TY - CONF A1 - Hünert, Daniela A1 - Schulz, Wencke A1 - Nitschke, Heike A1 - Saliwan Neumann, Romeo A1 - Oder, Gabriele A1 - Kranzmann, Axel T1 - Corrosion behaviour of ferritic and martensitic power plant steels under conditions of dual atmospheres N2 - The most efficient construction materials for boiler water walls and superheaters in steam power plants are ferritic and martensitic steels. In practical operation tubes are simultaneously exposed to combustion gas and air/steam on their opposite surfaces. The corrosion behaviour of ferritic-martensitic steels under such dual atmospheres is nondistinctive and has therefore been investigated in a special designed test equipment between 500 and 620°C. The power plant conditions were simulated wi th a flowing and pressurised (80 bar) combustion gas on the inner side of the tube which mainly consists of H2O and/or CO2. On the outer side, the tube material was exposed to air. It was discovered that under similar temperatures the oxides formed on the air side under dual atmosphere conditions were significantly different to the oxide scales formed when the alloy was exposed to air only. It is assumed that the anomalous corrosion behaviour during the dual atmosphere exposure is due to the hydrogen transport through the bulk alloy from the combustion gas side to the air side. T2 - NACE International corrosion conference 2009 CY - Atlanta, Georgia, USA DA - 2009-03-22 KW - High temperature corrosion KW - Dual atmosphere KW - Corrosive gases KW - Mild steels KW - 9-12% Cr-steels KW - Hydrogen transport PY - 2009 SP - 1 EP - 10 (Paper 09263) AN - OPUS4-22335 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rabe, Torsten A1 - Glitzky, Carsten A1 - Naghib Zadeh, Hamid A1 - Oder, Gabriele A1 - Eberstein, M. A1 - Töpfer, J. T1 - Silver in LTCC - Interfacial reactions, transport processes and influence on properties of ceramics T2 - 2009 IMAPS/ACerS - 5th International Conference and Exhibition on Ceramic Interconnect and Ceramic Microsystems Technologies (CICMT) CY - Denver, Colorado, USA DA - 2009-04-21 KW - LTCC KW - Silver conductors KW - Interface KW - Sintering KW - Ferrite KW - Capacitor PY - 2009 SN - 0-930815-87-4 SP - 000085 EP - 000093 AN - OPUS4-19428 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -