TY - CONF A1 - Usmani, Shirin M. A1 - Stephan, Ina A1 - Schlischka, Joerg A1 - Klutzny, Kerstin A1 - de Laval, Yvonne A1 - Plarre, RĂ¼diger A1 - Huebert, Thomas A1 - Saliwan Neumann, Romeo A1 - Kemnitz, Erhard T1 - Wood protection with MgF2 and CaF2 nanoparticles N2 - Sol-gel synthesis was used to prepare nanoparticles of MgF2 and CaF2. These nanoparticles were tested for their application in wood protection. In comparison to control samples, wood specimens treated with MgF2 and CaF2 showed lower mass loss under exposure to termites and fungi. Samples treated with MgF2 performed better at protecting wood from cellulose degradation when exposed to termites. Conversely, in the presence of fungi, mass loss in treated samples was similar irrespective of the chemical composition (MgF2 and CaF2) of the treatment. A possible explanation for this difference in results between termites and fungi could be their different mechanism of cellulose hydrolysis. Thus, future wood preservatives would need to be customized according to their specific application. T2 - 19th International Sol-Gel Conference CY - Liege, Belgium DA - 03.09.2017 KW - Nanoparticles KW - Wood protection KW - Fungi KW - Termites PY - 2017 AN - OPUS4-42541 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Usmani, Shirin A1 - Schlishka, Joerg A1 - Klutzny, Kerstin A1 - de Laval, Yvonne A1 - Plarre, RĂ¼diger A1 - Krahl, Thoralf A1 - Stephan, Ina A1 - Huebert, Thomas A1 - Kemnitz, Erhard T1 - Wood protection with nanoparticles: MgF2 and CaF2 N2 - Alkaline earth metal fluoride nanoparticles have been investigated for application in wood protection. Sols of MgF2 and CaF2 were synthesized and their efficacy was tested against fungi and termites (Rehmer 2016, Krahl et al. 2016). The sols were characterized by XRD and SEM. The wood specimens were vacuum impregnated with nanoparticles and then exposed to fungi and termites according to EU certified test conditions. Our results show that wood impregnated with metal fluoride nanoparticles significantly reduce cellulose hydrolysis by fungi and termites. The wood samples were exposed to brown-rot fungi; Coniophora puteana and Poria placenta. Between the two fungi, the overall mass lost due to fungal degradation was lower for treated (MgF2 and CaF2) wood samples exposed to Coniophora puteana. Thus, the metal fluoride nanoparticles impregnated in the wood samples were more efficient in reducing cellulose degradation from Coniophora puteana than from Poria placenta. However the mass loss in samples treated with MgF2 was similar to those treated with CaF2, irrespective of type of fungi. Therefore, it is likely that fungal degradation in treated samples was dependent on the biocidal action of fluorides rather than on the differences in chemical and physical properties of MgF2 and CaF2, respectively. Conversely, for termite exposure, wood samples treated with MgF2 had lower cellulose degradation compared to those treated with CaF2. A possible explanation for this difference in results could be fungi and termites use separate mechanisms for cellulose hydrolysis which will be further investigated. Future experiments include testing the leaching potential of MgF2 and CaF2 nanoparticles from wood. The results from the leaching experiment will test if metal fluoride nanoparticles can provide long-term and environmentally safe protection to wood. T2 - International Research Group (IRG48) Scientific Conference on Wood Protection CY - Ghent, Belgium DA - 04.06.2017 KW - Fluoride KW - Nanoparticles KW - Brown-rot fungi KW - Termites PY - 2017 AN - OPUS4-41019 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -