TY - JOUR A1 - Hüsken, Götz A1 - Shamsuddoha, Md A1 - Pirskawetz, Stephan A1 - Hofmann, Detlef A1 - Baeßler, Matthias A1 - Kühne, Hans-Carsten T1 - Potential of a Repair System for Grouted Connections in Offshore Structures: Development and Experimental Verification JF - Marine Structures N2 - Grouted connections are intensively used in offshore rigs, platforms as well as jacket and monopile offshore wind turbine structures. Being located in remote offshore conditions, these connections can experience considerable adverse loading during their lifetimes. Degradation was reported inside similar connections, which were installed in the last three decades. Grouting in the offshore sites may often be proven difficult, which eventually leads to reduced load-bearing capacity of connections in the long run. Thus, repair and rehabilitation of such connections should be planned ahead to minimize operational delays and costs. In this study, scaled grouted connections were manufactured using a novel mould, whose integrity were monitored using digital image correlation (DIC). The connections were loaded under static load to visualize the main failure pattern using distributed fibre optic sensors and acoustic emission (AE) analysis. Grouted connections were then repaired using a cementitious injectable grout. The effectiveness of the grout injection was monitored using dye penetration technique. Finally, specimens are reloaded to identify the potential of such repair for grouted connections. KW - Offshore KW - Grouted connection KW - Fibre optic sensors KW - Acoustic emission analysis KW - Cracks KW - Repair KW - Rehabilitation KW - Static loading PY - 2021 DO - https://doi.org/10.1016/j.marstruc.2021.102934 VL - 77 SP - 102934 PB - Elsevier Ltd. AN - OPUS4-52059 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Niederleithinger, Ernst A1 - Wolf, Julia A1 - Mielentz, Frank A1 - Wiggenhauser, Herbert A1 - Pirskawetz, Stephan T1 - Embedded ultrasonic transducers for active and passive concrete monitoring JF - Sensors N2 - Recently developed new transducers for ultrasonic transmission, which can be embedded right into concrete, are now used for non-destructive permanent monitoring of concrete. They can be installed during construction or thereafter. Large volumes of concrete can be monitored for changes of material properties by a limited number of transducers. The transducer design, the main properties as well as installation procedures are presented. It is shown that compressional waves with a central frequency of 62 kHz are mainly generated around the transducer's axis. The transducer can be used as a transmitter or receiver. Application examples demonstrate that the transducers can be used to monitor concrete conditions parameters (stress, temperature, …) as well as damages in an early state or the detection of acoustic events (e.g., crack opening). Besides application in civil engineering our setups can also be used for model studies in geosciences. KW - Ultrasound KW - Transmission KW - Concrete KW - Damages KW - Cracks KW - Stress KW - Monitoring KW - Acoustic emission KW - Transducers KW - Coda wave interferometry PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-345632 DO - https://doi.org/10.3390/s150509756 SN - 1424-8220 VL - 15 IS - 5 SP - 9756 EP - 9772 PB - MDPI CY - Basel AN - OPUS4-34563 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pahlavan, L. A1 - Pirskawetz, Stephan A1 - Hüsken, Götz A1 - Blacquière, G. T1 - Sensitivity of ultrasonic waves to surface-breaking cracks in reinforced concrete beams T2 - Progress in Acoustic Emission XVIII N2 - The interaction mechanism of ultrasonic waves with surface-breaking cracks in reinforced concrete has been studied. For this, a detailed numerical analysis of the medium was first conducted using the spectral finite element method. Subsequently, measurements were conducted on a reinforced beam sample before and after mechanical-load-induced cracking. It was concluded that for the considered configuration, waves passing through the cracks dominated the tip-diffracted ones. In addition, substantial changes in the travel time and amplitude of the signals were observed when cracks were present. T2 - 8th International Conference on Acoustic Emission - IIIAE 2016 CY - Kyoto, Japan DA - 5 December 2016 KW - Ultrasonic waves KW - Reinforced concrete beam KW - Cracks PY - 2016 SP - 237 EP - 242 AN - OPUS4-38913 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Shamsuddoha, Md A1 - Baeßler, Matthias A1 - Hüsken, Götz A1 - Pirskawetz, Stephan A1 - Kühne, Hans-Carsten A1 - Thiele, Marc ED - Banjad Pecur, Ivana ED - Baricevic, Ana ED - Stirmer, Nina ED - Bjegovic, Dubravka T1 - Identification of failure pattern in cylindrical grouted connection for wind structures - a pilot study T2 - Proceedings of the 1st International Conference on Construction Materials for Sustainable Future N2 - At present, Wind Turbine Generators (WTGs) operating in onshore and offshore wind farms are primary sources of renewable energy around the world. Cylindrical grouted sleeve connections are usually adopted in these WTG structures to connect the upper structure and foundation for ease of installation. These structures including grouted connections experience considerable adverse loading during their lifetimes. Settlements were reported inside similar connections used in energy structures especially oil and gas platforms, which were installed in last three decades. Thus, repair and rehabilitation of such connections in existing wind structures should also be planned ahead to keep them operating in the future. The nature of failure and crack generation in grouted connections are crucial prior to adopt a strengthening strategy. This pilot study is carried out to actualize the failure mechanism in the grouted connection, when subjected to axial loading. A novel reusable scaled cylindrical grouted connection with shear keys was designed and tested for its load bearing behaviour. The mechanical test was accompanied by classical measuring techniques (e.g. displacement transducer) as well as non-destructive measuring techniques (e.g. digital image correlation (DIC), acoustic emission analysis (AE)). The failure mechanism incorporating slippage of the shear keys and cracking of the grout was investigated. The capacity and applicability of such test mould were also discussed. The knowledge is expected to pave way towards repair of deteriorated grouted connections with similar geometry and failure pattern. T2 - 1st International Conference on Construction Materials for Sustainable Future (CoMS_2017) CY - Zadar, Croatia DA - 19.04.2017 KW - Grouted connections KW - Cracks KW - Failure KW - Strengthening strategy KW - Digital image correlation KW - Acoustic emission analysis PY - 2017 SN - 978-953-8168-04-8 SP - 544 EP - 551 AN - OPUS4-39914 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Shamsuddoha,, Md A1 - Hüsken, Götz A1 - Pirskawetz, Stephan A1 - Baeßler, Matthias A1 - Kühne, Hans-Carsten A1 - Thiele, Marc T1 - Remediation of Cracks Formed in Grouted Connections of Offshore Energy Structures under Static Loads T2 - Proceedings of the Twenty-eighth (2018) International Ocean and Polar Engineering Conference N2 - The future energy demand necessitates the exploration of all potential energy sources both onshore and offshore. Global trend has shifted towards offshore energy, which can be obtained from either carbon intensive or renewable options, hence requiring structures such as rigs, platforms, and monopiles. Most of these structures adopt easily installable construction techniques, where lower foundation need to be connected with the super structure by mean of grouted composite joints. Generally, these composite connections have exterior sleeve, interior pile and infill grout. Being located in remote offshore conditions, connections can experience considerable adverse loading during their lifetimes. Degradations were reported inside similar connections, which were installed in last three decades. Besides, grouting in the offshore sites may often be proven difficult, which eventually leads to reduced capacity of connections in the long run. Thus, repair and rehabilitation of such connections should be planned ahead to minimize operational delays and costs in the future. This study aims at characterizing the nature of crack generation in grouted connections and thereby identifying the potential of repair using suitable repair material. Scaled grouted joints were manufactured using a novel mold, and connections were loaded under static load to visualize the main failure pattern. The failure mechanism and loading capacity are found compatible to previous results from earlier literature. Grouted connection was then repaired using cementitious injectable grout. The effectiveness of the repair system is also discussed. T2 - Twenty-eighth (2018) International Ocean and Polar Engineering Conference CY - Sapporo, Japan DA - 10.06.2018 KW - Offshore KW - Energy KW - Grouted Connection KW - Cracks KW - Repair KW - Rehabilitation PY - 2018 SP - 120 EP - 126 AN - OPUS4-45227 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wolf, Julia A1 - Pirskawetz, Stephan A1 - Zang, A. T1 - Detection of crack propagation in concrete with embedded ultrasonic sensors JF - Engineering fracture mechanics N2 - This study evaluates the sensitivity of embedded ultrasonic sensors to detect propagating cracks within concrete. Because of the sensors constant coupling to the medium, highly sensitive data analysis techniques, such as the correlation between signals and their attenuation, are applied to detect changes in the signal due to propagating cracks. The accuracy of the detected onset of the crack is evaluated with the nondestructive testing methods acoustic emission and Digital Image Correlation. It shows that with embedded ultrasonic sensors crack propagation can be detected before it is visible on the surface of the concrete. KW - Embedded sensors KW - Ultrasound KW - Acoustic emission KW - Concrete KW - Cracks PY - 2015 DO - https://doi.org/10.1016/j.engfracmech.2015.07.058 SN - 0013-7944 SN - 1873-7315 VL - 146 SP - 161 EP - 171 PB - Elsevier Science CY - Kidlington AN - OPUS4-34479 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -