TY - JOUR A1 - Mietz, Jürgen T1 - Wasserstoffinduzierte Spannungsrißkorrosion an vergüteten Spannstählen KW - Baustoffe KW - Spannbetonbau KW - Korrosion KW - Spannungsrißkorrosion PY - 1999 SN - 0005-6650 SN - 1436-4867 N1 - Sprachen: Deutsch/Englisch - Languages: German/English VL - 74 IS - 9 SP - 403 EP - 411 PB - Springer-VDI-Verl. CY - Düsseldorf AN - OPUS4-724 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Burkert, Andreas A1 - Mietz, Jürgen A1 - Lehmann, Jens A1 - Eich, Gerd A1 - Burkert, Annette T1 - Verzinkte Bauteile in Kontakt mit Spanngliedern (Abschlussbericht für den Zeitraum 01.02.2005 bis 31.10.2007; Forschungsvorhaben 14218 N / 1) KW - Spannbeton KW - Spannstahl KW - Wasserstoffinduzierte Spannungsrisskorrosion KW - Verzinkte Einbauteile PY - 2007 SP - 1 EP - 42 PB - Bundesanstalt für Materialforschung und -prüfung CY - Berlin AN - OPUS4-16694 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Burkert, Andreas A1 - Mietz, Jürgen A1 - Lehmann, Jens A1 - Eich, Gerd A1 - Burkert, Annette T1 - Verzinkte Bauteile in Kontakt mit Spanngliedern N2 - Um zu klären unter welchen Umständen eine Gefährdung von Spannstählen beim Kontakt mit verzinkten Bauteilen gegeben ist, wurden umfangreiche Laborversuche in alkalischen Lösungen und verschiedenen Betonen sowie Zeitstandversuche an Spannbetonprobekörpern durchgeführt. Dabei zeigte sich, dass Abstandsvariationen im Nahbereich nur einen geringen Einfluss auf die Polarisation des Stahles haben. Ein praxisrelevanter, unkritischer Abstand für den indirekten Kontakt des Spannstahls, z. B. über die Bewehrung, konnte daher nicht definiert werden. Aus den Versuchsreihen wurde deutlich, dass ein wesentlicher Einfluss durch das Flächenverhältnisses Stahl: Zink gegeben ist. Hier konnte eine praxisrelevante Grenze ermittelt werden. Danach führen Flächenverhältnisse größer 10 : 1 nicht zu einer Polarisation des Spannstahls in den Bereich der Wasserstoffentwicklung. Die im Labor gewonnen Ergebnisse konnten durch Untersuchungen zunächst an realen Betonfertigteilen, später auch an Spannbetonfertigteilen bei der Fa. Rekers verifiziert werden. Auf der Grundlage dieser Untersuchungen wurde für eine spezielle Spannbetonbinderausführung, bei der die Flächenverhältnisse in unkritischen Breichen lagen, für die Verwendung von verzinkten Einbau- teilen im indirekten Kontakt mit Spannstählen eine Zustimmung im Einzelfall gegeben. Während der Vorhabensbearbeitung wurde von den beteiligten Firmen eine weitere Problematik angesprochen. Dabei ging es um den Einsatz von verzinkten Einbauteilen in Spann- betonfertigteilen aus Stahlfaserbeton. Auch hier war die Frage, ob eine Gefährdung der Spannstähle durch indirekten Kontakt über die nicht verzinkten Stahlfasern möglich ist. Durch Untersuchungen an realen Fertigteilabschnitten bei den Firmen Rekers und Max Bögl konnte gezeigt werden, dass ein Kontakt über die Stahlfasern selbst über sehr kurze Entfernungen nicht vorliegt. Auf der Grundlage dieser Ergebnisse wurden für derartige Fertigteile beim Deutschen Institut für Bautechnik entsprechende bauaufsichtliche Zulassungen unter Verwendung verzinkter Einbauteile beantragt. Um eine sichere Gefährdungsabschätzung bei indirektem Kontakt für Flächenverhältnisse vornehmen zu können, bei denen eine Polarisation der Spannstähle in den Bereich der Wasserstoffentwicklung erfolgt, wurden Zeitstandversuchsreihen unter Wasserstoffbeladung durchgeführt. Diese führten an zugelassenen Spannstählen nicht zu Brüchen während der Versuchszeit. Die anschließend ermittelten mechanischen Kennwerte zeigten keine signifikanten Änderungen. Aus den Ergebnissen dieser Untersuchungen, die bezüglich der Bela- dungsmenge, der Beladungszeiten und der gewählten Vorspannung sehr konservativ ausgelegt wurden, ist ein indirekter Kontakt von Spannstählen zu verzinkten Einbauteilen als unkritisch zu bewerten. Eine entsprechende Änderung der Norm ist anzustreben. Aus grundsätzlichen Gründen der direkte Kontakt durch Einhaltung des in der DIN 1045-1 geforderten Mindestabstandes von 2 cm aber weiterhin sicher auszuschließen. Dies stellt für die Anwender aus praktischer Sicht kein Problem dar. Durch die in enger Zusammenarbeit mit der Industrie durchgeführten Forschungsarbeiten wird es den Anwendern ermöglicht, zukünftig verzinkte Einbauteile in Spannbetonfertigteilen einzusetzen. Teilweise konnte der Einsatz durch Zustimmungen im Einzelfall bzw. durch bauaufsichtliche Zulassungen bereits unmittelbar in der Praxis umgesetzt werden. Damit wurde das Ziel des Vorhabens erreicht. T3 - BAM Forschungsberichtreihe - 282 PY - 2008 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-1695 SN - 978-3-9812072-6-2 SN - 0938-5533 VL - 282 SP - 1 EP - 28 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-169 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Burkert, Andreas A1 - Lehmann, Jens A1 - Burkert, Annette A1 - Mietz, Jürgen A1 - Eich, Gerd T1 - Verzinkte Bauteile im Kontakt mit Spanngliedern T2 - 4. Kolloquium des Kuratoriums Korrosionsschutz (KKF) CY - Düsseldorf, Deutschland DA - 2007-06-20 KW - Spannbeton KW - Spannstahl KW - Wasserstoffinduzierte Spannungsrisskorrosion KW - Verzinkte Einbauteile KW - Zink KW - DIN 1045 PY - 2007 SN - 978-3-935406-34-5 SP - 12 EP - 25 PB - GfKORR CY - Frankfurt am Main AN - OPUS4-15018 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burkert, Andreas A1 - Lehmann, Jens A1 - Burkert, Annette A1 - Mietz, Jürgen A1 - Eich, Gerd T1 - Verzinkte Bauteile im Kontakt mit Spanngliedern N2 - Um zu klären, unter welchen Umständen eine potentielle Gefährdung von Spannstählen beim Kontakt mit verzinkten Bauteilen gegeben ist, wurden Laborversuche in alkalischen Lösungen und Beton sowie Zeitstandversuche an Spannbetonprobekörpern durchgeführt. Abstandsvariationen im Nahbereich haben nur einen geringen Einfluss auf die Polarisation des Stahls. Ein praxisrelevanter, unkritischer Abstand für den indirekten Kontakt, z. B. über die schlaffe Bewehrung, kann nicht definiert werden. Hinsichtlich des Flächenverhältnisses Stahl : Zink wurde ein signifikanter Einfluss festgestellt. Flächenverhältnisse über 10 : 1 führen nicht zu einer Polarisation in den Bereich der Wasserstoffentwicklung. Die Ergebnisse wurden durch Untersuchungen an realen Spannbetonfertigteilen verifiziert. Zeitstandversuche unter Wasserstoffbeladung führten an zugelassenen Spannstählen nicht zu Brüchen während der Versuchszeit. Die anschließend ermittelten mechanischen Kennwerte zeigten keine signifikanten Änderungen. Ein indirekter Kontakt von Spannstählen zu verzinkten Einbauteilen ist deshalb als unkritisch zu bewerten. Der direkte Kontakt ist durch Einhaltung des in der DIN 1045-1 geforderten Mindestabstands von 2 cm sicher auszuschließen. KW - Spannstahl KW - Korrosion KW - Stahlbeton PY - 2008 U6 - https://doi.org/10.1002/best.200800619 SN - 0005-9900 SN - 1437-1006 VL - 103 IS - 6 SP - 413 EP - 421 PB - Ernst CY - Berlin AN - OPUS4-17626 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lehmann, Jens A1 - Burkert, Andreas A1 - Ebell, Gino A1 - Burkert, Annette A1 - Mietz, Jürgen T1 - Verwendung von verzinkten Einbauteilen in vorgespannten Fertigbetonbauteilen T2 - Tagung Korrosionsschutz der Stähle im Kontakt mit Beton - Neue Entwicklungen und Forschungsergebnisse CY - Stuttgart-Vaihingen, Deutschland DA - 2010-10-07 KW - Spannstahl KW - Wasserstoffinduzierte Spannungsrisskorrosion KW - Verzinkte Einbauteile KW - Spannbeton KW - Kathodische Polarisation KW - Einflussgrößen KW - Praktische Bedeutung PY - 2010 SN - 978-3-935406-43-7 SP - 101 EP - 114 CY - Frankfurt/M. AN - OPUS4-22199 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mietz, Jürgen A1 - Fischer, Joachim T1 - Verifizierung zerstörungsfreier Prüfverfahren zur Detektion von Spannstahlschäden an Spannbetonbauteilen mit nachträglichem Verbund N2 - For an assessment of the risk potential of existing structures where in the case of prestressing steel damage the load-bearing capacity could be significantly affected non-destructive testing techniques which enable reliable evaluation of the condition of the prestressing steels are of utmost importance. During the demolition of the Hohenzollerndamm bridge in Berlin where damage of prestressing wires due to hydrogen-induced stress corrosion cracking were found in former investigations parts of the girders of the bridge superstructure could be taken out. After non-destructive investigation by means of two testing techniques based on magnetic leakage flux measurement and one technique based on electromagnetic resonance measurement the single wires were inspected in order to verify the non-destructive testing results with respect to their reliability. From the results it can be concluded that areas with fractures of several wires could be detected by the two techniques based on magnetic leakage flux measurement. PY - 2005 U6 - https://doi.org/10.1002/best.200590181 SN - 0005-9900 SN - 1437-1006 VL - 100 IS - 8 SP - 656 EP - 663 PB - Ernst CY - Berlin AN - OPUS4-11148 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Mietz, Jürgen A1 - Raupach, M. A1 - Goltermann, P. T1 - Use of Embeddable Sensors in an Integrated Monitoring System for Reinforced Concrete Structures T2 - Corrosion 2003 CY - San Diego, CA, USA DA - 2003-03-16 KW - Chloride Induced Corrosion KW - Integrated Monitoring System KW - Embedded Sensors PY - 2003 IS - 03436 SP - 1(?) EP - 13(?) PB - NACE International CY - Houston, Tex. AN - OPUS4-2381 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mietz, Jürgen A1 - Baszynski, Joachim A1 - Fischer, Joachim T1 - Untersuchungen zur Spannungsrißkorrosionsbeständigkeit nichtrostender Stähle mit unterschiedlichem Verformungsgrad N2 - Im Rahmen der Erarbeitung einer neuen bauaufsichtlichen Zulassung für nichtrostende Stähle ergab sich die Fragestellung, ob durch eine Kaltverfestigung die Beständigkeit gegenüber Spannungsrißkorrosion negativ beeinflußt wird. Durch experimentelle Versuche an verschiedenen nichtrostenden Stählen sollte geklärt werden, ob kaltverformtes Material bei hoher Chloridbelastung, wie sie z. B. in Schwimmhallenatmosphäre vorkommen kann, eine höhere Empfindlichkeit gegenüber Spannungsrißkorrosion aufweist. Die Untersuchungen wurden mit den hochlegierten Stählen 1.4462 sowie 1.4529 durchgeführt. Als Vergleichswerkstoff mit bekannter Empfindlichkeit gegenüber Spannungsrißkorrosion bei hoher Chloridbelastung wurde der Stahl 1.4301 eingesetzt. Die Versuche erfolgten mittels Bügel- und Zugproben, auf die Tropfen aus gesättigter Magnesiumchloridlösung aufgebracht waren. Hinweise auf eine höhere Spannungsrißkorrosionsempfindlichkeit des kaltverformten Materials wurden aber sowohl bei den Versuchen mit Bügelproben als auch bei den Versuchen mit Zugproben nicht festgestellt. Translated Abstract Investigations on stress corrosion cracking resistivity of stainless steels with different degree of cold straining Within the context of the elaboration of a new approval for stainless steels for civil engineering applications the question arised whether cold straining could adversely affect the resistance against stress corrosion cracking. By means of experimental tests with different stainless steels it should be clarified whether cold straining increase the stress corrosion cracking susceptibility under high chloride loads like e.g. in swimming hall atmospheres. The investigations were carried out using the high-alloyed steels 1.4462 and 1.4529. As reference material with known susceptibility against stress corrosion cracking the steel 1.4301 was used. The tests were performed using U-bent and tension specimens with saturated MgCl2 salt spots. Indications for an increase in stress corrosion cracking susceptibility of the cold drawn steel were not found. KW - Spannungsrißkorrosionsbeständigkeit KW - Nichtrostender Stahl PY - 1999 U6 - https://doi.org/10.1002/(SICI)1521-4176(199905)50:5<273::AID-MACO273>3.0.CO;2-4 SN - 0947-5117 SN - 1521-4176 N1 - Sprachen: Deutsch/Englisch - Languages: German/English VL - 50 IS - 5 SP - 273 EP - 281 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-766 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Mietz, Jürgen A1 - Raupach, M. A1 - Ebell, Gino A1 - Poltavtseva, Marina A1 - Helm, C. T1 - Untersuchungen zur Anwendbarkeit leitfähiger Beschichtungen auf Karbonbasis für den Einsatz als Fremdstromanode im Kathodischen Korrosionsschutz von Stahlbetonbauteilen (Schlussbericht) N2 - Zur Wirkungsweise und zum Einfluss unterschiedlicher Parameter beim Kathodischen Korrosionsschutz von Stahl in Beton wurden in der Vergangenheit bereits zahlreiche Untersuchungen durchgeführt. Über die Dauerhaftigkeit leitfähiger Beschichtung auf Karbonbasis als Fremdstromanode beim KKS von Stahlbeton liegen bislang keine umfassenden wissenschaftlichen Untersuchungen vor. Die in den einzelnen Arbeitspaketen (AP) erzielten Ergebnisse und gewonnenen Erkenntnisse tragen zum Verständnis über die Elektrodenreaktion der einzelnen Systeme bei. Die Frage der Dauerhaftigkeit konnte im Rahmen dieses Forschungsvorhabens nicht zur Gänze geklärt werden. Die Ergebnisse aus dem AP 1a liefern einen wesentlichen Beitrag zur Beantwortung der offenen Fragestellung hinsichtlich der vorherrschenden Elektrodenreaktion. In Verbindung mit dem Pourbaixdiagramm für Kohlenstoff lässt sich für die Beschichtungssysteme CBCC 1 und CBCC 2, nach 500 h andauernder Polarisation mit 10 mA/m² in ges. Calziumhydroxidlösung, die vorherrschende Elektrodenreaktion als Sauerstoffelektrode verifizieren. Im AP 1b wurde festgestellt, dass die an einem Praxisobjekt applizierten Systeme CBCC 1 und CBCC 2 in der Lage sind, die Schutzkriterien zu erfüllen. Die an diesem Objekt erforderlichen Schutzspannungen liegen jeweils zwischen 1 und 2 V. Die Anodenstromdichten betragen ca. 2,5 mA/m². Aufgrund der hohen Depolarisationsraten kann das Niveau der anliegenden Anodenstromdichten in Zukunft noch nach unten angepasst werden. Die Ergebnisse aus dem AP 1b und 1a sind erst zeitlich nach Festlegung der Prüfparameter für das AP 2a erzielt worden. Mit den ursprünglich veranschlagten Stromdichten von max. 40 mA/m² traten langfristig nachfolgende Problemstellungen auf: Bei der Stromeinleitung mittels Primärelektrode und Stromdichten größer gleich 20 mA/m² wurde festgestellt, dass die Versuche bei allen Systemen eine deutliche Entkopplung zwischen Primärelektrode und Beschichtung verursacht haben. Dies ist auf die hohen lokalen Stromdichten am Übergang Primärelektrode/leitfähige Beschichtung zurückzuführen. Eine Untersuchung der erforderlichen Kontaktfläche der Primärelektrode bezogen auf die effektive Stromdichte konnte nicht erfolgen. Weiterhin wurden die Haftzugwerte über die Dauer der Polarisation untersucht und mit unpolarisierten Proben verglichen. Eine Reduktion des Verbundes infolge Polarisation mit den angesetzten Stromdichten konnte verzeichnet werden. Es wurde jedoch auch festgestellt, dass mit zunehmenden Probenalter auch reduzierte Haftzugwerte an den geschliffenen und unpolarisierten Oberflächen der Referenzprobekörper ermittelt wurden. Die Grundlagen für die Simulation konnten in AP 3 anhand der gewonnen Ergebnisse erstellt werden und Feldverteilungen unter Berücksichtigung verschiedener Parameter berechnet werden. Eine auf den gewonnenen Erkenntnisse basierende Modellentwicklung für die Dauerhaftigkeitsprognose unter variierenden Randbedingungen, wie sie für AP 4 vorgesehen war, konnte auf Basis der erzielten Ergebnisse nicht erfolgen. Dass die Beschichtungssysteme unter praxisüblichen Randbedingungen einsetzbar sind und bei dem Vergleich der Schutzspannung mit klassischen Systemaufbauten gleiche Schutzstromdichten erzielt werden, zeigt das AP 1b deutlich. Die zukünftigen Ergebnisse aus der Praxisanwendung (AP 1b) werden über die Projektlaufzeit hinaus ausgewertet und publiziert. Das Ziel des Vorhabens wurde teilweise erreicht. KW - KKS KW - Kathodischer Korrosionsschutz KW - Korrosion KW - Betonstahl KW - Stahlbeton KW - Beschichtung PY - 2015 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-336230 SP - 1 EP - 101 PB - Bundesanstalt für Materialforschung und-prüfung (BAM) / ibac RWTH Aachen AN - OPUS4-33623 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mietz, Jürgen A1 - Oldfield, J. W. T1 - The use of austenitic and duplex stainless steels in ground anchor environments T2 - International Congress Stainless Steels '96 ; Proceedings of the 2nd European congress CY - Düsseldorf and Neuss, Germany DA - 1996-06-03 KW - Stahl, austenitisch KW - Stahl, doppel rostfrei KW - Bodenanker PY - 1996 SN - 3-514-00601-6 SP - 149 EP - 156 PB - Verl. Stahleisen CY - Düsseldorf AN - OPUS4-674 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Isecke, Bernd A1 - Mietz, Jürgen A1 - Schütt, K. T1 - Temporärer Korrosionsschutz von Spannstählen in unverpressten Hüllrohren PY - 2003 U6 - https://doi.org/10.1002/maco.200390091 SN - 0947-5117 SN - 1521-4176 VL - 54 SP - 1 EP - 7 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-2489 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burkert, Andreas A1 - Lehmann, Jens A1 - Burkert, Annette A1 - Mietz, Jürgen A1 - Gümpel, P. T1 - Technische und wirtschaftliche Alternativen zu den klassischen nichtrostenden, austenitischen Stählen unter atmosphärischen Einsatzbedingungen N2 - Durch systematische Labor- und Auslagerungsuntersuchungen ist es möglich, sieben unterschiedliche nichtrostende Stahllegierungen hinsichtlich verschiedenster Anwendungen untereinander und auch in Bezug auf zwei austenitische Standardwerkstoffe (1.4301, 1.4404) zu vergleichen. Die parallele Untersuchung von fünf verschiedenen Oberflächenausführungen der jeweiligen Werkstoffe ermöglicht zudem, branchenspezifische Besonderheiten der Oberflächenausführung beim Werkstoffvergleich zu berücksichtigen. Der Einfluss der Oberflächenausführung wird überwiegend bei den Ergebnissen der Auslagerungsversuche in kritischen Atmosphären sichtbar, weniger bei den elektrochemischen Untersuchungen. Die drei Vertreter aus dem Bereich der Duplexstähle zeigten unter den meisten Untersuchungsbedingungen eine hervorragende Korrosionsbeständigkeit. Insbesondere für Anwendungen im Bauwesen können die Lean-Duplexstähle deutliche Vorteile bieten. Der Manganaustenit 1.4376 sowie der Ferrit 1.4509 sind nur eingeschränkt als Alternativen geeignet, da die Werkstoffe bei einigen Versuchen signifikante Schwächen zeigten.--------------------------------------------------------------------------- The systematic laboratory and field exposure tests allow to compare seven different stainless steels among each other and also regarding two standard austenitic materials (1.4301, 1.4401) with respect to various applications. Parallel investigations with five different surface finishes of the respective materials enable to consider also industry-specific features of the surface finish. The influence of the surface finish can mainly be seen in the results of the exposure tests in critical atmospheres and less in the electrochemical investigations. The three duplex stainless steels showed under most of the test conditions excellent corrosion resistance. Especially for applications in civil engineering the lean duplex steels offer clear advantages. The manganese alloyed 1.4376 and the ferritic steel 1.4509 are only limited suitable as alternatives as these materials showed significant weaknesses in some of the tests. KW - Nichtrostende Stähle KW - Bauwesen KW - Atmosphärische Korrosion PY - 2012 U6 - https://doi.org/10.1002/stab.201201624 SN - 0038-9145 SN - 1437-1049 SN - 0932-6375 VL - 81 IS - 11 SP - 875 EP - 888 PB - Ernst CY - Berlin AN - OPUS4-26825 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burkert, Andreas A1 - Lehmann, Jens A1 - Burkert, Annette A1 - Mietz, Jürgen A1 - Gümpel, P. T1 - Technical and economical stainless steel alternatives for civil engineering applications N2 - Systematic laboratory and field exposure tests allow to compare nine different stainless steels (three ferritic, three austenitic, and three duplex grades) for civil engineering applications. The influence of surface finish was also taken into account by choosing five different industry-specific features. The three duplex stainless steels revealed excellent corrosion resistance under most of the test conditions. Especially for applications in civil engineering the lean duplex steels offer distinct advantages. The manganese-alloyed 1.4376 and the ferritic steel 1.4509 cannot be recommended as alternative materials as they did not perform satisfactorily. KW - Atmospheric corrosion KW - Duplex stainless steels KW - Exposure tests KW - Surface finish PY - 2014 U6 - https://doi.org/10.1002/maco.201307057 SN - 0947-5117 SN - 1521-4176 VL - 65 IS - 11 SP - 1080 EP - 1095 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-32350 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mietz, Jürgen T1 - Stand der Überarbeitung zur EN 1993-1-4 - Werkstoffauswahl und Dauerhaftigkeit T2 - Arbeitskreissitzung Korrosion im Bauwesen CY - Heligoland, Germany DA - 2014-06-02 PY - 2014 AN - OPUS4-30911 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mietz, Jürgen A1 - Isecke, Bernd T1 - Stainless steels for applications in civil engineering T2 - Stainless Steel World Conference & Exposition CY - The Hague, The Netherlands DA - 2001-11-13 KW - Civil engineering KW - Atmospheric corrosion conditions KW - Stainless steels KW - Stress corrosion cracking KW - Approval PY - 2001 SN - 90-73168-14-7 IS - P0108 SP - 334 EP - 339 PB - KCI Publ. CY - Zutphen AN - OPUS4-1199 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ebell, Gino A1 - Achenbach, R. A1 - Angst, U. A1 - Dauberschmidt, C. A1 - Eichler, T. A1 - Hariri, K. A1 - Harnisch, J. A1 - Keßler, S. A1 - Kosalla, M. A1 - Mayer, T.F. A1 - Mietz, Jürgen A1 - Pruckner, F. A1 - Sodeikat, C. T1 - Specification B 12 - Corrosion monitoring in reinforced and prestressed concrete structures N2 - This specification describes how corrosion monitoring is used to check the condition of reinforced and prestressed concrete members. In this specification, the term "corrosion monitoring" covers all methods in which it is possible to continuously track corrosion-relevant variables in the area of stationary, built-in sensors. This specification does not cover other possible methods, such as potential field measurements, involving the use of mobile, portable sensors that are placed temporarily on the membersurface to take measurements. KW - Korrosion KW - Corrosion KW - Monitoring PY - 2021 SN - 978-3-947971-14-5 SP - 1 EP - 55 PB - DGZfP CY - Berlin AN - OPUS4-53092 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mietz, Jürgen A1 - Fischer, Joachim A1 - Isecke, Bernd T1 - Spannungsrißkorrosion an Spannstählen N2 - Im Rahmen einer Bauwerksuntersuchung an einer in nachträglicher Verbundbauweise hergestellten Brücke wurden Anrisse an Spannstählen der Quervorspannung festgestellt, ohne daß Verpreßmängel oder korrosionsfördernde Substanzen vorlagen. Bei dem verwendeten Werkstoff handelt es sich um einen in der ehemaligen DDR hergestellten vergüteten Stahl der Festigkeitsklasse St 140/160. Ursache für die Anrisse ist die in Laborversuchen nachgewiesene Empfindlichkeit dieses Stahles gegenüber wasserstoffinduzierter Spannungsrißkorrosion, die unter ungünstigen Bedingungen dazu führen kann, daß Vorschädigungen vor dem Verpressen eintreten. Zusätzlich durchgeführte Magnetpulverprüfungen an ausgewählten Bereichen der Längsvorspannung ergaben keinerlei Hinweise auf Anrisse. Translated Abstract Stress corrosion cracking of prestressing steels During the investigation of a post-tensioned bridge structure incipient cracks of the prestressing steels of the transverse prestressed members were observed. Defects related to non-injected ducts or the presence of corrosion inducing substances could not be detected. The prestressing steel used is a quenched and tempered steel, strength class St 140/160, which was produced in the former GDR. The cause for the cracks is the susceptibility of this type of steel to hydrogen-induced stress corrosion cracking as could be shown in laboratory tests. Under unfavourable conditions cracks can be initiated before grouting. Additional magnetic particle tests at selected areas of the longitudinal prestressed members did not indicate any signs for incipient cracks. KW - Corrosion PY - 1999 SN - 0947-5117 SN - 1521-4176 VL - 50 IS - 9 SP - 535 EP - 540 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-831 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Mietz, Jürgen A1 - Fischer, Joachim T1 - Spannungsrisskorrosion an Spannstahl - Ringversuch zur Prüfung der Spannungsrisskorrosion an Spannstählen N2 - Für Spannstähle muss im Rahmen der Überwachung die Beständigkeit gegenüber Spannungsrisskorrosion nach DIN EN ISO 15630-3 nachgewiesen werden. Die Stähle werden hierbei entweder einer konzentrierten Ammoniumthiocyanatlösung oder einer verdünnten Lösung, die eher die Verhältnisse in der Baupraxis wiedergibt, ausgesetzt. In den vergangenen Jahren gab es an Spannstäben der Festigkeitsklasse St 950/1050 immer wieder Probleme mit dem Erreichen der erforderlichen Standzeiten in der konzentrierten Lösung. Der Ringversuch sollte nun klären, inwieweit Unsicherheiten hinsichtlich der Zuverlässigkeit und Aussagekraft der Ergebnisse von Spannungsrisskorrosionsprüfungen bestehen. Außerdem sollten die Prüfanweisungen, die Prüfeinrichtungen sowie die Vor-Ort-Inspektion der Prüfstände kritisch beurteilt werden, um eventuell vorhandene versuchstechnische Probleme zu identifizieren und ggf. zu beheben. PY - 2015 SP - T 3306, 1 EP - 29 PB - Fraunhofer IRB Verl. AN - OPUS4-32461 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mietz, Jürgen A1 - Burkert, Andreas T1 - Selection and Durability of Stainless Steels for Civil Engineering N2 - Due to the large number of stainless steels with different chemical composition and different microstructure the selection of the suitable material represents a huge challenge. In order to facilitate the appropriate grade selection, in the current European standard EN 1993-1-4 a procedure is defined based on the use of a look-up table considering the key variables that influence the selection of stainless steels. The table uses descriptions that competent designers should be able to readily understand or define without prior knowledge. The output from the look-up table is used to select alloys based on a Corrosion Resistance Class (CRC) from I to V. The advantage of this approach is that the designer simply specifies the relevant CRC and does not need to consider in detail which of the many (very similar) alloys to specify. KW - Corrosion resistance KW - Stainless steel KW - Civil engineering KW - Atmospheric corrosion PY - 2020 U6 - https://doi.org/10.4028/www.scientific.net/KEM.843 SN - 1662-9795 VL - 843 SP - 125 EP - 131 PB - Trans Tech Publications Ltd, CY - Switzerland AN - OPUS4-50831 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mietz, Jürgen A1 - Isecke, Bernd ED - Page, C. ED - Bamforth, P. ED - Figg, J. T1 - Risks of failure in prestressed concrete structures due to stress corrosion cracking T2 - 4th International Symposium on Corrosion of Reinforcement in Concrete Construction CY - Cambridge, England, UK DA - 1996-07-01 KW - Betonkonstruktion KW - Korrosion KW - Streßkorrosion KW - Stahlbeton PY - 1996 SN - 0-85404-731-X SN - 0260-6291 N1 - Serientitel: Special publication / Royal Society of Chemistry – Series title: Special publication / Royal Society of Chemistry IS - 183 SP - 200 EP - 209 PB - Royal Society of Chemistry Information Services CY - Cambridge AN - OPUS4-702 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mietz, Jürgen A1 - Burkert, Andreas A1 - Lehmann, Jens A1 - Eich, G. ED - Castro-Borges, P. ED - Moreno, E.I. ED - Sakai, K. ED - Gjorv, O.E. ED - Banthia, N. T1 - Risk of stress corrosion cracking of prestressing steels in contact with galvanized components T2 - CONSEC`10 - 6th International conference on concrete under severe conditions CY - Mérida, Yucatán, Mexico DA - 2010-06-07 KW - Prestressing steel KW - Galvanized elements KW - Galvanic corrosion KW - Hydrogen evolution KW - Hydrogen-induced stress corrosion cracking PY - 2010 SN - 978-0-415-59316-8 VL - 1 SP - 239 EP - 246 PB - Taylor & Francis CY - London, UK AN - OPUS4-22037 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mietz, Jürgen A1 - Burkert, Andreas T1 - Regelwerke für die Werkstoffauswahl und Dauerhaftigkeit von nichtrostenden Stählen für Stahlbauten – Entwicklung und aktueller Stand T1 - Technical regulations for the selection of materials and durability for steel structures - Development and current status N2 - Eine der wesentlichsten Veränderungen der im Oktober 2015 erschienenen Neufassung der DIN EN 1993-1-4 findet sich im Anhang A „Werkstoffauswahl und Dauerhaftigkeit“. Im Gegensatz zur Vorgängerversion ist dieser Anhang jetzt normativ. Mit Hilfe eines Punktesystems, das die wichtigsten Einwirkungsparameter der relevanten Expositionsbedingungen berücksichtigt, wird eine Korrosionsbeständigkeitsklasse ermittelt, mit deren Hilfe man eine geeignete Legierung auswählen kann. Dieses Verfahren bietet eine zuverlässige Methode für Planer auch ohne spezielle Kenntnisse auf dem Gebiet der Korrosion bzw. der nichtrostenden Stähle. Die Arbeit geht auch auf Unterschiede sowie Gemeinsamkeiten mit der bisher in Deutschland gültigen allgemeinen bauaufsichtlichen Zulassung Z-30.3.6 ein. KW - Korrosionsschutz KW - Werkstoffauswahl KW - Exposition PY - 2017 U6 - https://doi.org/10.1002/stab.201710466 SN - 0038-9145 SN - 1437-1049 VL - 86 IS - 3 SP - 279 EP - 286 PB - Ernst & Sohn CY - Berlin AN - OPUS4-39570 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mietz, Jürgen ED - Schwarz, W. T1 - Realkalisierung, Chloridentzug und Kathodischer Korrosionsschutz - Elektrochemische Verfahren zur Instandsetzung von Stahlbetonbauwerken N2 - Referat: In Stahlbeton- und Spannbetonbauwerken wird der Korrosionsschutz des Bewehrungsstahles durch die Alkalität des Beton-Porenwassers und die sich daraus ergebende Passivierung der Stahloberfläche gewährleistet. Als Folge von Mechanismen, die die Passivschicht zerstören, wie z.B. die Karbonatisierung des Betons oder das Eindringen von Chloriden, kann es zu einer Depassivierung des Stahles kommen. In diesen Fällen sind Maßnahmen notwendig, die Korrosionsreaktionen vermeiden bzw. während der Nutzungsdauer des Bauwerkes in tolerierbaren Grenzen halten. Um die Nachteile der traditionellen Sanierungsverfahren zu umgehen, sind in letzter Zeit verschiedene elektrochemische Methoden zur Instandsetzung entwickelt und erfolgreich angewendet worden. Prinzip, Anwendungsmöglichkeiten sowie Forschungsergebnisse der folgenden Verfahren, elektrochemische Realkalisierung bei Karbonatisierung, elektrochemische Entsalzung bei Chloridkontamination und Kathodischer Korrosionsschutz mit Fremdstrom werden beschrieben und diskutiert. T2 - Seminar über Korrosion von Bewehrungsstahl in Beton CY - Wien, Österreich DA - 1999-01-01 KW - Realkalisierung KW - Chloridentzug KW - Kathodischer Korrosionsschutz PY - 1999 UR - http://www.baufachinformation.de/aufsatz.jsp?ul=99079009354 SN - 3-931681-29-7 SN - 0947-6830 N1 - Sprachen: Deutsch/Englisch - Languages: German/English N1 - Serientitel: WTA-Schriftenreihe – Series title: WTA-Schriftenreihe IS - 19 SP - 165 EP - 181 PB - Aedificatio Verl. CY - Freiburg AN - OPUS4-769 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mietz, Jürgen T1 - Problemlösungen für Bauteile und Verbindungsmittel im Ingenieurbau T2 - Jahrestagung der Gesellschaft für Korrosionsschutz ; GfKORR-Jahrestagung CY - Berlin, Deutschland DA - 2000-11-07 KW - Korrosion PY - 2000 SN - 3-935406-03-7 SP - 1(?) EP - 20(?) PB - Ges. für Korrosionsschutz CY - Frankfurt am Main AN - OPUS4-838 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mietz, Jürgen T1 - Nichtrostende Stähle für Bauteile und Verbindungsmittel KW - Nichtrostender Stahl KW - Stahlsorten KW - Korrosion PY - 1999 SN - 0007-5884 VL - 48 IS - 11 SP - 71 EP - 73 PB - Bauverlag BV CY - Gütersloh AN - OPUS4-736 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Burkert, Andreas A1 - Fischer, Joachim A1 - Mietz, Jürgen A1 - Lehmann, Jens A1 - Ebell, Gino T1 - Neues DGZfP - Merkblatt der elektrochemischen Potentialfeldmessung zur Detektion von Bewehrungsstahlkorrosion T2 - Tagung Korrosionsschutz der Stähle im Kontakt mit Beton - Neue Entwicklungen und Forschungsergebnisse CY - Stuttgart-Vaihingen, Deutschland DA - 2010-10-07 KW - Verfahrensbeschreibung KW - Messraster KW - Einflussgrößen KW - Fehlerquellen KW - Prüfprotokoll KW - Nachweisgrenzen PY - 2010 SN - 978-3-935406-43-7 SP - 149 EP - 156 CY - Frankfurt/M. AN - OPUS4-22197 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mietz, Jürgen T1 - Neue bauaufsichtliche Zulassung für Bauteile und Verbindungsmittel aus nichtrostenden Stählen KW - Nichtrostender Stahl KW - Korrosion PY - 1999 SN - 0038-9145 SN - 1437-1049 SN - 0932-6375 N1 - Sprachen: Deutsch/Englisch - Languages: German/English VL - 68 IS - 12 SP - 1037 EP - 1043 PB - Ernst CY - Berlin AN - OPUS4-812 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mietz, Jürgen T1 - Neue bauaufsichtliche Zulassung - Bauteile und Verbindungsmittel aus nichtrostenden Stählen für Schwimmhallen KW - Bauteile KW - Verbindungsmittel KW - Nichtrostender Stahl PY - 1999 SN - 0344-6492 VL - 5 SP - 29 EP - 32 PB - Krammer CY - Düsseldorf AN - OPUS4-726 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Burkert, Andreas A1 - Ebell, Gino A1 - Eichler, T. A1 - Hariri, K. A1 - Harnisch, J. A1 - Keßler, S. A1 - Mayer, T.F. A1 - Meier, J. A1 - Mietz, Jürgen A1 - Reichling, K. A1 - Sodeikat, C. T1 - Merkblatt für Elektrochemische Potentialmessungen zur Detektion von Bewehrungsstahlkorrosion KW - Stahlbeton KW - Korrosion KW - Bewehrung KW - Potentialmessung KW - Zerstörungsfreie Prüfung PY - 2014 SN - 978-3-940283-10-8 VL - B 03 SP - 1 EP - 19 CY - Berlin AN - OPUS4-31077 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Angst, U. A1 - Brem, M. A1 - Dauberschmidt, C. A1 - Ebell, Gino A1 - Eichler, T. A1 - Hariri, K. A1 - Harnisch, J. A1 - Keßler, S. A1 - Kosalla, M. A1 - Mayer, T. F. A1 - Mietz, Jürgen A1 - Pruckner, F. A1 - Sodeikat, C. T1 - Merkblatt B 12 Korrosionsmonitoring bei Stahl- und Spannbetonbauwerken N2 - Das Merkblatt B12 enthält alle gängigen und etablierten Monitoringverfahren für das Korrosionsmonitoring an Stahlbetonbauwerken. KW - Korrosion KW - Monitoring PY - 2018 SN - 978-3-940283-93-1 SP - 1 EP - 58 PB - DGZfP CY - Berlin AN - OPUS4-45235 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Burkert, Andreas A1 - Ebell, Gino A1 - Eichler, T. A1 - Hariri, K. A1 - Harnisch, J. A1 - Keßler, S. A1 - Mayer, T.F. A1 - Meier, J. A1 - Mietz, Jürgen A1 - Reichling, K. A1 - Sodeikat, C. T1 - Merkblatt B 03 - Merkblatt für Elektrochemische Potentialmessungen zur Detektion von Bewehrungsstahlkorrosion N2 - Dieses Merkblatt beschreibt die Anwendung elektrochemischer Potentialmessungen (häufig auch als Potentialfeldmessung bezeichnet) zur Detektion von Bewehrungsstahlkorrosion an Stahlbetonbauwerken. Mit Hilfe dieses Verfahrens können Bereiche korrodierender Bewehrung zerstörungsfrei lokalisiert werden. In der Regel kommt diese Messmethode bei der Detektion chloridinduzierter Korrosion zum Einsatz. In Abgrenzung hierzu sollte die Abschätzung der Gefahr einer karbonatisierungsinduzierten Korrosion durch Bestimmung der Karbonatisierungstiefe und der Betondeckung erfolgen. KW - Korrosion KW - Betonstahl KW - Chloridinduzierte Korrosion KW - Potentialfeldmessung PY - 2014 SN - 978-3-940283-10-8 SP - 1 EP - 19 CY - Berlin ET - Überarbeitete Ausgabe April 2014 AN - OPUS4-31518 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ebell, Gino A1 - Achenbach, R. A1 - Angst, U. A1 - Brem, M. A1 - Dauberschmidt, C. A1 - Eichler, T. A1 - Hariri, K. A1 - Harnisch, J. A1 - Keßler, S. A1 - Mayer, T.F. A1 - Mietz, Jürgen A1 - Pruckner, F. T1 - Merkblatt B 03 - Elektrochmische Potentialmessung zur Detektion von Bewehrungsstahlkorrosion N2 - Die Potentialmessung kann zum Auffinden korrosionsaktiver Bereiche neben Stahlbetonbauwerken auch bei Spannbetonbauwerken angewandt werden, die mit Spannstählen im direkten Verbund hergestellt werden. Bei Vorspannsystemen mit metallischen Hüllrohren im nachträglichen Verbund ist eine Aussage über den Korrosionszustand des Hüllrohrs, nicht aber des Spannstahls möglich. Messungen an Spannbetonbauteilen erfordern grundsätzlich die besonderen Kenntnisse eines Spezialisten. KW - Korrosion KW - Potentialfeldmessung KW - Corrosion KW - Concrete PY - 2021 SN - 978-3-947971-16-9 SP - 1 EP - 22 PB - DGZfP CY - Berlin AN - OPUS4-53091 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mietz, Jürgen A1 - Isecke, Bernd A1 - Fischer, Joachim T1 - Long-term experiences with cathodic corrosion protection of steel reinforced concrete structures T2 - 15th International Corrosion Congress CY - Granada, Spain DA - 2002-09-22 PY - 2002 PB - CSIC, Spanish Council for Scientific Research CY - Madrid AN - OPUS4-1728 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burkert, Andreas A1 - Müller, Thoralf A1 - Lehmann, Jens A1 - Mietz, Jürgen T1 - Long-term corrosion behaviour of stainless steels in marine atmosphere N2 - Nine different stainless steel alloys were exposed for 5 years under marine environment and their corrosion behaviour was compared and assessed. The investigation of four different surface finishes for all alloys tested further enabled to consider industry-specific features of the surface finish for the material comparison. The results of the exposure tests yield conclusions regarding the influence of alloy composition, surface finish and exposure duration under marine environment. The three duplex stainless steels revealed excellent corrosion resistance even in case of crevices during the 5 years of exposure under the given exposure conditions. Also the molybdenum-alloyed ferritic steel 1.4521 showed good corrosion resistance comparable to the classical austenitic materials 1.4301 and 1.4404. KW - Corrosion KW - Free weathering KW - Marine atmosphere KW - Stainless steels PY - 2018 U6 - https://doi.org/10.1002/maco.201709636 SN - 0947-5117 SN - 1521-4176 VL - 69 IS - 1 SP - 20 EP - 28 PB - Wiley-VCH Verlag GmbH & Co KGaA CY - Weinheim AN - OPUS4-43625 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mietz, Jürgen A1 - Burkert, Andreas A1 - Burkert, Annette A1 - Eich, Gerd T1 - Long-term Behaviour of Corrosion Protection Materials for Prestressed Systems T2 - 2nd International fib Congress CY - Naples, Italy DA - 2006-06-05 KW - Prestressed systems KW - Corrosion protection KW - Wax KW - Grease KW - Electrochemical tests PY - 2006 SN - 0-912053-94-1 SP - 12 pages PB - Society for Experimental Mechanics CY - St. Lous AN - OPUS4-12513 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gluth, Gregor A1 - Hlavacek, Petr A1 - Reinemann, Steffi A1 - Ebell, Gino A1 - Mietz, Jürgen ED - Alexander, M.G. ED - Beushausen, H. ED - Dehn, F. ED - Moyo, P. T1 - Leaching, carbonation and chloride ingress in reinforced alkali-activated fly ash mortars N2 - Alkali-activated fly ash mortars were studied with regard to durability-relevant transport coefficients and the electrochemical behaviour of embedded carbon steel bars on exposure of the mortars to leaching, carbonation and chloride penetration environments. The transport coefficients differed considerably between different formulations, being lowest for a mortar with BFS addition, but still acceptable for one of the purely fly ash-based mortars. Leaching over a period of ~300 days in de-ionized water did not lead to observable corrosion of the embedded steel, as shown by the electrochemical data and visual inspection of the steel. Exposure to 100 % CO2 atmosphere caused steel depassivation within approx. two weeks; in addition, indications of a deterioration of the mortar were observed. The results are discussed in the context of the different reaction products expected in high- and low-Ca alkali-activated binders, and the alterations caused by leaching and carbonation. T2 - International Conference on Concrete Repair, Rehabilitation and Retrofitting (ICCRRR 2018) CY - Cape Town, South Africa DA - 19.11.2018 KW - Alkali-activated materials KW - Steel corrosion KW - Leaching KW - Carbonation PY - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-464381 VL - 199 SP - Article Number 02025 PB - EDP Sciences AN - OPUS4-46438 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Isecke, Bernd A1 - Mietz, Jürgen A1 - Fischer, Joachim T1 - Langzeiterfahrungen mit einem kathodischen Korrosionsschutzsystem für Stahl in Beton N2 - Im Jahr 1986 wurde in Deutschland die erste kathodische Korrosionsschutzanlage für ein Stahlbetonbauwerk in Betrieb genommen. Die Installation, die Inbetriebnahme sowie die laufende Überwachung wurden wissenschaftlich begleitet. Im Zuge notwendiger verkehrstechnisch bedingter Umbaumaßnahmen wurde die Anlage nach etwa 15 Jahren außer Betrieb genommen. Die in dieser Zeit durchgeführten Untersuchungen dienten dem Ziel, die an Laborversuchen gewonnenen Ergebnisse an einem praktischen Bauwerk zu überprüfen sowie Informationen über das Langzeitverhalten hinsichtlich Dauerhaftigkeit, Potentialverteilung, Temperaturabhängigkeit, Chloridmigration usw. zu bekommen. Mit zunehmender Betriebsdauer konnten die Schutzkriterien nur durch Erhöhung der Gleichrichterspannung eingehalten werden (die Anlage wurde im Konstantspannungsmodus betrieben). Umfangreiche Untersuchungen an Anodenmaterialproben (leitfähiger Polymerdraht mit einem Kupferkern) nach 15-jährigem Einsatz zeigten, dass irreversible Veränderungen die Leitfähigkeit des Polymers erheblich vermindert haben, wodurch letztendlich die Funktionsfähigkeit der Anode nicht mehr gegeben war. Diese Art von Anoden werden aber heutzutage nicht mehr für den kathodischen Korrosionsschutz von Stahlbetonbauwerken eingesetzt. Translated Abstract Long-term experiences with a cathodic protection system for steel in concrete In 1986 in Germany the first cathodic protection system for reinforced concrete structures was put into service. Installation, commissioning and the regular monitoring were scientifically supported. Due to necessary traffic related reconstruction measures the system was switch off after 15 years of service. Investigations carried out during that period should verify laboratory test results at a real structure and furthermore yield information on the long-term behaviour concerning durability, temperature dependence, potential distribution, chloride migration etc. With increasing time of service the protection criteria could only be met by increasing the transformer rectifier voltage (the system worked in the constant voltage mode). Extensive investigations of the anode material (conductive polymer wire with a copper core) after 15 years of service showed that irreversible changes substantially decreased the polymer's conductivity limiting the functionality. Today, these kind of anodes are not used any more for the application in cathodic protection systems of reinforced concrete structures. PY - 2001 U6 - https://doi.org/10.1002/1521-4176(200112)52:12<920::AID-MACO920>3.0.CO;2-J SN - 0947-5117 SN - 1521-4176 VL - 52 IS - 12 SP - 920 EP - 930 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-1222 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lehmann, Jens A1 - Fischer, Joachim A1 - Burkert, Andreas A1 - Mietz, Jürgen T1 - Langzeiterfahrungen an einer Gabionenkonstruktion T1 - Long term experiences with a gabion construction N2 - Anhand der hier vorgestellten Untersuchungsergebnisse kann eine umfassende Einschätzung des Korrosionszustands einer Gabionenkonstruktion aus Drähten mit Zink-Aluminium-Überzug nach 20 Jahren Einsatzzeit in Abhängigkeit von unterschiedlichen Expositionsbedingungen vorgenommen werden. Die festgestellten Massenverluste der Zink-Aluminium-Überzüge waren an den Untersuchungspositionen, insbesondere hinsichtlich der verschiedenen Expositionsbedingungen der Probenentnahmestellen, unterschiedlich ausgeprägt. Gabionendrähte, die im direkten Bodenkontakt standen, wiesen dabei die geringsten Restauflagen auf. Atmosphärisch beanspruchte sowie durch Vlies vor direktem Bodenkontakt geschützte Gabionendrähte zeigten dagegen etwas größere Restauflagen. Über den Drahtumfang wurden bei allen untersuchten Drahtproben stark variierende Schichtdicken festgestellt, was offensichtlich herstellungsbedingte Ursachen hat. Die Untersuchungen an der Gabionenkonstruktion haben gezeigt, dass die Annahme einer mittleren linearen Abtragsrate des metallischen Überzugs von 1 mm/a unter den hier untersuchten Bedingungen ein realistischer Wert ist. An Positionen mit direktem Bodenkontakt kann dieser Wert aber deutlich größer ausfallen, sobald sich die Aggressivität des Bodens erhöht. Eine Rotrostbildung war an den Drahtproben nicht feststellbar. KW - Korrosionsschutz KW - Zink-Aluminium-Überzug KW - Gabionen KW - Boden PY - 2017 U6 - https://doi.org/10.1002/bate.201600030 SN - 0932-8351 VL - 94 IS - 1 SP - 37 EP - 48 PB - Ernst & Sohn CY - Weinheim AN - OPUS4-38950 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burkert, Andreas A1 - Lehmann, Jens A1 - Burkert, Annette A1 - Mietz, Jürgen T1 - Korrosionsschäden an nichtrostenden Stählen unter atmosphärischen Einsatzbedingungen N2 - Neben konstruktiven Anforderungen werden an nichtrostende Stähle im Bauwesen häufig hohe optische Ansprüche gestellt. Unerwartete Beeinträchtigungen des optischen Erscheinungsbildes nichtrostender Stähle unter wenig korrosiven Bedingungen sind in der Zwischenzeit ein weit verbreitetes Problemfeld und Gegenstand zahlreicher Streitfälle. Vielfach wird die Vermutung geäußert, dass eine veränderte Legierungszusammensetzung, veränderte Umweltbedingungen oder auch die unsachgemäße Verarbeitung die Ursache für diese Erscheinungen sind. Durch eine systematische Untersuchung zahlreicher Schadensfälle an Stabmaterial in den vergangenen zwei Jahren im Rahmen eines Forschungsvorhabens konnte gezeigt werden, dass die Ursachen in bekannten Werkstofffehlern zu finden sind. Hierzu gehören chemische Inhomogenitäten, wie zum Beispiel Ausscheidungen und örtliche Aufkohlung, sowie geometrische Fehler, wie zum Beispiel Hinterschnitte, Walzfehler und Schalenbildung. Die Fehler konnten damit eindeutig als Herstellungsfehler der jeweiligen Halbzeuge identifiziert werden. KW - Korrosion KW - Nichtrostende Stähle KW - Atmosphäre KW - Interkristalline Korrosion KW - Schäden PY - 2010 U6 - https://doi.org/10.1002/stab.201001288 SN - 0038-9145 SN - 1437-1049 SN - 0932-6375 VL - 79 IS - 5 SP - 389 EP - 395 PB - Ernst CY - Berlin AN - OPUS4-21242 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burkert, Andreas A1 - Mietz, Jürgen T1 - Korrosionsschäden an Lagertanks für Salzlake N2 - An einem Tankbehälter aus dem Werkstoff X2CrNiMo17-12-2, der zur Zwischenlagerung von Salzlake für die Käseherstellung dient, wurden trotz langjähriger positiver Erfahrungen an vergleichbaren Anlagen bereits kurze Zeit nach der Inbetriebnahme Lochkorrosionserscheinungen festgestellt. Durch entsprechende elektrochemische Laboruntersuchungen konnte gezeigt werden, dass die vorgefundene Lochkorrosion durch den Einsatz eines Oxidationsmittels zu Desinfektionszwecken verursacht wurde. Translated Abstract Corrosion damage at storage tanks for salt brine A tank made of stainless steel type X2CrNiMo17-12-2 for intermediate storage of salt brine for cheese production revealed significant pitting corrosion effects shortly after commissioning although comparable units have shown positive long-term behaviour. By means of electrochemical laboratory tests it could be demonstrated that the observed pitting corrosion was caused by the use of an oxidizing agent for desinfection purposes. PY - 2003 SN - 0947-5117 SN - 1521-4176 VL - 54 IS - 2 SP - 113 EP - 118 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-2378 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Mietz, Jürgen A1 - Burkert, Annette A1 - Burkert, Andreas A1 - Jonas, Bernhard A1 - Eich, Gerd A1 - Baszynski, Joachim T1 - Korrosionsschutzwirkung von Korrosionsschutzmassen für Spannglieder ohne Verbund KW - Spannstahl KW - Korrosion KW - Korrosionsschutzmittel KW - Wasseraufnahme KW - Schutzwirkung KW - Langzeitverhalten KW - Bodenkontakt PY - 2005 SN - 3-8167-6740-0 IS - T 3071 SP - 1 EP - 45 PB - IRB-Verl. CY - Stuttgart AN - OPUS4-11344 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ebell, Gino A1 - Burkert, Andreas A1 - Lehmann, Jens A1 - Mietz, Jürgen T1 - Korrosions- und Verbundverhalten verzinkter Betonstähle in Betonen mit chromatreduzierten Zementen N2 - Durch die Absenkung des Chromatgehalts der Zemente verändern sich die elektrochemischen Reaktionen von verzinkten Betonstählen in der Frischbetonphase. Mit Hilfe von elektrochemischen Messungen sowie Stabauszugsversuchen wurde an chromathaltigen und chromatreduzierten Zementen die Auswirkung des Chromats auf die Deckschichtbildung am Zink und auf das Verbundverhalten untersucht. Mit den Ergebnissen konnte eine Beeinträchtigung der Verbundzone als Folge der Chromatreduzierung für die Zementarten CEM I und CEM II nachgewiesen werden. Die Störung der Verbundzone ist in Bezug auf die sich ausbildende Porenstruktur als dauerhaft anzusehen. Die Auswirkungen auf das Verbundverhalten werden mit zunehmendem Betonalter weitgehend kompensiert. Die Ergebnisse der bezogenen Verbundspannung bei Verschiebewegen von 0,1 mm und 0,5 mm liegen trotz der Gefügestörung noch im Bereich der Erwartungswerte für den unverzinkten Betonstahl. Unter baupraktischen Gesichtspunkten muss die auftretende Gefügestörung hinsichtlich der Verbundspannung daher keine Berücksichtigung finden. KW - Verzinkt KW - Feuerverzinkt KW - Betonstahl KW - Verbund PY - 2011 U6 - https://doi.org/10.1002/best.201100038 SN - 0005-9900 SN - 1437-1006 VL - 106 IS - 9 SP - 629 EP - 639 PB - Ernst CY - Berlin AN - OPUS4-24307 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lehmann, Jens A1 - Burkert, Andreas A1 - Mietz, Jürgen T1 - Investigations proofing the passive layer stability of stainless steels N2 - The presented investigations have proved the principal suitability of the KorroPad method to assess the passive layer stability of stainless steels. The electrochemical mode of action could be described in detail and limitations of the applicability have been demonstrated. The influence of different surface finishes has been investigated and verified by known methods for describing corrosion resistances. As a result, the increased corrosion susceptibility of two ground surfaces has been detected, but also the corrosion resistance of further surface finishes could be confirmed. KW - Stainless steel KW - KorroPad KW - Passive layer PY - 2016 U6 - https://doi.org/10.1002/maco.201408202 VL - 1 IS - 67 SP - 84 EP - 91 PB - WILEY-VCH Verlag GmbH & Co. KGaA CY - Weinheim AN - OPUS4-35545 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mietz, Jürgen A1 - Burkert, Annette A1 - Burkert, Andreas A1 - Eich, Gerd T1 - Investigations on the protection effect of filling materials for post-tensioning systems under construction conditions N2 - About the long-term protection behaviour of corrosion protection materials (filling materials) for prestressed systems under critical environmental conditions is only little known. The corrosion protection effect is usually based on theoretical considerations and is proven by short-term tests. The selection of the different products is mainly made according to economical or workability criteria. In a research project the barrier effect of different commercial corrosion protection materials (waxes as well as oil-based greases) against water, their tendency for undercutting as well as their additional corrosion protection effect were investigated. The exposure tests were carried out with non-stressed as well as stressed prestressing steel specimens which were subjected to critical conditions (condensed water, artificial soil solution, direct soil contact). Parallel to these long-term exposure tests the applicability of different electrochemical techniques and their significance with respect to testing the corrosion protection ability and water absorption was evaluated. Within the project a suitable method for simple testing the performance of corrosion protection materials under real conditions was developed. By means of a small compact cell submicroscopical reactions of the used sensors could be measured. The high sensitivity of this measuring technique enables the detection of degradation processes at thin protection layers. KW - Prestressed systems KW - Corrosion KW - Corrosion protection KW - Electrochemical tests KW - Grease KW - Wax PY - 2006 U6 - https://doi.org/10.1002/maco.200603986 SN - 0947-5117 SN - 1521-4176 VL - 57 IS - 11 SP - 843 EP - 851 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-13931 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mietz, Jürgen T1 - Investigations on hydrogen-induced embrittlement of quenched and tempered prestressing steels N2 - In Germany in recent years failures of more than 30-year-old prestressed concrete structures have been observed. In all these cases a quenched and tempered steel type, strength class St. 1420/1570 was used. In order to assess the corrosion risk, i.e. crack initiation and propagation, under depassivating conditions lifetime tests in environments relevant for building practice were carried out using different prestressing steels of this quenched and tempered type of material. From the results it can be concluded that the specific susceptibility of certain prestressing steels is the determining factor with respect to the occurrence of cracks rather than environmental factors. Translated Abstract Untersuchungen zum wasserstoffinduzierten Sprödbruch vergüteter Spannstähle In den letzten Jahren ist es verschiedentlich zu Schadensfällen von Spannbetonbauteilen gekommen, bei denen vergüteter Spannstahl der Festigkeitsklasse St 1420/1570 eingesetzt war. Durch systematische Untersuchungen an verschiedenen Typen dieser Stahlsorte sollte geklärt werden, ob unter depassivierenden Bedingungen Rißeinleitung und -ausbreitung unter praxisnahen Verhältnissen zu erwarten ist. Die durchgeführten Untersuchungen lassen folgern, daß die spezifische Anfälligkeit des Spannstahls für das Auftreten von Rissen einen wesentlich höheren Einfluß besitzt als die elektrolytseitigen Parameter, da sich die verschiedenen Stähle auch bei vergleichbaren Korrosionsangriffen unterschiedlich verhalten. KW - Prestressing steels KW - Corrosion PY - 2000 U6 - https://doi.org/10.1002/(SICI)1521-4176(200002)51:2<80::AID-MACO80>3.0.CO;2-A SN - 0947-5117 SN - 1521-4176 N1 - Sprachen: Deutsch/Englisch - Languages: German/English VL - 51 IS - 2 SP - 80 EP - 90 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-807 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beck, Matthias A1 - Goebbels, Jürgen A1 - Isecke, Bernd A1 - Burkert, Andreas A1 - Mietz, Jürgen T1 - Investigations of corrosion on small cathodes in reinforced concrete - observations and suggestions N2 - Corrosion of steel reinforcement in concrete exposed to chloride containing environments is a serious problem in civil engineering practice. The standards and guidelines contain only minimum requirements regarding concrete quality and concrete cover. In very critical cases, for example the ingress of chlorides, the application of different coatings is currently the only possibility to protect the reinforced concrete structures. In this case the modelling of reinforcement corrosion would be more practical. One sub-project of a DFG-research project (FOR 537) is currently performed at the Federal Institute for Materials Research and Testing (BAM). Aim of the sub-project is the description of corrosion propagation and the characterization of the corrosion on specimens with small cathodes by electrochemical parameters. The electrochemical parameters are determined by suitable electrochemical measurements, considering concrete parameters as well as different environmental conditions. T2 - EUROCORR 2009 CY - Nice, France DA - 2009-09-06 KW - Self-corrosion KW - Steel reinforcement KW - Concrete parameters KW - X-ray tomography PY - 2009 IS - Paper 7976 SP - 1 EP - 13 AN - OPUS4-20063 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Babutzka, Martin A1 - Mietz, Jürgen A1 - Burkert, Andreas T1 - Investigation of the salinization of steel surfaces in marine environment N2 - The salinization and contamination of metal surfaces by chloride-containing aerosols is of great importance with regard to corrosion phenomena of damaged coated metal surfaces and stainless steels in the maritime sector and in offshore applications. Detailed questions have to be answered to clarify whether and to what extent salinization of the surface has an influence on the adhesion and durability of coatings in repairing applications and on pitting occurrence on stainless steels under atmospheric conditions. The questions arise which degree of salinization is reached after which period of time and how a defined and reproducible salinization can be simulated in the laboratory for further systematic investigations. The article is dedicated to these questions. Results of a field trial on the Island of Heligoland are presented and a simple procedure for a defined loading of metal surfaces with chlorides at a laboratory scale using a design of experiments (DoE) approach is introduced. KW - Maritime Atmosphäre KW - Versalzung KW - Maritime atmosphere KW - Salinization PY - 2018 U6 - https://doi.org/10.1002/maco.201810636 SN - 0947-5117 SN - 1521-4176 VL - 70 IS - 6 SP - 1016 EP - 1025 PB - Wiley-VCH Verlag CY - Weinheim AN - OPUS4-47727 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Babutzka, Martin A1 - Müller, Thoralf A1 - Mietz, Jürgen A1 - Burkert, Andreas T1 - Investigation of the influence of iron‐containing abrasives on the corrosion behaviour of the aluminium alloy AlSi1.2Mg0.4 N2 - The corrosion resistance of aluminium surfaces is closely linked to the surfacecstate after a grinding process. For years, iron‐containing abrasive materials were suspected to lead to increased corrosion susceptibility after processing of aluminium surfaces. To prove a possible correlation between the iron content of an abrasive and the corrosion behaviour of aluminium components, scientific investigations and experimentally practical corrosion tests are necessary. For the current investigation, specimens of a technical Al‐Si alloy from the same batch were used. The test specimens were mechanically ground with various resin‐bonded model abrasives containing different iron contents. The performed corrosion tests did not reveal a negative influence of the different iron‐containing abrasives on the corrosion behaviour of the Al–Si alloy. However, the most sensitive measuring method (electrochemical noise) showed differences in the surface activity depending on the type of abrasive. KW - Aluminium KW - Corrosion KW - Corrosion testing KW - Grinding PY - 2020 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-506762 SN - 0947-5117 SN - 1521-4176 VL - 71 IS - 10 SP - 1667 EP - 1679 PB - Wiley‐VCH Verlag GmbH & Co. KGaA CY - Weinheim AN - OPUS4-50676 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino A1 - Mietz, Jürgen A1 - Burkert, Andreas T1 - Investigation of chloride-induced pitting corrosion of steel in concrete by a combination of electrochemical methods with X-ray tomography N2 - Steel in concrete is protected by the alkaline pore water environment and the resulting formation of a protective passive layer against corrosion. Adverse environmental conditions due to carbonation or chloride ingress can destroy the passive layer on the steel surface. Corrosion processes starting in those areas lead to uniform corrosion or local corrosion like pitting corrosion. In comparison to uniform corrosion pitting corrosion is a form of increased local corrosion and thus leads to a progressive reduction in cross-section of the reinforcing steel. The corrosion products are first absorbed by the pores of the concrete matrix, without causing visible external changes at the concrete surface. T2 - EUROCORR 2014 - European corrosion congress CY - Pisa, Italy DA - 08.09.2014 KW - Corrosion KW - Rebar KW - Chloride KW - Pitting corrosion PY - 2014 SN - 978-3-89746-159-8 SP - O-7207, 274-275 AN - OPUS4-31431 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mietz, Jürgen A1 - Raupach, M. A1 - Goltermann, P. T1 - Integrated Monitoring System for Reinforced Concrete Structures T2 - 1st FIB congress CY - Osaka, Japan DA - 2002-10-13 KW - Reinforcement corrosion KW - Sensors KW - Inspection KW - Maintenance KW - Bridge management PY - 2002 IS - 15 SP - 29 EP - 38 CY - Osaka AN - OPUS4-1727 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Burkert, Andreas A1 - Heyn, Andreas A1 - Ebell, Gino A1 - Lehmann, Jens A1 - Müller, Thoralf A1 - Mietz, Jürgen A1 - Fischer, Joachim T1 - Innovative Methoden in der Korrosionsforschung an der BAM N2 - Im Zusammenhang mit Planungs- und Entwicklungsaufgaben, den Forderungen in Normen und Regelwerken, in betrieblichen Arbeitsanweisungen, den Vorgaben für Zulieferteile oder bei der Auseinandersetzung mit Schadensfällen stellen sich häufig Fragen zum Korrosionsschutz sowie zu entsprechenden Prüf- und Untersuchungsverfahren. Die daraus gewonnenen Ergebnisse sollen z. B. eine Eignung von Werkstoffen oder Schutzsystemen unter spezifischen Einsatzbedingungen, die Dauerhaftigkeit des Schutzes, den Nachweis einer gleichbleibenden Qualität, die Vergleichbarkeit bekannter mit neuen Korrosionsschutzkonzepten oder den Wirkungsnachweis für gezielte Systemeingriffe belegen. Schnell wird deutlich, dass sich aus dem Blickwinkel verschiedener Branchen ganz unterschiedliche Anforderungsprofile ergeben, die ihren Niederschlag dann in unterschiedlichen Strategien der Prüf- und Untersuchungsverfahren finden. PY - 2014 SN - 978-3-00-044008-3 SP - 2-1 EP - 2-26 AN - OPUS4-32753 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino A1 - Burkert, Andreas A1 - Mietz, Jürgen T1 - Hydrogen evolution on galvanized rebar in fresh concrete with different chromate-reduced cements N2 - The reduction of the chromate contents in cements affects the electrochemical reactions of galvanized reinforcing steels in fresh concrete. It is important to investigate the critical conditions in the first hours following the pouring of the concrete. T2 - EUROCORR 2015 - European corrosion congress CY - Graz, Austria DA - 06.09.2015 KW - Hydrogen evolution KW - Concrete KW - Galvanized rebar KW - Reinforcement KW - Chromate PY - 2015 SP - paper 9_703 AN - OPUS4-34619 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Burkert, Andreas A1 - Lehmann, Jens A1 - Burkert, Annette A1 - Eich, Gerd A1 - Mietz, Jürgen T1 - Galvanized constructional elements in contact with prestressing steel tendons T2 - 22nd International Galvanizing Conference CY - Madrid, Spain DA - 2009-06-08 KW - Prestressed concrete KW - Prestressing steel KW - Hydrogen-induced stress corrosion cracking KW - Galvanized construction elements PY - 2009 SP - 1 EP - 11 AN - OPUS4-20700 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mietz, Jürgen A1 - Burkert, Andreas A1 - Lehmann, Jens A1 - Burkert, Annette A1 - Eich, Gerd T1 - Galvanised constructional elements in contact with prestressing steel tendons N2 - In order to clarify under which practical conditions real risks for hydrogen-induced stress corrosion cracking of prestressing steels exist laboratory investigations in aqueous solutions and concrete as well as tests with stressed prestressing steels were carried out. While different distances between steel and zinc (cathode and anode) showed only a negligible influence on the polarisation of the steel a significant dependence on the area ratio steel/zinc was observed. A critical area ratio of 10:1 can be defined above which polarisation of the steel to hydrogen evolution potentials is unlikely. The results obtained in the laboratory concerning the critical area ratio were confirmed by on-site investigations in a precasting plant. Exposure tests with hydrogen loading did not lead to fractures during the testing time for approved prestressing steels. The characteristic mechanical values determined immediately after the hydrogen loading tests did not show significant changes. Thus, an indirect contact between prestressing steels and galvanised elements can be estimated as uncritical. But a direct contact has to be excluded by compliance with DIN 1045-1, i.e minimal distance of 2 cm between prestressing steel and galvanised elements. PY - 2008 U6 - https://doi.org/10.1002/maco.200804114 SN - 0947-5117 SN - 1521-4176 VL - 59 IS - 2 SP - 131 EP - 138 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-16724 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Beck, Matthias A1 - Rübner, Katrin A1 - Mietz, Jürgen ED - Ravinda K. Dhir, ED - Tom A. Harrison, ED - Li Zheng, ED - Sivakumar Kandasami, T1 - Experimental investigation of propagation of reinforcement corrosion T2 - Concrete Durability: Achievement and Enhancement, International Conference CY - Dundee, Scotland, UK DA - 2008-07-08 KW - Reinforced concrete KW - Electrochemical parameters KW - Self-corrosion KW - Damage symptoms KW - Fly ash KW - Mercury intrusion measurements KW - Pore structure KW - Pozzolan PY - 2008 SN - 978-1-84806-039-5 IS - EP88 SP - 83 EP - 94 PB - IHS BRE Press AN - OPUS4-18312 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mietz, Jürgen A1 - Fischer, Joachim T1 - Evaluation of NDT methods for detection of prestressing steel damage at post-tensioned concrete structures KW - Prestressing steel KW - Non-destructive testing KW - Post-tensioned concrete KW - Hydrogen-induced stress corrosion cracking PY - 2007 U6 - https://doi.org/10.1002/maco.200704074 SN - 0947-5117 SN - 1521-4176 VL - 58 IS - 10 SP - 789 EP - 794 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-16063 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Poltavtseva, Marina A1 - Ebell, Gino A1 - Mietz, Jürgen T1 - Entwicklung und Erprobung einer neuen Prüfmesszelle für elektrochemische Untersuchungen leitfähiger Beschichtungen auf Karbonbasis in Elektrolytlösungen T2 - 15. Sommerkurs Werkstoffe und Fügen am Institut für Werkstoff- und Fügetechnik CY - Magdeburg, Germany DA - 2014-09-12 PY - 2014 SN - 978-3-940961-85-3 SP - 207 EP - 214 AN - OPUS4-31474 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Eich, Gerd A1 - Burkert, Andreas A1 - Mietz, Jürgen T1 - Entwicklung eines kombinierten Schutzsystems für chloridbelastete Betonflächen aus Spritzverzinkung mit abdichtender Beschichtung (Kurzfassung, AiF 12 818 N) KW - Stahlbeton KW - Chlorinduzierte Korrosion KW - Thermische Spritzverzinkung KW - Kathodischer Korrosionsschutz KW - Oberflächenschutzsystem PY - 2004 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-44201 SP - 1 EP - 4 PB - Bundesanstalt für Materialforschung und -prüfung CY - Berlin AN - OPUS4-4420 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Raupach, M. A1 - Mietz, Jürgen A1 - Nürnberger, U. A1 - Wolff, L. A1 - Bruns, M. A1 - Burkert, Andreas A1 - Eich, Gerd A1 - Menzel, K. T1 - Entwicklung eines kombinierten Schutzsystems für chloridbelastete Betonflächen aus Spritzverzinkung mit abdichtender Beschichtung (Abschlussbericht, AiF 12 818 N/2) N2 - Die Zielsetzung dieses Projektes war es, ein kombiniertes Schutzsystem aus Spritzverzinkung und abdichtendem Oberflächenschutzsystem für die Instandsetzung chloridbelasteter und korrosionsgeschädigter Stahlbetonbauteile zu entwickeln. Dabei soll die Spritzverzinkung der Betonoberfläche in den ersten Jahren nach der Instandsetzung einen kathodischen Korrosionsschutz der Bewehrung bewirken, bis der Beton infolge des Oberflächenschutzsystems soweit ausgetrocknet ist, dass auch ohne kathodischen Schutz praktisch keine Korrosion der Bewehrung mehr stattfinden kann. Anhand von Untersuchungen zur Haftung zwischen Beton, Zinkschicht und verschiedenen Oberflächenschutzsystemen wurde der Aufbau des kombinierten Schutzsystems entwickelt. Es wurden verschiedene OS-11a-Systeme ein OS-13-System sowie zwei Systeme nach ZTV-ING, Teil 7 vor und nach künstlicher Bewitterung untersucht. Anhand der Ergebnisse wurde für das kombinierte System ein OS-11a-System ausgewählt und im weiteren hinsichtlich der Wirksamkeit des kathodischen Schutzes sowie hinsichtlich der Austrocknung des Betons untersucht. Es zeigte sich sowohl an ausgelagerten Prüfköpfen sowie auf einer angelegten Versuchsfläche auf Freideck eines Parkhauses, dass ein wirksamer galvanischer kathodischer Korrosionsschutz der Bewehrung nur bei sehr hohen Chloridgehalten (4 M.-% bezogen auf den Zementgehalt) erreicht werden kann. Bei geringeren untersuchten Chloridgehalten kam es vermutlich infolge der Austrocknung der Zink/Beton-Kontaktzone nach relativ kurzer Zeit zu einer Inaktivierung des Zinks. Bei Chloridgehalten von 4 M.-% bildeten sich zwischen der Zinkschicht und dem ausgewählten OS-System gasgefüllte Blasen. Diese Problematik, sowie die Tatsache dass die Wirksamkeit des Prinzips W (Austrocknung des Betons) bei derart hohen Chloridgehalten bezweifelt werden muss, grenzt die Anwendbarkeit des Kombinationssystems mit der Zinkschicht als Opferanode deutlich ein. An neun Jahre alten, ausgelagerten Prüfköpfen durchgeführte Untersuchungen zeigten jedoch, dass mittels Fremdstrombeaufschlagung zwischen Zinkschicht und Bewehrung ein wirksamer kathodischer Schutz auch bei geringeren Chloridgehalten erreicht werden kann. Der Einsatz des entwickelten Kombinationssystems mit Fremdstrombeaufschlagung erscheint somit durchaus durchführbar. Dabei sollte der Fremdstrom jedoch vorsichtig dosiert werden, um den Haftverbund zum Zink nicht zu sehr zu schwächen. Das Ziel des Vorhabens wurde somit erreicht. KW - Chlorinduzierte Korrosion KW - Kathodischer Korrosionsschutz KW - Oberflächenschutzsystem KW - Stahlbeton KW - Thermische Spritzverzinkung PY - 2004 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-355176 SP - 1 EP - 122 PB - IBAC Institut für Bauforschung CY - Aachen AN - OPUS4-35517 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Burkert, Andreas A1 - Eich, Gerd A1 - Mietz, Jürgen T1 - Entwicklung eines kombinierten Schutzsystems für chloridbelastete Betonflächen aus Spritzverzinkung mit abdichtender Beschichtung T2 - 2. Kolloquium Gemeinsame Forschung im Korrosionsschutz, Neue Entwicklungen bei Fügeverfahren und Oberflächenschutz CY - Frankfurt am Main, Deutschland DA - 2004-03-02 KW - Stahlbeton KW - Chlorinduzierte Korrosion KW - Thermische Spritzverzinkung KW - Kathodischer Korrosionsschutz KW - Oberflächenschutzsystem PY - 2004 SN - 3-935406-12-6 SP - 72 EP - 83 PB - GfKORR CY - Frankfurt am Main AN - OPUS4-3371 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mietz, Jürgen A1 - Burkert, Andreas ED - Cziesielski, E. T1 - Elektrochemische Verfahren zur Detektion von Bewehrungsstahlkorrosion KW - Potentialfeldmessungen KW - Galvanostatische Pulsmessungen KW - Bewehrungsstahlkorrosion PY - 2004 SN - 3-433-01705-0 SP - 379 EP - 385 PB - Ernst CY - Berlin AN - OPUS4-3519 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mietz, Jürgen A1 - Isecke, Bernd T1 - Electrochemical Rehabilitation of Corrosion affected steel reinforced concrete KW - Korrosion KW - Korrosionsschutz KW - Electrochemical realkalisation PY - 1999 SN - 1120-7302 VL - 10 IS - 1 SP - 45 EP - 59 PB - Ed. Communicazioni Tecniche CY - Modena AN - OPUS4-725 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ebell, Gino A1 - Burkert, Andreas A1 - Lehmann, Jens A1 - Mietz, Jürgen T1 - Electrochemical investigations on the corrosion behaviour of galvanized reinforcing steels in concrete with chromate-reduced cements N2 - The reduction of the chromate contents in cements affects the electrochemical reactions of galvanized reinforcing steels in fresh concrete. By means of electrochemical measurements and bar pull-out tests the effect of chromates on the formation of protective coatings at the zinc and the bond behaviour have been investigated using chromate-containing and chromate-reduced cements. The results have shown that the bond zone was affected as a result of chromate reduction for cement types CEM I and CEM II. The disturbance to the bond zone should be considered as long-term in relation to the pore structure which is formed. The effects on the bond are largely compensated for as the concrete ages. The results of the related bond strength with displacement paths of 0.1 and 0.5?mm, respectively, are still within the range of expected figures for non-galvanized reinforcing steel despite the structural disturbance. Under practical aspects it is not necessary that the existing structural disturbance with respect to bond strength is taken into consideration. KW - Cement KW - Chromate KW - Concrete KW - Electrochemical measurements KW - Galvanized steel KW - Polarization KW - Pull-out tests KW - Reinforcing steel KW - Zinc PY - 2012 U6 - https://doi.org/10.1002/maco.201106311 SN - 0947-5117 SN - 1521-4176 VL - 63 IS - 9 SP - 791 EP - 802 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-26568 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Poltavtseva, Marina A1 - Ebell, Gino A1 - Mietz, Jürgen T1 - Electrochemical investigations of carbon-based conductive coatings for application as anodes in ICCP systems of reinforced concrete structures N2 - Carbon-based conductive coatings are complex composites, consisting of an organic or inorganic binder and conductive carbon components, for application as anodes in impressed current cathodic protection systems of reinforced concrete structures. The electrochemical properties of three coatings at different humidity and in saturated calcium hydroxide solution were studied by electrochemical methods, such as electrochemical impedance measurement, measuring of open circuit potential over time and galvanostatic polarization. The dissolved organic and inorganic carbons in electrolyte solution were quantified by using a photometric method. The structures of the coatings were investigated before and after the electrochemical tests by microscopy and scanning electron microscope/EDX analysis. The results of the electrochemical impedance measurements show that the tested coatings all have a relatively low resistance, which is between 100 and 200 Ω. The binder and the surface porosity influence the degradation behavior of those coatings. Especially the organic binder reacts with the strong alkaline medium under dissolving of organic carbon. KW - Cathodic protection KW - Corrosion KW - Rebar KW - Reinforcement KW - Concrete KW - Potential PY - 2015 U6 - https://doi.org/10.1002/maco.201407680 SN - 0947-5117 SN - 1521-4176 VL - 66 IS - 7 SP - 627 EP - 634 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-33709 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino A1 - Poltavtseva, M. A1 - Mietz, Jürgen ED - Ottosen, L. T1 - Electrochemical investigation of carbon-based conductive coatings for application as anodes in ICCP system of reinforced concrete structures N2 - Carbon-based conductive coatings are complex composites, consisting of an organic or inorganic binder and conductive carbon components, for application as anodes in impressed current cathodic protection systems of reinforced concrete structures. The electrochemical properties of three coatings at different humidity and in saturated calcium hydroxide solution were studied by electrochemical methods, such as electrochemical impedance measurement, measuring of open circuit potential over time and galvanostatic polarization. T2 - International RILEM Conference on Materials, Systems and Structures in Civil Engineering 2016 CY - Lyngby, Denmark DA - 21.08.2016 KW - ICCP KW - Coating KW - Cunductive KW - Corrosion KW - reinforcement KW - Concrete KW - Cathodic protection PY - 2016 SN - 978-2-35158-176-6 SN - 978-2-35158-177-3 VL - Proceedings PRO 111 SP - 43 EP - 46 PB - RILEM Publications S.A.R.L. CY - Paris, France AN - OPUS4-37216 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino A1 - Poltavtseva, Marina A1 - Mietz, Jürgen T1 - Electrochemical investigation of carbon-based conductive coatings for application as anodes in ICCP system of reinforced concrete structures N2 - Carbon‐based conductive coatings are complex composites, consisting of an organic or inorganic binder and conductive carbon components, for application as anodes in impressed current cathodic protection systems of reinforced concrete structures. The electrochemical properties of three coatings at different humidity and in saturated calcium hydroxide solution were studied by electrochemical methods, such as electrochemical impedance measurement, measuring of open circuit potential over time and galvanostatic polarization. The dissolved organic and inorganic carbons in electrolyte solution were quantified by using a photometric method. The structures of the coatings were investigated before and after the electrochemical tests by microscopy and scanning electron microscope/EDX analysis. The results of the electrochemical impedance measurements show that the tested coatings all have a relatively low resistance, which is between 100 and 200V. The binder and the surface porosity influence the degradation behavior of those coatings. Especially the organic binder reacts with the strong alkaline medium under dissolving of organic carbon. T2 - EUROCORR 2014 - European corrosion congress CY - Pisa, Italy DA - 08.09.2014 KW - Cathodic protection KW - Concrete KW - ICCP PY - 2014 SN - 978-3-89746-159-8 SP - O-7489, 481 EP - O-7489, 481 AN - OPUS4-31430 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Burkert, Andreas A1 - Ebell, Gino A1 - Eichler, T. A1 - Hariri, K. A1 - Harnisch, J. A1 - Keßler, S. A1 - Mayer, T. A1 - Meier, J. A1 - Mietz, Jürgen A1 - Reichling, K. A1 - Sodeikat, C. T1 - Electrochemical half-cell potential measurements for the detection of reinforcement corrosion N2 - This specification describes the application of electrochemical half‐cell potential measurements (frequently also called potential mapping) for the detection of reinforcement corrosion in reinforced concrete structures. Areas of corroding reinforcement steel can be located in a nondestructive manner by means of this procedure. Half‐cell potential measurements are used in order to detect chloride‐induced corrosion. However, it is not recommended in order to assess the risk of carbonation‐induced corrosion. For this purpose the determination of the carbonation depth and the concrete cover appear to be more appropriate. The content of this specification exclusively refers to the application of mobile, local variable reference electrodes, which are only placed on the concrete surface while measuring. The technique distinguishes itself thereby from the range of corrosion monitoring systems with stationary installed reference electrodes and sensor systems, respectively, whereby it is possible to continuously track measurements within the area of the installed electrodes. However, these methods are not dealt with in this specification. KW - Monitoring KW - Corrosion KW - Reinforcement PY - 2014 SN - 978-940283-72-6 SP - B 03, 1 EP - 19 PB - DGZfP CY - Berlin AN - OPUS4-40419 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Isecke, Bernd A1 - Mietz, Jürgen T1 - Einsatz nichtrostender Stähle in Schwimmbädern T2 - Fachtagung des Nederlands Corrosie Centrum CY - Breda, Niederlande DA - 2002-11-14 PY - 2002 AN - OPUS4-1845 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Eich, Gerd A1 - Burkert, Annette A1 - Burkert, Andreas A1 - Mietz, Jürgen T1 - Einsatz des nichtrostenden Duplex-Stahls 1.4362 als preisgünstige Alternative im Bauwesen N2 - Aufgrund der in den letzten Jahren stark angestiegenen Rohstoffpreise sind die im Bauwesen häufig eingesetzten nichtrostenden Standardaustenite in vielen Fällen nicht mehr wettbewerbsfähig. Eine deutlich kostengünstigere Alternative stellt der Duplex-Stahl 1.4362 dar, der bisher aber noch nicht bauaufsichtlich zugelassen ist. Mit Hilfe von Auslagerungsversuchen sowie elektrochemischen Untersuchungen sollte das Korrosionsverhalten dieses Werkstoffs unter neutralen bis leicht sauren, chloridhaltigen Umgebungsbedingungen, wie sie in vielen Bereichen des Bauwesens vorkommen, geklärt werden. Insgesamt belegen die Ergebnisse, dass der kostengünstigere Werkstoff 1.4362 für baupraktische Anwendungen eine Alternative für Anwendungen darstellen kann, in denen bisher die Werkstoffe 1.4404 oder 1.4571 eingesetzt wurden. KW - Duplex-Stähle KW - Nichtrostende Stähle KW - Auslagerungsversuche KW - Elektrochemische Versuche KW - Lochkorrosionspotential KW - Spaltkorrosionspotential PY - 2007 U6 - https://doi.org/10.1002/stab.200710094 SN - 0038-9145 SN - 1437-1049 SN - 0932-6375 VL - 76 IS - 12 SP - 898 EP - 904 PB - Ernst CY - Berlin AN - OPUS4-16364 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mietz, Jürgen T1 - Ein halbes Leben für die BAM - Höhepunkte aus 30 Jahren T2 - GfKORR-Symposium CY - Frankfurt am Main, Germany DA - 2008-03-29 PY - 2008 AN - OPUS4-16715 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mietz, Jürgen A1 - Isecke, Bernd T1 - Development of stainless steels for civil engineering applications T2 - 14th International Corrosion Congress (ICC) CY - Cape Town, South Africa DA - 1999-09-26 KW - Nicht rostender Stahl KW - Korrosion PY - 1999 SN - 0-620-23943-3 PB - Document Transformation Technologies CY - Irene AN - OPUS4-727 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mietz, Jürgen A1 - Burkert, Andreas A1 - Eich, Gerd A1 - Raupach, M. T1 - Development of a new combined corrosion protection system for chloride-contaminated reinforced concrete structures N2 - Chloride-induced damage of reinforcing steel is especially for parking garages and bridges often very severe as large amounts of chlorides act on horizontal surfaces which could lead to fast ingress of these detrimental ions up to the level of the reinforcement and subsequently to high rates of corrosion. In order to avoid the disadvantages of conventional rehabilitation (unreliable prognosis with patch repair or high costs and regular maintenance with cathodic protection using impressed current) a new combined protection system was developed where the principle of drying out the concrete (by means of a surface protection system) is combined with a temporary cathodic protection (by means of a sprayed zinc layer) during the transitional period of the drying out process. This new system was tested both in the laboratory and on-site at a pilot application. Based on the results obtained the possibilities and limitations of the new system are discussed in this paper. KW - Chlorid-induced corrosion KW - Reinforcing steel KW - Cathodic protection KW - Sprayed zinc layer KW - Surface protection system PY - 2005 U6 - https://doi.org/10.1002/maco.200403836 SN - 0947-5117 SN - 1521-4176 VL - 56 IS - 2 SP - 104 EP - 110 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-7157 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ebell, Gino A1 - Burkert, Andreas A1 - Mietz, Jürgen T1 - Detection of reinforcement corrosion in reinforced concrete structures by potential mapping: Theory and practice N2 - Electrochemical potential mapping according to guideline B3 of DGZfP (German Society for Nondestructive Testing) is a recognized technique for the localization of corroding reinforcing steels. In reinforced concrete structures the measured potentials are not necessarily directly linked to the corrosion likelihood of the reinforcing steel. The measured values may be significantly affected, different from, e.g., stress measurement, by different influences on the potential formation at the phase boundary metal/concrete itself as well as the acquisition procedure. Due to the complexity of influencing factors there is a risk that the results are misinterpreted. Therefore, in a training concept firstly the theoretical basics of the test method should be imparted. Then, frequently occurring practical situations of various influencing factors will be made accessible to the participants by a model object specially designed for this purpose. The aim is to impart profound knowledge concerning the characteristics of potential mapping for detecting corrosion of reinforcing steel in order to apply this technique in practice as reliable and economical test method. KW - Corrosion KW - Potential mapping KW - Korrosion KW - Potentialfeldmessung PY - 2018 U6 - https://doi.org/10.1155/2018/3027825 SN - 1687-9333 SN - 1687-9325 VL - 2018 SP - Article 3027825, 1 EP - 6 PB - Hindawi AN - OPUS4-46206 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mietz, Jürgen A1 - Rückert, Joachim A1 - Isecke, Bernd T1 - Dauerhafte Anker für den Grundbau - neue Werkstoffkonzepte T2 - Jahrestagung der Gesellschaft für Korrosionsschutz ; GfKORR-Jahrestagung CY - Berlin, Deutschland DA - 2000-11-07 KW - Nichtrostende Stähle KW - Grundanker PY - 2000 SN - 3-935406-03-7 SP - 121 EP - 131 PB - Ges. für Korrosionsschutz CY - Frankfurt am Main AN - OPUS4-836 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mayer, T. F. A1 - Dauberschmidt, C. A1 - Bruns, M. A1 - Eichler, T. A1 - Wiens, U. A1 - Mietz, Jürgen A1 - Gehlen, C. A1 - Ebell, Gino A1 - Gerhard, G. A1 - Osterminski, K. T1 - Das Instandsetzungsprinzip W-Cl N2 - Während das Instandsetzungsprinzip W bei carbonatisierungsinduzierter Korrosion seit vielen Jahren als Standardverfahren etabliert ist, wird seine Anwendbarkeit bei chloridinduzierter Korrosion (W-Cl) in der Fachwelt bis heute kontrovers diskutiert. Zwar ergeben sich aus seiner Anwendung gegenüber anderen Instandsetzungsverfahren auf den ersten Blick u. U. deutliche wirtschaftliche Vorteile, allerdings besteht bei diesem Verfahren ein deutlich höheres Risiko, dass das Instandsetzungsziel nicht erreicht wird. Im vorliegenden Beitrag werden die technischen Grundlagen des Instandsetzungsprinzips W-Cl sowie der aktuelle Kenntnisstand - sowohl für den gerissenen als auch für den ungerissenen Beton - dargestellt und baurechtliche Konsequenzen, die sich aus dem erhöhten Ausführungsrisiko ergeben, diskutiert. Korrosionsmonitoring als Element zum Nachweis des Instandsetzungserfolgs bei Anwendung des Prinzips W-Cl wird vorgestellt. Anhand von Anwendungsbeispielen werden sowohl die Risiken, die mit dem Verfahren verbunden sind, als auch das Potenzial bei erfolgreicher Anwendung veranschaulicht. KW - Korrosion KW - Instandsetzung KW - W-Cl KW - Risse PY - 2020 U6 - https://doi.org/10.1002/bate.201900083 SN - 0932-8351 VL - 97 IS - 1 SP - 2 EP - 10 PB - Ernst & Sohn CY - Berlin AN - OPUS4-50246 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burkert, Andreas A1 - Lehmann, Jens A1 - Burkert, Annette A1 - Mietz, Jürgen T1 - Damage of stainless steel bars due to atmospheric corrosion N2 - In addition to constructional requirements in civil engineering stainless steels often have to fulfil high visual demands. Unexpected impairments of the visual appearance of stainless steels under low corrosive conditions are a widespread problem today. Frequently it is supposed that this is caused by changes in the alloy composition, worse environmental conditions or improper handling. Within a research project the systematic investigation of several cases of damaged stainless steel bars has shown that the reasons are based on well-known material defects like chemical inhomogeneities (e.g. precipitations or local carburization) or geometrical defects (e.g. undercuts, rolling defects or shell formation). Thus, the failures could be clearly identified as production failures of the respective semi-finished products. KW - Atmospheric corrosion KW - EPR test KW - Failure KW - Intercrystalline corrosion KW - Stainless steel KW - Nichtrostender Stahl KW - Werkstoffauswahl KW - Dauerhaftigkeit KW - Korrosion PY - 2012 U6 - https://doi.org/10.1002/maco.201005701 SN - 0947-5117 SN - 1521-4176 VL - 63 IS - 3 SP - 264 EP - 270 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-25702 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hlavacek, Petr A1 - Gluth, Gregor A1 - Reinemann, Steffi A1 - Ebell, Gino A1 - Kühne, Hans-Carsten A1 - Mietz, Jürgen T1 - Corrosion of steel reinforcement in geopolymer mortars - carbonation resistance, chloride migration, and preliminary corrosion potential data N2 - Alkali-activated materials such as geopolymers are currently receiving a lot of attention because of their potential to be used as binders for concrete with advantageous engineering properties and reduced manufacturing CO2 emissions. Knowledge of the durability of steel in these concretes and related properties of alkali-activated materials is a prerequisite for their application as building materials, if they are to be used for steel reinforced elements. However, to date only limited data exists on this topic. The present contribution focuses on durability-related transport properties of geopolymer-based mortars (as model systems for concrete). We report results of accelerated carbonation, rapid chloride migration (RCM) and air permeability measurements as well as porosity data for fly ash-based geopolymer mortars, including mixes containing ground granulated blast furnace slag (GGBFS). In addition, we report polarization resistance data and corrosion potential vs. time curves for carbon steel bars embedded in two of the fly ash-based geopolymer mortars and a CEM I-based mortar (as reference). Despite comparable total porosities, the carbonation depths, the chloride migration coefficients and the air permeabilities of the mortars differed significantly. In general, the addition of GGBFS to the binders improved the performance (decreased transport coefficients); however, this was not found to be true for the air permeability in all cases. This latter effect can be explained by drying damage of the C-(A-)S-H gel in GGBFS-containing binders. On the other hand, low transport coefficients can also be achieved by optimization of the binder formulation without the addition of GGBFS, which is also reflected in the material’s air permeability. Thus, there exists no simple correlation between air permeability (of harshly dried mortars) and durability-related transport coefficients for the studied alkali-activated materials. The corrosion potential vs. time curves in combination with polarization resistance values reveal that the steel reinforcement in geopolymer mortars assumed a passive state. However, this happened considerably later than for steel in CEM I-based mortars. The free corrosion potential of carbon steel reinforcement in the geopolymer mortars had different values than the free corrosion potential values for the CEM I-based mortar for both the active and the passive state; possible reasons for this behavior are discussed. T2 - EUROCORR 2017 CY - Prague, Czech Republic DA - 03.09.2017 KW - Geopolymers KW - Alkali-activated materials KW - Corrosion KW - Steel reinforcement KW - Concrete PY - 2017 SP - Paper 87351, 1 EP - 7 AN - OPUS4-41870 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mietz, Jürgen ED - Banthia, N. T1 - Corrosion behaviour of stainless steels for use in ground anchors T2 - 3rd International Conference on Concrete under Severe Conditions ; 3rd CONSEC '01 CY - Vancouver, Canada DA - 2001-06-18 PY - 2001 SN - 0-88865-790-0 VL - 1 SP - 341 EP - 348 PB - Univ. British Columbia, Dep. of Civil Engineering CY - Vancouver AN - OPUS4-1135 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino A1 - Burkert, Andreas A1 - Mietz, Jürgen T1 - Corrosion behavior of galvanized reinforcement in chloride containing mortar and carbonated mortar N2 - Korrosionseigenschaften von feuerverzinktem Betonstahl unterscheiden sich grundlegend von herkömmlichen Betonstahl. In diesem Vortrag sind Beispiele für das Korrosionsverhalten in chloridhaltigen und carbonatisierten Mörteln dargestellt T2 - Intergalva 2018 - 25th International Galvanizing Conference CY - Berlin, Germany DA - 17.06.2018 KW - Corrosion KW - Korrosion KW - Verzinkt KW - Betonstahl PY - 2018 SP - 301 EP - 309 AN - OPUS4-45240 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gluth, Gregor A1 - Ebell, Gino A1 - Hlavacek, Petr A1 - Mietz, Jürgen T1 - Chloride‐induced steel corrosion in alkali‐activated fly ash mortar: Increased propensity for corrosion initiation at defects N2 - Chloride contents at the steel–mortar interface that initiate steel corrosion were determined for carbon steel in alkali‐activated fly ash mortar for three different exposure conditions: exposure to 1 M NaCl solution; leaching in deionized water and then exposure to 1 M NaCl solution; and leaching in deionized water, aging in air at 20°C and natural CO2 concentration, and then exposure to 1 M NaCl solution. For comparison, a Portland cement mortar, exposed to 1 M NaCl solution, was studied. The median values of the corrosion‐initiating chloride contents (average over the full length of the rebar) in the alkali‐activated fly ash mortar varied between 0.35 and 1.05 wt% Cl with respect to binder, consistently lower than what was obtained for the Portland cement mortar, but with no clear trend regarding the exposure conditions. For most of the alkali‐activated fly ash mortar specimens, preferential corrosion at the connection between the working electrode and the external measurement setup was observed, while preferential corrosion did not occur for the Portland cement mortar. Scanning electron microscopy and auxiliary experiments in synthetic solutions indicated that this behavior was caused by inhomogeneities at the steel–mortar interface in the alkali‐activated mortar, likely due to its peculiar rheological properties in the fresh state. KW - Alkali-activated materials KW - Steel corrosion KW - Critical chloride content KW - Steel-concrete interface PY - 2020 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-507268 VL - 71 IS - 5 SP - 749 EP - 758 PB - Wiley-VCH AN - OPUS4-50726 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fischer, Joachim A1 - Burkert, Andreas A1 - Mietz, Jürgen T1 - Case studies of stainless steel corrsoion in indoor swimming pool environments N2 - In indoor swimming pools stainless steels are used not only due to structural and economic reasons but also due to aesthetic considerations. And therefore not only safety relevant load bearing components have to fulfil their tasks but also the visual appearance should be free of any staining. In a lot of cases basic requirements (e.g. design criteria, material selection and maintenance) being essential parts of technical regulations were not taken into account. Typical case studies with explanation of the cause of the corrosion problems and possibilities to prevent them are shown in the present paper. KW - Stainless steel KW - Atmospheric corrosion KW - Indoor swimming pools PY - 2011 U6 - https://doi.org/10.1179/174327809X409150 SN - 1478-422X VL - 46 IS - 1 SP - 76 EP - 79 PB - Maney Publishing CY - London, UK AN - OPUS4-23287 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Broomfield, J. A1 - Fischer, Joachim A1 - Mietz, Jürgen A1 - Schneck, U. T1 - Case studies N2 - In this paper, some quite different survey tasks are described, and it can be seen that corrosion surveys will follow a certain scheme of data acquisition (first NDT measurements, than detailed testing on suspect areas), but the individual scope of on-site measurements may have a vast variety according to the local circumstances, and the interpretation always has to refer to a wider set of information than the data readings only. KW - Corrosion surveys KW - Non-destructive testing KW - Reinforcement KW - Concrete KW - Potential mapping KW - Corrosion PY - 2013 U6 - https://doi.org/10.1002/maco.201206649 SN - 0947-5117 SN - 1521-4176 VL - 64 IS - 2 SP - 147 EP - 160 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-29730 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Hlavacek, Petr A1 - Ebell, Gino A1 - Gluth, Gregor A1 - Reinemann, Stefi A1 - Mietz, Jürgen A1 - Kühne, Hans-Carsten T1 - Betonstahlkorrosion in Geopolymerbetonen bei Angriff von Kohlenstoffdioxid und Chlorid N2 - Der kritische, Korrosion auslösende Chloridgehalt für die Beurteilung der Korrosions-beständigkeit von Betonstahl in Geopolymerbetonen ist von großer Bedeutung für die Dauerhaftigkeitsprognose für bewehrte Elemente aus solchen Materialien. Es sind kaum experimentelle Daten in der Fachliteratur vorhanden und die vorliegenden Werte unterscheiden sich zwischen den Studien erheblich. In diesem Projekt wurde der kritische, Korrosion auslösende Chloridgehalt für Betonstahl (BSt 500) in flugaschebasierten (Ca-armen) Geopolymermörtel für verschiedene Beaufschlagungskombinationen bestimmt: Chloridbeaufschlagung mit 1 M NaCl-Lösung; Auslaugen in entionisiertem Wasser und anschließende Chloridbeaufschlagung im 1 M NaCl-Lösung; Auslaugen in entionisiertem Wasser, Carbonatisierung in Luft bei 20 °C und natürlicher CO2 Konzentration und anschließende Chloridbeaufschlagung mit 1 M NaCl-Lösung. Für Referenz-Zwecke wurde zusätzlich der Korrosion auslösende Chloridgehalt für eine Portland-Zement Mischung bei Auslagerung in 1 M NaCl-Lösung bestimmt. KW - Korrosion KW - Geopolymer PY - 2019 SP - 1 EP - 83 AN - OPUS4-49752 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hlavacek, Petr A1 - Reinemann, Steffi A1 - Gluth, Gregor A1 - Ebell, Gino A1 - Mietz, Jürgen ED - Serdar, M. ED - Stirmer, N. ED - Provis, J. T1 - Behaviour of reinforced alkali-activated fly ash mortars under leaching conditions N2 - Corrosion of steel reinforcement in concrete is one of the major deterioration mechanisms limiting the service life of reinforced concrete structures. While for conventional (Portland cement-based) concretes a great amount of experience exists in this regard, the factors that determine the onset of reinforcement corrosion in alkali-activated materials are incompletely understood yet. One aspect of corrosion protection is leaching and the accompanying changes of the concrete pore solution. In the present study, alkali-activated fly ash mortars with embedded carbon steel rebars were exposed to de-ionised water for periods up to 330 days, and the electrochemical response of the steel (free corrosion potential, polarisation resistance), the alteration of the mortar (ohmic resistance, mechanical strength, pore size distribution) as well as the pore solution composition were monitored. Although substantial alkali leaching was observed, the pH of the pore solution remained at values sufficient to protect the embedded steel from depassivation. The mortar did not exhibit indications of significant deterioration. Thus, the present results suggest that leaching is not critical for protection of steel reinforcement in alkali-activated fly ash mortars and concretes. T2 - International Conference on Sustainable Materials, Systems and Structures (SMSS 2019) CY - Rovinj, Croatia DA - 20.03.2019 KW - Alkali-activated materials KW - Steel corrosion KW - Leaching PY - 2019 SN - 978-2-35158-223-7 VL - 1 SP - 118 EP - 124 PB - RILEM Publications CY - Paris AN - OPUS4-47585 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Isecke, Bernd A1 - Mietz, Jürgen T1 - Bau- und Instandsetzungsmethoden - Elektrochemische Schutzverfahren zur Beseitigung von Korrosionsrisiken an Stahlbetonbauwerken PY - 2003 SN - 3-935243-14-6 N1 - Serientitel: Schriftenreihe des Verbandes Deutscher Architekten- und Ingenieurvereine – Series title: Schriftenreihe des Verbandes Deutscher Architekten- und Ingenieurvereine IS - 2 SP - 149 EP - 157 PB - Verl. Das Beispiel CY - Darmstadt AN - OPUS4-2789 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mietz, Jürgen A1 - Isecke, Bernd T1 - Assessment of test methods for evaluation stress corrosion cracking susceptibility of prestressing steels N2 - Prestressing steels can be exposed in prestressed concrete structures in construction stage (ungrouted duct) to environmental conditions causing formation and growth of hydrogen induced cracks with brittle fracture of the steel. The risk of this hydrogen induced stress corrosion cracking can be minimized by appropriate treatment, but there is a requirement for construction to approve only prestressing steel having no enhanced susceptibility to stress corrosion cracking. The paper describes the historical development of the different test methods proposed in the past and gives an overview on the general requirements for a suitable test method to assess the hydrogen-induced stress corrosion susceptibility of prestressing steels. Since 1982, based on investigations on construction sites and transfer of the results into laboratory tests, a test method is available enabling realistic estimation of suitable application possibilities of prestressing steels. This so called DIBt-test is approved to distinguish between prestressing steels susceptible to hydrogen induced stress corrosion cracking and those suitable and therefore approvable steels at practical environmental conditions. Furthermore the test enables estimation of corrosion risk for newly developed prestressing steels with higher strength. Translated Abstract Beurteilung der Prüfverfahren zur Untersuchung der Spannungsrisskorrosionsempfindlichkeit von Spannstählen Spannstähle können in Spannbetonbauwerken im Bauzustand (unverpresstes Hüllrohr) Umgebungsbedingungen ausgesetzt sein, die zur Bildung und Ausbreitung wasserstoffinduzierter Risse mit Sprödbruch des Stahles führen können. Das Risiko dieser wasserstoffinduzierten Spannungsrisskorrosion kann einerseits durch eine sachgemäße Verarbeitung der Spannstähle minimiert werden, andererseits besteht die Notwendigkeit nur solche Spannstähle für die Baupraxis zuzulassen, die unter baupraktischen Bedingungen keine erhöhte Empfindlichkeit für Spannungsrisskorrosion besitzen. Die vorliegende Arbeit beschreibt die historische Entwicklung der verschiedenen vorgeschlagenen Prüfverfahren und gibt einen Überblick über die allgemeinen Anforderungen an ein geeignetes Verfahren zur Beurteilung der wasserstoffinduzierten Spannungsrisskorrosionsempfindlichkeit von Spannstählen. Seit 1982 steht, begründet durch Untersuchungen auf Baustellen und Umsetzung der Ergebnisse in Laborversuchen, ein Prüfverfahren zur Verfügung, das eine wesentlich realistischere Einschätzung der Einsatzmöglichkeiten von Spannstählen zulässt. Dieser sog. DIBt-Test hat sich bewährt, um unter praktischen Umgebungsbedingungen gegen H-induzierte Spannungsrisskorrosion empfindliche Spannstähle von geeigneten und damit zulassungswürdigen Stählen zu unterscheiden. Des weiteren erlaubt die Prüfung ebenfalls eine Abschätzung des Korrosionsrisikos für neuentwickelte, höherfeste Spannstähle. PY - 2002 SN - 0947-5117 SN - 1521-4176 VL - 53 IS - 6 SP - 373 EP - 384 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-1402 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mietz, Jürgen A1 - Isecke, Bernd T1 - Analyse von Spannbetonschäden und Strategien zu deren Vermeidung T2 - Tagung Werkstoffprüfung 2001 - Schadensanalyse und Schadensvermeidung CY - Bad Nauheim, Germany DA - 2001-12-06 PY - 2001 AN - OPUS4-3343 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mietz, Jürgen A1 - Isecke, Bernd ED - Lange, G. T1 - Analyse von Spannbetonschäden und Strategien zu deren Vermeidung T2 - 19. Tagung Werkstoffprüfung CY - Bad Nauheim, Deutschland DA - 2001-12-06 PY - 2001 SN - 3-527-30538-6 SP - 153 EP - 158 PB - Wiley-VCH CY - Weinheim AN - OPUS4-1216 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mietz, Jürgen T1 - Aktueller Stand der Überarbeitung der EN 1993-1-4 T2 - GfKORR-Arbeitskreis Korrosion im Bauwesen CY - Heligoland, Germany DA - 2013-06-03 PY - 2013 AN - OPUS4-28712 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mietz, Jürgen T1 - Aktuelle Probleme bei bestimmten vergüteten Spannstählen T2 - Fachtagung "Sonderkapitel aus dem Brücken- und Ingenieurbau" CY - Berlin, Deutschland DA - 2000-11-13 PY - 2000 SP - 87 EP - 99 PB - BAM CY - Berlin AN - OPUS4-981 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -