TY - JOUR A1 - Kricheldorf, H. R. A1 - Weidner, Steffen A1 - Scheliga, F. T1 - Ring-opening polymerizations of L-Lactide catalyzed by zinc caprylate: Syntheses of cyclic and linear poly(L-lactide)s N2 - Alcohol-initiated ring-opening polymerizations (ROPs) of L-Lactide (LA) were conducted in bulk at 130 °C catalyzed by Zn acetate (ZnAc2), lactate (ZnLac2), or caprylate (ZnCap2). 11-undecenol (UND), 1-hydroxymethylnaphtalene (HMN), and 4-nitrobenzylalcohol (4NB) were used as alcohols. Whereas variation of the alcohols had little effect, the usefulness of the catalysts increased in the order: acetate < lactate < caprylate. Hence, further alcohol-initiated polymerizations were performed with ZnCap2 alone and with variation of the lactide/catalyst (LA/Cat) ratio. With increasing LA/Cat ratio higher fractions of cyclic poly(L-lactide) (PLA) were found, so that the measured degree of polymerization (DP) is considerably lower than the theoretical value (i.e., 2 x LA/alcohol). With neat ZnCap2 cyclic PLAs were the largely prevailing reaction products. For these cyclic PLAs weight average molar masses (Mw) up to 134,000 were obtained and an optical purity around 99% was indicated by 13C NMR spectroscopy and DSC measurements even after 48 h at 150 or 160 °C. KW - Cyclization KW - Lactide KW - Ring opening polymerization KW - Transesterification KW - Zinc catalyst KW - MALDI PY - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-557565 SN - 2642-4150 SP - 1 EP - 10 PB - Wiley AN - OPUS4-55756 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, Hans A1 - Weidner, Steffen A1 - Scheliga, Felix T1 - Ring-Expansion Polymerization (REP) of L-lactide with cyclic Tin(II) Bisphenoxides N2 - Five new cyclic catalysts were prepared by a new synthetic method from tin(II)-2-ethyhexanoate and silylated catechols, silylated 2,2´dihydroxybiphenyl or silylated 1,1´-bisnaphthol. These catalysts were compared with regard to their usefulness as catalysts for the ring expansion polymerization (REP) of L-lactide in bulk at 160 °C, and with two different tin(IV) derivatives of 1,1´binaphthol. Best results were obtained using seven-membered cyclic tin(II)bisphenoxides, which yielded colorless cyclic poly(l-lactide)s free of racemization with weight average molecular weights (Mw) up to 305 000 g mol-1. Furthermore, these catalysts were active even at a lactide/catalyst ratio of 20 000/1. Our new results were superior to those obtained from all other previously published catalysts yielding cyclic poly(L-lactide). The seven-membered cycles also proved to be more active than tin(II) 2-ethylhexanoate with and without the addition of alcohol. KW - Lactide KW - Cyclization KW - Ring-expansion polymerization KW - Tin(II)octanoate KW - MALDI-TOF MS PY - 2019 U6 - https://doi.org/10.1016/j.eurpolymj.2019.04.024 SN - 0014-3057 SN - 1873-1945 VL - 116 SP - 256 EP - 264 PB - Elsevier Ltd. AN - OPUS4-47794 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lahcini, M. A1 - Weidner, Steffen A1 - Oumayama, J. A1 - Scheliga, F. A1 - Kricheldorf, H. R. T1 - Unsaturated Copolyesters of Lactide N2 - Four classes of unsaturated copolyesters of L-lactide were prepared either from isosorbide or bis(hydroxymethyl)tricyclodecane in combination with fumaric acid or from 1,4-butenediol or 1,4- butynediol with terephthalic acid. All syntheses were performed in such a way that lactide was oligomerized with a diol as the initiator and the resulting oligomers were polycondensed with a dicarboxylic acid dichloride either in a one-pot synthesis or in a two-step procedure. For most copolyesters the SEC measurements gave weight average molecular weights in the range of 30–60 kg mol⁻1 and dispersities in the range of 4.2–6.2. The MALDI-TOF mass spectra displayed a high content of cycles and indicated an irreversible kinetic course of all polycondensations. Glass-transition temperatures (Tg) above 90 °C were only found for two copolyesters of isosorbide. Addition of bromine to copolyesters of 1,4-butenediol yielded flame retarding biodegradable polymers. KW - Copolyester KW - MALDI-TOF MS KW - SEC KW - Lactide PY - 2016 U6 - https://doi.org/10.1039/c6ra16008e VL - 2016/6 IS - 96 SP - 93496 EP - 93504 PB - Royal Society of Chemistry AN - OPUS4-37913 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H.R. A1 - Mix, Renate A1 - Weidner, Steffen T1 - Poly(ester urethane)s derived from lactide, isosorbide, terephthalic acidm abd various diisocyanates N2 - Isosorbide-initiated oligomerizations of ʟ-lactide were preformed in bulk using SnCl2 as catalyst. The resulting telechelic OH-terminated oligoesters were in situ subjected to simultaneous polycondensation and polyaddition with mixtures of terephthaloyl chloride and diisocyanates. Most polymerizations were conducted with 4,4'-diisocyanatodiphenyl methane and 2,4-diisocyanato toluene. The consequences of excess diisocyanate and four different catalysts were studied. The isosorbide/lactide ratio and the terephthalic acid/diisocyanate ratio were varied. Number average molecular weights up to 15 kDa with polydispersities around 3–5 were obtained. Depending on the chemical structure of the copolyester and on the feed ratio, incorporation of urethane groups may reduce or enhance the glass-transition temperature, but the thermal stability decreases dramatically regardless of composition. KW - Cyclization KW - Isosorbide KW - Lactide KW - Polyaddition KW - Polycondensation KW - Polyesters KW - Polyurethanes PY - 2014 U6 - https://doi.org/10.1002/pola.27069 SN - 0360-6376 SN - 0887-624X VL - 52 IS - 6 SP - 867 EP - 875 PB - Wiley CY - Hoboken, NJ AN - OPUS4-30299 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H.R. A1 - Weidner, Steffen T1 - High Tg copolyesters of lactide, isosorbide and isophthalic acid N2 - Using SnCl2, ZnCl2, Zn-lactate or Zr-acetylacetonate as catalysts ʟ-lactide was oligomerized in bulk with isosorbide as initiator. The ratio isosorbide/lactide was varied from 8/2 to 2/8. The resulting oligomers were in situ polycondensed with isophthaloyl chloride in various aromatic solvents. In chlorobenzene homogeneous reaction mixtures were obtained, whereas molten copolyesters precipitated from toluene and xylene. The obtained average molecular weights indicated high polydispersities. According to MALDI-TOF MS the low molar mass reaction products (<4 kDa) almost exclusively consisted of cyclics with a composition depending on the feed ratio. The glass-transition temperatures (Tg) varied between the values of poly(ʟ-lactide (64 °C) and poly(isosorbide isophthalate) (180 °C). Four polyesters prepared from 5-tert-butyl isophthalic acid displayed higher Tg values. Differential thermoanalysis evidenced that the thermostability decreases with higher fractions of lactide, but processing from the melt seems to be feasible up to temperatures of 260 °C without risking degradation. KW - Lactide KW - Isosorbide KW - Ring-opening polymerization KW - Polycondensation KW - Cyclization PY - 2013 U6 - https://doi.org/10.1016/j.eurpolymj.2013.05.007 SN - 0014-3057 SN - 1873-1945 VL - 49 IS - 8 SP - 2293 EP - 2302 PB - Elsevier CY - Oxford AN - OPUS4-29014 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -