TY - JOUR A1 - Beygi Narsabadi, Hossein A1 - Vafaeenezhad, H. A1 - Klotz, U.E. A1 - Tiberto, D. A1 - Hosseinabadi, F. A1 - Mishurova, Tatiana A1 - Bruno, Giovanni A1 - Skrotzki, Birgit T1 - XCT-assisted micromechanical modeling of the effect of pores on the plastic deformation and mechanical characteristics of PBF-LB/M-produced copper alloys N2 - Due to the low absorption of fiber laser by copper particles, the laser-based powder bed fusion (PBF-LB/M) processing of copper components is accompanied by the development of different types of porosities within the printed samples. This research aims to assess the consequences of various process-induced pores on the me chanical characteristics and deformation of PBF-LB/M-produced copper alloys. Several copper alloys were processed using metal-coated particles and varied laser intensities, yielding samples with different types and amounts of porosities. For instance, CuCrZr alloys processed at 325 J/mm³ and 257 J/mm³ had 0.009 % and 1.117 % porosities, dominated by keyhole and lack-of-fusion pores, respectively. Moreover, PBF-LB/M pro cessing of Cr- and Nb-coated CuNi3SiCr particles accompanied by the generation of 0.004 % and 1.861 % porosities within the samples, predominantly featuring metallurgical and oxidation pores, respectively. Compression and nanoindentation tests revealed that the CuNi3SiCr alloy exhibited superior mechanical properties compared to the CuCrZr sample (nanoindentation hardness values 2.2 GPa and 1.4 GPa, respectively), while the presence of lack-of-fusion pores notably diminished their mechanical performance. X-ray computed tomography (XCT) reconstruction slices and scanning electron microscopy (SEM) images were then used for developing the representative volume elements (RVEs) based micromechanical models. The micromechanical simulations established a structure-property correlation that can simulate the compressive deformation and mechanical characteristics of PBF-LB/M-produced copper alloys as a function of their incorporated pore characteristics. Due to the closure of the pores at the first stages of deformation, samples with minimal keyhole and metallurgical porosities exhibited homogeneous plastic deformation. On the other side, based on the JohnsonCook model, strain concentration and crack propagation around the lack-of-fusion pores lead to damage initi ation in the printed samples at a strain level of 5 % KW - X-ray Computed tomography KW - Defects KW - Copper alloys KW - PBF-LB/M KW - Micromechanics PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-624004 DO - https://doi.org/10.1016/j.msea.2025.147836 SN - 0921-5093 VL - 924 PB - Elsevier B.V. AN - OPUS4-62400 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zia, Ghezal Ahmad Jan A1 - Hanke, Thomas A1 - Skrotzki, Birgit A1 - Völker, Christoph A1 - Bayerlein, Bernd T1 - Enhancing Reproducibility in Precipitate Analysis: A FAIR Approach with Automated Dark-Field Transmission Electron Microscope Image Processing N2 - AbstractHigh-strength aluminum alloys used in aerospace and automotive applications obtain their strength through precipitation hardening. Achieving the desired mechanical properties requires precise control over the nanometer-sized precipitates. However, the microstructure of these alloys changes over time due to aging, leading to a deterioration in strength. Typically, the size, number, and distribution of precipitates for a quantitative assessment of microstructural changes are determined by manual analysis, which is subjective and time-consuming. In our work, we introduce a progressive and automatable approach that enables a more efficient, objective, and reproducible analysis of precipitates. The method involves several sequential steps using an image repository containing dark-field transmission electron microscopy (DF-TEM) images depicting various aging states of an aluminum alloy. During the process, precipitation contours are generated and quantitatively evaluated, and the results are comprehensibly transferred into semantic data structures. The use and deployment of Jupyter Notebooks, along with the beneficial implementation of Semantic Web technologies, significantly enhances the reproducibility and comparability of the findings. This work serves as an exemplar of FAIR image and research data management. KW - Industrial and Manufacturing Engineering KW - General Materials Science KW - Automated image analysis KW - FAIR research data management KW - Reproducibility KW - microstructural changes PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-593905 DO - https://doi.org/10.1007/s40192-023-00331-5 SN - 2193-9772 SP - 1 EP - 15 PB - Springer Science and Business Media LLC CY - Heidelberg AN - OPUS4-59390 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ávila Calderón, Luis A1 - Graf, B. A1 - Rehmer, Birgit A1 - Petrat, T. A1 - Skrotzki, Birgit A1 - Rethmeier, Michael T1 - Characterization of Ti-6Al-4V fabricated by multilayer laser powder-based directed energy deposition N2 - Laser powder-based directed energy deposition (DED-L) is increasingly being used in additive manufacturing (AM). As AM technology, DED-L must consider specific challenges. It must achieve uniform volume growth over hundreds of layers and avoid heat buildup of the deposited material. Herein, Ti–6Al–4V is fabricated using an approach that addresses these challenges and is relevant in terms of transferability to DED–L applications in AM. The assessment of the obtained properties and the discussion of their relationship to the process conditions and resulting microstructure are presented. The quality of the manufacturing process is proven in terms of the reproducibility of properties between individual blanks and with respect to the building height. The characterization demonstrates that excellent mechanical properties are achieved at room temperature and at 400 °C. KW - AGIL KW - Laser powder-based directed energy deposition KW - Tensile properties KW - Ti-6Al-4V KW - Microstructure PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-542262 DO - https://doi.org/10.1002/adem.202101333 SN - 1438-1656 SN - 1527-2648 SP - 1 EP - 15 PB - Wiley-VCH CY - Weinheim AN - OPUS4-54226 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Peter, D. A1 - Pfetzing, J. A1 - Wagner, M.F.-X. A1 - Somsen, C. A1 - Pesicka, J. A1 - Skrotzki, Birgit A1 - Eggeler, G. T1 - Quantitative Charakterisierung der Gefüge-Anisotropie einer stranggepressten TiAl-Legierung / Quantitative Characterisation and Microstructural Anisotropy of a Hot-Extruded TiAl Alloy KW - Titanaluminide KW - Mikrostruktur KW - Quantitative Analyse KW - Kriechen KW - Anisotropie PY - 2008 SN - 0032-678X N1 - Sprachen: Deutsch/Englisch - Languages: German/English VL - 45 IS - 5 SP - 210 EP - 224 PB - Hanser CY - München AN - OPUS4-17562 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Olbricht, Jürgen A1 - Lippmann, Tim A1 - Klingelhöffer, Hellmuth A1 - Rehmer, Birgit A1 - Skrotzki, Birgit T1 - Mechanical characterisation of heat resistant power plant materials by creep and fatigue testing in controlled gas atmospheres N2 - The continuing increase of steam parameters of fossil fuelled high efficiency power plants and new combustion concepts for the capture and storage of carbon dioxide lead to harsher service conditions for the components and structural materials of such facilities. The present work introduces a test concept that allows testing of candidate materials under simultaneous mechanical and corrosive loading. The material's reaction can be directly investigated under simulated temperature, load and corrosion conditions of modern installations. First results obtained for different heat resistant steels suggest a strong influence of the environmental medium on the fatigue and creep behaviour. Such findings complement the data that is available from the classical qualification process of the materials and may support the material selection for new power plant installations. N2 - Die weitere Erhöhung der Dampfparameter von hocheffizienten fossil befeuerten Kraftwerken sowie neue Verbrennungskonzepte zur Realisierung der Kohlendioxidabscheidung und -speicherung führen zu erschwerten Einsatzbedingungen für die Bauteile und Strukturwerkstoffe solcher Anlagen. Die vorliegende Arbeit stellt ein Prüfkonzept vor, das die Prüfung von Kandidatenwerkstoffen unter überlagerter mechanischer und korrosiver Beanspruchung ermöglicht. Die Werkstoffreaktion kann direkt unter den simulierten Temperatur-, Last- und Korrosionsbedingungen moderner Anlagen untersucht werden. Erste Ergebnisse für verschiedene warmfeste Stähle deuten auf einen erheblichen Einfluss des Umgebungsmediums auf das Ermüdungs- und Kriechverhalten hin. Solche Erkenntnisse ergänzen die aus den Qualifizierungsuntersuchungen der Werkstoffe verfügbaren Daten und können so die Werkstoffauswahl für neue Anlagen unterstützen. KW - Hocheffiziente Kraftwerke KW - Kohlendioxidabscheidung und -speicherung (CCS) KW - Warmfeste Stähle KW - Mechanische Eigenschaften KW - Korrosionsverhalten KW - High efficiency power plants KW - Carbon capture and storage (CCS) KW - Heat resistant steels KW - Mechanical properties KW - Corrosion behaviour PY - 2014 DO - https://doi.org/10.1002/mawe.201400185 SN - 0933-5137 SN - 1521-4052 VL - 45 IS - 1 SP - 5 EP - 14 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-30309 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bayerlein, Bernd A1 - Hanke, T. A1 - Muth, Thilo A1 - Riedel, Jens A1 - Schilling, Markus A1 - Schweizer, C. A1 - Skrotzki, Birgit A1 - Todor, A. A1 - Moreno Torres, Benjami A1 - Unger, Jörg F. A1 - Völker, Christoph A1 - Olbricht, Jürgen T1 - A Perspective on Digital Knowledge Representation in Materials Science and Engineering N2 - The amount of data generated worldwide is constantly increasing. These data come from a wide variety of sources and systems, are processed differently, have a multitude of formats, and are stored in an untraceable and unstructured manner, predominantly in natural language in data silos. This problem can be equally applied to the heterogeneous research data from materials science and engineering. In this domain, ways and solutions are increasingly being generated to smartly link material data together with their contextual information in a uniform and well-structured manner on platforms, thus making them discoverable, retrievable, and reusable for research and industry. Ontologies play a key role in this context. They enable the sustainable representation of expert knowledge and the semantically structured filling of databases with computer-processable data triples. In this perspective article, we present the project initiative Materials-open-Laboratory (Mat-o-Lab) that aims to provide a collaborative environment for domain experts to digitize their research results and processes and make them fit for data-driven materials research and development. The overarching challenge is to generate connection points to further link data from other domains to harness the promised potential of big materials data and harvest new knowledge. KW - Data infrastructures KW - Digital representations KW - Digital workflows KW - Knowledge graphs KW - Materials informatics KW - Ontologies KW - Vocabulary providers PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-546729 DO - https://doi.org/10.1002/adem.202101176 SN - 1438-1656 SP - 1 EP - 14 PB - Wiley-VCH GmbH CY - Weinheim AN - OPUS4-54672 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Suárez Ocaño, Patricia A1 - Ávila Calderón, Luis A1 - Agudo Jácome, Leonardo A1 - Rehmer, Birgit A1 - Mohr, Gunther A1 - Evans, Alexander A1 - Skrotzki, Birgit T1 - Effect of 700–900 °C heat treatments and room and high temperature tensile deformation on the microstructure of laser powder bed fused 316L stainless steel N2 - The effect of post-processing heat treatments on the hierarchical microstructure evolution and mechanical strength of the austenitic stainless steel 316L produced by laser powder bed fusion has been investigated. Heat treatments between 700 and 900 ◦C and 0.5 to 3 h, were applied to samples treated at 450 ◦C for 4 h. The results showed a stable microstructure at all studied temperatures and times in terms of grain size, morphology, aspect ratio, density of low-angle grain boundaries, and texture. However, temperature and time promoted the diffusion of segregated elements together with a reduction in dislocation density and disappearance of the cellular structure. This was associated with a reduction in hardness and tensile proof strength at both room and high temperature. In addition, microstructural characterization coupled with thermodynamic CALPHAD-based equilibrium calculations showed that the formation of carbides and intermetallic phases was already visible after annealing at 800 ◦C for 3 hours, although these intermetallics did not affect the tensile properties at this level. Analysis of the microstructure evolution after tensile deformation showed differences in the deformation mechanisms at room and high temperature, with twinning and martensitic transformation occurring at room temperature, the latter not widely reported for additively manufactured 316L. Finally, comparisons with similar materials produced under comparable conditions showed differences in the tensile properties, attributed to differences in chemical composition and the associated presence of stacking faults in the undeformed state. KW - Additive manufacturing KW - 316L stainless steel KW - Heat treatments KW - Tensile properties KW - Microstructure PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-632471 DO - https://doi.org/10.1016/j.msea.2025.148469 SN - 0921-5093 VL - 939 SP - 1 EP - 24 PB - Elsevier CY - Amsterdam AN - OPUS4-63247 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rockenhäuser, Christian A1 - Rowolt, C. A1 - Milkereit, B. A1 - Darvishi Kamachali, Reza A1 - Kessler, O. A1 - Skrotzki, Birgit T1 - On the long-term aging of S-phase in aluminum alloy 2618A N2 - The aluminum alloy 2618A is applied for engine components such as radial compressor wheels which operate for long time at elevated temperatures. This results in coarsening of the hardening precipitates and degradation in mechanical properties during the long-term operation, which is not taken into account in the current lifetime prediction models due to the lack of quantitative microstructural and mechanical data. To address this issue, a quantitative investigation on the evolution of precipitates during long-term aging at 190 °C for up to 25,000 h was conducted. Detailed transmission electron microscopy (TEM) was combined with Brinell hardness measurements and thorough differential scanning calorimetry (DSC) experiments. The results showthat GPB zones and S-phase Al2CuMg grow up to < 1,000 h during which the GPB zones dissolve and S-phase precipitates form. For longer aging times, only S-phase precipitates coarsen, which can be well described using the Lifshitz–Slyozov Wagner theory of ripening. A thorough understanding of the underlying microstructural processes is a prerequisite to enable the integration of aging behavior into the established lifetime models for components manufactured from alloy 2618A. KW - Long-term aging KW - Transmission electron microscopy (TEM) KW - Differential scanning calorimetry (DSC) KW - Microstructure KW - S-phase KW - Ostwald ripening PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-519899 DO - https://doi.org/10.1007/s10853-020-05740-x SN - 0022-2461 VL - 56 IS - 14 SP - 8704 EP - 8716 PB - Springer Nature AN - OPUS4-51989 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Klingelhöffer, Hellmuth A1 - Affeldt, E. E. A1 - Bache, M. A1 - Bartsch, M. A1 - Beck, T. A1 - Christ, H. J. A1 - Fedelich, Bernard A1 - Hähner, P. A1 - Holdsworth, S. R. A1 - Lang, K.-H. A1 - McGaw, M. A1 - Olbricht, Jürgen A1 - Remy, L. A1 - Skrotzki, Birgit A1 - Stekovich, S. T1 - Editorial - Special issue: Recent developments in thermo-mechanical fatigue N2 - Components in the Aerospace, Power and Automotive engineering sectors are frequently subjected to cyclic stresses induced by thermal fluctuations and mechanical loads. For the design of such components, reliable material property data are required which need to be acquired using well accepted and reproducible test procedures for thermo-mechanical fatigue (TMF) loading. There is limited availability of proven TMF data indicating there is need for further research and testing. The TMF behaviour of materials is often desired to be simulated in models which describe the cyclic stress-strain behaviour, the fatigue life and the cyclic crack growth behaviour. There is a continuous need for the development and amendment of such models. Models can be validated by using materials in industrial applications which are subjected to TMF loading. The 3rd Workshop on Thermo-Mechanical Fatigue was held on 27–29 April 2016 at BAM, Berlin, Germany. The workshop was attended by 90 attendees coming from 17 countries in the world. 38 presentations including five poster presentations were held. The following topics were covered by the workshop: – TMF of materials coated with Thermal Barrier Coatings. – Thermal Gradient Mechanical Fatigue. – TMF crack growth. – TMF + High Cycle Fatigue. – TMF Modelling and Lifetime Prediction. – TMF Properties of steels, cast iron, Al-, Mg- and Ni-alloys – Advanced TMF Testing Techniques. – Industrial Applications. A panel discussion was held regarding the present state of TMF testing standards (ISO and ASTM) and their potential for improvement. The discussion and contributions were summarized and forwarded to the standard committees. The 3rd TMF-Workshop ensured the continuation of international exchange of knowledge providing a forum to present and discuss all recent developments in the field of thermo-mechanical fatigue. The current special issue publishes eleven selected papers of the 3rd TMF-Workshop 2016. The papers were peer reviewed by a number of experts in the Thermo-Mechanical Fatigue sector. I hope you will enjoy reading papers of this special issue. T2 - 3rd International Workshop on Thermo-Mechanical Fatigue (TMF-Workshop 2016) CY - Berlin, Germany DA - 27.04.2016 KW - Fatigue damage KW - Thermo-mechanical fatigue KW - Fatigue life time KW - Life time prediction KW - TMF PY - 2017 DO - https://doi.org/10.1016/j.ijfatigue.2017.02.002 SN - 0142-1123 VL - 99 IS - 2 SP - 215 PB - Elsevier CY - Oxford AN - OPUS4-40895 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Han, Ying A1 - Schriever, Sina A1 - von Hartrott, Philipp A1 - Rockenhäuser, Christian A1 - Skrotzki, Birgit T1 - Creep dataset for aluminum alloy EN AW-2618A in the T61 and overaged condition 1000 h/190 °C N2 - The article presents creep data for the precipitation-hardened aluminum alloy EN AW-2618A, which was tested in its initial slightly underaged T61 condition and after being aged at 190 °C for 1000 h. The creep test temperatures ranged between 160 °C and 230 °C, and the applied initial stresses between 40 MPa and 290 MPa. The testing times reached up to 4700 h. 19 data sets are provided as creep strain vs. time series. A data schema originally developed to manage creep reference data of a single-crystalline nickel-based superalloy was adapted for the research data set of the polycrystalline aluminum alloy and used to enrich the test data with extensive metadata. The dataset can be used to calibrate and validate creep models. The creep data supplement the hardness and microstructure data that have been previously published. KW - Aluminum alloy EN AW-2618A KW - Aging KW - Overaging KW - High temperature KW - Creep PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-641517 DO - https://doi.org/10.1016/j.dib.2025.112054 SN - 2352-3409 VL - 62 SP - 1 EP - 10 PB - Elsevier CY - Amsterdam [u.a.] AN - OPUS4-64151 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sonntag, Nadja A1 - Cabeza, S. A1 - Kuntner, M. A1 - Mishurova, Tatiana A1 - Klaus, M. A1 - Kling e Silva, L. A1 - Skrotzki, Birgit A1 - Genzel, Ch. A1 - Bruno, Giovanni T1 - Visualisation of deformation gradients in structural steel by macroscopic magnetic domain distribution imaging (Bitter technique) N2 - Abstract While classically used to visualise the magnetic microstructure of functional materials (e.g., for magnetic applications), in this study, the Bitter technique was applied for the first time to visualise macroscopic deformation gradients in a polycrystalline low-carbon steel. Spherical indentation was chosen to produce a multiaxial elastic–plastic deformation state. After removing the residual imprint, the Bitter technique was applied, and macroscopic contrast differences were captured in optical microscopy. To verify this novel characterisation technique, characteristic “hemispherical” deformation zones evolving during indentation were identified using an analytical model from the field of contact mechanics. In addition, near-surface residual stresses were determined experimentally using synchrotron radiation diffraction. It is established that the magnetic domain distribution contrast provides deformation-related information: regions of different domain wall densities correspond to different “hemispherical” deformation zones (i.e., to hydrostatic core, plastic zone and elastic zone, respectively). Moreover, the transitions between these three zones correlate with characteristic features of the residual stress profiles (sign changes in the radial and local extrema in the hoop stress). These results indicate the potential of magnetic domain distribution imaging: visualising macroscopic deformation gradients in fine-grained ferromagnetic material with a significantly improved spatial resolution as compared to integral, mean value-based measurement methods. KW - Bitter technique KW - Deformation KW - Expanding cavity model KW - Indentation KW - Magnetic domain distribution KW - Residual stress PY - 2018 DO - https://doi.org/10.1111/str.12296 SN - 1475-1305 VL - 54 IS - 6 SP - e12296, 1 EP - 15 PB - Wiley AN - OPUS4-46569 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bettge, Dirk A1 - Günther, Burkhard A1 - Wedell, Wolfgang A1 - Portella, Pedro Dolabella A1 - Hemptenmacher, J. A1 - Peters, P.W.M. A1 - Skrotzki, Birgit T1 - Mechanical behavior and fatigue damage of a titanium matrix composite reinforced with continuous SiC fibers N2 - A titanium (Ti-6242) matrix composite reinforced with continuous SiC fibers was studied. The mechanical behavior of the matrix and the composite was characterized by tensile, creep and isothermal fatigue tests at room temperature and up to 550°C. The thermo-mechanical fatigue behavior under in-phase and out-of-phase conditions was investigated for the composite between 100 and 550°C. Fracture surfaces were characterized by confocal light microscopy and by scanning electron microscopy to identify the damage mechanisms. KW - Metal matrix composites KW - Tensile strength KW - Creep strength KW - Isothermal fatigue KW - Thermo-mechanical fatigue KW - Damage analysis PY - 2007 SN - 0921-5093 SN - 1873-4936 VL - 452-453 SP - 536 EP - 544 PB - Elsevier CY - Amsterdam AN - OPUS4-14616 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - von Hartrott, P. A1 - Metzger, M. A1 - Rockenhäuser, Christian A1 - Skrotzki, Birgit T1 - Lebensdauerbewertung von alternden Werkstoffen N2 - Werkstoffe im Hochtemperatureinsatz verändern mit der Zeit ihre Mikrostruktur. Mit diesem Alterungsprozess einher geht eine Veränderung der mechanischen Eigenschaften ebenso wie eine Veränderung des Schädigungsverhaltens. Im Rahmen des FVV Vorhabens „Alterung und Lebensdauer“ haben das Fraunhofer IWM in Freiburg und die BAM in Berlin die weit verbreitete warmfeste Aluminiumlegierung EN AW-2618A in verschiedenen Alterungszuständen experimentell charakterisiert und darauf aufbauend Modelle für die Lebensdauerbewertung mit der Finite-Elemente- Methode implementiert. KW - Aluminiumlegierung KW - Alterung KW - Mikrostruktur KW - Lebensdauervorhersage KW - Schädigung PY - 2018 DO - https://doi.org/10.1007/s35146-018-0085-8 SN - 0024-8525 SN - 2192-8843 VL - 79 IS - 10 SP - 72 EP - 76 PB - Springer AN - OPUS4-46064 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Brookes, Stephen-Peter A1 - Kühn, Hans-Joachim A1 - Skrotzki, Birgit A1 - Klingelhöffer, Hellmuth A1 - Sievert, Rainer A1 - Pfetzing, J. A1 - Peter, D. A1 - Eggeler, G. T1 - Multi-Axial Thermo-Mechanical Fatigue Of A Near-Gamma TiAl-Alloy N2 - A material family to replace the current superalloys in aeronautical gas turbine engines is considered to be that of gamma Titanium Aluminide (γ-TiAl) alloys. Structural components in aeronautical gas turbine engines typically experience large variations in temperatures and multiaxial states of stress under non-isothermal conditions. The uniaxial, torsional and bi-axial thermomechanical fatigue (TMF) behaviour of this γ-TiAl alloy have been examined at 400 – 800°C with strain amplitudes from 0.15% to 0.7%. The tests were conducted at both in-phase (IP) and out-ofphase (OP). The effects of TMF on the microstructure were also investigated. For the same equivalent mechanical strain amplitude uniaxial IP tests showed significantly longer lifetimes than pure torsional TMF tests. The non-proportional multiaxial OP test showed the lowest lifetimes at the same equivalent mechanical strain amplitude compared to the other types of tests. KW - Gamma-Titanium Aluminide KW - Thermo-mechanical Fatigue KW - Axial-torsional Loading PY - 2005 DO - https://doi.org/10.4028/3-908454-01-8.283 SN - 1022-6680 SN - 1662-8985 VL - 59 SP - 283 EP - 287 PB - Trans Tech Publ. CY - Zurich AN - OPUS4-18720 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Beygi Nasrabadi, Hossein A1 - Skrotzki, Birgit T1 - Digital representation of materials testing data for semantic web analytics: Tensile stress relaxation testing use case N2 - This study aims to represent an approach for transferring the materials testing datasets to the digital schema that meets the prerequisites of the semantic web. As a use case, the tensile stress relaxation testing method was evaluated and the testing datasets for several copper alloys were prepared. The tensile stress relaxation testing ontology (TSRTO) was modeled following the test standard requirements and by utilizing the appropriate upper-level ontologies. Eventually, mapping the testing datasets into the knowledge graph and converting the data-mapped graphs to the machine-readable Resource Description Framework (RDF) schema led to the preparation of the digital version of testing data which can be efficiently queried on the web. KW - Digitalization KW - Tensile stress relaxation KW - Ontology KW - Mechanical testing KW - Semantic web PY - 2024 DO - https://doi.org/10.4028/p-xSmHN2 VL - 987 SP - 47 EP - 52 PB - Trans Tech Publications Ltd CY - Switzerland AN - OPUS4-61152 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bhadeliya, Ashok A1 - Rehmer, Birgit A1 - Skrotzki, Birgit A1 - Jokisch, Torsten A1 - Olbricht, Jürgen A1 - Fedelich, Bernard T1 - Fatigue crack growth in nickel-based alloy 247DS with side-brazed pre-sintered preform N2 - Pre-sintered preform (PSP) brazing is employed in the repair of gas turbine components made of nickel-based alloys, including restoring the surface and dimensions of turbine blades and vanes. This study investigates the fatigue crack growth (FCG) behavior of Alloy 247DS specimens with side-brazed PSP material, mimicking a typical sandwich structure formed during such repairs. FCG tests were conducted at an elevated temperature of 950 °C and a stress ratio (R) of 0.1 on specimens with PSP layer thicknesses of 1.5 mm, 2 mm, 3 mm, and 4.5 mm to assess the influence of PSP thickness on fatigue crack growth behavior. Fractographic and metallographic analyses were performed to elucidate the underlying crack growth mechanisms and the microstructural characteristics of both materials. The results revealed that a crack consistently initiated in the PSP material, originating from the starter notch, particularly at the specimen corner during the pre-cracking phase. Additionally, crack propagation in the PSP material consistently advanced ahead of the crack in the Alloy 247DS. This crack growth behavior is attributed to the difference in elastic properties and microstructural differences between the PSP and base material. Metallographic analysis revealed the presence of porosity and brittle precipitates within the PSP material, which led to faster intergranular crack growth. Conversely, Alloy 247DS exhibited transgranular crack growth, contributing to the observed crack propagation behavior. This study demonstrates the applicability of standard FCG testing methods and an approach to characterize the FCG behavior in sandwich specimens, where crack growth occurs simultaneously in both materials, providing a preliminary understanding of crack growth behavior in Alloy 247DS with side-brazed PSP. KW - High-temperature fatigue crack growth (FCG) KW - Nickel-based alloys KW - Alloy 247DS KW - Pre-Sintered Preform (PSP) PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-629783 DO - https://doi.org/10.1016/j.ijfatigue.2025.108961 VL - 197 SP - 1 EP - 13 PB - Elsevier BV AN - OPUS4-62978 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pulz, Robert A1 - Rehmer, Birgit A1 - Skrotzki, Birgit T1 - Thermoschock - Interpretation von makroskopischen Bruchmerkmalen / Thermal shock - an interpretation of the macroscopic characteristics of fracture N2 - Der vorliegende Beitrag beschreibt typische Bruchmuster, die an SSiC Proben nach Thermoschockexperimenten beobachtet wurden und korreliert diese qualitativ mit der aufgebrachten Belastung. Der Thermoschock wird durch eine schnelle, in der Probenmitte beginnende spiralförmige Aufheizung dünner Scheiben mit Laserstrahlung realisiert. Durch diese Versuchsführung wandert ein zunehmender Temperaturgradient von der Mitte beginnend in radialer Richtung durch die Probe. Dieser Temperaturgradient ist für die Ausbildung von Druckspannungen im Probeninneren und Zugspannungen im kalten Randbereich der Probe verantwortlich. Beim Erreichen einer kritischen, versagensrelevanten Spannung tritt Probenbruch auf. Dabei wird die bis zu diesem Zeitpunkt in der Probe gespeicherte elastische Energie teilweise in die Schaffung von Rissoberflächen umgewandelt. Der Zusammenhang zwischen gespeicherter elastischer Energie und Bruchmuster wird dargestellt. KW - Thermoschock KW - Fraktographie KW - Elastische Energie KW - SSiC PY - 2010 DO - https://doi.org/10.3139/147.110081 SN - 0032-678X N1 - Sprachen: Deutsch/Englisch - Languages: German/English VL - 47 IS - 6 SP - 302 EP - 312 PB - Hanser CY - München AN - OPUS4-21515 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Koch, Bernd A1 - Skrotzki, Birgit T1 - Strain controlled fatigue testing of the metastable Beta-titanium alloy Ti-6.8Mo-4.5Fe-1.5Al (Timetal LCB) N2 - The present work covers the mechanical behaviour of Timetal LCB under fatigue loading and utilizes transmission electron microscopy (TEM) to study the associated microstructural evolution. Fatigue specimens were taken out of LCB wire made for automotive suspension spring manufacturing in a solution treated as well as an additionally aged state. Uniaxial fatigue tests were carried out in total strain control with R = 0.1. Solution treated specimens tested at 3% and 4% maximum total strain showed a saturating force response, which differed from all other total strain controlled tests, and a distinct fracture behaviour. In addition, an increase of the dynamic Young's modulus is observed under these test conditions and in this material state. These findings are interpreted as a deformation induced precipitation of nanosize α- or ω-phase. In the aged state, the α-phase carries the major part of deformation work, noticeable by distinct α-substructures in fatigued specimen states. KW - Titanium alloys KW - Fatigue KW - Transmission electron microscopy KW - Fracture PY - 2011 DO - https://doi.org/10.1016/j.msea.2011.04.031 SN - 0921-5093 SN - 1873-4936 VL - 528 IS - 18 SP - 5999 EP - 6005 PB - Elsevier CY - Amsterdam AN - OPUS4-23731 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schicker, Johannes A1 - Sievert, Rainer A1 - Fedelich, Bernard A1 - Klingelhöffer, Hellmuth A1 - Skrotzki, Birgit T1 - Versagensabschätzung thermomechanisch belasteter Heissteile in Turboladern KW - Computersimulation KW - Materialmodell KW - Chaboche KW - Schädigung KW - Lebensdauerabschätzung PY - 2010 SN - 0024-8525 VL - 71 IS - 6 SP - 444 EP - 450 PB - Springer Automotive Media, GWV-Fachverl. CY - Wiesbaden AN - OPUS4-21290 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nies, Daniel A1 - Rehmer, Birgit A1 - Skrotzki, Birgit A1 - Vaßen, R. T1 - Damage characterization of thermal barrier coatings by acoustic emission and thermography N2 - Thermal barrier coatings allow increasing the operating temperature and efficiency of land-, sea-, or air-based turbines. As failure of the coating may result in serious damage of the turbine, reliable estimation of its lifetime is essential. To assess the lifetime, cyclic tests are conceived to combine thermal loading by heating the surface of the coating with laser irradiation and nondestructive methods for damage determination. Using laser irradiation allows a high reproducibility of the thermal load. The temperature of the sample surface during thermal loading is determined by an infrared-camera which also enables the possibility to detect damage in the coating via thermography. Additionally, four acoustic sensors, attached to the experimental setup, are used to detect damage in the sample and determine the source of acoustic events. Results of acoustic emission correlate well with thermographic images that visualize the formation and evolution of damage through delaminations in the samples. PY - 2012 DO - https://doi.org/10.1002/adem.201200107 SN - 1438-1656 VL - 14 IS - 9 SP - 790 EP - 794 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-26536 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -