TY - JOUR A1 - Seeburg, Dominik A1 - Liu, Dongjing A1 - Radnik, Jörg A1 - Atia, Hanan A1 - Pohl, Marga-Martina A1 - Schneider, Matthias A1 - Martin, Andreas A1 - Wohlrab, Sebastian T1 - Structural changes of highly active Pd/MeOx (Me = Fe, Co, Ni) during catalytic methane combustion JF - Catalysts N2 - Fe2O3, Co3O4 and NiO nanoparticles were prepared via a citrate method and further functionalized with Pd by impregnation. The pure oxides as well as Pd/Fe2O3, Pd/Co3O4, and Pd/NiO (1, 5 and 10 wt % Pd) were employed for catalytic methane combustion under methane lean (1 vol %)/oxygen rich (18 vol %, balanced with nitrogen) conditions. Already, the pure metal oxides showed a high catalytic activity leading to complete conversion temperature of T100 ≤ 500 °C. H2-TPR (Temperature-programmed reduction) experiments revealed that Pd-functionalized metal oxides exhibited enhanced redox activity compared to the pure oxides leading to improved catalytic combustion activity at lower temperatures. At a loading of 1 wt % Pd, 1Pd/Co3O4 (T100 = 360 °C) outperforms 1Pd/Fe2O3 (T100 = 410 °C) as well as 1Pd/NiO (T100 = 380 °C). At a loading of 10 wt % Pd, T100 could only be slightly reduced in all cases. 1Pd/Co3O4 and 1Pd/NiO show reasonable stability over 70 h on stream at T100. XPS (X-ray photoelectron spectroscopy) and STEM (Scanning transmission electron microscopy) investigations revealed strong interactions between Pd and NiO as well as Co3O4, respectively, leading to dynamic transformations and reoxidation of Pd due to solid state reactions, which leads to the high long-term stability. KW - Methane total oxidation KW - Methane removal KW - Carbon dioxide KW - X-ray photoelectron spectroscopy PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-439412 DO - https://doi.org/10.3390/catal8020042 SN - 2073-4344 VL - 8 IS - 2 SP - Article 42, 1 EP - 13 PB - MDPI AN - OPUS4-43941 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Radnik, Jörg ED - Wandelt, K. T1 - X-ray photoelectron spectroscopy for investigation of heterogeneous catalytic process T2 - Encyclopedia of Interfacial Chemistry: Surface Science and Electrochemistry N2 - Heterogeneous catalysis is a key technology in modern industrial societies. The main steps of a catalytic process take place at the surfaces of complex materials. For the investigations of these surfaces X-ray photoelectron spectroscopy is widely used and fits ideally. At some suitable examples, it will be explained how XPS can help to understand such catalysts better. The focus is on selective oxidation catalysts, one of the main challenges of present research. Here it will illustrate, how changes in the near surface region influence the catalyst performance and, herewith the different stages (activation, maximum performance and deactivation) in the life of catalysts. Additionally, it will be stressed out how important information at different depth regions (surface, near-surface region, bulk) can be useful for comprehensive understanding of the material. Another important subject is nanostructured catalysts with molecular sieves as supports or defined complexes as precursors. Finally, the combination of XPS with other methods used in the analysis of catalysts, e.g. electron microscopy, X-ray absorption spectroscopy and low energy ion scattering will be discussed. KW - X-ray photoelectron spectroscopy KW - Depth information KW - Heterogeneous catalysis KW - Structure-properties relationships PY - 2018 SN - 978-0-12-809739-7 VL - 1 SP - 607 EP - 614 PB - Elsevier AN - OPUS4-44876 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lee, Jun-Seob A1 - Radnik, Jörg A1 - Bäßler, Ralph T1 - Electrochemical behavior of UNS N08031 in Green-Death-solution T2 - Conference Proceedings NACE International Corrosion Conference 2018 N2 - The electrochemical behavior of UNS(1) N08031 was investigated as a function of electrode potential in Green-Death(2) solution at 40 °C. The UNS N08031 surface is in a stable passive state during cyclic potentiodynamic polarization without an initiation and/or propagation of localized corrosion. In potentiostatic polarization of UNS N08031 for 3600 s, passive current density increases with an increase in the passivation potential from 0.7 to 1.0 VSSE (silver/silver chloride reference electrode in saturated potassium chloride) Electrochemical impedance spectroscopy (EIS) and Mott-Schottky (M-S) analysis showed that a more defective n-type semiconductive passive film forms as the potential increases. X-ray photoelectron spectroscopy (XPS) revealed that passive film consists of mainly chromium and minor iron and nickel oxides. The mechanism of the defective passive film formation is discussed. The increase of the applied potential is considered to be a reason for the change in passive film stability. T2 - NACE International Annual Corrosion Conference CY - Phoenix, AZ, USA DA - 15.04.2018 KW - Steel KW - Passive film KW - X-ray photoelectron spectroscopy PY - 2018 SP - 10631, 1 EP - 9 PB - Omnipress CY - Houston AN - OPUS4-44915 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lee, Jun-Seob A1 - Radnik, Jörg A1 - Bäßler, Ralph T1 - Passivity of alloy 31 in green-death solution JF - Materials and Corrosion N2 - The passivation behavior of alloy 31 was investigated as a function of passivation potential in a green-death solution at 40 °C. The alloy 31 surface is in a stable passive state during cyclic potentiodynamic polarization. In potentiostatic polarization of alloy 31, passive current density increases with an increase in the passivation potential. Electrochemical impedance spectroscopy (EIS) and Mott–Schottky (M–S) analysis showed that a more defective n-type semiconductive passive film forms as the potential increases. X-ray photoelectron spectroscopy (XPS) revealed that passive film consists of mainly chromium and minor iron and nickel oxides. The increase of the applied potential is considered to be a reason for the change in passive film stability. KW - Passive film KW - Steel KW - Alloy 31 KW - X-ray photoelectron spectroscopy PY - 2018 DO - https://doi.org/10.1002/maco.201709996 SN - 0947-5117 SN - 1521-4176 VL - 69 IS - 9 SP - 1218 EP - 1226 PB - Wiley-VCH CY - Weinheim AN - OPUS4-45938 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -