TY - JOUR A1 - Weidner, Steffen A1 - Meyer, Andreas A1 - Falkenhagen, Jana A1 - Kricheldorf, Hans R. T1 - Cyclic polyglycolide by means of metal acetylacetonates N2 - Glycolide was polymerized in bulk at 160 °C using various metal acetylacetonates as catalysts. Zirconium acetylacetonate was particularly efficient, enabling rapid polymerization even at 130 °C. The formation of cyclic poly(glycolic acid) (PGA), most likely via a ring-expansion polymerization (REP) mechanism, was proven by matrix-assisted laser desorption/ionization time-of-flight (MALDI-TOF) mass spectrometry. Depending on the polymerization conditions, the formation of even-numbered cycles was favored to varying degrees. Number-average molecular weights (Mn) in the range of 2000–3500 g mol−1 were achieved with dispersities below 2.0. Wide-angle X-ray scattering (WAXS) powder patterns showed that the crystal lattice was the same as that of known linear PGAs, regardless of the Mn values. These patterns enabled a comparison of crystallinities with values derived from DSC measurements. KW - MALDI-TOF MS KW - Polyglycolide KW - Crystallization KW - Small-angle X-ray scattering KW - Cyclization PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-653731 DO - https://doi.org/10.1039/d5ra07961f SN - 2046-2069 VL - 16 IS - 2 SP - 1757 EP - 1764 PB - Royal Society of Chemistry (RSC) AN - OPUS4-65373 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H. R. A1 - Weidner, Steffen A1 - Falkenhagen, Jana T1 - The role of transesterifications in reversible polycondensations and a reinvestigation of the Jacobson-Beckmann-Stockmayer experiments N2 - The polycondensations of adipic acid and 1,10-decanediol catalyzed by toluene sulfonic acid (TSA) were reinvestigated using MALDI TOF mass spectrometry and NMR spectroscopy. Unexpected reactions of TSA were detected along with incomplete conversion of the monomers. Furthermore, transesterification reactions of end-capped poly(1,10-decanediol adipate) and end-capped poly(ε-caprolactone) catalyzed by TSA were studied. Despite the quite different (ionic) reaction mechanisms, it was found that for polycondensations performed in bulk intermolecular transesterification is more efficient than the intramolecular “back-biting”; this scenario was not considered in the Jacobson–Stockmayer theory of reversible polycondensations. These results also confirm that the Jacobson–Stockmayer explanation of reversible polycondensations solely on the basis of ring chain equilibration is not only devoid of any experimental evidence, but also in contradiction to the results elaborated in this work. KW - Polylactide KW - MALDI-TOF MS KW - Polycondensation PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-543402 DO - https://doi.org/10.1039/d1py01679b SN - 1759-9962 SP - 1 EP - 9 PB - RSC Publ. CY - Cambridge AN - OPUS4-54340 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weidner, Steffen A1 - Falkenhagen, Jana A1 - Krüger, Ralph-Peter A1 - Just, Ulrich T1 - Principle of Two-Dimensional Characterization of Copolymers N2 - Two-dimensional polymer characterization is used for a simultaneous analysis of molar masses and chemical heterogeneities (e.g., end groups, copolymer composition, etc.). This principle is based on coupling of two different chromatographic modes. Liquid adsorption chromatography at critical conditions (LACCC) is applied for a separation according to the chemical heterogeneity, whereas in the second-dimension fractions are analyzed with regard to their molar mass distribution by means of size exclusion chromatography (SEC). Because appropriate standards for a calibration of the SEC are seldom available, matrix-assisted laser desorption/ionization-time-of-flight mass spectrometry (MALDI-TOF MS) was used to substitute the SEC. The LACCC-MALDI MS coupling enables acquiring additional structural information on copolymer composition, which can considerably enhance the performance of this coupled method. KW - MALDI-TOF MS KW - Chromatographie KW - Kopplung PY - 2007 DO - https://doi.org/10.1021/ac062145f SN - 0003-2700 SN - 1520-6882 VL - 79 IS - 13 SP - 4814 EP - 4819 PB - American Chemical Society CY - Washington, DC AN - OPUS4-17722 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H. R. A1 - Weidner, Steffen A1 - Falkenhagen, Jana T1 - Reversible Polycondensations outside the Jacobson-Stockmayer Theory and a New Concept of Reversible Polycondensations N2 - L-Lactide was polymerized with tin(II)acetate, tin(II)2-ethyl hexanoate, diphenyltin dichloride and dibutyltin bis(pentafluorophenoxide) at 130 °C in bulk. When an alcohol was added as initiator, linear chains free of cycles were formed having a degree of polymerization (DP) according to the lactide/initiator (LA/In) ratio. Analogous polymerizations in the absence of an initiator yielded high molar mass cyclic polylactides. Quite similar results were obtained when ε-caprolactone was polymerized with or without initiator. Several transesterification experiments were conducted at 130 °C, either with polylactide or poly(ε-caprolactone) indicating that several transesterification mechanisms are operating under conditions that do not include formation of cycles by back-biting. Furthermore, reversible polycondensations (revPOCs) with low or moderate conversions were found that did not involve any kind of cyclization. Therefore, These results demonstrate the existence of revPOCs, which do neither obey the theory of irreversible polycondensation as defined by Flory nor the hypothesis of revPOCs as defined by Jacobson and Stockmayer. A new concept encompassing any kind of revPOCs is formulated in the form of a “polycondensation triangle”. KW - Polylactide KW - MALDI-TOF MS KW - Polycondensation PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-530831 DO - https://doi.org/10.1039/d1py00704a VL - 12 IS - 35 SP - 5003 EP - 5016 PB - Royal Society for Chemistry AN - OPUS4-53083 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weidner, Steffen A1 - Meyer, A. A1 - Falkenhagen, Jana A1 - Kricheldorf, H. R. T1 - Polycondensations and Cyclization of Poly(L-lactide) Ethyl Esters in the Solid State N2 - The usefulness of seven different Tin catalysts, Bismuth subsalicylate and Titan tetra(ethoxide) for the polycondensation of ethyl L-lactate (ELA) was examined at 150 °C/6 d. Dibutyltin bis(phenoxides) proved to be particularly effective. Despite the low reactivity of ELA, weight average molecular masses (Mw) up to 12 500 were found along with partial crystallization. Furthermore, polylactides (PLAs) of similar molecular masses were prepared via ELA-initiated ROPs of L-lactide by means of the four most effective polycondensation catalysts. The crystalline linear PLAs were annealed at 140 or 160 °C in the presence of these catalysts. The consequences of the transesterification reactions in the solid PLAs were studied by means of matrix-assisted laser desorption/ionization (MALDI TOF) mass spectrometry, gel permeation chromatography (GPC) and small-angle X-ray scattering (SAXS). The results indicate that polycondensation and formation of cycles proceed in the solid state via formation of loops on the surface of the crystallites. In summary, five different transesterification reactions are required to explain all results. KW - Polylactide KW - MALDI-TOF MS KW - Crystalinity PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-592934 DO - https://doi.org/10.1039/d3py01232h SN - 1759-9962 VL - 15 IS - 2 SP - 71 EP - 82 PB - RSC Publ. CY - Cambridge AN - OPUS4-59293 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Scholz, Philipp A1 - Wachtendorf, Volker A1 - Panne, Ulrich A1 - Weidner, Steffen ED - Scholz, Philipp T1 - Degradation of MDI-based polyether and polyester-polyurethanes in various environments - Effects on molecular mass and crosslinking N2 - Size-exclusion chromatography (SEC) was used to monitor changes of the molecular masses of thermoplastic polyether – and polyester urethane (TPU) exposed to thermal, hydrolytic, and photo-oxidative (UV) Degradation conditions for several days. The thermal treatment was performed at elevated temperatures (100–200 °C) under oxidative (air) as well as non-oxidative (nitrogen) conditions to evaluate the specific influence of oxygen on the degradation. At higher temperatures (≥175 °C) a fast decrease of the molecular masses of both PU accompanied by a high degree of crosslinking was found. At lower temperatures (≤150 °C) the polymers remained widely unaffected by thermal degradation within the investigated degradation interval of up to two weeks. Surprisingly, the influence of oxygen (air) was found to be less distinct. In contrast to that, UV treatment at 25 °C at less than 10% rel. humidity (RH) resulted in a fast crosslinking, whereas the molecular masses of both PU decreased slower than for thermal treatments. The depth of penetration of the UV radiation was estimated using 3D printed PU samples with different thicknesses. Hydrolysis based degradation effects were less significant. Only slight molecular mass changes were detected at temperatures ≤80 °C within a time span of 14 days, while no crosslinking could be measured. Considering the degradation results at the investigated exposure parameters, it could be shown that esterbased PU in general exhibits a significant higher stability compared to ether-based materials. KW - Polyurethane KW - Thermal degradation KW - UV degradation KW - Molecular masses KW - Crosslinking PY - 2019 UR - https://www.sciencedirect.com/science/article/pii/S0142941819302363 DO - https://doi.org/10.1016/j.polymertesting.2019.04.028 SN - 0142-9418 VL - 77 SP - 105881, 1 EP - 12 PB - Elsevier CY - Amsterdam AN - OPUS4-48619 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lahcini, M. A1 - Qayouh, H. A1 - Yashiro, T. A1 - Weidner, Steffen A1 - Kricheldorf, H.R. T1 - Bismuth-triflate-catalyzed polymerizations of epsilon-caprolactone N2 - εCL was polymerized using the triflates of lanthanum, samarium, magnesium, aluminum, scandium, and bismuth as catalysts. Bismuth triflate proved to be extraordinarily reactive, and catalyzed polymerizations of εCL even at 20 °C. Adding DTBMP reduced the polymerization rate only slightly. Furthermore, no evidence of a cationic mechanism was found by end‐group analyses. Polymerization at 20 °C either in bulk or in solution only yielded polyesters of low or medium molecular weights. Yet addition of alcohols allowed for a proper control of molecular weight and end‐groups. Additionally, low catalyst concentrations and low temperature resulted in narrow molecular weight distributions and polylactones almost free of cyclic compounds. KW - Bismuth KW - Epsilon-caprolactone KW - Ring-opening polymerization KW - Telechelic polyesters PY - 2011 DO - https://doi.org/10.1002/macp.201000517 SN - 1022-1352 SN - 1521-3935 VL - 212 IS - 6 SP - 583 EP - 591 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-23514 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wettmarshausen, Sascha A1 - Friedrich, Jörg Florian A1 - Meyer-Plath, Asmus A1 - Kalinka, Gerhard A1 - Hidde, Gundula A1 - Weidner, Steffen T1 - Coating of carbon fibers with adhesion-promoting thin poly(acrylic acid) and poly(hydroxyethylmethacrylate) layers using electrospray ionization N2 - Thin coatings of poly(acrylic acid) (PAA) and poly(hydroxyethylmethacrylate) (PHEMA) were deposited onto carbon fibers by means of the electrospray ionization (ESI) technique in ambient air. These high-molecular weight polymer layers were used as adhesion promoters in carbon fiber–epoxy resin composites. Within the ESI process, the carbon fibers were completely enwrapped with polymer in the upper 10 plies of a carbon fiber roving. As identified with scanning electron microscopy also shadowed fibers in a bundle as well as backsides of fiber rovings were pinhole-free coated with polymers (‘electrophoretic effect'). Under the conditions used, the layers have a granular structure. Residual solvent was absent in the deposit. PAA and PHEMA films did not show any changes in composition and structure in comparison with the original polymers as analyzed by X-ray photo-electron spectroscopy and matrix-assisted laser desorption/ionization time-of-flight mass spectrometry. Single-fiber pullout tests of coated fibers embedded in epoxy resin showed significantly increased interfacial shear strength. It is assumed that chemical bonds between carbon fiber poly(acrylic acid) and epoxy resin contribute significantly to the improved interactions. KW - Adhesion promotion KW - Thin polymer layers KW - Electrospray ionization (ESI) KW - Carbon fiber–epoxy resin laminates KW - Layer topography PY - 2015 DO - https://doi.org/10.1080/01694243.2015.1040980 SN - 0169-4243 SN - 1568-5616 VL - 29 IS - 15 SP - 1628 EP - 1650 PB - VNU Science Press CY - Utrecht AN - OPUS4-34564 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Chatti, S. A1 - Weidner, Steffen A1 - Fildier, A. A1 - Kricheldorf, H.R. T1 - Copolyesters of isosorbide, succinic acid, and isophthalic acid: biodegradable, high Tg engineering plastics N2 - Isosorbide, succinyl chloride and isophthaloyl chloride are polycondensed under various reaction conditions. The heating in bulk with or without catalysts as well in an aromatic solvent without catalyst, and polycondensation with the addition of pyridine only yield low molar mass copolyesters. However, heating in chlorobenzene with addition of SnCl2 or ZnCl2 produces satisfactory molar masses. The number average molecular weights (Mn) of most copolyesters fall into the range of 7000–15,000 Da with polydispersities (PD) in the range of 3–9. The MALDI-TOF mass spectra almost exclusively displayed peaks of cyclics indicating that the chain growth was mainly limited by cyclization and not by side reactions, stoichiometric imbalance or incomplete conversion. The glass-transition temperatures increased with the content of isophthalic acid from 75 to 180 °C and the thermo-stabilities also followed this trend. KW - Biodegradable KW - Cyclization KW - Cyclopolymerization KW - Isophthalic acid KW - Isosorbide KW - Polycondensation KW - Polyesters KW - Renewable resources KW - Succinic acid PY - 2013 DO - https://doi.org/10.1002/pola.26635 SN - 0360-6376 SN - 0887-624X VL - 51 IS - 11 SP - 2464 EP - 2471 PB - Wiley CY - Hoboken, NJ AN - OPUS4-28577 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gille, M. A1 - Viertel, A. A1 - Weidner, Steffen A1 - Hecht, S. T1 - Modular synthesis of monomers for on-surface polymerization to graphene architectures N2 - We developed a modular synthesis of halogenated polycyclic aromatic monomers for on-surface polymerization to generate graphene wires, ribbons, and networks. KW - Graphene monomers KW - Graphene nanoribbons KW - Functionalized graphene nanoribbons KW - Graphene wires KW - Hexabenzocoronene KW - On-surface polymerization PY - 2013 DO - https://doi.org/10.1055/s-0032-1317959 SN - 0936-5214 SN - 1437-2096 VL - 24 IS - 2 SP - 0259 EP - 0263 PB - Thieme CY - Stuttgart AN - OPUS4-27621 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -