TY - JOUR A1 - Beygi Narsabadi, Hossein A1 - Vafaeenezhad, H. A1 - Klotz, U.E. A1 - Tiberto, D. A1 - Hosseinabadi, F. A1 - Mishurova, Tatiana A1 - Bruno, Giovanni A1 - Skrotzki, Birgit T1 - XCT-assisted micromechanical modeling of the effect of pores on the plastic deformation and mechanical characteristics of PBF-LB/M-produced copper alloys N2 - Due to the low absorption of fiber laser by copper particles, the laser-based powder bed fusion (PBF-LB/M) processing of copper components is accompanied by the development of different types of porosities within the printed samples. This research aims to assess the consequences of various process-induced pores on the me chanical characteristics and deformation of PBF-LB/M-produced copper alloys. Several copper alloys were processed using metal-coated particles and varied laser intensities, yielding samples with different types and amounts of porosities. For instance, CuCrZr alloys processed at 325 J/mm³ and 257 J/mm³ had 0.009 % and 1.117 % porosities, dominated by keyhole and lack-of-fusion pores, respectively. Moreover, PBF-LB/M pro cessing of Cr- and Nb-coated CuNi3SiCr particles accompanied by the generation of 0.004 % and 1.861 % porosities within the samples, predominantly featuring metallurgical and oxidation pores, respectively. Compression and nanoindentation tests revealed that the CuNi3SiCr alloy exhibited superior mechanical properties compared to the CuCrZr sample (nanoindentation hardness values 2.2 GPa and 1.4 GPa, respectively), while the presence of lack-of-fusion pores notably diminished their mechanical performance. X-ray computed tomography (XCT) reconstruction slices and scanning electron microscopy (SEM) images were then used for developing the representative volume elements (RVEs) based micromechanical models. The micromechanical simulations established a structure-property correlation that can simulate the compressive deformation and mechanical characteristics of PBF-LB/M-produced copper alloys as a function of their incorporated pore characteristics. Due to the closure of the pores at the first stages of deformation, samples with minimal keyhole and metallurgical porosities exhibited homogeneous plastic deformation. On the other side, based on the JohnsonCook model, strain concentration and crack propagation around the lack-of-fusion pores lead to damage initi ation in the printed samples at a strain level of 5 % KW - X-ray Computed tomography KW - Defects KW - Copper alloys KW - PBF-LB/M KW - Micromechanics PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-624004 DO - https://doi.org/10.1016/j.msea.2025.147836 SN - 0921-5093 VL - 924 PB - Elsevier B.V. AN - OPUS4-62400 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schröder, Jakob A1 - Han, Ying A1 - Fritsch, Tobias A1 - Hejazi, Bardia A1 - Ulbricht, Alexander A1 - Skrotzki, Birgit A1 - Bruno, Giovanni T1 - X-ray computed tomography quantifies primary phases and reveals crack morphology in high-cycle fatigue of aluminum alloy EN AW-2618A N2 - Since the introduction of high-strength aluminum alloys understanding their fatigue behavior is of high interest for the structural integrity of engineering components, in this context, the alloy EN AW-2618A gains its high strength from both nanometer size precipitates and micrometer size primary phases. The latter phases are often identified as crack initiation sites. In this study, it uses a combination of synchrotron and laboratory-based X-ray computed tomography to image and quantify such primary phases and the fatigue cracks appearing in interrupted tests. Based on the gray-level differences in the synchrotron X-ray computed tomography scans, this study is able to distinguish low- and high-absorbing particles. The dominant (volume fraction >99%) high absorbing primary phase can be quantified in good agreement with results of Thermo-Calc calculations. To image the fatigue crack, laboratory X-ray computed tomography scans are performed at different tensile loads to open the crack. The results show that with an appropriate crack opening tensile load, the fatigue crack morphology can be reliably revealed. Based on these results, the influence of the primary phases on the fatigue crack initiation and propagation are discussed. KW - X-ray computed tomography KW - Fatigue KW - Aluminum KW - Primary phases PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-632724 DO - https://doi.org/10.1002/adem.202500235 SN - 1527-2648 SP - 1 EP - 9 PB - Wiley-VCH CY - Weinheim AN - OPUS4-63272 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sonntag, Nadja A1 - Cabeza, S. A1 - Kuntner, M. A1 - Mishurova, Tatiana A1 - Klaus, M. A1 - Kling e Silva, L. A1 - Skrotzki, Birgit A1 - Genzel, Ch. A1 - Bruno, Giovanni T1 - Visualisation of deformation gradients in structural steel by macroscopic magnetic domain distribution imaging (Bitter technique) N2 - Abstract While classically used to visualise the magnetic microstructure of functional materials (e.g., for magnetic applications), in this study, the Bitter technique was applied for the first time to visualise macroscopic deformation gradients in a polycrystalline low-carbon steel. Spherical indentation was chosen to produce a multiaxial elastic–plastic deformation state. After removing the residual imprint, the Bitter technique was applied, and macroscopic contrast differences were captured in optical microscopy. To verify this novel characterisation technique, characteristic “hemispherical” deformation zones evolving during indentation were identified using an analytical model from the field of contact mechanics. In addition, near-surface residual stresses were determined experimentally using synchrotron radiation diffraction. It is established that the magnetic domain distribution contrast provides deformation-related information: regions of different domain wall densities correspond to different “hemispherical” deformation zones (i.e., to hydrostatic core, plastic zone and elastic zone, respectively). Moreover, the transitions between these three zones correlate with characteristic features of the residual stress profiles (sign changes in the radial and local extrema in the hoop stress). These results indicate the potential of magnetic domain distribution imaging: visualising macroscopic deformation gradients in fine-grained ferromagnetic material with a significantly improved spatial resolution as compared to integral, mean value-based measurement methods. KW - Bitter technique KW - Deformation KW - Expanding cavity model KW - Indentation KW - Magnetic domain distribution KW - Residual stress PY - 2018 DO - https://doi.org/10.1111/str.12296 SN - 1475-1305 VL - 54 IS - 6 SP - e12296, 1 EP - 15 PB - Wiley AN - OPUS4-46569 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schicker, Johannes A1 - Sievert, Rainer A1 - Fedelich, Bernard A1 - Klingelhöffer, Hellmuth A1 - Skrotzki, Birgit T1 - Versagensabschätzung thermomechanisch belasteter Heissteile in Turboladern KW - Computersimulation KW - Materialmodell KW - Chaboche KW - Schädigung KW - Lebensdauerabschätzung PY - 2010 SN - 0024-8525 VL - 71 IS - 6 SP - 444 EP - 450 PB - Springer Automotive Media, GWV-Fachverl. CY - Wiesbaden AN - OPUS4-21290 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Beygi Nasrabadi, Hossein A1 - Hanke, T. A1 - Weber, M. A1 - Eisenbart, M. A1 - Bauer, F. A1 - Meissner, R. A1 - Dziwis, G. A1 - Tikana, L. A1 - Chen, Yue A1 - Skrotzki, Birgit T1 - Toward a digital materials mechanical testing lab N2 - To accelerate the growth of Industry 4.0 technologies, the digitalization of mechanical testing laboratories as one of the main data-driven units of materials processing industries is introduced in this paper. The digital lab infrastructure consists of highly detailed and standard-compliant materials testing knowledge graphs for a wide range of mechanical testing processes, as well as some tools that enable the efficient ontology development and conversion of heterogeneous materials’ mechanical testing data to the machine-readable data of uniform and standardized structures. As a basis for designing such a digital lab, the mechanical testing ontology (MTO) was developed based on the ISO 23718 and ISO/IEC 21838-2 standards for the semantic representation of the mechanical testing experiments, quantities, artifacts, and report data. The trial digitalization of materials mechanical testing lab was successfully performed by utilizing the developed tools and knowledge graph of processes for converting the various experimental test data of heterogeneous structures, languages, and formats to standardized Resource Description Framework (RDF) data formats. The concepts of data storage and data sharing in data spaces were also introduced and SPARQL queries were utilized to evaluate how the introduced approach can result in the data retrieval and response to the competency questions. The proposed digital materials mechanical testing lab approach allows the industries to access lots of trustworthy and traceable mechanical testing data of other academic and industrial organizations, and subsequently organize various data-driven research for their faster and cheaper product development leading to a higher performance of products in engineering and ecological aspects. KW - General Engineering KW - General Computer Science PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-582698 DO - https://doi.org/10.1016/j.compind.2023.104016 SN - 0166-3615 VL - 153 SP - 1 EP - 15 PB - Elsevier B.V. AN - OPUS4-58269 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Häusler, Ines A1 - Darvishi Kamachali, Reza A1 - Hetaba, W. A1 - Skrotzki, Birgit T1 - Thickening of T-1 Precipitates during Aging of a High Purity Al–4Cu–1Li–0.25Mn Alloy N2 - The age hardening response of a high-purity Al–4Cu–1Li–0.25Mn alloy (wt. %) during isothermal aging without and with an applied external load was investigated. Plate shaped nanometer size T1 (Al2CuLi) and θ′ (Al2Cu) hardening phases were formed. The precipitates were analyzed with respect to the development of their structure, size, number density, volume fraction and associated transformation strains by conducting transmission electron microscopy (TEM) and scanning transmission electron microscopy (STEM) studies in combination with geometrical Phase analysis (GPA). Special attention was paid to the thickening of T1 phase. Two elementary types of single-layer T1 precipitate, one with a Li-rich (Type 1) and another with an Al-rich (Defect Type 1) central layer, were identified. The results show that the Defect Type 1 structure can act as a precursor for the Type 1 structure. The thickening of T1 precipitates occurs by alternative stacking of These two elementary structures. The thickening mechanism was analyzed based on the magnitude of strain associated with the precipitation transformation normal to its habit plane. Long-term aging and aging under load resulted in thicker and structurally defected T1 precipitates. Several types of defected precipitates were characterized and discussed. For θ′ precipitates, a ledge mechanism of thickening was observed. Compared to the normal aging, an external load applied to the peak aged state leads to small variations in the average sizes and volume fractions of the precipitates. KW - Al-Cu-Li-alloy KW - Precipitation KW - T1 precipitate KW - Microstructure evolution KW - Thickening KW - Creep KW - Volume fraction KW - Number density KW - Strain difference PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-471207 DO - https://doi.org/10.3390/ma12010030 SN - 1996-1944 VL - 12 IS - 1 SP - 30, 1 EP - 23 PB - MDPI AN - OPUS4-47120 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pulz, Robert A1 - Rehmer, Birgit A1 - Skrotzki, Birgit T1 - Thermoschock - Interpretation von makroskopischen Bruchmerkmalen / Thermal shock - an interpretation of the macroscopic characteristics of fracture N2 - Der vorliegende Beitrag beschreibt typische Bruchmuster, die an SSiC Proben nach Thermoschockexperimenten beobachtet wurden und korreliert diese qualitativ mit der aufgebrachten Belastung. Der Thermoschock wird durch eine schnelle, in der Probenmitte beginnende spiralförmige Aufheizung dünner Scheiben mit Laserstrahlung realisiert. Durch diese Versuchsführung wandert ein zunehmender Temperaturgradient von der Mitte beginnend in radialer Richtung durch die Probe. Dieser Temperaturgradient ist für die Ausbildung von Druckspannungen im Probeninneren und Zugspannungen im kalten Randbereich der Probe verantwortlich. Beim Erreichen einer kritischen, versagensrelevanten Spannung tritt Probenbruch auf. Dabei wird die bis zu diesem Zeitpunkt in der Probe gespeicherte elastische Energie teilweise in die Schaffung von Rissoberflächen umgewandelt. Der Zusammenhang zwischen gespeicherter elastischer Energie und Bruchmuster wird dargestellt. KW - Thermoschock KW - Fraktographie KW - Elastische Energie KW - SSiC PY - 2010 DO - https://doi.org/10.3139/147.110081 SN - 0032-678X N1 - Sprachen: Deutsch/Englisch - Languages: German/English VL - 47 IS - 6 SP - 302 EP - 312 PB - Hanser CY - München AN - OPUS4-21515 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kühn, Hans-Joachim A1 - Rehmer, Birgit A1 - Skrotzki, Birgit T1 - Thermomechanical fatigue of heat-resistant austenitic cast iron EN-GJSA-XNiSiCr35-5-2 (Ni-Resist D-5S) N2 - TMF tests were carried out on EN-GJSA-XNiSiCr35-5-2 at constant minimum temperature (400 °C) and varying maximum temperatures (Tmax = 700 °C, 800 °C, 900 °C) with hold times of 180 s at Tmax and two phase angles (in-phase (IP), 180° out-of-phase (OP)). The results showed a comparable strength under OP- and IP-TMF loading. At Tmax = 700 °C and 900 °C, the lifetime in IP-tests was slightly longer than that of OP-tests, while it is vice versa at Tmax = 800 °C. The IP-tests at Tmax = 900 °C showed a similar lifetime as OP-tests at Tmax = 700 °C and 800 °C, which was unexpected for such a high testing temperature. All IP-tests at Tmax = 900 °C showed a continuous cyclic softening from the beginning on, which was different from all other testing conditions. Complementary metallographic investigations indicated that under this test condition, intergranular creep damage is present in the volume of the test pieces. T2 - 3rd International Workshop on Thermo-Mechanical Fatigue (TMF-Workshop 2016) CY - Berlin, Germany DA - 27.04.2016 KW - Cast iron KW - Cracks KW - Cyclic softening KW - Microscopy KW - Thermomechanical fatigue PY - 2017 DO - https://doi.org/10.1016/j.ijfatigue.2017.01.009 SN - 0142-1123 SN - 1879-3452 VL - 99 IS - 2 (Special issue: Recent developments in thermo-mechanical fatigue) SP - 295 EP - 302 PB - Elsevier CY - Oxford AN - OPUS4-39680 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pulz, Robert A1 - Rehmer, Birgit A1 - Schneider, G.A. A1 - Skrotzki, Birgit T1 - Thermal shock study on different advanced ceramics by laser irradiation in different media N2 - The thermal shock behavior of three commercial-advanced ceramics (SSiC, MgO–PSZ, Al2O3) is characterized in air and vacuum applying a laser thermal shock. The available testing system permits the reproducible setting of defined temperature profiles in thin disks and allows a heating-up thermal shock in various media. Due to the accurate determination of the time- and space-resolved temperature distribution, the local stress state can be calculated as a function of time. It is shown that the thermal shock strength is highest for SSiC and lowest in Al2O3 with MgO–PSZ in between. The approach presented in this work allows quantifying the stress state at failure in terms of tangential tensile stress. The investigated environment does not affect the thermal shock resistance under the studied experimental conditions. KW - Laser-thermal shock KW - Advanced ceramic KW - Stress distribution KW - Thermal shock stress KW - Weibull statistics PY - 2016 UR - http://onlinelibrary.wiley.com/doi/10.1002/adem.201500162/full DO - https://doi.org/10.1002/adem.201500162 SN - 1438-1656 VL - 18 IS - 1 SP - 132 EP - 140 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-33456 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sonntag, Nadja A1 - Skrotzki, Birgit A1 - Stegemann, Robert A1 - Löwe, Peter A1 - Kreutzbruck, M. T1 - The role of surface topography on deformation-induced magnetization under inhomogeneous elastic-plastic deformation N2 - It is widely accepted that the magnetic state of a ferromagnetic material may be irreversibly altered by mechanical loading due to magnetoelastic effects. A novel standardized nondestructive testing (NDT) technique uses weak magnetic stray fields, which are assumed to arise from inhomogeneous deformation, for structural health monitoring (i.e., for detection and assessment of damage). However, the mechanical and microstructural complexity of damage has hitherto only been insufficiently considered. The aim of this study is to discuss the phenomenon of inhomogeneous “self-magnetization” of a polycrystalline ferromagnetic material under inhomogeneous deformation experimentally and with stronger material-mechanical focus. To this end, notched specimens were elastically and plastically deformed. Surface magnetic states were measured by a three-axis giant magnetoresistant (GMR) sensor and were compared with strain field (digital image correlation) and optical topography measurements. It is demonstrated that the stray fields do not solely form due to magnetoelastic effects. Instead, inhomogeneous plastic deformation causes topography, which is one of the main origins for the magnetic stray field formation. Additionally, if not considered, topography may falsify the magnetic signals due to variable lift-off values. The correlation of magnetic vector components with mechanical tensors, particularly for multiaxial stress/strain states and inhomogeneous elastic-plastic deformations remains an issue. KW - Magnetic stray fields KW - Magnetomechanical effect KW - Damage KW - Topography KW - Multiaxial deformation KW - Notch KW - Plastic deformation KW - Metal magnetic memory KW - Digital image correlation KW - Structural steel PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-457878 DO - https://doi.org/10.3390/ma11091518 SN - 1996-1944 VL - 11 IS - 9 SP - 1518, 1 EP - 26 PB - MDPI CY - Basel, Switzerland AN - OPUS4-45787 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sturm, D. A1 - Heilmaier, M. A1 - Schneibel, J.H. A1 - Jéhanno, P. A1 - Skrotzki, Birgit A1 - Saage, H. T1 - The influence of silicon on the strength and fracture toughness of molybdenum N2 - Mo–Si alloys containing up to 1 wt.% Si were fabricated by powder-metallurgical processing and their lattice parameters, elastic constants, densities, grain sizes, strengths, ductilities, and fracture toughness values were measured. The yield strength was insensitive to the grain size, i.e., a Hall–Petch relationship was not observed. Generally, Si additions caused pronounced solid solution strengthening. However, for small Si concentrations (≤0.1 wt.%) solid solution softening was observed at room temperature and below. With increasing Si concentration, the room temperature ductility and fracture toughness dropped precipitously. This is attributed to the increase in strength and a transition from transgranular to intergranular fracture. KW - Molybdenum KW - Solid solution strengthening KW - Solid solution softening KW - Hall-Petch relationship PY - 2007 SN - 0921-5093 SN - 1873-4936 VL - 463 IS - 1-2 SP - 107 EP - 114 PB - Elsevier CY - Amsterdam AN - OPUS4-14820 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Jürgens, Maria A1 - Sonntag, Nadja A1 - Olbricht, Jürgen A1 - Fedelich, Bernard A1 - Skrotzki, Birgit T1 - The effect of dwell times on the thermomechanical fatigue life performance of grade P92 steel at intermediate and low strain amplitudes N2 - Results of an extended TMF test program on grade P92 steel in the temperature range of 620 °C - 300 °C, comprising in-phase (IP) and out-of-phase (OP) tests, partly performed with symmetric dwells at Tmax/Tmin, are presented. In contrast to previous studies, the low-strain regime is also illuminated, which approaches flexible operation in a power plant with start/stop cycles. At all strain amplitudes, the material performance is characterized by continuous cyclic softening, which is retarded in tests at lower strains but reaches similar magnitudes in the course of testing. In the investigated temperature range, the phase angle does not affect fatigue life in continuous experiments, whereas the IP condition is more detrimental in tests with dwells. Fractographic analyses indicate creep-dominated and fatigue-dominated damage for IP and OP, respectively. Analyses of the (micro)hardness distribution in the tested specimens suggest an enhanced microstructural softening in tests with dwell times for the low- but not for the high-strain regime. To rationalize the obtained fatigue data, the fracture-mechanics-based D_TMF concept, which was developed for TMF life assessment of ductile alloys, was applied. It is found that the D_TMF parameter correlates well with the measured fatigue lives, suggesting that subcritical growth of cracks (with sizes from a few microns to a few millimeters) governs failure in the investigated range of strain amplitudes. KW - 9-12%Cr steel KW - Thermomechanical fatigue KW - Symmetric dwell periods KW - Low strain KW - Parametric modeling PY - 2021 DO - https://doi.org/10.1016/j.msea.2020.140593 VL - 805 SP - 140593 PB - Elsevier B.V. AN - OPUS4-52374 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nies, Daniel A1 - Pulz, Robert A1 - Glaubitz, Steffen A1 - Finn, Monika A1 - Rehmer, Birgit A1 - Skrotzki, Birgit T1 - Testing of thermal barrier coatings by laser excitation N2 - Thermal barrier coatings (TBCs) are used to increase the operating temperature of land-, sea-, or air-based turbines. As failure of the coating may result in serious damage of the turbine, reliable estimation of the lifetime is essential. Most experiments to assess the lifetime or to determine parameters for simulations of the behavior of TBCs are done by burner-rig-tests, where the operating conditions are simulated by cyclic heating of the surface and cooling of the backside of a coated sample. In this work a possibility is presented to do comparable experiments by heating the surface with laser irradiation instead of a burner. For this purpose a Nd:YAG-laser with a maximum output power of 1?kW and a wavelength of 1064?nm is used. The laser spot can be moved by integrated optics across the sample surface to achieve homogeneous heating of the coating. Cooling of the backside is done by air. The temperature of the sample surface is determined by an infrared-camera which also enables the possibility to detect failures in the coating via thermography. Additionally, acoustic sensors attached to the sample holder are used to detect failures in the sample. The investigated ceramic material (yttria stabilized zirconia) has a very low absorption coefficient at the used laser wavelength. Therefore, a pre-treatment of the samples was needed to increase the absorption coefficient to be able to heat up the samples. In this paper, the experimental setup and first experimental results are presented. KW - Thermal barrier coating (TBC) KW - Yttria stabilized zirconia KW - Laser irradiation KW - Acoustic emission KW - Thermography PY - 2010 DO - https://doi.org/10.1002/adem.201000212 SN - 1438-1656 VL - 12 IS - 12 SP - 1224 EP - 1229 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-22896 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sonntag, Nadja A1 - Piesker, Benjamin A1 - Ávila Calderón, Luis A1 - Mohr, Gunther A1 - Rehmer, Birgit A1 - Agudo Jácome, Leonardo A1 - Hilgenberg, Kai A1 - Evans, Alexander A1 - Skrotzki, Birgit T1 - Tensile and Low‐Cycle Fatigue Behavior of Laser Powder Bed Fused Inconel 718 at Room and High Temperature N2 - This study investigates the room‐ and high‐temperature (650 °C) tensile and low‐cycle‐fatigue behavior of Inconel 718 produced by laser powder bed fusion (PBF‐LB/M) with a four‐step heat treatment and compares the results to the conventional wrought material. The microstructure after heat treatment is characterized on different length scales. Compared to the wrought variant, the elastic and yield properties are comparable at both test temperatures while tensile strength, ductility, and strain hardening capacity are lower. The fatigue life of the PBF‐LB/M variant at room temperature is slightly lower than that of the wrought material, while at 650 °C, it is vice versa. The cyclic stress response for both material variants is characterized by cyclic softening, which is more pronounced at the higher test temperature. High strain amplitudes (≥0.7%) at room temperature and especially a high testing temperature result in the formation of multiple secondary cracks at the transitions of regions comprising predominantly elongated grain morphology and columns of stacked grains with ripple patterns in the PBF‐LB/M material. This observation and pronounced crack branching and deflection indicate that the cracks are controlled by sharp micromechanical gradients and local crystallite clusters. KW - Additive manufacturing KW - Fatigue damage KW - Heat treatment KW - Inconel 718 KW - Laser powder bed fusion KW - Low-cycle fatigue KW - Tensile strength PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-599316 DO - https://doi.org/10.1002/adem.202302122 SN - 1527-2648 SP - 1 EP - 17 PB - Wiley AN - OPUS4-59931 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Koch, Bernd A1 - Skrotzki, Birgit T1 - Strain controlled fatigue testing of the metastable Beta-titanium alloy Ti-6.8Mo-4.5Fe-1.5Al (Timetal LCB) N2 - The present work covers the mechanical behaviour of Timetal LCB under fatigue loading and utilizes transmission electron microscopy (TEM) to study the associated microstructural evolution. Fatigue specimens were taken out of LCB wire made for automotive suspension spring manufacturing in a solution treated as well as an additionally aged state. Uniaxial fatigue tests were carried out in total strain control with R = 0.1. Solution treated specimens tested at 3% and 4% maximum total strain showed a saturating force response, which differed from all other total strain controlled tests, and a distinct fracture behaviour. In addition, an increase of the dynamic Young's modulus is observed under these test conditions and in this material state. These findings are interpreted as a deformation induced precipitation of nanosize α- or ω-phase. In the aged state, the α-phase carries the major part of deformation work, noticeable by distinct α-substructures in fatigued specimen states. KW - Titanium alloys KW - Fatigue KW - Transmission electron microscopy KW - Fracture PY - 2011 DO - https://doi.org/10.1016/j.msea.2011.04.031 SN - 0921-5093 SN - 1873-4936 VL - 528 IS - 18 SP - 5999 EP - 6005 PB - Elsevier CY - Amsterdam AN - OPUS4-23731 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ta, N. A1 - Bilal, M. U. A1 - Häusler, I. A1 - Saxena, A. A1 - Lin, Y.-Y. A1 - Schleifer, F. A1 - Fleck, M. A1 - Glatzel, U. A1 - Skrotzki, Birgit A1 - Darvishi Kamachali, Reza T1 - Simulation of the θ′ Precipitation Process with Interfacial Anisotropy Effects in Al-Cu Alloys N2 - The effects of anisotropic interfacial properties and heterogeneous elasticity on the growth and ripening of plate-like θ′-phase (Al2Cu) in Al-1.69 at.% Cu alloy are studied. Multi-phase-field simulations are conducted and discussed in comparison with aging experiments. The precipitate/matrix interface is considered to be anisotropic in terms of its energy and mobility. We find that the additional incorporation of an anisotropic interfacial mobility in conjunction with the elastic anisotropy result in substantially larger aspect ratios of the precipitates closer to the experimental observations. The anisotropy of the interfacial energy shows comparably small effect on the precipitate’s aspect ratio but changes the interface’s shape at the rim. The effect of the chemo-mechanical coupling, i.e., the composition dependence of the elastic constants, is studied as well. We show that the inverse ripening phenomenon, recently evidenced for δ’ precipitates in Al-Li alloys (Park et al. Sci. Rep. 2019, 9, 3981), does not establish for the θ′ precipitates. This is because of the anisotropic stress fields built around the θ′ precipitates, stemming from the precipitate’s shape and the interaction among different variants of the θ′ precipitate, that disturb the chemo-mechanical effects. These results show that the chemo-mechanical effects on the precipitation ripening strongly depend on the degree of sphericity and elastic isotropy of the precipitate and matrix phases. KW - Aging KW - Phase-field simulation KW - Interfacial anisotropy KW - Chemo-mechanical coupling KW - Precipitation KW - Elasticity KW - θ′-(Al2Cu) precipitate phase PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-522672 DO - https://doi.org/10.3390/ma14051280 VL - 14 IS - 5 SP - 1280 PB - MDPI AN - OPUS4-52267 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Jentzsch, Stefan A1 - Stock, Daniel A1 - Häcker, Ralf A1 - Skrotzki, Birgit A1 - Darvishi Kamachali, Reza A1 - Klingbeil, Dietmar A1 - Kindrachuk, Vitaliy T1 - Shear Band Formation with Split Hopkinson Bar Experiments N2 - The essence of dynamic failure is closely linked to dramatic shear deformations which often lead to the formation of adiabatic shear bands (ASB). Under high loading velocities and the subsequent rapid temperature increase, the localization of shear strain is crucial in view of safety issues of systems in mechanical and aircraft engineering, especially with respect to fast rotating components and diverse crash scenarios. In this research, we perform high speed impact tests at the split Hopkinson pressure bar (SHPB) setup and use particular hat-shaped specimen geometries that resemble the stresses and failure conditions at the component level. In the first step, we specify a notched specimen geometry using finite element (FE) simulations to ensure pure shear. Further, quasi-static compressive tests and a series of impact tests at high strain rates of 10^3-10^4 s^-1 are conducted on specimens manufactured from a fine-grain structural steel with the properties of S355. Optical microscopy and electron backscatter diffraction (EBSD) of the sheared zones unveil significant localization to maximal shear strains of about 0.9 accompanied by grain refinement by factors 5 to 14. The displacements across the surface of the specimens are captured with subset-based local digital image correlation (DIC) during the impact time, and serve as an objective to validate a viscoplastic constitutive relationship. More precisely, the deformation distribution is accurately reproduced by the widely recognized Johnson-Cook (JC) model, which features an enhanced description of damage evolution. Thus, combining experimental and characterization techniques, continuum mechanics and reasonable optimization strategies for the identification of model parameters provides an efficient approach for comprehensive insights into the strain localization behaviour and its impact on the mechanical performance of S355 under extreme strain rates and deformations. KW - Adiabatic shear bands KW - Finite element analysis KW - Viscoplastic material modelling KW - Split Hopkinson pressure bar KW - Hat-shaped specimen KW - Johnson–Cook parameter identification PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-613339 DO - https://doi.org/10.1016/j.ijmecsci.2024.109749 VL - 284 SP - 1 EP - 14 PB - Elsevier BV AN - OPUS4-61333 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Beygi Nasrabadi, Hossein A1 - Hanke, Thomas A1 - Skrotzki, Birgit T1 - Semantic Representation of Low‐Cycle‐Fatigue Testing Data Using a Fatigue Test Ontology and ckan.kupferdigital Data Management System N2 - Addressing a strategy for publishing open and digital research data, this article presents the approach for streamlining and automating the process of storage and conversion of research data to those of semantically queryable data on the web. As the use case for demonstrating and evaluating the digitalization process, the primary datasets from low‐cycle‐fatigue testing of several copper alloys are prepared. The fatigue test ontology (FTO) and ckan.kupferdigital data management system are developed as two main prerequisites of the data digitalization process. FTO has been modeled according to the content of the fatigue testing standard and by reusing the basic formal ontology, industrial ontology foundry core ontology, and material science and engineering ontology. The ckan.kupferdigital data management system is also constructed in such a way that enables the users to prepare the protocols for mapping the datasets into the knowledge graph and automatically convert all the primary datasets to those machine‐readable data which are represented by the web ontology language. The retrievability of the converted digital data is also evaluated by querying the example competency questions, confirming that ckan.kupferdigital enables publishing open data that can be highly reused in the semantic web. KW - Accessible KW - CKAN KW - Interoperable KW - Digitalizations KW - Ontologies KW - Reusable data KW - Fatigue testing PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-604991 UR - https://onlinelibrary.wiley.com/doi/10.1002/adem.202400675 DO - https://doi.org/10.1002/adem.202400675 SN - 1527-2648 SP - 1 EP - 11 PB - Wiley AN - OPUS4-60499 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lin, Y.-Y. A1 - Schleifer, F. A1 - Holzinger, M. A1 - Ta, N. A1 - Skrotzki, Birgit A1 - Darvishi Kamachali, Reza A1 - Glatzel, U. A1 - Fleck, M. T1 - Quantitative Shape-Classification of Misfitting Precipitates during Cubic to Tetragonal Transformations: Phase-Field Simulations and Experiments N2 - The effectiveness of the mechanism of precipitation strengthening in metallic alloys depends on the shapes of the precipitates. Two different material systems are considered: tetragonal γ′′ precipitates in Ni-based alloys and tetragonal θ′ precipitates in Al-Cu-alloys. The shape formation and evolution of the tetragonally misfitting precipitates was investigated by means of experiments and phase-field simulations. We employed the method of invariant moments for the consistent shape quantification of precipitates obtained from the simulation as well as those obtained from the experiment. Two well-defined shape-quantities are proposed: (i) a generalized measure for the particles aspect ratio and (ii) the normalized λ2, as a measure for shape deviations from an ideal ellipse of the given aspect ratio. Considering the size dependence of the aspect ratio of γ′′ precipitates, we find good agreement between the simulation results and the experiment. Further, the precipitates’ in-plane shape is defined as the central 2D cut through the 3D particle in a plane normal to the tetragonal c-axes of the precipitate. The experimentally observed in-plane shapes of γ′′-precipitates can be quantitatively reproduced by the phase-field model. KW - γ″ phase KW - Phase-field simulation KW - Misfitting precipitate KW - Nickel-base alloy KW - Al-Cu alloy KW - θ′ phase KW - Precipitate shape PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-522743 DO - https://doi.org/10.3390/ma14061373 VL - 14 IS - 6 SP - 1373 PB - MDPI AN - OPUS4-52274 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Peter, D. A1 - Pfetzing, J. A1 - Wagner, M.F.-X. A1 - Somsen, C. A1 - Pesicka, J. A1 - Skrotzki, Birgit A1 - Eggeler, G. T1 - Quantitative Charakterisierung der Gefüge-Anisotropie einer stranggepressten TiAl-Legierung / Quantitative Characterisation and Microstructural Anisotropy of a Hot-Extruded TiAl Alloy KW - Titanaluminide KW - Mikrostruktur KW - Quantitative Analyse KW - Kriechen KW - Anisotropie PY - 2008 SN - 0032-678X N1 - Sprachen: Deutsch/Englisch - Languages: German/English VL - 45 IS - 5 SP - 210 EP - 224 PB - Hanser CY - München AN - OPUS4-17562 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -