TY - JOUR A1 - Schempp, P. A1 - Rethmeier, Michael T1 - Understanding grain refinement in aluminium welding N2 - Grain refinement is an important opportunity to improve mechanical properties of fusion welds and the weldability (susceptibility to solidification cracking) of the base metal. In this study, grain refinement was achieved in aluminium welds through additions of grain refiner to the weld metal. Increasing grain refiner additions led to a decrease of the weld metal mean grain size (down to −86 %). The grain refinement efficiency was the highest in commercial pure Al (Alloy 1050A, Al 99.5), followed by Alloy 6082 (Al Si1MgMn) and Alloy 5083 (Al Mg4.5Mn0.7). To investigate this clear influence of alloy content on grain size, the undercooling parameters P and Q were calculated. Temperature measurements revealed that solidification parameters such as solidification growth rate or cooling rate vary significantly along the solidification front, dependent upon torch speed and alloy. On the basis of this comparison, an analytical approach was used to model the columnar to equiaxed transition (CET). Moreover, wavelength dispersive X-ray spectroscopy (WDS) and transmission electron microscopy (TEM) analyses revealed particles rich in Ti and B that are probably TiB2 particles coated by Al3Ti nucleating Al grains during solidification. Also, Ti/B contents needed in commercial filler wires to allow optimum weld metal grain refinement were calculated dependent upon base alloy and welding process. PY - 2015 DO - https://doi.org/10.1007/s40194-015-0251-2 SN - 0043-2288 SN - 1878-6669 VL - 59 IS - 6 SP - 767 EP - 784 PB - Springer CY - Oxford AN - OPUS4-34840 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schneider, André A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Mobile vacuum in pocket format, mobile local low-pressure cap for high power laser beam welding of thick materials N2 - The presented apparatus enables laser beam welding of thick materials under local reduced pressure conditions, thus improving the quality of welds and reducing the laser beam power necessary for complete penetration welding. The vacuum cap presented in this article uses a local reduced ambient pressure environment in a tight zone around the welding area and, in contrast to a conventional vacuum chamber, it is movable in the welding direction. The mobile installation is very compact and reaches pressure values of around 200 mbar. The reduced pressure in the vacuum cap is sufficient to generate 50 % higher penetration depth in comparison to welding under ambient pressure conditions. The low pressure around the keyhole reduces the vapour-plasma plume and therefore prevents a defocusing and scattering of the laser radiation. This allows to raise the amount of laser beam power entering the keyhole as well as the effective power density. KW - High power laser beam welding KW - Mobile vacuum KW - Local reduced pressure KW - Vapor plume KW - Keyhole PY - 2015 DO - https://doi.org/10.1002/latj.201500025 SN - 1613-7728 SN - 1863-9119 VL - 12 IS - 4 SP - 43 EP - 44 PB - Wiley-VCH CY - Weinheim AN - OPUS4-34583 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bachmann, Marcel A1 - Kunze, R. A1 - Avilov, Vjaceslav A1 - Rethmeier, Michael T1 - Finite element modeling of an alternating current electromagnetic weld pool support in full penetration laser beam welding of thick duplex stainless steel plates N2 - An electromagnetic weld pool support system for 20 mm thick duplex stainless steel AISI 2205 was investigated numerically and compared to experiments. In our former publications, it was shown how an alternating current (AC) magnetic field below the process zone directed perpendicular to the welding direction can induce vertically directed Lorentz forces. These can counteract the gravitational forces and allow for a suppression of material drop-out for austenitic stainless steels and aluminum alloys. In this investigation, we additionally adopted a steady-state complex magnetic permeability model for the consideration of the magnetic hysteresis behavior due to the ferritic characteristics of the material. The model was calibrated against the Jiles–Atherton model. The material model was also successfully tested against an experimental configuration before welding with a 30 mm diameter cylinder of austenitic stainless steel sur-rounded by duplex stainless steel. Thereby, the effects of the Curie temperature on the magnetic characteristics in the vicinity of the later welding zone were simulated. The welding process was modeled with a three-dimensional turbulent steady-state model including heat transfer and fluid dy-namics as well as the electromagnetic field equations. Main physical effects, the thermo-capillary (Marangoni) convection at the weld pool boundaries, the natural convection due to gravity as well as latent heat of solid–liquid phase transitions at the phase boundaries were accounted for in the model. The feedback of the electromagnetic forces on the weld pool was described in terms of the electromagnetic-induced pressure. The finite element software COMSOL Multiphysics 4.2 was used in this investigation. It is shown that the gravity drop-out associated with the welding of 20 mm thick duplex stainless steel plates due to the hydrostatic pressure can be prevented by the application of AC magnetic fields between around 70 and 90 mT. The corresponding oscillation frequencies were between 1 and 10 kHz and the electromagnetic AC powers were between 1 and 2.3 kW. In the experiments, values of the electromagnetic AC power between 1.6 and 2.4 kW at os-cillation frequencies between 1.2 and 2.5 kHz were found to be optimal to avoid melt sagging or drop-out of melt in single pass full-penetration laser beam welding of 15 and 20 mm thick AISI 2205. KW - Laser KW - Numerical simulation KW - Laser beam welding KW - Electromagnetic weld pool support KW - Duplex stainless steel PY - 2016 DO - https://doi.org/10.2351/1.4943906 VL - 28 IS - 2 SP - 022404-1 EP - 022404-9 PB - AIP Publishing AN - OPUS4-35676 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gebhardt, M.O. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Solidification cracking in laser GMA hybrid welding of thick-walled parts N2 - Laser GMA hybrid welds, producing partial penetration, were conducted on stiff tubes made of S460NH. Experiments, using a design-of-experiments plan were conducted to examine the influence of the welding parameters on the occurrence of solidification cracks. Results say that cracks diminish, when high levels of arc power are applied, while their number increases with rising laser beam power. The weld velocity had no measurable impact. KW - Laser hybrid welding KW - Solidification cracking KW - Partial penetration welding KW - Tube welding KW - Thick walled parts KW - Design of experiments PY - 2014 DO - https://doi.org/10.1179/1362171813Y.0000000171 SN - 1362-1718 SN - 1743-2936 VL - 19 IS - 3 SP - 209 EP - 213 PB - Maney CY - London AN - OPUS4-30297 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bachmann, Marcel A1 - Avilov, Vjaceslav A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Magnets improve quality of high-power laser beam welding N2 - Welding is one of the most critical operations for the construction of reliable metal structures in everything from ships to reactor vessels. When welds fail, often the entire structure fails, and expectations on weld quality have never been higher. Any process that uses a localized heat source, such as welding, is likely to result in some distortion. The welding process of very thick metal components is not inherently stable and is barely controllable without external forces. KW - Electromagnetic weld pool control KW - Laser beam weliding KW - Marangoni effect PY - 2014 VL - 2013-2014 SP - 30 EP - 32 AN - OPUS4-30338 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Heinze, Christoph A1 - Michael, Thomas A1 - Pittner, Andreas A1 - Rethmeier, Michael T1 - Microcrack formation during gas metal arc welding of high-strength fine-grained structural steel N2 - The recent development of high-performance-modified spray arc processes in gas metal arc welding due to modern digital control technology and inverter power sources enables a focused spray arc, which results in higher penetration depths and welding speed. However, microcracks occurred in the weld metal while approaching the process limits of the modified spray arc, represented by a 20-mm double layer DV-groove butt-weld. These cracks were detected in structural steel exhibiting a yield strength level of up to 960 MPa and are neither dependent on the used weld power source nor a consequence of the modified spray arc process itself. The metallographic and fractographic investigations of the rather exceptional fracture surface lead to the classification of the microcracks as hot cracks. The effects of certain welding parameters on the crack probability are clarified using a statistical design of experiment. However, these microcracks do not impact the design specification for toughness in the Charpy V-notch test (absorbed energy at -40 °C for the present material is 30 J). KW - High-strength low-alloy steel KW - Welding KW - Fracture KW - Design of experiments KW - Microcracking PY - 2014 DO - https://doi.org/10.1007/s40195-013-0011-5 SN - 1006-7191 SN - 1000-9442 VL - 27 IS - 1 SP - 140 EP - 148 PB - Springer CY - Shenyang AN - OPUS4-30123 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Neubert, Sebastian A1 - Pittner, Andreas A1 - Rethmeier, Michael T1 - Numerical sensitivity analysis of TRIP-parameter K on weld residual stresses for steel S355J2+ N N2 - A combined experimental numerical approach is applied for sensitivity analysis of the transformation induced plasticity (TRIP)-parameter K on weld residual stresses for welding of structural steel of grade S355J2+N. K was determined experimentally using the Gleeble 3500 facility. A thermomechanical FE model of the real welding process was experimentally validated against temperature field and X-ray stress measurements. Within sensitivity analyses K was varied by several orders of magnitude and the influence on the calculated residual stresses is evaluated by performing corresponding FEA. The correct order of magnitude is sufficient to reproduce the residual stresses qualitatively and quantitatively. KW - TRIP - transformation induced plasticity KW - welding residual stresses KW - sensitivity analysis KW - FEA PY - 2016 DO - https://doi.org/10.1080/01495739.2015.1124641 SN - 0149-5739 VL - 2016 IS - 39/2 SP - 201 EP - 219 PB - Journal of Thermal Stresses AN - OPUS4-35880 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bachmann, Marcel A1 - Rethmeier, Michael A1 - Wu, Chuan Song T1 - Sensitivity analysis of the residual stress state in friction stir welding of high strength aluminium alloy N2 - In this paper, the friction stir welding process was numerically investigated for 6 mm thick aluminum alloy AA2024-T3. The finite element software COMSOL Multiphysics was used to calculate the transient thermal field during welding and the mechanical reaction depending on different mechanical clamping conditions and hardening models subsequently. A thermal pseudo-mechanical (TPM) heat source was implemented. Softening effects of the material due to precipitation hardening dissolution caused by the frictional heat were accounted for. The transient temperature evolution measured by thermocouple elements at various locations was compared to the numerical results. A good agreement was found for the thermal field. A sensitivity study of the mechanical models showed the strong influence of the clamping conditions and the softening model. PY - 2016 DO - https://doi.org/10.3139/120.110809 SN - 0025-5300 VL - 58 IS - 1 SP - 20 EP - 26 PB - Hanser CY - München AN - OPUS4-35269 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sproesser, Gunther A1 - Chang, Ya-Ju A1 - Pittner, Andreas A1 - Rethmeier, Michael A1 - Finkbeiner, Matthias T1 - Laser-MSG-Hybridschweißen und die Ökobilanz: Sieg nach Punkten N2 - Es ist ein Naturgesetz: Mit der verarbeiteten Blechdicke steigt der Zeit-, Material- und Energiebedarf beim Fügen überproportional. Aber ist das noch umweltverträglich ? Dieser Frage stellte sich Gunther Sproesser mit seinen Kollegen an der Technischen Universität Berlin. KW - MSG-Schweißen KW - Hochleistungsschweißen KW - Ökobilanz KW - Laser-MSG-Hybridschweißen PY - 2015 UR - http://www.laser-community.com/de/schweiss-verfahren-im-oeko-check/ N1 - In Deutsch und Englisch erschienen. Titel in English: "A win on points: LAHW/GMAW welding tops life-cycle analysis study" IS - 21/November 2015 SP - 6 EP - 6 AN - OPUS4-35438 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - El-Batahgy, A. A1 - Saiyah, A. A1 - Khafagi, S. A1 - Gumenyuk, Andrey A1 - Gook, S. A1 - Rethmeier, Michael T1 - Shielded metal arc welding of 9%Ni steel using matching ferritic filler metal N2 - Motivated by the tensile strength loss of 9%Ni steel arc welded joints made using Ni-based austenitic filler metals, the feasibility of maintaining the tensile strength using matching ferritic filler metal has been demonstrated. In comparison with shielded metal arc welded joint made using Ni-based austenitic electrode ENiCrMo-6, higher tensile strength comparable to that of the base metal was obtained using matching ferritic electrode. Besides, sufficient impact toughness energies with much lower mismatch were obtained for weld metal and heat-affected zone. Welded joint with a lower mechanical mismatching is of considerable importance for achieving acceptable combination of tensile strength and impact toughness.Abetter combination of These mechanical properties is ensured by applying a post weld heat treatment. KW - Mechanical mismatching KW - Mechanical properties KW - Microstructure KW - Austenitic welding electrode KW - Matching ferritic welding electrode PY - 2020 DO - https://doi.org/10.1080/13621718.2020.1846936 SN - 1362-1718 SP - 1 EP - 7 PB - Taylor & Francis AN - OPUS4-51835 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Üstündag, Ömer A1 - Bakir, Nasim A1 - Gook, S. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Neueste Entwicklungen im Bereich des Hochleistungslaserstrahl- und Hybridschweißens von hohen Blechdicken N2 - Bislang kommt das Laserstrahlschweißen bzw. Laserhybridschweißen hauptsächlich bei Dickblechen mit einer Wandstärke von bis zu 15 mm zum Einsatz. Für Anwendungen über 20 mm war dieses Verfahren aufgrund einiger Herausforderungen bisher nur bedingt realisierbar. Eine von der Bundesanstalt für Materialforschung und -prüfung (BAM) entwickelte elektromagnetische Schmelzbadunterstützung ermöglicht nun ein einlagiges Schweißen von bis zu 30 mm Wandstärke. KW - Laserstrahlschweißen KW - Laserhybridschweißen KW - Modellierung KW - Elektromagnetische Schmelzbadunterstützung KW - Kaltzähe Stähle PY - 2020 VL - 2 SP - 26 EP - 30 PB - DVV Media Group GmbH CY - Hamburg AN - OPUS4-51632 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gook, S. A1 - El-Sari, B. A1 - Biegler, M. A1 - Rethmeier, Michael A1 - Lichtenthäler, F. A1 - Stark, M. T1 - Multiple-wire submerged arc welding of high-strength fine-grained steels N2 - Ensuring the required mechanical-technological properties of welds is a critical issue in the application of multi-wire submerged arc welding processes for welding high-strength fine-grained steels. Excessive heat input is one of the main causes for microstructural zones with deteriorated mechanical properties of the welded joint, such as a reduced notched impact strength and a lower structural robustness. A process variant is proposed which reduces the weld volume as well as the heat input by adjusting the welding wire configuration as well as the energetic parameters of the arcs, while retaining the advantages of multiwire submerged arc welding such as high process stability and production speed. KW - Submerged arc welding KW - High-strength fine-grained steels KW - Mechanical properties of the joints KW - Energy parameters of the arc PY - 2022 DO - https://doi.org/10.37434/tpwj2022.01.02 SN - 0957-798X IS - 1 SP - 9 EP - 13 PB - Paton Publishing House CY - Kiev AN - OPUS4-54701 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kampffmeyer, D. A1 - Wolters, M. A1 - Raute, J. A1 - Biegler, M. A1 - Rethmeier, Michael T1 - Laserstrahlauftragschweißen – Einfluss von Schutzgasgemischen auf die Bauteilqualität N2 - Im Additive Manufacturing Verfahren Directed Energy Deposition (DED) wird bei der Verarbeitung von Werkzeugstahl in der Regel reines Argon als Schutzgas verwendet. Dabei kann die Verwendung von speziellen Schutzgasgemischen, auch bei geringen Anteilen zugemischter Gase, durchaus die Bauteilqualität positiv beeinflussen. In Vorarbeiten der Messer SE & Co. KGaA zeigte ein gewisser Sauerstoffanteil im Schutzgas die Tendenz, den Flankenwinkel von Schweißspuren beim DED zu verbessern. In der vorliegenden Studie wurde daher detailliert untersucht in wie weit unterschiedliche Schutzgasgemische einen Einfluss auf die Qualität sowie die geometrischen Eigenschaften der additiv gefertigten Strukturen des Werkzeugstahls 1.2709 beim Laser-DED ausüben. Es erfolgten zunächst Testschweißungen in Form von Einzelspuren mit unterschiedlichen Gemischen aus dem Basisschutzgas Argon mit geringen Anteilen verschiedener Gase. Dabei wurde der Einfluss der Zusätze auf die Spurgeometrie und Aufbauqualität untersucht. Auf Basis dieser Vorversuche wurde eine Auswahl vielversprechender Gasgemische getroffen und Detailuntersuchungen in Form von Spuren, Flächen und Quadern unter Zugabe verschiedener Mengen an Zusätzen durchgeführt. Zur Bewertung des Einflusses der Schutzgasbeimengungen wurden der Flankenwinkel, die Porosität und das Gefüge der Proben anhand metallografischer Schliffe untersucht. Es zeigte sich, dass eine Zugabe von geringen Anteilen an Zusätzen zunächst zu einer Vergrößerung des Flankenwinkels im Vergleich zu reinem Argon führt. Mit steigendem Anteil der Gase nimmt dieser Winkel jedoch ab. So kann je nach Menge des zugesetzten Gases eine individuelle Benetzung des aufgetragenen Materials an der Oberfläche erreicht werden. Auch die Porosität ließ sich durch Schutzgasgemische beeinflussen und zeigt ein abweichendes Verhalten im Vergleich zu reinem Argon. T2 - DVS Congress 2023 Große Schweißtechnische Tagung DVS CAMPUS CY - Essen, Germany DA - 11.09.2023 KW - Laser-Pulver-Auftragschweißen KW - DED-LB KW - Schutzgas KW - Additive Fertigung PY - 2023 SN - 978-3-96144-230-0 SP - 505 EP - 511 PB - DVS-Media AN - OPUS4-58585 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yang, Chunliang A1 - Yan, Fan A1 - Meng, Xiangmeng A1 - Putra, Stephen Nugraha A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Phase-field simulation of the dendrite growth in aluminum alloy AA5754 during alternating current electromagnetic stirring laser beam welding N2 - Electromagnetic stirring is known to promote material flow, reduce porosity, uniform elements distribution, and refine grain in laser beam welding (LBW), which enhances the applicability of LBW in various industries. In this study, a phase-field model of dendrite growth in AA5754 Al alloy electromagnetic stirring laser beam welding was established. The model considered the thermal electromagnetic Lorentz force resulting from the interaction between the electric field generated by the Seebeck effect and the magnetic field, as well as the temperature gradient and solidification rate of the solidification interface obtained from the computational fluid dynamics electromagnetic stirring LBW model. The variation rules of dendrite growth with different magnetic parameters and effects are analyzed. Comprehensively, the magnetic field promotes the solidification rate, thus promoting interfacial instability and a large magnetic flux density leads to a faster interface instability. The solidification rate as well as the temperature gradient affect the growth rate, and the accelerated growth caused by the so lidification rate with a high frequency and a large magnetic flux density effectively inhibits the slow growth caused by the temperature gradient. The thermal electromagnetic Lorentz force is the main factor for the branch increment at low frequencies, while both thermal electromagnetic Lorentz force and temperature gradient in crease the number of branches at high frequencies. The calculated average branch numbers considering various factors in the stable stage under different magnetic parameters were consistent with the results of the scanning electron microscope tests. KW - Laser beam welding KW - Electromagnetic KW - Aluminum alloys KW - Phase field method KW - Dendrite growth PY - 2024 DO - https://doi.org/10.1016/j.ijheatmasstransfer.2023.124754 SN - 0017-9310 VL - 218 SP - 1 EP - 16 PB - Elsevier Ltd. AN - OPUS4-58489 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Jokisch, T. A1 - Gook, S. A1 - Marko, A. A1 - Üstündag, Ömer A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Laser beam welding of additive manufactured components: Applicability of existing valuation regulations N2 - With additive manufacturing in the powder bed, the component size is limited by the installation space. Joint welding of additively manufactured parts offers a possibility to remove this size limitation. However, due to the specific stress and microstructure state in the additively built material, it is unclear to what extent existing evaluation rules of joint welding are also suitable for welds on additive components. This is investigated using laser beam welding of additively manufactured pipe joints. The welds are evaluated by means of visual inspection, metallographic examinations as well as computed tomography. The types of defects found are comparable to conventional components. This is an indicator that existing evaluation regulations also map the possible defects occurring for weld seams on additive components. KW - Weld imperfections KW - Additive manufacturing KW - Weldability KW - Laser welding PY - 2022 VL - 2 SP - 109 EP - 113 PB - DVS Media GmbH AN - OPUS4-56374 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Marko, A. A1 - Bähring, S. A1 - Raute, J. A1 - Biegler, M. A1 - Rethmeier, Michael T1 - Transferability of ANN-generated parameter sets from welding tracks to 3D-geometries in Directed Energy Deposition N2 - Directed energy deposition (DED) has been in industrial use as a coating process for many years. Modern applications include the repair of existing components and additive manufacturing. The main advantages of DED are high deposition rates and low energy input. However, the process is influenced by a variety of parameters affecting the component quality. Artificial neural networks (ANNs) offer the possibility of mapping complex processes such as DED. They can serve as a tool for predicting optimal process parameters and quality characteristics. Previous research only refers to weld beads: a transferability to additively manufactured three-dimensional components has not been investigated. In the context of this work, an ANN is generated based on 86 weld beads. Quality categories (poor, medium, and good) are chosen as target variables to combine several quality features. The applicability of this categorization compared to conventional characteristics is discussed in detail. The ANN predicts the quality category of weld beads with an average accuracy of 81.5%. Two randomly generated parameter sets predicted as “good” by the network are then used to build tracks, coatings,walls, and cubes. It is shown that ANN trained with weld beads are suitable for complex parameter predictions in a limited way. KW - Welding parameter KW - Quality assurance KW - DED KW - Artificial neural network KW - Additive manufacturing PY - 2022 DO - https://doi.org/10.1515/mt-2022-0054 SN - 0025-5300 VL - 64 IS - 11 SP - 1586 EP - 1596 PB - De Gruyter AN - OPUS4-56278 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Marko, A. A1 - Bähring, S. A1 - Raute, J. A1 - Biegler, M. A1 - Rethmeier, Michael T1 - Prognose von Qualitätsmerkmalen durch Anwendung von KI-Methoden beim Directed 10 Energy Deposition N2 - Dieser Beitrag enthält die Ergebnisse eines im Rahmen der DVS Forschung entwickelten Ansatzes zur Qualitätssicherung im Directed Energy Deposition. Es basiert auf der Verarbeitung verschiedener während des Prozesses gesammelter Sensordaten unter Anwendung Künstlicher Neuronale Netze (KNN). So ließen sich die Qualitätsmerkmale Härte und Dichte auf der Datenbasis von 50 additiv gefertigten Probenwürfel mit einer Abweichung < 2 % vorhersagen. Des Weiteren wurde die Übertragbarkeit des KNN auf eine Schaufelgeometrie untersucht. Auch hier ließen sich Härte und Dichte hervorragend prognostizieren (Abweichung < 1,5 %), sodass der Ansatz als validiert betrachtet werden kann. KW - Kl KW - Directed Energy Depositio KW - Qualitätssicherung PY - 2022 SN - 0036-7184 VL - 74 IS - 10 SP - 672 EP - 679 PB - DVS Media CY - Düsseldorf AN - OPUS4-56284 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Marko, A. A1 - Graf, B. A1 - Rethmeier, Michael T1 - Statistical analysis of weld bead geometry in Ti6Al4V laser cladding N2 - The process of laser cladding has become more important during recent years because of its broad application for cladding, repair or additive manufacturing. In the field of mechanical engineering, one use is the repair of turbine blades. For high quality and reliability of the repaired components, it is necessary to adjust the weld bead geometry to the specific repair task. The bead geometry influences the metallurgical bonding and the degree of dilution as well as the formation of defects like pores or cracks. Therefore, it is important to know the effects of the different parameters on the welding bead. A valuable tool to meet this industrial challenge is the design of experiments (DoE). In this context, the user can choose between a huge number of test plans. Greater Profit of information is expected by a larger test range. In order to confirm the acceptance, a five-step full factorial test plan is compared to a central composite design in this paper. Moreover, the limits of the experimental range are indicated and restrictions can be derived. As the results show, the essential effects are detected with a full factorial test plan as well as with a central composite design. Merely the effect strength could not always be specified unambiguously. On this account and in consideration of cost efficiency, the use of central compound design is recommended in industrial applications. KW - Laser metal deposition KW - Design of experiments KW - Laser cladding KW - Cladding parameter KW - Additive manufacturing PY - 2017 DO - https://doi.org/10.3139/120.111077 SN - 0025-5300 SN - 2195-8572 VL - 59 IS - 10 SP - 837 EP - 843 PB - Carl Hanser Verlag CY - München AN - OPUS4-42882 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Neubert, S. A1 - Pittner, Andreas A1 - Rethmeier, Michael T1 - Strain-rate controlled Gleeble experiments to determine the stress-strain behavior of HSLA steel S960QL N2 - In order to generate a material data base for computational welding mechanics, temperature and strain-rate dependent stress-strain experiments were performed by using a Gleeble®3500 testing system. The object of the investigation was HSLA transformable steel S960QL and related solid phases as bainite, martensite and austenite. For the production of these solid phases, the base material was heat treated according to an average weld temperature cycle which was extracted within the heat affected zone of a thermal numerical weld simulation of a GMA weld. The hot tensile tests were carried out via cost-saving flat specimen geometries. Two experimental series with different strain-rates were conducted, where the longitudinal strain-rate was controlled by specification of the transversal strain-rate applying Poisson’s-ratio. Subsequently, the resulting stress-strain curves were approximated in accordance with the Ramberg-Osgood-materials law. Consequently, it is shown that the temperature and strain-rate dependent stress-strain behavior of metals can be successfully characterized by means of a Gleeble®-system. However, this requires a control of the longitudinal strain-rate by specification of the transversal strain-rate. The related experimental procedure and the method of evaluation are explained in detail. With regard to all tested solid phases, a significant strain-rate dependency can only be observed upwards from temperatures of 400 °C. Based on experimental results, Ramberg-Osgood-parameters will be presented to describe the stress-strain behavior of steel S960QL and related solid phases for temperatures between 25 °C and 1200 °C. Furthermore, the use of costsaving flat specimen-geometry appears reasonable. N2 - Für die Generierung einer Materialdatenbank zur Schweißstruktursimulation wurden temperatur- und dehnratenabhängige Spannungs-Dehnungsexperimente unter Einsatz einer Gleeble® 3500-Anlage durchgeführt. Als Untersuchungsgegenstand diente der hochfeste niedriglegierte Feinkornbaustahl S960QL und seine zugehörigen Festphasen Bainit, Martensit und Austenit. Zur Herstellung dieser Festphasen wurde der Grundwerkstoff Wärmebehandlungen ausgesetzt, welche die charakteristischen Merkmale eines durchschnittlichen Schweißzeittemperaturzyklus aufweisen. Dieser Temperaturzyklus wurde aus der Wärmeeinflusszone eines numerisch nachgebildeten Temperaturfeldes einer MAG-Schweißverbindung extrahiert. Die Zugversuche wurden an einer kostengünstig herzustellenden Flachprobengeometrie durchgeführt, wobei zwei Experimentalreihen mit jeweils unterschiedlichen Dehnraten realisiert wurden. Die resultierenden Spannungs-Dehnungskurven wurden durch die Ramberg-Osgood-Beziehung approximiert. Es konnte gezeigt werden, dass das temperatur- und dehnratenabhängige Spannungs-Dehnungsverhalten von Metallen durch die Anwendung eines Gleeble®-Systems erfolgreich charakterisiert werden kann. Die Einstellung der Längsdehnrate muss dabei durch die Kontrolle der Querdehnrate unter Berücksichtigung des Poisson-Verhältnisses erfolgen. Die experimentellen Prozeduren und die zugehörigen Auswertemethodiken wurden detailliert erläutert. Für alle getesteten Festphasen wurde ein signifikanter Dehnrateneinfluss erst für Temperaturen ab 400 °C aufwärts beobachtet. Die anhand der Messergebnisse abgeleiteten Ramberg-Osgood-Parameter zur Beschreibung des Verfestigungsverhaltens für den Temperaturbereich zwischen 25 °C und 1200 °C werden vollständig präsentiert. KW - Stress-strain behavior KW - Gleeble testing KW - HSLA KW - Strain-rate KW - Numerical welding simulation KW - Transformable steels PY - 2018 DO - https://doi.org/10.3139/120.111208 SN - 0025-5300 VL - 60 IS - 7-8 SP - 733 EP - 748 PB - Carl Hanser CY - München AN - OPUS4-45791 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Spranger, Felix A1 - Graf, B. A1 - Schuch, M. A1 - Hilgenberg, Kai A1 - Rethmeier, Michael T1 - Build-up strategies for additive manufacturing of three dimensional Ti-6Al-4V-parts produced by laser metal deposition N2 - Laser metal deposition (LMD) has been applied as a coating technology for many years. Today, the technologies capacity to produce 3D depositions leads to a new field of application as additive manufacturing method. In this paper, 3D laser metal deposition of titanium alloy Ti-6Al-4V is studied with special regard to the demands of additive manufacturing. Therefore, only the coaxial LMD powder nozzle is used to create the shielding gas atmosphere, which ensures high geometric flexibility. Furthermore, specimen with high aspect ratio and hundreds of layers are manufactured, which represent typical features in additive manufacturing. The presented study contains the following steps: First, cylindrical specimens are manufactured with a standard shell-core build-up strategy and mechanical properties as well as fracture mechanisms are determined. Based on the results, experiments are conducted to improve the build-up strategy and new tensile test specimens are built with the improved strategy. The improved strategy incorporates variable track overlap ratios to achieve a constant growth in the shell and core area. As blanks, lean cylinders comprising more than 240 layers and a height of more than 120mm are manufactured. The specimens are analyzed by X-ray inspection for material defects. Fractured surfaces are observed via scanning electron microscopy and the composition of the surfaces is determined using energy dispersive X-ray spectroscopy. The tensile test results prove mechanical properties close to ASTM F1108 specification for wrought material. KW - Laser metal deposition KW - Ti-6Al-4V KW - Additive manufacturing KW - Titanium alloy KW - Turbine components PY - 2018 DO - https://doi.org/10.2351/1.4997852 SN - 1938-1387 SN - 1042-346X VL - 30 IS - 2 SP - UNSP 022001, 1 EP - 13 PB - Laser Institute of America AN - OPUS4-44655 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Graf, B. A1 - Marko, A. A1 - Petrat, T. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - 3D laser metal deposition: process steps for additive manufacturing N2 - Laser metal deposition (LMD) is an established technology for two-dimensional surface coatings. It offers high deposition rates, high material flexibility, and the possibility to deposit material on existing components. Due to these features, LMD has been increasingly applied for additive manufacturing of 3D structures in recent years. Compared to previous coating applications, additive manufacturing of 3D structures leads to new challenges regarding LMD process knowledge. In this paper, the process steps for LMD as additive manufacturing technology are described. The experiments are conducted using titanium alloy Ti-6Al-4Vand Inconel 718. Only the LMD nozzle is used to create a shielding gas atmosphere. This ensures the high geometric flexibility needed for additive manufacturing, although issues with the restricted size and quality of the shielding gas atmosphere arise. In the first step, the influence of process parameters on the geometric dimensions of single weld beads is analyzed based on design of experiments. In the second step, a 3D build-up strategy for cylindrical specimen with high dimensional accuracy is described. Process parameters, travel paths, and cooling periods between layers are adjusted. Tensile tests show that mechanical properties in the as-deposited condition are close to wrought material. As practical example, the fir-tree root profile of a turbine blade is manufactured. The feasibility of LMD as additive technology is evaluated based on this component. KW - Laser metal deposition KW - Build-up strategy KW - Deposition rate KW - Additive manufacturing PY - 2018 DO - https://doi.org/10.1007/s40194-018-0590-x SN - 0043-2288 SN - 1878-6669 VL - 62 IS - 4 SP - 877 EP - 883 PB - Springer Berlin Heidelberg CY - Heidelberg AN - OPUS4-44868 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Meschut, G. A1 - Janzen, V. A1 - Rethmeier, Michael A1 - Gumenyuk, Andrey A1 - Frei, J. T1 - Charakterisierung des Bruch- und Festigkeits verhaltens von widerstandspunktgeschweißten Aluminiumverbindungen N2 - Die Reduktion des Fahrzeuggewichts ist ein wesentlicher Ansatz zur Ver-ringerung des Energie- und Ressourcenverbrauchs und damit zur Senkung der CO2-Emissionen im Automobilbau. In der Karosserieentwicklung kann der vermehrte Einsatz von Aluminiumwerkstoffen einen bedeutenden Beitrag dazu leisten. Im preissensitiven Umfeld des Karosseriebaus etabliert sich das bei Stahlanwendungen genutzte Widerstandspunktschweißen zunehmend auch für Aluminiumverbindungen. Verfahrensbedingte Herausforderungen, wie verkürzte Elektrodenstandzeiten und mangelnde Kenntnis über den Einfluss von Imperfektionen auf die Festigkeit, begrenzen dennoch die Weiterverbreitung des Verfahrens und stellen die Prozessrobustheit insgesamt in Frage. Im Rahmen des hier vorgestellten Forschungsvorhabens wurden das Auftreten verschiedener Brucharten experimentell untersucht und Prognosefunktionen zur Abschätzung der Tragfähigkeit von Widerstandspunktschweißverbindungen unter verschiedenen Belastungsfällen erstellt. Anschließend wurde der Einfluss von Oberflächenrissen und Rissen in der Schweißlinse auf die Scherzugfestigkeit sowohl experimentell als auch simulativ analysiert. KW - Aluminium KW - Widerstandspressschweißen KW - Rissbildung KW - Festigkeit KW - Werkstofffragen PY - 2017 UR - http://www.schweissenundschneiden.de/article/charakterisierung-des-bruch-und-festigkeitsverhaltens-von-widerstandspunktgeschweissten-aluminiumverbindungen/ VL - 69 IS - 3 SP - 126 EP - 133 PB - DVS Media GmbH AN - OPUS4-39577 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sproesser, G. A1 - Chang, Y.-J. A1 - Pittner, Andreas A1 - Finkbeiner, M. A1 - Rethmeier, Michael T1 - Environmental energy efficiency of single wire and tandem gas metal arc welding N2 - This paper investigates gas metal arc welding (GMAW) with respect to energy consumption and its associated environmental impacts. Different material transfer modes and power levels for single wire GMAW (SGMAW) and tandem GMAW (TGMAW) are evaluated by means of the indicator electrical deposition efficiency. Furthermore, the wall-plug efficiency of the equipment is measured in order to describe the total energy consumption from the electricity grid. The results show that the energy efficiency is highly affected by the respective process and can be significantly enhanced by a TGMAW process. The wall-plug efficiency of the equipment shows no significant dependency on the power range or the material transfer mode. Moreover, the method of life cycle assessment (LCA) is adopted in order to investigate the influences of energy efficient welding on the environmental impacts. In the comparative LCA study, the demand of electrical energy is reduced up to 24%. In consequence, the indicator values for global warming potential (100), acidification potential, eutrophication potential, and photochemical ozone creation potential are reduced up to 11%. KW - Energy input KW - Tandem welding KW - MAG welding KW - Environment KW - Lifetime PY - 2017 DO - https://doi.org/10.1007/s40194-017-0460-y SN - 0043-2288 SN - 1878-6669 VL - 61 IS - 4 SP - 733 EP - 743 PB - Springer CY - Heidelberg AN - OPUS4-39877 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Graf, B. A1 - Gook, S. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Combined laser additive manufacturing for complex turbine blades N2 - Laser beam processes are increasingly used in the field of additive manufacturing. Prominent methods are either powderbed-based like Laser Metal Fusion (LMF), or utilizing a powder nozzle like Laser Metal Deposition (LMD). While LMF allows the manufacturing of complex structures, build rate, part volumes and material flexibility are limited. In contrast, LMD is able to operate with high deposition rates on existing parts, and materials can be changed easily during the process. However LMD shape complexity is limited. Utilizing their respective strengths, a combination of these two additive technologies has the potential to produce complex parts with high deposition rates and increased material flexibility. In this paper, combined manufacturing with additive technologies LMF and LMD is described. Its benefit for industry with emphasis on turbomachinery is shown. As reality test for the innovation, an industrial turbine blade is manufactured. KW - Turbine blade KW - Additive manufacturing KW - Laser metal fusion KW - Laser metal deposition PY - 2016 SN - 2499-9733 VL - 3 IS - 20 SP - 34 EP - 42 AN - OPUS4-38709 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Numerical simulation of solidification crack formation during laser beam welding of austenitic stainless steels under external load N2 - Solidification cracking phenomena taking place under controlled tensile weldability (CTW) test conditions have already been investigated both experimentally and numerically via FEA in order to get a better understanding of the mechanisms of hot crack formation during laser beam welding of austenitic steel grades. This paper develops a threedimensional finite element model employing the contact element technique to simulate the formation and propagation of solidification cracks during laser full penetration welding of fully austenitic stainless steel 1.4376. During the experimental procedure, the resulting strain and displacement directed to the laser beam in the close vicinity of the weld pool was measured at the surface of the workpiece using a digital image correlation (DIC) technique with an external diode laser as an illuminating source. Local strain fields, global loads and crack lengths predicted by the model are in good agreement with those observed in experiments. KW - Solidification cracking KW - Finite element analysis KW - Imaging KW - Laser welding KW - Austenitic stainless steels PY - 2016 DO - https://doi.org/10.1007/s40194-016-0357-1 SN - 0043-2288 SN - 1878-6669 VL - 60 IS - 5 SP - 1001 EP - 1008 PB - Springer CY - Berlin, Heidelberg AN - OPUS4-37287 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sproesser, Gunther A1 - Chang, Y.-J. A1 - Pittner, Andreas A1 - Finkbeiner, M. A1 - Rethmeier, Michael T1 - Life cycle assessment of welding technologies for thick metal plate welds N2 - Life Cycle Assessment (LCA) is applied in evaluating environmental impacts of state-of-the-art welding technologies. Manual Metal Arc Welding (MMAW), Laser Arc-Hybrid Welding (LAHW) and two Gas Metal Arc Welding (GMAW) variants are used to join a plate of 20 mm thick structural steel. The LCA results indicate that for 1 m weld seam, MMAW causes the highest environmental impacts in global warming potential (GWP), eutrophication potential (EP), acidification potential (AP), and photochemical ozone creation potential (POCP) among the selected processes, and the LAHW variant performances the least. Filler material and electricity consumptions generally dominate the impacts and reach shares of up to 80% and 61% in the respective impact categories. However, electrode coating consumption in MMAW remarkably contributes impacts on AP and EP, for instance 52% of AP and 76% of EP. Strategies for improvement of the applied welding technologies are discussed. KW - Life Cycle Assessment (LCA) KW - Arc welding KW - Laser arc-hybrid welding KW - Resource efficiency PY - 2015 DO - https://doi.org/10.1016/j.jclepro.2015.06.121 SN - 0959-6526 VL - 108 IS - Part: A SP - 46 EP - 53 PB - Elsevier Science CY - Amsterdam AN - OPUS4-34969 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bachmann, Marcel A1 - Avilov, Vjaceslav A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Numerical assessment and experimental verification of the influence of the Hartmann effect in laser beam welding processes by steady magnetic fields N2 - Controlling the dynamics in the weld pool is a highly demanding challenge in deep-penetration laser beam welding with modern high power laser systems in the multi kilowatt range. An approach to insert braking forces in the melt which is successfully used in large-scaled industrial applications like casting is the so-called Hartmann effect due to externally applied magnetic fields. Therefore, this study deals with its adaptation to a laser beam welding process of much smaller geometric and time scale. In this paper, the contactless mitigation of fluid dynamic processes in the melt by steady magnetic fields was investigated by numerical simulation for partial penetration welding of aluminium. Three-dimensional heat transfer, fluid dynamics including phase transition and electromagnetic field partial differential equations were solved based on temperature-dependent material properties up to evaporation temperature for two different penetration depths of the laser beam. The Marangoni convection in the surface region of the weld pool and the natural convection due to the gravitational forces were identified as main driving forces in the weld pool. Furthermore, the latent heat of solide-liquid phase transition was taken into account and the solidification was modelled by the Carman-Kozeny equation for porous medium morphology. The results show that a characteristic change of the flow pattern in the melt can be achieved by the applied steady magnetic fields depending on the ratio of magnetic induced and viscous drag. Consequently, the weld bead geometry was significantly influenced by the developing Lorentz forces. Welding experiments with a 16 kW disc laser with an applied magnetic flux density of around 500 mT support the numerical results by showing a dissipating effect on the weld pool dynamics. KW - Electromagnetic weld pool control KW - Hartmann effect KW - Laser beam weliding KW - Lorentz force KW - Marangoni flow KW - Natural convection KW - Aluminium PY - 2016 DO - https://doi.org/10.1016/j.ijthermalsci.2015.10.030 SN - 1290-0729 VL - 101 SP - 24 EP - 34 PB - Elsevier CY - Paris AN - OPUS4-35034 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pittner, Andreas A1 - Schwenk, Christopher A1 - Rethmeier, Michael A1 - Weiß, D. T1 - Automated generation of temperature fields for numerical welding simulation KW - Welding simulation KW - Temperature field generation KW - Optimization KW - Neural networks PY - 2009 SN - 0288-4771 VL - 27 IS - 2 SP - 219 EP - 224 CY - Tokyo, Japan AN - OPUS4-19826 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Grünenwald, S. A1 - Seefeld, T. A1 - Vollertsen, F. A1 - Gook, Sergej A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Laserstrahl-MSG-Hybridschweißen dicker Bleche aus Rohrleitungsstahl mit Faserlasern hoher Leistung N2 - In diesem Beitrag werden die Ergebnisse aus einem gemeinschaftlich durchgeführten Forschungsprojekt zur Schweißeignung unlegierter Stähle mit Laserstrahl- und Lichtbogenschweißverfahren vorgestellt. Es wurden Schweißversuche in Ein- sowie Mehrlagentechnik mit Blechdicken von 16, 20 und 28 mm durchgeführt sowie die Prozessgrenzen für die Spaltüberbrückbarkeit, den Kantenversatz und das Schweißen in Zwangspositionen untersucht. Für die Schweißversuche kamen Faserlaser mit Leistungen von 8, 20 und 30 kW in Verbindung mit einem MAG-Schweißprozess als Laserstrahl-MSG-Hybridschweißen zum Einsatz. Mit dem 30-kW-Faserlaser war es möglich, 28 mm dicke Bleche einlagig zu schweißen, jedoch besteht weiterer Forschungsbedarf, um Aussagen über die erreichbare Qualität treffen zu können. Bei 20 kW Laserstrahlleistung wurde zum einlagigen Schweißen von Blechen mit einer Dicke von 20 mm eine entsprechende Nahtvorbereitung benötigt, 16 mm dicke Bleche konnten dagegen ohne Vorbereitung der Naht im Stumpfstoß geschweißt werden. In der Mehrlagentechnik wurden mit dem 8-kW-Faserlaser 16 mm dicke Bleche vorbereitet mit einer Y-Naht geschweißt. Hierbei wurde die Wurzellage hybrid geschweißt, die Füll- und Decklagen mit einem reinen MAG-Prozess. PY - 2010 SN - 0036-7184 VL - 62 IS - 6 SP - 338 EP - 347 PB - Verl. für Schweißen u. Verwandte Verfahren, DVS-Verl. CY - Düsseldorf AN - OPUS4-21810 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gook, Sergej A1 - Gumenyuk, Andrey A1 - Lammers, Marco A1 - Rethmeier, Michael T1 - Peculiarities of the process of orbital laser-arc welding of thick-walled large-diameter pipes KW - Hybrid laser-arc welding KW - Orbital welding KW - High-pressure pipelines KW - Fibre-optic lasers PY - 2010 SN - 0005-111x SN - 0005-2302 VL - 689 IS - 9 SP - 5 EP - 13 CY - Kiev, Ukraine AN - OPUS4-22979 LA - rus AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weber, Gert A1 - Thommes, H. A1 - Gaul, Holger A1 - Hahn, O. A1 - Rethmeier, Michael T1 - Resistance spot welding and weldbonding of advanced high strength steels KW - Resistance spot welding KW - High strength steel KW - Weldbonding KW - Widerstandspunktschweißen KW - Hochfester Stahl KW - Punktschweißkleben PY - 2010 DO - https://doi.org/10.1002/mawe.201000687 SN - 0933-5137 SN - 1521-4052 VL - 41 IS - 11 SP - 931 EP - 939 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-22948 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schwenk, Christopher A1 - Rethmeier, Michael T1 - Distortion optimisation of beam-welded industrial parts by means of numerical welding simulation KW - Distortion KW - Optimisation KW - Weld plan modification KW - Industrial parts KW - Automotive application KW - Numerical welding simulation KW - Laser beam welding KW - Electron beam welding KW - Finite element analysis KW - FEA PY - 2010 SN - 1741-8410 SN - 1741-8429 VL - 5 IS - 4/5 SP - 412 EP - 422 PB - Inderscience Enterprises Ltd CY - Genève, Switzerland AN - OPUS4-22705 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pittner, Andreas A1 - Weiß, D. A1 - Schwenk, Christopher A1 - Rethmeier, Michael T1 - Methodology to improve applicability of welding simulation N2 - The objective of this paper is to demonstrate a new simulation technique which allows fast and automatic generation of temperature fields as input for subsequent thermomechanical welding simulation. The basic idea is to decompose the process model into an empirical part based on neural networks and a phenomenological part that describes the physical phenomena. The strength of this composite modelling approach is the automatic calibration of mathematical models against experimental data without the need for manual interference by an experienced user. As an example for typical applications in laser beam and GMA-laser hybrid welding, it is shown that even 3D heat conduction models of a low complexity can approximate measured temperature fields with a sufficient accuracy. In general, any derivation of model fitting parameters from the real process adds uncertainties to the simulation independent of the complexity of the underlying phenomenological model. The modelling technique presented hybridises empirical and phenomenological models. It reduces the model uncertainties by exploiting additional information which keeps normally hidden in the data measured when the model calibration is performed against few experimental data sets. In contrast, here the optimal model parameter set corresponding to a given process parameter is computed by means of an empirical submodel based on relatively large set of experimental data. The approach allows making a contribution to an efficient compensation of modelling inaccuracies and lack of knowledge about thermophysical material properties or boundary conditions. Two illustrating examples are provided. KW - Welding simulation KW - GMA-laser hybrid welding KW - Laser beam welding KW - Neural networks KW - Global optimisation KW - Stochastic search method KW - Inverse heat conduction problem KW - Model prediction PY - 2008 DO - https://doi.org/10.1179/136217108X329322 SN - 1362-1718 SN - 1743-2936 VL - 13 IS - 6 SP - 496 EP - 508 PB - Maney CY - London AN - OPUS4-18300 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Karkhin, Victor A1 - Pittner, Andreas A1 - Schwenk, Christopher A1 - Rethmeier, Michael T1 - Simulation of inverse heat conduction problems in fusion welding with extended analytical heat source models N2 - The paper presents bounded volume heat sources and the corresponding functional-analytical expressions for the temperature field. The power density distributions considered here are normal, exponential and parabolic. The sources model real heat sources like the welding arc, laser beam, electron beam, etc., the convection in the weld pool as well as the latent heat due to fusion and solidification. The parameters of the heat source models are unknown a priori and have to be evaluated by solving an inverse heat conduction problem. The functional-analytical technique for calculating 3D temperature fields in butt welding is developed. The proposed technique makes it possible to reduce considerably the total time for data input and solution. It is demonstrated with an example of laser beam welding of steel plates. KW - Laser beam welding KW - Volume heat source KW - Functional-analytical solution KW - Inverse modelling PY - 2011 DO - https://doi.org/10.1007/s11706-011-0137-1 SN - 2095-025X SN - 2095-0268 VL - 5 IS - 2 SP - 119 EP - 125 PB - Springer CY - Secaucus, N.J. AN - OPUS4-24164 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gaul, Holger A1 - Weber, Gert A1 - Rethmeier, Michael T1 - Influence of HAZ cracks on fatigue resistance of resistance spot welded joints made of advanced high strength steels N2 - A method is reported with which heat affected zone (HAZ) cracks in a specific region of spot welded joints, made of advanced high strength steels, could be realised. The influence of HAZ cracks on the fatigue behaviour, which is the focus of the contribution, was studied by evaluating the stiffness characteristics as a function of the number of cycles N in comparison with crack-free specimens, i.e. by analysing HAZ and fatigue cracks on the specimen surface and the surface of fatigue fractures containing beach marks. It was found that the fatigue cracks are not initiated at the HAZ cracks. The number of cycles to failure Nf is not significantly reduced for specimens with HAZ cracks. Overall, the examinations did not reveal any influence of HAZ cracks on the fatigue strength of resistance spot welded joints. KW - Discontinuities KW - AHSS KW - HAZ crack KW - Spot welding KW - Advanced high strength steels KW - Fatigue PY - 2011 DO - https://doi.org/10.1179/1362171810Y.0000000031 SN - 1362-1718 SN - 1743-2936 VL - 16 IS - 5 SP - 440 EP - 445 PB - Maney CY - London AN - OPUS4-24214 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pittner, Andreas A1 - Weiß, D. A1 - Schwenk, Christopher A1 - Rethmeier, Michael T1 - Fast temperature field generation for welding simulation and reduction of experimental effort N2 - The quality of welding processes is governed by the occurring induced distortions yielding an increase in production costs due to necessary reworking. Especially for more complex specimens, it is difficult to evaluate the optimal configuration of welding sequences in order to minimize the distortion. Even experienced welding operators can solve this task only by trial and error which is time and cost consuming. In modern engineering the application of welding simulation is already known to be able to analyse the heat effects of welding virtually. However, the welding process is governed by complex physical interactions. Thus, recent weld thermal models are based on many simplifications. The state of the art is to apply numerical methods in order to solve the transient heat conduction equation. Therefore, it is not possible to use the real process parameters as input for the mathematical model. The model parameters which allow calculating a temperature field that is in best agreement with the experiments cannot be defined directly but inversely by multiple simulations runs. In case of numerical simulation software based on finite discretization schemes this approach is very time consuming and requires expert users. The weld thermal model contains an initial weakness which has to be adapted by finding an optimal set of model parameters. This process of calibration is often done against few experiments. The range of model validity is limited. An extension can be obtained by performing a calibration against multiple experiments. The focus of the paper is to show a combined modelling technique which provides an efficient solution of the inverse heat conduction problem mentioned above. On the one hand the inverse problem is solved by application of fast weld thermal models which are closed form solutions of the heat conduction equation. In addition, a global optimization algorithm allows an automated calibration of the weld thermal model. This technique is able to provide a temperature field automatically that fits the experimental one with high accuracy within minutes on ordinary office computers. This fast paradigm permits confirming the application of welding simulation in an industrial environment as automotive industry. On the other hand, the initial model weakness is compensated by calibrating the model against multiple experiments. The unknown relationship between model and process parameters is approximated by a neural network. The validity of the model is increased successively and enables to decrease experimental effort, For a test case, it is shown that this approach yields accurate temperature fields within very short amount of time for unknown process parameters as input data to the model contributing to the requirement to construct a substitute system of the real welding process. KW - Heat flow KW - Neural networks KW - Simulating KW - Temperature KW - Welding PY - 2011 SN - 0043-2288 SN - 1878-6669 VL - 55 IS - 09-10 SP - 83 EP - 90 PB - Springer CY - Oxford AN - OPUS4-24603 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schempp, Philipp A1 - Schwenk, Christopher A1 - Rethmeier, Michael A1 - Cross, C.E. T1 - Weld metal grain refinement of aluminium alloy 5083 through controlled additions of Ti and B N2 - Kornfeinung im Schweißgut kann die mechanischen Eigenschaften der Schweißnaht und die Schweißeignung des Grundwerkstoffs deutlich verbessern. Eine Möglichkeit korngefeintes Schweißgut zu erreichen, ist das Versetzen des Schmelzbades mit kornfeinenden Mitteln. In dieser Studie wird gezeigt wie Titan- und Borzusätze Korngröße und -struktur von WIG-Schweißnähten der Al-Legierung 5083 (Al Mg4,5Mn0,7) beeinflussen. Dazu wurden in einem Gießprozess stäbchenförmige Einlagen hergestellt, die aus Grundwerkstoff und definierten Zusätzen der Kornfeinungslegierung Al Ti5B1 bestanden. Sie wurden als Ersatz für einen Schweißzusatzwerkstoff in einer Nut im Grundwerkstoff untergebracht und im WIG-Verfahren überschweißt. Durch die Steigerung des Titan- und Borgehalts im Schweißgut konnte dessen mittlere Korngröße deutlich verringert werden. Außerdem wurde eine Änderung der Kornstruktur beobachtet. Die Ergebnisse können als Grundlage genutzt werden, um die empfohlene chemische Zusammensetzung von Schweißzusätzen für Lichtbogenschweißen von Aluminium anzupassen. KW - Aluminium-Legierung 5083 KW - Kornfeinung KW - WIG-Schweißen PY - 2011 DO - https://doi.org/10.3139/120.110265 SN - 0025-5300 VL - 53 IS - 10 SP - 604 EP - 609 PB - Hanser CY - München AN - OPUS4-24654 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Heinze, Christoph A1 - Michael, Thomas A1 - Pittner, Andreas A1 - Rethmeier, Michael T1 - Schwierigkeiten bei der Anwendung der aktuellen Normung in Bezug auf Mikrorisse in Schweißverbindungen hochfester vergüteter Feinkornbaustähle N2 - Die aktuelle Normung bezüglich mikroskopischer Untersuchungen von Schweißverbindungen und die Zulässigkeit von Mikrorissen sowie deren Definition ist nicht eindeutig. Nach der Darstellung derzeit gültiger Normen im Bereich der Bewertung von Schweißnähten, Qualifizierung von Schweißverfahren und Ausführung von Schweißverbindungen, wird auf Grundlage aktueller Schweißversuche an hochfesten vergüteten Feinkornbaustählen die Problematik von Mikrorissen diskutiert. Offene Punkte und Fragen bzw. Verbesserungsmöglichkeiten werden aufgezeigt und zur Diskussion gestellt. Schließlich wird auf die Klärung des Einflusses von Mikrorissen auf die mechanisch- technologischen Werkstoffkennwerte der Schweißverbindung unter statischer sowie zyklischer Beanspruchung hingewiesen. --------------------------------------------------------------------------------------------------------------------------------------------------------------- Neither the latest standardisation with regard to microscopic investigations on welded joints nor the permissibility of microcracks and their definition are unambiguous. According to the representation of currently applicable standards in the fields of the assessment of welds, the qualification of welding processes and the execution of welded joints, the problems associated with microcracks are discussed on the basis of the latest welding tests on high-strength quenched-and-tempered fine-grained structural steels. Not only outstanding points and questions but also improvement possibilities are indicated and opened for discussion. Finally, attention is drawn to the clarification of the influence of microcracks on the mechanical- technological material parameters of the welded joint subjected to both static and cyclic stresses. KW - Festigkeit KW - Hochfester Stahl KW - Normen KW - Rissbildung KW - Schweißnahtfehler KW - Werkstofffragen KW - Strength KW - High-strength steel KW - Standards KW - Crack formation KW - Weld defects KW - Material questions PY - 2012 SN - 0036-7184 VL - 64 IS - 7 SP - 412 EP - 416 PB - Verl. für Schweißen u. Verwandte Verfahren, DVS-Verl. CY - Düsseldorf AN - OPUS4-26338 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Heinze, Christoph A1 - Pittner, Andreas A1 - Rethmeier, Michael A1 - Babu, S. S. T1 - Dependency of martensite start temperature on prior austenite grain size and its influence on welding-induced residual stresses N2 - Austenite grain growth during welding is a critical factor for controlling weld microstructure in addition to nominal composition and thermal cycles. Recently, experimental data suggesting a decrease in martensite start temperature with a decrease in prior austenite grain size has been published. However, the actual sensitivity of this phenomenon on residual stresses evolution in the heat-affected zone has not been investigated, yet. Therefore, a numerical model was modified to consider this phenomenon. Numerical simulations were performed for welding of a low-alloy structural steel with minimum yield strength of 355 MPa (S355J2+N) and a heat-resistant steel P91 or 9Cr–1Mo, respectively. The results clarify the influence of prior austenite grain size on the residual stress development and show the importance martensite transformation temperatures and final martensite fraction. Consequently, the residual stress evolution of P91, which completely transforms to martensite while cooling, based on the enhanced model leads to maximum stress differences of 200 MPa in the heat-affected zone. KW - Prior austenite grain size KW - Martensite start temperature KW - Welding-induced residual stress KW - Numerical simulation KW - Gas metal arc welding PY - 2013 DO - https://doi.org/10.1016/j.commatsci.2012.11.058 SN - 0927-0256 VL - 69 SP - 251 EP - 260 PB - Elsevier CY - Amsterdam AN - OPUS4-27633 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kolkoori, Sanjeevareddy A1 - Höhne, Christian A1 - Prager, Jens A1 - Rethmeier, Michael A1 - Kreutzbruck, Marc T1 - Quantitative evaluation of ultrasonic C-scan image in acoustically homogeneous and layered anisotropic materials using three dimensional ray tracing method N2 - Quantitative evaluation of ultrasonic C-scan images in homogeneous and layered anisotropic austenitic materials is of general importance for understanding the influence of anisotropy on wave fields during ultrasonic non-destructive testing and evaluation of these materials. In this contribution, a three dimensional ray tracing method is presented for evaluating ultrasonic C-scan images quantitatively in general homogeneous and layered anisotropic austenitic materials. The directivity of the ultrasonic ray source in general homogeneous columnar grained anisotropic austenitic steel material (including layback orientation) is obtained in three dimensions based on Lamb's reciprocity theorem. As a prerequisite for ray tracing model, the problem of ultrasonic ray energy reflection and transmission coefficients at an interface between (a) isotropic base material and anisotropic austenitic weld material (including layback orientation), (b) two adjacent anisotropic weld metals and (c) anisotropic weld metal and isotropic base material is solved in three dimensions. The influence of columnar grain orientation and layback orientation on ultrasonic C-scan image is quantitatively analyzed in the context of ultrasonic testing of homogeneous and layered austenitic steel materials. The presented quantitative results provide valuable information during ultrasonic characterization of homogeneous and layered anisotropic austenitic steel materials. KW - Ultrasonic non-destructive evaluation KW - Ultrasonic C-scan image KW - Anisotropic austenitic steel KW - 3D ray tracing KW - Directivity PY - 2014 DO - https://doi.org/10.1016/j.ultras.2013.08.007 SN - 0041-624x VL - 54 IS - 2 SP - 551 EP - 562 PB - Elsevier CY - Amsterdam AN - OPUS4-29733 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yang, Fan A1 - Meng, Xiangmeng A1 - Putra, Stephen Nugraha A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Numerical studies of process porosity suppression by magnetohydrodynamic technology during the laser beam welding of aluminum alloy N2 - Magnetohydrodynamic (MHD) technology is acknowledged as a promising method for mitigating the porosity defects in laser-welded joints of aluminum alloys. A transient 3D multi-physical numerical model of laser beam welding (LBW), coupled with the MHD and oscillating metal vapor plume model, is developed to study the suppression mechanisms of process porosity by an external magnetic field. The experimental results demonstrate that the porosity ratio is reduced by 93.5 % as the oscillating magnetic field is applied. This significant reduction confirms the effectiveness of the MHD technology in suppressing porosity defects. A downward time-averaged Lorentz force is induced in the weld pool, which affects the fluid flow pattern and the weld pool profile. The change of the flowing pattern in the weld pool by the magnetic field does not always have a positive effect on the porosity suppression. In addition, an analytical model shows that the bubble escape window is expanded by 62 % under the effect of the oscillating magnetic field. The additional upward velocity provided by the electromagnetic expulsive force on the bubbles and the change of weld pool profile are considered favorable factors in eliminating the porosity defects. The numerical and analytical model developed for analyzing the bubble escape window have been validated by experimental results. KW - Laser beam welding KW - Aluminum alloy KW - Process porosity defects KW - Magnetohydrodynamic technology KW - Bubble escape KW - Numerical simulation PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-637642 DO - https://doi.org/10.1016/j.ijheatmasstransfer.2025.127525 SN - 0017-9310 VL - 253 SP - 1 EP - 13 PB - Elsevier Ltd. AN - OPUS4-63764 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Petrat, T. A1 - Winterkorn, René A1 - Graf, B. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Build-up strategies for temperature control using laser metal deposition for additive manufacturing N2 - The track geometry created with laser metal deposition (LMD) is influenced by various parameters. In this case, the laser power has an influence on the width of the track because of an increasing energy input. A larger melt pool is caused by a rising temperature. In the case of a longer welding process, there is also a rise in temperature, resulting in a change of the track geometry. This paper deals with the temperature profiles of different zigzag strategies and spiral strategies for additive manufacturing. A two-color pyrometer is used for temperature measurement on the component surface near the melt pool. Thermocouples measure the temperatures in deeper regions of a component. The welds are located in the center and in the edge area on a test part to investigate the temperature evolution under different boundary conditions. The experiments are carried out on substrates made from mild steel 1.0038 and with the filler material 316L. The investigations show an influence on the temperature evolution by the travel path strategy as well as the position on the part. This shows the necessity for the development and selection of build-up strategies for different part geometries in additive manufacturing by LMD. KW - Laser welding KW - Clad steels KW - Temperature distribution KW - Heat flow KW - Laser surfacing PY - 2018 DO - https://doi.org/10.1007/s40194-018-0604-8 SN - 0043-2288 SN - 1878-6669 VL - 62 IS - 5 SP - 1073 EP - 1081 PB - Springer AN - OPUS4-45773 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Artinov, Antoni A1 - Karkhin, V. A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Mathematical modeling of the geometrical differences between the weld end crater and the steady-state weld pool N2 - The geometrical characteristics of the weld end crater are commonly used as a means of validating numerical results in welding simulations. In this paper, an analytical model is developed for calculating the cooling stage of the welding process after the moving energy source is turned off. Solutions for various combinations of heat sources and heated bodies are found. It is shown that after turning off the Energy source, additional melting of the base material in the longitudinal direction may occur due to the overheated liquid metal. The developed technique is applied to complete-penetration keyhole laser beam welding of 2 mm thick austenitic stainless-steel plate 316L at a Welding speed of 20 mm/s and a laser power of 2.3 kW. The results show a theoretical increase in the weld end crater length of up to 19% compared to the length of the steady-state weld pool. It is found that at the moment of switch off, the weld end crater center, where solidification of the liquid metal ends, is shifted from the heat source axis toward the weld pool tail. The solidification rate and the direction of crystallization of the molten material during the welding process and those in the weld end crater differ significantly. A good agreement between the computational results and the welding experiments is achieved. KW - Weld end crater KW - Steady-state weld pool KW - Mathematical modeling KW - Solidification KW - Laser beam welding PY - 2020 DO - https://doi.org/10.2351/7.0000068 VL - 32 IS - 2 SP - 022024-1 EP - 022024-6 PB - AIP Publishing AN - OPUS4-50767 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bachmann, Marcel A1 - Avilov, Vjaceslav A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - High-power laser welding of austenitic stainless steel with electromagnetic control of weld pool N2 - Laser deep-penetration welding became a widely applied tool in industrial applications due to available laser power of 20 kW and more for the single-pass welding of steel plates of up to 20 mm thikness. Above a critical limit, liquid metal tends to drop out of the bead due to hydrostatic pressure. Laser welding, in contrast to electron beam welding technique, allows for an electromagnetic manipulation of fluid flow in the weld pool. AC electromagnetic system for compensation of the hydrostatic pressure by induced Lorentz forces in the melt was experimentally and numerically investigated for single-pass full-penetration welding of up to 20 mm thikness austenitic stainless steel plates of grade AISI 304. It was shown that the application of 200-234 mT magnetic fields at oscillation frequency of around 2.6 kHZ lead to a full compensation of hydrostatic forces in the melt for plate 10-20 mm thick, respectively. Coupled fluid flow, thermal and electromagnetic finite element simulations were done with different applied magnetic flux densities and oscillation frequencies calculating for the optimal magnetic field strength to avoid melt sagging in the weld pool. The simulation results point to a lower magnetic field density needed for that purpose. The reason for that can lie in the magnetic properties of the material not being totally non-ferromagnetic. 17 Ref., 1 Table, 5 Figures. KW - Laser welding KW - High power KW - Austenitic stainless steels KW - Drop out of bead KW - Control magnetic field KW - Hydrostatic force compensation KW - Modeling of fluid flow KW - Calculation PY - 2014 SN - 0957-798X VL - 3 SP - 21 EP - 24 PB - E. O. Paton Electric Welding Institute of the National Acad. of Sciences of Ukraine CY - Kyïv AN - OPUS4-30823 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bachmann, Marcel A1 - Carstensen, J. A1 - Bergmann, L. A1 - dos Santos, J. F. A1 - Wu, C. S. A1 - Rethmeier, Michael T1 - Numerical simulation of thermally induced residual stresses in friction stir welding of aluminum alloy 2024-T3 at different welding speeds N2 - The paper deals with a numerical finite element simulation of the residual stress evolution in friction stir welding of 6 mm thick aluminum alloy AA2024-T3. The transient thermal field during the welding process was calculated with the commercial code COMSOL Multiphysics 5.0. Therefore, a thermal-pseudo-mechanical (TPM) heat source was implemented. A subsequent mechanical simulation was performed with varying hardening models for different welding speeds of 60 and 300 mm/min. The influence of softening of the material, which was due to hardening precipitation dissolution associated to the heating, was also investigated. Experiments in terms of thermocouple measurements as well as Vickers hardness and X-ray measurements of the residual stresses were conducted and compared to numerically obtained results. A qualitatively as well as quantitatively good agreement was found for different applied welding speeds. KW - Friction stir welding KW - Residual stress KW - Finite element simulation KW - Thermal softening KW - Aluminum alloy 2024-T3 PY - 2017 DO - https://doi.org/10.1007/s00170-016-9793-8 SN - 0268-3768 SN - 1433-3015 VL - 91 SP - 1443 EP - 1452 PB - Springer CY - London AN - OPUS4-40511 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fritzsche, André A1 - Hilgenberg, Kai A1 - Teichmann, F. A1 - Pries, H. A1 - Dilger, K. A1 - Rethmeier, Michael T1 - Improved degassing in laser beam welding of aluminum die casting by an electromagnetic field N2 - The paper describes an experimental investigation of the electromagnetic porosity reduction in partial penetration laser beam welding of 6 mm thick aluminum die casting AlSi9MnMg. The Investigation reveals that the usage of an electromagnetic field leads to a significant reduction of the porosity as well as to a surface smoothing of aluminum die casting. Based on the reference case without an electromagnetic influence, the porosity area was reduced gradually up to 76%. Metallurgical pores as well as process pores were removed from the weld pool. Also the weld reinforcement was improved up to 78%. Best results were reached with a frequency of 4325 Hz and a magnetic flux density of 348 mT. Although a complete prevention of porosity was not achieved, the best weld seam reached a high quality and can be ranked in valuation group B of DIN EN ISO 13919-2:2001–12. KW - Laser beam welding KW - Die-cast aluminum KW - Porosity reduction KW - Electromagnetic influence PY - 2018 DO - https://doi.org/10.1016/j.jmatprotec.2017.10.021 SN - 0924-0136 VL - 253 SP - 51 EP - 56 PB - Elsevier CY - Amsterdam AN - OPUS4-42767 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yang, Keke A1 - Wang, Zhuoqun A1 - Haak, Viktor A1 - Olfert, Viktoria A1 - El-Sari, Bassel A1 - Hein, David A1 - Biegler, Max A1 - Rethmeier, Michael A1 - Meschut, Gerson T1 - A novel welding schedule for expanding the expulsion-free process window in resistance spot welding of dissimilar joints with ultra-high strength steel N2 - This study introduces a novel approach to expanding the maximum expulsion-free process window in resistance spot welding (RSW) of dissimilar joints between ultra-high strength steel (UHSS) and mild steel. Quantitative analysis revealed that expulsion is driven by the interaction between nugget growth rate and plastic shell thickness. Based on this finding, the welding schedule was optimized by applying a preheating current to form an initial plastic shell, followed by a ramp-up current profile during the main welding phase. Welding simulations indicated that the ramp-up current slowed nugget growth, improved plastic shell formation, and prevented nugget breakthrough, thereby reducing the risk of expulsion. Experimental validation showed a 19 % increase in maximum expulsion-free heat input, with the nugget diameter increasing by 7.6 % to 8.94 mm compared to the reference welding schedule. Furthermore, even when expulsion occurred beyond the process window, this optimization delayed its occurrence, minimizing its impact on spot weld quality. Finally, the optimized welding schedule also exhibited significant robustness. Despite a 2 mm initial gap disturbance, the maximum expulsionfree heat input increased by 57 %, while the nugget diameter grew by 30 % to 8.92 mm. These results confirm that the proposed approach effectively extends the process window by preventing expulsion and enhances process stability. KW - Expulsion KW - Resistance spot welding KW - Finite element modelling KW - Preheating KW - Ultra-high-strength steel PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-626877 DO - https://doi.org/10.1016/j.jmapro.2025.02.009 SN - 2212-4616 VL - 137 SP - 306 EP - 309 PB - Elsevier BV AN - OPUS4-62687 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Frei, J. A1 - Alexandrov, B. T. A1 - Rethmeier, Michael T1 - Low heat input gas metal arc welding for dissimilar metal weld overlays part II: the transition zone N2 - Dissimilar metal weld overlays (DMWOL) of nickel base alloys on low alloy steel components are commonly used in the oil and gas, petrochemical, and power generation industries to provide corrosion and oxidation resistance in a wide range of service environments and temperatures. Traditionally, dissimilar weld overlays are produced using cold or hot wire gas tungsten arc welding. This study aims to identify and evaluate potential advantages of low heat input gas metal arc welding processes over the conventional gas tungsten arc welding in the production of dissimilar weld overlays. In order to evaluate the quality of these overlays regarding resistance against hydrogen-assisted cracking, their transition zone region is investigated in this part of the publication series. Metallurgical characterization, including energy-dispersive x-ray spectroscopy, is performed on Alloy 625/grade 22 steel overlays. The transition zone is characterized by a narrow planar growth zone and steep compositional gradients from the fusion boundary towards the weld metal. Evidence of low carbon contents in the planar growth zone, as well as for carbide precipitation in the cellular growth zone was found. The microstructure in the transition zone region of the fusion zone shows characteristics known to be suitable for good resistance against hydrogen embrittlement. KW - Low heat input Gma welding KW - Dissimilar metal weld overlays KW - Coarse grained heat affected zone KW - Grain size KW - Microstructure KW - Fusion zone, nickel alloys PY - 2018 DO - https://doi.org/10.1007/s40194-017-0539-5 VL - 62 IS - 2 SP - 317 EP - 324 PB - Springer CY - Heidelberg, Germany AN - OPUS4-44721 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Heinze, Christoph A1 - Schwenk, Christopher A1 - Rethmeier, Michael A1 - Caron, J. T1 - Numerical sensitivity analysis of welding-induced residual stress depending on variations in continuous cooling transformation behavior N2 - The usage of continuous cooling transformation (CCT) diagrams in numerical welding simulations is state of the art. Nevertheless, specifications provide limits in chemical composition of materials which result in different CCT behavior and CCT diagrams, respectively. Therefore, it is necessary to analyze the influence of variations in CCT diagrams on the developing residual stresses. In the present paper, four CCT diagrams and their effect on numerical calculation of residual stresses are investigated for the widely used structural steel S355J2 + N welded by the gas metal arc welding (GMAW) process. Rather than performing an arbitrary adjustment of CCT behavior, four justifiable data sets were used as input to the numerical calculation: data available in the Sysweld database, experimental data acquired through Gleeble dilatometry tests, and TTT/CCT predictions calculated from the JMatPro and Edison Welding Institute (EWI) Virtual Joining Portal software. The performed numerical analyses resulted in noticeable deviations in residual stresses considering the different CCT diagrams. Furthermore, possibilities to improve the prediction of distortions and residual stress based on CCT behavior are discussed. KW - Welding simulation KW - GMAW KW - CCT sensitivity KW - Welding residual stress PY - 2011 DO - https://doi.org/10.1007/s11706-011-0131-7 SN - 1673-7377 SN - 1673-7482 VL - 5 IS - 2 SP - 168 EP - 178 PB - Springer ; [Beijing] : Higher Education Press CY - Secaucus, N.J. ; Heidelberg AN - OPUS4-23835 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sproesser, G. A1 - Chang, Y.-J. A1 - Pittner, Andreas A1 - Finkbeiner, M. A1 - Rethmeier, Michael T1 - Energy efficiency and environmental impacts of high power gas metal arc welding N2 - Single-wire gas metal arc welding (SGMAW) and high power tandem GMAW (TGMAW) are evaluated with respect to energy efficiency. The key performance indicator electrical deposition efficiency is applied to reflect the energy efficiency of GMAW in different material transfer modes. Additionally, the wall-plug efficiency of the equipment is determined in order to identify the overall energy consumption. The results show that energy efficiency can be increased by 24% and welding time is reduced over 50% by application of the tandem processes. A comparative life cycle assessment of a 30-mm-thick weld is conducted to investigate the influences of the energy efficiency on the environmental impacts. The environmental impacts on the categories global warming potential, acidification potential, eutrophication potential, and photochemical ozone creation potential can be reduced up to 11% using an energy-efficient TGMAW process. KW - Tandem gas metal arc welding KW - Life cycle assessment (LCA) KW - Energy efficiency KW - High power welding PY - 2017 DO - https://doi.org/10.1007/s00170-017-9996-7 SN - 0268-3768 SN - 1433-3015 VL - 91 IS - 9-12 SP - 3503 EP - 3513 PB - Springer CY - London AN - OPUS4-39564 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -