TY - JOUR A1 - Nützmann, Kathrin A1 - Kranzmann, Axel A1 - Stephan-Scherb, Christiane T1 - The influence of chromium on early high temperature corrosion of ferritic alloys under SO₂ atmosphere N2 - Comprehensive insights into the early stages of corrosion mechanisms provide fundamental knowledge to further understand and model long time material behaviour. The present work studies the early stages of combined oxidation and sulphidation of ferritic model alloys for time scales up to 250 h at 650 °C to observe the influence of chromium during the corrosion under SO2. Model alloys were used to focus on the reaction of the intended elements: Fe, Cr, S, and O. Pure iron simultaneously forms magnetite and iron sulphide in an early stage of corrosion, covered by a pure oxide layer after 100 h. Iron with 13 wt% Cr shows hematite and mixed Fe-Cr-oxides first, before sulphides nucleate in the inner corrosion zone. With increasing ageing time a magnetite layer is observed below the hematite layer. Quantitative phase fractions of all corrosion products observed were determined from cross section images. Characterization of the Fe13Cr corrosion scale by FIB revealed a highly porous structure in the inner corrosion zone where Cr-rich (Fe, Cr)-sulphides are present, and caused the scale to spall easily. KW - Early stages KW - Sulphidation KW - High temperature corrosion PY - 2018 U6 - https://doi.org/10.1080/09603409.2018.1446705 SN - 0960-3409 VL - 36 IS - 6 SP - 558 EP - 568 PB - Taylor & Francis AN - OPUS4-44707 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -