TY - JOUR A1 - Kricheldorf, H. A1 - Weidner, Steffen A1 - Meyer, A. T1 - About alcohol-initiated polymerization of glycolide and separate crystallization of cyclic and linear polyglycolides N2 - Alcohol-initiated polymerizations of glycolide (GL) catalyzed by tin(II) 2-ethylhexanoate (SnOct2) were carried out in bulk with variation of GA/In ratio, temperature and time. Due to a rather strong competition of cyclization polyglycolide (PGA) free of cycles were never obtained. When the cyclic catalysts 2,2-dibutal-2-stanna − 1,3-dithiolane (DSTL) or 2-stanna 1,3-dioxo-4,5,6,7 bibenzepane (SnBiph) were used in combination with 1,4-butanediol the influence of cyclization was even stronger. Furthermore, the degrees of polymerization were higher than the GA/alcohol ratio due to rapid polycondensation in the solid state. At 160 °C or below, the matrixassisted laser desorption/ionization time-of-flight (MALDI-TOF) mass spectra indicated separate crystallization of low molar mass cyclic and linear PGAs from the same reaction mixture (also observed for poly(L-lactide)s). KW - MALDI TOF MS KW - Polyglycolide KW - Ring opening polymerization KW - Cyclization KW - Crystallization PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-607282 DO - https://doi.org/10.1016/j.polymer.2024.127440 SN - 0032-3861 VL - 309 SP - 1 EP - 9 PB - Elsevier Ltd. AN - OPUS4-60728 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, Hans R. A1 - Weidner, Steffen A1 - Meyer, A. T1 - About Polycondensation, Disproportionation, and Cyclization of Acetylated Poly(L-Lactide) Esters N2 - L-lactide (LA) is polymerized with ethyl L-lactate or trifluoroethanol as initiators (LA/In = 30/1), and the resulting poly(L-lactide) esters are acetylated with acetic anhydride. The acetylated PLA esters are mixed with SnOct2, dibutyltin bis(4-chlorophenoxide), or dibutyltin bis(pentafluorophenoxide) in solution and crystallized at 120 °C. The doped crystals are annealed at 140 °C or at 160 °C for 7, 14, and 28 days, and the chemical modifications that occurred in the solid state are monitored by matrix-assisted laser desorption/ionization time-of-flight (MALDI TOF) mass spectrometry, gel permeation chromatography (GPC), and differential scanning calorimetry (DSC) measurements. All catalysts promoted polycondensation, while no significant formation of cycles is observed. However, in the presence of SnOct2, disproportionation of chains occurred upon annealing at 120 or 140 °C, and crystallites consisting of extended chains with Mn values ≈3500 – 3600 and low dispersities (Ð < 1.5) are formed. KW - MALDI-TOF MS KW - Polycondensation KW - Polylactides KW - Transesterifcation PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-630349 DO - https://doi.org/10.1002/macp.202400175 SN - 1521-3935 VL - 225 IS - 19 PB - Wiley VHC-Verlag AN - OPUS4-63034 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weidner, Steffen A1 - Meyer, A. A1 - Kricheldorf, H. T1 - Cyclic polyglycolides via ring-expansion polymerization with cyclic tin catalysts N2 - Glycolide was polymerized in bulk with two cyclic catalysts − 2,2-dibutyl-2-stanna-1,3-dithiolane (DSTL) and 2-stanna-1,3-dioxa-4,5,6,7-dibenzepane (SnBiph). The monomer/initiator ratio, temperature (140 – 180 °C) and time (1–––4 days) were varied. The MALDI TOF mass spectra exclusively displayed peaks of cyclic polyglycolide (PGA) and revealed an unusual “saw-tooth pattern” in the mass range below m/z 2 500 suggesting formation of extended ring crystallites. The DSC measurements indicated increasing crystallinity with higher temperature and longer time, and after annealing for 4 d at 160 °C a hitherto unknown and unexpected glass transition was found in the temperature range of 170–185 °C. Linear PGAs prepared by means of metal alkoxides under identical conditions did not show the afore-mentioned features of the cyclic PGAs, neither in the mass spectra nor in the DSC measurements. All PGAs were also characterized by SAXS measurements, which revealed relatively small L-values suggesting formation of thin crystallites in all cases with little influence of the reaction conditions. KW - Polyglycolide KW - MALDI-TOF MS KW - Ring-expansion polymerization KW - Crystals PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-595541 DO - https://doi.org/10.1016/j.eurpolymj.2024.112811 SN - 0014-3057 VL - 207 SP - 1 EP - 9 PB - Elsevier Ltd. AN - OPUS4-59554 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Cherbib, S. A1 - Jlalia, I. A1 - Chabbah, T. A1 - Chatti, S. A1 - Marestin, C. A1 - Mercier, R. A1 - Weidner, Steffen A1 - Casabianca, H. A1 - Jaffrezic-Renault, N. A1 - Abderrazak, H. T1 - Design of New Partially Bio-Based Polyguanamines for the Reversible Adsorption of Phenolic Molecules from Olive Mill Wastes N2 - Olive mill wastewater produces a variety of potent antioxidants, including hydroxytyrosol, oleuropein, and tyrosol, that have been widely used in agriculture, pharmacy, and cosmetics. This study aims to design new poly(guanamine)s phases by polycondensation of modified triazine monomers with both petro-based and biosourced diamines, to act as stationary phases for the uptake of these phenolic molecules. Obtained polymers were characterized by NMR spectroscopy, differential scanning calorimetry (DSC), and thermogravimetric analysis (TGA). The adsorption results showed that the newly synthesized polymers can effectively uptake the less polar phenolic compounds, ferulic acid, and caffeic acid. The isosorbide-based polymer (P6) presented the highest sorption efficiency, due to the hydrophilic properties of isosorbide associated with the proton affinity of the triazine groups. All the phenolic compounds were successfully desorbed from the P6 polymer using a minimal amount of a methanol/acetonitrile mixture. P6 polymer could be used for four successive adsorption processes without loss of efficiency. KW - Olive mill wastewater KW - Triazine KW - Isosorbide KW - Adsorption KW - Phenolic compounds PY - 2024 DO - https://doi.org/10.1007/s42250-024-01081-3 SN - 2522-5758 SP - 1 EP - 11 PB - Springer Science and Business Media LLC AN - OPUS4-61348 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H. A1 - Weidner, Steffen T1 - Low Molar Mass Cyclic Poly(L-lactide)s: Separate Transesterification Reactions of Cycles and Linear Chains in the Solid State N2 - L-Lactide (LA) was polymerized with neat tin(II) 2-ethylhexanoate (SnOct2) in toluene at 115 °C at low concentration with variation of the LA/Cat ratio. Cyclic polylactides (cPLAs) with number average molecular weights (Mn) between 7 000 and 17 000 were obtained. MALDI-TOF mass spectrometry also revealed the formation of a few percent of linear chains. Crystalline cPLAs with Mn around 9 000 and 14 000 were annealed at 140 °C in the presence of ScOct2 or dibutyl-2-stanna-1,3-dithiolane (DSTL). Simultaneously, crystallites of extended linear chains and crystallites of extended cycles were formed regardless of the catalyst, indicating that transesterification reaction proceeded different for linear chains and for cycles, governed by thermodynamic control. The formation of extended chain crystallites with low dispersity indicates the existence of symproportionation of short and long chains. A complementary experiment was carried out with a PLA ethyl ester composed mainly of linear chains with a small fraction of cycles KW - Polylactide KW - MALDI-TOF MS KW - Annealing PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-606228 DO - https://doi.org/10.1039/D4SM00567H SN - 1744-6848 SP - 1 EP - 12 PB - Royal Society of Chemistry (RSC) AN - OPUS4-60622 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weidner, Steffen T1 - MALDI TOF MS zur Aufklärung von Kristallisationsprozessen in Polyestern N2 - MALDI TOF Massenspektrometrie wurde verwendet, um Kristallisationsprozesse in Polyestern (Polylactide, Polyglycolide) zu untersuchen. Dabei konnte gezeigt werden, dass Zyklen und Linearen simultan, aber in unterschiedlichen Kristalliten, kristallisieren. Die dabei ablaufenden Umesterungen (Transesterifizierungen) konnten mit der MALDI TOF Massenspektrometrie nachgewiesen werden. Damit wurde ein völlig neues Anwendungsgebiet dieser MS Methode demonstriert. T2 - 28. Kolloquium Massenspektrometrie von Polymeren CY - Berlin, Germany DA - 14.05.2024 KW - MALDI TOF MS KW - Bioabbaubare Polymere KW - Crystallinity PY - 2024 AN - OPUS4-60029 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Trimpin, Sarah A1 - Yenchick, Frank S. A1 - Lee, Chuping A1 - Hoang, Khoa A1 - Pophristic, Milan A1 - Karki, Santosh A1 - Marshall, Darrell D. A1 - Lu, I-Chung A1 - Lutomski, Corinne A. A1 - El-Baba, Tarick J. A1 - Wang, Beixi A1 - Pagnotti, Vincent S. A1 - Meher, Anil K. A1 - Chakrabarty, Shubhashis A1 - Imperial, Lorelei F. A1 - Madarshahian, Sara A1 - Richards, Alicia L. A1 - Lietz, Christopher B. A1 - Moreno-Pedraza, Abigail A1 - Leach, Samantha M. A1 - Gibson, Stephen C. A1 - Elia, Efstathios A. A1 - Thawoos, Shameemah M. A1 - Woodall, Daniel W. A1 - Jarois, Dean R. A1 - Davis, Eric T.J. A1 - Liao, Guochao A1 - Muthunayake, Nisansala S. A1 - Redding, McKenna J. A1 - Reynolds, Christian A. A1 - Anthony, Thilani M. A1 - Vithanarachchi, Sashiprabha M. A1 - DeMent, Paul A1 - Adewale, Adeleye O. A1 - Yan, Lu A1 - Wager-Miller, James A1 - Ahn, Young-Hoon A1 - Sanderson, Thomas H. A1 - Przyklenk, Karin A1 - Greenberg, Miriam L. A1 - Suits, Arthur G. A1 - Allen, Matthew J. A1 - Narayan, Srinivas B. A1 - Caruso, Joseph A. A1 - Stemmer, Paul M. A1 - Nguyen, Hien M. A1 - Weidner, Steffen A1 - Rackers, Kevin J. A1 - Djuric, Ana A1 - Shulaev, Vladimir A1 - Hendrickson, Tamara L. A1 - Chow, Christine S. A1 - Pflum, Mary Kay H. A1 - Grayson, Scott M. A1 - Lobodin, Vladislav V. A1 - Guo, Zhongwu A1 - Ni, Chi-Kung A1 - Walker, J. Michael A1 - Mackie, Ken A1 - Inutan, Ellen D. A1 - McEwen, Charles N. T1 - New Processes for Ionizing Nonvolatile Compounds in Mass Spectrometry: The Road of Discovery to Current State-of-the-Art N2 - This Perspective covers discovery and mechanistic aspects aswell as initial applications of novel ionization processes for use in massspectrometry that guided us in a series of subsequent discoveries, instrumentdevelopments, and commercialization. Vacuum matrix-assisted ionization onan intermediate pressure matrix-assisted laser desorption/ionization sourcewithout the use of a laser, high voltages, or any other added energy wassimply unbelievable, at first. Individually and as a whole, the variousdiscoveries and inventions started to paint, inter alia, an exciting new pictureand outlook in mass spectrometry from which key developments grew thatwere at the time unimaginable, and continue to surprise us in its simplisticpreeminence. We, and others, have demonstrated exceptional analyticalutility. Our current research is focused on how best to understand, improve, and use these novel ionization processes throughdedicated platforms and source developments. These ionization processes convert volatile and nonvolatile compounds from solid orliquid matrixes into gas-phase ions for analysis by mass spectrometry using, e.g., mass-selected fragmentation and ion mobilityspectrometry to provide accurate, and sometimes improved, mass and drift time resolution. The combination of research anddiscoveries demonstrated multiple advantages of the new ionization processes and established the basis of the successes that lead tothe Biemann Medal and this Perspective. How the new ionization processes relate to traditional ionization is also presented, as wellas how these technologies can be utilized in tandem through instrument modification and implementation to increase coverage ofcomplex materials through complementary strengths. KW - Mass spectrometry PY - 2024 DO - https://doi.org/10.1021/jasms.3c00122 SN - 1879-1123 VL - 35 IS - 12 SP - 2753 EP - 2784 PB - American Chemical Society (ACS) AN - OPUS4-61417 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H. A1 - Weidner, Steffen A1 - Scheliga, F. T1 - Polycondensation of poly(L-lactide) alkyl esters combined with disproportionation and symproportionation of the chain lengths N2 - Ring-opening polymerizations (ROPs) of l-lactide (LA) were performed with ethyl l-lactate or 11-bromoundecanol as initiators (In) and tin(II) ethyl hexanoate (SnOct2) as catalyst (Cat) using four different LA/In ratios (20/1, 40/1, 60/1, and 100/1). One series of ROPs was conducted in bulk at 120 °C, yielding PLAs with low dispersities (Ð ~ 1.2–1.4), and a second series was conducted in bulk at 160 °C, yielding higher dispersities (Ð ~ 1.3–1.9). Samples from both series were annealed for 1 or 14 days at 140 °C in the presence of SnOct2. Both polycondensation and disproportionation reactions occurred, so that all four samples tended to form the same type of molar mass distribution below 10,000 Da, regardless of their initially different number average molar masses (Mn). Both initiators gave nearly identical results. The thermodynamic control of all reversible transesterification processes favored the formation of crystallites composed of chains with a Mn around 3500–3700, corresponding to a crystal thickness of 10–13 nm. KW - Polylactide KW - MALDI-TOF MS KW - Crystalinity PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-600081 DO - https://doi.org/10.1002/pol.20240118 SN - 2642-4150 SP - 1 EP - 12 PB - Wiley AN - OPUS4-60008 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weidner, Steffen A1 - Scheliga, Felix A1 - Kricheldorf, Hans R. T1 - Polycondensation, Cyclization and Disproportionation of Solid Poly(L-lactide) Trifluoroethyl Esters and the Simultaneous Formation of Extended Chain Crystals and Extended Ring Crystals N2 - Two poly(L-lactide)s (PLAs) with a degree of polymerization (DP) of 20 or 100 were prepared by trifluoroethanol-initiated ring-opening polymerization (ROP) catalyzed by tin(II) 2-ethyl hexanoate (SnOct2). These PLAs were annealed at 140 ◦C or at 160 ◦C in the presence of SnOct2, and the changes in topology and molecular weight distribution (MWD) were monitored by matrix-assisted laser desorption/ionization time-of flight (MALDI TOF) mass spectrometry and gel permeation chromatography (GPC). For the PLA with a DP 20, the main reaction was polycondensation combined with higher dispersities. In the case of the DP 100, PLA polycondensation was combined with disproportionation and the formation of a new MWD maximum around m/z 3500. In addition, extensive cyclization occurred, and the resulting cyclic PLAs crystallized separately from the linear chains in the form of extended ring crystals. These results also suggest that both extended chain and extended ring crystals posses the same crystal thickness as a result of thermodynamically controlled transesterification in the solid state. KW - Polycondensation KW - MALDI KW - Polylactide KW - Cyclization PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-616441 DO - https://doi.org/10.1016/j.polymer.2024.127800 VL - 315 SP - 1 EP - 9 PB - Elsevier Ltd. AN - OPUS4-61644 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weidner, Steffen A1 - Meyer, A. A1 - Falkenhagen, Jana A1 - Kricheldorf, H. R. T1 - Polycondensations and Cyclization of Poly(L-lactide) Ethyl Esters in the Solid State N2 - The usefulness of seven different Tin catalysts, Bismuth subsalicylate and Titan tetra(ethoxide) for the polycondensation of ethyl L-lactate (ELA) was examined at 150 °C/6 d. Dibutyltin bis(phenoxides) proved to be particularly effective. Despite the low reactivity of ELA, weight average molecular masses (Mw) up to 12 500 were found along with partial crystallization. Furthermore, polylactides (PLAs) of similar molecular masses were prepared via ELA-initiated ROPs of L-lactide by means of the four most effective polycondensation catalysts. The crystalline linear PLAs were annealed at 140 or 160 °C in the presence of these catalysts. The consequences of the transesterification reactions in the solid PLAs were studied by means of matrix-assisted laser desorption/ionization (MALDI TOF) mass spectrometry, gel permeation chromatography (GPC) and small-angle X-ray scattering (SAXS). The results indicate that polycondensation and formation of cycles proceed in the solid state via formation of loops on the surface of the crystallites. In summary, five different transesterification reactions are required to explain all results. KW - Polylactide KW - MALDI-TOF MS KW - Crystalinity PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-592934 DO - https://doi.org/10.1039/d3py01232h SN - 1759-9962 VL - 15 IS - 2 SP - 71 EP - 82 PB - RSC Publ. CY - Cambridge AN - OPUS4-59293 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, Hans R. A1 - Weidner, Steffen T1 - Ring-ring equilibration (RRE) of cyclic poly(L-lactide)s by means of cyclic tin catalysts N2 - With 2,2-dibutyl-2-stanna-1,3-dithiolane (DSTL) and 2-stanna-1,3-dioxa-4,5,6,7-dibenzoxepane (SnBiPh) as catalysts ring-expansion polymerizations (REP) were performed either in 2 M solution using three different solvents and two different temperatures or in bulk at 140 and 120 ◦C. A kinetically controlled rapid REP up to weight average molecular masses (Mẃs) above 300 000 was followed by a slower degradation of the molecular masses at 140 ◦C, but not at 120 ◦C Furthermore, a low molecular mass cyclic poly(L-lactide) (cPLA) with a Mn around 16 000 was prepared by polymerization in dilute solution and used as starting material for ring-ring equilibration at 140 ◦C in 2 M solutions. Again, a decrease of the molecular mass was detectable, suggesting that the equilibrium Mn is below 5 000. The degradation of the molecular masses via RRE was surprisingly more effective in solid cyclic PLA than in solution, and a specific transesterification mechanism involving loops on the surface of crystallites is proposed. This degradation favored the formation of extended-ring crystallites, which were detectable by a “saw-tooth pattern” in their MALDI mass spectra. KW - Organic Chemistry KW - Polymers and Plastics KW - MALDI-TOF MS KW - Materials Chemistry PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-593819 DO - https://doi.org/10.1016/j.eurpolymj.2024.112765 SN - 0014-3057 VL - 206 SP - 1 EP - 8 PB - Elsevier B.V. AN - OPUS4-59381 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dalgic, Mete-Sungur A1 - Weidner, Steffen T1 - Solvent-free sample preparation for matrix-assisted laserdesorption/ionization time-of-flight mass spectrometry ofpolymer blends N2 - Solvent-free sample preparation offers some advantages over solvent-based techniques, such as improved accuracy, reproducibility and sensitivity, for matrix-assisted laser desorption/ionization (MALDI) analysis. However, little or no information is available on the application of solvent-free techniques for the MALDI analysis of polymer blends. Solvent-free sample preparation by ball milling was applied with varying sample-to-matrix ratios for MALDI time-of-flight mass spectrometry analysis of various polymers, including polystyrenes, poly(methyl methacrylate)s and poly(ethylene glycol)s. The peak intensity ratios were compared with those obtained after using the conventional dried droplet sample preparation method. In addition, solvent-assisted milling was also applied to improve sample homogeneities. Depending on the sample preparation method used, different peak intensity ratios were found, showing varying degrees of suppression of the signal intensities of higher mass polymers. Ball milling for up to 30 min was required to achieve constant intensity ratios indicating homogeneous mixtures. The use of wet-assisted grinding to improve the homogeneity of the blends was found to be disadvantageous as it caused partial degradation and mass-dependent segregation of the polymers in the vials.The results clearly show that solvent-free sample preparation must be carefully considered when applied to synthetic polymer blends, as it may cause additional problems with regard to homogeneity and stability of the blends. KW - MALDI TOF MS KW - Sample preparation KW - Polymer blends KW - Solvent-free PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-598570 DO - https://doi.org/10.1002/rcm.9756 SN - 0951-4198 VL - 38 IS - 12 SP - 1 EP - 9 PB - Wiley online library AN - OPUS4-59857 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H. A1 - Weidner, Steffen A1 - Meyer, A. T1 - Syntheses of high molecular mass polyglycolides via ring-opening polymerization with simultaneous polycondensation (ROPPOC) by means of tin and zinc catalysts N2 - Glycolide was polymerized in bulk by means of four different ROPPOC catalysts: tin(II) 2-ethylhexanoate (SnOct2), dibutyltin bis(pentafluoro-phenoxide) (BuSnOPF),zinc biscaproate (ZnCap), and zinc bis(pentafluoro-phenyl sulfide) (ZnSPF). The temperature was varied between 110 and 180°C and the time between 3 h and 7 days. For the few polyglycolides (PGAs) that were soluble extremely high molecular masses were obtained. The MALDI TOF mass spectra had all a low signal-to-noise ration and displayed the peaks of cyclic PGAs with a“saw-tooth pattern ”indicating formation of extended-ring crystallites in the mass range below m/z 2500. The shape of DSC curves varied considerably with catalyst and reaction conditions, whereas the long-distance values measured by SAXS were small and varied little with the polymeriza-tion conditions. KW - MALDI TOF MS KW - Polyglycolide KW - Crystalinity PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-598221 DO - https://doi.org/10.1002/pat.6365 VL - 35 IS - 4 SP - 1 EP - 10 PB - John Wiley & Sons Ltd. AN - OPUS4-59822 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H. A1 - Weidner, Steffen A1 - Meyer, A. T1 - Syntheses of Polyglycolide via Polycondensation: A Reinvestigation N2 - The Na salt of chloroacetic acid is condensed in suspension. Furthermore,glycolic acid is condensed in bulk or in concentrated solution by means of SnCl2 or 4-toluene sulfonic acid (TSA) as catalysts. The temperatures are varied from 160 to 200°C and the time from 1 to 5 days. Low molar mass cyclic poly(glycolic acid) (PGA) is detected by means of matrix-assisted laser desorption ionization time-of-flight (MALDI TOF) mass spectrometry in most PGAs. A predominance of certain cycles having an even number of repeat units is observed suggesting a thermodynamically favored formation of extended-ring crystals. Extremely high melting temperatures (up to 237.5°C)and high melting enthalpies are found for polycondensations with TSA in 1,2-dichlorobenzene. KW - MALDI TOF MS KW - Polycondensation KW - Polyglycolide KW - Cyclization PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-596856 DO - https://doi.org/10.1002/macp.202300397 IS - 2300397 SP - 1 EP - 7 PB - Wiley VHC-Verlag AN - OPUS4-59685 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weidner, Steffen A1 - Meyer, A. A1 - Kricheldorf, H. T1 - Transformation of poly(L-lactide) crystals composed of linear chains into crystals composed of cycles N2 - A poly(L-lactide) with a trifluoroethyl ester end group and an average degree of polymerization (DP) of 50 was synthesized by ROP of L-lactide initiated with trifluoroethanol. Small-angle X-ray scattering (SAXS) in combination with differential scanning calorimetry (DSC) measurements revealed an average crystal thickness of 13 nm, corresponding to 45 repeat units. This suggests that most crystallites were formed by extended PLA chains, and both flat surfaces were covered by CF3 groups. The crystalline PLAs were annealed at 140 or 160 °C in the presence of two catalysts: tin(II) 2-ethylhexanoate, (SnOct2) or dibutyltin bis(pentafluorophenoxide) (BuSnPhF). The chemical reactions, such as polycondensation and cyclization, proceeded in the solid state and were monitored by matrix-assisted laser desorption/ionization time-offlight (MALDI TOF) mass spectrometry and gel permeation chromatography (GPC) measurements. Under optimal conditions a large fraction of linear chains was transformed into crystallites composed of extended cycles. Additionally, MALDI TOF MS analysis of GPC fractions from samples annealed for 28 or 42 days detected chain elongation of the linear species up to a factor of 20. KW - Polylactide KW - MALDI-TOF MS KW - Crystalinity KW - Transesterification PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-597250 DO - https://doi.org/10.1039/D3PY01370G SN - 1759-9954 VL - 15 IS - 12 SP - 1173 EP - 1181 PB - Royal Society for Chemistry AN - OPUS4-59725 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -