TY - JOUR A1 - Nikoonasab, Ali A1 - Licht, M. A1 - Weiler, L. A1 - Achenbach, R. A1 - Raupach, M. A1 - Gluth, Gregor T1 - Pore solution compositions and redox potentials of ground granulated blast furnace slag-containing cement pastes N2 - The pore solutions of hardened ground granulated blast furnace slag (GGBFS)-containing cements differ from the pore solutions of other cements with effects on reinforcement corrosion, application of electrochemical methods and immobilisation of radioactive waste. In the present study, the pore solutions of seven different GGBFS-containing cements (alkali-activated slag, alkali-activated slag/fly ash blends, hybrid alkaline cement (HAC), CEM III/C and CEM III/B) were extracted and their elemental and sulfate concentration, pH, redox potential and conductivity were determined; a Portland cement (CEM I) pore solution was analysed analogously. The silicon and aluminium concentrations of the alkali-activated cements increased with fly ash fraction, reaching values up to 5 mM and 10 mM, respectively, and thus were considerably higher than those of the standard cements. The redox potentials of the pore solutions of the GGBFS-containing cements were in the range from −100 mV to –500 mV vs Ag/AgCl, that is considerably lower than that of the Portland cement (8–20 mV vs Ag/AgCl), with the value depending on the GGBFS fraction and whether the cements were alkali-activated or not. These results indicate that the effects of reduced sulfur species from GGBFS in cements are more pronounced in alkali-activated materials, including HAC, and increase with GGBFS fraction. KW - Alkali-activated materials KW - Ground granulated blast furnace slag KW - Sulfide KW - Redox potential KW - Pore solution PY - 2025 DO - https://doi.org/10.1680/jadcr.25.00041 SN - 1751-7605 SN - 0951-7197 SP - 1 EP - 12 PB - Emerald AN - OPUS4-64619 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mundra, S. A1 - Samson, G. A1 - Masi, G. A1 - Achenbach, R. A1 - Bastidas, D. M. A1 - Bernal, S. A. A1 - Bignozzi, M. C. A1 - Criado, M. A1 - Cyr, M. A1 - Gartner, N. A1 - von Greve-Dierfeld, S. A1 - Legat, A. A1 - Nikoonasab, Ali A1 - Provis, J. L. A1 - Raupach, M. A1 - Gluth, Gregor T1 - Application of electrochemical methods for studying steel corrosion in alkali-activated materials N2 - Alkali-activated materials (AAMs) are binders that can complement and partially substitute the current use of conventional cement. However, the present knowledge about how AAMs protect steel reinforcement in concrete elements is incomplete, and uncertainties exist regarding the application of electrochemical methods to investigate this issue. The present review by EFC WP11-Task Force ‘Corrosion of steel in alkali-activated materials’ demonstrates that important differences exist between AAMs and Portland cement, and between different classes of AAMs, which are mainly caused by differing pore solution compositions, and which affect the outcomes of electrochemical measurements. The high sulfide concentrations in blast furnace slag-based AAMs lead to distinct anodic polarisation curves, unusually low open circuit potentials, and low polarisation resistances, which might be incorrectly interpreted as indicating active corrosion of steel reinforcement. No systematic study of the influence of the steel–concrete interface on the susceptibility of steel to corrosion in AAMs is available. Less common electrochemical methods present an opportunity for future progress in the field. KW - Alkali-activated materials KW - Reinforcement corrosion KW - Steel corrrosion KW - Electrochemical methods KW - Concrete PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-572241 DO - https://doi.org/10.1002/maco.202313743 SN - 1521-4176 VL - 74 IS - 7 SP - 988 EP - 1008 PB - Wiley-VCH CY - Weinheim AN - OPUS4-57224 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -