TY - JOUR A1 - Timme, Sebastian A1 - Trappe, Volker A1 - Korzen, Manfred A1 - Schartel, Bernhard T1 - Fire stability of carbon fiber reinforced polymer shells on the intermediate-scale N2 - The fire stability of carbon fiber reinforced polymer (CFRP) shell structures was investigated using an intermediate-scale test setup. The shell specimens are representative of typical load-bearing CFRPs in modern civil aviation. The CFRP shell specimens were exposed to a fully developed fire with direct flame impingement to one side at a heat flux of 182 kW/m2. Specimens were simultaneously loaded with constant compressive force equal to 40% of the ultimate failure load. CFRP shells and four different fire retarding configurations, using integrated protective layers, were investigated. Unprotected CFRP specimens failed after just 27 s. Specimens with integrated protective layers with low heat conductivity and high burn-through resistance showed the most promising results. An integrated titanium foil decelerated the decomposition of the epoxy matrix and increased the time to failure by 68% compared to the unprotected CFRP shell. KW - Fire stability KW - Carbon fiber reinforced polymer (CFRP) KW - Thermomechanical properties KW - Buckling KW - Fully developed fire PY - 2017 U6 - https://doi.org/10.1016/j.compstruct.2017.07.025 SN - 0263-8223 SN - 1879-1085 VL - 178 SP - 320 EP - 329 PB - Elsevier Ltd. AN - OPUS4-41283 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Tabaka, Weronika A1 - Timme, Sebastian A1 - Lauterbach, Tobias A1 - Medina, L. A1 - Berglund, L. A. A1 - Carosio, F. A1 - Duquesne, S. A1 - Schartel, Bernhard T1 - Bench-scale fire stability testing - Assessment of protective systems on carbon fibre reinforced polymer composites N2 - Fire resistance testing of components made of carbon fibre reinforced polymers (CFRP) usually demands intermediate-scale or full-scale testing. A bench-scale test is presented as a practicable and efficient method to assess how different fire protective systems improve the structural integrity of CFRPs during fire. The direct flame of a fully developed fire was applied to one side of the CFRP specimen, which was simultaneously loaded with compressive force. Three different approaches (film, non-woven, and coatings) were applied: paper with a thickness in the range of μm consisting of cellulose nanofibre (CNF)/clay nanocomposite, nonwoven mats with thickness in the range of cm and intumescent coatings with a thickness in the range of mm. The uncoated specimen failed after just 17 s. Protection by these systems provides fire stability, as they multiply the time to failure by as much as up to 43 times. The reduced heating rates of the protected specimens demonstrate the reduced heat penetration, indicating the coatings’ excellent heat shielding properties. Bench-scale fire stability testing is shown to be suitable tool to identify, compare and assess different approaches to fire protection. KW - Fire stability KW - Bench-scale fire resistance KW - Carbon fibre reinforced polymer KW - Protective coatings PY - 2021 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-532401 SN - 0142-9418 SN - 1873-2348 VL - 102 SP - 7340 PB - Elsevier CY - Amsterdam AN - OPUS4-53240 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -