TY - CONF A1 - Trubiroha, P. A1 - Geburtig, Anja A1 - Wachtendorf, Volker ED - Reichert, T. T1 - Surface temperatures of irradiated test specimens - decisive physical quantities and a largely unsolved problem N2 - Temperature is an important parameter in weathering tests. In many (photo-)chemical degradation processes a Variation of the specimen temperature by A t = + 1 °C can cause a Variation of AP(property change) by ± 8%. Since the early eighties it is well known that some types of black panel thermometers can show temperatures that are far below the maximum surface temperature of a black specimen. Although, there were precise requirements for the black coating of the BPT, a replacement by a white coating - depending on the design of the BPT - did not really change the temperature shown by the thermometer. There was no correlation between the BPT and the specimen surface temperature. In Europe and later at ISO the so-called black- and white-standard thermometers BST/WST were introduced. Now, there are BST and WST (ISO) and there are thermally uninsulated and insulated BPT and WPT (ASTM), partly for artificial or for outdoor exposure. And there are other adventurous procedures to determine surface temperatures. The different types of thermometers and different procedures will be discussed and it will be shown that there is no procedure which establishes a correlation between outdoor surface temperatures and surface temperatures in artificial exposure tests. T2 - 6th European weathering symposium Natural and artificial ageing of polymers CY - Bratislava, Slovak Republic DA - 11.09.2013 PY - 2013 SN - 978-3-9813136-8-0 N1 - Serientitel: CEEES Publication – Series title: CEEES Publication IS - 16 SP - 185 EP - 194 AN - OPUS4-31292 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Geburtig, Anja A1 - Wachtendorf, Volker A1 - Trubiroha, P. A1 - Zäh, M. A1 - Schönlein, A. A1 - Müller, A. A1 - Vatahska, T. A1 - Manier, G. A1 - Reichert, T. ED - White, C. C. ED - Martin, J. ED - Chapin, J.T. T1 - Polypropylene numerical photoageing simulation by dose-response functions with respect to irradiation and temperature: vipquali project N2 - The aim of the joint project ViPQuali (Virtual Product Qualification) was to describe a component’s ageing behaviour in a given environment, by numerical simulation. Having chosen polypropylene (PP) as the material, which does not show sensitivity to moisture, the relevant weathering parameters of the dose–response functions could be limited to spectral irradiance and temperature. In artificial irradiation tests, for PP plates of varied stabiliser content, spectral sensitivity as well as temperature dependence of irradiation-caused crack formation was quantified. For that purpose, samples were exposed both to artificial weathering tests at various constant temperatures and to spectrally resolved irradiation. The temperature dependence could be modelled by an Arrhenius fit. For fitting the spectral sensitivity, a plateau function was chosen. Subsequently, the stabiliser content was parameterised and extrapolated. The formed dose–response functions were incorporated into a Computational Fluid Dynamics (CFD) software program, simulating the environment of a sample within a Phoenix-exposed IP/DP (Instrument Panel/Door Panel box) box, based on sun position and weather conditions, including radiation interactions. Observed local effects as well as the general ageing advance of PP hats are compared with respect to simulation and experiment. Resulting from this project, for this most simple example of PP of varied stabiliser content, the time to failure can be estimated for each weathering exposure environment with known time-resolved irradiance and temperature conditions. PY - 2015 SN - 978-3-319-06033-0 SN - 978-3-319-06034-7 DO - https://doi.org/10.1007/978-3-319-06034-7_14 SP - Chapter 14, 215 EP - 229 PB - Springer AN - OPUS4-32062 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wachtendorf, Volker T1 - Schadensanalyse im Bauwesen: Untersuchungen zu witterungsbedingten Schäden an einer polymeren Stadionverglasung T2 - PolymerTec 2014 (Veranstalter: Kunststoff-Kompetenzzentrum Halle-Merseburg, Insitut für Polymerwerkstoffe e. V.; Stiftung Akademie Mitteldeutsche Kunststoffinnovationen, Hochschule Merseburg) CY - Merseburg, Germany DA - 2014-06-25 PY - 2014 AN - OPUS4-30953 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Appajaiah, Anilkumar A1 - Wachtendorf, Volker A1 - Daum, Werner T1 - Climatic exposure of polymer optical fibers: Thermooxidative stability characterization by chemiluminescence N2 - The optical transmission stability was investigated for commercially available polymer optical fibers (POFs) which were exposed to a climate of 92°C and 95% relative humidity for about 3300 h. The optical transmission stability of POFs was correlated to their thermooxidative stability. POFs possessed identical core material, poly(methyl methacrylate), but they differed in the materials used for the claddings. The optical transmission was measured online using a prototype device called multiplexer. The chemiluminescence (CL) technique was applied to characterize the thermooxidative stability and degradation of POFs. CL analysis reveals the thermooxidative degradation of bare POFs (core and cladding), predominantly of the claddings, as a result of climatic exposure. Ultraviolet-visible transmittance measurements demonstrated more changes in the claddings as compared to the cores due to degradation. The CL and optical measurements data indicated that the optical transmission stability of POFs was dependent mainly on the thermooxidative stability of the claddings and their chemical compositions. KW - Ageing KW - Polymer optical fiber KW - Degradation KW - Chemiluminescence KW - Transparency PY - 2007 DO - https://doi.org/10.1002/app.23955 SN - 0021-8995 SN - 1097-4628 VL - 103 IS - 3 SP - 1593 EP - 1601 PB - Wiley InterScience CY - Hoboken, NJ AN - OPUS4-19072 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wachtendorf, Volker A1 - Geburtig, Anja T1 - Künstliche Bewitterungstests für polymere Beschichtungen T2 - TAW Symposium: "3. Korrosionsschutz-Symposium - Korrosionsschutz durch Beschichtungen in Theorie und Praxis" CY - Titisee-Neustadt, Germany DA - 2009-06-17 PY - 2009 AN - OPUS4-19590 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wachtendorf, Volker A1 - Geburtig, Anja A1 - Trubiroha, Peter T1 - Spezifische Witterungsempfindlichkeiten verschiedener Kunststoffe im Außenbereich T2 - SKZ Fachtagung "Bewitterung von Kunststoffen und Lacken" CY - Würzburg, Germany DA - 2009-03-04 PY - 2009 AN - OPUS4-19591 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geburtig, Anja A1 - Wachtendorf, Volker A1 - Trubiroha, Peter T1 - Accelerated weathering test for plastics and coatings that are exposed to acidic precipitation T2 - 7th International Symposium on Weatherability (Proceedings ) CY - Yokohama, Japan DA - 2008-10-23 KW - Acid rain KW - ADF KW - Acid dew and fog test KW - Artificial weathering test PY - 2008 SP - 49 EP - 54 CY - Yokohama AN - OPUS4-21116 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wachtendorf, Volker A1 - Geburtig, Anja T1 - Chemiluminescence for the early detection of weathering effects of coatings - Part I: Fundamentals KW - Chemiluminescence KW - Weathering KW - Polymer KW - Oxidation PY - 2010 SN - 1547-0083 VL - 7 IS - 4 SP - 66 EP - 71 PB - Federation of Societies for Coatings Technology CY - Blue Bell, Pa. AN - OPUS4-21493 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wachtendorf, Volker A1 - Geburtig, Anja T1 - Chemiluminescence for the early detection of weathering effects of coatings - Part II: Experimental set-up and examination KW - Chemiluminescence KW - Weathering KW - Polymer KW - Oxidation PY - 2010 SN - 1547-0083 VL - 7 IS - 5 SP - 38 EP - 44 PB - Federation of Societies for Coatings Technology CY - Blue Bell, Pa. AN - OPUS4-21494 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Geburtig, Anja A1 - Wachtendorf, Volker T1 - Determination of the spectral sensitivity and temperature dependence of polypropylene crack formation caused by UV-irradiation N2 - For polypropylene of varied stabilization, spectral sensitivity as well as temperature dependence of irradiation caused crack formation was determined in artificial irradiation tests. UV radiant exposure HUV necessary to generate crack formation was measured both in spectrally dispersed irradiation and artificial irradiation in a Fluorescent UV lamp device. Dependencies were fitted to a plateau function and an Arrhenius function, respectively, to describe the action of irradiation by response functions. Applied to weather data from Phoenix, the results were compared with respective outdoor exposure results. KW - Weathering KW - UV KW - Temperature KW - Numerical simulation PY - 2010 DO - https://doi.org/10.1016/j.polymdegradstab.2010.06.014 SN - 0141-3910 SN - 1873-2321 VL - 95 IS - 10 SP - 2118 EP - 2123 PB - Applied Science Publ. CY - London AN - OPUS4-21913 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Wachtendorf, Volker A1 - Geburtig, Anja T1 - Alterungsvorgänge durch Bewitterung bei Beschichtungen und deren Untersuchung und Prüfung T2 - 42. Fortbildungskurs SAH - Holzoberflächen in der Fassadengestaltung CY - Weinfelden, Schweiz DA - 2010-10-26 KW - Bewitterung KW - Alterung KW - Holz PY - 2010 SN - 978-3-906703-26-8 SP - 29 EP - 38 CY - Zürich, Schweiz AN - OPUS4-22601 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wachtendorf, Volker A1 - Damerau, T. A1 - Hennecke, Manfred T1 - Degradation of poly(phenylphenylene-vinylene)-films during illumination and thermal treatment T2 - 5th Polymer Federation Symposium on Polymer Materials CY - Basel, Switzerland DA - 1994-10-09 PY - 1994 AN - OPUS4-23133 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geburtig, Anja A1 - Wachtendorf, Volker ED - Ziegahn, K.-F. T1 - Lebensdauerabschätzungen für Polypropylen durch Dosis-Wirkungsfunktionen bezüglich Bestrahlungsstärke und Temperatur (ViPQuali-Projekt) N2 - Für Polypropylen unterschiedlicher Stabilisierung wurden in künstlichen Bestrahlungstests sowohl die spektrale Empfindlichkeit als auch die Temperaturabhängigkeit der Rissbildung quantitativ ermittelt. Dafür wurde die Dauer bis zur Rissbildung sowohl bei spektraler Bestrahlung als auch bei Bestrahlung in einem UV-Leuchtstofflampengerät bei verschiedenen Temperaturen bestimmt. Die Temperaturabhängigkeit konnte als Arrhenius-Abhängigkeit beschrieben werden; das Wirkungsspektrum wurde an eine Stufenfunktion angepasst. Anschließend wurde auch noch der Einfluss des Stabilisatorgehalts als Potenzfit parametrisiert. Die Einzelabhängigkeiten wurden zu einer Gesamtfunktion der Wirkungen in Abhängigkeit der Dosis zusammengesetzt, die es ermöglicht die Wirkungen unterschiedlicher Dosiskombinationen abzuschätzen. Zur Validierung der Dosis-Wirkungsfunktionen wurden Freibewitterungsergebnisse aus Phoenix/Arizona herangezogen. Mit der Dosis, die sich aus den Wetterdaten dieser Freibewitterung ergibt, wurden anhand der Dosis-Wirkungs-Funktionen die jeweiligen Lebensdauern errechnet und mit dem experimentell bestimmten Versagen in der Freibewitterung verglichen. Die Arbeiten erfolgten im Rahmen des ViPQuali-Projektes mit dem Ziel der Bestimmung der Materialkenngrößen. T2 - 40. Jahrestagung der GUS 2011 - Umwelteinflüsse erfassen, simulieren, bewerten CY - Stutensee-Blankenloch/Karlsruhe, Germany DA - 30.03.2011 KW - Bewitterung KW - UV KW - Lebensdauer KW - Simulation KW - Polypropylen PY - 2011 SN - 978-3-9813136-1-1 IS - V17 SP - 227 EP - 237 PB - DWS Werbeagentur und Verlag GmbH CY - Karlsruhe AN - OPUS4-23474 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Maskos, Michael A1 - Berger, Georg A1 - Braun, Ulrike A1 - Heyn, Andreas A1 - Klinger, Christian A1 - Wachtendorf, Volker T1 - Schadensanalyse und Beständigkeit von Materialien in biomedizinischen Einsatzgebieten N2 - Der Anteil von Polymeren als Funktions- und Konstruktionswerkstoffe in dauerhaften medizinischen Anwendungen steigt beständig. Derartige Materialien müssen den mechanischen, biologischen und chemischen Bedingungen im Körper widerstehen (u.a. Abrieb, Hydrolyse, Degradation) und gleichzeitig gut verträglich sein. Der sichere Einsatz von polymeren Materialien erfordert die Kenntnisse über ihre Langzeitstabilität unter verschiedenen äußeren Bedingungen. Diese sind nicht nur beeinflusst durch die unmittelbare Umgebung in vivo, sondern auch durch die Historie der verwendeten Materialien. Dazu zählen u. a. erhöhte Temperaturen unter sauerstoffhaltiger Atmosphäre während der Verarbeitung oder die Exposition von ionisierender Strahlung oder reaktiven Radikalen während der Sterilisation. PY - 2011 SP - 83 EP - 85 CY - Berlin AN - OPUS4-23592 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wachtendorf, Volker A1 - Geburtig, Anja T1 - Chancen und Grenzen der Verkürzung von Bewitterungstests durch empfindliche Chemilumineszenz-Detektion T2 - DFO Qualitätstage 2008, Appearance, Bewitterung, Korrosion, Farbe CY - Fürth, Germany DA - 2008-10-07 PY - 2008 AN - OPUS4-18710 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Geburtig, Anja A1 - Wachtendorf, Volker A1 - Trubiroha, Peter T1 - Aussagekraft von Korrelationskoeffizienten T2 - 38. Jahrestagung der GUS CY - Stutensee-Blankenloch/Karlsruhe, Deutschland DA - 2009-03-18 KW - Witterungsbeständigkeit KW - Korrelation KW - Künstliche Bewitterung PY - 2009 SN - 978-3-9810472-7-1 SP - 61 EP - 70 CY - Pfinztal (Berghausen) AN - OPUS4-19161 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Geburtig, Anja A1 - Wachtendorf, Volker A1 - Trubiroha, Peter T1 - Systematisierung der Alterungsvorgänge bei der Bewitterung von Polymerwerkstoffen T2 - 38. Jahrestagung der GUS CY - Stutensee-Blankenloch/Karlsruhe, Deutschland DA - 2009-03-18 KW - Witterungsbeständigkeit KW - Photochemische Alterung PY - 2009 SN - 978-3-9810472-7-1 SP - 51 EP - 60 CY - Pfinztal (Berghausen) AN - OPUS4-19162 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Geburtig, Anja A1 - Wachtendorf, Volker A1 - Trubiroha, Peter T1 - Correlations in weathering results T2 - 4th European weathering symposium - Natural and artificial ageing of polymers CY - Budapest, Hungary DA - 2009-09-16 KW - Witterungsbeständigkeit KW - Korrelation KW - Künstliche Bewitterung KW - Artificial weathering PY - 2009 SN - 978-3-9810472-8-8 IS - Publication 11 SP - 251 EP - 261 PB - DWS Werbeagentur und Verlag GmbH CY - Karlsruhe AN - OPUS4-20020 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wachtendorf, Volker A1 - Geburtig, Anja A1 - Trubiroha, Peter T1 - Alterung von Polymeren durch Witterungsbeanspruchung T2 - 25. Darmstädter Kunststoff-Kolloquium, "Schadensanalytik heute - Methoden und Anwendungen" CY - Darmstadt, Germany DA - 2009-09-10 PY - 2009 AN - OPUS4-20573 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Wachtendorf, Volker A1 - Geburtig, Anja A1 - Trubiroha, Peter ED - Ziegahn, K.-F. T1 - Grundsätzliches zur Verkürzung von Bewitterungstests durch künstliche Bewitterung T2 - 35. Jahrestagung der GUS 2006 - Umwelteinflüsse erfassen, simulieren, bewerten CY - Pfinztal, Deutschland DA - 2006-03-22 PY - 2006 SN - 3-9810472-0-6 SP - 165 EP - 175 PB - DWS Werbeagentur und Verlag GmbH CY - Pfinztal AN - OPUS4-21345 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -