictions. Polycondensations in bulk did neither generate cyclics by 'back-biting' nor by end-to-end cyclization, when the maximum temperature was limited to 210 °C. The dispersities of these perfectly linear polyesters were again higher than the theoretical values. Regardless of the synthetic method monomeric cycles were never observed. Furthermore, SEC measurements performed in tetrahydrofuran and in chloroform and SEC measurements performed in three different institutes were compared. Finally, SEC measurements of five samples were performed with universal calibration and a correction factor of 0.71 ± 0.02 was found for normal calibration with polystyrene. KW - Cyclization KW - Polycondensation KW - Polyesters KW - Size exclusion chromatography KW - Cyclics KW - Dispersity KW - SEC KW - Universal calibration KW - MALDI mass spectrometry PY - 2016 DO - https://doi.org/10.1002/pola.27892 SN - 0360-6376 SN - 0887-624X VL - 54 IS - 1 SP - 197 EP - 208 PB - Wiley CY - Hoboken, NJ AN - OPUS4-33731 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zydziak, N. A1 - Konrad, W. A1 - Feist, F. A1 - Afonin, S. A1 - Weidner, Steffen A1 - Barner-Kowollik, C. T1 - Coding and decoding libraries of sequence-defined functional copolymers synthesized via photoligation N2 - Designing artificial macromolecules with absolute sequence order represents a considerable challenge. Here we report an advanced light-induced avenue to monodisperse sequencedefined functional linear macromolecules up to decamers via a unique photochemical approach. The versatility of the synthetic strategy—combining sequential and modular concepts—enables the synthesis of perfect macromolecules varying in chemical constitution and topology. Specific functions are placed at arbitrary positions along the chain via the successive addition of monomer units and blocks, leading to a library of functional homopolymers, alternating copolymers and block copolymers. The in-depth characterization of each sequence-defined chain confirms the precision nature of the macromolecules. Decoding of the functional information contained in the molecular structure is achieved via tandem mass spectrometry without recourse to their synthetic history, showing that the sequence information can be read.We submit that the presented photochemical strategy is a viable and advanced concept for coding individual monomer units along a macromolecular chain. KW - Photoligation KW - Copolymer sequence KW - MALDI-TOF MS/MS PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-391542 DO - https://doi.org/10.1038/ncomms13672 SN - 2041-1723 VL - 7 SP - Artikel Nr. 13672 AN - OPUS4-39154 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, Hans R. A1 - Weidner, Steffen T1 - Ring-expansion polymerization of meso-lactide catalyzed by dibutyltin derivatives N2 - Meso-Lactide was polymerized in bulk at 60, 80, and 100 °C by means of three different types of catalysts: dibutyltinsulfides (2,2-dibutyl-2-stanna-1,3-dithiolane and 2,20-dibutyl-2-stanna-1,3-dithiane), dibutyltin derivatives of substituted cate-chols (BuCa, CyCa, and BzCa), and dibutyltin derivatives of2,2 dihydroxybiphenyl (SnBi) and 2,2-dihydroxy-1,10-binaphthyl(SnNa. Only the latter two catalysts were active at 60 °C. The architecture of the resulting polylactides depends very much on the structure of the catalyst and on the temperature. At the lowest temperature (60 °C), SnBi and SnNa mainly yielded even-numbered linear chains, but SnNa also yielded even-numbered cycles at 100 °C and short reaction times. In contrast,BuCa, CyCa, and BzCa mainly yielded odd-numbered cycles, although the same catalysts yielded even-numbered linear chains when benzylalcohol was added. KW - MALDI-TOF MS KW - Cyclisation KW - Catalysts KW - Polyester KW - Polymerization PY - 2018 DO - https://doi.org/10.1002/pola.28948 SN - 1099-0518 SN - 0022-3832 VL - 56 IS - 7 SP - 749 EP - 759 PB - Wiley Periodicals Inc. AN - OPUS4-44278 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, Hans A1 - Weidner, Steffen T1 - High molar mass cyclic poly(L-lactide) via ring-expansion polymerizationwith cyclic dibutyltin bisphenoxides N2 - Two new catalysts (SnNa and SnBi) were prepared from dibutyltin oxide and 2,2′-dihydroxybiphenyl or2,2′dihydroxy(1,1′-binaphtyl). These catalysts enabled rapid polymerizations of L-lactide at 160 or 180 °C in bulk, whereby almost exclusively cyclic polylactides were formed. These polymerizations were free of racemization and yielded pol(L-lactide)s having weight average molecular weights (Mw's) up to 140 000 g mol−1. The Mw's varied little with the Lac/Cat ratio as expected for a ring expansion polymerization (REP). Polymerizations performed in bulk at 140, 120 and 102 °C yielded cyclic polylactides with lower molecular weights. At 102 °C a strong predominance of even-numbered cycles was found with SnNa as catalyst. SnNa can also catalyze alcohol-initiated ROPs yielding linear poly(L-lactide) free of cyclics. KW - MALDI-TOF MS KW - Polylactide KW - Ring-opening Polymerization KW - Cyclization KW - Catalysts PY - 2018 DO - https://doi.org/10.1016/j.eurpolymj.2018.05.036 SN - 0014-3057 SN - 1873-1945 VL - 105 SP - 158 EP - 166 PB - Elsevier Ltd. AN - OPUS4-45439 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Trimpin, S. A1 - Lee, C. A1 - Weidner, Steffen A1 - El-Baba, T. A1 - Lutomski, C. A1 - Inutan, E. A1 - Foley, C. A1 - Ni, C.-K. A1 - McEwen, C. T1 - Unprecedented Ionization Processes in Mass SpectrometryProvide Missing Link between ESI and MALDI N2 - In the field of mass spectrometry,producing intact, highly-charged protein ions from surfaces is a conundrum with significant potential payoff in application areas ranging from bio-medical to clinical research. Here, we report on the ability to form intact, highly-charged protein ions on high vacuum time-of-flight mass spectrometers in the linear and reflectron modes achievable using experimental conditions that allow effective matrix removal from both the sample surfaces and from the charged clusters formed by the laser Ablation event. The charge states are the highest reported on high vacuum mass spectrometers, yet they remain at only around athird of the highest charge obtained using laser ablation with a suitable matrix at atmospheric pressure. Other than physical instrument modifications, the key to forming abundant and stable highly-charged ions appears to be the volatility of the matrix used. Cumulative results suggest mechanistic links between the ionization process reported here and traditional ionization methods of electrospray ionization and matrix-assisted laser desorp-tion/ionization. KW - MALDI KW - Electrospray KW - Mass spectrometry KW - Ionization PY - 2018 DO - https://doi.org/10.1002/cphc.201701246 SN - 1439-4235 SN - 1439-7641 VL - 19 IS - 5 SP - 581 EP - 589 PB - Wiley-VCH AN - OPUS4-44404 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lauer, Franziska A1 - Diehn, Sabrina A1 - Seifert, Stephan A1 - Kneipp, Janina A1 - Sauerland, V. A1 - Barahona, C. A1 - Weidner, Steffen T1 - Multivariate analysis of MALDI imaging mass spectrometry data of mixtures of single pollen grains N2 - Mixtures of pollen grains of three different species (Corylus avellana, Alnus cordata, and Pinus sylvestris) were investigated by matrixassisted laser desorption/ionization time-of-flight imaging mass spectrometry (MALDI-TOF imaging MS). The amount of pollen grains was reduced stepwise from > 10 to single pollen grains. For sample pretreatment, we modified a previously applied approach, where any additional extraction steps were omitted. Our results show that characteristic pollen MALDI mass spectra can be obtained from a single pollen grain, which is the prerequisite for a reliable pollen classification in practical applications. MALDI imaging of laterally resolved pollen grains provides additional information by reducing the complexity of the MS spectra of mixtures, where frequently peak discrimination is observed. Combined with multivariate statistical analyses, such as principal component analysis (PCA), our approach offers the chance for a fast and reliable identification of individual pollen grains by mass spectrometry. KW - MALDI Imaging MS KW - Pollen grains KW - Multivariate Statistics KW - Hierarchical cluster analysis KW - Principal component analysis PY - 2018 DO - https://doi.org/10.1007/s13361-018-2036-5 SN - 1044-0305 SN - 1879-1123 VL - 29 IS - 11 SP - 2237 EP - 2247 PB - Springer AN - OPUS4-45607 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Theiler, Geraldine A1 - Wachtendorf, Volker A1 - Elert, Anna Maria A1 - Weidner, Steffen T1 - Effects of UV radiation on the friction behavior of thermoplastic polyurethanes N2 - The effects of weathering exposure on unfilled and filled thermoplastic polyurethanes (TPU) materials are described as performed under different humidity conditions. For this purpose, a weathering device was used with UV-A 340 nm lamps at a constant temperature of 40 °C. The effects of environmental (UV and humidity condition) degradation on the frictional properties of TPU materials are presented along with surface analyses to characterize the chemistry of the degradative process. Photooxidative degradation of unfilled polymer leads to deterioration of physical and mechanical properties, which affects its tribological behavior significantly. Due to crosslinking, the stiffness of the material increases, reducing drastically the friction coefficient of unfilled TPUs. The frictional behavior of glass fiber reinforced TPU is less affected by radiation. KW - Photooxidation KW - UV radiation KW - Friction KW - TPU KW - Humidity PY - 2018 DO - https://doi.org/10.1016/j.polymertesting.2018.08.006 SN - 0142-9418 SN - 1873-2348 VL - 70 SP - 467 EP - 473 PB - Elsevier Ltd. CY - Amsterdam AN - OPUS4-45709 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H. R. A1 - Weidner, Steffen T1 - High molar mass cyclic poly(L-lactide)s by means of neat tin (II) 2-ethylhexanoate N2 - L-lactide was polymerized in bulk at 120, 140, 160 and 180°C with neat tin(II) 2-ethylhexanoate (SnOct2) as catalyst. At 180°C the Lac/Cat ratio was varied from 25/1 up to 8 000/1 and at 160°C from 25/1 up to 6 000/1. The vast majority of the resulting polylactides consist of cycles in combination with a small fraction of linear chains having one octanoate and one COOH end group. The linear chains almost vanished at high Lac/Cat ratios, as evidenced by MALDI-TOF mass spectrometry and measurements of intrinsic viscosities and dn/dc values. At Lac/Cat ratios <1000/1 the number average molar masses (Mn) are far higher than expected for stoichiometic initiation, and above 400/1 the molar masses vary relatively little with the Lac/Cat ratio. At 180° slight discoloration even at short times and degradation of the molar masses were observed, but at 160°C or below colorless products with weight average molar masses (Mw) up to 310 000 g mol-1 were obtained. The formation of high molar mass cyclic polylactides is explained by a ROPPOC (Ring-Opening Polymerizatiom with simultaneous Polycondensation) mechanism with intermediate formation of linear chains having one Sn-O-CH end group and one mixed anhydride end group. Additional experiments with tin(II)acetate as catalyst confirm this interpretation. These findings together with the detection of several transesterification mechanisms confirm previous critique of the Jacobson-Stockmayer theory. KW - Polylactide KW - MALDI-TOF MS KW - Cyclization PY - 2020 DO - https://doi.org/10.1039/d0py00811g VL - 11 IS - 32 SP - 5249 EP - 5260 PB - Royal Society for Chemistry AN - OPUS4-51130 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H. R. A1 - Weidner, Steffen T1 - The Ring-Opening Polymerisation-Polycondensation (ROPPOC) Approach to cyclic Polymers N2 - A new concept called “Ring-Opening Polymerization (ROP) combined with simultaneous POlyCondensation” (ROPPOC) is presented and discussed. This synthetic strategy is based on the intermediate formation of chains having two end groups that can react with each other. The ROPPOC syntheses are subdivided into three groups according to the nature of the chain ends: two ionic end groups, one ionic and one covalent chain end and a combination of two reactive covalent end groups may be involved, depending on the catalyst. The usefulness for the preparation of cyclic polymers is discussed with a review of numerous previously published examples. These examples concern to following classes of cyclic polymers: polypeptides, polyamides, polyesters, including polycarbonates, and cyclic polysiloxanes. It is demonstrated, that the results of certain ROPPOC syntheses are in contradiction to the Jacobson-Stockmayer theory. Finally, the usefulness of ROPPOCs for the detection of polydisperse catenanes is discussed. KW - Ring-opening Polymerisation KW - MALDI-TOF MS KW - ROPPOC KW - Cyclic PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-508509 DO - https://doi.org/10.1002/marc.202000152 SP - 2000152 PB - Wiley AN - OPUS4-50850 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Steinkönig, J. A1 - Bloesser, F. R. A1 - Huber, B. A1 - Welle, A. A1 - Trouillet, V. A1 - Weidner, Steffen A1 - Barner, L. A1 - Roesky, P. W. A1 - Yuan, J. A1 - Goldmann, A. S. A1 - Barner-Kowollik, C. T1 - Controlled radical polymerization and in-depth mass-spectrometric characterization of poly(ionic liquid)s and their photopatterning on surfaces N2 - The preparation and characterization of poly(ionic liquid)s (PILs) bearing a polystyrene backbone via reversible addition fragmentation chain transfer (RAFT) polymerization and their photolithographic patterning on silicon wafers is reported. The controlled radical polymerization of the styrenic ionic liquid (IL) monomers ([BVBIM]X, X = Cl− or Tf2N−) by RAFT polymerization is investigated in detail. We provide a general synthetic tool to access this class of PILs with controlled molecular weight and relatively narrow molecular weight distribution (2000 g mol−1 ≤ Mn ≤ 10 000 g mol−1 with dispersities between 1.4 and 1.3 for p([BVBIM]Cl); 2100 g mol−1 ≤ MP ≤ 14 000 g mol−1 for p([BVBIM]Tf2N)). More importantly, we provide an in-depth characterization of the PILs and demonstrate a detailed mass spectrometric analysis via matrix-assisted laser desorption ionization (MALDI) as well as – for the first time for PILs – electrospray ionization mass spectrometry (ESI-MS). Importantly, p([BVBIM]Cl) and p([DMVBIM]Tf2N) were photochemically patterned on silicon wafers. Therefore, a RAFT agent carrying a photoactive group based on ortho-quinodimethane chemistry – more precisely photoenol chemistry – was photochemically linked for subsequent controlled radical polymerization of [BVBIM]Cl and [DMVBIM]Tf2N. The successful spatially-resolved photografting is evidenced by surface-sensitive characterization methods such as X-ray photoelectron spectroscopy (XPS) and time-of-flight secondary ion mass spectrometry (ToF-SIMS). The presented method allows for the functionalization of diverse surfaces with poly(ionic liquid)s. KW - reversible addition fragmentation chain transfer (RAFT) polymerization KW - polyionic liquids KW - mass spectrometry KW - surface modification PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-355202 DO - https://doi.org/10.1039/C5PY01320H VL - 7 SP - 451 EP - 461 PB - Royal Society of Chemistry CY - Cambridge AN - OPUS4-35520 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H.R. A1 - Weidner, Steffen A1 - Lahcini, M. T1 - Multicyclic polyesters of trimesic acid and alkanediols and the theory of network formation N2 - Trimesoyl chloride is polycondensed with various alpha,omega'-alkanediols in dichloromethane at different concentrations using equifunctional feed ratios. As evidenced by MALDI-TOF (matrix assisted laser desorption/ionization-time of flight) mass spectrometry the soluble reaction products mainly consist of perfect multicyclic oligomers and polymers. The solphase extracted from the gels also consists of perfect multicycles. SEC (size exclusion chromatography) measurements show that both soluble reaction products and extracted solphases also contain a high molar mass fraction of perfect and nonperfect multicycles extending up to masses beyond 10 5 g mol-1. When the polycondensation is stopped after a few minutes perfect multicycles are already detectable in the reaction mixture along with functional (multi)cyclic oligomers. These results prove that at initial monomer concentrations < 0.2 mol L-1 networks and large multicyclic polymers are synthesized from functional cyclic oligomers formed in early stages of the polycondensation and not from hyperbranched polymers. This interpretation is presented as 'egg-first theory' and compared with the 'hen-first theory' of Stockmayer and Flory. KW - a2 + b3 polycondensation KW - Cyclization KW - MALDI KW - Multicyclic polymers KW - Networks PY - 2015 DO - https://doi.org/10.1002/macp.201500245 SN - 1022-1352 SN - 1521-3935 VL - 216 IS - 21 SP - 2095 EP - 2106 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-35282 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Doriti, A. A1 - Brosnan, S. A1 - Weidner, Steffen A1 - Schlaad, H. T1 - Synthesis of polysarcosine from air and moisture stable N-phenoxycarbonyl-N-methylglycine assisted by tertiary amine base N2 - Polysarcosine (M-n = 3650-20 000 g mol(-1), D similar to 1.1) was synthesized from the air and moisture stable N-phenoxycarbonyl-N-methylglycine. Polymerization was achieved by in situ transformation of the urethane precursor into the corresponding N-methylglycine-N-carboxyanhydride, when in the presence of a non-nucleophilic tertiary amine base and a primary amine initiator. KW - Polysarcosine KW - MALDI-TOF MS KW - Synthesis PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-359309 DO - https://doi.org/10.1039/c6py00221h SN - 1759-9954 SN - 1759-9962 VL - 7 IS - 18 SP - 3067 EP - 3070 AN - OPUS4-35930 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -