TY - JOUR A1 - Dabah, Eitan A1 - Pfretzschner, Beate A1 - Schaupp, Thomas A1 - Kardjilov, N. A1 - Manke, I. A1 - Boin, M. A1 - Woracek, R. A1 - Griesche, Axel T1 - Time-resolved Bragg-edge neutron radiography for observing martensitic phase transformation from austenitized super martensitic steel N2 - Neutron Bragg-edge imaging was applied for the visualization of a γ-Austenite to α'-martensite phase transformation. In the present study, a super martensitic stainless steel sample was heated until complete austenitization and was subsequently cooled down to room temperature. The martensitic phase Transformation started at Ms = 190 °C. Using a monochromatic neutron beam with λ = 0.390 nm, the transmitted intensity was significantly reduced during cooling below Ms, since the emerging martensitic phase has a higher attenuation coefficient than the austenitic phase at this wavelength. The phase Transformation process was visualized by filming the transmission images from a scintillator screen with a CCD camera with a temporal resolution of 30 s and a spatial resolution of 100 µm. KW - Neutron imaging KW - Bragg-edge imaging KW - Phase transformation PY - 2017 DO - https://doi.org/10.1007/s10853-016-0642-9 SN - 0022-2461 SN - 1573-4803 VL - 52 IS - 6 SP - 3490 EP - 3496 AN - OPUS4-38574 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaupp, Thomas A1 - Kannengießer, Thomas T1 - Untersuchungen zur Kaltrissempfindlichkeit hochfester Feinkornbaustähle mittels Implant-Test N2 - Der Implant-Test nach ISO 17642-3 gehört zur Gruppe der fremdbeanspruchten Kaltrisstests, bei dem eine äußere Beanspruchung auf einen zylindrischen Stab (Implant-Probe) definiert aufgebracht wird. Mit dieser Kaltrissprüfung wurde vergleichende Analysen zur Kaltrissempfindlichkeit der modernen hochfesten Feinkornbaustähle S960MC und S960QL durchgeführt. T2 - BMDK - Bachelor-, Master- und Doktorandenkolloquium CY - Universität Magdeburg, Germany DA - 28.11.2019 KW - Hochfeste Feinkornbaustähle KW - Implant-Test KW - MAG-Schweißen KW - Wasserstoff PY - 2019 AN - OPUS4-49837 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaupp, Thomas A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas T1 - Vergleich von Schweißeigenspannungen bei vergüteten und thermomechanisch gewalzten hochfesten Feinkornbaustählen T2 - MDDK-, Master-, Diplomanden- und Doktorandenkolloguium CY - Magdeburg, Germany DA - 2013-07-04 PY - 2013 AN - OPUS4-28807 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaupp, Thomas A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas T1 - Vergleich von Schweißeigenspannungen bei vergüteten und thermomechanisch gewalzten hochfesten Feinkornbaustählen T2 - BAM Alumni Kolloquium CY - Berlin, Germany DA - 2014-09-11 PY - 2014 AN - OPUS4-31416 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schaupp, Thomas A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas T1 - Vermeidung von Kaltrissen beim Mehrlagenschweißen mit modifizierten Sprühlichtbogenprozessen - Welchen Einfluss haben Nahtgeometrie und Wärmeführung? N2 - Das Schweißen hochfester Feinkornbaustähle mit modifizierten Sprühlichtbögen bietet die Möglichkeit, kleinere Nahtöffnungswinkel zu schweißen. Allerdings findet der modifizierte Sprühlichtbogen in den Regelwerken zur schweißtechnischen Verarbeitung hochfester Feinkornbaustähle unter Vermeidung von Kaltrissbildung bisher keine Berücksichtigung. Dieser Beitrag betrachtet die Wechselwirkungen der Haupteinflussgrößen auf die Kaltrissbildung beim Schweißen mit kleineren Nahtöffnungswinkeln am Beispiel des hochfesten Stahls S960QL. KW - Hochfeste Feinkornbaustähle KW - Kaltrisse KW - Wärmeführung KW - Nahtgeometrie KW - Wasserstoff KW - Eigenspannungen PY - 2019 SN - 0554-9965 VL - 71 IS - 7 SP - 342 EP - 347 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-48491 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Kannengießer, Thomas A1 - Schaupp, Thomas ED - Brockmann, S. ED - Krupp, U. T1 - Wasserstoffunterstützte Kaltrissbildung in Schweißnähten hochfester Stahlgüten - Anforderungen an die Prüfung N2 - Wasserstoff kann eine Rissbildung u.U. auch noch nach Tagen in der Schweißnaht bewirken. Dabei stellen höherfeste Stähle etablierte Kaltrissprüftests vor Herausforderungen. Generell nimmt die zur Rissvermeidung tolerierbare Wasserstoffkonzentration mit zunehmender Festigkeit der Werkstoffe ab. Zudem verändern weiterentwickelte Schweißverfahren die Nahtgeometrie und Wärmeeinbringung und die Ausbildung risskritischer Mikrostrukturen (z.B. Wärmeeinflusszone). Am Beispiel des Implant- und Tekken-Tests werden die Einsatz- u. Anwendungsgrenzen bewertet. Zu berücksichtigen ist, dass beim Schweißen eine äußere mechan. Beanspruchung durch bauteilspezifische Steifigkeitsverhältnisse wirksam ist. Zusätzlich werden weiterführende Prüfverfahren zur Bestimmung der Wasserstoffkonzentration und -diffusion in Schweißnähten vorgestellt, wie die Trägergasheißextraktion (TGHE) für die Ermittlung der Wasserstoffkonzentration (ISO 3690) oder Hochtemperaturdiffusionskoeffizienten. Diese Werte sind für die schweißtechnische Praxis von großer Bedeutung, um Haltezeiten z.B. für das Wasserstoffarmglühen abzuleiten. T2 - Tagung Werkstoffprüfung 2021 CY - Online meeting DA - 02.12.2021 KW - Wasserstoff KW - Kaltrissprüfung KW - Schweißen KW - Stahl KW - Hochfest PY - 2021 SN - 978-3-941269-98-9 SP - 15 EP - 20 PB - Stahlinstitut VDEh CY - Düsseldorf AN - OPUS4-53900 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schaupp, Thomas A1 - Schröpfer, Dirk A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Welding residual stress distribution of quenched and tempered and thermo-mechanically hot rolled high strength steels N2 - Beside quenched and tempered (QT) high strength steels advanced technologies in steel manufacturing provide steels produced by the thermo-mechanical controlled process (TMCP) with yield strength of 960 MPa. These steels differ in the carbon and micro-alloying element content. With variation of heat control TIG-welded dummy seams on both steel types were performed. Analyses concerning microstructure and residual stress evolution due to welding showed typical stress distributions according to common concepts. Yet, the TMCP-steel shows higher residual stresses than the QT-steel. KW - Mill Scale KW - Quenched KW - Residual Stress KW - Tempered High Strength Steel KW - Thermo-Mechanical Controlled Process KW - Welding PY - 2014 DO - https://doi.org/10.4028/www.scientific.net/AMR.996.457 SN - 1022-6680 SN - 1662-8985 VL - 996 SP - 457 EP - 462 PB - Trans Tech Publ. CY - Zurich AN - OPUS4-31443 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schaupp, Thomas A1 - Schröpfer, Dirk A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Welding residual stresses in 960 MPa grade QT and TMCP high-strength steels N2 - High-strength steels with yield strengths ≥ 690 MPa are becoming increasingly significant for modern steel constructions. Both quenched and tempered (QT) high-strength steels and steels produced by the thermo-mechanically controlled process (TMCP) are currently available. TMCP-steels are usually provided with a typical mill scale. Apart from the manufacturing process these steels differ also in their chemical composition. The influence of these differences are investigated here with focus on the residual stresses formed during TIG welding. Bead on plate welds have shown characteristic residual stress distributions depending on the type of steel as well as on the heat input and preheat temperature. The following work demonstrates that the fluid flow, induced by the elements present in the mill scale, leads to a deeper penetration of the material. This can also lead to increased residual stresses in the surface of the weld and the HAZ. Furthermore, higher heat input and preheat temperature can induce higher tensile residual stresses − which are evident in the present study. KW - Residual stresses KW - High-strength steel KW - Welding KW - Mill scale KW - Phase transformation PY - 2017 DO - https://doi.org/10.1016/j.jmapro.2017.05.006 SN - 1526-6125 VL - 27 SP - 226 EP - 232 PB - ELSEVIER AN - OPUS4-40312 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schröpfer, Dirk A1 - Kromm, Arne A1 - Schaupp, Thomas A1 - Kannengießer, Thomas T1 - Welding stress control in high-strength steel components using adapted heat control concepts N2 - High-strength steels are increasingly applied in modern steel constructions to meet today’s lightweight requirements. Welding of these steels demands a profound knowledge of the interactions between the welding process, cooling conditions, heat input, and the resulting metallurgical occurrences in the weld and its vicinity. Additionally, welding stresses may be detrimental for the safety and performance of high-strength steel component welds during fabrication and service, especially due to the high yield ratio. For a development of strategies to adjust welding heat control, all these effects should be considered, to reach a complete exploitation of the high-strength steel potential. In recent researches at BAM, multilayer GMAW experiments were performed with high-strength steels, in which cooling conditions and resulting microstructure were analyzed for varied heat control parameters. The application of a unique 3d-operating testing facility and X-ray diffraction measurements allowed the analysis of local stresses in the weld while welding and cooling under component relevant shrinkage restraints. As a result, correlations between material behavior, welding, and cooling condition and the arising multi-axial stresses and forces were found. Based on this study, statements for the development of adapted heat control concepts were derived, which are presented by means of specific analysis examples. KW - Residual stresses KW - GMA welding KW - Restraint KW - High-strength steels KW - Process parameters PY - 2019 DO - https://doi.org/10.1007/s40194-018-00691-z SN - 0043-2288 VL - 63 IS - 3 SP - 647 EP - 661 PB - Springer AN - OPUS4-48006 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaupp, Thomas A1 - Kannengießer, Thomas T1 - Zum Einfluss der Wärmeführung auf den Wasserstoffeintrag und die Kaltrissbildung beim Schweißen höherfester Feinkornbaustähle N2 - In vielen Industriebranchen werden zunehmend hochfeste Feinkornbaustähle mit Streckgrenzen ≥ 690 MPa eingesetzt. Allerdings werden mit zunehmender Festigkeit deutlich höhere Anforderungen an deren schweißtechnische Verarbeitung gestellt, da gerade die Sensibilität gegenüber einer Degradation der mechanischen Eigenschaften, durch den beim Schweißen aufgenommenen Wasserstoff, mit steigender Festigkeit stark zunimmt. In der vorliegenden Präsentation sind Ergebnisse aus vergleichenden Untersuchungen mit konventionellem Übergangslichtbogen und modifiziertem Sprühlichtbogen mit reduziertem Nahtöffnungswinkel hinsichtlich der Wasserstoffaufnahme beim Schweißen unter Variation von Streckenenergie, Arbeitstemperatur und Nachwärmprozedur dargestellt. Grundsätzlich ist den erarbeiteten Ergebnissen zu entnehmen, dass im Schweißgut von Stumpfstoßverbindungen mit reduziertem Nahtöffnungswinkel erhöhte mittlere Wasserstoffkonzentrationen vorliegen. Geeignete Wärmeführungen führten zu einer signifikanten Reduzierung der Wasserstoffkonzentration beim Einsatz der Nahtkonfiguration mit abgesenktem Nahtöffnungswinkel. Dabei erwies sich eine Nachwärmprozedur aus der Schweißwärme heraus als zielführend. Des weiteren sind Gradienten der Wasserstoffkonzentration in Blechdickenrichtung aufgezeigt. T2 - Forschungsseminar OvGU CY - Magdeburg, Germany DA - 15.11.2018 KW - Höherfeste Feinkornbaustähle KW - MAG-Schweißen KW - Schweißprozessparameter KW - Wärmeführung KW - Wasserstoff PY - 2018 AN - OPUS4-46776 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -