TY - JOUR A1 - Klaffke, Dieter A1 - Santner, Erich A1 - Spaltmann, Dirk A1 - Woydt, Mathias T1 - Influences on the tribological behaviour of slip-rolling DLC-coatings N2 - Diamond like carbon (DLC)-coatings are applied very successfully on computer discs. Sliding friction tests confirm their high performance as dry lubricants with friction coefficients (COFs) below 0.1. In contrast to sliding tests, until very recently most of the DLC-coatings failed in slip-rolling test after fewer cycles than uncoated samples. However, present tests with DLC-coatings of seven different suppliers show a more promising tribological behaviour under slip-rolling conditions. The DLC-coatings were deposited onto steel 100Cr6, HRC 60, with a thickness of 2–3 ?m. The counter bodies were uncoated, grinded or polished 100Cr6 discs with 30 mm radius of curvature. The tests were performed on a twin disc testing rig (Amsler type) with paraffin oil under boundary/mixed lubrication and rolling with 10% slip. The initial, average Hertzian contact pressure was adjusted to Pm = 1.0, 1.25, and 1.5 GPa. The failure criterion was defined as the occurrence of a single damaged area larger than 1 mm2, which was controlled by optical microscopy (OM). An acoustic emission (AE) measurement system was installed as an additional online control for coating failure. The stressed coatings and the chipping areas were analyzed by OM, SEM, EDX, AFM and Raman spectroscopy. Until now, the results reveal that a large scatter in lifetime of coatings occurs not only between samples of different coaters but also between the samples of one single batch. The highest lifetime reached by a DLC-coating under these testing conditions is 10 × 106 cycles. That is the highest life time for a coating tested under the testing conditions above in our laboratory so far. The following factors were identified to influence the life time of the coatings: coating thickness, interlayer type, topography of the coatings, counter body roughness and mechanical properties. But the most important factor determining the life time of the coatings is that the coating process does produce homogenous layers free of faults. KW - DLC-coatings KW - Slip-rolling KW - Life time KW - Acoustic emission PY - 2005 DO - https://doi.org/10.1016/j.wear.2005.01.008 SN - 0043-1648 VL - 259 SP - 752 EP - 758 PB - Elsevier CY - Amsterdam AN - OPUS4-7557 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Klaffke, Dieter A1 - Löhr, Manuel A1 - Spaltmann, Dirk A1 - Woydt, Mathias A1 - Santner, Erich ED - Franek, F. ED - Pauschitz, A. T1 - Zuverlässige Wälzsysteme durch DLC-Schichten? Bedeutung und Aufgaben von Schichtsystemen T2 - Symposium der Österreichischen Tribologischen Gesellschaft CY - Wien, Österreich DA - 2003-11-20 PY - 2003 SN - 3-901657-13-4 SP - 59 EP - 68 PB - ÖTG CY - Wien AN - OPUS4-3131 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kirner, Sabrina V. A1 - Slachciak, Nadine A1 - Elert, Anna Maria A1 - Griepentrog, Michael A1 - Fischer, Daniel A1 - Hertwig, Andreas A1 - Sahre, Mario A1 - Dörfel, Ilona A1 - Sturm, Heinz A1 - Pentzien, Simone A1 - Koter, Robert A1 - Spaltmann, Dirk A1 - Krüger, Jörg A1 - Bonse, Jörn T1 - Tribological performance of titanium samples oxidized by fs-laser radiation, thermal heating, or electrochemical anodization N2 - Commercial grade-1 titanium samples (Ti, 99.6%) were treated using three alternative methods, (i) femtosecond laser processing, (ii) thermal heat treatment, and (iii) electrochemical anodization, respectively, resulting in the formation of differently conditioned superficial titanium oxide layers. The laser processing (i) was carried out by a Ti:sapphire laser (pulse duration 30 fs, central wavelength 790 nm, pulse repetition rate 1 kHz) in a regime of generating laser-induced periodic surface structures (LIPSS). The experimental conditions (laser fluence, spatial spot overlap) were optimized in a sample-scanning setup for the processing of several square-millimeters large surface areas covered homogeneously by these nanostructures. The differently oxidized titanium surfaces were characterized by optical microscopy, micro Raman spectroscopy, variable angle spectroscopic ellipsometry, and instrumented indentation testing. The tribological performance was characterized in the regime of mixed friction by reciprocating sliding tests against a sphere of hardened steel in fully formulated engine oil as lubricant. The specific tribological performance of the differently treated surfaces is discussed with respect to possible physical and chemical mechanisms. KW - Femtosecond laser KW - Titanium KW - Oxidation KW - Friction PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-445609 DO - https://doi.org/10.1007/s00339-018-1745-8 SN - 0947-8396 SN - 1432-0630 VL - 124 IS - 4 SP - 326, 1 EP - 10 PB - Springer-Verlag AN - OPUS4-44560 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Joseba Ayerdi, J. A1 - Slachciak, Nadine A1 - Llavori, I. A1 - Zabala, A. A1 - Aginagalde, A. A1 - Bonse, Jörn A1 - Spaltmann, Dirk T1 - On the role of a ZDDP in the tribological performance of femtosecond laser-induced periodic surface structures on titanium alloy against different counterbody materials N2 - Laser-induced periodic surface structures (LIPSS, ripples) with ~500–700 nm period were produced on titanium alloy (Ti6Al4V) surfaces upon scan processing in air by a Ti:sapphire femtosecond laser. The tribological performance of the surfaces were qualified in linear reciprocating sliding tribological tests against balls made of different materials using different oilbased lubricants. Extending our previous work, we studied the admixture of the additive 2-ethylhexyl-zinc-dithiophosphate to a base oil containing only anti-oxidants and temperature stabilizers. The presence of this additive along with the variation of the chemical composition of the counterbodies allows us to explore the synergy of the additive with the laseroxidized nanostructures. KW - Additives KW - Surface structures KW - Wear KW - Friction PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-488458 DO - https://doi.org/10.3390/lubricants7090079 SN - 2075-4442 VL - 7 SP - 79, 1 EP - 13 PB - MDPI AN - OPUS4-48845 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Herr, M. A1 - Borras, F. X. A1 - Spaltmann, Dirk A1 - Kröll, Mirco A1 - Pirker, F. A1 - Cihak-Bayr, U. T1 - How to create trusted tribological characterization data of soft polymers as input for FEM simulations? N2 - Soft polymers such as the investigated polyurethane, characterized by low Young’s moduli and prone to high shear deflection, are frequently applied in pneumatic cylinders. Their performance and lifetime without external lubrication are highly determined by the friction between seal and shaft and the wear rate. FEM simulation has established itself as a tool in seal design processes but requires input values for friction and wear depending on material, load, and velocity. This paper presents a tribological test configuration for long stroke, reciprocating movement, allowing the generation of data which meet the requirements of input parameters for FEM simulations without the geometrical influences of specific seal profiles. A numerical parameter study, performed with an FEM model, revealed the most eligible sample geometry as a flat, disc-shaped sample of the polymer glued on a stiff sample holder. At the same time, the study illustrates that the sensitivity of the contact pressure distribution to Poisson’s ratio and CoF can be minimized by the developed and verified setup. It ensures robust, reliable, and repeatable experimental results with uniform contact pressures and constant contact areas to be used in databases and FEM simulations of seals, enabling upscaling from generically shaped samples to complex seal profiles. KW - Tribologie KW - FEM KW - Simulation KW - Polymere KW - Charakterisierung KW - i-TRIBOMAT KW - Modellierung KW - Polyurethan KW - Dichtungen KW - Upscaling PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-567683 DO - https://doi.org/10.3390/ma16010131 SN - 1996-1944 VL - 16 IS - 1 SP - 1 EP - 20 PB - MDPI CY - Basel AN - OPUS4-56768 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Florian, Camilo A1 - Wonneberger, R. A1 - Undisz, A. A1 - Kirner, Sabrina V. A1 - Wasmuth, Karsten A1 - Spaltmann, Dirk A1 - Krüger, Jörg A1 - Bonse, Jörn T1 - Chemical effects during the formation of various types of femtosecond laser-generated surface structures on titanium alloy N2 - In this contribution, chemical, structural, and mechanical alterations in various types of femtosecond laser-generated surface structures, i.e., laser-induced periodic surface structures (LIPSS, ripples), Grooves, and Spikes on titanium alloy, are characterized by various surface analytical techniques, including X-ray diffraction and glow-discharge optical emission spectroscopy. The formation of oxide layers of the different laser-based structures inherently influences the friction and wear performance as demonstrated in oil-lubricated reciprocating sliding tribological tests (RSTTs) along with subsequent elemental mapping by energy-dispersive X-ray analysis. It is revealed that the fs-laser scan processing (790 nm, 30 fs, 1 kHz) of near-wavelength-sized LIPSS leads to the formation of a graded oxide layer extending a few hundreds of nanometers into depth, consisting mainly of amorphous oxides. Other superficial fs-laser-generated structures such as periodic Grooves and irregular Spikes produced at higher fluences and effective number of pulses per unit area present even thicker graded oxide layers that are also suitable for friction reduction and wear resistance. Ultimately, these femtosecond laser-induced nanostructured surface layers efficiently prevent a direct metal-to-metal contact in the RSTT and may act as an anchor layer for specific wear-reducing additives contained in the used engine oil. KW - Laser-induced oxide layer KW - Laser-induced periodic surface strctures (LIPSS) KW - Femtosecond laser processing KW - Tribology KW - Surface processing PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-505660 DO - https://doi.org/10.1007/s00339-020-3434-7 SN - 0947-8396 SN - 1432-0630 VL - 126 IS - 4 SP - 266 PB - Springer Nature Switzerland AG AN - OPUS4-50566 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Effner, Ute A1 - Löhr, Manuel A1 - Spaltmann, Dirk A1 - Woydt, Mathias T1 - Überrollbeständige DLC-Schichten unter Wälzverschleißbedingungen bis 2 GPa? T2 - Tribologie-Fachtagung 2002 CY - Göttingen, Deutschland DA - 2002-09-23 PY - 2002 SN - 3-00-003404-8 VL - 1 SP - 17-1-17-11 PB - GfT CY - Moers AN - OPUS4-3422 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Cappella, Brunero A1 - Spaltmann, Dirk A1 - Gee, M. T1 - Editorial: Tribology and Atomic Force Microscopy - Towards Single Asperity Contact N2 - The concept behind this Research Topic (RT) was to collect works, in which Atomic Force Microscopy (AFM) techniques are employed to study tribological phenomena and to push the resolution of measurements towards single asperity contact. Thanks to the direct determination of sample height with sub-nanometer resolution and the possibility of measuring local friction, AFM can be employed after a tribotest to detect topography and friction changes at the nanometer scale. Recently, efforts are being expended to use AFM cantilevers as tribometers, i.e., as probes altering the volume of suitable samples, thereby measuring tip and/or sample wear and friction at the nano/microscale. Thus, single asperity contact, friction, and wear can be investigated. Since friction and wear at the macroscale are the result of asperities interactions, such experiments are of great importance for better understanding of tribological processes. KW - Nanotribology KW - Friction KW - Wear KW - Single asperity KW - AFM PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-571037 DO - https://doi.org/10.3389/fmech.2022.853934 SN - 2297-3079 VL - 8 SP - 1 EP - 2 PB - Frontiers Media CY - Lausanne AN - OPUS4-57103 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bonse, Jörn A1 - Spaltmann, Dirk T1 - Editorial: Special issue "Laser-induced periodic surface nano- and microstructures for tribological applications" N2 - Laser material processing is an emerging technology that generates surface functionalities on the basis of optical, mechanical, or chemical properties. In the form of laser surface texturing (LST), it has attracted a remarkable amount of research to tailor surface properties towards various tribological applications. The main advantages of this single-step, laser-based technology are the contactless machining, featuring a high flexibility, efficiency, and speed, along with the excellent quality of the processed products. LST can be applied precisely localized to sub-micrometric areas, but, via laser beam scanning, it is also feasible for structuring large surface areas at the square meter size. This Special Issue focuses on the latest developments concerning the tribological performance of laser-generated periodic surface nano- and microstructures and their applications. This includes the laser-based processing of different surface patterns, such as “self-organized” laser-induced periodic surface structures (LIPSS, ripples), grooves, micro-spikes, hierarchical hybrid nano-/micro-structures, microfeatures generated by direct laser interference patterning (DLIP), or even dimples or other topographic geometries shaped by direct laser modification or ablation. The applications of these periodically nano- and micro-patterned surfaces may improve the lubricated or non-lubricated tribological performance of surfaces in conformal and even non-conformal contact through a reduction of wear, a variation of the coefficient of friction, altered load carrying capacity, etc., resulting in energy saving, improved reliability, increased lifetimes as well as durability, leading in turn to extended maintenance intervals/reduced down-time. This can be beneficial in terms of bearings, gears, engines, seals, cutting tools, or other tribological components. Fundamental aspects addressed may involve the investigation of the relevant physical and chemical effects accompanying the laser-generated nano- and microscale topographies, such as alterations of the material structures, the hardness, superficial oxidation, the role of additives contained in lubricants, surface wettability, micro-hydrodynamic effects, etc. For this Special Issue we aim to attract both academic and industrial researchers and would like to provide a bridge between research in the fields of tribology and laser material processing in order to foster the current knowledge and present new ideas for future applications and new technologies. KW - Laser-induced periodic surface structures (LIPSS) KW - Tribology KW - Applications KW - Wear KW - Friction PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-505948 DO - https://doi.org/10.3390/lubricants8030034 SN - 2075-4442 VL - 8 IS - 3 SP - 34, 1 EP - 34, 3 PB - MDPI CY - Basel AN - OPUS4-50594 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bonse, Jörn A1 - Koter, Robert A1 - Hartelt, Manfred A1 - Spaltmann, Dirk A1 - Pentzien, Simone A1 - Höhm, S. A1 - Rosenfeld, A. A1 - Krüger, Jörg T1 - Femtosecond laser-induced periodic surface structures on steel and titanium alloy for tribological applications N2 - Laser-induced periodic surface structures (LIPSS, ripples) were generated on stainless steel (100Cr6) and titanium alloy (Ti6Al4V) surfaces upon irradiation with multiple femtosecond laser pulses (pulse duration 30 fs, central wavelength 790 nm). The experimental conditions (laser fluence, spatial spot overlap) were optimized in a sample-scanning geometry for the processing of large surface areas (5 × 5 mm²) covered homogeneously by the nanostructures. The irradiated surface regions were subjected to white light interference microscopy and scanning electron microscopy revealing spatial periods around 600 nm. The tribological performance of the nanostructured surface was characterized by reciprocal sliding against a ball of hardened steel in paraffin oil and in commercial engine oil as lubricants, followed by subsequent inspection of the wear tracks. For specific conditions, on the titanium alloy a significant reduction of the friction coefficient by a factor of more than two was observed on the laser-irradiated (LIPSS-covered) surface when compared to the non-irradiated one, indicating the potential benefit of laser surface structuring for tribological applications. PY - 2014 DO - https://doi.org/10.1007/s00339-014-8229-2 SN - 0947-8396 VL - 117 IS - 1 SP - 103 EP - 110 PB - Springer CY - Berlin AN - OPUS4-31450 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -