TY - GEN A1 - Fedelich, Bernard A1 - Kiyak, Yusuf A1 - May, Thomas A1 - Pfennig, Anja ED - Gdoutos, E. T1 - Simulation of crack growth under low cycle fatigue at high temperature in a single crystal superalloy T2 - 16th European Conference of Fracture "Fracture of Nano and Engineering Materials and Structures" CY - Alexandroupolis, Greece DA - 2006-07-03 KW - Simulation KW - Experiment KW - Crack growth KW - Low cycle fatigue KW - High temperature KW - Single crystal KW - Superalloy KW - Oxidation PY - 2006 SN - 1-402-04971-4 IS - 900_tra SP - 8 pages PB - Springer CY - Dordrecht AN - OPUS4-12556 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Schulz, Sabrina A1 - Kranzmann, Axel T1 - Supercritical CO2-corrosion of steels in CCS environment T2 - TMS 2013, The Minerals, Metals & Materials Society, 142nd Annual Meeting CY - San Antonio, TX, USA DA - 2013-03-03 PY - 2013 AN - OPUS4-27934 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Linke, Barbara A1 - Schulz, Sabrina A1 - Kranzmann, Axel T1 - Supercritical CO2-corrosion in pipe steels during carbon capture and storage CCS T2 - 4th International Conference on Sustainable Energy and Environment CY - Bangkok, Thailand DA - 2012-02-23 PY - 2012 AN - OPUS4-27935 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Schulz, Sabrina A1 - Kranzmann, Axel T1 - Influence of pressure, CO2 and cromium-content of injection pipe steels on the reliability of a saline aquifer water CCS-site in the Northern German Basin T2 - Green House Gase Emission Reduction Technologies Conference (GHGT11) CY - Kyoto, Japan DA - 2012-11-18 PY - 2012 AN - OPUS4-27936 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Wiegand, Reiner A1 - Wolf, Marcus A1 - Kranzmann, Axel A1 - Bork, Claus-Peter T1 - Corrosion fatigue behavior and S-N-curve of AiSi 420 exposed to CCS-environment obtained from laboratory in-situ-experiments T2 - Green House Gase Emission Reduction Technologies Conference (GHGT11) CY - Kyoto, Japan DA - 2012-11-18 PY - 2012 AN - OPUS4-27937 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Zastrow, Philip A1 - Kranzmann, Axel T1 - Supercritical CO2-corrosion in heat treated pipe steels during carbon capture and storage CCS T2 - Sustainable Future Energy 2012 and 10th SEE Forum CY - Brunei Darussalam DA - 2012-11-21 PY - 2012 AN - OPUS4-27938 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Zastrow, Philip A1 - Wiegand, Reiner A1 - Wolf, Marcus A1 - Kranzmann, Axel T1 - Determining Corrosion behaviour of steels from experiments in CCS-conditions T2 - 9th International Congress "Machines, Technologies, Materials" CY - Varna, Bulgaria DA - 2012-09-19 PY - 2012 AN - OPUS4-27939 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Zastrow, Philip A1 - Kranzmann, Axel T1 - Influence of heat treatment on the corrosion behaviour of stainless steels exposed to CO2-saturated saline aquifer water T2 - EUROCORR 2012 CY - Istanbul, Turkey DA - 2012-09-09 PY - 2012 AN - OPUS4-27940 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Schulz, Sabrina A1 - Werlitz, T. A1 - Bülow, E. A1 - Wetzlich, S. A1 - Tietböhl, J. A1 - Frieslich, C. A1 - Kranzmann, Axel T1 - Predicting the life time of steels in CCS environment from long term local corrosion experiments T2 - 20th International Confernece on Modelling, Monitoring and Management of Air Pollution (Air Pollution XX) CY - A Coruna, Spain DA - 2012-05-16 PY - 2012 AN - OPUS4-27941 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Schulz, S. A1 - Werlitz, T. A1 - Bülow, E. A1 - Wetzlich, S. A1 - Tietböhl, J. A1 - Frieslich, C. A1 - Kranzmann, Axel T1 - Influence of heat treatment on the corrosion of steels in CCS environment T2 - TMS 2012 - 141st Annual Meeting & Exhibition CY - Orlando, FL, USA DA - 2012-03-11 KW - CCS KW - Carbon capture and storage KW - Corrosion KW - Steel KW - Pipeline KW - Carbon KW - Heat treatment KW - CO2-storage PY - 2012 SN - 978-1-11829-607-3 VL - 1 IS - Supplemental Proceedings SP - 103 EP - 110 PB - John Wiley & Sons CY - Hoboken, NJ, USA AN - OPUS4-28007 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Linke, B. A1 - Schulze, S. A1 - Kranzmann, Axel T1 - Corrosion in pipe steels exposed to supercritical CO2 during carbon capture and storage CCS N2 - The CCS technique involves the compression of emission gasses in deep geological layers. To guarantee the safety of the site, CO2-corrosion of the injection pipe steels has to be given special attention when engineering CCS-sites. To get to know the corrosion behaviour samples of the heat treated steel 1.72252CrMo4, used for casing, and the stainless injection-pipe steel 1.4034 X46Cr13 were kept at T=60 °C and ambient pressure as well as p=100 bar for 700 h - 8000 h in a CC 2-saturated synthetic aquifer environment similar to possible geological on-shore CCS-sites in the northern German Basin. The isothermal corrosion behaviour obtained by mass gain of the steels in the gas phase, the liquid phase and the intermediate phase gives surface corrosion rates around 0.1 to 0.8 mm/year at ambient pressure and much lower about 0.02 to 0.2 mm/year at 100 bar where the CO 2 is in its supercritical state. Severe pit corrosion with pit heights around 4.5 mm are only located on the 42CrMo4 steel. Main phase of the continuous complicated multi-layered carbonate/oxide structure is siderite FeCO 3 in both types of steel. T2 - EUROCORR 2011 - Developing solutions for the global challenge CY - Stockholm, Sweden DA - 04.09.2011 KW - Steel KW - Pipeline KW - Corrosion KW - Carbonate layer KW - CCS KW - CO2-storage PY - 2011 SP - Paper 1044-1 EP - Paper 1044-8 AN - OPUS4-28008 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Linke, B. A1 - Schulze, S. A1 - Kranzmann, Axel T1 - Static and dynamic long term corrosion experiments in CCS-conditions N2 - Dealing with first corrosion screening experiments to predict the reliability and safety of Germanys first Carbon Capture and Storage site in the northern Bassin of Germany, northwest of the Capital Berlin, laboratory experiments have been established to simulate the particular conditions at T=60 °C, highly saline aquifer water similar to 'Stuttgart Aquifer', but only at ambient pressure. With mounting 2 independent full 2-grade titanium autoclave systems (running up to 250 bar and 300 °C) pressures up to p=100 bar are possible. In 2010 a specific corrosion chamber of 2-grade titanium working up to 100 °C, flowing aqui fer water with different gas mixtures was designed to fit to a high cycle fatigue testing machine. Long term fatigue experiments simulating fatigue crack growth under corrosive environments will soon start. These experiments may not only help engineering a CCS site, but results can be used to improve the maintenance of geothermal energy production sites, especially moved parts such as pumps and shafts. T2 - EUROCORR 2011 - Developing solutions for the global challenge CY - Stockholm, Sweden DA - 04.09.2011 KW - CO2 KW - Static corrosion KW - High cycle fatigue KW - Steel KW - CCS KW - CO2-storage KW - Corrosion PY - 2011 SP - 1 EP - 7 (Paper 1087) AN - OPUS4-28009 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Schulz, Sabrina A1 - Kranzmann, Axel A1 - Werlitz, T. A1 - Bülow, E. A1 - Wetzlich, S. A1 - Frieslich, C. A1 - Tietböhl, J. T1 - Influence of heat treatment on the corrosion of steels in CCS Environment T2 - TMS 2012, 141st Annual Meeting and Exhibition CY - Orlando, FL, USA DA - 2012-03-11 PY - 2012 AN - OPUS4-27942 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Wolf, Marcus A1 - Bork, Claus-Peter T1 - Corrosion fatigue of X46Cr13 at 60 °C exposed to CO2-saturated geothermal brine N2 - In geothermal power plants the materials used in pumps are loaded cyclically and exposed constantly to the highly corrosive hot thermal water. The lifetime reduction of AISI 420C (X46Cr13, 1.4034) is demonstrated in in-situ-laboratory experiments (T=60 °C, geothermal brine: Stuttgart Aquifer flow rate: 9 l/h, CO2). S-N plots, micrographic-, phase-, fractographic- and surface analysis were applied to obtain sustainable information on the corrosion fatigue behavior. Maximum number of cycles (here 12.5 x 106 cycles to failure) is reached at σa =173 MPa. No typical fatigue strength exists and passive corrosion fatigue may be identified as failure cause. T2 - EUROCORR 2012 - The European corrosion congress CY - Istanbul, Turkey DA - 2012-09-09 KW - Steel KW - Corrosion fatigue KW - Corrosion chamber KW - CCS KW - CO2-storage PY - 2012 SP - 1 EP - 11 AN - OPUS4-28586 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pfennig, Anja A1 - Kranzmann, Axel T1 - Reliability of pipe steels with different amounts of C and Cr during onshore carbon dioxide injection N2 - During the compression of emission gasses into deep geological layers (Carbon Dioxide Capture and Storage, CCS) CO2-corrosion will become a relevant safety issue. The reliability of the steels used at a geological onshore CCS-site in the Northern German Bassin 42CrMo4 (1.7225, AISI 4140) used for casing, and the injection pipe steels X46Cr13 (1.4034, AISI 420 C), X20Cr13 (1.4021, AISI 420 J) as well as X35CrMo17 (1.4122) is demonstrated in laboratory experiments. Samples were kept in a synthetic aquifer environment at T = 60 °C. This corrosive environment is then saturated with technical CO2 at a flow rate of 3 l/h. Microstructures were characterized by X-ray diffraction, light microscopy, scanning electron microscopy, and energy dispersive X-ray analysis, after a series of heat treatments (700 h to 2 years). The non-linear isothermal surface corrosion behaviour of the steels reveals surface corrosion rates around 0.1–0.8 mm/year, when obtained by mass gain. Severe pit corrosion (pit heights ca. 4.5 mm) are only located on the injection pipe steels. Main phases of the continuous scales are siderite FeCO3 and goethite α-FeOOH. The formation of the non-protective layer is likely to form via a transient Fe(OH)2-phase. KW - Steel KW - Pipe KW - Corrosion KW - Carbonate layer KW - CO2-injection KW - CO2-storage CCS PY - 2011 DO - https://doi.org/10.1016/j.ijggc.2011.03.006 SN - 1750-5836 VL - 5 IS - 4 SP - 757 EP - 769 PB - Elsevier CY - New York, NY [u.a.] AN - OPUS4-25533 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Schulz, Sabrina A1 - Linke, Barbara A1 - Kranzmann, Axel T1 - Supercritical CO2-corrosion in pipe steels during carbon capture and storage CCS N2 - The CCS technique involves the compression of emission gasses in deep geological layers. To guarantee the safety of the site, C02-corrosion of the injection pipe steels has to be given special attention when engineering CCSsites. To get to know the corrosion behaviour samples of the heat treated Steel 1.72252CrMo4, used for casing, and the stainless injection-pipe Steel 1.4034 X46Cr 13 were kept at T=60 °C and ambient pressure as well as p=100 bar for 700 h - 8000 h in a C02-saturated synthetic aquifer environment similar to possible geological on-shore CCS-sites in the northern German Basin. The isothermal corrosion behaviour obtained by mass gain of the steels in the gas phase, the liquid phase and the intermediate phase gives surface corrosion rates around 0.1 to 0.8 mm/year at ambient pressure and much lower about 0.02 to 0.2 mm/year at 100 bar where the C02 is in its supercritical state. Severe pit corrosion with pit heights around 4.5 mm are only located on the 42CrMo4 Steel. Main phase of the continuous complicated multi-layered carbonate/oxide structure is siderite FeCO} in both types of Steel. T2 - 4th International conference on sustainable energy and environment (SEE 2011) - A paradigm shift to low carbon society CY - Bangkok, Thailand DA - 23.11.2011 KW - Steel KW - Pipeline KW - Corrosion KW - Carbonate layer KW - CCS KW - Supercritical CO2- KW - CO2-storage PY - 2011 SP - 1 EP - 6 AN - OPUS4-25534 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Linke, Barbara A1 - Schulz, Sabrina A1 - Kranzmann, Axel T1 - Supercritical CO2-corrosion in pipe steels during carbon capture and storage CCS N2 - The CCS technique involves the compression of emission gasses in deep geological layers. To guarantee the safety of the site, CC>2-corrosion of the injection pipe steels has to be given special attention when engineering CCS-sites. To get to know the corrosion behaviour samples of the heat treated Steel 1.72252CrMo4, used for casing, and the stainless injection-pipe Steel 1.4034 X46Crl3 were kept at T=60 °C and ambient pressure as well as p=100 bar for 700 h - 8000 h in a CC>2-saturated synthetic aquifer environment similar to possible geological onshore CCS-sites in the northern German Basin. The isothermal corrosion behaviour obtained by mass gain of the steels in the gas phase, the liquid phase and the intermediate phase gives surface corrosion rates around 0.1 to 0.8 mm/year at ambient pressure and much lower about 0.02 to 0.2 mm/year at 100 bar where the CO2 is in its supercritical state. Severe pit corrosion with pit heights around 4.5 mm are only located on the 42CrMo4 Steel. Main phase of the continuous complicated multi-layered carbonate/oxide structure is siderite FeCCh in both types of Steel. T2 - 3rd International congress on green process engineering (GPE 2011) CY - Kuala-Lumpur, Malaysia DA - 06.12.2011 KW - Steel KW - Pipeline KW - Corrosion KW - Carbonate layer KW - CCS KW - Supercritical CO2- KW - CO2-storage PY - 2011 SP - 1 EP - 6 AN - OPUS4-25535 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Wojtas, P. A1 - Spengler, I. A1 - Kranzmann, Axel T1 - Effect of heat treatment of injection pipe steels on the formation of local corrosion in CCS-environment N2 - When engineering a Carbon Capture and Storage site (CCS) local corrosion (pitting) of the injection pipe steel may become an issue when emission gasses from oxyfuel power plants are compressed into deep geological layers. This highly corrosive environment arises when the flue gasses, mainly composed of CO2 , are injected into saline aquifer water. Immediately carbonic acid is formed causing corrosive attack of the injection steels. The influence of heat treatment on the local corrosion resistance was demonstrated in laboratory experiments at 60 °C and ambient pressure for three steels X46Cr13 (1.4034), X20Cr13 (1.4021) and X5CrNiCuNb16-4 (1.4543) under a similar liquid corrosive environment as found at a geological onshore CCS-site in the Northern German Bassin. T2 - 2nd Oxyfuel combustion conference CY - Yeppoon, Queensland, Australia DA - 12.09.2011 KW - Steel KW - Pipe KW - Corrosion KW - Heat treatment KW - CO2-injection KW - CO2-storage CCS KW - Carbonate KW - Ambient pressure KW - CCS KW - Steels PY - 2011 SP - 1 EP - 3 AN - OPUS4-25536 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kiyak, Yusuf A1 - Fedelich, Bernard A1 - May, Thomas A1 - Pfennig, Anja T1 - Simulation of crack growth under low cycle fatigue at high temperature in a single crystal superalloy N2 - Crack growth tests have been performed at 950 °C with Single Edge Notch specimens of the Ni-based single crystal superalloy PWA1483. In particular, several orientations and frequencies have been investigated, thus allowing the assessment of the influence of these parameters on the crack growth rate. In addition, oxidation experiments have been carried out to characterize the kinetics of the outer oxide scale growth at the same temperature. On the other side, crack growth has been simulated with the Finite Element program ABAQUS in real test conditions by the node release technique. The nodes are released according to the measured crack growth rate. The simulation results are compared with the test results on the basis of the computed Crack Tip Opening Displacement (CTOD). For this purpose, the crack is propagated until a stabilized value of the CTOD is obtained. This is usually the case when the crack has crossed the initial plastic zone. The procedure provides an evaluation of the effects of cycle frequency, crystal orientation, plasticity and oxide induced crack closure. KW - Finite element analysis KW - Low cycle fatigue KW - Creep-fatigue KW - Crack growth KW - Nickel-based superalloys PY - 2008 DO - https://doi.org/10.1016/j.engfracmech.2007.08.002 SN - 0013-7944 SN - 1873-7315 VL - 75 IS - 8 SP - 2418 EP - 2443 PB - Elsevier Science CY - Kidlington AN - OPUS4-16690 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Kranzmann, Axel T1 - Oxidation of a single crystal Nickel-Base Superalloy at 950°C - a kinetik and microstructure study T2 - NACE Corrosion Conference CY - New Orleans, LA, USA DA - 2008-03-16 PY - 2008 AN - OPUS4-17196 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Kranzmann, Axel T1 - Oxidation of a single crystal nickel-base superalloy at 950 °C - a kinetic and microstructure study N2 - The nickel-base single crystal alloy investigated is a widely used material for first and second row blades in stationary gas turbines. Nickel-base superalloys are especially designed to resist high temperature oxidation by process gases. To determine this high temperature behaviour oxidation testing was carried out using samples cut perpendicular to (001)-direction. Microstructures were characterized by X-ray diffraction XRD, Light Microscopy LM, Scanning Electron Microscopy SEM, and X-ray energy dispersive spectroscopy (EDS), after a series of heat treatments (950 °C, 0 h - 1000 h). Mass gain and the respective thicknesses of the different oxide layers were measured to determine oxidation kinetics. In general, the isothermal oxidation behaviour at 950 °C, as defined by weight gain, follows a parabolic law with a parabolic rate constant around 1.4 · 10-2 mg2/(cm4 · h). A short incubation time is followed by the constitution of a multi-layered oxide scale. The oxide scale consists of a three layer structure. An outer scale contains a Ti-bearing thin film associated as TiO2 and NiTiO3 but mostly Cr attributed to Cr2O3, (Ni/Co)Cr2O4 beside NiTaO4. This outer scale is connected to a discontinuous layer of inner oxidation consisting mainly of Al2O3, which is followed by an area of γ´-depletion within the base material. PY - 2008 SP - 1 EP - 9 AN - OPUS4-17263 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pfennig, Anja T1 - Isothermal Oxidation Behaviour and Microstructure of the single crystal superalloy PWA 1483 at 950° C N2 - To determine the high temperature behaviour of the single crystal Ni-base superalloy PWA 1483 oxidation testing (950° C, 0 h - 1000 h) in air was carried out using samples cut perpendicular to (001)-direction. T2 - 1st EUCOMAS Conference CY - Berlin, Germany DA - 2008-05-26 PY - 2008 SN - 978-3-18-092028-3 SN - 0083-5560 IS - 2028 SP - 391 EP - 392 PB - VDI-Verl. CY - Düsseldorf AN - OPUS4-17548 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Kranzmann, Axel T1 - Isothermal oxidation behavior and microstructure of the single crystal superalloy PWA 1483 at 950 C T2 - EUCOMAS 1st European Conference on Materials and Structures in Aerospace CY - Berlin, Germany DA - 2008-05-26 PY - 2008 AN - OPUS4-17686 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pfennig, Anja A1 - Kranzmann, Axel ED - Roland Span, ED - Ingo Weber, T1 - Effect of CO2 on the stability of steels with 1% and 13% Cr in saline water T2 - 15th International Conference on the Properties of Water and Steam (ICPWS XV), "Water, Steam, and Aqueous Solutions - Advances in Science and Technology for Power Generation" CY - Berlin, Germany DA - 2008-09-07 KW - Steel KW - Corrosion KW - Injection tube KW - Carbonate scale KW - CO2-storage KW - CO2-injection PY - 2008 SN - 978-3-931384-64-7 IS - Session 06: Electro-12 SP - 1 EP - 11 AN - OPUS4-17869 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pfennig, Anja A1 - Fedelich, Bernard T1 - Oxidation of single crystal PWA 1483 at 950 °C in flowing air N2 - The oxidation behaviour of single crystal PWA 1483 at 950 °C was investigated by means of XRD, SEM and EDS. The parabolic oxidation behaviour, as defined by mass gain and the respective oxide layer thicknesses, is characterized by a parabolic rate constant of about 4 × 10-6 mg²/(cm4 × s) and the formation of a multi-layered oxide scale. An outer scale contains a Ti-bearing thin film composed of TiO2 and NiTiO3 but mostly Cr in Cr2O3 and (Ni/Co)Cr2O4 besides NiTaO4. This outer scale is connected to a discontinuous layer of Al2O3 and an area of γ?'-depletion within the base material. KW - A. Superalloys KW - B. Weight loss KW - C. Oxidation KW - C. High temperature corrosion KW - C. Kinetic parameters PY - 2008 DO - https://doi.org/10.1016/j.corsci.2008.06.033 SN - 0010-938X VL - 50 IS - 9 SP - 2484 EP - 2492 PB - Elsevier CY - Orlando, Fla. AN - OPUS4-17879 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pfennig, Anja A1 - Wolf, Marcus A1 - Wiegand, Reiner A1 - Kranzmann, Axel A1 - Bork, Claus-Peter T1 - Corrosion fatigue behavior and S-N-curve of X46Cr13 exposed to CCS-environment obtained from laboratory in-situ-experiments N2 - In corrosive environments such as CCS bore holes or geothermal power plants the materials loaded cyclically are also exposed constantly to the highly corrosive hot thermal water. The lifetime reduction of (X46Cr13, AISI 420C) is demonstrated in in-situ-laboratory experiments (T=60 °C, geothermal brine: Stuttgart Aquifer flow rate: 9 Nl/h, CO2). S-N plots, micrographic-, phase-, fractographic- and surface analysis were applied to obtain sustainable information on the corrosion fatigue behavior. Maximum number of cycles (here 12.5 x 106 cycles to failure) is reached at σa =173 MPa. No typical fatigue strength exists and passive corrosion fatigue is most likely failure cause. KW - Steel KW - Supercritical CO2 KW - Pipeline KW - Corrosion KW - CCS KW - CO2-storage PY - 2013 DO - https://doi.org/10.1016/j.egypro.2013.06.499 SN - 1876-6102 VL - 37 SP - 5764 EP - 5772 PB - Elsevier Ltd. CY - Amsterdam AN - OPUS4-29342 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pfennig, Anja A1 - Kranzmann, Axel ED - C.A. Brebbia, ED - V. Popov, T1 - Influence of CO2 on the corrosion behaviour of 13Cr martensitic stainless steel AISI 420 and low-alloyed steel AISI 4140 exposed to saline aquifer water environment T2 - 17th International Conference on Modelling, Monitoring and Management of Air Pollution CY - Tallinn, Estonia DA - 2009-07-20 KW - Steel KW - Pipeline KW - Corrosion KW - CCS KW - Carbon capture KW - CO2-injection PY - 2009 SN - 978-1-84564-195-5 DO - https://doi.org/10.2495/AIR090371 SN - 1746-448X SN - 1746-3541 VL - 123 SP - 409 EP - 418 PB - WIT Press AN - OPUS4-19783 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pfennig, Anja A1 - Linke, Barbara A1 - Kranzmann, Axel T1 - Carbon capture and storage technique (CCS): Reliability of pipe steels used in Ketzin, Germany verified in laboratory saline aquifer corrosion experiments N2 - During the compression emission gasses in deep geological layers (Carbon Capture and Storage, CCS) CO2-corrosion will become a relevant safety issue. The reliability of the steels used at the geological onshore CCS-site at Ketzin, Germany, (heat treated steel 42CrMo4 (1.7225, AISI 4140) used for casing, and the martensitic stainless injection pipe steels X46Cr13 (1.4034, AISI 420 C), X20Cr13 (1.4021, AISI 420 J), X35CrMo17 (1.4122)) is demonstrated in 1 and 2 years laboratory experiments. Samples were kept in a synthetic aquifer environment similar to the geological CCS-site at Ketzin, Germany at T=60 °C. This corrosive environment is then saturated with technical CO2 at a flow rate of 3 l/h. Microstructures were characterized by X-ray diffraction, light microscopy, scanning electron microscopy, and energy dispersive X-ray, after a series of heat treatments (700 h to 2 years). Due to very slow mass loss at extended exposure times to CCS-environment one year is sufficient to predict stable surface corrosion rates from laboratory experiments. The non-linear isothermal surface corrosion behaviour of the steels reveals surface corrosion rates around 0.1 to 0.8 mm/year, when obtained by mass gain. The loss of the base material is higher when calculated from the corrosion layer magnitude due to the unpredictable local corrosion attacks. Severe pit corrosion (pit heights ca. 4.5 mm) are only located on the high chromium steels. Main phases of the continuous scales are siderite FeCO3 and goethite α-FeOOH. The formation of the non-protective layer is likely to form via a transient Fe(OH)2-phase. T2 - MWWD & IEMES 2010 - 6th International conference on marine waste water discharges and coastal environment CY - Langkawi, Malaysia DA - 2010-10-25 KW - Saline aquiver KW - Environmental issues KW - CCS KW - CO2-injection KW - CO2-storage KW - Corrosion KW - Phase formation PY - 2010 SN - 978-9944-5566-4-4 IS - Paper 047_P SP - 1 EP - 17 AN - OPUS4-22333 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pfennig, Anja A1 - Wojtas, P. A1 - Spengler, I. A1 - Linke, B. A1 - Kranzmann, Axel ED - Villacampa, V. ED - Brebbia, C.A. ED - Mammoli, A.A. T1 - Influence of heat treatment on the corrosion behavior of steels exposed to CCS environment N2 - The influence of heat treatment on pit corrosion needs to be considered to guarantee reliability and safety during the injection of compressed emission gasses – mainly containing CO2 – into deep geological layers (CCS-technology, Carbon Capture and Storage). In laboratory experiments different heat treated steels used as injection pipe with 13% Chromium and 0.46% Carbon (X46Cr13, 1.4034) as well as 0.2% Carbon (X20Cr13, 1.4021) were tested. Also X5CrNiCuNb16-4 (1.4542) was investigated as typical steel used for geothermal pumps. Keeping stable environmental conditions in laboratory experiments the samples were exposed to the distinct synthetic aquifer environment saturated with technical CO2 at a flow rate of 3 l/h for up to 6 months. Independent of the exposure time the least amount of pits is found on hardened steels with martensitic microstructure where X5CrNiCuNb16-4 shows fewer pits than X46Cr13 and X20Cr13. Regarding steels with similar Cr-content the higher Ccontent in 1.4034 results in fewer pits compared to 1.4021. KW - Steel KW - Heat treatment KW - Pit corrosion KW - CCS KW - CO2-injection KW - CO2-storage PY - 2011 SN - 978-1-84564-508-3 DO - https://doi.org/10.2495/ESUS110411 SN - 1746-448X SN - 1743-3541 SP - 487 EP - 498 PB - WIT Press CY - Southampton, UK AN - OPUS4-23840 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Linke, Barbara A1 - Kranzmann, Axel T1 - Corrosion behavior of pipe steels at the CCS-site Ketzin, Germany T2 - 10. Technologietransfertrag CY - Wildau, Germany DA - 2011-06-22 PY - 2011 AN - OPUS4-25492 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Wolf, Marcus A1 - Wiegand, Reiner A1 - Bork, Claus-Peter T1 - Predicting corrosion fatigue of steels in geothermal environment from new laboratory insitu measurement technique T2 - EnMat 2013, 2nd International Conference on Materials for Energy CY - Karlsruhe, Germany DA - 2013-05-12 PY - 2013 AN - OPUS4-30521 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pfennig, Anja A1 - Kranzmann, Axel T1 - Effects of saline aquifere water on the corrosion behaviour of injection pipe steels 1.4034 and 1.7225 during exposure to CO2 environment N2 - CO2-corrosion of injection pipe steels is a relevant safety issue when emission gasses are compressed in deep geological layers (CCS). The reliability of the steels used at the geological onshore CCS-site at Ketzin, Germany, is demonstrated in laboratory experiments under an equivalent corrosive environment (T=60 °C,p=1-60 bar, aquifer water, CO2-flow rate of 3 l/h, 700 h–8000 h heat treatment). Corrosion kinetics and microstructures were characterized using samples of the heat treated steel 1.7225 (AISI 4140, 42CrMo4) used for casing, and samples of the martensitic stainless injection-pipe steel 1.4034 (AISI 420, X46Cr13). KW - Steel KW - Pipeline KW - Corrosion KW - Carbonate layer KW - CCS KW - CO2-injection KW - CO2-storage PY - 2009 DO - https://doi.org/10.1016/j.egypro.2009.02.080 SN - 1876-6102 VL - 1 IS - 1 SP - 3023 EP - 3029 PB - Elsevier CY - Amsterdam AN - OPUS4-19393 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Kranzmann, Axel T1 - Integrity of casing and injection pipe steels during carbon capture and storage CCS N2 - During carbon capture and storage (CCS) CO2-corrosion of pipe steels is a relevant safety issue when emission gasses are compressed in deep geological layers. The reliability of the steels 42CrMo4, X20Cr13, X46Cr13 and X35CrMo17 is demonstrated in long term laboratory experiments up to 2 years of exposure time. Testings were carried out at ambient pressure under an equivalent corrosive environment as found at the geological onshore CCS-site at Ketzin, Germany (T=60 °C, aquifer water). T2 - i-SUP 2010 (Innovation for Sustainable Production) CY - Bruges, Belgium DA - 2010-04-18 KW - CCS KW - Corrosion rate KW - Corrosion layer KW - Steel KW - Pipeline PY - 2010 SP - 1 EP - 5(?) AN - OPUS4-23620 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pfennig, Anja A1 - Linke, Barbara A1 - Kranzmann, Axel T1 - Corrosion behaviour of pipe steels exposed for 2 years to CO2 -saturated saline aquifer environment similar to the CCS-site Ketzin, Germany N2 - When emission gasses are compressed into deep geological layers (CCS) CO2-corrosion of injection pipe steels is a relevant safety issue. The reliability of the steels used at the geological onshore CCS-site at Ketzin, Germany, is demonstrated in 2 years laboratory experiments under an equivalent corrosive environment at ambient pressure (T=60 °C, aquifer water, CO2-flow rate of 3 l/h). Corrosion kinetics and microstructures were characterized using samples of the heat treated steel 42CrMo4 (casing), and samples of the martensitic stainless steel X46Cr13 (injection). KW - Steel KW - Pipeline KW - Corrosion KW - CCS KW - CO2-storage PY - 2011 SN - 1876-6102 VL - 4 SP - 5122 EP - 5129 PB - Elsevier CY - Amsterdam AN - OPUS4-23621 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pfennig, Anja A1 - Kranzmann, Axel T1 - Influence of CO2 on the corrosion behaviour of 13%Cr martensitic stainless steel AISI 420 and low alloyed steel AISI 4140 exposed to saline aquifer water environment T2 - International Conference on Environment 2008 (ICENV 2008) - Environmental Management and Technologies Towards Sustainable Development CY - Penang, Malaysia DA - 2008-12-15 KW - Steel KW - Pipeline KW - Corrosion KW - Carbonate layer KW - CCS KW - CO2-injection KW - CO2-storage PY - 2008 SN - 978-983-3986-39-2 SP - 1 EP - 9 AN - OPUS4-18669 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pfennig, Anja A1 - Bäßler, Ralph T1 - Effect of CO2 on the stability of steels with 1% and 13% Cr in saline water N2 - In engineering storage sites for Carbon Sequestration the CO2-induced corrosion of injection pipe steels is a relevant safety issue when emission gasses are compressed in deep geological layers. The reliability of the steels suitable for the geological onshore CCS-site (Carbon Capture and Storage) at Ketzin, Germany, is demonstrated in laboratory experiments in equivalent corrosive environment (T = 60 °C, p = 1–60 bar, aquifer water, CO2-flow rate of 3 L/h, 700–8000 h exposure time). Corrosion kinetics and microstructures were characterized using specimens of the heat treated steel 42CrMo4 (1.7225) used for casing, and specimens of the martensitic stainless injection-pipe steel X46Cr13 (1.4034). KW - Corrosion KW - Layer products KW - Kinetics KW - Steel KW - Carbon Capture and Storage KW - Low alloyed steel KW - Stainless steel KW - SEM KW - Pitting corrosion KW - Kinetic parameters PY - 2009 DO - https://doi.org/10.1016/j.corsci.2009.01.025 SN - 0010-938X VL - 51 IS - 4 SP - 931 EP - 940 PB - Elsevier CY - Orlando, Fla. AN - OPUS4-19144 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Kranzmann, Axel T1 - Borehole integrity of austenitized and annealed pipe steels suitable for carbon capture and storage (CCS) N2 - Properties of pipe steels for CCS (carbon capture and storage) technology require resistance against the corrosive environment of a potential CCS-site (heat, pressure, salinity of the aquifer, CO2-partial pressure). The influence of austenitzing in heat treatment routines of two different injection pipe Steels (1.4034, X46Cr13 and 1.4021, X20Cr13) was evaluated. Steel coupons were austenitized at different temperatures (900- 1050 °C) for different lengths of time (30-90 min) before quenching and annealing prior to long term corrosion experiments (60°C, 100 bar, artificial brine close to a CCS-site in the Northern German Basin, Germany). In general, fewer pits are found on X46Cr13. Comparing steels with 13% chromium each the higher carbon content of X46Cr13 (0.46% C) results in a lower number of pits compared to X20Cr13 (0.20% C). It is found that neither the carbon content of the steels nor austenitizing temperature has much influence, but local corrosion behaviour is most susceptible towards austenitzing time. T2 - 2016 APCBEES Pattaya Conference CY - Pattaya, Thailand DA - 23.01.2016 KW - Heat Treatment KW - CCS KW - CO2 KW - Corrosion KW - Steel PY - 2016 AN - OPUS4-38444 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pfennig, Anja A1 - Schiz, J. A1 - Kranzmann, Axel ED - Jha, A. ED - Wang, C. ED - Neelameggham, N.R. ED - Guillen, D.P. ED - Li, L. ED - Belt, C.K. ED - Kirchain, R. ED - Spangenberger, J.S. ED - Johnson, F. ED - Gomes, A.J. ED - Pandey, A. ED - Hosemann, P. T1 - The role of austenitizing routines of pipe steels during CCS N2 - Properties of pipe steels for CCS technology require resistance against the corrosive environment of a potential CCS-site (heat, pressure, salinity of the aquifer, CO2-partial pressure). The influence of austenitizing in heat treatment routines of two different injection pipe steels (1.4034, X46Cr13 and 1.4021, X20Cr13) was evaluated. Steel coupons were austenitized at different temperatures (900 – 1050 °C) for different lengths of time (30–90 min) before quenching and annealing prior to long term corrosion experiments (60°C, 100 bar, artificial brine close to a CCS-site in the Northern German Basin, Germany). In general, fewer pits are found on X46Cr13. Comparing steels with 13% chromium each the higher carbon content of X46Cr13 (0.46% C) results in a lower number of pits compared to X20Cr13 (0.20% C). It is found that neither the carbon content of the steels nor austenitizing temperature has much influence, but local corrosion behaviour is most susceptible towards austenitizing time KW - Corrosion KW - CCS KW - Carbon storage KW - Aquifer KW - Austenitizing PY - 2015 SN - 978-1-119-08240-8 DO - https://doi.org/10.1002/9781119093220.ch15 SP - 131 EP - 137 PB - Wiley AN - OPUS4-34924 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Schiz, Johann A1 - Kranzmann, Axel T1 - The Role of Austenitizing Routines of Pipe Steels During CCS T2 - TMS 2015 144th Annual Meeting & Exhibition CY - Orlando, Florida, USA DA - 2015-03-15 PY - 2015 AN - OPUS4-34745 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Wolf, Marcus T1 - High-Temperatur-High Pressure Stress-Strain Testing of Materials in CO2-Containing Saline Solutions T2 - TMS 2015, 144th Annual Meeting and Exhibition CY - Orlando, Florida, USA DA - 2015-03-15 PY - 2015 AN - OPUS4-34746 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Kranzmann, Axel T1 - Einfluss der Wärmebehandlung auf die Korrosionsbeständigkeit von hochlegierten Chromhaltigen Stählen unter CCS-Bedingungen T2 - Kraftwerksforum 2015 CY - Dresden, Germany DA - 2015-10-13 PY - 2015 AN - OPUS4-34828 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Kranzmann, Axel T1 - Borehole integrity of austenitized and annealed pipe steels suitable for carbon capture and storage (CCS) N2 - Properties of pipe steels for CCS (carbon capture and storage) technology require resistance against the corrosive environment of a potential CCS-site (heat, pressure, salinity of the aquifer, CO2-partial pressure). The influence of austenitzing in heat treatment routines of two different injection pipe steels (1.4034, X46Cr13 and 1.4021, X20Cr13) was evaluated. Steel coupons were austenitized at different temperatures (900-1050 °C) for different lengths of time (30-90 min) before quenching and annealing prior to long term corrosion experiments (60°C, 100 bar, artificial brine close to a CCS-site in the Northern German Basin, Germany). In general, fewer pits are found on X46Cr13. Comparing steels with 13% chromium each the higher carbon content of X46Cr13 (0.46% C) results in a lower number of pits compared to X20Cr13 (0.20% C). It is found that neither the carbon content of the steels nor austenitizing temperature has much influence, but local corrosion behaviour is most susceptible towards austenitzing time. T2 - 6th International Conference on Future Environment and Energy (ICFEE 2016) CY - Pattaya, Thailand DA - 23.01.2016 KW - CCS KW - CO2 KW - Corrosion KW - Steel KW - Heat treatment PY - 2016 SP - 9 EP - 14 AN - OPUS4-38980 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Wolthusen, Helmut A1 - Zastrow, Philip A1 - Kranzmann, Axel T1 - Evaluation of heat treatment performance of potential pipe steels in CCS-environment T2 - TMS 2015 144th Annual Meeting & Exhibition CY - Orlando, Florida, USA DA - 2015-03-15 PY - 2015 AN - OPUS4-34744 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Kranzmann, Axel T1 - Einfluss der Wärmebehandlung auf die Korrosionsbeständigkeit von hochlegierten chromhaltigen Stählen unter CCS-Bedingungen N2 - Proben unterschiedlich wärmebehandelter, hochlegierter, rostfreier Stahlqualitäten, die potenziell als Injektionsrohr-Stähle eingesetzt werden können - AISI 420 X46Cr13, AISI 420J X20Cr13 und AISI 630 X5CrNICuNb16-4 - wurden bei 60 °C sowohl bei Normaldruck als auch bei 100 bar für 700 bis 8.000 Stunden in einem C02-gesättigtem, synthetisch hergestellten Laboraquiferwasser ausgelagert. Dieses Laboraquiferwasser entspricht der erwarteten Zusammensetzung des Aquiferwassers des norddeutschen Beckens, in das im CCS- Versuchsfeld von Ketzin (CCS Carbon Capture and Storage) über zwei Jahre hinweg technisch reines C02 injiziert wurde. Die Korrosionsraten und Schichtwachstumsraten auf den Stählen sind am niedrigsten für Stähle, die vor der Langzeitauslagerung gehärtet und anschließend zwischen 600 °C und 670 °C angelassen wurden. Lokale Korrosion (Lochfraß) zeigt sich in Form von kleinsten Löchern auf der Stahloberfläche. Der Durchmesser dieser Löcher nimmt mit steigendem Kohlenstoffgehalt des Stahls ab. Gleichzeitig nimmt die Anzahl der gezählten Löcher auf der Oberfläche zu. Insgesamt wird festgestellt, dass Stähle mit einer martensitischen Gefügestruktur in dieser nachempfundenen CCS-Atmosphäre die beste Korrosionsbeständigkeit gegenüber dem C02-gesättigten, salinen Aquifer bietet. T2 - 47. Kraftwerktechnisches Kolloquium CY - Dresden, Germany DA - 13.10.2015 PY - 2015 SN - 978-3-934409-70-5 SP - 926 EP - 936 PB - SAXONIA CY - Freiberg AN - OPUS4-35008 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pfennig, Anja A1 - Wolf, Marcus A1 - Schulze, Thomas ED - Knaut, M. T1 - Werkstoffcharakterisierung für Implantattechnologie in in-situ Ermüdungsversuchen KW - Werkstoffcharakterisierung KW - Schwingungskorrosion PY - 2014 SN - 978-3-8305-3368-9 SP - 160 EP - 165 PB - BWV - Berliner Wissenschafts-Verlag CY - Berlin AN - OPUS4-31208 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pfennig, Anja A1 - Kranzmann, Axel A1 - Wolthusen, Helmut T1 - Unusual Corrosion Behavior of 1.4542 Exposed a Laboratory Saline Aquifer Water CCS-Environment N2 - Differently heat treated coupons of 1.4542 were kept at T=60 °C and ambient pressure as well as p=100 bar for 700 h - 8000 h in an a) water saturated supercritical CO2 and b) CO2-saturated synthetic aquifer environment similar to on-shore CCS-sites in the Northern German Basin. Surface corrosion layers are homogeneous but unusually discontinuously ellipsoidal. After 8000 h at 100 bar maximum corrosion rate in the liquid phase is approximately 0.014 mm/year, with normalizing providing best corrosion resistance and approximately 0.003 mm/year in the supercritical phase where hardening+tempering at 670 °C leads to lowest corrosion rates. KW - CO2-storage KW - Supercritical CO2 KW - Steel KW - Pipeline KW - Corrosion KW - CCS PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-418472 DO - https://doi.org/10.1016/j.egypro.2017.03.1679 VL - 114 SP - 5229 EP - 5240 PB - Elsevier Ltd. AN - OPUS4-41847 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Wolf, Marcus A1 - Gröber, Andre A1 - Böllinghaus, Thomas A1 - Kranzmann, Axel T1 - Corrosion fatigue of 1.4542 exposed to a laboratory saline aquifer water CCS-environment N2 - X5CrNiCuNb16-4 has been proven to be sufficient resistant in corrosive environments, but shows rather unusual corrosion behaviour in CCS environment. Therefore a series of 30 specimens was tested at stress amplitudes between 150 MPa and 500 MPa (sinusoidal dynamic test loads, R=-1; resonant frequency ∼ 30 Hz). Due to the rather heterogeneous fine machined surfaces (Rz=4) the specimens are comparable with prefabricated parts. X5CrNiCuNb16-4 reached the maximum number of cycles (10 x 106) at a stress amplitude of 150 MPa and lies 60% below the stress amplitude measured in air. The scatter range TN = 1:34 is disproportionately large. Although the fracture surface exhibited the typical striations and corroded surface areas no significant differences were found. The hardness was found to be homogeneous in all specimens tested at 335 HV10. Non-metallic inclusions were found within the microstructure, but no correlation could be found between the inclusions and early rupture. Still specimens that showed inclusions at the fracture surface and its cross section endured lower number of cycles. Additionally Aluminium was analysed in specimens with low number of cycles and may be cause for early rupture during corrosion fatigue tests. These findings reveal a very high sensitivity on a homogeneous microstructure upon the corrosion and corrosion fatigue behaviour of X5CrNiCuNb16-4 and needs to be taken into account when regarding this steel as pipe steel during injection of CO2 into saline aquifers. T2 - 13th International Conference on Greenhouse Gas Control Technologies CY - Lausanne, Switzerland DA - 14.11.2016 KW - Steel KW - Corrosion fatigue KW - Electrochemistry KW - Reliability KW - CCS KW - CO2-storage PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-418525 DO - https://doi.org/10.1016/j.egypro.2017.03.1678 SN - 1876-6102 VL - 114 SP - 5219 EP - 5228 AN - OPUS4-41852 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Kranzmann, Axel T1 - Borehole integrity of austenitized and annealed pipe steels suitable for carbon capture and storage (CCS) N2 - Properties of pipe steels for CCS (carbon capture and storage) technology require resistance against the corrosive environment of a potential CCS-site (heat, pressure, salinity of the aquifer, CO2-partial pressure). The influence of austenitzing in heat treatment routines of two different injection pipe steels (1.4034, X46Cr13 and 1.4021, X20Cr13) was evaluated. Steel coupons were austenitized at different temperatures (900- 1050 °C) for different lengths of time (30-90 min) before quenching and annealing prior to long term corrosion experiments (60°C, 100 bar, artificial brine close to a CCS-site in the Northern German Basin, Germany). In general, fewer pits are found on X46Cr13. Comparing steels with 13% chromium each the higher carbon content of X46Cr13 (0.46% C) results in a lower number of pits compared to X20Cr13 (0.20% C). It is found that neither the carbon content of the steels nor austenitizing temperature has much influence, but local corrosion behaviour is most susceptible towards austenitzing time. T2 - International Conference on Future Environment and Energy CY - Pattaya, Thailand DA - 23.01.2016 KW - Corrosion KW - CCS KW - Carbon storage KW - Aquifer KW - Austenitizing PY - 2017 SP - Article A0005, 213 EP - 219 AN - OPUS4-41854 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pfennig, Anja A1 - Kranzmann, Axel T1 - Potential of martensitic stainless steel X5CrNiCuNb 16-4 as pipe steel in corrosive CCS environment N2 - Pipe steels suitable for carbon capture and storage technology (CCS) require resistance against the corrosive environment of a potential CCS-site (heat, pressure, salinity of the aquifer, CO2-partial pressure). X5CrNiCuNb16-4 has been proven to be sufficient resistant in corrosive environments, but shows rather unusual corrosion behaviour in CCS environment. Therefore differently heat treated coupons of 1.4542 were kept at T=60 °C and ambient pressure as well as p=100 bar for 700 h - 8000 h in an a) water saturated supercritical CO2 and b) CO2-saturated synthetic aquifer environment similar to on-shore CCS-sites in the Northern German Basin. Additionally fatigue tests were performed via push-pull tests with a series of 30 specimens was tested at stress amplitudes between 150 MPa and 500 MPa (sinusoidal dynamic test loads, R=-1; resonant frequency ~ 30 Hz). Best corrosion resistance in the liquid phase is achieved via normalizing prior to exposure and hardening+tempering at 670 °C leads to lowest corrosion rates in the supercritical phase. With no regard to atmosphere discontinuously ellipsoidal surface corrosion regions appear after exposure of 4000 h and more. The endurance limit of X5CrNiCuNb16-4 measured in air is reduced by more than 50% when exposed to CCS environment (maximum number of cycles (10 x 106) at a stress amplitude of 150 MPa) The scatter range TN = 1:34 is disproportionately large contributing to an overall unusual corrosion behaviour. KW - Corrosion KW - CCS KW - Carbon storage KW - Aquifer KW - Heat treatment KW - Fatigue KW - Endurance limit PY - 2017 DO - https://doi.org/10.18178/ijesd.2017.8.7.998 SN - 2010-0264 VL - 8 IS - 7 SP - 466 EP - 473 AN - OPUS4-41863 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pfennig, Anja T1 - Improving Learning Outcome for GSL (German as a Second Language) Students in a Blended Learning Cumulative Assessment Material Science Course N2 - First year students especially with migration background and language deficiencies rate material science in mechanical engineering as one of the fundamental courses with high work load and necessity of language skills due to the descriptive nature of the course. Therefore a blended learning course structure using based on inverted classroom teaching scenarios was established. Heart of the self-study period are visualizing peer-to-peer lecture films supported by micro-lectures along with various online teaching materials. Although students with migration background generally scored lower in tests due to the lack of language skills improved learning outcomes are demonstrated in high quality class discussions and in overall understanding. This paper introduces the learning structure and graded activities, evaluates the course and compares results of native German-speaking students to those of students with migration background. KW - Portfolio KW - Diversity KW - Blended learning KW - Inverted classroom KW - Lecture films PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-541557 DO - https://doi.org/10.17706/ijeeee.2021.11.3.93-100 SN - 2010-3654 VL - 11 IS - 3 SP - 93 EP - 100 AN - OPUS4-54155 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -