TY - GEN A1 - Rhode, Michael A1 - Wetzel, Annica A1 - Oczan, Ozlem A1 - Nietzke, Jonathan A1 - Richter, Tim A1 - Schröpfer, Dirk T1 - Corrigendum: Hydrogen diffusion and local Volta potential in high- and medium-entropy alloys (2020 IOP Conf. Ser.: Mater. Sci. Eng. 882 012015) N2 - In the sub-section “2.1 Investigated materials” the chemical composition of Co, Cr and Mn was in wrong order for both HEA and MEA. The content of table 1 is here included in the correct version. PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-527050 DO - https://doi.org/10.1088/1757-899X/882/1/012027 VL - 882 SP - 1 EP - 2 PB - IOP Publishing CY - Bristol AN - OPUS4-52705 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Richter, Tim A1 - Diese, Marcel A1 - Rhode, Michael A1 - Schröpfer, Dirk T1 - Characterization of cracking phenomena in TIG welds of high and medium entropy alloy N2 - Multi-element systems with defined entropy (HEA - High Entropy Alloy or MEA - Medium Entropy Alloy) are rather new material concepts that are becoming increasingly important in materials research and development. Some HEA systems show significantly improved properties or combinations of properties, e.g., the overcome of the trade-off between high strength and ductility. Thus, the synthesis, the resulting microstructures, and properties of HEA have been primarily investigated so far. In addition, processing is crucial to achieve a transfer of potential HEA/MEA materials to real applications, e.g. highly stressed components. Since fusion welding is the most important joining process for metals, it is of vital importance to investigate the weldability of these materials. However, this has rarely been the subject of research up to date. For that reason, in this work the weldability depending on the surface preparation of a CoCrFeMnNi-HEA and a CoCrNi-MEA for TIG welding is investigated. The fusion welding of longer plates is described here for the first time for the CoCrNi alloy. The welds of both materials showed distinct formation of cracks in the heat affected zone (HAZ). Optical and scanning electron microscopy analysis clearly confirmed an intergranular fracture topography. But based on the results, the crack mechanism cannot be conclusively clarified as either a liquid metal embrittlement (LME) or hot cracking like liquid film separation occurred. T2 - 2nd International Conference on Advanced Joining Processes CY - Online meeting DA - 21.10.2021 KW - High Entropy Alloy KW - TIG welding KW - Cracking PY - 2021 AN - OPUS4-53607 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Becker, Amadeus A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas A1 - Michael, Thomas T1 - Konstruktive Einflüsse bei der beanspruchungsgerechten Reparatur geschweißter Bauteile aus hochfesten Feinkornbaustählen N2 - Für eine nachhaltige und ressourceneffiziente Fertigung von Windkraftanlagen ist der Einsatz moderner hochfester Feinkornbaustähle vielfach notwendig. Bei der Montage hochfester Stahlkonstruktionen kommt es trotz anforderungsgerechter schweißtechnischer Fertigung vereinzelt zur Detektion von unzulässigen Unregelmäßigkeiten im Schweißbereich. Derzeitige Normen und Verarbeitungsrichtlinien geben hierbei kaum Informationen zu adäquaten Reparaturkonzepten, insbesondere für hochfeste Stähle. Vor diesem Hintergrund werden an der Bundesanstalt für Materialforschung und -prüfung (BAM) bauteilrelevante Untersuchungen zu den schweißbedingten Beanspruchungen und Gefügeveränderungen bei der schweißtechnischen Reparatur durch lokales thermisches Ausfugen und erneutes Schweißen durchgeführt. Hierzu werden einige wesentliche Ergebnisse an Beispielen des Ingenieurbaus, mit Blick auf die mechanisch-technologischen Eigenschaften und Eigenspannungen erörtert. In einem aktuellen Vorhaben (FOSTA P1311, IGF 20162N) sind darauf aufbauend die Einflüsse durch die Schrumpfbehinderung und Wärmeführung beim Reparaturschweißen hochfester Feinkornbaustähle (S500MLO, S960QL) sowie die Reparaturzyklenanzahl Fokus systematischer Untersuchungen. Mittels strukturmechanischer Berechnungen ließen sich hierzu selbstbeanspruchende Probenformen identifizieren, die unterschiedliche definierte Steifigkeitsverhältnisse von Reparaturschweißnähten realer Bauteile abbilden. Schweißnähte an diesen bauteilähnlichen Proben weisen signifikant erhöhte schweißbedingte Beanspruchungen mit zunehmenden (Biege-)Einspanngraden auf. Im Vergleich mit bisherigen Erkenntnissen wird gezeigt, dass eine sichere Reparatur solcher Schweißnähte nur mittels optimaler Reparaturkonzepte und Wärmeführung gelingt, um diesen hohen Beanspruchungen und auch den speziellen Gefügen hochfester Stähle Rechnung zu tragen. Ziel der Untersuchungen ist es letztlich, Empfehlungen für beanspruchungs- und werkstoffgerechte Reparaturkonzepte gerade für KMU abzuleiten, um Schäden und zumeist teure Nacharbeiten zu vermeiden. T2 - 4. Niedersächsisches Symposium Materialtechnik CY - Online meeting DA - 25.02.2021 KW - Eigenspannungen KW - Gefügedegradation KW - Hochfester Feinkornbaustahl KW - Reparatur KW - Schweißen PY - 2021 SN - 978-3-8440-8021-6 SN - 2364-0804 VL - 10 SP - 488 EP - 501 PB - Shaker Verlag CY - Düren AN - OPUS4-53315 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scharf-Wildenhain, R. A1 - Hälsig, A. A1 - Schröpfer, Dirk A1 - Wandtke, Karsten A1 - Kannengießer, Thomas T1 - Wire Arc Additive Manufacturing (WAAM) mit hochfesten Feinkornbaustählen N2 - Die additive Verarbeitung hochfester Feinkornbaustähle mittels Wire Arc Additive Manufacturing (WAAM) ist ein komplexes, aber zugleich auch effizientes Verfahren, bei dem Werkstoff, Bauteilgeometrie und Schweißprozess gezielt aufeinander abgestimmt sein müssen. Ziel dieser Studie war es, einen Zusammenhang zwischen den Prozessparametern und der generierten Schichtgeometrie zu ermitteln. Dazu wurden definierte Referenzkörper mit einem robotergestützten Schweißsystem additiv gefertigt und hinsichtlich Schichthöhe, Wandstärke und Mikrostruktur analysiert. Fokus der Untersuchung waren sowohl konventionelle als auch für die WAAM-Fertigung speziell entwickelte hochfeste Schweißzusatzwerkstoffe. Die geometrischen Eigenschaften additiv gefertigter Bauteile lassen sich insbesondere durch die Faktoren Drahtvorschubgeschwindigkeit und Schweißgeschwindigkeit gezielt einstellen. Jedoch können diese Parameter nicht beliebig variiert werden, auch aufgrund der rheologischen Eigenschaften der Zusatzwerkstoffe. Zu hohe Streckenenergien führen zu lokalen Überhitzungen und Fehlstellen in der generierten Schicht. Undefinierte Fließ- und Erstarrungsvorgänge im überhitzten Bereich erschweren die maßhaltige Fertigung. Deshalb wird bei speziellen WAAM-Schweißdrähten das Fließverhalten gezielt modifiziert, sodass es über einen größeren Temperaturbereich hinweg konstant ist. Erst die Kenntnis über die komplexen Zusammenhänge zwischen den Prozessparametern und der Bauteilgeometrie ermöglicht die Erzeugung exakter Schichtmodelle für die additive Fertigung. Dies bildet die Grundlage für die Bearbeitung weiterer Fragestellungen auf dem Gebiet der additiven Fertigung mit hochfesten Zusatzwerkstoffen und insbesondere deren Anwendung in modernen hochfesten Bauteilen. T2 - 41. Assistentenseminar Fügetechnik CY - Magdeburg, Germany DA - 03.09.2020 KW - MAG-Schweißen KW - Eigenspannungen KW - Additive Fertigung KW - Hochfester Stahl KW - Kaltrisssicherheit PY - 2021 SN - 978-3-96144-141-9 VL - 370 IS - 41 SP - 113 EP - 124 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-56641 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rhode, Michael A1 - Richter, Tim A1 - Schröpfer, Dirk A1 - Manzoni, Anna Maria A1 - Schneider, M. A1 - Laplanche, G. T1 - Welding of high-entropy alloys and compositionally complex alloys - an overview N2 - High-entropy alloys (HEAs) and compositionally complex alloys (CCAs) represent new classes of materials containing five or more alloying elements (concentration of each element ranging from 5 to 35 at. %). In the present study, HEAs are defined as single-phase solid solutions; CCAs contain at least two phases. The alloy concept of HEAs/CCAs is fundamentally different from most conventional alloys and promises interesting properties for industrial applications (e.g., to overcome the strength-ductility trade-off). To date, little attention has been paid to the weldability of HEAs/CCAs encompassing effects on the welding metallurgy. It remains open whether welding of HEAs/CCAs may lead to the formation of brittle intermetallics and promote elemental segregation at crystalline defects. The effect on the weld joint properties (strength, corrosion resistance) must be investigated. The weld metal and heat-affected zone in conventional alloys are characterized by non-equilibrium microstructural evolutions that most probably occur in HEAs/CCAs. The corresponding weldability has not yet been studied in detail in the literature, and the existing information is not documented in a comprehensive way. Therefore, this study summarizes the most important results on the welding of HEAs/CCAs and their weld joint properties, classified by HEA/CCA type (focused on CoCrFeMnNi and AlxCoCrCuyFeNi system) and welding process. KW - High-entropy alloy KW - Compositionally complex alloy KW - Welding KW - Properties KW - Review PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-527068 DO - https://doi.org/10.1007/s40194-021-01110-6 SP - 1 EP - 15 PB - Springer Nature AN - OPUS4-52706 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schröpfer, Dirk A1 - Kromm, Arne A1 - Lausch, Thomas A1 - Rhode, Michael A1 - Wimpory, R. C. A1 - Kannengießer, Thomas T1 - Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel: Part III - Assessment of residual stresses from small-scale to real component welds N2 - For higher operational temperatures and pressures required in petrochemical plants, the modified 13CrMoV9-10 steel was developed providing high resistance against creep and compressed hydrogen. Extreme care during the welding procedure is necessary for this steel, attributed to low toughness, high strength in as-welded state, and increased susceptibility to stress relief cracking (SRC) during post-weld heat treatment (PWHT). Previous research of SRC in creep-resistant steels discussed mainly thermal and metallurgical factors. Few previous findings addressed the influences of welding procedure on crack formation during PWHT considering real-life manufacturing conditions. These investigations focus on effects of welding heat control on stresses during welding and subsequent PWHT operations close to realistic restraint and heat dissipation conditions using a special 3D testing facility, which was presented in parts I and II of this contribution. Part III addresses investigations on residual stress evolution affecting crack formation and discusses the transferability of results from large-scale testing to laboratory-scale. Experiments with test set-ups at different scales under diverse rigidity conditions and an assessment of the residual stresses of the weld-specimens using X-ray (surface near) and neutron diffraction analysis (bulk) were performed. This study aims to provide a way of investigating the SRC behaviour considering component-specific residual stresses via small-scale testing concepts instead of expensive weld mock-ups. KW - Welding KW - Creep-resistant steel KW - Residual stresses KW - Post-weld heat treatment KW - Stress relief cracking PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-524403 DO - https://doi.org/10.1007/s40194-021-01101-7 SN - 1878-6669 VL - 65 SP - 1671 EP - 1685 PB - Springer CY - Berlin AN - OPUS4-52440 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schröpfer, Dirk A1 - Treutler, K. A1 - Börner, Andreas A1 - Gustus, R. A1 - Kannengießer, Thomas A1 - Wesling, V. A1 - Maus-Friedrichs, W. T1 - Surface finishing of hard-to-machine cladding alloys for highly stressed components N2 - The supply and processing of materials for highly stressed components are usually cost-intensive. Efforts to achieve cost and resource efficiency lead to more complex structures and contours. Additive manufacturing steps for component repair and production offer significant economic advantages. Machining needs to be coordinated with additive manufacturing steps in a complementary way to produce functional surfaces suitable for the demands. Regarding inhomogeneity and anisotropy of the microstructure and properties as well as production-related stresses, a great deal of knowledge is still required for efficient use by small- and medium-size enterprises, especially for the interactions of subsequent machining of these difficult-to-machine materials. Therefore, investigations on these influences and interactions were carried out using a highly innovative cost-intensive NiCrMo alloy (IN725). These alloys are applied for claddings as well as for additive component manufacturing and repair welding using gas metal arc welding processes. For the welded specimens, the adequate solidification morphology, microstructure and property profile were investigated. The machinability in terms of finishing milling of the welded surfaces and comparative analyses for ultrasonic-assisted milling processes was examined focussing on surface integrity. It was shown that appropriate cutting parameters and superimposed oscillating of the milling tool in the direction of the tool rotation significantly reduce the mechanical loads for tool and workpiece surface. This contributes to ensure a high surface integrity, especially when cutting has to be carried out without cooling lubricants. KW - WAAM KW - IN725 KW - Machining KW - Ultrasonic-assisted milling KW - Residual stresses KW - Cutting forces KW - Surface integrity KW - Microstructure PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-524872 DO - https://doi.org/10.1007/s00170-021-06815-y VL - 114 IS - 5-6 SP - 1427 EP - 1442 PB - Springer AN - OPUS4-52487 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schröpfer, Dirk A1 - Scharf-Wildenhain, R. A1 - Hälsig, A. A1 - Wandtke, Karsten A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Process-related influences and correlations in wire arc additive manufacturing of high-strength steels N2 - High-strength fine-grained structural steels have great potential for weight-optimized, efficient structures in many modern steel applications. Further advances in efficiency can be achieved through additive manufacturing and bionic design. Commercial high-strength filler materials for wire arc additive manufacturing (WAAM) are already provided by the consumable producers. Today, application would be strictly limited due to absence of quantitative findings or any guidelines for the industry regarding welding-related stresses and component safety during manufacturing and service. Hence, process- and material-related influences and design-related restraint conditions associated with formation of residual stresses and cold cracking risk are investigated. The aim is the accessibility of special WAAM self-restraining cold cracking tests and easy applicable processing recommendations, enabling an economical, fit-for-purpose and crack-safe WAAM of high-strength steels. This first study focuses on determination of interactions between WAAM process parameters, resulting layer geometry, microstructure and residual stresses, analyzed via X-ray diffraction. Defined reference specimens are automated welded using a special WAAM solid wire (yield strength >820 MPa). Geometric properties can be specifically adjusted by wire feed and welding speed, but cannot be varied arbitrarily, since a high heat input causes local overheating, inadmissible changes of microstructure and mechanical properties, defects and comparable high tensile residual stresses. T2 - 22. Werkstofftechnischen Kolloquium der TU Chemnitz CY - Online meeting DA - 24.03.2021 KW - Residual stresses KW - Additive Manufacturing KW - High-strength steel PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-533300 DO - https://doi.org/10.1088/1757-899X/1147/1/012002 VL - 1147 SP - 012002 PB - IOP Publishing Ltd AN - OPUS4-53330 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Richter, Tim A1 - Schröpfer, Dirk A1 - Rhode, Michael A1 - Börner, Andreas T1 - Rührreibschweißen von Hoch- und Mittelentropie-Legierungen N2 - Hoch- und Mittelentropie-Legierungen (engl. High/Medium Entropy Alloys–HEA/MEA) sind relativ neue Werkstoffklassen. Im Gegensatz zu herkömmlichen Le-gierungen bestehen HEA aus fünf bzw. MEA aus drei oder vier Legierungselementen im äquiatomaren Gleichgewicht. Viele HEA weisen aufgrund hervorragender struktu-reller Eigenschaftskombinationen von sehr tiefen bis zu hohen Temperaturen enor-mes Anwendungspotential auf. Die Anwendung für reale Bauteile stellt jedoch die zentrale Frage der Eignung für die fügetechnische Verarbeitung. Dieser Aspekt findet in der weltweiten Materialforschung bisher kaum Beachtung. Anforderungen an die zuverlässige und sichere fügetechnische Verarbeitung dieser Werkstoffe sind von wesentlicher Bedeutung hinsichtlich wirtschaftlicher Bauteilfertigung für spätere po-tenzielle Anwendungsbereiche, bspw. in der Energietechnik. Das Rührreibschweißen (engl. Friction Stir Welding–FSW) stellt hierbei einen vielversprechenden Fügepro-zess dar, dessen Hauptvorteil in der Schweißprozesstemperatur unterhalb der Schmelztemperatur der zu fügenden Werkstoffe liegt. Dies bedingt die Vermeidung der Ausbildung von harten, versprödenden intermetallischen Phasen, wie sie z. B. beim konventionellen Schmelzschweißen von Eisen-Aluminium-Verbindungen auf-treten. Die vorliegende Arbeit stellt grundlegende Untersuchungen zur Schweißbar-keit einer CoCrFeMnNi-Legierung (HEA) und einer CoCrNi-Legierung (MEA) mit dem FSW-Prozess vor. Die Versuchsschweißungen werden mittels mikroskopischer Analysen hinsichtlich des Schweißnahtaufbaus sowie Schweißnahtfehlern charakte-risiert. FSW zeigt sich als grundlegend geeignet zur Verbindungsschweißung der HEA bzw. MEA. Anhand dieser Ergebnisse kann eine weitere Bewertung der Schweißbar-keit erfolgen. T2 - 4 Niedersächsisches Symposium Materialtechnik Clausthal CY - Online meeting DA - 25.02.2021 KW - Hochentropie Legierung KW - Rührreibschweißen KW - Mediumentropie Legierung PY - 2021 SP - 502 EP - 511 AN - OPUS4-52255 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Engelking, Lorenz A1 - Eissel, A. A1 - Schröpfer, Dirk A1 - Treutler, K. A1 - Kannengießer, Thomas A1 - Wesling, V. ED - Brockmann, S. ED - Krupp, U. T1 - Untersuchungsmethoden beim Fräsen additiv gefertigter schwer spanbarer Kobalt-Chrom-Legierungen N2 - Für den Anlagenbau werden hochbelastete Komponenten aus Co-Cr-Legierungen hergestellt. Dabei ist die Zerspanung so herausfordernd, dass additive Fertigungsschritte oft wirtschaftlicher sind. Diese bedingen aber vorwiegende heterogene, anisotrope Gefüge und Eigenschaften und bei nachfolgender Fräsbearbeitung unstetige Zerspankräfte und instabile Spanvorgänge. Hierbei können hybride Zerspanprozesse helfen, hohe Belastungen für Werkzeug und Werkstückoberfläche zu minimieren. Diesbezügliche Charakterisierungen erfordern speziell adaptierte Zerspanungsanalysen. Anhand eines Anwendungsbeispiels, bei dem eine Modifikation der Ausgangslegierung mit 1 % Hf erfolgte, wird die Wechselwirkung zwischen Gefügemorphologie und Fräsprozess dargestellt, der konventionelle mit einem hybriden ultraschallunterstützten Fräsprozess verglichen und die Charakterisierung des Werkzeugverschleißes anhand zweier verschiedener Fräser betrachtet. Analysen auftretender Prozesskräfte mittels Piezo-Mehrkomponenten-Dynamometer, der Werkzeugoszillation mittels Laser-Vibrometer und zusätzliche In-situ-Temperaturmessungen der Werkzeugschneiden mittels Highspeed-Pyrometer bilden den Kern der neuen Zerspanungsprüftechnik. Die vorgestellten Untersuchungsmethoden bilden die Vorgänge bei der Zerspanung additiv gefertigter Werkstoffe detailliert und reproduzierbar ab. Sowohl Legierungsmodifikation als auch hybride Prozessbedingungen lassen gezielte Einflüsse zur deutlichen Verbesserung der Zerspanungssituation zu. T2 - Tagung Werkstoffprüfung 2021 CY - Online meeting DA - 02.12.2021 KW - Ultraschallunterstütztes Fräsen KW - Legierungsmodifikation KW - Additive Fertigung KW - Plasma-Pulver-Auftragschweißen KW - Werkzeugverschleiß PY - 2021 SN - 978-3-941269-98-9 SP - 93 EP - 98 PB - Stahlinstitut VDEh CY - Düsseldorf AN - OPUS4-54921 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -