TY - JOUR A1 - Yang, Keke A1 - Sowada, Matthias A1 - Olfert, Viktoria A1 - Seitz, Georg A1 - Schreiber, Vincent A1 - Heitmann, Marcel A1 - Hein, David A1 - Biegler, Max A1 - Jüttner, Sven A1 - Rethmeier, Michael A1 - Meschut, Gerson T1 - Influence of liquid metal embrittlement on the failure behavior of dissimilar spot welds with advanced high-strength steel: A component study N2 - This study investigates the effects of liquid metal embrittlement (LME) cracks on the mechanical performance of resistance spot-welded joints in zinc-coated advanced high-strength steel (AHSS) at the component level. To this end, a novel component-level test specimen featuring a hat and L-shaped profile was developed to identify critical failure points under three-point bending loads. Load-bearing capacity tests were subsequently conducted under both quasi-static and impact loading conditions, specifically targeting LME cracks with an average depth reaching 63.6% of the sheet thickness. By monitoring the surface strain of spot welds affected by LME cracks, the study visualizes stress concentration effects at the crack tips and traces the propagation of these cracks into the base material, which ultimately leads to material tearing and joint failure. The findings reveal that the effect of LME cracks in reducing load-bearing capacity is more pronounced under impact loading than under quasi-static loading, highlighting a previously underexplored aspect of LME behavior under impact loading. Specifically, the peak load decreased by 3.9% and 10.8%, while energy absorption declined by 52.2% and 78.3% under quasistatic and impact loading, respectively. KW - Liquid metal embrittlement KW - Resistance spot welding KW - Impact loading KW - Crack propagation KW - Advanced high-strength steel PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-621727 DO - https://doi.org/10.1016/j.jmrt.2024.11.166 VL - 33 SP - 8321 EP - 8328 PB - Elsevier B.V. AN - OPUS4-62172 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lemke, Josefine A1 - Höfemann, Matthias A1 - Biegler, Max A1 - Rethmeier, Michael T1 - Process strategies for optimizing the cooling behaviour of laser-welded Tailor Welded Blanks made of advanced high strength steels (AHSS) N2 - AHSS with 1000 MPa tensile strength show promising properties for the use in Tailor Welded Blanks (TWBs) to locally strengthen car body parts. Challenges in laser beam welding of the sheets are hardness-drops and -peaks in the heat-affected zone (HAZ) and weld, which cause risks during cold-forming. This happens due to rapid cooling caused by laser welding. A numerical approach aiming for slower cooling rates in the weld region is presented in this article. Laser welded sheets served as reference for setting up a process simulation. Models for pre-heating and a coaxial setup with power split were set up. A correlation between cooling-rate and hardness in the joining zone was established and applied to the modelled strategy. Splitting the power led to a slightly narrower weld seam and experimental pre-heating of the sheets to 600 °C could lower total seam hardening. It achieved a homogenization of the fusion zone. KW - AHSS KW - Laser welding KW - Tailor Welded Blanks KW - Hardness KW - FEM KW - HAZ PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-622324 DO - https://doi.org/10.1016/j.procir.2024.08.176 VL - 124 SP - 570 EP - 573 PB - Elsevier B.V. AN - OPUS4-62232 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Akyel, Fatma A1 - Üstündag, Ömer A1 - Bakir, Nasim A1 - Brunner-Schwer, Christian A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Influence of heat input on cooling rates and mechanical properties of laser hybrid welded thick structural steels N2 - Laser hybrid welding presents several challenges when used to weld thick steels. A typical weld is divided into the arcdominated and laser-dominated zone. These zones lead to variations in the mechanical properties of the weld. The laserdominated zone is of particular importance regarding mechanical properties, notably Charpy impact toughness, due to the high cooling rates and the absence of filler wire. The low heat input of the laser can lead to martensitic microstructure causing hardening and deterioration of impact toughness. The high heat input of the arc can lead to grain coarsening and even loss of impact toughness. This study examines the influence of heat input on the cooling rates, microstructure and mechanical properties of single-pass laser hybrid welded steels of S355J2 and EH36 with thicknesses up to 30 mm. The experiments were performed with a 20-kW fibre laser and a contactless electromagnetic weld backing in the butt-joint configuration in 1G welding position. The cooling time was measured in three different locations near the fusion lines corresponding to different heights of the seam using a special configuration with pyrometers, collimators and optical fibres. The test specimens for the Charpy impact testing and tensile testing were extracted in three different depths. The experiments indicated that a heat input of 1.6 kJ/mm–2 kJ/mm, 2 kJ/mm–2.4 kJ/mm and 3.7 kJ/mm were recommended when single-pass laser hybrid welding of 20-, 25-, and 30-mm-thick structural steels regarding the minimum requirements of the mechanical properties, respectively. KW - Laser hybrid welding KW - Heat input KW - Mechanical properties KW - Charpy impact toughness KW - Cooling rate PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-625282 DO - https://doi.org/10.1007/s40194-025-01924-8 SN - 1878-6669 SP - 1 EP - 15 PB - Springer CY - United Kingdom AN - OPUS4-62528 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yang, Chunliang A1 - Yang, Fan A1 - Meng, Xiangmeng A1 - Putra, Stephen Nugraha A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Multi-refining effects of an AC electromagnetic field on the microstructure in AA5754 laser beam welding N2 - Fine-grain structure is beneficial to the mechanical properties of the joint. Different kinds of grain and sub-grain structures refined by magnetic field during laser beam welding of AA5754 aluminum alloy are analyzed in this manuscript, and the influences of different magnetic field parameters (magnetic flux density and frequency) in these refining effects are also studied. Using the scanning electron microscope (SEM), the sub-grain structure near the fusion line was obtained, and it was found that the branching promotion and branches refinement can be achieved by the magnetic field. The branches become finer with the magnetic flux density or frequency increases, and this effect is stronger in the dendritic region than in the equiaxed region. The results of electron backscatter diffraction (EBSD) in the equiaxed region show that a high-frequency magnetic field can greatly reduce the average grain size, while a low-frequency one has little effect. A phenomenological nucleation model based on dendrite fragmentation theory was established, and it was introduced into the phase field model to analyze the equiaxed grains evolution process. In addition, another refinement mechanism was also observed. The periodic solidification pattern caused by the unstable solidification in the molten pool can refine the grains, and the magnetic field promotes this kind of grain refinement by promoting the solidification period. KW - Laser beam welding KW - Magnetic field KW - Aluminum alloy KW - Crystal branch development KW - Periodic solidification pattern KW - Grain refinement PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-637222 DO - https://doi.org/10.1016/j.ijheatmasstransfer.2025.127509 SN - 0017-9310 VL - 252 SP - 1 EP - 16 PB - Elsevier Ltd. AN - OPUS4-63722 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schempp, Philipp A1 - Cross, C.E. A1 - Häcker, Ralf A1 - Pittner, Andreas A1 - Rethmeier, Michael T1 - Influence of grain size on mechanical properties of aluminium GTA weld metal N2 - Grain refinement is an important possibility to enhance the mechanical properties such as strength, ductility and toughness of aluminium weld metal. In this study, grain refinement was achieved through the addition of commercial grain refiner Al Ti5B1 to gas tungsten arc weld metal of the aluminium alloys 1050A (Al 99.5) and 5083 (Al Mg4.5Mn0.7). The grain refiner additions led to a significant reduction of the weld metal mean grain size (Alloy 1050A, 86 %; Alloy 5083, 44 %) with a change in grain shape from columnar to equiaxed. Tensile tests showed for Alloy 5083 that the weld metal's ductility can be increased through grain refinement. No improvement in weld metal strength (i.e. yield strength and ultimate tensile strength) was observed. Furthermore, tear tests with notched specimens revealed that the resistance against initiation and propagation of cracks in the weld metal can be enhanced through grain refinement. The toughness was observed to increase clearly by grain refinement in weld metal of commercial pure Al (Alloy 1050A). In Alloy 5083 weld metal, the toughness was not improved through grain refinement, likely because of a semi-continuous network of brittle intermetallic phases that facilitate crack propagation. KW - GTA welding KW - Aluminium KW - Grain size KW - Tensile tests KW - Dynamic fracture tests PY - 2013 DO - https://doi.org/10.1007/s40194-013-0026-6 SN - 0043-2288 SN - 1878-6669 VL - 57 IS - 3 SP - 293 EP - 304 PB - Springer CY - Oxford AN - OPUS4-28065 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zhang, L. J. A1 - Zhang, J. X. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael A1 - Na, S.J. T1 - Numerical simulation of full penetration laser welding of thick steel plate with high power high brightness laser N2 - Full penetration laser welding was carried out on a 10 mm steel plate using a 16 kW maximum power continuous wave thin disk laser. Upper surface and lower surface of molten pool were observed synchronously with two high speed CCD cameras during the welding process. The lower surface was much longer and more unstable than the upper one. A three dimensional laser deep penetration welding model in which volume of fluid (VOF) method was combined with a ray-tracing algorithm was used to simulate the dynamic coupling between keyhole and molten pool in laser full penetration welding. The calculated weld cross-section morphology and molten pool length on both upper side and lower side agree well with experimental results. Evolution of molten pool in lower side during full penetration laser welding was analyzed, periodical features of energy coupling, molten pool behavior and keyhole dynamics in laser full penetration welding were identified and discussed. KW - Full penetration laser welding KW - Molten pool KW - Keyhole KW - Thick plate PY - 2014 DO - https://doi.org/10.1016/j.jmatprotec.2014.03.016 SN - 0924-0136 SN - 1873-4774 VL - 214 IS - 8 SP - 1710 EP - 1720 PB - Elsevier CY - Amsterdam AN - OPUS4-30549 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gook, Sergej A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Hybrid laser arc welding of X80 and X120 steel grade N2 - The aim of the present work was to investigate the possibilities of hybrid laser arc welding regarding reliable production of longitudinal welds of high strength pipe steels X80 and X120 and to evaluate achievable mechanical properties of laser hybrid welds. The study focused on weld toughness examination in low temperature range up to –60°C. Suitable filler materials were identified in the context of this task. It could be shown that metal cored electrodes guaranteed sufficient Charpy impact toughness at low temperature for both investigated materials. Modern arc welding technologies such as modified pulsed spray arc were used to promote deeper penetration of the filler material into the narrow laser welding gap. Edge preparation with a 14 mm deep root face was considered as optimum, because no penetration of the filler material could be detected beyond this depth limit, and therefore, any metallurgical influences on the weld metal properties through the welding wire could be excluded. KW - High strength steel KW - Laser hybrid welding KW - Modified spray arc KW - Longitudinal weld KW - Pipeline PY - 2014 UR - http://www.maneyonline.com/doi/full/10.1179/1362171813Y.0000000154 DO - https://doi.org/10.1179/1362171813Y.0000000154 SN - 1362-1718 SN - 1743-2936 VL - 19 IS - 1 SP - 15 EP - 24 PB - Maney CY - London AN - OPUS4-29593 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gook, Sergej A1 - Üstündag, Ömer A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Method for defect-free hybrid laser-arc welding of closed circumferential welds N2 - This paper presents investigation results of a process for defect-free hybrid laser arc welding (HLAW) of closed circumferential welds. The process aims to avoid weld imperfections in the overlap area of a HLAW circumferential weld. A process control strategy for closing the circumferential weld was developed to achieve a defect-free overlap region by controlling the solidification conditions at the end of the weld. The controlled heat flow is achieved by adjusting the parameters of both welding processes involved, the laser beam as well as gas metal arc welding (GMAW) process. Experimental investigations were carried out on 12 mm to 15 mm thick tube sections. The influence of process parameters such as the laser ramp time, the change in magnification scale and the defocusing of the laser beam on the solidifi-cation conditions at the end of the circumferential weld was investigated to find an optimum strategy for ramping out the process energy. Within the framework of the experimental studies, it was demonstrated that defocusing the laser beam in the range between 60 mm and 100 mm over a short run-out area of the weld of approximately 15 mm led to a significantly better weld formation in the overlap area. A favourable cup-shaped weld shape could be achieved without a tendency to crack. The laser optics with a motor-driven lens system made it possible to increase the laser beam diameter without changing the position of the GMAW arc relative to the component surface. KW - Weld defects KW - Hybrid welding KW - Laser beam welding KW - Pipe manufacturing KW - Gas shielded arc welding PY - 2021 VL - 20 IS - 4 SP - 334 EP - 339 PB - DVS Media AN - OPUS4-54665 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Vollertsen, F. A1 - Grünenwald, S. A1 - Rethmeier, Michael A1 - Gumenyuk, Andrey A1 - Reisgen, U. A1 - Olschok, S. T1 - Welding thick steel plates with fibre lasers and GMAW N2 - The results of a collaborative research project on laser beam weldability of carbon steels of high sheet thickness are presented. That includes single and multiple pass welding of 16 mm and 20 mm thick plates, as well as the investigation of acceptable tolerances i.e. gap bridgeability and edge misalignment. For the welding experiments fibre lasers with 8 kW, 20 kW laser power and different GMAW-techniques were used in various applications. With the 20 kW fibre laser 16 mm plates could be welded with a single pass, 20 mm required a seam preparation or alternatively preheating of the material. For multi pass welding with 8 kW laser power a joint preparation with a single V-butt joint with a broad root face (Y-groove) was applied. The root pass was always welded with a hybrid process, the filler passes with a hybrid process as well as a GMAW process which produced the best results. KW - Arc welding KW - Carbon steels KW - Combined processes KW - Fibre lasers KW - Gas shielded arc welding KW - GMA welding KW - Multirun welding KW - Reference lists KW - Steels KW - Unalloyed steels PY - 2010 SN - 0043-2288 SN - 1878-6669 VL - 54 IS - 3/4 SP - R62 EP - R70 PB - Springer CY - Oxford AN - OPUS4-21224 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gaul, Holger A1 - Weber, Gert A1 - Rethmeier, Michael T1 - Evaluation of fatigue crack propagation in spot welded joints by stiffness measurements N2 - Resistance spot welded joints made of two advanced high strength steels (AHSS) and one high strength steel (HSS) were examined. In the high cycle fatigue regime tests were realised for one loading condition, and the load and the displacement were measured. From the load and displacement range, the stiffness was calculated and in situ normalised to its value after 1000 cycles. It was thus possible to use the normalised stiffness evaluated during the experiment as failure criterion for the fatigue test of resistance spot welded joints. In order to evaluate this failure criterion, fatigue cracks were produced in the three different steel grades mentioned above according to user-specified levels of the normalised stiffness. It was found that the fatigue crack area increases linearly and the through-sheet-thickness crack length exponentially with decreasing stiffness. The comparison of the fatigue crack propagation during the fatigue test of the three different tested base metals showed very similar values. The comparability of fatigue tests performed on spot welded joints might thus be improved by the in situ evaluated stiffness as a failure criterion. This can be also used in further work to verify results of computer simulations of the stress intensity factor at spot welds with the help of experimental results. KW - Resistance spot welding KW - Fatigue KW - Frequency KW - Stiffness KW - Advanced high strength steels KW - Crack growth PY - 2011 DO - https://doi.org/10.1016/j.ijfatigue.2010.12.005 SN - 0142-1123 VL - 33 IS - 5 SP - 740 EP - 745 PB - Elsevier CY - Oxford AN - OPUS4-22207 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Perret, William A1 - Schwenk, Christopher A1 - Rethmeier, Michael T1 - Comparison of analytical and numerical welding temperature field calculation N2 - Analytical and numerical methods are used to estimate the temperature field due to the heat effects of welding. Numerical techniques are more adapted for industrial complex applications where analytical solutions do not exist yet. However, computational time is much lower with analytical models and a combination of both methods is investigated. Therefore, the two approaches are introduced and confronted in this paper. The finite-element software Ansys has been used for numerical simulations and Scilab for analytical simulations. In order to get a similar result quality, both methods have to be analysed and compared with respect to boundary conditions. These configurations are presented in this paper. Before starting any analysis, the analytical and numerical models have to be comparable. For the numerical simulation, every in- or output is given in discrete form and, for the analytical simulation, in continuous form. Thus, an analysis of the energy input distribution in both models is compulsory to ensure that the same amount of energy is applied. After this first study, a comparison of the analytical and numerical temperature field simulation is done from a fix point source in an infinite volume in steady state to a moving point source in a finite dimension in a transient state. A good agreement between the analytical and the numerical simulation results is found. However, some techniques, like a consideration of an image heat source for the analytical model or the selection of boundary conditions for the numerical model, need to be taken into consideration when the degree of complexity of the study (finite dimension or cooling time) increases. The limit of the comparison is reached when the geometry becomes too complex and when the effect of variable thermal properties with temperature cannot be neglected. KW - Welding simulation KW - Temperature field KW - Analytical approach KW - Numerical approach KW - Heat conduction PY - 2010 DO - https://doi.org/10.1016/j.commatsci.2009.11.032 SN - 0927-0256 VL - 47 IS - 4 SP - 1005 EP - 1015 PB - Elsevier CY - Amsterdam AN - OPUS4-20887 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kannengießer, Thomas A1 - Kromm, Arne A1 - Gibmeier, J. A1 - Rethmeier, Michael T1 - In-situ-Analyse der Phasenumwandlungskinetik während des Schweißens N2 - Zugeigenspannungen, wie sie beim Schweißprozess durch inhomogene Temperaturverteilungen und Schrumpfungen hervorgerufen werden, können die Lebensdauer geschweißter Verbindungen signifikant herabsetzen. Eine neue und außerordentlich attraktive Methode, um Druckeigenspannungen bereits während des Schweißens gezielt einzustellen, gelingt mit sogenannten LTT (Low Transformation Temperature)-Legierungen. LTT-Legierungen weisen eine martensitische Phasenumwandlung bei relativ niedrigen Temperaturen auf, wobei die damit verbundene Volumenexpansion zu einer Reduktion der Schrumpfeigenspannungen bzw. Erzeugung von Druckeigenspannungen führt. Zum direkten Nachweis der Phasenumwandlungen und der damit verbundenen resultierenden Schweißeigenspannungen wurden erstmals In-situ-Schweißexperimente unter Nutzung hoch energetischer, polychromatischer Synchrotronstrahlung (Weißstrahl) realisiert, um die Umwandlungskinetik während eines realen Schweißprozesses und die daraus resultierenden Schweißeigenspannungen zu analysieren. Es wird gezeigt, dass mit LTT-Legierungen signifikante Druckeigenspannungen in der Schweißnaht erreicht werden. PY - 2010 SN - 0025-5300 VL - 52 IS - 4 SP - 204 EP - 210 PB - Hanser CY - München AN - OPUS4-21219 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Caron, J. A1 - Heinze, Christoph A1 - Schwenk, Christopher A1 - Rethmeier, Michael A1 - Babu, S. S. A1 - Lippold, J. T1 - Effect of continuous cooling transformation variations on numerical calculation of welding-induced residual stresses N2 - Continuous cooling transformation (CCT) behavior affects the transient state of material properties employed in a numerical welding simulation, having a direct influence on the developing stress state. Three different CCT diagrams for S355J2 steel were employed to understand the influence of variations in CCT behavior on the numerical calculation of welding-induced residual stresses. The CCT diagrams were constructed from transformation data contained in the Sysweld software database, measured dilatometric data from Gleeble experiments, and transformation data calculated from the JMatPro software. The calculated transverse and longitudinal residual stress distributions provided a qualitative correction only in comparison to experimental measurements, with the largest deviation occurring near the weld interface. Overall, the results indicate a weak dependency of the calculated residual stresses due to anticipated CCT variations. The most significant effect on the calculated residual stresses was shown to be related to the proportion of formed martensite. It is suggested that CCT data of approximate accuracy is sufficient for reliable calculation of welding-induced residual stresses. KW - Continuous cooling transformation diagrams KW - Residual stresses KW - Gas metal arc welding KW - C-Mn steels KW - Welding simulation KW - Schweißsimulation KW - Eigenspannungen KW - Martensitbildung KW - Sensitivitätsanalyse KW - Sysweld KW - Martensite kinetic KW - Sensitivity analysis PY - 2010 SN - 0043-2296 SN - 0096-7629 VL - 89 SP - 151-s - 160-s PB - American Welding Society CY - New York, NY AN - OPUS4-21444 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Brauser, Stephan A1 - Weber, Gert A1 - Rethmeier, Michael T1 - Potenzial optischer Dehnungsfeldmessung zur Charakterisierung der Eigenschaften von Widerstandspunktschweißverbindungen N2 - Die Ermittlung lokaler Werkstoffkennwerte im Schweißbereich ist für die Auslegung sicherheitsrelevanter Bauteile insbesondere durch Finite-Elemente-Berechnungen von großer Bedeutung. Konventionelle Prüfmethoden können lediglich globale Kennwerte bereitstellen, die jedoch gerade für die Berechnung widerstandspunktgeschweißter Bauteile häufig nicht ausreichen, da diese durch das Vorliegen örtlich eng begrenzter Fügezonen gekennzeichnet sind. Moderne Prüfmethoden wie die optische Dehnungsfeldmessung ermöglichen hingegen eine orts- und zeitkonkrete Bestimmung der Werkstoffkenndaten. Um das Potenzial optischer Dehnungsfeldmessungen für das Charakterisieren des lokalen Werkstoffverhaltens von Punktschweißverbindungen zu ermitteln, wurden Scherzugversuche sowie Zugversuche an widerstandspunktgeschweißten hochfesten Stählen durchgeführt. Die Ergebnisse zeigen das hohe Potenzial dieses Verfahrens sowohl für die Quantifizierung des lokalen Dehnungsverhaltens im Fügebereich als auch für die Ermittlung lokaler Werkstoffkenndaten. PY - 2010 SN - 0036-7184 VL - 62 IS - 9 SP - 496 EP - 500 PB - Verl. für Schweißen u. Verwandte Verfahren, DVS-Verl. CY - Düsseldorf AN - OPUS4-22163 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Brauser, Stephan A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Rethmeier, Michael T1 - In-situ synchrotron diffraction and digital image correlation technique for characterizations of retained austenite stability in low-alloyed transformation induced plasticity steel N2 - Direct measurement and quantification of phase transformation in a low-alloyed transformation induced plasticity steels depending on the tensile load as well as determination of the real true stress and true strain values were carried out in-situ using high energy synchrotron radiation. Digital image correlation technique was used to quantify more precisely the true strain values. The aim of the work was to obtain a better understanding of the phase transformation of commercial low-alloyed transformation induced plasticity steel depending on the true strain and true stress values. KW - Transformation induced plasticity KW - In-situ synchrotron diffraction KW - Austenite stability KW - Digital image correlation PY - 2010 DO - https://doi.org/10.1016/j.scriptamat.2010.08.007 SN - 1359-6462 SN - 1872-8456 VL - 63 IS - 12 SP - 1149 EP - 1152 PB - Elsevier CY - Oxford AN - OPUS4-22164 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Heinze, Christoph A1 - Kromm, Arne A1 - Schwenk, Christopher A1 - Kannengießer, Thomas A1 - Rethmeier, Michael T1 - Welding residual stresses depending on solid-state transformation behaviour studied by numerical and experimental methods N2 - The development of high-strength structural steels with yield strengths up to 1000 MPa results in the requirement of suitable filler materials for welding. Recently designed low transformation temperature (LTT) alloys offer appropriate strength. The martensitic phase transformation during welding induces compressive residual stress in the weld zone. Therefore, the mechanical properties of welded joints can be improved. The present paper illustrates numerical simulation of the residual stresses in LTT-welds taking into account the effect of varying Ms/Mf-temperatures, and therefore different retained austenite contents, on the residual stresses. Residual stress distributions measured by synchrotron diffraction are taken as evaluation basis. A numerical model for the simulation of transformation affected welds is established and can be used for identification of appropriate Ms-temperatures considering the content of retained austenite. KW - Welding simulation KW - Residual stress KW - Low transformation temperature filler material KW - Martensitic transformation KW - Retained austenite PY - 2011 DO - https://doi.org/10.4028/www.scientific.net/MSF.681.85 SN - 0255-5476 VL - 681 SP - 85 EP - 90 PB - Trans Tech Publications CY - Aedermannsdorf, Switzerland AN - OPUS4-23357 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rethmeier, Michael A1 - Brauser, Stephan A1 - Weber, Gert T1 - Potential of optical strain field measurement for the characterisation of the properties of resistance-spot-welded joints N2 - For the designing of safety-relevant components particularly by means of finite element calculations, great significance is attached to the determination of local material parameters in the welding region. Conventional test methods can merely provide global parameters which, however, are frequently not sufficient precisely for the calculation of resistance-spot-welded components since these are characterised by the existence of joining zones with tight local limitations. In contrast, modern test methods such as optical strain field measurement permit the determination of the characteristic material data for concrete locations and times. In order to establish the potential of optical strain field measurements for the characterisation of the local material behaviour of spotwelded joints, tensile shear tests as well as tensile tests were carried out on resistance-spot-welded high-strength steels. The results show the high potential of this procedure not only for the quantification of the local strain behaviour in the joining region but also for the determination of local characteristic material data. PY - 2011 SN - 1612-3433 VL - 10 IS - 1 SP - 48 EP - 52 PB - DVS - German Welding Society CY - Düsseldorf AN - OPUS4-23220 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gook, Sergej A1 - Gumenyuk, Andrey A1 - Lammers, Marco A1 - Rethmeier, Michael T1 - Peculiarities of the process of orbital laser-arc welding of thick-walled large-diameter pipes KW - Hybrid laser-arc welding KW - Orbital welding KW - High-pressure pipelines KW - Fibre-optic lasers PY - 2010 SN - 0957-798X VL - 9 SP - 2 EP - 8 PB - E. O. Paton Electric Welding Institute of the National Acad. of Sciences of Ukraine CY - Kyïv AN - OPUS4-22956 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weber, Gert A1 - Thommes, H. A1 - Gaul, H. A1 - Hahn, O. A1 - Rethmeier, Michael T1 - Mechanical properties of weldbonded joints of advanced high strength steels N2 - In lightweight car body shell mass production, due to requirements on vehicle weight reduction and carbon dioxide emissions, joining of advanced high strength steels (AHSS) with different joining procedures and especially hybrid bonding techniques is becoming more and more important. One of these hybrid bonding techniques is the combination of resistance spot welding and adhesive bonding called weldbonding. One of the important advantages of weldbonded joints in comparison to resistance spot welded joints are the enhanced mechanical properties. To guarantee sufficiently high quality conditions regarding the strength of the weldbonded joints, the influences of the applied adhesive systems and of different base metal combinations are studied. This is carried out for both non-corrosive and corrosive environments and for the choice of different joining parameters settings. In particular, the mechanical behaviour of the weldbonded joints is investigated under quasi-static, impact and fatigue loads. Furthermore, the energy absorption of the weldbonded joints for both non-corrosive and corrosive environments is studied. It is shown that the weldbonded joints possess higher mechanical strengths in all load cases (quasi-static, impact and fatigue). Corrosive attack affects weldbonded joints, and the quasi-static strength is reduced. Resistance spot welded joints are not affected by the corrosive attack, but even after several weeks of corrosive attack, the quasi-static strength of weldbonded joints remains higher than that of resistance spot welded joints. KW - Weldbonded joints KW - Corrosion KW - Mechanical strength KW - Fracture behaviour KW - Fatigue KW - Crash behaviour PY - 2011 DO - https://doi.org/10.1163/016942411X580090 SN - 0169-4243 SN - 1568-5616 VL - 25 IS - 18 SP - 2369 EP - 2389 PB - VNU Science Press CY - Utrecht AN - OPUS4-24513 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schwenk, Christopher A1 - Tikhomirov, D. A1 - Eßer, G. A1 - Rethmeier, Michael T1 - General standard for welding simulation N2 - Für die Abgrenzung der Anwendbarkeit verschiedener Methoden der numerischen Schweißsimulation sowie für die Vereinheitlichung der Voraussetzungen und der durchzuführenden Schritte bei der Simulation sind normative Regelwerke für den Anwender erforderlich. Da es derzeit noch keine normähnlichen Dokumente auf diesem Gebiet gibt, wurde vom Deutschen Institut für Normung e.V. DIN in Zusammenarbeit mit der Forschungsvereinigung des DVS Deutscher Verband für Schweißen und verwandte Verfahren e.V. ein Arbeitsausschuss gegründet, welcher sich mit der Erarbeitung der entsprechenden Dokumente befasst. Der vorliegende Beitrag konzentriert sich auf die Vorstellung der neuen DIN Spec 32534-1, welche die grundlegenden Simulations-Schritte erläutert und ihre Anwendungsfelder sowie die Schlüsselbegriffe spezifiziert. Des Weiteren wurde eine allgemein gültige Simulationsstruktur erarbeitet, welche als Empfehlung für den Auftraggeber und den Auftragnehmer bei der Formulierung und Abwicklung eines Dienstleistungsauftrages sowie für den Neueinstieg in die Schweißsimulation dienen soll. Schließlich wird ein Ausblick auf die weiteren Themenfelder des Arbeitsausschusses sowie auf die internationalen Aktivitäten auf diesem Gebiet gegeben. N2 - For differentiating the applicability of various numerical welding simulation methods as well as unifying the prerequisites and the steps to be taken in simulation, normative codes are required for the user. Since any standard-like documents are currently still lacking in this field, the DIN German Institute for Standardization in partnership with the Research Association of DVS German Welding Society have set up a standards committee dealing with the preparation of respective documents. This article focuses on the presentation of the new DIN Spec 32534-1 explaining the major simulation steps and specifying the application fields and the key terms of welding simulation. In addition, a generally valid simulation structure has been established which is intended to serve as a recommendation for customers and suppliers in formulating and handling a service order as well as for persons who start doing welding simulation for the first time. It additionally gives an overview of the other subject areas dealt with in the standards committee as well as of the international activities in this field. PY - 2011 UR - 10.3139/120.110257 SN - 0025-5300 VL - 53 IS - 9 SP - 522 EP - 527 PB - Hanser CY - München AN - OPUS4-24355 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -