TY - JOUR A1 - Schulz, Wencke A1 - Nofz, Marianne A1 - Feigl, Michael A1 - Dörfel, Ilona A1 - Saliwan Neumann, Romeo A1 - Kranzmann, Axel T1 - Corrosion of uncoated and alumina coated steel X20CrMoV12-1 in H2O-CO2-O2 and air at 600 °C N2 - Future coal power plants will in case of oxyfuel combustion be operated with altered atmospheres. Hence, corrosion attack might become more severe and steels have to be protected. An alumina-sol was used to coat X20CrMoV12-1 (X20) with alumina to test the protection. Testing was performed at 600 °C in flowing H2O–CO2–O2 and static laboratory air for 1000 h. Oxidation under air is minor compared to exposure in oxyfuel atmosphere. In both cases a multilayered oxide (hematite, magnetite, spinel) was formed on uncoated steels. Carburization appeared on uncoated X20 in H2O–CO2–O2. The coating demonstrates a high protection. KW - A. Steel KW - B. SEM KW - B. STEM KW - C. Carburization KW - C. High temperature corrosion KW - C. Oxide coatings PY - 2013 U6 - https://doi.org/10.1016/j.corsci.2012.10.031 SN - 0010-938X VL - 68 SP - 44 EP - 50 PB - Elsevier Ltd. CY - Orlando, Fla. AN - OPUS4-27636 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schulz, Wencke A1 - Feigl, Michael A1 - Dörfel, Ilona A1 - Nofz, Marianne A1 - Kranzmann, Axel T1 - Influence of a sol-gel alumina coating on oxidation of X20CrMoV12-1 in air up to 650 °C N2 - The need for a more efficient coal power plant generation (e.g. oxyfuel technology) results in modified process parameters and enhanced corrosion. To reach the necessary service life of high temperature parts protective coatings may be a sufficient technical solution. A modified Yoldas sol (Al2O3 based) was used to coat X20CrMoV12-1 by spin coating. After appropriate heat treatments transition alumina coatings being about 400 nm thick were obtained. Oxidation studies were carried out in laboratory air at temperatures up to 650 °C for up to 500 h exposure time. In case of the uncoated sample a rough oxide layer formed on the surface and a remarkable weight gain (2.62 mg/cm²) were detected. The sol–gel alumina layer (mainly δ-Al2O3) demonstrated a high protection, i.e. a very low weight gain (0.05 mg/cm²). Diffusion of alloying elements into the coating was observed. No indication of spallation of the coating occurred. Local defects (2 µm–30 µm) in the coating led to the formation of iron-oxide islands. KW - X20CrMoV12-1 KW - Sol-gel deposition KW - Alumina KW - Air oxidation KW - Transmission electron microscopy KW - Chromium KW - Diffusion KW - Manganese PY - 2013 U6 - https://doi.org/10.1016/j.tsf.2013.04.132 SN - 0040-6090 VL - 539 SP - 29 EP - 34 PB - Elsevier B.V. CY - Amsterdam AN - OPUS4-29162 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -