TY - JOUR A1 - Schmidt, Wolfram A1 - Brouwers, H.J.H. A1 - Kühne, Hans-Carsten A1 - Meng, Birgit T1 - Interactions of polysaccharide stabilising agents with early cement hydration without and in the presence of superplasticizers N2 - Polysaccharides are incorporated into cement based Systems in order to modify the rheological properties. Typically, cellulose ethers, sphingan gums, guar gum or starch ethers are applied. Depending upon their chemistry, molecular architecture, and adsorption tendency, polysaccharides interact differently with the entire cementitious system. Some stabilising agents like diutan gum mainly affect the cementitious paste; other stabilising agents like starch tend to interact with the sand fraction and even with the coarse aggregates. Cellulose and guar gum shows more diverse performances. Typically stabilising admixtures like polysaccharides are used, when sophisticated rheological properties are adjusted. Therefore, polysaccharides are often used in combination with superplasticisers, which are added to reduce the yield stress of concrete. This can cause interactions, particularly when the stabilising Agent shows a strong tendency to adsorb on particle surfaces. Adsorptive stabilising agents may reduce the amount of adsorbed superplasticisers, thus affecting both viscosity and yield stress, while non-adsorptive stabilising agents mainly affect the plastic viscosity independently of the superplasticiser. Due to the strong influence of superplasticisers on the yield stress, influences of the stabilising agent on the yield stress retreat into the background, so that their major effect is an increase of the plastic viscosity. The paper provides a comprehensive overview of how different polysaccharide superplasticisers affect cementitious flowable systems and points out the challenges of the combined use of polysaccharides and superplasticisers. Based on rheometric experiments and observations of the hydration process, time dependent effects on the workability as well as of the hydration of cement are presented and discussed. KW - Concrete KW - Polysaccharides KW - Rheology KW - Stabilising agents KW - Starch KW - Sphingan PY - 2017 DO - https://doi.org/10.1016/j.conbuildmat.2016.11.022 SN - 0950-0618 SN - 1879-0526 VL - 139 SP - 584 EP - 593 PB - Elsevier AN - OPUS4-40597 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sonebi, M. A1 - Khatib, J. A1 - Schmidt, Wolfram ED - Diouri, A. ED - Khachani, N. ED - Alami Talbi, M. ED - Ait Brahim, L. ED - Bahi, L. T1 - Influence of the type of viscosity-modifying admixtures and metakaolin on the rheology of grouts N2 - The Viscosity-modifying admixtures (VMAs) contribute to the control of the rheology of grouts and are used to enhance plastic viscosity, cohesion, stability, and resistance to bleeding of cement-based systems. This paper reports the results of an investigation on the effect of type of VMAs, namely two types of diutan gums and a welan gum and metakaolin (MTK), plus a superplasticiser, on the rheology behaviour of cement grouts. All mixes were made with polycarboxylic superplasticiser at 0.6% and 0.9%. The dosages of VMAs were 0.05%, and 0.10%, with a fixed water-to-binder ratio of 0.40. The investigated fresh properties of the grouts included the mini-slump flow, plate cohesion, and rheology parameters: namely yield value and plastic viscosity. The rheological parameters were obtained using a vane viscometer. Control grouts (with and without superplasticiser and VMA) were also tested and compared to mixes containing VMAs. The results indicated that the incorporation of MTK reduced the fluidity and increased the plate cohesion and yield stress, and plastic viscosity due to the higher surface area of MTK. The diutan gum grouts improved the grout fresh properties and rheology compared to the welan gum grouts. T2 - CMSS 2013 - International congress on materials & structural stability - Building up sustainable materials & constructions CY - Rabat, Morocco DA - 27.11.2013 KW - Viscosity modifying agent KW - Metakaolin KW - Diutan gum KW - Welan gum KW - Rheology PY - 2013 SN - 978-9954-32-689-3 SP - 1 EP - 6 AN - OPUS4-30041 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sturm, Patrick A1 - Gluth, Gregor A1 - Schmidt, Wolfram A1 - Astorg, Adéle A1 - Kühne, Hans-Carsten A1 - Brouwers, H.J.H. T1 - Rheological properties of microsilica and sodium aluminate based one-part geopolymers compared to ordinary Portland cement N2 - One-part (“just-add-water”) geopolymers are a new dass of mineral binders that are produced without the use of alkaline activating Solutions. Compared to conventional geopolymers, i. e. those activated by highly alkaline Solutions, much less is known about the one-part geopolymers ’ microstructure and with regard to their rheology. In this work, the rheology of one-part geopolymers, produced from microsilica and sodium aluminate, with several SiO-flACOiratios and two different water/binder-ratios (w/b) were investigated qualitatively with a viscometer (mortar measuring cellj. Absolute values of plastic viscosity and yield stress were determined with a double gap measuring cell. In addition spread flow tests were conducted. The aim was to classify the early behavior of geopolymer pastes and to compare it to ordinary Portland cement (CEM 142.5 R) pastes. At moderate to high shear rates, the measured flow curves cotdd be fltted well by the Bingham model. With increasing silica content the yield stress increased. Up to a certain SiOi/Al2O3-ratio viscosity also increased with increasing silica content; however, at higher silica/alumina-ratios the viscosity decreased again. Higher w/b-ratios caused lower yield stresses and viscosities. Compared to Portland cement pastes, most of the considered geopolymers were signiflcantly stiffer. The results were further Interpreted in terms of pore solution viscosity and volume-based water to binder ratios (w/b) of the geopolymer pastes. T2 - 5th International Conference Non-Traditional Cement & Concrete CY - Brno, Czech Republic DA - 16.06.2014 KW - Alkali-activated binders KW - One-part geopolymers KW - Rheology PY - 2014 SN - 978-80-214-4867-4 SP - 71 EP - 74 AN - OPUS4-31159 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - de Carvello, J. M. F. A1 - Schmidt, Wolfram A1 - Kühne, Hans-Carsten A1 - Fiorotti Peixoto, R. A. T1 - Influence of high-charge and low-charge PCE-based superplasticizers on Portland cement pastes containing particle-size designed recycled mineral admixtures N2 - Design : and use of engineered recycled mineral admixtures obtained from industrial and mineral waste are promising strategies to increase the range of materials suitable for use in cement-based composites. In this work, Portland cement-blended pastes containing mineral admixtures designed for improving particle packing were evaluated in the presence of low- and high-charge polycarboxylate-based superplasticizers. The powders were obtained from basic oxygen furnace slag, iron ore tailings, quartz mining tailings, and quartzite mining tailings. The zeta-potentials of the particles were obtained via electrophoretic mobility. The flow properties were evaluated by rheological tests performed in a Couette type rheometer. The hydration kinetics was evaluated by isothermal calorimetry and an adapted method based on the Vicat needle test. The high-charge PCE and the finer mineral admixtures produced more stable blends. Coarser mineral admixtures led to increased flowability and delayed hydration compared to finer ones. Steel slag powders presented the most significant plasticizer effects, but also the largest setting delays and segregation tendency. Quartz-rich superfines reduced the setting delays caused by the superplasticizers. In summary, both superplasticizers were effective in improving flow properties, but the high-charge PCE was effective in preventing segregation in pastes containing mineral admixtures coarser and heavier than cement. KW - Engineered recycled mineral admixtures KW - Rheology KW - PCE-Based superplasticizer KW - Steel slag KW - Mining tailing PY - 2020 DO - https://doi.org/10.1016/j.jobe.2020.101515 VL - 32 SP - 1 EP - 16 PB - Elsevier AN - OPUS4-58395 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Govin, A. A1 - Schmidt, Wolfram A1 - Bartholin, M. C. A1 - Grosseau, P. ED - Amziane, Sofiane ED - Sonebi, M. T1 - Effect of Guar Gum Derivatives Combined with Superplasticizers on Properties of Portland Cement-Pastes N2 - Chemical admixtures allow to the create a variety of fresh and hardened state properties in cementitious materials. In the case of self-compacting concrete, plasticizers or superplasticizers are introduced with the aim to decrease the yield stress and the viscosity of the materials. However, in order to prevent segregation and bleeding, and to improve the water retention of cement-based system, stabilizing agents or viscosity agents are often introduced in addition. Among these admixtures, polysaccharides are most commonly used. The aim of this study is to provide an understanding of competitive or synergetic effects induced by the combination of hydroxypropyl guar stabilizing agents (HPG) and superplasticizers on cement pastes. Two polycarboxylate superplasticizers (PCE) exhibiting different charge densities and one HPG were studied. It was found that the combination of HPG with PCE superplasticizer strongly affects the rheological behavior of cement pastes. Despite the presence of HPG, the viscosity of the pastes strongly decreased with increasing dosage of PCE until it became close to the viscosity of a cement paste with PCE only. However, the use of HPG in combination with PCE allows maintaining a significant yield stress in the cement paste compared to PCE alone. The increase in the charge density of the PCE seemed to amplify the drop of the viscosity and to reduce the gain on the yield stress induced by HPG. The results also highlight a delay in the setting-time of the cement paste by adding HPG and PCE. The delay induced by HPG is significantly lower than that generated by PCEs. However, the combination of the both kind of admixtures leads to a slightly shorter setting-time compared to the PCE alone. T2 - 2nd International Conference on Bio-based Building Materials & 1st Conference on ECOlogical valorisation of GRAnular and FIbrous materials CY - Clermont-Ferrand, France DA - 21.06.2017 KW - Guar gum KW - Polysaccharides KW - Superplasticizer KW - Cement KW - Rheology PY - 2017 VL - PRO 119 SP - 55 EP - 61 PB - RILEM Publications S.A.R.L. CY - Paris AN - OPUS4-41038 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Wolfram A1 - Olonade, K. A. A1 - Mbugua, R. N. A1 - Lenz, F. J. A1 - Tchetgnia Ngassam, I. T1 - Bio-Based Rheology Modifiers for High Performance Concrete – Possible Modes of Actions and Case Study for Cassava Starch in West Africa N2 - Polymers that help tailoring rheological properties during the casting process have become inevitable constituents for all kinds of high-performance concrete technologies. Due to lacking industries, these typically crude-oil based admixtures are not readily available in many parts of the world, which limits the implementation of more sustainable high-performance construction technologies in these regions. Alternative polymers, which often demand for less processing, can be derived from local plant-based resources. The paper provides experimental data of flow tests of cement pastes with polysaccharides from Triumfetta pendrata A. Rich, acacia gum and cassava without and in the presence of polycarboxylate ether superplasticizer. The flow tests are amended by observations of the zeta potentials and the hydrodynamic diameters in the presence of and without calcium ions in the dispersion medium. The results show that in the presence of and without calcium ions all polysaccharides provide negative zeta potentials, yet, they affect flowability and thixotropy in different ways. Cassava starch, acacia gum, and the gum of Triumfetta pendrata A. Rich qualified well for robustness improvement, strong stiffening, and additive manufacturing, respectively. The reason for the different effects can be found in their average sizes and size distribution. Due to the promising results, a flow chart for local value chains is derived on the example of yet unused cassava wastes, which can be converted in parallel. T2 - 3rd International Conference on the Application of Superabsorbent Polymers CY - Skukuza, South Africa KW - Admixtures KW - Polysaccharides KW - Rheology KW - Thixotropy KW - Concrete PY - 2020 SN - 978-3-030-33341-6 SN - 978-3-030-33342-3 DO - https://doi.org/10.1007/978-3-030-33342-3_17 SP - 158 EP - 166 PB - Springer AN - OPUS4-58404 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmidt, Wolfram A1 - Tchetgnia Ngassam, Ines Leana A1 - Olonade, K. A. A1 - Mbugua, R. A1 - Kühne, Hans-Carsten T1 - Plant based chemical admixtures – potentials and effects on the performance of cementitious materials N2 - While today, engineers can choose from a wide range of rheology modifying admixtures, in some parts of the world, these are difficult to access, due to their complex processing. However, alternatives can be bio‐based polymers such as polysaccharides from various sources. These are easily accessible all over the world, do not demand for complicated processing, and typically they are more sustainable than many established materials, which are crude oil‐based. The paper presents the effects of acacia gum, cassava starch and the gum of triumfetta pendrata A. Rich on the rheological performance of cementitious systems. It is shown that acacia gum can be as efficient as polycarboxylate based superplasticisers, cassava starch can reduce the yield stress slightly with little effect on the plastic viscosity, and the gum of triumfet ta pendrata A. Rich increases the thixotropy of cement pastes with plasticizing polymers significantly. KW - Polysaccharides KW - Rheology KW - Cement KW - Chemical admixtures KW - Bio-based concrete PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-476748 DO - https://doi.org/10.21809/rilemtechlett.2018.83 VL - 3 SP - 124 EP - 128 PB - RILEM S.A.R.L. CY - Paris AN - OPUS4-47674 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Wolfram A1 - Kühne, Hans-Carsten A1 - Leinitz, Sarah ED - Diouri, A. ED - Boukhari, A. ED - Ait Brahim, L. ED - Bahi, L. ED - N., Khachani ED - Saadi, M ED - Aride, J. ED - Nounah, A. T1 - Concrete casting robustness improvement due to active rheology N2 - With ongoing innovation in process technology, the challenges of concrete technology are more and more focused on the rheological optimisation for these processes, since improper mixture stability or poor compaction ability negatively affect the concrete homogeneity and quality. However, along with the increasing complexity of today’s concrete mixture compositions, concrete becomes more prone to failure regarding the casting process. Variable properties of the raw materials typically cause changing workability. The reasons can be found among others in scattering water contents, physical or chemical properties of the cement or varying environmental temperatures. Robustness in the delicately adjusted rheology, however, is of utmost importance for modern and future process technology, from sprayed concrete over pumpable concrete towards 3D-printing, with regard to the long-term strength, the function and the durability. Typically, material induced changes cannot be identified easily due to the complex interactions of concrete constituents. Therefore, a precise and prompt counteraction is impossible. However, it is known that the yield stress can be controlled by addition of supplementary superplasticizer or stabilising agent. In combination with computerized process observation tools that can rapidly interpret and react on changes in the rheology, it is therefore thinkable, that only these two admixture types can adjust the rheology steadily and permanently, regardless of the actual root cause for observed macroscopic rheology change. The presentation will firstly give a comprehensive overview of effects at the interface between pore solution, particles and hydrates, which affect the rheology of fresh concrete. Secondly, ways are recommended how the rheology can be actively manipulated before eventually computerized methods are demonstrated that help to actively and rapidly assess and counteract performance scatter during steady casting processes. T2 - 2nd International Congress on Materials & Structural Stability (CMSS-2017) CY - Rabat, Morocco DA - 22.11.2017 KW - Cusum KW - Rheology KW - Control Chart KW - Concrete KW - Robustness PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-444317 DO - https://doi.org/10.1051/matecconf/201814901001 SN - 2261-236X VL - 149 SP - 01001-1 EP - 01001-7 PB - EDP Sciences CY - Les Ulis AN - OPUS4-44431 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Wolfram T1 - Potentials for sustainable cement and concrete technologies - Comparison between Africa and Europe N2 - Cement and concrete technologies in Africa provide vast potentials for sustainable future technologies as well as enormous challenges. The main focus of the symposium is to address existing challenges, possible solutions, and future potentials with all participants. This symposium also aims at offering a platform for networking with relevant players in science and industry. T2 - Cement and Concrete Related Issues for the African Market CY - Yaoundé, Cameroon DA - 02.11.2017 KW - Cement KW - Admixtures KW - Rheology KW - Sustainability KW - Environment PY - 2017 AN - OPUS4-43541 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Franco de Carvalho, J. M. A1 - Defàveri, K- A1 - Castro Mendes, J. A1 - Schmidt, Wolfram A1 - Kühne, Hans-Carsten A1 - Fiorotti Peixoto, R. A. T1 - Influence of particle size-designed recycled mineral admixtures on the properties of cement-based composites N2 - In this work, engineered recycled mineral admixtures were obtained from four different industrial residues: basic oxygen furnace slag, iron ore tailings, quartz mining tailings and quartzite mining tailings. The grinding performance was evaluated in two different programs and the characterization included chemical and mineralogical composition, particle morphology, and physical properties. Performance evaluations were carried out in blended pastes and mortars, including flow properties, hydration kinetics, soundness, pozzolanic activity, and compressive strength. Coarser-than-cement admixtures allowed better flow performance, greater dimensional stability and more economical production, while finer-thancementn admixtures improved mechanical performance by both filler effect and cementing activity. KW - Engineered recycled mineral admixtures KW - Rheology KW - Hydration kinetics KW - Basic oxygen furnace slag KW - Iron ore tailings KW - Mining tailings PY - 2021 DO - https://doi.org/10.1016/j.conbuildmat.2020.121640 SN - 0950-0618 VL - 272 SP - 1 EP - 13 PB - Elsevier Ltd. AN - OPUS4-58255 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -