TY - CONF A1 - Völker, Tobias A1 - Millar, S. A1 - Licht, M. A1 - Wilsch, Gerd T1 - Round robin test for chloride analysis in cement pastes with LIBS N2 - In civil engineering, clear regulations and standards, such as the European standard DIN EN 206 apply to ensure that the existing infrastructure is sufficiently resistant to a wide range of exposure conditions. Despite these regulations, in practice concrete structures often show severe damage during their service life. One of these damages is pitting corrosion of the reinforcement, which can be caused by chloride ingress into the structure. Therefore, determining the distribution and depth of chloride ingress is important in predicting the service life. LIBS provides an alternative method to conventional wet chemistry in civil engineering. Despite many advantages, the use of LIBS has been severely limited due to a lack of regulations. Together with project partners from research and industry, we are currently working on a leaflet that will regulate chloride analysis in civil engineering using LIBS. This year, an international round robin test was organized to evaluate the performance of LIBS for chloride analysis in cement pastes. No specifications were given for the experimental LIBS setup and data evaluation. The preliminary results are presented. T2 - 11th Euro-Mediterranean Symposium on Laser-Induced Breakdown Spectroscopy (EMSLIBS) CY - Online meeting DA - 29.11.2021 KW - LIBS KW - Cement KW - Chloride KW - Round robin KW - Interlaboratory comparison PY - 2021 AN - OPUS4-53898 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wilsch, Gerd A1 - Völker, Tobias A1 - Klewe, Tim A1 - Kruschwitz, Sabine T1 - Laser-based building material sorting for the processing of construction and demolition waste for the circular economy N2 - A joint project of partners from industry and research institutions for the research and construction of an analysis system for an automated, sensor-supported sorting of construction and demolition waste will be presented. This is intended to supplement or replace the previously practiced manual sorting, which harbors many risks and dangers for the staff and only enables obvious, visually detectable differences for separation. The method of laser-induced breakdown spectroscopy is to be used in combination with hyperspectral sensors. Due to the jointly processed information (data fusion), this should lead to a significant improvement in the separation of types. In addition to the sorting of different materials (concrete, main masonry building materials, organic components, glass, etc.), impurities such as SO3-containing building materials (gypsum, aerated concrete, etc.) could also be detected and separated. The subsequent recycling and sales opportunities are examined, such as the use of recycled aggregates in concrete, the recycling of building materials containing sulphate as a gypsum substitute for the cement industry or the agglomeration of synthetic lightweight aggregates for lightweight concrete or as a substrate for green roofs. At the same time, it is investigated whether soluble components (sulfates, heavy metals, etc.) can be detected by LIBS without a wet chemical analysis and what impact the recycling materials have on the environment. The entire value chain is examined using the example of the Berlin location in order to minimize economic / technological barriers and obstacles on a cluster level and to sustainably increase the recovery and recycling rates. T2 - Materials Week 2021 CY - Online meeting DA - 07.09.2021 KW - Laser induced breakdown spectroscopy KW - Building waste KW - Circular economy KW - Material sorting PY - 2021 AN - OPUS4-53286 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völker, Tobias A1 - Klewe, Tim A1 - Wilsch, Gerd A1 - Kruschwitz, Sabine T1 - Application of LIBS to identify construction and demolition waste for circular economy N2 - Responsible treatment of the environment and resources is a key element of sustainability. The building and construction industry is one of the largest consumers of natural resources. Consequently, there is a particular need for regulations and technologies that help to create closed material cycles. From the technological point of view, such efforts are complicated by the growing material diversity and the amount of composites contained in present and future construction and demolition waste (CDW). Nowadays, simple but proven techniques like manual sorting are mainly used. However, this practice not only poses health risks and dangers to the staff performing the work, but also relies on merely obvious, visually striking differences. Automated, sensor-based sorting of these building materials could complement or replace this practice to improve processing speed, recycling rates, sorting quality, and prevailing health conditions. The preliminary results for the identification of a wide variety of building materials with LIBS are presented. T2 - XII Laser Induced Breakdown Spectroscopy (LIBS 2022) CY - Bari, Italy DA - 04.09.2022 KW - LIBS KW - Construction and demolition waste KW - Circular economy PY - 2022 AN - OPUS4-55679 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völker, Tobias A1 - Millar, Steven A1 - Strangfeld, Christoph A1 - Wilsch, Gerd T1 - Classification of cement pastes with laser-induced breakdown spectroscopy N2 - In civil engineering, the investigation of existing infrastructure is of major importance for maintaining and ensuring stability of the structures. To ensure durability, uniform regulations and standards apply e.g. the European standard EN 206-1. In some countries, the EN-standard is supplemented by additional standards, as in Germany with DIN 1045-2. Here, specific application rules are described, e.g. for the cement type, to ensure the resistant to different exposures. Therefore, the knowledge of the materials originally used is important in assessing the condition of existing concrete structure. Unfortunately, these are often unknown and must be determined retrospectively. Therefore, we present the application of the laser-induced breakdown spectroscopy to distinguish between different types of cement. Spectral information’s are used to build a classification model. First, the accuracy of the classification is analyzed on ten pure laboratory cement samples. To investigate possible sources of error, the model was then applied to cement samples with different moisture content. The study shows that LIBS is a promising tool for distinguishing between cement types. For further industrial application, however, factors influencing the LIBS signal must be included to ensure a robust model. T2 - 10th Euro-Mediterranean Symposium on Laser-Induced Breakdown Spectroscopy CY - Brno, Czech Republic DA - 08.09.2019 KW - Spectroscopy KW - LIBS KW - Cement KW - Classification PY - 2019 AN - OPUS4-49253 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völker, Tobias A1 - Gornushkin, Igor B. A1 - Kazakov, Alexander Ya. A1 - Wilsch, Gerd T1 - Application of two calibration-free LIBS techniques N2 - Two calibration-free (CF) LIBS approaches are used for the quantitative analysis of cement samples: the CF-LIBS based on the Boltzmann plot method and the Monte Carlo (MC) LIBS based on the iterative spectrum fitting. In CF-LIBS, the inverse problem is solved, i.e. the elemental concentrations are determined by the reconstruction of plasma parameters from spectra. The MC-LIBS technique solves the direct problem by finding the highest correlation between the model-generated and experimental spectrum. The accuracy of both calibration-free LIBS methods suffers from factors such as inaccurately determined instrumental function, the deviation of experimental plasma from the mathematical model used, not taking into account the collection geometry, and from the uncertainty of spectroscopic data. The both calibration-free LIBS approaches are first applied to synthetic spectra which perfectly suit the mathematical model of the method, i.e. the model of the uniform, isothermal, and stationary plasma. This test yields the accuracy of both the approaches for the ideal case. In addition, the accuracy of both the methods is investigated for non-uniform and non-isothermal plasma, because real laser-induced plasma often has high gradients in temperature and particle number densities. Finally, both calibration-free LIBS approaches are applied to experimental spectra obtained from cement samples. The figures of merits of two approaches are compared when working with both synthetic and experimental spectra. T2 - LIBS 2018 at SciX 2018 CY - Atlanta, GA DA - 21.10.2018 KW - Plasma diagnostics KW - Laser induced plasma KW - LIBS KW - Plasma modeling PY - 2018 AN - OPUS4-46931 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völker, Tobias A1 - Gornushkin, Igor B. A1 - Kazakov, Alexander Ya. A1 - Wilsch, Gerd T1 - Application of two calibration-free LIBS techniques for synthetic spectra of cement samples N2 - Two calibration-free LIBS techniques are used for the quantitative analysis of synthetic cement samples: the CF-LIBS based on the Boltzmann plot method and the Monte Carlo (MC) LIBS based on the iterative spectrum fitting. In CF-LIBS, the inverse problem is solved, i.e. the elemental concentrations are determined by the reconstruction of plasma parameters from spectra. The MC-LIBS technique solves the direct problem by finding the highest correlation between the model-generated and experimental spectrum. The accuracy of both calibration-free LIBS methods suffers from factors such as inaccurately determined instrumental function, the deviation of experimental plasma from the mathematical model used, not taking into account the collection geometry and from the uncertainty of spectroscopic data. Therefore, the both calibration-free LIBS approaches are applied to synthetic spectra which perfectly suit the mathematical model of the method. This test yields the accuracy of both the approaches for the ideal case. In addition, the accuracy of both methods is investigated for non-isothermal plasma, because real laser-induced plasma often has high gradients in temperature. Both methods assume an isothermal plasma. T2 - Xth international conference on Laser-Induced Breakdown Spectroscopy CY - Atlanta, GA, USA DA - 21.10.2018 KW - Cement KW - MC-LIBS KW - LIBS KW - CF-LIBS PY - 2018 AN - OPUS4-46774 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völker, Tobias A1 - Günther, Tobias A1 - Millar, Steven A1 - Wilsch, Gerd T1 - Quantitative on-site analysis of harmful elements in building structures with a mobile LIBS-System N2 - Environmental influences and damage processes drastically reduce the durability of concrete and reinforced concrete structures. Much of this damage can be traced back to the penetration of harmful elements into the concrete. These elements cause damage processes such as the chlorine-induced corrosion, the alkali-silica reaction or the carbonization. For the maintenance the knowledge of the element concentration and the penetration depth of these harmful elements is essential. Based on this data, a maintenance concept can be developed and an estimation of the remaining service life-time can be carried out. Typically, chemical analyzes are used to determine harmful elements in concrete, which are costly and time consuming. As an alternative method LIBS is used. On-site measurements were carried out with a mobile LIBS-System to determine harmful elements in a parking garage. A scanner is used to obtain a two-dimensional element mapping. For the quantitative analysis, a calibration of the system is carried out with 15 reference samples based on cement with NaCl with a concentration range of chlorine of 0.05 to 2.5 wt.%. To determine the penetration profile of the harmful element chlorine, concrete cores were drilled, split and analyzed directly on-site. T2 - Xth international conference on Laser-Induced Breakdown Spectroscopy CY - Atlanta, GA, USA DA - 21.10.2018 KW - LIBS KW - Mobile-LIBS KW - On-site analysis KW - Concrete PY - 2018 AN - OPUS4-46790 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völker, Tobias A1 - Klewe, Tim A1 - Kruschwitz, Sabine A1 - Landmann, M. T1 - LIBS ConSort Laserbasierte Baustoffsortierung zur Aufbereitung von Bau und Abbruchabfällen für die Kreislaufwirtschaft N2 - Geschlossene Materialkreisläufe und sortenreine Materialfraktionen sind erforderlich, um hohe Verwertungs und Recyclingquoten in der Bauindustrie zu erreichen Beim Recycling von Bau und Abbruchabfällen wurden bisher bevorzugt einfache, aber bewährte Techniken eingesetzt, um große Mengen Bauschutt in kurzer Zeit zu verarbeiten Dies steht im Gegensatz zu den immer komplexer werdenden Verbundwerkstoffen in der Mineralbaustoffindustrie Die aktuell oft praktizierte händische Klaubung bürgt viele Risiken und Gefahren für das ausführende Personal und basiert lediglich auf offensichtlichen, visuell erkennbaren Unterschieden zur Trennung Eine automatisierte, sensorgestützte Sortierung dieser Baustoffe könnte diese Praxis ergänzen oder ersetzen, um die Verarbeitungsgeschwindigkeit, die Recyclingraten, die Sortierqualität und die vorherrschenden Gesundheitsbedingungen zu verbessern. T2 - ReMin Statuskonferenz 2023 CY - Clausthal Zellerfeld, Germany DA - 20.06.2023 KW - LIBS PY - 2023 AN - OPUS4-57753 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -