TY - CONF A1 - Graf, Benjamin A1 - Schuch, M. A1 - Kersting, R. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Additive process chain using selective laser melting and laser metal deposition T2 - LiM 2015 - Lasers in manufacturing conference 2015 N2 - Selective Laser Melting (SLM) and Laser Metal Deposition (LMD) are prominent methods in the field of additive manufacturing technology. While the powder-bed based SLM allows the manufacturing of complex structures, buildrate and part volumes are limited. In contrast, LMD is able to operate with high deposition rates on existing parts, however shape complexity is limited. Utilizing their respective strengths, a combination of these two additive technologies has the potential to produce complex parts with high deposition rates. In this paper, a process chain consisting of additive technologies SLM and LMD is described. The experiments are conducted using the alloys Ti-6Al-4V and Inconel 718. A cylindrical test specimen is produced and the microstructure along the SLM-LMD zone is described. In addition, this process chain was tested in the manufacturing of a turbine blade. The feasibility of implementing this process chain for small batch production is discussed. The results are evaluated to show advantages and limitations of the SLM-LMD process chain. This paper is relevant for industrial or scientific users of additive manufacturing technologies, who are interested in the feasibility of a SLM-LMD process chain and its potential for increased deposition rates. T2 - LiM 2015 - Lasers in manufacturing conference 2015 CY - Munich, Germany DA - 22.06.2015 KW - Macro processing KW - Additive manufacturing KW - Laser metal deposition KW - Ti-6Al-4V KW - Inconel 718 KW - Process chain KW - Deposition rate PY - 2015 SP - 1 EP - 6 AN - OPUS4-33778 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Petrat, Torsten A1 - Graf, B. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Build-up strategies for generating components of cylindrical shape with laser metal deposition T2 - Lasers in Manufacturing Conference 2015 N2 - Laser Metal Deposition LMD) as additive manufacturing process offers the potential to produce near net shape components. This reduces the amount of material and post-processing. The components are composed of individual layers. Already mall irregularities within a layer can add up over multiple layers and lead to error propagation. This paper deals with the issue of build-up strategies to minimize irregularities and prevent error propagation. Different travel paths and the influence of a changing starting point regarding to error propagation are discussed. Different deposition rates between core and peripheral area are detected and successfully compensated by adjusting the build-up sequence. Stainless steel and titanium alloy Ti-6Al-4V are used in the experiments. The results are intended to illustrate the potential of an adjusted build-up strategy and provide basic information on the way to an automated deposition process. This paper is of interest for engineers in industry or science using LMD as additive manufacturing process. T2 - Lasers in Manufacturing Conference 2015 CY - Munich, Germany DA - 22.06.2015 KW - Ti - 6Al - 4V KW - Additive Manufacturing KW - Build - up Strategy KW - Laser Metal Deposition KW - Stainless Steel PY - 2015 UR - http://www.wlt.de/lim/Proceedings/Stick/sessions.html SP - 1 EP - 6 AN - OPUS4-37829 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fabry, Cagtay A1 - Pittner, Andreas A1 - Rethmeier, Michael T1 - Datenerfassung und -analyse zur Prozessüberwachung und -regelung beim Lichtbogenschweißen T2 - Roboter 2015 N2 - Der Beitrag stellt am Beispiel eines für adaptive MSG-Lichtbogen-Engspaltschweißungen im Dickblech-Bereich entwickelten Versuchsstandes ein Automatisierungskonzept für vernetzte kommerziell verfügbare Anlagenkomponenten über ein zentrales echtzeitfähiges Steuersystem auf Basis des EtherCAT-Protokolls vor. Der Fokus liegt hierbei auf der Eignung für Aufgaben im Bereich der Qualitätssicherung sowie Forschung und Entwicklung leistungsfähiger Algorithmen zur Prozessüberwachung und -regelung. Die sich daraus ergebende Vielzahl zu messender und steuernder Parameter stellen vor allem in Verbindung mit präzisen und hochfrequenten Messgeräten höchste Anforderungen an die Datenverarbeitung sowohl in Echtzeit als auch zur Auswertung nach dem Prozess. Die Einbindung etablierter Programmiertools wie MATLAB/Simulink in gängigen Automatisierungsstandards ermöglichen flexible und innovative Forschungsarbeit. Durch die automatisierte Datenerfassung in einer übergelagerten Datenbank stehen die Messungen sämtlicher Schweißvorgänge jederzeit zur Entwicklung neuer Abläufe zur Prozessteuerung und -regelung oder zur Verbesserung der bestehenden Algorithmen zur Verfügung, was insbesondere den sukzessiven Aufbau komplexer Regressionsmodelle aus der Anwendung heraus ermöglicht. Als Applikationsbeispiel wird die Entwicklung eines dynamischen Lichtbogensensors vorgestellt und diskutiert. Die Versuchsdurchführung mit dem Ziel der Ableitung nichtlinearer Regressionsmodelle erfolgt automatisiert mithilfe eines optischen Sensors. Der Vorteil dieses Verfahrens liegt dabei neben der schnellen Umsetzbarkeit in der direkten Korrelation der Messwerte zu realen physikalischen Systemgrößen und der schnellen Adaption auf unterschiedliche Schweißparameter und -prozesse. T2 - Roboter 2015 CY - Nürnberg, Germany DA - 16.09.2015 KW - Lichtbogenschweißen KW - Prozessüberwachung PY - 2015 SN - 978-3-945023-45-7 N1 - Serientitel: DVS-Berichte – Series title: DVS-Berichte IS - 317 SP - 17 EP - 23 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-34584 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rethmeier, Michael A1 - Suwala, H. A1 - Gumenyuk, Andrey T1 - Development of a test method for determining the cracking susceptibility of resistance spot welded high strength steel sheets N2 - Test procedure to characterize the cracking susceptibility of RSW-steels has been developed During externally loaded test procedure all investigated steels (HDT780CD+Z100, HDT780C+ZE75/75, HX340LAD+Z100, HCT690TD+Z100) showed a cracking behavior With increased specimen load, the crack length grows for the micro-alloyed-steel and TRIP-steel Complex phase steels behavior during test procedure: Crack length growth with increasing force could not be determined The cracking susceptibility of electro-galvanized steels is less than hot-dip galvanized steels (in this case) 30 T2 - The METEC and 2nd European Steel Technology and Application Days (ESTAD)conference CY - Düsseldorf, Germany DA - 15.06.2015 KW - Externally loaded hot cracking test KW - Variables influencing hot cracking KW - Self-restraint hot cracking KW - Welding jig PY - 2015 AN - OPUS4-38348 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thater, R. A1 - Pittner, Andreas A1 - Rethmeier, Michael T1 - Einsatz der Schweißsimulation zur Verzugsoptimierung an Praxisbauteilen T2 - DVS Congress 2015 - Große Schweißtechnische Tagung N2 - Der Fokus des vorliegenden Beitrages liegt in der Anwendung der numerischen Schweißsimulation zur Berechnung des schweißbedingten Verzugs an industriellen Bauteilen. Anhand einiger Applikationsbeispiele werden die Möglichkeiten und Einschränkungen am Markt verfügbarer Softwareprodukte aufgezeigt. Hierbei liegt die Gewichtung in einer qualitativ korrekten Abbildung der zu analysierenden Phänomene. Diese stellt die Basis für nachfolgende Parameterstudien dar, welche signifikante Einflussgrößen auf die Verzugsausbildung detektieren. Der Vorteil derartiger simulationsgestützter Analysemethoden gegenüber rein experimentellen Ansätzen wird diskutiert. Aufgrund der heutigen Verfügbarkeit spezialisierter anwenderfreundlicher Schweißsimulationssoftware und günstiger Rechenressourcen macht die Industrie in den letzten Jahren immer mehr von den zahlreichen Vorteilen einer virtuellen Prozessauslegung mit Hilfe der Schweißsimulation Gebrauch. Komplexe Praxisanwendungen können heutzutage innerhalb von 1-2 Wochen unter Berücksichtigung aller Arbeitsschritte bearbeitet werden. Die Anforderungen an den Anwender seitens der Numerik und Materialmodellierung hat sich drastisch verringert, wohingegen ein gewisses Maß an Wissen und Erfahrung vom simulierten Prozess weiterhin entscheidend für den Erfolg der Simulation ist. Am Beispiel des Einspritzventils konnte das Potential einer virtuellen Prozessauslegung anschaulich aufgezeigt werden. T2 - DVS Congress 2015 - Große Schweißtechnische Tagung CY - Nuremberg, Germany DA - 14.09.2015 PY - 2015 SN - 978-3-945023-46-4 N1 - Serientitel: DVS-Berichte – Series title: DVS-Berichte IS - 315 SP - 892 EP - 895 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-34771 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Chang, Y.-J. A1 - Sproesser, G. A1 - Neugebauer, S. A1 - Wolf, K. A1 - Scheumann, R. A1 - Pittner, Andreas A1 - Rethmeier, Michael A1 - Finkbeiner, M. T1 - Environmental and social life cycle assessment of welding technologies JF - Procedia CIRP N2 - Life Cycle Assessment (LCA) and Social Life Cycle Assessment (SLCA) are applied in evaluating possible social and environmental impacts of the state-of-art welding technologies, such as Manual Metal Arc Welding (MMAW), Manual Gas Metal Arc Welding (GMAW), Automatic GMAW and Automatic Laser-Arc Hybrid Welding (LAHW). The LCA results indicate that for 1 meter weld seam, MMAW consumes the largest amount of resources (like filler material and coating on electrodes) and energy, which contributes to comparatively higher environmental impacts in global warming potential, acidification, photochemical ozone creation potential and eutrophication than other chosen processes. With regard to social aspects, the health issues and fair salary are under survey to compare the relative potential risk on human health caused by fumes in different welding technologies, and to indicate the sufficiency of current salary of welders in Germany. The results reflect that the wage status of welders is still fair and sufficient. The manual processes bring much higher potential risk of welders’ health than the automatic processes, especially MMAW. KW - Fair salary KW - Human health KW - Life Cycle Assessment (LCA) KW - Social Life Cycle Assessment (SLCA) KW - Welding PY - 2015 DO - https://doi.org/10.1016/j.procir.2014.07.084 SN - 2212-8271 VL - 26 SP - 293 EP - 298 PB - Elsevier CY - Amsterdam [u.a.] AN - OPUS4-33036 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rethmeier, Michael A1 - Bakir, Nasim A1 - Gumenyuk, Andrey T1 - Experimental study and numerical simulation of hot crack formation for novel laser weldability test N2 - Hot cracking susceptibility in laser beam welding was assessed for several stainless steels by means of the CTW test The strain rate has a significant influence on the formation of the hot crack It was possible to determine the critical strain and strain rate that led to shot crack formation A material ranking of hot cracking resistance could be made.A three-dimensional FEM using the contact element technique to simulate hot cracking during LBW under external load conditions was developed. Good agreement between the strain field measured using the DIC technique and the simulation results Susceptibility to hot cracking can be predicted by using FEM with the correct mechanical and thermo-physical material properties T2 - 8th International Conference Beam Technologies & Laser Application CY - St. Petersburg, Russia DA - 21.09.2015 KW - CTW-Test KW - Investigated materials KW - FEM study KW - Hot cracking PY - 2015 AN - OPUS4-38347 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rethmeier, Michael A1 - Bakir, Nasim A1 - Gumenyuk, Andrey T1 - Experimental study and numerical simulation of hot crack formation for novel laser weldability test T2 - 8th International conference "Beam technologies & laser Application T2 - 8th International conference "Beam technologies & laser Application CY - St. Petersburg, Russia DA - 2015-09-21 PY - 2015 AN - OPUS4-35020 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Experimental study and numerical simulation of hot crack formation for novel laser weldability test. T2 - BEAM TECHNOLOGIES & LASER APPLICATION Proceedings of the International scientific and technical Conference N2 - Laser beam welding is a widely established manufacturing process in several industries. The solidification cracking seriously effecting the safety of welded joints could arise during the beam welding of stainless steels caused by high solidification rates. In this study the controlled tensile weldability test (CTW) was used to investigate the solidification cracking susceptibility the fully austenitic stainless steels CrMnNi (1.4376), CrNi (1.4301), CrNiMo (1.4404) and CrNiSi (1.4828) during laser beam welding. The test facility allows welding of specimens with simultaneous application of tensile load along or cross to the welding direction while the speed of tensile force application is either constant or increases linearly. The tensile force increment and/or the displacement are set by means of a CNC controller. Trials were conducted by varying the ultimate tensile strain and cross-head speed while keeping the welding parameters constant. By observing the crack-no crack behaviour and estimating the generated crack length for each trail using a new optimized experimental procedure the influence of the two important conditions (the strain and the strain rate) for the formation of solidification cracks can be investigated, the critical values of strain and strain rate that are responsible for solidification cracking formation have been determined. In the present study a three-dimensional FEM using the contact element technique was developed to simulate the solidification cracking during laser full penetration welding under external load conditions for the steel 1.4376 in order to get a better understanding of the mechanisms of hot crack initiation and the theoretical results were compared to the experimental ones. By comparing the resulting solidification crack with simulated crack, it is possible to determine the critical condition of solidification crack formation in the region where the strains and the strain rates cannot be measured due to the high temperature. The results show a good agreement between numerical calculation and experiment. It is proposed that the solidification cracking susceptibility may be predicted by FEM analysis by using the correct mechanical and thermo-physical constants of the materials. T2 - BEAM TECHNOLOGIES & LASER APPLICATION CY - St. Petersburg, Russia DA - 21.09.2015 KW - Solidification cracking KW - Hot cracking test KW - FEM KW - Laser beam welding PY - 2015 SN - 978-5-7422-5150-7 SP - 55 EP - 68 AN - OPUS4-36615 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bachmann, Marcel A1 - Kunze, R. A1 - Avilov, Vjaceslav A1 - Rethmeier, Michael T1 - Finite element modelling of an AC electromagnetic weld pool support in full penetration laser beam welding of thick duplex stainless steel plates T2 - ICALEO 2015 - 34th International congress on applications of lasers & electro-optics (Proceedings) N2 - An electromagnetic weld pool support system for 20 mm thick duplex stainless steel AISI 2205 was investigated numerically and compared to experiments. In our former publications, it was shown how an AC magnetic field below the process zone directed perpendicular to the welding direction can induce vertically directed Lorentz forces. These can counteract the gravitational forces and allow for a suppression of material drop-out for austenitic stainless steels and aluminum alloys. In this investigation, we additionally adopted a steady-state complex magnetic permeability model for the consideration of the magnetic hysteresis behavior due to the ferritic characteristics of the material. The model was calibrated against the Jiles-Atherton model. The material model was also successfully tested against an experimental configuration before welding with a 30 mm diameter cylinder of austenitic stainless steel surrounded by duplex stainless steel. Thereby, the effects of the Curie temperature on the magnetic characteristics in the vicinity of the later welding zone were simulated. The welding process was modelled with a 3D turbulent steady-state model including heat transfer and fluid dynamics as well as the electromagnetic field equations. Main physical effects, the thermo-capillary (Marangoni) convection at the weld pool boundaries, the natural convection due to gravity as well as latent heat of solid–liquid phase transitions at the phase boundaries were accounted for in the model. The feedback of the electromagnetic forces on the weld pool was described in terms of the electromagneticinduced pressure. The FE software COMSOL Multiphysics 4.2 was used in this investigation. It is shown that the gravity drop-out associated with the welding of 20 mm thick duplex stainless steel plates due to the hydrostatic pressure can be prevented by the application of AC magnetic fields between around 70 mT and 90 mT. The corresponding oscillation frequencies were between 1 kHz and 10 kHz and the electromagnetic AC powers were between 1 kW and 2.3 kW. In the experiments, values of the electromagnetic AC power between 1.6 kW and 2.4 kW at oscillation frequencies between 1.2 kHz and 2.5 kHz were found to be optimal to avoid melt sagging or drop-out of melt in single pass fullpenetration laser beam welding of 15 mm and 20 mm thick AISI 2205. T2 - ICALEO 2015 - 34th International congress on applications of lasers & electro-optics CY - Atlanta, GA, USA DA - 2015-10-18 KW - Electromagnetic weld pool support KW - Laser beam welding KW - FE simulation KW - Duplex stainless steel PY - 2015 SN - 978-1-940168-05-0 SP - 650 EP - 659 AN - OPUS4-35036 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Uhlmann, E. A1 - Rethmeier, Michael A1 - Graf, B. A1 - Kersting, R. A1 - Bergmann, A. T1 - Flexible manufacturing with an additive process chain design, production and surface finish T2 - ASPE Spring topical meeting - Achieving precision tolerances in additive manufacturing (Proceedings) N2 - The industrial demand for flexible and innovative manufacturing technologies is continuously increasing. These technologies have to be sustainable and resource-efficient, and have to allow the production of long-life capital goods. Consequently, the additive processes gain in importance as they offer an enormous potential of application, especially for the turbomachinery industry. In order to use additive manufacturing technologies in industrial applications, it is necessary to consider the complete process chain, including all necessary pre- and postprocessing. Although additive manufacturing is increasingly covered in scientific research, the linking between this technology and conventional industrial processes is rarely described. T2 - ASPE Spring topical meeting - Achieving precision tolerances in additive manufacturing CY - Raleigh, NC, USA DA - 26.04.2015 PY - 2015 SN - 978-1-887706-67-4 SP - Session I, 5 EP - 9 AN - OPUS4-34855 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Na, S.-J. A1 - Han, S.-W. A1 - Muhammad, S. A1 - Zhang, L. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael A1 - Karhu, M. A1 - Kujanpa, V. T1 - Flow and Bead Formation Characteristics in High Power Laser Welding at Different Welding Positions (Invited Talk) T2 - Lasers in Manufacturing Conference 2015 N2 - The numerical simulations of high power laser keyhole welding at different welding positions are performed by using Volume-Of-Fluid (VOF) method. The main material is SS400. The multi-physics phenomenon is considered using several models, such as the heat flux of Gaussian heat source, the recoil pressure with Clausisus-Clapeyron equation, the Marangoni flow considering temperature gradient, the buoyancy force with Boussinesq approximation, the additional shear stress and heat source due to metallic vapor ejected through keyhole entrance, the bubble formation assumed as adiabatic bubble, and the multiple-reflection by solving proper discriminant, are used. To analyze the fluid flow pattern, the concept of streamline formed by reconstructing the value of the velocity vector is applied. Partial and full penetration cases at different welding positions are considered. The welding position seems to have only a minor influence on bead formation characteristics in both cases. This is probably due to the fact that the recoil pressure has a major influence when compared to other driving forces. The flow characteristics and fluid velocity in weld pool are analyzed to compare the gravity direction effect at different welding positions. It is observed that the clockwise flow pattern is mainly formed by the recoil pressure on the keyhole surface in the case of partial penetration. The laser energy can't maintain the whole weld pool when the weld pool size becomes too large. And then the solidification starts from the middle part of weld pool and a necked weld pool shape is formed. In the full penetration welding, the weld pool flow patterns are affected by the leakage of laser power through the full penetration keyhole and also by surface tension. Furthermore, the numerical simulation of full penetration welding with AISI316L is also performed to analyze the effect of material properties. The weld bead shapes obtained by simulations were compared with the corresponding experimental results to confirm the validity of the process models adopted and the CFD simulation tool. T2 - Lasers in Manufacturing Conference 2015 CY - München, Germany DA - 22.06.2015 KW - Macro Processing (Joining, Welding) KW - Weld pool KW - Flow pattern KW - Different welding position KW - Numerical simulation KW - High power laser keyhole welding PY - 2015 SP - 1 EP - 6 AN - OPUS4-37163 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Avilov, Vjaceslav A1 - Fritzsche, André A1 - Bachmann, Marcel A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Full penetration laser beam welding of thick duplex steel plates with electromagnetic weld pool support T2 - ICALEO 2015 - 34th International congress on applications of lasers & electro-optics (Proceedings) N2 - Full penetration high power bead-on-plate laser beam welding tests of up to 20 mm thick 2205 duplex steel plates were performed in PA position. A contactless inductive electromagnetic (EM) weld pool support system was used to prevent gravity drop-out of the melt. Welding experiments with 15 mm thick plates were carried out using IPG fiber laser YLR 20000 and Yb:YAG thin disk laser TruDisk 16002. The laser power needed to achieve a full penetration was found to be 10.9 and 8.56kW for welding velocity of 1.0 and 0.5 m min(-1), respectively. Reference welds without weld pool support demonstrate excessive root sag. The optimal value of the alternating current (AC) power needed to completely compensate the sagging on the root side was found to be approximate to 1.6 kW for both values of the welding velocity. The same EM weld pool support system was used in welding tests with 20 mm thick plates. The laser beam power (TRUMPF Yb:YAG thin disk laser TruDisk 16002) needed to reach a full penetration for 0.5 m min(-1) was found to be 13.9 kW. Full penetration welding without EM weld pool support is not possible-the surface tension cannot stop the gravity drop-out of the melt. The AC power needed to completely compensate the gravity was found to be 2 kW. (C) 2016 Laser Institute of America T2 - ICALEO 2015 - 34th International congress on applications of lasers & electro-optics CY - Atlanta, GA, USA DA - 2015-10-18 KW - Electromagnetic weld pool support KW - Laser beam welding KW - Duplex stainless steel PY - 2015 SN - 978-1-940168-05-0 SP - 571 EP - 579 PB - Amer inst physics CY - Melville, NY, USA AN - OPUS4-35035 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Investigation of hot crack susceptibility of laser welded joints of four austenitic steels T2 - European Steel Technology and Application Days N2 - Laser welding is a widely established manufacturing process in many industry sectors. Solidification cracking represents one of the most inadequately solved problems in welding and has major economic implications. The avoidance of hot crack is for most fusion welding processes a key challenge for an important range of metallic construction materials and affects not only the manufacturers of welding equipment and material manufacturers, but also a large number of customers using welding technologies, as well as welding standardization and research. In this study a new investigation programme has been developed to qualify the hot cracking susceptibility of a variety of austenitic stainless steels. The results show the possibility of using this technique to determinate the critical values that occur with initiation of solidification cracking during laser beam welding T2 - The METEC and 2nd European Steel Technology and Application Days CY - Düsseldorf, Germany DA - 15.06.2015 KW - Laser beam welding KW - Hot cracking KW - Solidification cracking KW - Hot cracking test PY - 2015 SP - 1 EP - 5 AN - OPUS4-36525 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Investigation of solidification cracking susceptibility of laser welded joints of austenitic stainless steels T2 - Welding and failure analysis of engineering materials (WAFA-2015) N2 - Laser welding is a widely established manufacturing process in many industry sectors. Solidification cracking represents one of the most inadequately solved problems in welding and has major economic implications. The avoidance of hot crack forms for most fusion welding processes poses a key challenge for an important range of metallic construction materials and affects not only the manufacturers of welding equipment and material manufacturers, but also a large number of customers using welding technologies, as well as welding technical standardization and research. Solidification cracking susceptibility was examined with the help of the Controlled Tensile Weldability Test (CTW) developed by Federal Institute for Materials Research and Testing (BAM), Berlin. The test is based on the fact that hot crack formation depends on a critical strain that emerges within a critical temperature range, the so called brittle temperature range (BTR). Using this test and defined investigation programme a centreline solidification crack was generated. By controlling the applied strain during the laser beam welding process, it was possible to determine the critical strain and strain rate that led to solidification cracking formation. The hot cracking susceptibility of the tested stainless steels was qualified and quantified. The results demonstrate that the crack length increases with increasing applied strain. Furthermore, the strain rate has a significant influence on the formation of the solidification crack. T2 - 3rd International conference in Africa and Asia CY - Luxor, Egypt DA - 02.11.2015 KW - Laser beam welding KW - Hot cracking KW - Solidification cracking KW - Hot cracking test PY - 2015 SP - A-29, 1 EP - A-29, 9 AN - OPUS4-36522 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schneider, André A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Laser beam welding of thick materials under the influence of local reduced ambient pressure T2 - VIII BTLA 2015 - 8th International conference "Beam technologies & laser application" N2 - The development of the vapour plume during the laser beam welding of metals with propagation directions along the laser beam axis leads to a reduction of the absorbed laser power in the keyhole. The main reasons are the scattering of the laser radiation on the condensed phase of metallic vapour as well as the defocusing of the laser beam due to the density gradient in the vapour plume. These unfavourable effects can be significantly mitigated by the application of a reduced ambient pressure thus decreasing the interaction between the laser beam and evaporation products, which leads to more stable welding process and results in increased penetration depth, as known from previous studies. A conventional technique use a vacuum chamber principle, similar to that, used for electron beam welding. Application of this technique is restricted by the chamber size and reduces thus the advantages of this approach especially for large components. We demonstrate a possibility of mobile local vacuum application, which allows to generate a reduced pressure only in small region around the keyhole. By using of specially designed mobile pressure lock which can be moved along the welding direction absolute pressure of around 200 mbar could be obtained. This is sufficient to increase the welding depth by around 50%. Coupons from S355 were welded with an incremental laser power from 5 kW to 12 kW at atmospheric pressure and compared to those welded at ambient pressure of 200 mbar. The evaluation of the longitudinal section revealed an increase of the welding depth by about 35%. Furthermore, the welding trials in butt joint configuration on 15 mm thick plates at various laser beam power performed for atmospheric and reduced ambient pressure of around 200 mbar. The increase in welding depth up to 40% was established for reduced pressure. Particularly, low welding speeds under reduced pressure were especially advantageous in terms of increasing the welding depth. T2 - VIII BTLA 2015 - 8th International conference "Beam technologies & laser application" CY - St. Petersburg, Russia DA - 21.09.2015 KW - High power laser beam welding KW - Mobile vacuum KW - Local reduced pressure KW - Vapour plume KW - Keyhole PY - 2015 SP - 45 EP - 46 AN - OPUS4-34973 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rethmeier, Michael A1 - Gook, S. A1 - Gumenyuk, Andrey T1 - Laser-GMA-hybrid welding of longitudinally welded large-diameter pipes of grades API- X80/ X120 N2 - Potentials of the hybrid laser arc welding processes were investigated regarding reliable production of longitudinal welds of high strength pipe steels X80 and X120 Hybrid laser arc welding of the root pass: Significant reduction in the weld cross section – savings of filler material Lower heat input into the base material - improvement of mechanical properties of the weld joint  The arc type does not have any influence on the character of dilution in the laser part of the hybrid weld  14 mm deep root face was considered as optimum. No penetration of the filler material could be detected beyond this depth limit Metal powder filler wires, micro alloyed with Ni and partly with Cr and Mo, guaranteed sufficient Charpy impact toughness at low temperature for the both investigated materials: Hybrid laser arc welding is a very efficient process for the root pass in multi-pass welding and opens a large technical and economic potential for the manufacture of large pipes T2 - The METEC and 2nd European Steel Technology and Application Days (ESTAD)conference CY - Düsseldorf, Germany DA - 15.06.2015 KW - High power laser KW - Hybrid laser arc welding KW - Weld specimens KW - Charpy V-notch tests KW - Tensile tests PY - 2015 AN - OPUS4-38342 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sproesser, G. A1 - Chang, Y.-J. A1 - Pittner, A. A1 - Finkbeiner, M. A1 - Rethmeier, Michael T1 - Laser-MSG-Hybridschweissen und die Ökobilanz: Sieg nach Punkten JF - Laser community - das Laser-Magazin von Trumpf PY - 2015 UR - http://www.laser-community.com/de/11945 IS - 21 SP - 6 PB - Trumpf GmbH + Co. KG CY - Ditzingen AN - OPUS4-35252 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sproesser, Gunther A1 - Chang, Ya-Ju A1 - Pittner, Andreas A1 - Rethmeier, Michael A1 - Finkbeiner, Matthias T1 - Laser-MSG-Hybridschweißen und die Ökobilanz: Sieg nach Punkten JF - Laser Community N2 - Es ist ein Naturgesetz: Mit der verarbeiteten Blechdicke steigt der Zeit-, Material- und Energiebedarf beim Fügen überproportional. Aber ist das noch umweltverträglich ? Dieser Frage stellte sich Gunther Sproesser mit seinen Kollegen an der Technischen Universität Berlin. KW - MSG-Schweißen KW - Hochleistungsschweißen KW - Ökobilanz KW - Laser-MSG-Hybridschweißen PY - 2015 UR - http://www.laser-community.com/de/schweiss-verfahren-im-oeko-check/ N1 - In Deutsch und Englisch erschienen. Titel in English: "A win on points: LAHW/GMAW welding tops life-cycle analysis study" IS - 21/November 2015 SP - 6 EP - 6 AN - OPUS4-35438 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Petrat, T. A1 - Graf, B. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Laser-Pulver-Auftragschweißen zum additiven Aufbau komplexer Formen T2 - DVS Congress 2015 - Große Schweißtechnische Tagung N2 - Das Laser-Pulver-Auftragschweißen als additives Fertigungsverfahren ermöglicht einen endformnahen Aufbau von Bauteilen. Ein Zielkonflikt besteht zwischen der Forderung nach hoher Aufbaurate und hoher Endformnähe, welcher von der Schweißraupengröße wesentlich beeinflusst wird. In dieser Veröffentlichung wird das Laser-Pulver-Auftragschweißen eingesetzt, um komplexe Formen additiv aufzubauen. Am Beispiel eines Tannenbaumprofiles werden unterschiedliche Einflussfaktoren dargestellt. Dazu gehören die Raupengeometrie, die Überlappung einzelner Raupen, die Verwendung unterschiedlicher Aufbaustrategien und die Teilung des Gesamtkörpers in Teilkörper. Der Zielkonflikt wird durch die Herstellung von Probekörpern mit unterschiedlichen Steigungswinkeln an den Seitenflächen verdeutlicht. Die Ergebnisse zeigen eine verbesserte Endformnähe in Bereichen flacher Steigung beim Einsatz kleiner Schweißraupen. Im Vergleich dazu erlauben die Schweißparameter der großen Raupen eine 5-fach höhere Aufbaurate. Bei einer Raupenüberlappung kleiner und großer Raupengeometrien innerhalb einer Lage treten Anbindungsfehler auf. Strategien zur Behebung dieses Fehlers durch Anpassung der Schweißreihenfolge werden in dieser Veröffentlichung aufgezeigt. Diese Erfahrungen werden genutzt, um einen Gesamtkörper aus Teilkörpern unterschiedlicher Raupengeometrien zu fertigen. T2 - DVS Congress 2015 - Große Schweißtechnische Tagung CY - Nuremberg, Germany DA - 14.09.2015 PY - 2015 SN - 978-3-945023-46-4 N1 - Serientitel: DVS-Berichte – Series title: DVS-Berichte IS - 315 SP - 126 EP - 129 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-34770 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -