TY - JOUR A1 - Seeburg, Dominik A1 - Liu, Dongjing A1 - Radnik, Jörg A1 - Atia, Hanan A1 - Pohl, Marga-Martina A1 - Schneider, Matthias A1 - Martin, Andreas A1 - Wohlrab, Sebastian T1 - Structural changes of highly active Pd/MeOx (Me = Fe, Co, Ni) during catalytic methane combustion N2 - Fe2O3, Co3O4 and NiO nanoparticles were prepared via a citrate method and further functionalized with Pd by impregnation. The pure oxides as well as Pd/Fe2O3, Pd/Co3O4, and Pd/NiO (1, 5 and 10 wt % Pd) were employed for catalytic methane combustion under methane lean (1 vol %)/oxygen rich (18 vol %, balanced with nitrogen) conditions. Already, the pure metal oxides showed a high catalytic activity leading to complete conversion temperature of T100 ≤ 500 °C. H2-TPR (Temperature-programmed reduction) experiments revealed that Pd-functionalized metal oxides exhibited enhanced redox activity compared to the pure oxides leading to improved catalytic combustion activity at lower temperatures. At a loading of 1 wt % Pd, 1Pd/Co3O4 (T100 = 360 °C) outperforms 1Pd/Fe2O3 (T100 = 410 °C) as well as 1Pd/NiO (T100 = 380 °C). At a loading of 10 wt % Pd, T100 could only be slightly reduced in all cases. 1Pd/Co3O4 and 1Pd/NiO show reasonable stability over 70 h on stream at T100. XPS (X-ray photoelectron spectroscopy) and STEM (Scanning transmission electron microscopy) investigations revealed strong interactions between Pd and NiO as well as Co3O4, respectively, leading to dynamic transformations and reoxidation of Pd due to solid state reactions, which leads to the high long-term stability. KW - Methane total oxidation KW - Methane removal KW - Carbon dioxide KW - X-ray photoelectron spectroscopy PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-439412 DO - https://doi.org/10.3390/catal8020042 SN - 2073-4344 VL - 8 IS - 2 SP - Article 42, 1 EP - 13 PB - MDPI AN - OPUS4-43941 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Radnik, Jörg ED - Wandelt, K. T1 - X-ray photoelectron spectroscopy for investigation of heterogeneous catalytic process N2 - Heterogeneous catalysis is a key technology in modern industrial societies. The main steps of a catalytic process take place at the surfaces of complex materials. For the investigations of these surfaces X-ray photoelectron spectroscopy is widely used and fits ideally. At some suitable examples, it will be explained how XPS can help to understand such catalysts better. The focus is on selective oxidation catalysts, one of the main challenges of present research. Here it will illustrate, how changes in the near surface region influence the catalyst performance and, herewith the different stages (activation, maximum performance and deactivation) in the life of catalysts. Additionally, it will be stressed out how important information at different depth regions (surface, near-surface region, bulk) can be useful for comprehensive understanding of the material. Another important subject is nanostructured catalysts with molecular sieves as supports or defined complexes as precursors. Finally, the combination of XPS with other methods used in the analysis of catalysts, e.g. electron microscopy, X-ray absorption spectroscopy and low energy ion scattering will be discussed. KW - X-ray photoelectron spectroscopy KW - Depth information KW - Heterogeneous catalysis KW - Structure-properties relationships PY - 2018 SN - 978-0-12-809739-7 VL - 1 SP - 607 EP - 614 PB - Elsevier AN - OPUS4-44876 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Radnik, Jörg A1 - Dang, Thi Thuy Hanh A1 - Gatla, Suresh A1 - Ruguwanshi, A1 - Hoell, Armin T1 - Redox properties of Cu ions in molecular sieves N2 - Molecular sieves as materials with defined pores offer new opportunities in the preparation of nanostructured materials for different applications in chemistry, medicine and biology. Typical examples for such materials are zeolites, porous glass, different silicas and active carbon. Introducing transition metal ions in such materials can widen the possibilities of these materials in terms of chemical activity. Especially, the opportunity to tailor the redox properties of the transition metal ions by varying the location of the ion in the sieves is a promising way to obtain catalysts with the desired properties. For this purpose, Cu2+ ions were introduced into a SAPO-5 (silicoaluminaphosphate) by a hydrothermal method and by impregnation. As expected, the different preparation methods led to different locations of the Cu2+ ions: by the hydrothermal method the ions were incorporated in the SAPO-5 framework, by impregnation mononuclear Cu species randomly distributed in the pores of the support or CuO particles were formed depending on the Cu amount. These locations could be determined by Extended X-ray Absorption Fine Structure and Anomalous Small-Angle X-ray Scattering investigations. For investigating the redox properties of the Cu2+ ions the differently prepared sample were treated in Ar and H2 atmosphere until 550°C. X-ray Photoelectron Spectroscopy was performed to study the valence states of Cu after each of such treatment. For a definite determination of the valence states, both Cu 2p and Cu LMM spectra must be recorded. Cu2+ exhibits a clear chemical shift and a typical satellite structure in Cu2p spectra, but between mono- and zerovalent Cu a differentiation is not possible. On the other hand, these two species show a clear shift in the Auger spectra. Whereas in H2 atmosphere in any case metallic Cu was formed, the treatment in Ar showed significant differences between the samples. Cu2+ incorporated in the framework could not be reduced by this treatment. In contrast, the mononuclear Cu2+ species were reduced to stable Cu+. Likewise, the CuO nanoparticles were reduced to the monovalent Cu, but this species can be much more easily reoxidized in air. The consequences for the catalytic properties will be discussed. T2 - ECASIA 2017 CY - Montpellier, France DA - 24.09.2017 KW - Catalysis KW - X-ray photoelectron spectroscopy KW - Nanostructured materials PY - 2017 AN - OPUS4-42323 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, Anja A1 - Krahl, T. A1 - Radnik, Jörg A1 - Wagner, Andreas A1 - Werner, W. S. M. A1 - Ritter, B. A1 - Kemnitz, E. A1 - Unger, Wolfgang T1 - Chemical in-depth analysis of (Ca/Sr)F2 core–shell like nanoparticles by X-ray photoelectron spectroscopy with tunable excitation energy N2 - The fluorolytic sol–gel synthesis is applied with the intention to obtain two different types of core–shell nanoparticles, namely, SrF2–CaF2 and CaF2–SrF2. In two separate fluorination steps for core and shell formation, the corresponding metal lactates are reacted with anhydrous HF in ethylene glycol. Scanning transmission electron microscopy (STEM) and dynamic light scattering (DLS) confirm the formation of particles with mean dimensions between 6.4 and 11.5 nm. The overall chemical composition of the particles during the different reaction steps is monitored by quantitative Al Kα excitation X-ray photoelectron spectroscopy (XPS). Here, the formation of stoichiometric metal fluorides (MF2) is confirmed, both for the core and the final core–shell particles. Furthermore, an in-depth analysis by synchrotron radiation XPS (SR-XPS) with tunable excitation energy is performed to confirm the core–Shell character of the nanoparticles. Additionally, Ca2p/Sr3d XPS intensity ratio in-Depth profiles are simulated using the software Simulation of Electron Spectra for Surface Analysis (SESSA). In principle, core–shell like particle morphologies are formed but without a sharp interface between calcium and strontium containing phases. Surprisingly, the in-depth chemical distribution of the two types of nanoparticles is equal within the error of the experiment. Both comprise a SrF2-rich core domain and CaF2-rich shell domain with an intermixing zone between them. Consequently, the internal morphology of the final nanoparticles seems to be independent from the synthesis chronology. KW - Metal fluorides KW - Sol-gel synthesis KW - Synchrotron radiation KW - X-ray photoelectron spectroscopy PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-522284 DO - https://doi.org/10.1002/sia.6937 SN - 0142-2421 VL - 53 IS - 5 SP - 494 EP - 508 PB - Wiley VCH AN - OPUS4-52228 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Radnik, Jörg A1 - Kersting, R. A1 - Hagenhoff, B. A1 - Bennet, Francesca A1 - Ciornii, Dmitri A1 - Nymark, P. A1 - Grafström, R. A1 - Hodoroaba, Vasile-Dan T1 - Reliable Surface Analysis Data of Nanomaterials in Support of Risk Assessment Based on Minimum Information Requirements N2 - The minimum information requirements needed to guarantee high-quality surface Analysis data of nanomaterials are described with the aim to provide reliable and traceable Information about size, shape, elemental composition and surface chemistry for risk assessment approaches. The widespread surface analysis methods electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS), X-ray photoelectron spectroscopy (XPS) and secondary ion mass spectrometry (SIMS) were considered. The complete analysis sequence from sample preparation, over measurements, to data analysis and data format for reporting and archiving is outlined. All selected methods are used in surface analysis since many years so that many aspects of the analysis (including (meta)data formats) are already standardized. As a practical analysis use case, two coated TiO2 reference nanoparticulate samples, which are available on the Joint Research Centre (JRC) repository, were selected. The added value of the complementary analysis is highlighted based on the minimum information requirements, which are well-defined for the analysis methods selected. The present paper is supposed to serve primarily as a source of understanding of the high standardization level already available for the high-quality data in surface analysis of nanomaterials as reliable input for the nanosafety community. KW - Electron microscopy KW - X-ray photoelectron spectroscopy KW - Secondary ion mass spectrometry KW - Energy dispersive X-ray spectroscopy KW - Standardization PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-522683 DO - https://doi.org/10.3390/nano11030639 VL - 11 IS - 3 SP - 639 PB - MDPI AN - OPUS4-52268 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Radnik, Jörg A1 - Chemello, Giovanni A1 - Hodoroaba, Vasile-Dan A1 - Howe, T. A1 - Vyas, N. A1 - Reed, B. P. A1 - Pollard, A. J. A1 - Clifford, C. A. T1 - Reliable Chemical Characterization Protocols for Industrial Graphene-Related Materials N2 - Since its isolation, graphene has received growing attention from academia and industry due to its unique properties. Promising opportunities for applications are discussed in different field like electronics and optoelectronics, detection, and sensing devices, biosystems or chemical and environmental corrosion inhibition. Here, functionalization with elements like oxygen, nitrogen or fluorine can broaden the application, for example in composite materials. However, lack of generally accepted operation procedures hinders the commercialization, the so-called “what is my material” barrier. Therefore, first efforts were done to develop common, reliable, and reproducible ways to characterize the morphological and chemical properties of the industrially produced material. In this contribution, our efforts in the development of reliable chemical characterizations protocols for functionalized graphene are presented. An ISO standard for the chemical characterization of graphene-related (GRM) is under development with X-ray photoelectron spectroscopy (XPS) having a prominent role. With its information depth of around 10 nm, which is the similar length scale as the thickness of particles of 2D materials consisting of a few monolayers, XPS seems to be highly suitable for the quantitative analysis of (functionalized) GRM. Thereby, different sample preparation methods like pressing the powders onto adhesive tapes, into recesses, or into solid pellets result in inconsistencies in the quantification. Furthermore, different morphologies like stacks of graphene layers (left figure) or irregular particles (right figure) lead to different analysis results for the chemical composition. For the validation of the quantification with XPS and the further development of standards an international interlaboratory comparison was initiated under the head of the “Versailles Project on Advanced Materials and Standards” (VAMAS). First results are reported showing the suitability of the protocols. Finally, the XPS results are compared with the elemental composition results obtained after quantification with energy-dispersive X-ray spectroscopy (EDS) as a fast analytical method which is usually combined with electron microscopy. T2 - nanoSAFE 2023 CY - Grenoble, France DA - 05.06.2023 KW - X-ray photoelectron spectroscopy KW - Functionalized graphene KW - Interlaboratory comparison KW - VAMAS PY - 2023 AN - OPUS4-57652 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Radnik, Jörg A1 - Chemello, Giovanni A1 - Hodoroaba, Vasile-Dan A1 - Howe, T. A1 - Vyas, N. A1 - Reed, B.P. A1 - Pollard, A.J. A1 - Clifford, C.A. T1 - Reliable chemical characterization of industrial graphene related materials N2 - International standards describing reliable protocols will facilitate the commercialization of graphene and related 2D materials. One physico-chemical key property next to flake size and thickness is the chemical composition of the material. Therefore, an ISO standard is under development with X-ray photoelectron spectroscopy having a prominent role. With its information depth of around 10 nm which is the similar length scale as the thickness as of particles of 2D materials consisting of a few monolayer XPS seems to be highly suitable for this purpose. Different sample preparation methods like pressing the powders onto adhesive tapes, into recesses, or into solid pellets result in inconsistencies in the quantification. For the validation of the quantification with XPS an interlaboratory comparison was initiated under the auspice of the “Versailles Project on Advanced Materials and Standards” (VAMAS). First results confirm that the sample preparation method (pellet vs. powder) influences the quantification results clearly. Considering this effect, a good agreement of the results from the different participants were observed. Similar results were observed for raw, N- and F-functionalized graphene. T2 - Graphene CY - Manchester, England, UK DA - 27.06.2023 KW - X-ray photoelectron spectroscopy KW - Functionalized graphene KW - Interlaboratory comparison KW - VAMAS PY - 2023 AN - OPUS4-57895 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Radnik, Jörg A1 - Chemello, Giovanni A1 - Knigge, Xenia A1 - Al-Sabbgh, Dominik A1 - Hodoroaba, Vasile-Dan T1 - XPS, HAXPES, XRD and SEM datasets of functionalized graphene nanoplateletes N2 - The datasets from (Hard Energy) X-ray photoelectron spectroscopy, X-ray diffraction and Scanning Electron Microsopy are related to the publication G. Chemello, X. Knigge, D. Ciornii, B.P. Reed, A.J. Pollard, C.A. Clifford, T. Howe, N. Vyas, V.-D. Hodoroaba, J. Radnik "Influence of the morphology on the functionalization of graphene nanoplatelets analyzed by comparative photoelectron spectroscopy with soft and hard X-rays" Advanced Materials Interfaces (2023), DOI: 10.1002/admi.202300116. KW - Graphene related 2D materials KW - X-ray photoelectron spectroscopy KW - Hard-energy X-ray photoelectron spectroscopy KW - Scanning electron microscopy KW - Powder X-ray diffraction PY - 2023 DO - https://doi.org/10.5281/zenodo.7956497 PB - Zenodo CY - Geneva AN - OPUS4-57898 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hünger, K.-J. A1 - Kositz, M. A1 - Danneberg, M. A1 - Radnik, Jörg T1 - Enrichment of aluminium in the near‐surface region of natural quartzite rock after aluminium exposure N2 - Alkali–silica reaction (ASR) is an ongoing problem that causes damage to concrete constructions and reduces their durability. Therefore, minimizing this undesired reaction is of great interest for both safety and economic reasons. Additives containing high aluminium content are very effective in reducing the release of silica and enhancing the durability of concrete; however, the mechanism for this effect is still under discussion. In this study, an enrichment of aluminium in the near‐surface region was observed for natural quartzite rock after storage in Al (OH)3 and metakaolin as aluminium sources, from which we conclude that the formation of aluminosilicate sheets of a few nanometres inhibits the silica release; this hypothesis is supported by high‐resolution spectra of Al 2p, Si 2p and O 1s. KW - Alkali-silica reaction KW - Quartzite rock KW - X-ray photoelectron spectroscopy PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-519394 DO - https://doi.org/10.1002/sia.6918 SN - 0142-2421 SP - 1 EP - 7 PB - Wiley VCH AN - OPUS4-51939 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Radnik, Jörg T1 - How to perform reliable xps-measurements? N2 - Reliable measurements are a great challenge in X-ray photoelectron spectroscopy. It will be shown, how to check the performance and calibration of the instrument, the charge compensation, quantification, fitting, and depth profiling. T2 - Course for PhD students at SFB 1073 CY - Göttingen, Germany DA - 23.02.2024 KW - X-ray photoelectron spectroscopy KW - Reproducibility crisis KW - Reliability PY - 2024 AN - OPUS4-59590 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -