TY - CONF A1 - Wachtendorf, Volker A1 - Schulz, Ulrich T1 - Shortening of Weathering Tests for Automotive Coatings by Chemiluminescence Detection T2 - 27th FATIPEC Congress CY - Aix-en-Provence, France DA - 2004-04-19 KW - Chemiluminescence KW - Artificial weathering KW - ADF KW - Automotive coatings KW - Chemilumineszenz KW - Künstliche Bewitterung KW - Automobillacke PY - 2004 VL - 3 SP - 931 EP - 940 PB - Association Francaise des Techniciens des Peintures, Vernis,Encres CY - Aix en Provence AN - OPUS4-3561 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brademann-Jock, Kerstin A1 - Krüger, Simone A1 - Wachtendorf, Volker A1 - Goering, Harald T1 - Degradation effects of automotive coatings after weathering as detected by thermoluminescence T2 - 27th FATIPEC Congress CY - Aix-en-Provence, France DA - 2004-04-19 KW - Automobillacke KW - Bewitterung KW - Thermolumineszenz KW - Automotive coatings KW - Weathering KW - Thermoluminescence PY - 2004 VL - 3 SP - 1045 EP - 1050 PB - Association Francaise des Techniciens des Peintures, Vernis,Encres CY - Aix en Provence AN - OPUS4-4054 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ramanujam, Maalolan A1 - Wachtendorf, Volker A1 - Purohit, Purv A1 - Mix, Renate A1 - Schönhals, Andreas A1 - Friedrich, Jörg Florian T1 - A detailed dielectric relaxation spectroscopy study of artificial UV weathered low density polyethylene N2 - Artificial weathering of LDPE under dry conditions (<10% of relative humidity) by UV radiation was monitored by dielectric spectroscopy. For an apolar polymer like LDPE, dielectric study yields information about the change in structure and dynamics of the system. The fluctuations of the polar groups which are generated as a result of photooxidation such as carbonyl groups can be monitored as characteristic relaxation processes like the αc or β mode. The dielectric loss characterized by typical dielectric parameters like the activation energy and dielectric strength are strongly dependent upon changes induced by photooxidation in the amorphous and crystalline domains. This paper discusses in detail how the foil reached its mechanical disintegration. It was found that initial stages of weathering induce chain scission and/or crosslinking in the amorphous domains of the polymer and the motional processes in the crystalline regions are not affected. After this induction period, an increase in the degree of crystallization was observed by employing differential calorimetry. The increasing crystallinity is considered as one of the reasons for embrittlement which finally leads to the complete loss of the structural integrity. KW - Artificial weathering KW - UV radiation KW - Dielectric relaxation KW - LDPE PY - 2012 DO - https://doi.org/10.1016/j.tca.2011.12.003 SN - 0040-6031 SN - 1872-762X VL - 530 SP - 73 EP - 78 PB - Elsevier CY - Amsterdam AN - OPUS4-25547 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Krüger, Simone A1 - Wachtendorf, Volker A1 - Rauth, W. A1 - Klimmasch, T. A1 - Krüger, P. T1 - Screening the weathering stability of automotive coatings by chemiluminescence N2 - Chemiluminescence (CL) is a sensitive method of investigating the thermo-oxidative stability of polymers in the early stages of degradation. Therefore, CL measurements were applied to different automotive coatings to evaluate their degradation behavior during artificial weathering. In this work, CL measurements were carried out for different automotive coatings to follow their degradation behavior during artificial weathering. The CL emission depends on sample-specific parameters like stabilizer, matrix, or hardener; experimental parameters like the oxygen partial pressure; and exposure parameters like the duration of weathering. The potential of CL could be demonstrated by classifying materials into categories of good, medium, and low degradation performance at a much earlier stage of weathering exposure than in combination with the usual visual detection of weathering effects. KW - Accelerated weathering KW - Coating KW - Chemiluminescence KW - Sensitive detection KW - Weathering PY - 2008 DO - https://doi.org/10.1007/s11998-007-9071-7 SN - 1547-0091 SN - 1935-3804 VL - 5 IS - 1 SP - 17 EP - 24 PB - Springer CY - Blue Bell, Pa. AN - OPUS4-16723 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Appajaiah, Anilkumar A1 - Wachtendorf, Volker A1 - Daum, Werner T1 - Characterization of thermo-oxidative stability of polymer optical fibers using chemiluminescence technique N2 - The thermo-oxidative stability of commercially available polymer optical fibers (POFs) and their components (cores and claddings) was investigated. All the bare POFs (core and cladding only) studied here were based on poly(methyl methacrylate) (PMMA) core. The fibers were exposed to 100 °C/low humidity for about 4200 h. Chemiluminescence (CL) technique was applied to investigate the thermo-oxidative stability and for measuring the transmission loss during exposure a prototype device called multiplexer was used. POFs exhibited variation in thermo-oxidative stability although they possessed identical core material PMMA. This was due to difference in the chemical compositions of claddings. Claddings were more susceptible to the thermo-oxidative degradation compared to cores. The thermo-oxidative degradation of both the cladding and the core was found in POFs as a result of climatic exposure. POFs showed an early drop-off followed by a slow decline of transmission. The early drop-off of transmission was attributed to physical changes like thermal expansion and the slow decline of transmission to chemical changes like oxidative degradation of POFs. A good linear relationship between optical transmission stability and thermo-oxidative stability of POFs was established from these studies. KW - Polymer optical fibers (POFs) KW - Chemiluminescence (CL) KW - Thermo-oxidative stability KW - Aging KW - Optical transmission stability PY - 2006 DO - https://doi.org/10.1016/j.polymdegradstab.2006.05.006 SN - 0141-3910 SN - 1873-2321 VL - 91 IS - 11 SP - 2605 EP - 2613 PB - Applied Science Publ. CY - London AN - OPUS4-13984 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wachtendorf, Volker A1 - Geburtig, Anja T1 - Alterungseffekte bei Polymerwerkstoffen messen N2 - Bei der Auswahl von Werkstoffen spielt deren Alterung oft eine untergeordnete Rolle, stattdessen wird häufig der ungealterte Ausgangszustand optimiert. Materialien altern aber unterschiedlich. Der Effekt der molekularen Alterung spiegelt sich in den Eigenschaften mehr oder weniger stark und in unterschiedlichem zeitlichen Verlauf wider. Da es kein physikalisch-chemisches Modell dafür gibt, sind Alterungseffekte empirisch zu bestimmen. KW - Alterung KW - Polymerwerkstoff KW - Eigenschaftsänderung PY - 2012 DO - https://doi.org/10.1002/nadc.201290356 SN - 1439-9598 SN - 1521-3854 VL - 60 IS - 10 SP - 1018 EP - 1022 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-26666 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Geburtig, Anja A1 - Goedecke, Thomas A1 - Wachtendorf, Volker T1 - Combined impact of ultraviolet and chemical fluids on high-density polyethylene packaging material N2 - To investigate the ageing behaviour of filled plastic containers outdoors, square cuts of the wall of two high-density polyethylene (HDPE) types were exposed to ultraviolet (UV) radiation at their front side and to specific liquid chemicals (de-ionized water, surfactant or White Spirit) at their back. The UV radiant exposure at the front side was 80 MJ/m². To compare the actions of the different exposures, separate dark backside fluid exposures were performed, in parallel. Besides, UV weathering was carried out until a UV radiant exposure of 325 MJ/m², being roughly comparable to outdoor exposure of one year in Northern Australia. An unpigmented HDPE included in the investigation gave no sufficient protection for the White Spirit. In addition, it showed clear degradation after several of these exposures. In combination with the White Spirit, an increase of carbonyl bonds was measured, presumably assignable to degradation products of the White Spirit. For a pigmented HDPE material, with the implemented combined exposures, no relevant damage was observed, within applied the exposure period. KW - Weathering KW - UV KW - HDPE KW - Packaging PY - 2012 DO - https://doi.org/10.1002/pts.959 SN - 0894-3214 VL - 25 IS - 1 SP - 53 EP - 61 PB - Wiley CY - Chichester, UK AN - OPUS4-25417 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Geburtig, Anja A1 - Wachtendorf, Volker A1 - Schmidt, Anita A1 - Goedecke, Thomas T1 - Combined impact of UV radiation and nitric acid on HDPE containers during outdoor exposure T1 - Kombinierte Einwirkung von UV-Strahlung und Salpetersäure auf HDPE-Behälter bei der Freibewitterung N2 - Unpigmented HDPE jerrycans filled with nitric acid (55%) and water respectively had been exposed to outdoor conditions for one Berlin summer season. As both liquids underwent equal temperature progression, exposure effects of UV radiation and nitric acid as well as of their combination can be separated and compared. On the basis of various property changes after these exposures, synergistic action is evaluated and compared to a damaged Intermediate Bulk Container (IBC) from a transport accident. It is found that carbonyl formation goes along with lightness increase in color measurement due to microcracking and with a worsening in mechanical behavior, all of them showing synergistic effects of UV and nitric acid exposure. In contrast, embedding nitrogen compounds goes along with yellowing of the material but cannot be correlated to oxidation. The reason for intensified damaging is the decomposition of the 55-percent nitric acid and formation of nitrogen oxides even at ambient temperatures, caused by UV radiation. Thus, damaging effects become similar to those caused by fuming nitric acid exposure at temperatures above 60 °C, with the result of strong oxidative degradation of the polyethylene. In contrast, exclusive exposure to the 55-percent nitric acid at 40 °C does not cause any failure. It can therefore be assumed that also the damaged IBC had been exposed to both UV radiation and nitric acid, probably outdoors. KW - Polyethylene KW - Nitric acid KW - UV radiation KW - Outdoor weathering KW - Resistance PY - 2018 DO - https://doi.org/10.3139/120.111148 SN - 0025-5300 VL - 60 IS - 3 SP - 257 EP - 264 PB - Carl Hanser Verlag CY - München AN - OPUS4-44567 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wachtendorf, Volker A1 - Schulz, Ulrich A1 - Geburtig, Anja A1 - Stephan, Ina T1 - Mildew growth on automotive coatings influencing the results of outdoor weathering N2 - As the results of a 14 weeks outdoor exposure of a series of automotive coatings in South Florida, the panels were found to be overgrown with an almost closed layer of mildew. Pinholes remained as permanent surface damage after removing the mildew mycelium. The extent of the damage differed in dependence of the kind of the coating. By tracing the images and profiles of the coating surfaces systematically over all phases of weathering and the subsequent cleaning procedure, a connection between formation of pinholes and mildew growth could be found. Outdoor weathering tests in other regions of Florida as well as in Europe and Australia showed that pinholes caused by mildew attack could also be found in all other locations, but always to a lower extent than in South Florida. The standardised mildew tests EN ISO 846 and MIL-STD 810F for laboratory exposure failed to reproduce the formation of pinholes. KW - Coatings KW - Mildew KW - Weathering KW - South Florida PY - 2012 DO - https://doi.org/10.1002/maco.201005784 SN - 0947-5117 SN - 1521-4176 VL - 63 IS - 2 SP - 140 EP - 147 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-25467 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Theiler, Geraldine A1 - Wachtendorf, Volker A1 - Elert, Anna Maria A1 - Weidner, Steffen T1 - Effects of UV radiation on the friction behavior of thermoplastic polyurethanes N2 - The effects of weathering exposure on unfilled and filled thermoplastic polyurethanes (TPU) materials are described as performed under different humidity conditions. For this purpose, a weathering device was used with UV-A 340 nm lamps at a constant temperature of 40 °C. The effects of environmental (UV and humidity condition) degradation on the frictional properties of TPU materials are presented along with surface analyses to characterize the chemistry of the degradative process. Photooxidative degradation of unfilled polymer leads to deterioration of physical and mechanical properties, which affects its tribological behavior significantly. Due to crosslinking, the stiffness of the material increases, reducing drastically the friction coefficient of unfilled TPUs. The frictional behavior of glass fiber reinforced TPU is less affected by radiation. KW - Photooxidation KW - UV radiation KW - Friction KW - TPU KW - Humidity PY - 2018 DO - https://doi.org/10.1016/j.polymertesting.2018.08.006 SN - 0142-9418 SN - 1873-2348 VL - 70 SP - 467 EP - 473 PB - Elsevier Ltd. CY - Amsterdam AN - OPUS4-45709 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -