TY - JOUR A1 - Shabir Mahr, Muhammad A1 - Hübert, Thomas A1 - Stephan, Ina A1 - Militz, H. T1 - Decay protection of wood against brown-rot fungi by titanium alkoxide impregnations N2 - Decay resistance of pine sapwood treated with titanium alkoxide solutions was tested against the brown-rot fungi Coniophora puteana and Poria placenta for exposure times of 10 and 16 wk. In practice, wood-specimens were vacuum-impregnated by alcoholic solutions of titanium alkoxide with concentrations in the range of 5–16 mass % (solid content in solution) and subsequently cured under different humidity conditions. Results reveal that treated wood degraded up to 5% in comparison to untreated one that deteriorated 38% and 50%, respectively against both wood-decay fungi. Even full protection (mass loss below 3%) was achieved against brown rot with titanium alkoxide solution containing solid content of around 5 mass% with a weight percentage gain (WPG) of 9 mass%. With increased concentration, fungal resistance decreased slightly which was associated with more cracks and imperfections formed in the deposited layers of titanium dioxide in the adjacent wood matrix. Thermal analysis verified that a considerable amount of precursor remained in the wood structure as un-hydrolyzed organic residues. These organics, being bioactive, had the tendency to induce similar fungicidal effects as those of conventional fungicides. The amount of organic residues is correlated with the decay resistance of the tested samples. In a prolonged decay test, mass losses of 16-wk incubated samples do not show behavior different from that of the wood samples incubated for 10 wk. This result implies that the decay protection is permanent and confirms further the fungicidal activity of titanium-alkoxide-treated wood. KW - Precursor solutions KW - Sol-gel process KW - Equivalent solid content KW - Brown rot KW - Coniophora puteana KW - Poria placenta KW - Fungal colonization KW - Biocidal effect PY - 2013 DO - https://doi.org/10.1016/j.ibiod.2012.04.026 SN - 0964-8305 VL - 77 SP - 56 EP - 62 PB - Elsevier Ltd. CY - Barking AN - OPUS4-27622 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Shabir Mahr, Muhammad A1 - Hübert, Thomas A1 - Stephan, Ina A1 - Bücker, Michael A1 - Militz, H. T1 - Reducing copper leaching from treated wood by sol-gel derived TiO2 and SiO2 depositions N2 - The antileaching efficacy of sol-gel-derived TiO2- and SiO2-based precursors has been evaluated through laboratory leaching trials with pine sapwood in two different ways. In a one-step process, wood was vacuum impregnated by the precursor solutions containing CuCl2. The copper (Cu) emission rates of the sol-gel-based impregnated woods were up to 70% lower than that of wood treated with pure CuCl2 solution at the same level of concentration. More improvement (80%) could be achieved in a two-step process, in which sol-gel precursors were introduced into an already CuCl2-treated wood. The refinement was attributed to several effects. In the one-step approach, Cu was embedded in the TiO2/SiO2 gels formed in the wood texture. During a two-step impregnation, gel layers that were formed in the wooden interior acted as an effective diffusion barrier. The sol-gel impregnations made wood more hydrophobic; therefore, the low amount of water that penetrated the cell wall was less efficient to leach out Cu. KW - Copper leachability KW - SiO2-based gel KW - Sol-gel treatment of wood KW - TiO2-based gel KW - Wood impregnation KW - Wood protection PY - 2013 DO - https://doi.org/10.1515/hf-2012-0105 SN - 0018-3830 SN - 1437-434X VL - 67 IS - 4 SP - 429 EP - 435 PB - De Gruyter CY - Berlin AN - OPUS4-28892 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stephan, Ina T1 - ISO 846 - Part A and B, Resistance to Fungi; Documentation and discussion of ring-test results T2 - International Biodeterioration Research Group, Plastics CY - Athens, Greece DA - 2013-10-10 PY - 2013 AN - OPUS4-29248 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stephan, Ina A1 - Wachtendorf, Volker A1 - Geburtig, Anja A1 - Schulz, Ulrich T1 - Mould growth on automotive coatings influencing the results of outdoor weathering T2 - Smart and Functional Coatings CY - Turin, Italy DA - 2013-09-26 PY - 2013 AN - OPUS4-29249 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stephan, Ina T1 - ISO 846 - Revision of Part C: Restance to Bacteria T2 - Meeting of International Biodeterioration Research Group CY - Prague, Czech Republic DA - 2013-04-16 PY - 2013 AN - OPUS4-28378 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stephan, Ina T1 - Understanding treated articles: Why they are treated and how to demonstrate their effects T2 - Biocides 2013 CY - Vienna, Austria DA - 2013-11-18 PY - 2013 AN - OPUS4-29704 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -