TY - JOUR A1 - Burkert, Andreas A1 - Lehmann, Jens A1 - Burkert, Annette A1 - Mietz, Jürgen A1 - Gümpel, P. T1 - Technical and economical stainless steel alternatives for civil engineering applications N2 - Systematic laboratory and field exposure tests allow to compare nine different stainless steels (three ferritic, three austenitic, and three duplex grades) for civil engineering applications. The influence of surface finish was also taken into account by choosing five different industry-specific features. The three duplex stainless steels revealed excellent corrosion resistance under most of the test conditions. Especially for applications in civil engineering the lean duplex steels offer distinct advantages. The manganese-alloyed 1.4376 and the ferritic steel 1.4509 cannot be recommended as alternative materials as they did not perform satisfactorily. KW - Atmospheric corrosion KW - Duplex stainless steels KW - Exposure tests KW - Surface finish PY - 2014 DO - https://doi.org/10.1002/maco.201307057 SN - 0947-5117 SN - 1521-4176 VL - 65 IS - 11 SP - 1080 EP - 1095 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-32350 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burkert, Andreas A1 - Lehmann, Jens A1 - Burkert, Annette A1 - Mietz, Jürgen A1 - Eich, Gerd T1 - Verzinkte Bauteile im Kontakt mit Spanngliedern N2 - Um zu klären, unter welchen Umständen eine potentielle Gefährdung von Spannstählen beim Kontakt mit verzinkten Bauteilen gegeben ist, wurden Laborversuche in alkalischen Lösungen und Beton sowie Zeitstandversuche an Spannbetonprobekörpern durchgeführt. Abstandsvariationen im Nahbereich haben nur einen geringen Einfluss auf die Polarisation des Stahls. Ein praxisrelevanter, unkritischer Abstand für den indirekten Kontakt, z. B. über die schlaffe Bewehrung, kann nicht definiert werden. Hinsichtlich des Flächenverhältnisses Stahl : Zink wurde ein signifikanter Einfluss festgestellt. Flächenverhältnisse über 10 : 1 führen nicht zu einer Polarisation in den Bereich der Wasserstoffentwicklung. Die Ergebnisse wurden durch Untersuchungen an realen Spannbetonfertigteilen verifiziert. Zeitstandversuche unter Wasserstoffbeladung führten an zugelassenen Spannstählen nicht zu Brüchen während der Versuchszeit. Die anschließend ermittelten mechanischen Kennwerte zeigten keine signifikanten Änderungen. Ein indirekter Kontakt von Spannstählen zu verzinkten Einbauteilen ist deshalb als unkritisch zu bewerten. Der direkte Kontakt ist durch Einhaltung des in der DIN 1045-1 geforderten Mindestabstands von 2 cm sicher auszuschließen. KW - Spannstahl KW - Korrosion KW - Stahlbeton PY - 2008 DO - https://doi.org/10.1002/best.200800619 SN - 0005-9900 SN - 1437-1006 VL - 103 IS - 6 SP - 413 EP - 421 PB - Ernst CY - Berlin AN - OPUS4-17626 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burkert, Andreas A1 - Lehmann, Jens A1 - Burkert, Annette A1 - Mietz, Jürgen T1 - Korrosionsschäden an nichtrostenden Stählen unter atmosphärischen Einsatzbedingungen N2 - Neben konstruktiven Anforderungen werden an nichtrostende Stähle im Bauwesen häufig hohe optische Ansprüche gestellt. Unerwartete Beeinträchtigungen des optischen Erscheinungsbildes nichtrostender Stähle unter wenig korrosiven Bedingungen sind in der Zwischenzeit ein weit verbreitetes Problemfeld und Gegenstand zahlreicher Streitfälle. Vielfach wird die Vermutung geäußert, dass eine veränderte Legierungszusammensetzung, veränderte Umweltbedingungen oder auch die unsachgemäße Verarbeitung die Ursache für diese Erscheinungen sind. Durch eine systematische Untersuchung zahlreicher Schadensfälle an Stabmaterial in den vergangenen zwei Jahren im Rahmen eines Forschungsvorhabens konnte gezeigt werden, dass die Ursachen in bekannten Werkstofffehlern zu finden sind. Hierzu gehören chemische Inhomogenitäten, wie zum Beispiel Ausscheidungen und örtliche Aufkohlung, sowie geometrische Fehler, wie zum Beispiel Hinterschnitte, Walzfehler und Schalenbildung. Die Fehler konnten damit eindeutig als Herstellungsfehler der jeweiligen Halbzeuge identifiziert werden. KW - Korrosion KW - Nichtrostende Stähle KW - Atmosphäre KW - Interkristalline Korrosion KW - Schäden PY - 2010 DO - https://doi.org/10.1002/stab.201001288 SN - 0038-9145 SN - 1437-1049 SN - 0932-6375 VL - 79 IS - 5 SP - 389 EP - 395 PB - Ernst CY - Berlin AN - OPUS4-21242 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mietz, Jürgen A1 - Burkert, Andreas A1 - Burkert, Annette A1 - Eich, Gerd T1 - Long-term Behaviour of Corrosion Protection Materials for Prestressed Systems T2 - 2nd International fib Congress CY - Naples, Italy DA - 2006-06-05 KW - Prestressed systems KW - Corrosion protection KW - Wax KW - Grease KW - Electrochemical tests PY - 2006 SN - 0-912053-94-1 SP - 12 pages PB - Society for Experimental Mechanics CY - St. Lous AN - OPUS4-12513 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Mietz, Jürgen A1 - Burkert, Annette A1 - Burkert, Andreas A1 - Jonas, Bernhard A1 - Eich, Gerd A1 - Baszynski, Joachim T1 - Korrosionsschutzwirkung von Korrosionsschutzmassen für Spannglieder ohne Verbund KW - Spannstahl KW - Korrosion KW - Korrosionsschutzmittel KW - Wasseraufnahme KW - Schutzwirkung KW - Langzeitverhalten KW - Bodenkontakt PY - 2005 SN - 3-8167-6740-0 IS - T 3071 SP - 1 EP - 45 PB - IRB-Verl. CY - Stuttgart AN - OPUS4-11344 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mietz, Jürgen A1 - Burkert, Annette A1 - Burkert, Andreas A1 - Eich, Gerd T1 - Investigations on the protection effect of filling materials for post-tensioning systems under construction conditions N2 - About the long-term protection behaviour of corrosion protection materials (filling materials) for prestressed systems under critical environmental conditions is only little known. The corrosion protection effect is usually based on theoretical considerations and is proven by short-term tests. The selection of the different products is mainly made according to economical or workability criteria. In a research project the barrier effect of different commercial corrosion protection materials (waxes as well as oil-based greases) against water, their tendency for undercutting as well as their additional corrosion protection effect were investigated. The exposure tests were carried out with non-stressed as well as stressed prestressing steel specimens which were subjected to critical conditions (condensed water, artificial soil solution, direct soil contact). Parallel to these long-term exposure tests the applicability of different electrochemical techniques and their significance with respect to testing the corrosion protection ability and water absorption was evaluated. Within the project a suitable method for simple testing the performance of corrosion protection materials under real conditions was developed. By means of a small compact cell submicroscopical reactions of the used sensors could be measured. The high sensitivity of this measuring technique enables the detection of degradation processes at thin protection layers. KW - Prestressed systems KW - Corrosion KW - Corrosion protection KW - Electrochemical tests KW - Grease KW - Wax PY - 2006 DO - https://doi.org/10.1002/maco.200603986 SN - 0947-5117 SN - 1521-4176 VL - 57 IS - 11 SP - 843 EP - 851 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-13931 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Burkert, Andreas A1 - Lehmann, Jens A1 - Burkert, Annette A1 - Mietz, Jürgen A1 - Eich, Gerd T1 - Verzinkte Bauteile im Kontakt mit Spanngliedern T2 - 4. Kolloquium des Kuratoriums Korrosionsschutz (KKF) CY - Düsseldorf, Deutschland DA - 2007-06-20 KW - Spannbeton KW - Spannstahl KW - Wasserstoffinduzierte Spannungsrisskorrosion KW - Verzinkte Einbauteile KW - Zink KW - DIN 1045 PY - 2007 SN - 978-3-935406-34-5 SP - 12 EP - 25 PB - GfKORR CY - Frankfurt am Main AN - OPUS4-15018 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Eich, Gerd A1 - Burkert, Annette A1 - Burkert, Andreas A1 - Mietz, Jürgen T1 - Einsatz des nichtrostenden Duplex-Stahls 1.4362 als preisgünstige Alternative im Bauwesen N2 - Aufgrund der in den letzten Jahren stark angestiegenen Rohstoffpreise sind die im Bauwesen häufig eingesetzten nichtrostenden Standardaustenite in vielen Fällen nicht mehr wettbewerbsfähig. Eine deutlich kostengünstigere Alternative stellt der Duplex-Stahl 1.4362 dar, der bisher aber noch nicht bauaufsichtlich zugelassen ist. Mit Hilfe von Auslagerungsversuchen sowie elektrochemischen Untersuchungen sollte das Korrosionsverhalten dieses Werkstoffs unter neutralen bis leicht sauren, chloridhaltigen Umgebungsbedingungen, wie sie in vielen Bereichen des Bauwesens vorkommen, geklärt werden. Insgesamt belegen die Ergebnisse, dass der kostengünstigere Werkstoff 1.4362 für baupraktische Anwendungen eine Alternative für Anwendungen darstellen kann, in denen bisher die Werkstoffe 1.4404 oder 1.4571 eingesetzt wurden. KW - Duplex-Stähle KW - Nichtrostende Stähle KW - Auslagerungsversuche KW - Elektrochemische Versuche KW - Lochkorrosionspotential KW - Spaltkorrosionspotential PY - 2007 DO - https://doi.org/10.1002/stab.200710094 SN - 0038-9145 SN - 1437-1049 SN - 0932-6375 VL - 76 IS - 12 SP - 898 EP - 904 PB - Ernst CY - Berlin AN - OPUS4-16364 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Burkert, Andreas A1 - Mietz, Jürgen A1 - Lehmann, Jens A1 - Eich, Gerd A1 - Burkert, Annette T1 - Verzinkte Bauteile in Kontakt mit Spanngliedern (Abschlussbericht für den Zeitraum 01.02.2005 bis 31.10.2007; Forschungsvorhaben 14218 N / 1) KW - Spannbeton KW - Spannstahl KW - Wasserstoffinduzierte Spannungsrisskorrosion KW - Verzinkte Einbauteile PY - 2007 SP - 1 EP - 42 PB - Bundesanstalt für Materialforschung und -prüfung CY - Berlin AN - OPUS4-16694 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mietz, Jürgen A1 - Burkert, Andreas A1 - Lehmann, Jens A1 - Burkert, Annette A1 - Eich, Gerd T1 - Galvanised constructional elements in contact with prestressing steel tendons N2 - In order to clarify under which practical conditions real risks for hydrogen-induced stress corrosion cracking of prestressing steels exist laboratory investigations in aqueous solutions and concrete as well as tests with stressed prestressing steels were carried out. While different distances between steel and zinc (cathode and anode) showed only a negligible influence on the polarisation of the steel a significant dependence on the area ratio steel/zinc was observed. A critical area ratio of 10:1 can be defined above which polarisation of the steel to hydrogen evolution potentials is unlikely. The results obtained in the laboratory concerning the critical area ratio were confirmed by on-site investigations in a precasting plant. Exposure tests with hydrogen loading did not lead to fractures during the testing time for approved prestressing steels. The characteristic mechanical values determined immediately after the hydrogen loading tests did not show significant changes. Thus, an indirect contact between prestressing steels and galvanised elements can be estimated as uncritical. But a direct contact has to be excluded by compliance with DIN 1045-1, i.e minimal distance of 2 cm between prestressing steel and galvanised elements. PY - 2008 DO - https://doi.org/10.1002/maco.200804114 SN - 0947-5117 SN - 1521-4176 VL - 59 IS - 2 SP - 131 EP - 138 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-16724 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -