TY - CONF A1 - Govin, Alexandre A1 - Schmidt, Wolfram A1 - Bartholin, M. C. A1 - Grosseau, P. ED - Amziane, Sofiane ED - Sonebi, Mohammed ED - Charlet, Karine T1 - Effect of Guar gum derivatives combined with superplasticizers on properties of Portland cement pastes N2 - Chemical admixtures allow to create a variety of fresh and hardened state properties in cementitious materials. In the case of self-compacting concrete, plasticizers or superplasticizers are introduced with the aim to decrease the yield stress and the viscosity of the materials. However, in order to prevent segregation and bleeding, and to improve the water retention of cement-based system, stabilizing agents or viscosity agents are often introduced in addition. Among these admixtures, polysaccharides are most commonly used. The aim of this study is to provide an understanding of competitive or synergetic effects induced by the combination of hydroxypropyl guar stabilizing agents (HPG) and superplasticizers on cement pastes. Two polycarboxylate superplasticizers (PCE) exhibiting different charge densities and one HPG were studied. It was found that the combination of HPG with PCE superplasticizer strongly affects the rheological behavior of cement pastes. Despite the presence of HPG, the viscosity of the pastes strongly decreased with increasing dosage of PCE until it became close to the viscosity of a cement paste with PCE only. However, the use of HPG in combination with PCE allows maintaining a significant yield stress in the cement paste compared to PCE alone. The increase in the charge density of the PCE seemed to amplify the drop of the viscosity and to reduce the gain on the yield stress induced by HPG. The results also highlight a delay in the setting-time of the cement paste by adding HPG and PCE. The delay induced by HPG is significantly lower than that generated by PCEs. However, the combination of the both kind of admixtures leads to a slightly shorter setting-time compared to the PCE alone. T2 - Second International RILEM Conference on Bio-based Building Materials, 21-23 June 2017 CY - Clermont-Ferrand, France DA - 21.06.2017 KW - Rheology KW - Cement KW - Guar Gum KW - Polysaccharide KW - Superplasticizer PY - 2017 SN - 978-2-35158-192-6 SP - 55 EP - 61 PB - RILEM Publications S.A.R.L. CY - Paris, France AN - OPUS4-43547 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Akindahunsi, A. A. A1 - Uzoegbo, H. Ch. A1 - Schmidt, Wolfram ED - Schmidt, Wolfram ED - Priebe, Nsesheye Susan T1 - Effect of Cassava Starch on Shrinkage Characteristics of Concrete N2 - The use of starch and its derivatives in concrete as an admixture to modify relevant properties of concrete is on the increase in recent times. It is known to modify the rheology, to affect the hydration kinetics of cement, and influence on initial and final setting time of cement. This paper examines the effect of cassava starch on concrete. shrinkage properties of concrete, with and without starch addition, were studied. Various percentages (0, 0.5, 1.0, 1.5 and 2 %) of starches by weight of cement were added to concrete mixes prepared in the laboratory. Shrinkage tests were conducted for duration of up to one year. The result show that concretes with starch additions exhibit lower shrinkage, which is an indication the addition of starch as admixture in concrete improves the ability of the concrete reduce shrinkage problems. T2 - 2nd International Conference on Advances in Cement and Concrete Technology in Africa CY - Dar es Salaam, Tanzania DA - 27.01.2016 KW - Cassava KW - Starch KW - Cement KW - Concrete KW - Shrinkage PY - 2016 SN - 978-3-9817502-3-2 N1 - Geburtsname von Priebe, Nsesheye Susan: Msinjili, N. S. - Birth name of Priebe, Nsesheye Susan: Msinjili, N. S. VL - 187 SP - 196 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-36880 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Wolfram A1 - Grünewald, S. A1 - Ferrara, L. A1 - Dehn, F. T1 - Design of concrete for high flowability: progress report of fib task group 4.3 N2 - Flowable concretes can differ significantly from traditional vibrated concrete. Concrete types like self-compacting concrete (SCC), ultra high performance concrete (UHPC) and high performance fibre reinforced cementitious composites (HPFRCCs) require novel mix design approaches. This has consequences for the production and the performance in the hardened state. Mix designs for flowable concretes can incorporate a wide variety of innovative admixtures or components: e.g. superplasticisers increase the flowability and allow for significant reduction of the water content, shrinkage compensating admixtures or superabsorbent polymers support sound and damage free curing processes, viscosity modifying admixtures enhance the robustness, and new fibre types allow for sophisticated and tailored structural performance. The new Model Code has limitations regarding the application of flowable concrete, e.g. thresholds for the minimum aggregate size and the maximum strength. Provisions are added to include fibres for structural design. fib Task Group 4.3 aims at facilitating the use of innovative flowable materials for designing concrete structures and considers three aspects of flowable concrete: material properties, production effects and structural boundary conditions and performance. This paper reports about the progress of fib TG 4.3 related to the mix design of flowable concrete and discusses the present state-of-the-art concerning admixtures and robustness. T2 - fib Symposium (Proceedings) - Concrete - Innovation and design CY - Copenhagen, Denmark DA - 18.05.2015 KW - Admixtures KW - Fib model code KW - Fibres KW - Flowable concrete KW - Mix design KW - Robustness PY - 2015 SP - 1 EP - 10 AN - OPUS4-33800 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Paul, S. C. A1 - Ebell, Gino A1 - Van Zijl, G. P. A. G. A1 - Schmidt, Wolfram ED - Schlangen, E. ED - Sierra Beltran, M.G. ED - Lukovic, M. ED - Ye, G. T1 - Cracked and uncracked SHCC specimens under different exposure conditions N2 - This paper describes the fibre-reinforced strain hardening cement-based composite (SHCC) performance under various exposure conditions. Cracked and uncracked SHCC beam specimens were subjected to cyclic wetting and drying under chloride exposure to observe the time of depassivation and corrosion potential of the imbedded reinforcement. Two reference mortars, one of the same strength class as the SHCC (Mortar 1) and the other of high strength class (Mortar 2) were used under the same conditions. Finally, tests for determining the rapid chloride migration coefficient, electrical resistivity, capillary water absorption and freezethaw were also performed to observe the corrosion probability and diffusion rate in uncracked SHCC and mortars. T2 - SHCC3 - 3rd International RILEM conference on strain hardening cementitious composites CY - Dordrecht, The Netherlands DA - 03.11.2014 KW - Depassivation KW - SHCC corrosion crack KW - Lochkorrosion KW - Betonstahl PY - 2014 SN - 978-2-35158-150-6 SN - 978-2-35158-151-3 SP - 25 EP - 32 AN - OPUS4-32462 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Wolfram A1 - Brouwers, H.J.H. A1 - Kühne, Hans-Carsten A1 - Meng, Birgit T1 - Correlation between setting, heat evolution, and deformations of cementitious binder systems depending on type and amount of superplasticizer N2 - Today polycarboxylate ether based superplasticizer (PCE) is commonly used in concrete technology when high flow properties and water reduction are specified. The ionic strength of the polymers’ backbones determines the adsorption behaviour of polymers on clinker and early hydration products. The amount of required polymers for specified flow properties and the performance over the time of casting is thus determined by the molecular structure of the superplasticizer. The time depending consumption of polycarboxylate ether polymers strongly affects the reaction of aluminates and sulphate ions as well as the hydration process in general. Hence, the choice of polymers for particular flow properties greatly affects the very early properties of cementitious materials such as setting, heat evolution and autogenous deformations. In order to better understand how PCEs influence the early properties, mixes from cement, limestone filler, viscosity modifying agent and water were varied with a high and a low charge density superplasticizer in differing amounts. Results are presented from measurements with an automatic Vicat device, an isothermal heat flow calorimeter, and shrinkage cones. Tests were conducted at 5, 20, and 30 °C. It is shown that in presence of PCE the final set correlates well with the inflexion point of the heat flow curve, which emphasises the interrelation between C-S-H formation and setting. No such clear correlation can be found for the initial set, which is attributed to the fact that the initial set is rather a rheological than a structural phenomenon, so that other effects overlap with C-S-H formation. The results demonstrate that for a given polymer concentration low charge density polymers yield earlier setting than high charge polymers. However, this influence is overridden by the influence of the total amount of polymers in a cementitious system. Since PCE is typically added according to rheological specifications, and low charge PCE typically requires higher amounts of polymers than high charge PCE for comparable flow performance, low charge PCE retards setting more than high charge PCE. The paper furthermore points out that there is no significant influence of the polymer type or amount on the early deformations. Since type and amount strongly affect the hydration, it is demonstrated that early setting causes higher strain after the final set. It is hence concluded that higher PCE solid contents reduce the risk of early cracks that occur at time of setting, when a solid structure has already been formed but without resistance against cracks yet. T2 - 13th International congress on the chemistry of cement CY - Madrid, Spain DA - 03.07.2011 KW - Polycarboxylate superplasticizer KW - Setting KW - Heat evolution KW - Autogenous deformation KW - Self-compacting concrete KW - Calorimetry PY - 2011 SN - 978-84-7292-400-0 SP - 384 EP - 391 AN - OPUS4-24097 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Wolfram T1 - Controlling rheology - The key to individual concrete performance specifications N2 - During the last three decades concrete has emerged from a rather simple mass construction material based on only the three components cement, water, and aggregates towards a high performance material, which can be adjusted for high performance applications and according to ultimate user specifications. The reason for the rapid evolvement was the increasing awareness about how the rheology of concrete can be improved without negatively affecting the mechanical properties of concrete. Hence, mineral additions and in particular Chemical admixtures have been the most influential factors for the technological boost since approximately the 1980s. The incorporation of superplasticizers into concrete mixture compositions eventually facilitated concrete engineers to improve the workability properties without need to increase the water-cement-ratio (w/c) and furthermore to significantly reduce the w/c without loss of workability. This finally resulted in concrete with higher performance and specified properties. Fillers are basically used to improve the particle packing of cementitious Systems, but they can also be used beneficially to support the rheology, since they modify the water demand and may interact with superplasticizers as well. Finally, supplementary admixtures like polysaccharides have become more populär in the field of mortar, plaster, and grout technology. They can have a variety of rheological effects on cementitious Systems, which can be used to individually adjust their performance. The possibility to control the rheology and the significantly widened ränge of consistencies that can be adjusted opened up the gates for modern concrete and any type of high performance concrete. Therefore, without doubt, it can be concluded that the capability to control the rheology of concrete Systems can be considered as the catalyst for the invention of the many recent mortar and concrete innovations such as polymer modified cementitious composites (PCC) self-compacting concrete (SCC), high-performance concrete (HPC), ultra-high performance concrete (UHPC) or engineered cementitious composites (ECC). Therefore, understanding the rheology of cementitious Systems and how to control the workability by the use of Chemical admixtures is the key to innovations in concrete technology. However, the other side of the coin of versatility is that sophisticated cementitious Systems have become more sensitive. Hence, concrete mixture composition with admixtures demands for a high level of expertise and often there is lack of awareness about the mode of Operation of rheology modifying admixtures among concrete technoiogists. The paper gives a comprehensive overview about rheology modifying constituents such as superplasticizers, stabilising agents, and mineral fillers, and how they can be used depending upon the application in the most favourable way. T2 - Facade coatings and plasters - European coatings conference CY - Düsseldorf, Germany DA - 29.10.2013 PY - 2013 SP - 93 EP - 102 PB - Vincentz AN - OPUS4-30827 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Barthel, Maria A1 - Schmidt, Wolfram A1 - Kühne, Hans-Carsten ED - Uzoegbo, H.C. ED - Schmidt, Wolfram T1 - Concrete pavers for the mitigation of the urban heat island effect N2 - Nowadays an increasing population escapes from rural to urban regions worldwide. Especially in developing countries the number of inhabitants in urban areas triplicated from the 1950s until today. These changes entail a higher demand for residential buildings and infrastructure. Therefore, the building density and the land sealing rise because of the growing cities. Existing vegetation is replaced by sealed or paved surfaces. Concrete as building material provides a high capacity for heat storage, so that the temperature in densely populated inner cities increases. Hence, the microclimate in cities has become warmer than in the surrounding rural areas. This phenomenon is called Urban Heat Island Effect. In the presented research the aim is to reduce this effect by applying self-cooling concrete pavers at large open areas. These concrete pavers differ from normal pavers by their ability to store water temporarily. Thus these pavements counterbalance the absorption of solar radiation and the subsequent transfer of this heat to the surroundings based on the use of evaporation enthalpy. To bring this concept into practice without losing the mandatory specifications like sufficient compressive strength a multilayer design for the pavers was selected and the concrete mixture compositions were optimized for appropriate water transport properties. For the utilization in climate zones with marginal precipitation events only the concept has to be adapted to the circumstances, for example with a separate water supply. T2 - ACCTA - International conference on advances in cement and concrete technology in Africa 2013 CY - Johannesburg, South Africa DA - 28.01.2013 KW - Urban heat island effect KW - Earth-moist concrete KW - Concrete multilayers pavers KW - Water storage KW - Self-cooling pavement PY - 2013 SN - 978-3-9815360-3-4 SP - 953 EP - 960 AN - OPUS4-27769 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Wolfram A1 - Kühne, Hans-Carsten A1 - Leinitz, Sarah ED - Diouri, A. ED - Boukhari, A. ED - Ait Brahim, L. ED - Bahi, L. ED - N., Khachani ED - Saadi, M ED - Aride, J. ED - Nounah, A. T1 - Concrete casting robustness improvement due to active rheology N2 - With ongoing innovation in process technology, the challenges of concrete technology are more and more focused on the rheological optimisation for these processes, since improper mixture stability or poor compaction ability negatively affect the concrete homogeneity and quality. However, along with the increasing complexity of today’s concrete mixture compositions, concrete becomes more prone to failure regarding the casting process. Variable properties of the raw materials typically cause changing workability. The reasons can be found among others in scattering water contents, physical or chemical properties of the cement or varying environmental temperatures. Robustness in the delicately adjusted rheology, however, is of utmost importance for modern and future process technology, from sprayed concrete over pumpable concrete towards 3D-printing, with regard to the long-term strength, the function and the durability. Typically, material induced changes cannot be identified easily due to the complex interactions of concrete constituents. Therefore, a precise and prompt counteraction is impossible. However, it is known that the yield stress can be controlled by addition of supplementary superplasticizer or stabilising agent. In combination with computerized process observation tools that can rapidly interpret and react on changes in the rheology, it is therefore thinkable, that only these two admixture types can adjust the rheology steadily and permanently, regardless of the actual root cause for observed macroscopic rheology change. The presentation will firstly give a comprehensive overview of effects at the interface between pore solution, particles and hydrates, which affect the rheology of fresh concrete. Secondly, ways are recommended how the rheology can be actively manipulated before eventually computerized methods are demonstrated that help to actively and rapidly assess and counteract performance scatter during steady casting processes. T2 - 2nd International Congress on Materials & Structural Stability (CMSS-2017) CY - Rabat, Morocco DA - 22.11.2017 KW - Cusum KW - Rheology KW - Control Chart KW - Concrete KW - Robustness PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-444317 DO - https://doi.org/10.1051/matecconf/201814901001 SN - 2261-236X VL - 149 SP - 01001-1 EP - 01001-7 PB - EDP Sciences CY - Les Ulis AN - OPUS4-44431 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Wolfram A1 - Kamashanju, Kabibi Charles ED - Rogge, Andreas ED - Meng, Birgit T1 - Circular, bio-based, intelligent ecosystems for climate friendly construction materials supplies N2 - Abstract: Concrete is a major contributor to global energy demand and CO2-emissions, necessitating mitigation strategies. Utilising bio-based resources like polysaccharides, pozzolanic ashes from agricultural waste, and bio-based fibres and aggregates can reduce carbon footprints. However, implementation is hindered by stand- ards favouring scarce and traditionally European materials like fly ash and slag. This highlights the need to diversify resource streams to benefit the global South's abundance of bio-based resources and arable land. An inclusive approach recognizing bio-based resources is required through innovation and regional adaptation. T2 - 63. Forschungskolloquium Green Intelligent Building CY - Berlin, Germany DA - 16.10.2024 KW - Intelligent ecosystems KW - CO2-emissions PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-613160 SN - 978-3-9818564-7-7 SP - 102 EP - 113 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-61316 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Wolfram A1 - Tchetgnia Ngassam, Ines A1 - Breitschaft, G. A1 - Virchow, S. ED - Diouri, A. ED - Boukhari, A. ED - Ait Brahim, L. ED - Bahi, L. ED - Khachani, N. ED - Saadi, M. ED - Aride, J. ED - Nounah, A. T1 - Challenges of the growing African cement market – environmental issues, regulative framework, and quality infrastructure requirements N2 - The African cement, concrete and construction business is growing at rapid pace. The cement sales are expected to grow rapidly until 2050. The number of newly built cement plants increases dramatically and in addition more cements are being imported from outside the continent, e.g. from Turkey, Pakistan, Indonesia, and China, driven by overcapacities in the countries of origin. This causes a high number of potentials and challenges at the same time. Newly built cement plants can operate directly at best technological state of the art and thus incorporate more sustainable technologies as well as produce new and more sustainable products such as cements blended with sustainable supplementary cementitious materials such as calcined clays, and industrial or agricultural by products. At the same time the new variety of binding agent as well as the international imports, which are driven by price considerations, make the cement market prone to quality scatter. This puts pressure on the quality control regulations and institutions to ensure safety of construction, healthy application, and environmental safety for the population. The paper presents possible solutions to build up the rapidly increasing African cement production more sustainably than in the rest of the world as well as the related challenges and obstacles that need to be overcome. Based on experiences with a series of pan-African cement testing laboratory proficiency schemes conclusions are made on technical, regulative and political level. T2 - 2nd International Congress on Materials & Structural Stability (CMSS-2017) CY - Rabat, Morocco DA - 22.11.2017 KW - Quality Infrastructure KW - Africa KW - Proficiency Testing KW - Cement KW - Admixtures PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-444330 DO - https://doi.org/10.1051/matecconf/201814901014 SN - 2261-236X VL - 149 SP - 01014-1 EP - 01014-8 PB - EDP Sciences CY - Les Ulis AN - OPUS4-44433 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -