TY - JOUR A1 - Kricheldorf, Hans A1 - Weidner, Steffen T1 - About the influence of salicylic acid on tin(II)octanoate-catalyzed ring opening polymerizationof L-lactide N2 - L-Lactide was polymerized in bulk with tin(II)2-ethylhexanoate SnOct2) as catalyst and salicylic acid as cocatalyst. The Lac/Cat ratio, Cocat/Cat ratio, temperature and time were varied. Increasing Cocat/Cat ratios reduced both,polymerization rate and molecular weight. However,under optimized conditions high molar mass (Mw up to 178,000), colorless, cyclic polylactides were formed in a short time. A few polymerizations performed at 160 and 180°C with the combination of SnOct2 and silylated salicylic acid gave similar results. Neat tin II) salicylate was prepared from SnOct2 and used for REPs of L-lactide in bulk, but the results were not better than those obtained from combinations of SnOct2 and salicylic acid. Furthermore, dibutyltin salicylate was synthesized and used as catalyst for polymerizations of L-lactide in bulk at temperatures varying from 102 to 160°C. Cyclic polylactides with Mw’s up to 40,000 were the main reaction products. At 100–102°C a predominance of odd-numbered cycles was found proving a REP mechanism. KW - Polylactide KW - MALDI-TOF MS KW - Cyclization KW - Catalyst KW - Ring-opening polymerization PY - 2019 DO - https://doi.org/10.1016/j.eurpolymj.2019.07.003 VL - 119 SP - 37 EP - 44 PB - Elsevier Ltd. AN - OPUS4-49211 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weidner, Steffen A1 - Kühn, Gerhard A1 - Werthmann, Barbara A1 - Schröder, Hartmut A1 - Just, Ulrich A1 - Borowski, Renate A1 - Decker, Renate A1 - Schwarz, Bärbel A1 - Schmücking, I. A1 - Seifert, Ingetraut T1 - A new approach of characterizing the hydrolytic degradation of poly(ethylene terephthalate) by MALDI-MS N2 - The hydrolytic degradation of technical poly(ethylene terephthalate) (PET) was investigated by means of different methods such as size-exclusion chromatography (SEC), viscometry, light-scattering, thin-layer chromatography, end-group titration, and matrix-assisted laser desorption/ionization mass spectrometry (MALDI-MS). The long-term degradation was simulated by exposing PET filament yarns to aqueous neutral conditions at 90°C for up to 18 weeks. By means of MALDI-MS and thin-layer chromatography, the formation of different oligomers was obtained during polymer degradation. As expected, an ester scission process was found generating acid terminated oligomers (H-[GT]m-OH) and T-[GT]m-OH and ethylene glycol terminated oligomers (H-[GT]m-G), where G is an ethylene glycol unit and T is a terephthalic acid unit. Additionally, the scission of the ester bonds during the chemical treatment led to a strong decrease in the number of cyclic oligomers ([GT]m). The occurrence of di-acid terminated species demonstrated a high degree of degradation. PY - 1997 DO - https://doi.org/10.1002/(SICI)1099-0518(199708)35:11<2183::AID-POLA9>3.0.CO;2-Z SN - 0360-6376 SN - 0887-624X VL - 35 IS - 11 SP - 2183 EP - 2192 PB - Wiley CY - Hoboken, NJ AN - OPUS4-11357 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Just, Ulrich A1 - Weidner, Steffen A1 - Kilz, P. A1 - Hofe, T. T1 - Polymer Reference Materials: Round-Robin Tests for the Determination of Molar Masses N2 - This article reports round-robin tests dealing with static light scattering (LS), size exclusion chromatography (SEC), and viscometry measurements of 10 reference materials of various polymer classes: poly(styrene)s (PS), poly(methyl methacrylate)s (PMMA), poly(ethylene oxide)s (PEO), and poly(lactide)s (PLA). In the certificates, molar masses and intrinsic viscosities as well as their uncertainties are specified. Additional values from nuclear magnetic resonance (NMR), infrared spectroscopy (IR), differential scanning calorimetry (DSC), melt flow index (MFR), and matrix-assisted laser desorption/ionization time-of-flight mass spectrometry (MALDI-TOF-MS), which were determined exclusively in BAM laboratories are given, as well. These results represent the base for the BAM certification work of creating polymer reference materials according to the BAM Guidelines for the Production and Certification of BAM Reference Materials, a version of the European guidelines (BCR/01/97). These samples are available for third-party user. KW - Polymer reference materials KW - CRM KW - Molar mass determination KW - Intrinsic viscosity KW - Light scattering (LS) KW - Size exclusion chromatography (SEC) PY - 2005 DO - https://doi.org/10.1080/10236660500418039 SN - 1023-666X SN - 1563-5341 VL - 10 IS - 3-4 SP - 225 EP - 243 PB - Gordon and Breach Publ. CY - Amsterdam AN - OPUS4-11815 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kühn, Gerhard A1 - Weidner, Steffen A1 - Just, Ulrich A1 - Hohner, G. T1 - Characterization of technical waxes - Comparison of chromatographic techniques and matrix-assisted laser-desorption/ionization mass spectrometry N2 - Technical waxes and paraffins were investigated using supercritical fluid chromatography (SFC), matrix-assisted laser-desorption/ionization mass spectrometry (MALDI-MS) and size-exclusion chromatography (SEC). SEC enables the simultaneous determination of molecular masses up to high values and molecular mass distributions. The resolution of homologous species, however, is poor. In this respect the use of SFC is advantageous. Proper resolution of homologues may be provided up to Mr~1200 without great difficulty. To compare these chromatographic results MALDI-MS was applied for the determination of molecular masses and mass distributions in technical waxes for the first time. Using reflectron mode excellent MALDI mass spectra could be achieved in the molecular mass range up to 1000 Da. The mean values of the molecular masses calculated by MALDI-MS were in sufficient agreement with those of SFC. In the linear mode of MALDI-MS molecular masses could be determined to nearly 3000 Da. Beyond this mass range SEC still remains the method of choice. Advantages and difficulties of the used methods are discussed in this paper. PY - 1996 DO - https://doi.org/10.1016/0021-9673(95)01255-9 SN - 0021-9673 VL - 732 IS - 1 SP - 111 EP - 117 PB - Elsevier CY - Amsterdam AN - OPUS4-11347 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, Hans A1 - Weidner, Steffen A1 - Scheliga, Felix T1 - Ring-Expansion Polymerization (REP) of L-lactide with cyclic Tin(II) Bisphenoxides N2 - Five new cyclic catalysts were prepared by a new synthetic method from tin(II)-2-ethyhexanoate and silylated catechols, silylated 2,2´dihydroxybiphenyl or silylated 1,1´-bisnaphthol. These catalysts were compared with regard to their usefulness as catalysts for the ring expansion polymerization (REP) of L-lactide in bulk at 160 °C, and with two different tin(IV) derivatives of 1,1´binaphthol. Best results were obtained using seven-membered cyclic tin(II)bisphenoxides, which yielded colorless cyclic poly(l-lactide)s free of racemization with weight average molecular weights (Mw) up to 305 000 g mol-1. Furthermore, these catalysts were active even at a lactide/catalyst ratio of 20 000/1. Our new results were superior to those obtained from all other previously published catalysts yielding cyclic poly(L-lactide). The seven-membered cycles also proved to be more active than tin(II) 2-ethylhexanoate with and without the addition of alcohol. KW - Lactide KW - Cyclization KW - Ring-expansion polymerization KW - Tin(II)octanoate KW - MALDI-TOF MS PY - 2019 DO - https://doi.org/10.1016/j.eurpolymj.2019.04.024 SN - 0014-3057 SN - 1873-1945 VL - 116 SP - 256 EP - 264 PB - Elsevier Ltd. AN - OPUS4-47794 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lahcini, M. A1 - Weidner, Steffen A1 - Oumayama, J. A1 - Scheliga, F. A1 - Kricheldorf, H. R. T1 - Unsaturated Copolyesters of Lactide N2 - Four classes of unsaturated copolyesters of L-lactide were prepared either from isosorbide or bis(hydroxymethyl)tricyclodecane in combination with fumaric acid or from 1,4-butenediol or 1,4- butynediol with terephthalic acid. All syntheses were performed in such a way that lactide was oligomerized with a diol as the initiator and the resulting oligomers were polycondensed with a dicarboxylic acid dichloride either in a one-pot synthesis or in a two-step procedure. For most copolyesters the SEC measurements gave weight average molecular weights in the range of 30–60 kg mol⁻1 and dispersities in the range of 4.2–6.2. The MALDI-TOF mass spectra displayed a high content of cycles and indicated an irreversible kinetic course of all polycondensations. Glass-transition temperatures (Tg) above 90 °C were only found for two copolyesters of isosorbide. Addition of bromine to copolyesters of 1,4-butenediol yielded flame retarding biodegradable polymers. KW - Copolyester KW - MALDI-TOF MS KW - SEC KW - Lactide PY - 2016 DO - https://doi.org/10.1039/c6ra16008e VL - 2016/6 IS - 96 SP - 93496 EP - 93504 PB - Royal Society of Chemistry AN - OPUS4-37913 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Enthaler, S. A1 - Krackl, S. A1 - Epping, J.D. A1 - Eckhardt, B. A1 - Weidner, Steffen A1 - Fischer, A. T1 - Iron-based pre-catalyst supported on polyformamidine for C-C bond formation N2 - In the present study the incorporation of iron into an organic polymer, composed of formamidine subunits [R–N=C(H)–NH–R], has been examined. The catalytic ability of the recyclable material was investigated in the iron-catalyzed formation of C–C bonds. After optimization of the reaction conditions, excellent yields and chemoselectivities were feasible. KW - Polyforamidine KW - Synthesis KW - Catalytic ability PY - 2012 DO - https://doi.org/10.1039/c2py00540a SN - 1759-9954 SN - 1759-9962 VL - 3 IS - 3 SP - 751 EP - 756 AN - OPUS4-25461 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Brirmi, M A1 - Chabbah, T. A1 - Chatti, S. A1 - Schiets, F. A1 - Casabianca, H. A1 - Marestin, C. A1 - Mercier, R. A1 - Weidner, Steffen A1 - Errachid, A. A1 - Jaffrezic-Renault, N. A1 - Ben Romdhane, H. T1 - Effect of the pendent groups on biobased polymers, obtained from click chemistry suitable, for the adsorption of organic pollutants from water N2 - In this work, four triazole-based poly(ether-pyridine)s polymers were synthesized and used as an adsorbent for the removal of phenolic compounds from aqueous solutions. For this purpose, new fluoromonomers containing 1,2,3-triazole units were prepared by the Cu(I)-catalyzed 1,3-dipolar cycloaddition reaction and then used for the elaboration of novel poly(ether-pyridine-triazole)s (PEPTs) by direct polyconden-sation with isosorbide and bisphenol A. Chemical structure of fluorinated pyridinicmonomers as well as resulting polymers was confirmed by 1H and 19F NMR spectroscopic methods. The thermal behavior of the obtained PEPTs was characterized using differential scanning calorimetry and thermogravimetric analysis. Results of sorption showed that polymers can be effectively used as a sorbent for the removal of polarorganic pollutants. The isosorbide-based poly(ether-pyridine-triazole) which contains hydrophilic hydroxyl groups as pendants chains (P4) exhibited the highest sorption efficiencies (78%–100% after 1 h). In order to explain the results an adsorption mech-anism mainly based on π–π interactions and hydrogen bonding with the pendent groups is proposed. KW - Adsorption KW - Biobased polymers KW - Cycloaddition KW - Pentafluoropyridine KW - Phenolic compounds PY - 2022 DO - https://doi.org/10.1002/pat.5809 SN - 1042-7147 SP - 1 EP - 21 PB - Wiley online library AN - OPUS4-55389 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Jlalia, I. A1 - Gomri, M. A1 - Chabbah, T. A1 - Chatti, S. A1 - Weidner, Steffen A1 - Abderrazak, H. A1 - Marestin, C. A1 - Mercier, R. A1 - Ben Halima, H. A1 - Lakard, B. A1 - Jaffrezic Renault, N. T1 - Design of Fluorinated Poly(Ether-Pyridine) Films for Impedimetric Detection of Heavy Metal Ions N2 - A series of fluorinated poly(ether-pyridine)s were synthesized via polycondensation of bis-perfluoropyridine with either bisphe-nol A (BPA) or isosorbide, a bio-sourced diol. The polymers were characterized using 1 H and 19 F NMR spectroscopy, and their molecular weights were determined using GPC. Thermal properties were assessed using thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). The presence of isosorbide in polymer P2 increases the glass transition temperature and results in a lower molecular weight and a higher hydrophilicity. On the other hand, polymer P3, based on BPA, shows the best thermal stability, the highest molecular weight, and the most pronounced hydrophobic character. Electrochemical impedance spectroscopy (EIS) was used to evaluate the modified gold electrodes for the selective detection of metal ions. Among the four target ions (Ni 2+, Cd 2+, Pb2+, and Hg 2+), defined by the European Water Framework Directive, Pb2+ was selectively detected on the hydrophilic polymer P2, while Cd 2+ was selectively detected on the hydrophobic polymer P3. The achieved detection limits were 5 × 10−11 M, corresponding to 10 ng/L for Pb2+ and 5.6 ng/L for Cd 2+, respectively. KW - Cadmium KW - Electrochemical impedance spectroscopy KW - Fluorinated polyether pyridines KW - Isosorbide KW - Lead PY - 2025 DO - https://doi.org/10.1002/pat.70038 SN - 1099-1581 VL - 36 IS - 1 SP - 1 EP - 14 PB - John Wiley & Sons Ltd. AN - OPUS4-62384 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H.R. A1 - Weidner, Steffen A1 - Scheliga, F. T1 - Poly(Epsilon-caprolactone) by combined ring-opening polymerization and azeotropic polycondensation - the role of cyclization and equilibration N2 - Using three different catalysts, water-initiated polymerizations of ε-caprolactone were conducted in bulk with variation of the monomer/water ratio. The resulting CH2OH and CO2H- terminated polylactones were subjected in situ to azeotropic polycondensations. With Bi-triflate and temperatures, the polycondensations were not much successful and involved side reactions. With ZnCl2, and especially SnCl2, considerably higher molar masses were achieved. The substitution of toluene for chlorobenzene for refluxing gave better results. The polycondensations broadened the molar mass distribution of the ROP-based prepolymers, and polydispersities between 1.4–1.8 were obtained. The MALDI–TOF mass spectra revealed that the polycondensations significantly enhanced the fraction of rings due to efficient 'end-biting' reactions. By comparison with copolymerization experiments and Sn methoxide-initiated polymerizations, it was demonstrated that equilibration reactions, such as the formation of rings by 'back-biting,' did not occur. KW - Ring-opening polymerization KW - Epsilon-caprolactone (e-CL) KW - Cyclization KW - MALDI-TOF mass spectrometry KW - Polycondensation KW - Polyesters PY - 2012 DO - https://doi.org/10.1002/pola.26222 SN - 0360-6376 SN - 0887-624X VL - 50 IS - 20 SP - 4206 EP - 4214 PB - Wiley CY - Hoboken, NJ AN - OPUS4-26500 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zhao, J. A1 - Schlaad, H. A1 - Weidner, Steffen A1 - Antonietti, M. T1 - Synthesis of terpene-poly(ethylene oxide)s by t-BuP4-promoted anionic ring-opening polymerization N2 - Terpene alcohols (menthol, retinol, cholesterol, and betulin) together with the phosphazene base t-BuP4 were used as initiating systems for anionic ring-opening polymerization of ethylene oxide. The polymerizations were conducted in a controlled manner with the initial molar ratio of t-BuP4 to hydroxyl groups of 0.01–0.2, yielding a series of biohybrid polymers comprising terpene entities and poly(ethylene oxide) (PEO) chains with low polydispersities and tunable compositions (57–87 wt% of PEO). Samples were characterized by NMR and UV/visible spectroscopy, MALDI-TOF mass spectrometry, and size exclusion chromatography; thermal properties were studied by differential scanning calorimetry. The concept of this study opens a new toolbox of terpene-based biohybrid polymers with variable properties and functions. KW - ROMP KW - MALDI KW - Amphiphilic polymers KW - Polyethylene oxide PY - 2012 DO - https://doi.org/10.1039/c1py00388g SN - 1759-9954 SN - 1759-9962 VL - 3 IS - 7 SP - 1763 EP - 1768 AN - OPUS4-26026 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weidner, Steffen A1 - Kühn, Gerhard A1 - Just, Ulrich T1 - Characterization of oligomers in poly(ethylene terephthalate) by matrix-assisted laser desorption/ionization mass spectrometry PY - 1995 SN - 0951-4198 SN - 1097-0231 IS - 9 SP - 697 EP - 702 PB - Wiley CY - Chichester AN - OPUS4-11278 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Böhmert, L. A1 - Girod, Matthias A1 - Hansen, Ulf A1 - Maul, Ronald A1 - Knappe, Patrick A1 - Niemann, B. A1 - Weidner, Steffen A1 - Thünemann, Andreas A1 - Lampen, A. T1 - Analytically monitored digestion of silver nanoparticles and their toxicity on human intestinal cells N2 - Orally ingested nanoparticles may overcome the gastrointestinal barrier, reach the circulatory system, be distributed in the organism and cause adverse health effects. However, ingested nanoparticles have to pass through different physicochemical environments, which may alter their properties before they reach the intestinal cells. In this study, silver nanoparticles are characterised physicochemically during the course of artificial digestion to simulate the biochemical processes occurring during digestion. Their cytotoxicity on intestinal cells was investigated using the Caco-2 cell model. Using field-flow fractionation combined with dynamic light scattering and small-angle X-ray scattering, the authors found that particles only partially aggregate as a result of the digestive process. Cell viabilities were determined by means of CellTiter-Blue® assay, 4',6-diamidino-2-phenylindole-staining and real-time impedance. These measurements reveal small differences between digested and undigested particles (1–100 µg/ml or 1–69 particles/cell). The findings suggest that silver nanoparticles may indeed overcome the gastrointestinal juices in their particulate form without forming large quantities of aggregates. Consequently, the authors presume that the particles can reach the intestinal epithelial cells after ingestion with only a slight reduction in their cytotoxic potential. The study indicates that it is important to determine the impact of body fluids on the nanoparticles of interest to provide a reliable interpretation of their nano-specific cytotoxicity testing in vivo and in vitro. KW - Silver nanoparticles KW - In vitro digestion KW - Field-flow fractionation KW - Small-angle X-ray scattering KW - Dynamic light scattering KW - Caco-2 cells PY - 2014 DO - https://doi.org/10.3109/17435390.2013.815284 SN - 1743-5390 SN - 1743-5404 VL - 8 IS - 6 SP - 631 EP - 642 PB - Informa Healthcare CY - London AN - OPUS4-29926 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Friedrich, Jörg Florian A1 - Unger, Wolfgang A1 - Lippitz, Andreas A1 - Koprinarov, Ivaylo A1 - Kühn, Gerhard A1 - Weidner, Steffen A1 - Vogel, Lydia T1 - Chemical reactions at polymer surfaces interacting with a gas plasma or with metal atoms - their relevance to adhesion N2 - The chemical and morphological stabilities of polymer segments in the near-surface layer were investigated by spectroscopic methods such as X-ray photoelectron spectroscopy and near-edge X-ray absorption fine structure spectroscopy. Model studies were undertaken with Langmuir–Blodgett films, self-assembled monolayers and oligomer films. For thin polymer layers (30 to 500 nm), the changes in molecular-weight distributions of some polymers were investigated systematically by size exclusion chromatography, matrix-assisted laser desorption/ionization–time-of-flight mass spectrometry and thermal-field flow fractionation for oxygen- and helium-plasma exposures. The polymer surfaces were found to be relatively stable at exposure to an oxygen low-pressure plasma up to ca. 2 s. This is important information to get maximum adhesion to metals in composites. In correlation to their redox potentials, potassium, aluminium and chromium react with oxygen functional groups at the polymer/metal interface. In a dedicated study, chromium was found to attack aromatic rings and form different reaction products. PY - 1999 DO - https://doi.org/10.1016/S0257-8972(99)00229-7 SN - 0257-8972 VL - 116-119 SP - 772 EP - 782 PB - Elsevier Science CY - Lausanne AN - OPUS4-6981 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Friedrich, Jörg Florian A1 - Unger, Wolfgang A1 - Lippitz, Andreas A1 - Geng, Sh. A1 - Koprinarov, Ivaylo A1 - Kühn, Gerhard A1 - Weidner, Steffen T1 - Modelling plasma-induced reactions on polymer surfaces using aliphatic self-assembling and LB layers PY - 1998 SN - 0257-8972 VL - 98 SP - 1132 EP - 1141 PB - Elsevier Science CY - Lausanne AN - OPUS4-6999 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H. A1 - Weidner, Steffen A1 - Meyer, A. T1 - Ring-expansion polymerization (REP) of L-lactide with cyclic tin catalysts – About formation of extended ring crystals and optimization of Tm and ΔHm N2 - L-Lactide was polymerized in bulk at 140 °C with three different cyclic tin catalysts and the time was varied from 1 d up to 14 d. The MALDI TOF spectra confirmed the formation of cyclic polylactides (PLAs) and displayed a characteristic change of peak intensity distribution with formation of a “saw tooth pattern”. This pattern confirms a previous hypothesis that cyclic PLAs tend to form crystallites with extended ring conformation and relatively smooth surface. This type of crystallites is formed under thermodynamic control by transesterification on the surface of the crystallites. In this way PLAs with extraordinarily high melting temperatures (Tm's up to 200.6 °C) and extraordinarily high melting enthalpy were obtained (ΔHm's up to 105 J g−1). These ΔHm values require a revision of the maximum ΔHm value calculated in the literature for ideal PLA crystals. KW - Polylactide KW - MALDI-TOF MS KW - ring-expansion polymerization PY - 2022 DO - https://doi.org/10.1016/j.polymer.2022.125516 SN - 0032-3861 VL - 263 SP - 125516 PB - Elsevier Ltd. AN - OPUS4-56338 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Appelhans, Dietmar A1 - Oertel, U. A1 - Mazzeo, R. A1 - Komber, H. A1 - Hoffmann, J. A1 - Weidner, Steffen A1 - Brutschy, B. A1 - Voit, B. A1 - Ottaviani, M.F. T1 - Dense-shell glycodendrimers: UV/Vis and electron paramagnetic resonance study of metal ion complexation N2 - The development of dendritic metal ion carrier systems for use in a biological environment is a challenging task as the carrier system must possess multiple features (e.g. a protective shell for metal decomplexation, targeting functions, metal-intradendrimer complexes, etc.) to substitute for the function of metal proteins in processes such as copper metabolism. Thus, Cu(II) complexation by a series of poly(propyleneimine) glycodendrimers ranging up to the fifth generation that have either a dense maltose or maltotriose shell was investigated by UV/Vis spectroscopy and electron paramagnetic resonance (EPR). As a necessary step towards potential biological application, we elucidated the complexation capacity, location of the Cu(II)-dendrimer complexes and the Cu(II) coordination sphere in the dendritic environment. A generation-dependent Cu(II) complexation was found. Furthermore, analysis of the EPR spectra revealed that internal and external Cu(II) coordination and the symmetry (axial and rhombic) of the generated complexes depend on the oligosaccharide shell, dendrimer generation and the relative concentrations of Cu(II) and the dendrimers. Both axial and rhombic symmetries are generation dependent, but also distort with increasing generation number. External coordination of Cu(II) is supported by sugar groups and water molecules. Finally, a third-generation dendrimer with a maltose shell was used to explore the general complexation behaviour of the dendritic poly(propyleneimine) scaffold towards different metal ions [Cu(II), Ag(I), VO(IV), Ni(II), Eu(III) and UO2(VI)]. KW - Glycodendrimers KW - Metal ion complexation KW - Metal ion-intradendrimer complexes KW - Electron paramagnetic resonance study PY - 2010 DO - https://doi.org/10.1098/rspa.2009.0107 SN - 1364-5021 SN - 0962-8444 SN - 0080-4630 SN - 0950-1207 SN - 1471-2946 VL - 466 SP - 1489 EP - 1513 CY - London, UK AN - OPUS4-21622 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kona, Balakantha Rao A1 - Weidner, Steffen A1 - Friedrich, Jörg Florian T1 - Epoxidation of Polydienes Investigated by MALDI-TOF Mass Spectrometry and GPC-MALDI Coupling N2 - Polybutadienes (PB) and polyisoprenes (PI) with various molecular weights and polydispersities were epoxidized applying two different synthetic routes. The degree of epoxidation was determined by means of matrix-assisted laser desorption/ionization-time of flight mass spectrometry (MALDI-TOF MS). It has been found that the degree of functionalization of polybutadiene is generally lower than that for polyisoprenes. Additionally, PB shows lower degrees of epoxidation at higher masses, whereas the level of functionalization of PI was unaffected by the molar mass. Coupling of gel permeation chromatography (GPC) with MALDI-TOF mass spectrometry was successfully used for the investigation of epoxidized polymers with higher masses. Using mass spectra of single fractions, the degree of epoxidation could be determined and applied for a calibration of GPC. PY - 2005 DO - https://doi.org/10.1080/10236660490935736 SN - 1023-666X SN - 1563-5341 VL - 10 IS - 1-2 SP - 85 EP - 109 PB - Gordon and Breach Publ. CY - Amsterdam AN - OPUS4-11860 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weidner, Steffen A1 - Falkenhagen, Jana T1 - LC-MALDI-TOF imaging MS: a new approach in combining chromatography and mass spectrometry of copolymers N2 - A new approach that utilizes MALDI-TOF imaging mass spectrometry as a new detector for polymer chromatography is presented. For the first time, the individual retention behavior of single structural units of polyethylene oxide (PEO)/polypropylene oxide (PPO) copolymers and changes of the copolymer composition could be monitored. Composition specific calibration curves could be easily obtained by displaying the copolymer ion intensity data. This approach provides completely new insights in the chromatographic principle of copolymer separation and could be used to easily modify and adapt conditions for separation. In combination with electrospray deposition, homogeneous sample/matrix traces of surprisingly high spatial resolution could be obtained. KW - MALDI KW - Massenspektrometrie KW - Imaging KW - Chromatographie KW - Polymere PY - 2011 DO - https://doi.org/10.1021/ac202380n SN - 0003-2700 SN - 1520-6882 VL - 83 IS - 23 SP - 9153 EP - 9158 PB - American Chemical Society CY - Washington, DC AN - OPUS4-24974 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weidner, Steffen A1 - Kühn, Gerhard A1 - Friedrich, Jörg Florian A1 - Unger, Wolfgang A1 - Lippitz, Andreas T1 - Plasmaoxidative Degradation of Polymers Studied by Matrix-assisted Laser Desorption/Ionization Mass Spectrometry PY - 1996 SN - 0951-4198 SN - 1097-0231 VL - 10 SP - 727 EP - 732 PB - Wiley CY - Chichester AN - OPUS4-7004 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -