TY - JOUR A1 - Chatti, S. A1 - Weidner, Steffen A1 - Fildier, A. A1 - Kricheldorf, H.R. T1 - Copolyesters of isosorbide, succinic acid, and isophthalic acid: biodegradable, high Tg engineering plastics N2 - Isosorbide, succinyl chloride and isophthaloyl chloride are polycondensed under various reaction conditions. The heating in bulk with or without catalysts as well in an aromatic solvent without catalyst, and polycondensation with the addition of pyridine only yield low molar mass copolyesters. However, heating in chlorobenzene with addition of SnCl2 or ZnCl2 produces satisfactory molar masses. The number average molecular weights (Mn) of most copolyesters fall into the range of 7000–15,000 Da with polydispersities (PD) in the range of 3–9. The MALDI-TOF mass spectra almost exclusively displayed peaks of cyclics indicating that the chain growth was mainly limited by cyclization and not by side reactions, stoichiometric imbalance or incomplete conversion. The glass-transition temperatures increased with the content of isophthalic acid from 75 to 180 °C and the thermo-stabilities also followed this trend. KW - Biodegradable KW - Cyclization KW - Cyclopolymerization KW - Isophthalic acid KW - Isosorbide KW - Polycondensation KW - Polyesters KW - Renewable resources KW - Succinic acid PY - 2013 U6 - https://doi.org/10.1002/pola.26635 SN - 0360-6376 SN - 0887-624X VL - 51 IS - 11 SP - 2464 EP - 2471 PB - Wiley CY - Hoboken, NJ AN - OPUS4-28577 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H.R. A1 - Weidner, Steffen A1 - Scheliga, F. T1 - Poly(Epsilon-caprolactone) by combined ring-opening polymerization and azeotropic polycondensation - the role of cyclization and equilibration N2 - Using three different catalysts, water-initiated polymerizations of ε-caprolactone were conducted in bulk with variation of the monomer/water ratio. The resulting CH2OH and CO2H- terminated polylactones were subjected in situ to azeotropic polycondensations. With Bi-triflate and temperatures, the polycondensations were not much successful and involved side reactions. With ZnCl2, and especially SnCl2, considerably higher molar masses were achieved. The substitution of toluene for chlorobenzene for refluxing gave better results. The polycondensations broadened the molar mass distribution of the ROP-based prepolymers, and polydispersities between 1.4–1.8 were obtained. The MALDI–TOF mass spectra revealed that the polycondensations significantly enhanced the fraction of rings due to efficient 'end-biting' reactions. By comparison with copolymerization experiments and Sn methoxide-initiated polymerizations, it was demonstrated that equilibration reactions, such as the formation of rings by 'back-biting,' did not occur. KW - Ring-opening polymerization KW - Epsilon-caprolactone (e-CL) KW - Cyclization KW - MALDI-TOF mass spectrometry KW - Polycondensation KW - Polyesters PY - 2012 U6 - https://doi.org/10.1002/pola.26222 SN - 0360-6376 SN - 0887-624X VL - 50 IS - 20 SP - 4206 EP - 4214 PB - Wiley CY - Hoboken, NJ AN - OPUS4-26500 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H.R. A1 - Mix, Renate A1 - Weidner, Steffen T1 - Poly(ester urethane)s derived from lactide, isosorbide, terephthalic acidm abd various diisocyanates N2 - Isosorbide-initiated oligomerizations of ʟ-lactide were preformed in bulk using SnCl2 as catalyst. The resulting telechelic OH-terminated oligoesters were in situ subjected to simultaneous polycondensation and polyaddition with mixtures of terephthaloyl chloride and diisocyanates. Most polymerizations were conducted with 4,4'-diisocyanatodiphenyl methane and 2,4-diisocyanato toluene. The consequences of excess diisocyanate and four different catalysts were studied. The isosorbide/lactide ratio and the terephthalic acid/diisocyanate ratio were varied. Number average molecular weights up to 15 kDa with polydispersities around 3–5 were obtained. Depending on the chemical structure of the copolyester and on the feed ratio, incorporation of urethane groups may reduce or enhance the glass-transition temperature, but the thermal stability decreases dramatically regardless of composition. KW - Cyclization KW - Isosorbide KW - Lactide KW - Polyaddition KW - Polycondensation KW - Polyesters KW - Polyurethanes PY - 2014 U6 - https://doi.org/10.1002/pola.27069 SN - 0360-6376 SN - 0887-624X VL - 52 IS - 6 SP - 867 EP - 875 PB - Wiley CY - Hoboken, NJ AN - OPUS4-30299 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weidner, Steffen A1 - Kricheldorf, H.R. A1 - Scheliga, F. T1 - Cyclization and dispersity of poly(alkylene isophthalate)s N2 - Poly(alkylene isophthalate)s were prepared by different methods, either in solution or in bulk. The SEC measurements were evaluated in such a way that all oligomers were included. In solution (monomer conc. 0.1–0.7 mol/L) large fractions of rings were formed and high dispersities (up to 12) were obtained, which disagree with theoretical predictions. Polycondensations in bulk did neither generate cyclics by 'back-biting' nor by end-to-end cyclization, when the maximum temperature was limited to 210 °C. The dispersities of these perfectly linear polyesters were again higher than the theoretical values. Regardless of the synthetic method monomeric cycles were never observed. Furthermore, SEC measurements performed in tetrahydrofuran and in chloroform and SEC measurements performed in three different institutes were compared. Finally, SEC measurements of five samples were performed with universal calibration and a correction factor of 0.71 ± 0.02 was found for normal calibration with polystyrene. KW - Cyclization KW - Polycondensation KW - Polyesters KW - Size exclusion chromatography KW - Cyclics KW - Dispersity KW - SEC KW - Universal calibration KW - MALDI mass spectrometry PY - 2016 U6 - https://doi.org/10.1002/pola.27892 SN - 0360-6376 SN - 0887-624X VL - 54 IS - 1 SP - 197 EP - 208 PB - Wiley CY - Hoboken, NJ AN - OPUS4-33731 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -