TY - JOUR A1 - Gook, S. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael A1 - El-Batahgy, A.M. T1 - Laser and hybrid laser-arc welding of cryogenic 9 % NI Steel N2 - Heat treated 9%Ni steel is considered the most suitable and economic material for construction of large-size liquefied natural gas (LNG) storage tanks which operate at cryogenic temperatures (-196°C). Strength above 700 MPa as well as a minimum impact value of 60 J are required to ensure reliable operation of the LNG tanks at operating temperature. Conventional arc welding processes, including shielded metal arc welding, gas metal arc welding, gas tungsten arc welding and submerged arc welding, are currently used in construction of LNG tanks. Ni based filler wire is the preferred filler metal of choice in LNG tank construction. The main problem with this choice is the lower mechanical properties, particularly tensile strength of the weld metal. To compensate, the wall thickness needs to be excessively thick to ensure the strength of the welded structures. Ni based filler material is expensive and a large quantity is needed to fill the multi-pass weld grooves. These factors significantly add to the cost in the fabrication of LNG storage tanks. For these reasons, exploration of new welding technologies is a priority. A big potential can be seen in laser based welding techniques. Laser beam welding results in much smaller fusion zone with chemical composition and mechanical properties similar to that of the base material. Laser welding is a much faster process and allows for a joint geometry which requires less filler material and fewer welding passes. The advantages of laser welding can help to overcome the problems pointed out above. Trials of autogenous laser welding, laser cold-wire welding and hybrid laser-arc welding conducted on the 9%Ni steel are presented in this paper. Chemical composition of the weld metal as well as effects of welding parameters on the weld formation, microstructure and tensile strength is discussed. Filler wire penetration depth as well as character of its distribution in the narrow laser welds was examined using EPMA - electron probe microanalysis. KW - hardness KW - cryogenic steel KW - laser welding KW - microstructure KW - tensile strength PY - 2016 UR - http://gns.mephi.ru/sites/default/files/journal/file/en.2016.1-4.pdf SN - 2499-9733 VL - 1 IS - 18 SP - 34 EP - 45 PB - Research Nuclear University MEPHl CY - Moskau, Russia AN - OPUS4-36553 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Frei, J. A1 - Suwala, H. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Bestimmung der Rissanfälligkeit von hochfesten Stählen beim Widerstandspunktschweißen N2 - Die stetig zunehmenden Anforderungen an Kraftstoffverbrauch, Schadstoffemission, sowie passive Sicherheit haben die Automobilindustrie vor Herausforderungen gestellt, die nur durch einen konsequenten Einsatz moderner hochfester Stahlwerkstoffe zu bewältigen sind. Obgleich eine generelle Eignung dieser Stähle für das Widerstandspunktschweißen (WPS) gegeben ist, kann es durch verschiedene externe Einflüsse im betrieblichen Umfeld zur Rissbildung in der Schweißverbindung kommen. Der Einfluss dieser Risse auf die mechanischen Eigenschaften ist derzeit nicht hinreichend genau erfasst, so dass häufig die Vorgabe einer rissfreien Schweißverbindung besteht. Die Kenntnis der Rissanfälligkeit der verarbeiteten Materialkombinationen sowie von ungünstigen Schweißparametern ist daher für viele Unternehmen von erheblicher wirtschaftlicher Bedeutung. Im Rahmen des FOSTA Projekts P921 „Entwicklung eines Verfahrens zur Bestimmung der Rissanfälligkeit von hochfesten Stählen beim Widerstandspunktschweißen“ wurde ein Ansatz zur Bestimmung der Rissanfälligkeit von WPS-Verbindungen hochfester Stähle entwickelt. Mittels einer hydraulischen Vorrichtung unter Zugbelastung wurden geschweißte, rissbehaftete Proben optisch ausgewertet. Das Verfahren ist geeignet, um ein Werkstoffranking bezüglich der Rissanfälligkeit beim Widerstandspunktschweißen für Werkstoffe aufzustellen. KW - Widerstandspunktschweißen KW - Werkstoffranking KW - Rissanfälligkeit KW - hochfeste Stähle KW - Liquid Metal Embrittlement KW - Lötrissigkeit PY - 2016 U6 - https://doi.org/10.3139/120.110904 VL - 58 IS - 7-8 SP - 612 EP - 616 PB - Carl Hanser Verlag CY - München AN - OPUS4-37161 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Neubert, Sebastian A1 - Pittner, Andreas A1 - Rethmeier, Michael T1 - Experimental determination of TRIP parameter K for mild- and high strength low alloy steels and a super martensitic filler material N2 - A combined experimental numerical approach is applied to determine the transformation induced plasticity (TRIP)-parameter K for different strength low-alloy steels of grade S355J2+N and S960QL as well as the super martensitic filler CN13-4-IG containing 13 wt% chromium and 4 wt% nickel. The thermo-physical analyses were conducted using a Gleeble® 3500 facility. The thermal histories of the specimens to be tested were extracted from corresponding simulations of a real gas metal arc weldment. In contrast to common TRIP-experiments which are based on complex specimens a simple flat specimen was utilized together with an engineering evaluation method. The evaluation method was validated with literature values for the TRIP-parameter. It could be shown that the proposed approach enables a correct description of the TRIP behavior. KW - Transformation induced plasticity (TRIP) KW - Phase transformation KW - High-strength low-alloy steel KW - Super martensitic filler material KW - Thermo physical simulation KW - Gleeble experiments PY - 2016 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-367297 VL - 5 IS - 575 SP - Paper 754, 1 EP - 16 PB - SpringerPlus AN - OPUS4-36729 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Numerical simulation of solidification crack formation during laser beam welding of austenitic stainless steels under external load N2 - Solidification cracking phenomena taking place under controlled tensile weldability (CTW) test conditions have already been investigated both experimentally and numerically via FEA in order to get a better understanding of the mechanisms of hot crack formation during laser beam welding of austenitic steel grades. This paper develops a threedimensional finite element model employing the contact element technique to simulate the formation and propagation of solidification cracks during laser full penetration welding of fully austenitic stainless steel 1.4376. During the experimental procedure, the resulting strain and displacement directed to the laser beam in the close vicinity of the weld pool was measured at the surface of the workpiece using a digital image correlation (DIC) technique with an external diode laser as an illuminating source. Local strain fields, global loads and crack lengths predicted by the model are in good agreement with those observed in experiments. KW - Solidification cracking KW - Finite element analysis KW - Imaging KW - Laser welding KW - Austenitic stainless steels PY - 2016 U6 - https://doi.org/10.1007/s40194-016-0357-1 SN - 0043-2288 SN - 1878-6669 VL - 60 IS - 5 SP - 1001 EP - 1008 PB - Springer CY - Berlin, Heidelberg AN - OPUS4-37287 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Frei, J. A1 - Rethmeier, Michael A1 - Alexandrov, B. T. T1 - Low heat input gas metal arc welding for dissimilar metal weld overlays part I: the heat-affected zone N2 - Dissimilar metal weld overlays of nickel base alloys on low alloy steel components are commonly used in the oil and gas, petro-chemical, and power generation industries to provide corrosion and oxidation resistance in a wide range of service environments and temperatures. Traditionally, weld overlays are produced using cold or hot wire gas tungsten arc welding (GTAW). Potential advantages of cold metal Transfer (CMT) welding, a low heat input gas metal arc welding process, over the conventional GTAW in production of weld overlays were evaluated. Metallurgical characterization was performed on CMT overlays of Alloy 625 filler metal on Grade 11 and Grade 22 steels. Significant grain refinement was found in the high temperature HAZ compared to the traditional coarse-grained HAZ in arc welding. Evidences of incomplete carbide dissolution, limited carbon diffusion, and incomplete transformation to austenite were also found. These phenomena were related to high heating and cooling rates and short dwell times of the high-temperature HAZ in austenitic state. Tempering effects in the steel HAZ were identified, showing a potential for development of CMT temperbead procedures. Based on the results of this study, the steel HAZ regions in CMT overlays were classified as high-temperature HAZ and intercritical HAZ. KW - Clad steels KW - Nickel alloys KW - Low alloy steels KW - GMA surfacing KW - DIP transfer KW - Coarse-grained heat-affected zone KW - Microstructure PY - 2016 U6 - https://doi.org/10.1007/s40194-016-0306-z SN - 0043-2288 SN - 1878-6669 VL - 60 IS - 3 SP - 459 EP - 473 PB - Springer CY - Heidelberg, Germany AN - OPUS4-36377 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fritzsche, André A1 - Avilov, Vjaceslav A1 - Gumenyuk, Andrey A1 - Hilgenberg, Kai A1 - Rethmeier, Michael T1 - High power laser beam welding of thick-walled ferromagnetic steels with electromagnetic weld pool support N2 - The paper describes an experimental investigation of high power laser beam welding with an electromagnetic weld pool support for up to 20 mm thick plates made of duplex steel (AISI 2205) and mild steel (S235JR). The results of the welding tests show a successful application of this technology at ferromagnetic metals. Irregular sagging was suppressed successfully. An ac-power of less than 2 kW at oscillation frequencies between 800 Hz and 1.7 kHz is necessary for a full compasation of the hydrostatic pressure. Thus, it was demonstrated that the electromagnetic weld pool support is not only limited to non-ferromagnetic metals like austenitic steels. For future studies with duplex steel, the use of filler material has to take into account with regard to the balance of the mixed austenitic and ferritic phases. KW - Laser beam welding KW - Thick-walled steel KW - Ferromagnetic steel KW - Weld pool support PY - 2016 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-377593 SN - 1875-3892 VL - 83 SP - 362 EP - 372 PB - Elsevier CY - Amsterdam [u.a.] AN - OPUS4-37759 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Petrat, T. A1 - Graf, B. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael ED - Schmidt, M. ED - Vollertsen, F. ED - Arnold, C. B. T1 - Laser metal deposition as repair technology for a gas turbine burner made of Inconel 718 N2 - Maintenance, repair and overhaul of components are of increasing interest for parts of high complexity and expensive manufacturing costs. In this paper a production process for laser metal deposition is presented, and used to repair a gas turbine burner of Inconel 718. Different parameters for defined track geometries were determined to attain a near net shape deposition with consistent build-up rate for changing wall thicknesses over the manufacturing process. Spot diameter, powder feed rate, welding velocity and laser power were changed as main parameters for a different track size. An optimal overlap rate for a constant layer height was used to calculate the best track size for a fitting layer width similar to the part dimension. Deviations in width and height over the whole build-up process were detected and customized build-up strategies for the 3D sequences were designed. The results show the possibility of a near net shape repair by using different track geometries with laser metal deposition. T2 - LANE - 9 International Conference on Photonic Technologies CY - Fürth, Germany DA - 19.09.2016 KW - Laser metal deposition KW - Inconel 718 KW - Additive manufacturing KW - Maintenance KW - Repair and overhaul PY - 2016 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-376723 UR - http://ac.els-cdn.com/S1875389216301857/1-s2.0-S1875389216301857-main.pdf?_tid=ed1d75de-84a2-11e6-af94-00000aab0f6c&acdnat=1474974777_4917d753cb3d316c4b000ba0760778b5 SN - 1875-3892 VL - 83 SP - 761 EP - 768 PB - Elservier AN - OPUS4-37672 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bachmann, Marcel A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Welding with high-power lasers: trends and developments N2 - High-power laser beam welding became new stimuli within the last 10 years due to the availability of a new generation of high brightness multi kilowatt solid state lasers. In the welding research new approaches have been developed to establish reliable and praxis oriented welding processes meeting the demands of modern industrial applications during this time. The paper focuses on some of the current scientific and technological aspects in this research field like hybrid laser arc welding, simulation techniques, utilization of electromagnetic fields or reduced pressure environment for laser beam welding processes, which contributed to the further development of this technology or will play a crucial role in its further industrial implementation. T2 - 9th International Conference on Photonic Technologies - LANE 2016 CY - Fürth, Germany DA - 19.09.2016 KW - High-power Laserbeam Welding KW - Electromagnetic Force KW - Vacuum KW - Simulation PY - 2016 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-377280 VL - 83 SP - 15 EP - 25 PB - Elsevier B.V. CY - Berlin, Germany AN - OPUS4-37728 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Frei, Julian A1 - Rethmeier, Michael T1 - Influence of manufacturing conditions on the cracking susceptibility of AHSS during resistance spot welding N2 - The complex microstructure and the advanced mechanical properties of AHSS steel types lead to an increased susceptibility to weld cracking, especially during resistance spot welding under ‘rough’ manufacturing conditions. Various activities have been conducted in recent years at the Federal Institute for Materials Research and Testing (BAM) and the Fraunhofer IPK on this matter. Understandings about the safe spot weldability and the process of crack-forming itself were gained, and solutions for handling this issue given. The performed work includes investigations on the influence of initial gaps as well as restraint intensity. An experimental method for the determination of the general cracking susceptibility, i.e. a material ranking of AHSS in respective to current restraints was developed. Coupled mechanical and thermal simulations of the welding process show the present internal stress-strain-conditions and values responsible for the formation of cracks, deepening the understanding of the process. By using this easy to perform and material-independent method for the determination of the cracking susceptibility in resistance spot welded joints, small and medium sized companies can profit by rapidly evaluating the joinability of their handled material combinations as well as OEMs. T2 - Sheet Metal Welding Conference XVII CY - Livonia, Michigan, USA DA - 18.10.2016 KW - Welding under external loading KW - Cracking susceptibility of AHSS KW - Resistance spot welding KW - Initial gap PY - 2016 SP - Session 1-2, 1 EP - Session 1-2, 15 AN - OPUS4-38137 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Quiroz, V. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Saldabilita di lamiere in acciaio inossidabile austenico ed austeno-ferritico ad alto contenuto di manganese con processo laser N2 - Manganese alloyed stainless steels represent a cost-effective alternative to conventional CrNi- stainless steels due to strong fl uctuations of the market prices for nickel seen during the last years. In CrMnNi steels, nickel is partially replaced by lower-cost manganese and small amounts of nitrogen for stabilization of the austenitic phase. This also brings benefi ts regarding the mechanical properties, as it results in an increased material strength. Laser beam welding of such materials was investigated for direct comparison with Standard CrNi steels. Main emphasis was laid on fi nding adequate process parameters to achieve a stable welding process and obtain a good weld quality. Two different laser sources, a 4.4 kW Nd:YAG and a 5 kW CO2 laser, were used to weld 1.5 mm stainless steel sheets in continuous wave mode. A high-Mn austenitic (1.4376) and a lean duplex (1.4162) steel, as well as the standard austenitic (1.4301) and duplex (1.4362) grades were selected as test materials. Both butt and lap joint confi gurations were studied. Experiments were carried out systematically, varying the welding speed, laser power and focal point position in order to determine adequate process windows. The infl uence of the shielding gas type and fl ow rate on the process stability and the weld quality were investigated. The effects of weld edge preparation on the weld appearance and quality levels attained were also examined. The obtained welded joints were subjected to radiographic tests for detection of internal imperfections. Also a metallurgical characterization of the samples regarding the resulting phase composition or balance and hardness depending on the welding process parameters was conducted. Furthermore, tensile and potentiodynamic tests were performed to evaluate the mechanical and corrosion properties, respectively. The results provide an insight into the advantages and limitations of the laser beam welding process for joining high-manganese alloyed stainless steels. Conditions for the production of defect-free and corrosion-resistant welds having good mechanical properties could be determined. KW - Weldability KW - Austenitic stainless steels KW - Corrosion KW - CO2 lasers KW - Duplex stainless steels KW - Laser welding KW - Manganese KW - Mechanical properties KW - Shielding gases KW - YAG lasers PY - 2016 SN - 0035-6794 VL - 68 IS - 1 SP - 33 EP - 43 AN - OPUS4-38100 LA - ita AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -