TY - CONF A1 - Schraut, Katharina A1 - Adamczyk, Burkart A1 - Simon, Sebastian A1 - von Werder, Julia A1 - Meng, Birgit A1 - Stephan, Dietmar A1 - Adam, Christian T1 - Formation and hydraulic reactivity of an alite rich material from post treated basic oxygen furnace slag N2 - Basic oxygen furnace slag (BOFS) is a by-product of steelmaking of which about 10.4 Mt are produced annually in the EU. BOFS is mostly used in road construction, earthwork and hydraulic engineering. However, in this use, the iron bound in BOFS is lost and the opportunity to produce higher value products from BOFS is forgone. In recent decades, many researchers have investigated a thermochemical process to reduce iron oxides to metallic iron in molten BOFS. The metallic iron formed separates from the reduced slag due to its higher density and can be recovered. An advantage of this process is that simultaneously the chemical composition of the reduced slag is adapted to that of the Portland cement clinker and the hydraulic reactive mineral alite is formed. In this study, BOFS was reduced in a small-scale electric arc furnace using petrol coke as reducing agent, and the hydraulic properties of the reduced, low-iron BOFS were investigated. Despite a chemical and mineralogical composition similar to that of Portland cement clinker, the reduced BOFS produced less heat of hydration, and its reaction was delayed compared to Portland cement. However, the addition of gypsum, as is also done in cement production from Portland cement clinker, has been found to accelerate the hydration rate of reduced BOFS. Further research to improve the hydraulic properties of the reduced slag is essential. If successful, the production of a hydraulic binder and crude iron from BOFS could have economic and ecological benefits for both the cement and steel industry. T2 - GeoMin Köln 2022 CY - Cologne, Germany DA - 11.09.2022 KW - BOFS KW - Portland Cement KW - Hydraulic reactivity PY - 2022 AN - OPUS4-56080 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schraut, Katharina A1 - Adamczyk, Burkart A1 - Adam, Christian T1 - Reductive treatment of steel making slags to produce a hydraulic binder and crude iron N2 - Steelmaking slags are a by-product of steel production, that are currently used primarily in road construction, earthwork, and hydraulic engineering. In this use, the iron bound in the steelmaking slags (< 30 wt.%) is lost. Recovery of iron from steelmaking slags is possible by thermochemical reductive treatment. The reductive treatment of liquid steelmaking slags causes iron oxides to be reduced to metallic iron, which separates from the mineral phase due to its higher density. The chemical composition of the mineral phase is thus adapted to that of the Portland cement clinker and the mineral alite, the most important component of Portland cement, is formed. This way, crude iron can be recovered, and at the same time a hydraulic binder can be produced. This process, however, is uneconomical due to the high temperatures required (~1800 °C). In the current project, the process is to be adapted so that the reduction of liquid steelmaking slag can be carried out at ~1600 °C. The chemical composition is to be modified in such a way that the melting temperature of the slags as well as their viscosity are in a technically suitable range and still a product with good cementitious properties is obtained. T2 - LithiumDays CY - Online meeting DA - 06.12.2021 KW - BOFS KW - Portland Cement KW - Hydraulic reactivity PY - 2021 AN - OPUS4-56081 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schraut, Katharina A1 - Adamczyk, Burkart A1 - Simon, Sebastian A1 - von Werder, Julia A1 - Meng, Birgit A1 - Stephan, Dietmar A1 - Adam, Christian T1 - Portland cement clinker from reduced basic oxygen furnace slag N2 - Basic oxygen furnace slag (BOFS) is a by-product of the steelmaking process, of which about 10.4 Mt are produced annually in the European Union. Besides its predominant use in road construction, earthwork, and hydraulic engineering, it is also possible to use BOFS as a source material for Portland cement clinker. The main difference in the chemical composition of BOFS from the chemical composition of Portland cement clinker is its high content of iron oxides (7-50 wt.%). In recent decades, many researchers have investigated the production of both Portland cement clinker and crude iron from BOFS via thermochemical reductive treatment. Carbothermal treatment of liquid BOFS causes reduction of iron oxides to metallic iron, which separates from the mineral phase due to its higher density. In this study, German BOFS was reduced in a small-scale electric arc furnace using petrol coke as reducing agent. The produced low-iron mineral product was chemically similar to Portland cement clinker and contained the most important Portland cement mineral alite (Ca3SiO5) as main component. Besides alite, the mineral product contained other Portland cement clinker constituents such as belite (β-Ca2SiO4) and tricalcium aluminate (Ca3Al2O6). The production of Portland cement clinker and crude iron from BOFS has economic and ecological benefits for both the cement and steel industry. Cement clinker from reduced BOFS may be used as a substitute for cement clinker from conventional cement production, thereby CO2 emissions will be reduced. The steel industry benefits from a high-value application for its by-products that avoids cost expensive landfilling and may even bring economic advantages. However, reductive treatment requires high temperatures and, for economic reasons, has to be carried out immediately after casting of the liquid BOFS, which is a logistical challenge for most steel plants. A cost-benefit analysis is therefore essential. T2 - European Congress and Exhibition on Advanced Materials and Processes CY - Online meeting DA - 13.09.2021 KW - BOFS KW - Portland Cement KW - Hydraulic reactivity PY - 2021 AN - OPUS4-53475 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schraut, Katharina A1 - Adamczyk, Burkart A1 - Simon, Sebastian A1 - von Werder, Julia A1 - Meng, Birgit A1 - Stephan, D. A1 - Kargl, F. A1 - Adam, Christian T1 - Formation and chemical stabilisation of tricalcium-silicate during solidification from the melt of post-treated metallurgical slags T2 - Proceedings of the 15th International Congress on the Chemistry of Cement N2 - Tricalcium-silicate (C3S) or Alite is the most important mineral in Portland cement. Since pure tricalcium-silicate is only stable above temperatures of 1250 °C, its decomposition has to be prevented technically by fast cooling after the sintering process. At room temperature, the decomposition velocity is very slow so that metastable tricalcium-silicate is obtained. Although the mechanisms of clinker phase formation during burning process of Portland cement in a rotary kiln were solved and improved over the years, in view of possible economic and ecological benefits current projects aim to produce clinker phases from metallurgical slags. Recent studies discovered that the mineral phase which remained after a reducing treatment and separation of formed metallic iron from molten Linz-Donawitz (LD-) slags contained about 60 wt.% Alite despite it was cooled slowly. Because the results could be verified using slags from different origins and varying cooling velocities a chemical stabilisation of the Alite can be assumed. First tests in mortars indicate that workability, hardening and solid state properties are comparable with an ordinary Portland cement. An application of the observed phenomenon in cement production requires enhanced knowledge about formation and stabilisation conditions of Alite during crystallisation from melts in contrast to the sintering reactions in conventional Portland cement production. Therefore, this study focuses on the stabilisation mechanisms of Alite in consolidating melts. Samples from different melting experiments are analysed to determine stabilising factors. T2 - 15th International Congress on the Chemistry of Cement CY - Prag, Czech Republic DA - 16.09.2019 KW - Tricalcium-silicate KW - Portland Cement KW - Alite KW - Steelmaking slag PY - 2019 SP - Paper 492, 1 EP - 10 AN - OPUS4-49050 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schraut, Katharina A1 - Adamczyk, Burkart A1 - Simon, Sebastian A1 - von Werder, Julia A1 - Meng, Birgit A1 - Stephan, D. A1 - Adam, Christian T1 - Formation of tricalciumsilicate from post-treated metallurgical slags N2 - LD-slags differ from Ordinary Portland Cement (OPC) mainly in a higher content of iron oxides and a low content of Tricalciumsilicate (Alite). In the context of an improved resource usage, a procedure to convert LDslags into cement clinker was investigated. T2 - 15th International Congress on the Chemistry of Cement CY - Prague, Czech Republic DA - 16.09.2019 KW - Tricalcium-silicate KW - Portland Cement KW - Alite KW - Steelmaking slag PY - 2019 AN - OPUS4-49591 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -