TY - JOUR A1 - Nies, Daniel A1 - Pulz, Robert A1 - Glaubitz, Steffen A1 - Finn, Monika A1 - Rehmer, Birgit A1 - Skrotzki, Birgit T1 - Testing of thermal barrier coatings by laser excitation N2 - Thermal barrier coatings (TBCs) are used to increase the operating temperature of land-, sea-, or air-based turbines. As failure of the coating may result in serious damage of the turbine, reliable estimation of the lifetime is essential. Most experiments to assess the lifetime or to determine parameters for simulations of the behavior of TBCs are done by burner-rig-tests, where the operating conditions are simulated by cyclic heating of the surface and cooling of the backside of a coated sample. In this work a possibility is presented to do comparable experiments by heating the surface with laser irradiation instead of a burner. For this purpose a Nd:YAG-laser with a maximum output power of 1?kW and a wavelength of 1064?nm is used. The laser spot can be moved by integrated optics across the sample surface to achieve homogeneous heating of the coating. Cooling of the backside is done by air. The temperature of the sample surface is determined by an infrared-camera which also enables the possibility to detect failures in the coating via thermography. Additionally, acoustic sensors attached to the sample holder are used to detect failures in the sample. The investigated ceramic material (yttria stabilized zirconia) has a very low absorption coefficient at the used laser wavelength. Therefore, a pre-treatment of the samples was needed to increase the absorption coefficient to be able to heat up the samples. In this paper, the experimental setup and first experimental results are presented. KW - Thermal barrier coating (TBC) KW - Yttria stabilized zirconia KW - Laser irradiation KW - Acoustic emission KW - Thermography PY - 2010 DO - https://doi.org/10.1002/adem.201000212 SN - 1438-1656 VL - 12 IS - 12 SP - 1224 EP - 1229 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-22896 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Skrotzki, Birgit A1 - Uckert, Danilo A1 - Kühn, Hans-Joachim A1 - Matzak, Kathrin A1 - Rehmer, Birgit ED - Grellmann, W. ED - Frenz, H. T1 - Ermüdungsverhalten des warmfesten austenitischen Gusseisens EN-GJSA-XNiSiCr35-5-2 bei hoher Temperatur T1 - Fatigue behavior of the heat resistant austenitic cast iron EN-GJSA-XNiSiCr35-5-2 at high temperature N2 - Das Ermüdungsverhalten des austenitischen Gusseisens EN-GJSA-XNiSiCr35-5-2 mit Kugelgraphit wurde mittels LCF- und TMF-Versuchen bei hoher Temperatur charakterisiert. Neben der Lebensdauer wurden das zyklische Ver- und Entfestigungsverhalten und das zyklische Spannungs- Dehnungs-Verhalten untersucht. Die Ergebnisse zeigen einen deutlichen Einfluss der Temperatur auf die Festigkeit und das isotherme Ermüdungsverhalten. Dies gilt für die Ermüdungslebensdauer ebenso wie für das Wechselverformungsverhalten. Das TMF-Verhalten wird von der gewählten Maximaltemperatur bestimmt. Der Einfluss der Phasenlage ist bei dem hier untersuchten Werkstoff deutlich weniger ausgeprägt als z.B. bei einem ebenfalls untersuchten ferritischen Gusseisen vom Typ SiMo. N2 - The fatigue behavior of the austenitic ductile cast iron EN-GJSA-XNiSiCr35-5-2 was characterized by LCF and TMF tests at high temperature. Beside the lifetime, the cydic hardening and softening behavior as well as the cydic stress strain behavior were studied. The results show a distinct effect of the temperature on strength and on isothermal fatigue behavior. This is true for fatigue life as well as for the cydic deformation behavior. The TMF behavior is determined by the chosen maximum temperature. The effect of the phase angle, is deariy less pronounced than e.g. in the likewise investigated ferritic ductile cast iron of type SiMo. T2 - Tagung Werkstoffprüfung 2014 - Fortschritte in der Werkstoffprüfung für Forschung und Praxis - Werkstoffeinsatz, Qualitätssicherung und Schadensanalyse CY - Berlin, Germany DA - 04.12.2014 KW - EN-GJSA-XNiSiCr35-5-2 KW - LCF KW - TMF KW - Ermüdung bei hoher Temperatur KW - Fatigue at high temperature PY - 2014 SN - 978-3-9814516-8-9 SN - 1861-8154 SP - 61 EP - 66 AN - OPUS4-32223 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Uckert, Danilo A1 - Matzak, Kathrin A1 - Kühn, Hans-Joachim A1 - Rehmer, Birgit A1 - Peter, Frauke A1 - Fedelich, Bernard A1 - Falkenberg, Rainer A1 - Haftaoglu, Cetin A1 - Kindrachuk, Vitaliy A1 - Skrotzki, Birgit T1 - TMF-Lebensdauerberechnung ATL-Heißteile II - Erweiterung bestehender Werkstoff- und Rechenmodelle zur Lebensdauervorhersage für Abgasturbolader-Heißteile unter thermomechanischer Ermüdungsbeanspruchung (Abschlussbericht) N2 - In diesem Forschungsvorhaben erfolgte eine Überprüfung der Übertragbarkeit der Werkstoff- und Rechenmodelle für die Lebensdauervorhersage von ATL-Heißteilen unter TMF-Beanspruchung auf eine andere Werkstoffklasse als im Vorgängervorhaben, d.h. auf das austenitische Gusseisen EN-GJSA-XNiSiCr35-5-2 (Ni-Resist D-5S). Zunächst wurde dafür eine experimentelle Datenbasis geschaffen, da diese vor Beginn des Vorhabens nicht ausreichend war. Dazu wurden Zug-, Kriech-, LCF- und TMF-Versuche durchgeführt, die der Kalibrierung der Modelle dienten. Das Spannungs-Verformungs-Verhalten und die Lebensdauer in den LCF- und TMF-Versuchen werden durch das Modell auch für den neuen Werkstoff überwiegend gut beschrieben. LCF-Versuche mit Haltezeit bei 900 °C sowie IP-TMFVersuche mit einer Obertemperatur von 900 °C werden weniger gut vorhergesagt, da sich der Schädigungsmechanismus ändert. Eine Verifikation des Modells erfolgte mit Hilfe eines Bauteilversuchs an einem Abgassammler. Die überwiegende Anzahl der experimentell ermittelten Rissorte wurden von dem Modell vorhergesagt. Ein wesentliches Ziel des Vorhabens war, den Einfluss von HCF-Schwingungen auf die TMF-Lebensdauer vertieft experimentell zu untersuchen und das bereits bestehende Lebensdauermodell auf HCF-Überlagerung zu erweitern. Es wurde ein bruchmechanisch motivierter Ansatz entwickelt, in dem die Lebensdauerminderung durch die im TMF-Zyklus überlagerten HCF-Schwingungen abgebildet wird. Mit diesem Ansatz lassen sich die Lebensdauern sowohl für den Werkstoff SiMo 4.05 als auch für den Ni-Resist in guter Übereinstimmung mit dem Experiment Vorhersagen. Das Ziel des Forschungsvorhabens ist erreicht worden. PY - 2015 IS - 1082 SP - 1 EP - 168 CY - Frankfurt/Main AN - OPUS4-35112 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pulz, Robert A1 - Rehmer, Birgit A1 - Schneider, G.A. A1 - Skrotzki, Birgit T1 - Thermal shock study on different advanced ceramics by laser irradiation in different media N2 - The thermal shock behavior of three commercial-advanced ceramics (SSiC, MgO–PSZ, Al2O3) is characterized in air and vacuum applying a laser thermal shock. The available testing system permits the reproducible setting of defined temperature profiles in thin disks and allows a heating-up thermal shock in various media. Due to the accurate determination of the time- and space-resolved temperature distribution, the local stress state can be calculated as a function of time. It is shown that the thermal shock strength is highest for SSiC and lowest in Al2O3 with MgO–PSZ in between. The approach presented in this work allows quantifying the stress state at failure in terms of tangential tensile stress. The investigated environment does not affect the thermal shock resistance under the studied experimental conditions. KW - Laser-thermal shock KW - Advanced ceramic KW - Stress distribution KW - Thermal shock stress KW - Weibull statistics PY - 2016 UR - http://onlinelibrary.wiley.com/doi/10.1002/adem.201500162/full DO - https://doi.org/10.1002/adem.201500162 SN - 1438-1656 VL - 18 IS - 1 SP - 132 EP - 140 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-33456 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Rehmer, Birgit A1 - Bayram, Faruk A1 - Ávila Calderón, Luis A1 - Mohr, Gunther A1 - Skrotzki, Birgit T1 - BAM reference data: Temperature-dependent Young's and shear modulus data for additively and conventionally manufactured variants of Ti-6Al-4V N2 - The elastic properties (Young's modulus, shear modulus) of titanium alloy Ti-6Al-4V were investigated between room temperature and 400 °C in an additively manufactured variant (laser-based directed energy deposition with powder as feedstock, DED-LB/M) and from a conventional process route (hot rolled bar). The moduli were determined using the dynamic resonance method. The data set includes information on processing parameters, heat treatments, microstructure, grain size, specimen dimensions and weight, Young’s and shear modulus as well as their measurement uncertainty. The dataset was generated in an accredited testing lab using calibrated measuring equipment. The calibrations meet the requirements of the test procedure and are metrologically traceable. The dataset was audited as BAM reference data. KW - Elastic modulus KW - Young's modulus KW - Shear modulus KW - Additive manufacturing KW - Ti-6Al-4V PY - 2023 DO - https://doi.org/10.5281/zenodo.7813732 PB - Zenodo CY - Geneva AN - OPUS4-57286 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pulz, Robert A1 - Rehmer, Birgit A1 - Skrotzki, Birgit T1 - Pyrometric temperature measurement of ceramic thermal shock samples N2 - The determination of critical failure parameters during thermal shock requires a time and space resolved temperature measurement of the sample. High frequency pyrometry is a suitable technique for such a measurement task, which usually requires the knowledge of the optical properties of the investigated material. Another challenge is the infrared transparency of materials to be checked in the wavelength range of the pyrometer. The thermal shock disks are very thin, due to the need of homogeneous temperature distribution and to maintain a two-dimensional problem. To allow a pyrometric temperature measurement a universal calibration method for high frequency infrared cameras has been developed. Pyrometry in various media was demanded, as well as the estimation of optical properties (reflection, transmittance and emission) for the selected ceramics to be tested. KW - Temperature measurement KW - Ceramics KW - Emission coefficient KW - Radiation thermometry KW - Thermal shock PY - 2011 DO - https://doi.org/10.1016/j.measurement.2010.09.050 SN - 0263-2241 SN - 1873-412X VL - 44 IS - 1 SP - 259 EP - 266 PB - Elsevier Ltd. CY - London AN - OPUS4-22474 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bhadeliya, Ashok A1 - Rehmer, Birgit A1 - Fedelich, Bernard A1 - Jokisch, T. A1 - Skrotzki, Birgit A1 - Olbricht, Jürgen T1 - Fatigue and fracture in dual-material specimens of nickel-based alloys fabricated by hybrid additive manufacturing N2 - The integration of additive manufacturing with traditional processes, termed hybrid additive manufacturing, has expanded its application domain, particularly in the repair of gas turbine blade tips. However, process-related defects in additively manufactured materials, interface formation, and material property mismatches in dual-material structures can significantly impact the fatigue performance of components. This investigation examines the low cycle fatigue and fatigue crack growth behaviors in dual-material specimens of nickel-based alloys, specifically the additively manufactured STAL15 and the cast alloy 247DS, at elevated temperatures. Low cycle fatigue experiments were conducted at temperatures of 950 °C and 1000 °C under a range of strain levels (0.3%–0.8%) and fatigue crack growth tests were conducted at 950 °C with stress ratios of 0.1 and −1. Fractographic and microscopic analyses were performed to comprehend fatigue crack initiation and crack growth mechanisms in the dual-material structure. The results consistently indicated crack initiation and fatigue fracture in the additively manufactured STAL15 material. Notably, fatigue crack growth retardation was observed near the interface when the crack extended from the additively manufactured STAL15 material to the perpendicularly positioned interface. This study highlights the importance of considering yield strength mismatch, as well as the potential effects of residual stresses and grain structure differences, in the interpretation of fatigue crack growth behavior at the interface. KW - Hybrid additive manufacturing KW - Dual-material nickel-based alloys KW - High-temperature fatigue crack growth KW - Low cycle fatigue PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-609340 DO - https://doi.org/10.1016/j.jmrt.2024.08.211 SN - 2238-7854 VL - 32 SP - 3737 EP - 3749 PB - Elsevier B.V. AN - OPUS4-60934 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sonntag, Nadja A1 - Piesker, Benjamin A1 - Ávila Calderón, Luis A1 - Mohr, Gunther A1 - Rehmer, Birgit A1 - Agudo Jácome, Leonardo A1 - Hilgenberg, Kai A1 - Evans, Alexander A1 - Skrotzki, Birgit T1 - Tensile and Low‐Cycle Fatigue Behavior of Laser Powder Bed Fused Inconel 718 at Room and High Temperature N2 - This study investigates the room‐ and high‐temperature (650 °C) tensile and low‐cycle‐fatigue behavior of Inconel 718 produced by laser powder bed fusion (PBF‐LB/M) with a four‐step heat treatment and compares the results to the conventional wrought material. The microstructure after heat treatment is characterized on different length scales. Compared to the wrought variant, the elastic and yield properties are comparable at both test temperatures while tensile strength, ductility, and strain hardening capacity are lower. The fatigue life of the PBF‐LB/M variant at room temperature is slightly lower than that of the wrought material, while at 650 °C, it is vice versa. The cyclic stress response for both material variants is characterized by cyclic softening, which is more pronounced at the higher test temperature. High strain amplitudes (≥0.7%) at room temperature and especially a high testing temperature result in the formation of multiple secondary cracks at the transitions of regions comprising predominantly elongated grain morphology and columns of stacked grains with ripple patterns in the PBF‐LB/M material. This observation and pronounced crack branching and deflection indicate that the cracks are controlled by sharp micromechanical gradients and local crystallite clusters. KW - Additive manufacturing KW - Fatigue damage KW - Heat treatment KW - Inconel 718 KW - Laser powder bed fusion KW - Low-cycle fatigue KW - Tensile strength PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-599316 DO - https://doi.org/10.1002/adem.202302122 SN - 1527-2648 SP - 1 EP - 17 PB - Wiley AN - OPUS4-59931 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bhadeliya, Ashok A1 - Rehmer, Birgit A1 - Fedelich, Bernard A1 - Jokisch, T. A1 - Skrotzki, Birgit A1 - Olbricht, Jürgen T1 - Fatigue crack growth behavior of Alloy 247DS brazed joints at high temperatures N2 - Gas turbine components made of nickel-based alloys can be repaired through diffusion brazing. However, process-induced imperfections, defects within the brazing zone, and material property mismatches between the braze alloy and base material may facilitate crack initiation and propagation, ultimately leading to early component failure. To gain insight into the crack growth mechanism and quantitatively characterize fatigue crack growth behavior within brazing zones, fatigue crack growth (FCG) experiments were conducted on brazed joint specimens of nickel-based alloy Alloy 247DS at a temperature of 950 ◦C and a stress ratio R = 0.1. The FCG tests were complemented by fractographic and microstructural analyses, to elucidate the relationship between crack growth mechanisms and the microstructure of the brazed joint. The results demonstrate stable crack propagation within the brazing zone and the nickel-based braze alloy. The latter contains brittle eutectic boride phases and intermetallic phases that reduce the resistance to crack propagation compared to the parent material. This study demonstrates the applicability of standard FCG experimental procedures to fusion zones, thereby enabling a preliminary understanding of crack growth behavior in brazing zones. KW - Diffusion brazing KW - High-temperature fatigue crack growth KW - Nickel-based alloys KW - Alloy 247DS PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-615250 DO - https://doi.org/10.1016/j.msea.2024.147488 SN - 0921-5093 VL - 918 SP - 1 EP - 15 PB - Elsevier B.V. AN - OPUS4-61525 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rehmer, Birgit A1 - Finn, Monika A1 - Uhlemann, Patrick A1 - Skrotzki, Birgit A1 - Scheuerlein, C. ED - Frenz, H. ED - Langer, B. T1 - Vergleichende Bewertung verschiedener Verfahren der E-Modulbestimmung für metallische Werkstoffe N2 - Für numerische Beanspruchungs- und Lebensdaueranalysen ist die Kenntnis des E-Moduls der eingesetzten Werkstoffe von zentraler Bedeutung. Für seine experimentelle Bestimmung wurden eine Vielzahl von Verfahren entwickelt, die zum Teil werkstoffspezifisch Eingang in die Normung gefunden haben. Prinzipiell können diese Verfahren in zwei Gruppen eingeteilt werden - die statischen und die dynamischen Prüfverfahren. Während die statischen Verfahren auf der direkten Messung des Spannungs-Dehnungs-Zusammenhangs während einer Belastung im elastischen Verformungsbereich beruhen (Zug-, Biege- bzw. Druckversuch) nutzen die dynamischen Verfahren die Analyse der resultierenden Schwingungen nach einer entsprechenden Anregung eines Prüfkörpers (Resonanz- bzw. Impulsanregungsmethode). Für verschiedene Werkstoffe wurden statische und dynamische Verfahren zur E-Modulbestimmung eingesetzt. Die Unterschiede und Vorteile der verschiedenen Verfahren werden vergleichend diskutiert. T2 - Tagung Werkstoffprüfung 2017 CY - Berlin, Germany DA - 30.11.2017 KW - E-Modul KW - Zugversuch KW - Druckversuch KW - Resonanzmethode KW - Impuls-Anregungsmethode PY - 2017 SN - 978-3-9814516-7-2 SN - 1861-8154 SP - 217 EP - 224 PB - Deutscher Verband für Materialforschung und -prüfung CY - Berlin AN - OPUS4-43255 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Singh, Shobhit Pratap A1 - Löwe, Peter A1 - Schriever, Sina A1 - Olbricht, Jürgen A1 - Rehmer, Birgit A1 - Nolze, Gert A1 - Skrotzki, Birgit T1 - High-throughput creep evaluation of IN738LC in bending using digital image correlation at 850 °C N2 - High-temperature alloys, when used in structural applications, undergo slow time-dependent deformation known as creep. Assessing creep behavior is critical for estimating the in-service life of these alloys. Conventionally, uniaxial creep tests are widely conducted at elevated temperatures to determine creep rates. In recent years, bending creep of cantilevers, when combined with digital image correlation (DIC), has emerged as a promising high-throughput technique for rapidly estimating creep life. However, the applicability of bending creep above 700 ◦C for high-temperature alloys using DIC has not been fully established. In this work, we compare uniaxial creep rates of the nickel-based superalloy IN738LC with bending creep rates measured at 850 ◦C using high-temperature DIC. The bending creep data show excellent agreement with uniaxial creep results in the stress range of 240–360 MPa. The measured creep xponent, a critical rate-determining parameter, is found to be ~8 for both uniaxial and bending creep, with the rate data scattered within a factor of two. An in-house experimental setup was developed to perform bending creep tests at high temperatures, with strain monitored through DIC. Our results demonstrate that bending creep, combined with DIC, provides a reliable and efficient method for creep testing of high-temperature alloys. Compared to conventional uniaxial creep experiments, this approach requires significantly less time and material, thereby reducing effort, energy, and cost. We anticipate that this technique will serve as a foundation for testing precious high-temperature materials. For instance, in ongoing rapid discoveries of advanced alloys, in-service creep life can be evaluated much faster with reduced material requirements. Moreover, this method holds strong potential for application to high-entropy alloys and additively manufactured alloys designed for demanding high-temperature environments. KW - Digital image correlation KW - Bending creep KW - Nickel-based superalloys KW - High throughput testing KW - High-temperature materials PY - 2025 UR - https://www.sciencedirect.com/science/article/pii/S0921509325017034?via%3Dihub DO - https://doi.org/10.1016/j.msea.2025.149479 VL - 950 SP - 1 EP - 12 PB - Elsevier B.V. AN - OPUS4-64814 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Rehmer, Birgit A1 - Bayram, Faruk A1 - Ávila Calderón, Luis A1 - Mohr, Gunther A1 - Skrotzki, Birgit T1 - BAM reference data: Temperature-dependent Young's and shear modulus data for additively and conventionally manufactured variants of Ni-based alloy Inconel IN718 N2 - The elastic properties (Young's modulus, shear modulus) of Ni-based alloy Inconel IN718 were investigated between room temperature and 800 °C in an additively manufactured variant (laser powder bed fusion, PBF‑LB/M) and from a conventional process route (hot rolled bar). The moduli were determined using the dynamic resonance method. The data set includes information on processing parameters, heat treatments, grain size, specimen dimensions and weight, Young’s and shear modulus as well as their measurement uncertainty. The dataset was generated in an accredited testing lab using calibrated measuring equipment. The calibrations meet the requirements of the test procedure and are metrologically traceable. The dataset was audited as BAM reference data. KW - Elastic modulus KW - Young's modulus KW - Shear modulus KW - Additive manufacturing KW - IN718 PY - 2023 DO - https://doi.org/10.5281/zenodo.7813824 PB - Zenodo CY - Geneva AN - OPUS4-57287 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fedelich, Bernard A1 - Kühn, Hans-Joachim A1 - Rehmer, Birgit A1 - Skrotzki, Birgit T1 - Experimental and analytical investigation of the TMF-HCF lifetime behavior of two cast iron alloys N2 - The combined loading Thermomechanical Fatigue (TMF) with High Cycle Fatigue (HCF) has been experimentally investigated for two cast iron alloys. Both alloys contain globular graphite nodules but the first one has a ferritic structure while the second one has an austenitic crystal structure. In particular, the influences of the HCF frequency, of the HCF loading amplitude and of the location of the superposed HCF cycles have been investigated. It was observed that the HCF frequency has a limited impact on the fatigue life. On the other side, the HCF-strain amplitude has a highly non-linear influence on the fatigue life. The experimental results can be understood in terms of a fracture mechanics based damage mechanism: Cracks quickly initiate due to the TMF loading and the growth of the cracks up to a few mm controls the fatigue life. If HCF-loading cycles are superposed, cyclic crack propagation dramatically accelerates after a threshold has been reached. This threshold is regarded as controlling the fatigue life reduction. The previous ideas have been expressed in a model that can be very simply applied to estimate the fatigue life reduction ratio due to the superposed HCF cycles. It only contains two adjustable parameters and can be combined with any TMF life assessment model. T2 - 3rd International Workshop on Thermo-Mechanical Fatigue (TMF-Workshop 2016) CY - Berlin, Germany DA - 27.04.2016 KW - Thermomechanical Fatigue (TMF) KW - High Cycle Fatigue (HCF) KW - Cast iron KW - Fatigue assessment PY - 2017 DO - https://doi.org/10.1016/j.ijfatigue.2016.11.013 SN - 0142-1123 SN - 1879-3452 VL - 99 IS - 2 (Special issue: Recent developments in thermo-mechanical fatigue) SP - 266 EP - 278 PB - Elsevier CY - Oxford AN - OPUS4-39810 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rehmer, Birgit A1 - Skrotzki, Birgit A1 - Glaubitz, Steffen T1 - Influence of casting skin on fatigue lifetime of ferritic ductile cast iron N2 - The fatigue behaviour of cast iron is usually investigated on machined specimens. Components of cast iron, however, have a casting skin; therefore the investigation of the influence of the casting skin on the lifetime is of interest. To study this influence isothermal fatigue tests were carried out on heat-resisting spheroidal graphite cast iron EN GJS SiMo 4.05 in 4–point-bending set-up at 400 °C. Specimens with and without casting skin were investigated comparatively. The number of cycles to failure was significantly lower for specimens with casting skin. Metallographic investigations underline the reduction of lifetime caused by casting skin. KW - Cast iron KW - Casting skin KW - Fatigue KW - Lifetime PY - 2017 SN - 0025-5300 VL - 59 IS - 1 SP - 5 EP - 10 PB - Carl Hanser Verlag CY - München AN - OPUS4-38929 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ávila Calderón, Luis A1 - Rehmer, Birgit A1 - Schriever, Sina A1 - Ulbricht, Alexander A1 - Agudo Jácome, Leonardo A1 - Sommer, Konstantin A1 - Mohr, Gunther A1 - Skrotzki, Birgit A1 - Evans, Alexander T1 - Creep and creep damage behavior of stainless steel 316L manufactured by laser powder bed fusion N2 - This study presents a thorough characterization of the creep properties of austenitic stainless steel 316L produced by laser powder bed fusion (LPBF 316L) contributing to the sparse available data to date. Experimental results (mechanical tests, microscopy, X-ray computed tomography) concerning the creep deformation and damage mechanisms are presented and discussed. The tested LPBF material exhibits a low defect population, which allows for the isolation and improved understanding of the effect of other typical aspects of an LPBF microstructure on the creep behavior. As a benchmark to assess the material properties of the LPBF 316L, a conventionally manufactured variant of 316L was also tested. To characterize the creep properties, hot tensile tests and constant force creep tests at 600 °C and 650 °C are performed. The creep stress exponents of the LPBF material are smaller than that of the conventional variant. The primary and secondary creep stages and the times to rupture of the LPBF material are shorter than the hot rolled 316L. Overall the creep damage is more extensive in the LPBF material. The creep damage of the LPBF material is overall mainly intergranular. It is presumably caused and accelerated by both the appearance of precipitates at the grain boundaries and the unfavorable orientation of the grain boundaries. Neither the melt pool boundaries nor entrapped gas pores show a significant influence on the creep damage mechanism. KW - 316L KW - Laser Powder Bed Fusion (LPBF) KW - Creep behavior KW - Additive Manufacturing KW - AGIL PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-539373 DO - https://doi.org/10.1016/j.msea.2021.142223 SN - 0921-5093 VL - 830 SP - 142223 PB - Elsevier B.V. AN - OPUS4-53937 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fedelich, Bernard A1 - Kühn, Hans-Joachim A1 - Rehmer, Birgit A1 - Skrotzki, Birgit ED - Iacoviello, Francesco T1 - Modeling the lifetime reduction due to the superposition of TMF and HCF loadings in cast iron alloys N2 - The superposition of small amplitude, high frequency loading cycles (HCF) to slow, large amplitude loading cycles (TMF) can significantly reduce the fatigue life. In this work, the combined TMF+HCF loading has been experimentally investigated for a cast iron alloy. In particular, the influence of the HCF frequency of the HCF amplitude and of the location of the superposed HCF cycles has been assessed. It was observed that the HCF frequency has a limited impact on the TMF fatigue life. On the other side, the HCF-strain amplitude has a highly non-linear influence on the TMF fatigue life. A simple estimate for the fatigue life reduction due to the superposed HCF cycles has been derived from fracture mechanics considerations. It is assumed that the number of propagation cycles up to failure can be neglected after a threshold for the HCF loading has been reached. The model contains only two adjustable parameters and can be combined with any TMF life prediction model. The model predictions are compared with the test results for a large range of TMF+HCF loading conditions. T2 - 21st European Conference on Fracture, ECF21 CY - Catania, Italy DA - 20.06.2016 KW - Thermomechanical Fatigue (TMF); High Cycle Fatigue (HCF); Cast iron; Fatigue assessment PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-369550 DO - https://doi.org/doi:10.1016/j.prostr.2016.06.274 VL - 2 SP - 2190 EP - 2197 PB - Elsevier CY - Radarweg 29, 1043 NX Amsterdam, The Netherlands, AN - OPUS4-36955 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rehmer, Birgit T1 - Thermo-mechanical fatigue of heat resistant austenitic cast iron EN-GJSA-NiSiCr35-5-2 (Ni-Resist D-5S) N2 - Austenitic cast iron was primarily used as material for pumps and mountings due to their excellent corrosion resistance. Certain grades, especially those with spherical graphite morphology, offer also a good high temperature strength and a high scaling resistance, which opened new fields of application e.g. for casing part of gas turbines, exhaust manifolds and turbo chargers. For such applications, a high ductility and creep resistance is beneficial, as exhibited by the studied alloy EN-GJSA-XNiSiCr35-5-2. Its high Ni-content produces the austenitic matrix, while Cr increases strength, hardness and scaling resistance. The alloy is standardized according to DIN EN 13835 with respect to chemical composition and mechanical properties (strength, elongation at fracture, Young's modulus, hardness and impact energy) at room temperature. However, data on mechanical properties at high temperature were rarely published in the open literature. In a recently completed research project, we comprehensively characterized the alloy EN-GJSA-XNiSiCr35-5-2 in terms of its temperature dependent mechanical behavior concerning strength and to isothermal as well as non-isothermal fatigue behavior. The results were used to calibrate a material and lifetime model. TMF tests were carried out with a constant minimum temperature (Tmin = 400 °C) and varying maximum temperatures (Tmax = 700 °C, 800 °C, 900 °C) with hold times of 180 s at Tmax and two phase angles (in-phase (IP), 180° out-of-phase (OP)). The investigated alloy showed a strongly deviating TMF behavior as compared to ferritic SiMo alloys investigated in a previous project: the austenitic material exhibits a comparable strength under OP- and IP-TMF loading, while the ferritic alloys showed a distinct higher strength under IP- than under OP-TMF load. At Tmax = 700 °C and 900 °C, the lifetime of Ni-Resist in IP-tests is slightly longer than that of OP-tests, while it is vice versa at Tmax = 800 °C. The IP-tests at Tmax = 900 °C show a comparable lifetime as OP-tests at Tmax = 700 °C and 800 °C, which was unexpected for such a high testing temperature. When plotting the stress range versus N it becomes clear that the behavior at Tmax = 900 °C is different from the other investigated temperatures: at 700 °C and 800 °C the stress-curve exhibits a range of stabilized stress for both phase angles. This is also true for the OP-tests at Tmax = 900 °C. However, all IP-tests at Tmax = 900 °C show a continuous cyclic softening from the beginning on. The stiffness of the test pieces decrease continuously with increasing number of cycles and their surfaces show numerous cracks. Complementary metallographic investigations showed that beside classical fatigue damage with cracks initiated at the surface, intergranular creep damage was found in the volume of the test pieces. Pores and cracks are formed at grain boundaries perpendicular to the applied load. This is also a distinct difference to the SiMo alloys. T2 - 3rd International Workshop on Thermo-mechanical Fatigue CY - Berlin, Germany DA - 27.04.2016 KW - cast iron. fatigue KW - cyclic softening PY - 2016 AN - OPUS4-35912 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mishurova, Tatiana A1 - Artzt, K. A1 - Rehmer, Birgit A1 - Haubrich, J. A1 - Ávila Calderón, Luis A1 - Schoenstein, F. A1 - Serrano-Munoz, Itziar A1 - Requena, G. A1 - Bruno, Giovanni T1 - Separation of the impact of residual stress and microstructure on the fatigue performance of LPBF Ti-6Al-4V at elevated temperature N2 - Manufacturing defects, high residual stress (RS), and microstructures affect the structural integrity of laser powder bed fusion (LPBF) Ti-6Al-4V. In this study, the individual effect of these factors on fatigue performance at elevated temperature (300 °C) was evaluated. Material in as-built condition and subjected to post-processing, including two heat treatments and hot isostatic pressing, was investigated. It was found that in the absence of tensile RS, the fatigue life at elevated temperature is primary controlled by the defects; and densification has a much stronger effect than the considered heat treatments on the improvement of the mechanical performance. KW - Additive manufacturing KW - Ti-6Al-4V KW - Residual stress KW - Fatigue performance KW - Computed tomography PY - 2021 DO - https://doi.org/10.1016/j.ijfatigue.2021.106239 SN - 0142-1123 VL - 148 SP - 106239 PB - Elsevier Ltd. AN - OPUS4-52369 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bhadeliya, Ashok A1 - Rehmer, Birgit A1 - Fedelich, Bernard A1 - Jokisch, Torsten A1 - Skrotzki, Birgit A1 - Olbricht, Jürgen T1 - High Temperature Fatigue Crack Growth in Nickel-Based Alloys Refurbished by Additive Manufacturing N2 - Hybrid additive manufacturing plays a crucial role in the restoration of gas turbine blades, where, e.g., the damaged blade tip is reconstructed by the additive manufacturing process on the existing blade made of a parent nickel-based alloy. However, inherent process-related defects in additively manufactured material, along with the interface created between the additively manufactured and the cast base material, impact the fatigue crack growth behavior in bi-material components. This study investigates the fatigue crack growth behavior in bi-material specimens of nickel-based alloys, specifically, additively manufactured STAL15 and cast alloy 247DS. The tests were conducted at 950 °C with stress ratios of 0.1 and −1. Metallographic and fractographic investigations were carried out to understand crack growth mechanisms. The results revealed significant retardation in crack growth at the interface. This study highlights the potential contributions of residual stresses and microstructural differences to the observed crack growth retardation phenomenon, along with the conclusion from an earlier study on the effect of yield strength mismatch on crack growth behavior at a perpendicular interface in bi-material specimens. T2 - Superalloys 2024 Conference CY - Champion, Pennsylvania, USA DA - 08.09.2024 KW - Fatigue crack growth KW - Bi-material structure KW - Additive manufacturing KW - Nickel-based alloys PY - 2024 SN - 978-3-031-63937-1 DO - https://doi.org/10.1007/978-3-031-63937-1_92 SN - 2367-1181 SN - 2367-1696 VL - 15th SP - 994 EP - 1001 PB - Springer CY - Cham AN - OPUS4-60907 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ávila Calderón, Luis A1 - Graf, B. A1 - Rehmer, Birgit A1 - Petrat, T. A1 - Skrotzki, Birgit A1 - Rethmeier, Michael T1 - Characterization of Ti-6Al-4V fabricated by multilayer laser powder-based directed energy deposition N2 - Laser powder-based directed energy deposition (DED-L) is increasingly being used in additive manufacturing (AM). As AM technology, DED-L must consider specific challenges. It must achieve uniform volume growth over hundreds of layers and avoid heat buildup of the deposited material. Herein, Ti–6Al–4V is fabricated using an approach that addresses these challenges and is relevant in terms of transferability to DED–L applications in AM. The assessment of the obtained properties and the discussion of their relationship to the process conditions and resulting microstructure are presented. The quality of the manufacturing process is proven in terms of the reproducibility of properties between individual blanks and with respect to the building height. The characterization demonstrates that excellent mechanical properties are achieved at room temperature and at 400 °C. KW - AGIL KW - Laser powder-based directed energy deposition KW - Tensile properties KW - Ti-6Al-4V KW - Microstructure PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-542262 DO - https://doi.org/10.1002/adem.202101333 SN - 1438-1656 SN - 1527-2648 SP - 1 EP - 15 PB - Wiley-VCH CY - Weinheim AN - OPUS4-54226 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Olbricht, Jürgen A1 - Lippmann, Tim A1 - Klingelhöffer, Hellmuth A1 - Rehmer, Birgit A1 - Skrotzki, Birgit T1 - Mechanical characterisation of heat resistant power plant materials by creep and fatigue testing in controlled gas atmospheres N2 - The continuing increase of steam parameters of fossil fuelled high efficiency power plants and new combustion concepts for the capture and storage of carbon dioxide lead to harsher service conditions for the components and structural materials of such facilities. The present work introduces a test concept that allows testing of candidate materials under simultaneous mechanical and corrosive loading. The material's reaction can be directly investigated under simulated temperature, load and corrosion conditions of modern installations. First results obtained for different heat resistant steels suggest a strong influence of the environmental medium on the fatigue and creep behaviour. Such findings complement the data that is available from the classical qualification process of the materials and may support the material selection for new power plant installations. N2 - Die weitere Erhöhung der Dampfparameter von hocheffizienten fossil befeuerten Kraftwerken sowie neue Verbrennungskonzepte zur Realisierung der Kohlendioxidabscheidung und -speicherung führen zu erschwerten Einsatzbedingungen für die Bauteile und Strukturwerkstoffe solcher Anlagen. Die vorliegende Arbeit stellt ein Prüfkonzept vor, das die Prüfung von Kandidatenwerkstoffen unter überlagerter mechanischer und korrosiver Beanspruchung ermöglicht. Die Werkstoffreaktion kann direkt unter den simulierten Temperatur-, Last- und Korrosionsbedingungen moderner Anlagen untersucht werden. Erste Ergebnisse für verschiedene warmfeste Stähle deuten auf einen erheblichen Einfluss des Umgebungsmediums auf das Ermüdungs- und Kriechverhalten hin. Solche Erkenntnisse ergänzen die aus den Qualifizierungsuntersuchungen der Werkstoffe verfügbaren Daten und können so die Werkstoffauswahl für neue Anlagen unterstützen. KW - Hocheffiziente Kraftwerke KW - Kohlendioxidabscheidung und -speicherung (CCS) KW - Warmfeste Stähle KW - Mechanische Eigenschaften KW - Korrosionsverhalten KW - High efficiency power plants KW - Carbon capture and storage (CCS) KW - Heat resistant steels KW - Mechanical properties KW - Corrosion behaviour PY - 2014 DO - https://doi.org/10.1002/mawe.201400185 SN - 0933-5137 SN - 1521-4052 VL - 45 IS - 1 SP - 5 EP - 14 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-30309 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Skrotzki, Birgit A1 - Uckert, Danilo A1 - Matzak, Kathrin A1 - Kühn, Hans-Joachim A1 - Rehmer, Birgit A1 - Peter, Frauke A1 - Fedelich, Bernard A1 - Falkenberg, Rainer A1 - Haftaoglu, Cetin A1 - Kindrachuk, Vitaliy T1 - Erweiterung bestehender Werkstoff- und Rechenmodelle zur Lebensdauervorhersage für Abgasturbolader-Heißteile unter thermomechanischer Ermüdungsbeanspruchung N2 - In diesem Forschungsvorhaben erfolgte eine Überprüfung der Übertragbarkeit der Werkstoff- und Rechenmodelle für die Lebensdauervorhersage von ATL-Heißteilen unter TMF-Beanspruchung auf eine andere Werkstoffklasse, d. h. auf eine austenitische Gusseisenlegierung mit Kugelgraphit. Dafür wurde die Legierung EN-GJSA-XNiSiCr35-5-2 (Ni-Resist D-5S) ausgewählt. Zunächst wurde für diesen Werkstoff eine experimentelle Datenbasis geschaffen, da diese vor Beginn des Vorhabens nicht ausreichend war. Dazu wurden Zug-, Kriech-, LCF- und TMF-Versuche durchgeführt, die der Kalibrierung der Modelle dienten. Unter TMF-Belastung zeigte der untersuchte Werkstoff ein stark abweichendes Verhalten von den im vorangegangenen Vorhaben untersuchten ferritischen SiMo-Legierungen: Der Werkstoff Ni-Resist zeigte insgesamt eine vergleichbare Festigkeit unter OP- und IP-Bedingungen, während die ferritischen Legierungen unter IP-Beanspruchung eine deutlich höhere Festigkeit aufweisen. Mit zunehmenden Temperaturen und Haltezeiten unter Zugspannungen wurden dagegen beim Werkstoff Ni-Resist Hinweise auf Kriechschädigung gefunden, die schädigungsrelevant sind. Auch dies ist ein deutlicher Unterschied zu den SiMo-Legierungen. Das Spannungs-Verformungs-Verhalten in den LCF- und TMF-Versuchen wird durch das Modell auch für den neuen Werkstoff überwiegend gut beschrieben. Das Gleiche gilt für die Lebensdauervorhersage, die mit Ausnahme der Prüftemperatur 900 °C innerhalb eines Fak-tors zwei liegt. Eine Verifikation des Modells erfolgte mit Hilfe eines Bauteilversuchs an einem Abgassammler, der abwechselnd mit heißem und kaltem Gas durchströmt wurde. Ziel der Bauteilsimulation war insbesondere die Vorhersage der Rissbildungsorte. Eine Vorhersage der exakten Lebensdauer wurde nicht erwartet, da das Bauteil mit einer Gusshaut behaftet war, während die für die Kalibrierung des Lebensdauermodells verwendeten Versuche an bearbeiteten, glatten Proben ohne Gusshaut durchgeführt wurden. Die überwiegende Anzahl der experimentell ermittelten Rissorte wurden vorhergesagt. Schließlich war ein wesentliches Ziel des Vorhabens, den Einfluss von HCF-Schwingungen auf die TMF-Lebensdauer vertieft experimentell zu untersuchen und das bereits bestehende Lebensdauermodell auf HCF-Überlagerung zu erweitern. Dazu wurde zunächst die Daten-basis aus dem Vorgängervorhaben am Bespiel von SiMo 4.05 deutlich ausgebaut, um die verschiedenen Einflussparameter zu erfassen. Es wurde ein Ansatz entwickelt, in dem die Lebensdauerminderung durch die überlagerten HCF-Schwingungen abgebildet wird. Dabei wird davon ausgegangen, dass ab einer bestimmten Risstiefe die Überlagerung der HCF-Schwingungen die Rissausbreitung stark beschleunigt. Der Zeitpunkt, wann diese Beschleunigung eintritt, wird als maßgeblich für die Lebensdauerminderung angesehen. Mit diesem Ansatz lassen sich die Lebensdauern für beide Werkstoffe in guter Übereinstimmung mit dem Experiment vorhersagen. T2 - Informationstagung Turbomaschinen, Frühjahr 2016 CY - Bad Neuenahr, Germany DA - 13.04.2016 KW - Ermüdung KW - LCF KW - Modellierung KW - Schädigung KW - Simulation KW - TMF PY - 2016 VL - Heft R575 SP - 1 EP - 35 AN - OPUS4-35823 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Suárez Ocaño, Patricia A1 - Ávila Calderón, Luis A1 - Agudo Jácome, Leonardo A1 - Rehmer, Birgit A1 - Mohr, Gunther A1 - Evans, Alexander A1 - Skrotzki, Birgit T1 - Effect of 700–900 °C heat treatments and room and high temperature tensile deformation on the microstructure of laser powder bed fused 316L stainless steel N2 - The effect of post-processing heat treatments on the hierarchical microstructure evolution and mechanical strength of the austenitic stainless steel 316L produced by laser powder bed fusion has been investigated. Heat treatments between 700 and 900 ◦C and 0.5 to 3 h, were applied to samples treated at 450 ◦C for 4 h. The results showed a stable microstructure at all studied temperatures and times in terms of grain size, morphology, aspect ratio, density of low-angle grain boundaries, and texture. However, temperature and time promoted the diffusion of segregated elements together with a reduction in dislocation density and disappearance of the cellular structure. This was associated with a reduction in hardness and tensile proof strength at both room and high temperature. In addition, microstructural characterization coupled with thermodynamic CALPHAD-based equilibrium calculations showed that the formation of carbides and intermetallic phases was already visible after annealing at 800 ◦C for 3 hours, although these intermetallics did not affect the tensile properties at this level. Analysis of the microstructure evolution after tensile deformation showed differences in the deformation mechanisms at room and high temperature, with twinning and martensitic transformation occurring at room temperature, the latter not widely reported for additively manufactured 316L. Finally, comparisons with similar materials produced under comparable conditions showed differences in the tensile properties, attributed to differences in chemical composition and the associated presence of stacking faults in the undeformed state. KW - Additive manufacturing KW - 316L stainless steel KW - Heat treatments KW - Tensile properties KW - Microstructure PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-632471 DO - https://doi.org/10.1016/j.msea.2025.148469 SN - 0921-5093 VL - 939 SP - 1 EP - 24 PB - Elsevier CY - Amsterdam AN - OPUS4-63247 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -