TY - JOUR A1 - Mietz, Jürgen A1 - Burkert, Andreas T1 - Selection and Durability of Stainless Steels for Civil Engineering N2 - Due to the large number of stainless steels with different chemical composition and different microstructure the selection of the suitable material represents a huge challenge. In order to facilitate the appropriate grade selection, in the current European standard EN 1993-1-4 a procedure is defined based on the use of a look-up table considering the key variables that influence the selection of stainless steels. The table uses descriptions that competent designers should be able to readily understand or define without prior knowledge. The output from the look-up table is used to select alloys based on a Corrosion Resistance Class (CRC) from I to V. The advantage of this approach is that the designer simply specifies the relevant CRC and does not need to consider in detail which of the many (very similar) alloys to specify. KW - Corrosion resistance KW - Stainless steel KW - Civil engineering KW - Atmospheric corrosion PY - 2020 DO - https://doi.org/10.4028/www.scientific.net/KEM.843 SN - 1662-9795 VL - 843 SP - 125 EP - 131 PB - Trans Tech Publications Ltd, CY - Switzerland AN - OPUS4-50831 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lehmann, Jens A1 - Burkert, Andreas A1 - Mietz, Jürgen T1 - Investigations proofing the passive layer stability of stainless steels N2 - The presented investigations have proved the principal suitability of the KorroPad method to assess the passive layer stability of stainless steels. The electrochemical mode of action could be described in detail and limitations of the applicability have been demonstrated. The influence of different surface finishes has been investigated and verified by known methods for describing corrosion resistances. As a result, the increased corrosion susceptibility of two ground surfaces has been detected, but also the corrosion resistance of further surface finishes could be confirmed. KW - Stainless steel KW - KorroPad KW - Passive layer PY - 2016 DO - https://doi.org/10.1002/maco.201408202 VL - 1 IS - 67 SP - 84 EP - 91 PB - WILEY-VCH Verlag GmbH & Co. KGaA CY - Weinheim AN - OPUS4-35545 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burkert, Andreas A1 - Müller, Thoralf A1 - Lehmann, Jens A1 - Mietz, Jürgen T1 - Long-term corrosion behaviour of stainless steels in marine atmosphere N2 - Nine different stainless steel alloys were exposed for 5 years under marine environment and their corrosion behaviour was compared and assessed. The investigation of four different surface finishes for all alloys tested further enabled to consider industry-specific features of the surface finish for the material comparison. The results of the exposure tests yield conclusions regarding the influence of alloy composition, surface finish and exposure duration under marine environment. The three duplex stainless steels revealed excellent corrosion resistance even in case of crevices during the 5 years of exposure under the given exposure conditions. Also the molybdenum-alloyed ferritic steel 1.4521 showed good corrosion resistance comparable to the classical austenitic materials 1.4301 and 1.4404. KW - Corrosion KW - Free weathering KW - Marine atmosphere KW - Stainless steels PY - 2018 DO - https://doi.org/10.1002/maco.201709636 SN - 0947-5117 SN - 1521-4176 VL - 69 IS - 1 SP - 20 EP - 28 PB - Wiley-VCH Verlag GmbH & Co KGaA CY - Weinheim AN - OPUS4-43625 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Babutzka, Martin A1 - Mietz, Jürgen A1 - Burkert, Andreas T1 - Investigation of the salinization of steel surfaces in marine environment N2 - The salinization and contamination of metal surfaces by chloride-containing aerosols is of great importance with regard to corrosion phenomena of damaged coated metal surfaces and stainless steels in the maritime sector and in offshore applications. Detailed questions have to be answered to clarify whether and to what extent salinization of the surface has an influence on the adhesion and durability of coatings in repairing applications and on pitting occurrence on stainless steels under atmospheric conditions. The questions arise which degree of salinization is reached after which period of time and how a defined and reproducible salinization can be simulated in the laboratory for further systematic investigations. The article is dedicated to these questions. Results of a field trial on the Island of Heligoland are presented and a simple procedure for a defined loading of metal surfaces with chlorides at a laboratory scale using a design of experiments (DoE) approach is introduced. KW - Maritime Atmosphäre KW - Versalzung KW - Maritime atmosphere KW - Salinization PY - 2018 DO - https://doi.org/10.1002/maco.201810636 SN - 0947-5117 SN - 1521-4176 VL - 70 IS - 6 SP - 1016 EP - 1025 PB - Wiley-VCH Verlag CY - Weinheim AN - OPUS4-47727 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burkert, Andreas A1 - Lehmann, Jens A1 - Burkert, Annette A1 - Mietz, Jürgen A1 - Gümpel, P. T1 - Technical and economical stainless steel alternatives for civil engineering applications N2 - Systematic laboratory and field exposure tests allow to compare nine different stainless steels (three ferritic, three austenitic, and three duplex grades) for civil engineering applications. The influence of surface finish was also taken into account by choosing five different industry-specific features. The three duplex stainless steels revealed excellent corrosion resistance under most of the test conditions. Especially for applications in civil engineering the lean duplex steels offer distinct advantages. The manganese-alloyed 1.4376 and the ferritic steel 1.4509 cannot be recommended as alternative materials as they did not perform satisfactorily. KW - Atmospheric corrosion KW - Duplex stainless steels KW - Exposure tests KW - Surface finish PY - 2014 DO - https://doi.org/10.1002/maco.201307057 SN - 0947-5117 SN - 1521-4176 VL - 65 IS - 11 SP - 1080 EP - 1095 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-32350 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beck, Matthias A1 - Goebbels, Jürgen A1 - Isecke, Bernd A1 - Burkert, Andreas A1 - Mietz, Jürgen T1 - Investigations of corrosion on small cathodes in reinforced concrete - observations and suggestions N2 - Corrosion of steel reinforcement in concrete exposed to chloride containing environments is a serious problem in civil engineering practice. The standards and guidelines contain only minimum requirements regarding concrete quality and concrete cover. In very critical cases, for example the ingress of chlorides, the application of different coatings is currently the only possibility to protect the reinforced concrete structures. In this case the modelling of reinforcement corrosion would be more practical. One sub-project of a DFG-research project (FOR 537) is currently performed at the Federal Institute for Materials Research and Testing (BAM). Aim of the sub-project is the description of corrosion propagation and the characterization of the corrosion on specimens with small cathodes by electrochemical parameters. The electrochemical parameters are determined by suitable electrochemical measurements, considering concrete parameters as well as different environmental conditions. T2 - EUROCORR 2009 CY - Nice, France DA - 2009-09-06 KW - Self-corrosion KW - Steel reinforcement KW - Concrete parameters KW - X-ray tomography PY - 2009 IS - Paper 7976 SP - 1 EP - 13 AN - OPUS4-20063 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fischer, Joachim A1 - Burkert, Andreas A1 - Mietz, Jürgen T1 - Case studies of stainless steel corrsoion in indoor swimming pool environments N2 - In indoor swimming pools stainless steels are used not only due to structural and economic reasons but also due to aesthetic considerations. And therefore not only safety relevant load bearing components have to fulfil their tasks but also the visual appearance should be free of any staining. In a lot of cases basic requirements (e.g. design criteria, material selection and maintenance) being essential parts of technical regulations were not taken into account. Typical case studies with explanation of the cause of the corrosion problems and possibilities to prevent them are shown in the present paper. KW - Stainless steel KW - Atmospheric corrosion KW - Indoor swimming pools PY - 2011 DO - https://doi.org/10.1179/174327809X409150 SN - 1478-422X VL - 46 IS - 1 SP - 76 EP - 79 PB - Maney Publishing CY - London, UK AN - OPUS4-23287 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mietz, Jürgen A1 - Burkert, Andreas A1 - Lehmann, Jens A1 - Eich, G. ED - Castro-Borges, P. ED - Moreno, E.I. ED - Sakai, K. ED - Gjorv, O.E. ED - Banthia, N. T1 - Risk of stress corrosion cracking of prestressing steels in contact with galvanized components T2 - CONSEC`10 - 6th International conference on concrete under severe conditions CY - Mérida, Yucatán, Mexico DA - 2010-06-07 KW - Prestressing steel KW - Galvanized elements KW - Galvanic corrosion KW - Hydrogen evolution KW - Hydrogen-induced stress corrosion cracking PY - 2010 SN - 978-0-415-59316-8 VL - 1 SP - 239 EP - 246 PB - Taylor & Francis CY - London, UK AN - OPUS4-22037 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mietz, Jürgen A1 - Burkert, Andreas A1 - Eich, Gerd A1 - Raupach, M. T1 - Development of a new combined corrosion protection system for chloride-contaminated reinforced concrete structures N2 - Chloride-induced damage of reinforcing steel is especially for parking garages and bridges often very severe as large amounts of chlorides act on horizontal surfaces which could lead to fast ingress of these detrimental ions up to the level of the reinforcement and subsequently to high rates of corrosion. In order to avoid the disadvantages of conventional rehabilitation (unreliable prognosis with patch repair or high costs and regular maintenance with cathodic protection using impressed current) a new combined protection system was developed where the principle of drying out the concrete (by means of a surface protection system) is combined with a temporary cathodic protection (by means of a sprayed zinc layer) during the transitional period of the drying out process. This new system was tested both in the laboratory and on-site at a pilot application. Based on the results obtained the possibilities and limitations of the new system are discussed in this paper. KW - Chlorid-induced corrosion KW - Reinforcing steel KW - Cathodic protection KW - Sprayed zinc layer KW - Surface protection system PY - 2005 DO - https://doi.org/10.1002/maco.200403836 SN - 0947-5117 SN - 1521-4176 VL - 56 IS - 2 SP - 104 EP - 110 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-7157 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mietz, Jürgen A1 - Burkert, Andreas A1 - Burkert, Annette A1 - Eich, Gerd T1 - Long-term Behaviour of Corrosion Protection Materials for Prestressed Systems T2 - 2nd International fib Congress CY - Naples, Italy DA - 2006-06-05 KW - Prestressed systems KW - Corrosion protection KW - Wax KW - Grease KW - Electrochemical tests PY - 2006 SN - 0-912053-94-1 SP - 12 pages PB - Society for Experimental Mechanics CY - St. Lous AN - OPUS4-12513 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -