TY - JOUR A1 - Priebe, Nsesheye Susan A1 - Schmidt, Wolfram A1 - Rogge, Andreas A1 - Kühne, Hans-Carsten T1 - Performance of rice husk ash as an alternative binder in a modified cementitious system with added superplasticizers N2 - Rice husk as (RHA) is an eco-friendly material, which can be used as a supplementary cementitious material (SCM) in cement and concrete. Due to the high water demand for the material, superplasticizers (SPs) are essential to improve the performance. However, the interaction between the SPs and RHA systems is limited. This paper investigates the interaction of the binders with three SPs, i.e. two polycarboxylate ethers (PCEs) and one lignosulphonate (LS). The investigations are performed on blended systems of mortar containing various percentages of RHA and limestone powder (LSP). LSP is used in this research to improve the workability of the mortar. The results from the zeta potential (ZP) shows that the SPs are extremely dependent on the pH of the suspension. At higher pH values such as in a cementitious system, the ZP becomes less negative indicating that the ions in the suspension interact with the carboxyl groups in the backbone of the polymers thus reducing the surface charges of the SP. The mini-slump flow shows that the workability of the blended mortar systems is significantly improved with the addition of SPs. LS systems with increasing RHA is observed to have similar workability as the control mix over time. The compressive strength test results show increased strength for all mortar specimens with added RHA and LSP at later ages. KW - Compressive strength KW - Rice husk ash KW - Superplasticizers KW - Zeta potential KW - Workability PY - 2017 DO - https://doi.org/10.1016/j.cemconcomp.2017.07.014 N1 - Geburtsname von Priebe, Nsesheye Susan: Msinjili, N. S. - Birth name of Priebe, Nsesheye Susan: Msinjili, N. S. VL - 83 SP - 202 EP - 208 PB - Elsevier Ltd. AN - OPUS4-42602 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sonebi, M. A1 - Khatib, J. A1 - Schmidt, Wolfram ED - Diouri, A. ED - Khachani, N. ED - Alami Talbi, M. ED - Ait Brahim, L. ED - Bahi, L. T1 - Influence of the type of viscosity-modifying admixtures and metakaolin on the rheology of grouts N2 - The Viscosity-modifying admixtures (VMAs) contribute to the control of the rheology of grouts and are used to enhance plastic viscosity, cohesion, stability, and resistance to bleeding of cement-based systems. This paper reports the results of an investigation on the effect of type of VMAs, namely two types of diutan gums and a welan gum and metakaolin (MTK), plus a superplasticiser, on the rheology behaviour of cement grouts. All mixes were made with polycarboxylic superplasticiser at 0.6% and 0.9%. The dosages of VMAs were 0.05%, and 0.10%, with a fixed water-to-binder ratio of 0.40. The investigated fresh properties of the grouts included the mini-slump flow, plate cohesion, and rheology parameters: namely yield value and plastic viscosity. The rheological parameters were obtained using a vane viscometer. Control grouts (with and without superplasticiser and VMA) were also tested and compared to mixes containing VMAs. The results indicated that the incorporation of MTK reduced the fluidity and increased the plate cohesion and yield stress, and plastic viscosity due to the higher surface area of MTK. The diutan gum grouts improved the grout fresh properties and rheology compared to the welan gum grouts. T2 - CMSS 2013 - International congress on materials & structural stability - Building up sustainable materials & constructions CY - Rabat, Morocco DA - 27.11.2013 KW - Viscosity modifying agent KW - Metakaolin KW - Diutan gum KW - Welan gum KW - Rheology PY - 2013 SN - 978-9954-32-689-3 SP - 1 EP - 6 AN - OPUS4-30041 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kumaran, G.S. A1 - Priebe, Nsesheye Susan A1 - Schmidt, Wolfram A1 - Florea, M.V.A. A1 - Nibasumba, P. ED - Uzoegbo, H.C. ED - Schmidt, Wolfram T1 - A study on sustainable energy for cement industries in Rwanda N2 - Rwanda is a landlocked country in the East Africa. It is surrounded by Uganda, Tanzania, Congo and Burundi. Rwanda is a fast developing country and it spends most of its revenues to import fossil fuels from either through Mombasa Port in Kenya or Dar es Salaam port in Tanzania because the energy production in Rwanda is not sufficient for its development. Transporting the fuels from these ports, add on to the cost of all materials, cement industry being no exception. There are three cement companies in Rwanda. The cement industries could not run in full production due to the shortage of fuel. Moreover, Rwanda is importing all the construction materials such as steel, roofing materials, etc from its neighbouring countries. This increases the cost of construction and the common man find difficult to own a house. In order to sustain the energy needs of Rwanda, different sources of energies should be focused. They are Peat, Geothermal, Methane gas, solar, wind, waste materials and Municipal wastes. Without affecting the environment, there is an urgent need to find a solution on sustainable energy in Rwanda. This paper discusses about the possible sources of energy in Rwanda which will improve the energy sustainability and turn the economy of Rwanda. T2 - ACCTA - International conference on advances in cement and concrete technology in Africa 2013 CY - Johannesburg, South Africa DA - 28.01.2013 KW - Biomass KW - Cement production KW - Peat KW - Energy sustainability PY - 2013 SN - 978-3-9815360-3-4 N1 - Geburtsname von Priebe, Nsesheye Susan: Msinjili, N. S. - Birth name of Priebe, Nsesheye Susan: Msinjili, N. S. SP - 1169 EP - 1175 AN - OPUS4-27766 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sturm, Patrick A1 - Gluth, Gregor A1 - Schmidt, Wolfram A1 - Astorg, Adéle A1 - Kühne, Hans-Carsten A1 - Brouwers, H.J.H. T1 - Rheological properties of microsilica and sodium aluminate based one-part geopolymers compared to ordinary Portland cement N2 - One-part (“just-add-water”) geopolymers are a new dass of mineral binders that are produced without the use of alkaline activating Solutions. Compared to conventional geopolymers, i. e. those activated by highly alkaline Solutions, much less is known about the one-part geopolymers ’ microstructure and with regard to their rheology. In this work, the rheology of one-part geopolymers, produced from microsilica and sodium aluminate, with several SiO-flACOiratios and two different water/binder-ratios (w/b) were investigated qualitatively with a viscometer (mortar measuring cellj. Absolute values of plastic viscosity and yield stress were determined with a double gap measuring cell. In addition spread flow tests were conducted. The aim was to classify the early behavior of geopolymer pastes and to compare it to ordinary Portland cement (CEM 142.5 R) pastes. At moderate to high shear rates, the measured flow curves cotdd be fltted well by the Bingham model. With increasing silica content the yield stress increased. Up to a certain SiOi/Al2O3-ratio viscosity also increased with increasing silica content; however, at higher silica/alumina-ratios the viscosity decreased again. Higher w/b-ratios caused lower yield stresses and viscosities. Compared to Portland cement pastes, most of the considered geopolymers were signiflcantly stiffer. The results were further Interpreted in terms of pore solution viscosity and volume-based water to binder ratios (w/b) of the geopolymer pastes. T2 - 5th International Conference Non-Traditional Cement & Concrete CY - Brno, Czech Republic DA - 16.06.2014 KW - Alkali-activated binders KW - One-part geopolymers KW - Rheology PY - 2014 SN - 978-80-214-4867-4 SP - 71 EP - 74 AN - OPUS4-31159 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Lu, Z. A1 - Becker, S. A1 - Leinitz, Sarah A1 - von Klitzing, R. A1 - Schmidt, Wolfram A1 - Stephan, D. ED - Mechtcherine, V. ED - Khayat, K. ED - Secrieru, E. T1 - Rheological properties of silica beads in the presence of different polymers and electrolyte N2 - Properties of interstitial liquid phase in cement paste, including the species and concentrations of polymers and ion etc., play an important role for the rheological properties of cementitious materials. In order to better understand their effect, an inert model substance, spherical silica beads (SBs) with defined surface and granulometry were used in the presence of electrolytes (CaCl2) and/or different polymers, including polycarboxylate superplasticizer (PCE) and polyethylene glycol (PEG). It was found the presence of Ca2+ greatly increases the viscosity and yield stress of silica beads paste (SBP), which is proportional to the [Ca2+]. For the effect of PCE, the addition of PCE is beneficial to the flowability of SBP, but a high dosage of PCE leads to a reversal effect. Furthermore, the yield stress firstly increases and then decreases with increasing [Ca2+] under the same dosage of PCE. The addition of PEG always increases the yield stress of SBP, regardless of the ion concentration and the presence or not of PCE. KW - Rheological properties KW - Ions KW - Superplasticizer KW - Silica beads PY - 2019 SN - 978-3-030-22565-0 SN - 978-3-030-22566-7 DO - https://doi.org/10.1007/978-3-030-22566-7_72 SN - 2211-0844 VL - 23 SP - 619 EP - 627 PB - Springer ET - 1 AN - OPUS4-49185 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Werner, Steve A1 - Schmidt, Wolfram A1 - Pirskawetz, Stephan A1 - Rogge, Andreas ED - Khayat, Kamal Henry T1 - Fire spalling of self-compacting concrete mixtures with different limestone powder contents N2 - Self-compacting concrete typically contains a higher content of powder materials than normal concrete. Furthermore it is assumed that the use of superplasticizers yields a more homogenous microstructure in the hardened paste. Both aspects generate a very dense microstructure, which can be assumed to cause material behaviour that differs from than normal concrete when it is exposed to elevated temperatures. However, the paste volumes in SCC can vary significantly based on the mixture composition. At a low paste volumes SCC can be very similar to normal concrete at hardened state while it can vary greatly at higher paste volumes. Since the high temperature behaviour of concrete is strongly affected by the different physical behaviour of the paste and the aggregates, it is likely that the high temperature behaviour is consequently strongly affected by the ratio of these mixture components. In the present study different SCC mixtures were observed with similar mechanical properties, but with significantly differing paste to aggregate ratios. Based on observations of the heat evolution at the fire exposed surface and at different depths inside the specimens as well as based on photogrammetric observations of the spalled dimensions, the results indicate that with increasing paste volumes the heat conductivity is reduced and as a result concrete with higher paste to aggregate ratios shows less spalling. T2 - 8th RILEM Symposium on Self-Compacting Concrete CY - Washington, USA DA - 15.05.2016 KW - Spalling KW - High temperature behaviour KW - Fire exposure KW - Mixture composition KW - Photogrammetry PY - 2016 SN - 978-2-35158-157-5 SP - 353 EP - 363 PB - RILEM Publications S.A.R.L. CY - Paris, France AN - OPUS4-36873 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmidt, Wolfram A1 - Kanjee, J. A1 - Motukwa, G. A1 - Olonade, K. A1 - Dodoo, A. T1 - A snapshot review of future‑oriented standards for cement, admixtures, and concrete: How Africa can spearhead the implementation of green urban construction materials N2 - The existing cement and concrete standards are not capable of making full use of the current technology capacity due to strong focus on conventional concrete and thus they are not fit for the current and future challenges of construction industry. The paper highlights shortcomings with regard to the implementation of the existing standards. It can be seen that future-oriented standards are generally required to contribute to a lower-carbon footprint of the industry. These changes are significantly more relevant in sub-Saharan Africa, due to the rapidly increasing urbanisation challenge and the enormous potentials to develop lower-carbon technologies than elsewhere in the world. KW - Future‑oriented standards KW - Green urban construction KW - Cement PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-582563 DO - https://doi.org/10.1557/s43580-023-00563-9 SN - 2731-5894 VL - 4 IS - 8 SP - 557 EP - 565 PB - Springer International Publishing CY - Springer Nature Switzerland, Cham AN - OPUS4-58256 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lu, Z. A1 - Becker, S. A1 - Leinitz, Sarah A1 - Schmidt, Wolfram A1 - von Klitzing, R. A1 - Stephan, D. T1 - Interaction of Different Charged Polymers with Potassium Ions and Their Effect on the Yield Stress of Highly Concentrated Glass Bead Suspensions N2 - The interaction of different charged polymers, namely anionic polycarboxylate superplasticizer (PCE) and neutral polyethylene glycol (PEG) with potassium ions, and their effect on the yield stress of highly concentrated glass bead suspension (GBS), were studied under different concentrations of potassium ions ([K+]). It was found that, compared to the neutral PEG, the negatively charged PCE can be adsorbed on glass beads (GB), and then decreases the yield stress of GBS. The increasing concentration of free polymer in the interstitial liquid phase with the increased polymer dosage leads to the higher yield stress of GBS, which may be caused by the higher Depletion force. In addition, this effect is also related to the charge density of the polymer and the [K+] in the solution. Along with the increase in [K+], the yield stress of GBS increases significantly with the addition of PCE, but this cannot be observed with PEG, which indicates that potassium ions can interact with negatively charged PCE instead of the neutral PEG. At last, the interparticle Forces between two single GB with adsorbed PCE in solutions containing [K+] and PCE were measured by colloidal probe atomic force microscopy to better understand the interaction of the charged polymer with counterions. KW - Yield stress KW - Free polymer KW - Charge density KW - Depletion force KW - Potassium ions PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-506015 DO - https://doi.org/10.3390/ma13071490 SN - 1996-1944 VL - 13 IS - 7 SP - 1490, 1 EP - 1490, 16 PB - MDPI AN - OPUS4-50601 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zhang, K. A1 - Mezhov, Alexander A1 - Schmidt, Wolfram T1 - Chemical and thixotropic contribution to the structural build-up of cementitious materials N2 - The structural build-up of fresh cement paste is often considered as a purely thixotropic phenomenon in literature even though cementitious materials undergo a non-reversible hydration process that can have an influence on the structuration process. In the current paper a method is proposed to validate the impact of the non-reversible structural build-up. It is shown that fresh cement paste samples lose their structural gain almost completely due to thixotropy while the structural build-up due to hydration can be observed but occurs in a significantly lower order of magnitude over the course of the first hours of hydration. In addition, it is shown, that the chemical component of the structural build-up accelerates with the onset of the acceleration period of hydration, while its contribution in the entire structural build-up remains constant. KW - Thixotropy KW - Structural build-up KW - Penetration test KW - Rheological properties PY - 2022 DO - https://doi.org/10.1016/j.conbuildmat.2022.128307 SN - 0950-0618 VL - 345 IS - 128307 SP - 1 EP - 10 PB - Elsevier Ltd. AN - OPUS4-58248 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Wolfram A1 - Radlinska, A. A1 - Nmai, C. A1 - Buregyeya, A. A1 - Lai, W.L. A1 - Kou, S. ED - Uzoegbo, H.C. ED - Schmidt, Wolfram T1 - Why does Africa need African concrete? An observation of concrete in Europe, America, and Asia - and conclusions for Africa N2 - Portland cement, as we know it today, has its origin in Great Britain approximately 170 years ago. Since then, concrete technology has spread out to Europe, the United States, and Japan, where it became a key component for rapid industrial development. Europe, the Unites States and many Asian countries today have developed a high level of technology regarding concrete construction. However, each of them has a unique history and as a result, different “concrete philosophy” depending upon the social, environmental and financial boundary conditions, as well as their evolution throughout the years and local construction traditions. As a result, the word concrete may refer to rather different materials in America, Europe, and Asia. Apart from South Africa, most sub-Saharan African countries cannot look back on a similarly long cement and concrete history. Cement and concrete are rather new materials and not yet well established. This gives African engineers the unique opportunity to learn from past mistakes and to develop a concrete technology, which refers to the best available practice. However, in many sub-Saharan African countries, standards and regulations are adopted (preferably from Europe or the US) without consideration of the historical background of these standards. Although this practice helps saving resources for the implementation, it does not necessarily yield the best result in the African environment, and also from an economic point of view it might come back disadvantageously due to unnecessary overdesigning. By comparing the differing states-of-the-art in North America, Europe, and Asia, this paper emphasizes, how regional conditions determine the practice of concrete technology in the sub-Saharan area. It is therefore important for Africa to develop a unique African concrete technology, which is perfectly fitted to the specific local conditions, even if it may vary distinctively from the established practice elsewhere. The paper concludes that African nations should effort into adapting existing principles that have proved to function well rather than adopting existing standards. T2 - ACCTA - International conference on advances in cement and concrete technology in Africa 2013 CY - Johannesburg, South Africa DA - 28.01.2013 KW - Cement KW - Casting environment KW - Concrete KW - Durability KW - Standards PY - 2013 SN - 978-3-9815360-3-4 SP - 1139 EP - 1147 AN - OPUS4-27767 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -