TY - CONF A1 - Beck, Matthias A1 - Goebbels, Jürgen A1 - Isecke, Bernd A1 - Burkert, Andreas A1 - Mietz, Jürgen T1 - Investigations of corrosion on small cathodes in reinforced concrete - observations and suggestions N2 - Corrosion of steel reinforcement in concrete exposed to chloride containing environments is a serious problem in civil engineering practice. The standards and guidelines contain only minimum requirements regarding concrete quality and concrete cover. In very critical cases, for example the ingress of chlorides, the application of different coatings is currently the only possibility to protect the reinforced concrete structures. In this case the modelling of reinforcement corrosion would be more practical. One sub-project of a DFG-research project (FOR 537) is currently performed at the Federal Institute for Materials Research and Testing (BAM). Aim of the sub-project is the description of corrosion propagation and the characterization of the corrosion on specimens with small cathodes by electrochemical parameters. The electrochemical parameters are determined by suitable electrochemical measurements, considering concrete parameters as well as different environmental conditions. T2 - EUROCORR 2009 CY - Nice, France DA - 2009-09-06 KW - Self-corrosion KW - Steel reinforcement KW - Concrete parameters KW - X-ray tomography PY - 2009 IS - Paper 7976 SP - 1 EP - 13 AN - OPUS4-20063 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Isecke, Bernd A1 - Mietz, Jürgen T1 - Bau- und Instandsetzungsmethoden - Elektrochemische Schutzverfahren zur Beseitigung von Korrosionsrisiken an Stahlbetonbauwerken PY - 2003 SN - 3-935243-14-6 N1 - Serientitel: Schriftenreihe des Verbandes Deutscher Architekten- und Ingenieurvereine – Series title: Schriftenreihe des Verbandes Deutscher Architekten- und Ingenieurvereine IS - 2 SP - 149 EP - 157 PB - Verl. Das Beispiel CY - Darmstadt AN - OPUS4-2789 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Isecke, Bernd A1 - Mietz, Jürgen A1 - Schütt, K. T1 - Temporärer Korrosionsschutz von Spannstählen in unverpressten Hüllrohren PY - 2003 DO - https://doi.org/10.1002/maco.200390091 SN - 0947-5117 SN - 1521-4176 VL - 54 SP - 1 EP - 7 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-2489 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mietz, Jürgen A1 - Isecke, Bernd T1 - Stainless steels for applications in civil engineering T2 - Stainless Steel World Conference & Exposition CY - The Hague, The Netherlands DA - 2001-11-13 KW - Civil engineering KW - Atmospheric corrosion conditions KW - Stainless steels KW - Stress corrosion cracking KW - Approval PY - 2001 SN - 90-73168-14-7 IS - P0108 SP - 334 EP - 339 PB - KCI Publ. CY - Zutphen AN - OPUS4-1199 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mietz, Jürgen A1 - Isecke, Bernd ED - Lange, G. T1 - Analyse von Spannbetonschäden und Strategien zu deren Vermeidung T2 - 19. Tagung Werkstoffprüfung CY - Bad Nauheim, Deutschland DA - 2001-12-06 PY - 2001 SN - 3-527-30538-6 SP - 153 EP - 158 PB - Wiley-VCH CY - Weinheim AN - OPUS4-1216 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Isecke, Bernd A1 - Mietz, Jürgen A1 - Fischer, Joachim T1 - Langzeiterfahrungen mit einem kathodischen Korrosionsschutzsystem für Stahl in Beton N2 - Im Jahr 1986 wurde in Deutschland die erste kathodische Korrosionsschutzanlage für ein Stahlbetonbauwerk in Betrieb genommen. Die Installation, die Inbetriebnahme sowie die laufende Überwachung wurden wissenschaftlich begleitet. Im Zuge notwendiger verkehrstechnisch bedingter Umbaumaßnahmen wurde die Anlage nach etwa 15 Jahren außer Betrieb genommen. Die in dieser Zeit durchgeführten Untersuchungen dienten dem Ziel, die an Laborversuchen gewonnenen Ergebnisse an einem praktischen Bauwerk zu überprüfen sowie Informationen über das Langzeitverhalten hinsichtlich Dauerhaftigkeit, Potentialverteilung, Temperaturabhängigkeit, Chloridmigration usw. zu bekommen. Mit zunehmender Betriebsdauer konnten die Schutzkriterien nur durch Erhöhung der Gleichrichterspannung eingehalten werden (die Anlage wurde im Konstantspannungsmodus betrieben). Umfangreiche Untersuchungen an Anodenmaterialproben (leitfähiger Polymerdraht mit einem Kupferkern) nach 15-jährigem Einsatz zeigten, dass irreversible Veränderungen die Leitfähigkeit des Polymers erheblich vermindert haben, wodurch letztendlich die Funktionsfähigkeit der Anode nicht mehr gegeben war. Diese Art von Anoden werden aber heutzutage nicht mehr für den kathodischen Korrosionsschutz von Stahlbetonbauwerken eingesetzt. Translated Abstract Long-term experiences with a cathodic protection system for steel in concrete In 1986 in Germany the first cathodic protection system for reinforced concrete structures was put into service. Installation, commissioning and the regular monitoring were scientifically supported. Due to necessary traffic related reconstruction measures the system was switch off after 15 years of service. Investigations carried out during that period should verify laboratory test results at a real structure and furthermore yield information on the long-term behaviour concerning durability, temperature dependence, potential distribution, chloride migration etc. With increasing time of service the protection criteria could only be met by increasing the transformer rectifier voltage (the system worked in the constant voltage mode). Extensive investigations of the anode material (conductive polymer wire with a copper core) after 15 years of service showed that irreversible changes substantially decreased the polymer's conductivity limiting the functionality. Today, these kind of anodes are not used any more for the application in cathodic protection systems of reinforced concrete structures. PY - 2001 DO - https://doi.org/10.1002/1521-4176(200112)52:12<920::AID-MACO920>3.0.CO;2-J SN - 0947-5117 SN - 1521-4176 VL - 52 IS - 12 SP - 920 EP - 930 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-1222 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mietz, Jürgen A1 - Isecke, Bernd T1 - Assessment of test methods for evaluation stress corrosion cracking susceptibility of prestressing steels N2 - Prestressing steels can be exposed in prestressed concrete structures in construction stage (ungrouted duct) to environmental conditions causing formation and growth of hydrogen induced cracks with brittle fracture of the steel. The risk of this hydrogen induced stress corrosion cracking can be minimized by appropriate treatment, but there is a requirement for construction to approve only prestressing steel having no enhanced susceptibility to stress corrosion cracking. The paper describes the historical development of the different test methods proposed in the past and gives an overview on the general requirements for a suitable test method to assess the hydrogen-induced stress corrosion susceptibility of prestressing steels. Since 1982, based on investigations on construction sites and transfer of the results into laboratory tests, a test method is available enabling realistic estimation of suitable application possibilities of prestressing steels. This so called DIBt-test is approved to distinguish between prestressing steels susceptible to hydrogen induced stress corrosion cracking and those suitable and therefore approvable steels at practical environmental conditions. Furthermore the test enables estimation of corrosion risk for newly developed prestressing steels with higher strength. Translated Abstract Beurteilung der Prüfverfahren zur Untersuchung der Spannungsrisskorrosionsempfindlichkeit von Spannstählen Spannstähle können in Spannbetonbauwerken im Bauzustand (unverpresstes Hüllrohr) Umgebungsbedingungen ausgesetzt sein, die zur Bildung und Ausbreitung wasserstoffinduzierter Risse mit Sprödbruch des Stahles führen können. Das Risiko dieser wasserstoffinduzierten Spannungsrisskorrosion kann einerseits durch eine sachgemäße Verarbeitung der Spannstähle minimiert werden, andererseits besteht die Notwendigkeit nur solche Spannstähle für die Baupraxis zuzulassen, die unter baupraktischen Bedingungen keine erhöhte Empfindlichkeit für Spannungsrisskorrosion besitzen. Die vorliegende Arbeit beschreibt die historische Entwicklung der verschiedenen vorgeschlagenen Prüfverfahren und gibt einen Überblick über die allgemeinen Anforderungen an ein geeignetes Verfahren zur Beurteilung der wasserstoffinduzierten Spannungsrisskorrosionsempfindlichkeit von Spannstählen. Seit 1982 steht, begründet durch Untersuchungen auf Baustellen und Umsetzung der Ergebnisse in Laborversuchen, ein Prüfverfahren zur Verfügung, das eine wesentlich realistischere Einschätzung der Einsatzmöglichkeiten von Spannstählen zulässt. Dieser sog. DIBt-Test hat sich bewährt, um unter praktischen Umgebungsbedingungen gegen H-induzierte Spannungsrisskorrosion empfindliche Spannstähle von geeigneten und damit zulassungswürdigen Stählen zu unterscheiden. Des weiteren erlaubt die Prüfung ebenfalls eine Abschätzung des Korrosionsrisikos für neuentwickelte, höherfeste Spannstähle. PY - 2002 SN - 0947-5117 SN - 1521-4176 VL - 53 IS - 6 SP - 373 EP - 384 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-1402 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mietz, Jürgen A1 - Isecke, Bernd A1 - Fischer, Joachim T1 - Long-term experiences with cathodic corrosion protection of steel reinforced concrete structures T2 - 15th International Corrosion Congress CY - Granada, Spain DA - 2002-09-22 PY - 2002 PB - CSIC, Spanish Council for Scientific Research CY - Madrid AN - OPUS4-1728 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Isecke, Bernd A1 - Mietz, Jürgen T1 - Einsatz nichtrostender Stähle in Schwimmbädern T2 - Fachtagung des Nederlands Corrosie Centrum CY - Breda, Niederlande DA - 2002-11-14 PY - 2002 AN - OPUS4-1845 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mietz, Jürgen A1 - Isecke, Bernd ED - Page, C. ED - Bamforth, P. ED - Figg, J. T1 - Risks of failure in prestressed concrete structures due to stress corrosion cracking T2 - 4th International Symposium on Corrosion of Reinforcement in Concrete Construction CY - Cambridge, England, UK DA - 1996-07-01 KW - Betonkonstruktion KW - Korrosion KW - Streßkorrosion KW - Stahlbeton PY - 1996 SN - 0-85404-731-X SN - 0260-6291 N1 - Serientitel: Special publication / Royal Society of Chemistry – Series title: Special publication / Royal Society of Chemistry IS - 183 SP - 200 EP - 209 PB - Royal Society of Chemistry Information Services CY - Cambridge AN - OPUS4-702 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -