TY - CONF A1 - Lee, Jun-Seob A1 - Radnik, Jörg A1 - Bäßler, Ralph T1 - Electrochemical behavior of UNS N08031 in Green-Death-solution N2 - The electrochemical behavior of UNS(1) N08031 was investigated as a function of electrode potential in Green-Death(2) solution at 40 °C. The UNS N08031 surface is in a stable passive state during cyclic potentiodynamic polarization without an initiation and/or propagation of localized corrosion. In potentiostatic polarization of UNS N08031 for 3600 s, passive current density increases with an increase in the passivation potential from 0.7 to 1.0 VSSE (silver/silver chloride reference electrode in saturated potassium chloride) Electrochemical impedance spectroscopy (EIS) and Mott-Schottky (M-S) analysis showed that a more defective n-type semiconductive passive film forms as the potential increases. X-ray photoelectron spectroscopy (XPS) revealed that passive film consists of mainly chromium and minor iron and nickel oxides. The mechanism of the defective passive film formation is discussed. The increase of the applied potential is considered to be a reason for the change in passive film stability. T2 - NACE International Annual Corrosion Conference CY - Phoenix, AZ, USA DA - 15.04.2018 KW - Steel KW - Passive film KW - X-ray photoelectron spectroscopy PY - 2018 SP - 10631, 1 EP - 9 PB - Omnipress CY - Houston AN - OPUS4-44915 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lee, Jun-Seob A1 - Radnik, Jörg A1 - Bäßler, Ralph T1 - Passivity of alloy 31 in green-death solution N2 - The passivation behavior of alloy 31 was investigated as a function of passivation potential in a green-death solution at 40 °C. The alloy 31 surface is in a stable passive state during cyclic potentiodynamic polarization. In potentiostatic polarization of alloy 31, passive current density increases with an increase in the passivation potential. Electrochemical impedance spectroscopy (EIS) and Mott–Schottky (M–S) analysis showed that a more defective n-type semiconductive passive film forms as the potential increases. X-ray photoelectron spectroscopy (XPS) revealed that passive film consists of mainly chromium and minor iron and nickel oxides. The increase of the applied potential is considered to be a reason for the change in passive film stability. KW - Passive film KW - Steel KW - Alloy 31 KW - X-ray photoelectron spectroscopy PY - 2018 U6 - https://doi.org/10.1002/maco.201709996 SN - 0947-5117 SN - 1521-4176 VL - 69 IS - 9 SP - 1218 EP - 1226 PB - Wiley-VCH CY - Weinheim AN - OPUS4-45938 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -