TY - GEN A1 - Angst, U. A1 - Brem, M. A1 - Dauberschmidt, C. A1 - Ebell, Gino A1 - Eichler, T. A1 - Hariri, K. A1 - Harnisch, J. A1 - Keßler, S. A1 - Kosalla, M. A1 - Mayer, T. F. A1 - Mietz, Jürgen A1 - Pruckner, F. A1 - Sodeikat, C. T1 - Merkblatt B 12 Korrosionsmonitoring bei Stahl- und Spannbetonbauwerken N2 - Das Merkblatt B12 enthält alle gängigen und etablierten Monitoringverfahren für das Korrosionsmonitoring an Stahlbetonbauwerken. KW - Korrosion KW - Monitoring PY - 2018 SN - 978-3-940283-93-1 SP - 1 EP - 58 PB - DGZfP CY - Berlin AN - OPUS4-45235 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ebell, Gino A1 - Achenbach, R. A1 - Angst, U. A1 - Brem, M. A1 - Dauberschmidt, C. A1 - Eichler, T. A1 - Hariri, K. A1 - Harnisch, J. A1 - Keßler, S. A1 - Mayer, T.F. A1 - Mietz, Jürgen A1 - Pruckner, F. T1 - Merkblatt B 03 - Elektrochmische Potentialmessung zur Detektion von Bewehrungsstahlkorrosion N2 - Die Potentialmessung kann zum Auffinden korrosionsaktiver Bereiche neben Stahlbetonbauwerken auch bei Spannbetonbauwerken angewandt werden, die mit Spannstählen im direkten Verbund hergestellt werden. Bei Vorspannsystemen mit metallischen Hüllrohren im nachträglichen Verbund ist eine Aussage über den Korrosionszustand des Hüllrohrs, nicht aber des Spannstahls möglich. Messungen an Spannbetonbauteilen erfordern grundsätzlich die besonderen Kenntnisse eines Spezialisten. KW - Korrosion KW - Potentialfeldmessung KW - Corrosion KW - Concrete PY - 2021 SN - 978-3-947971-16-9 SP - 1 EP - 22 PB - DGZfP CY - Berlin AN - OPUS4-53091 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ebell, Gino A1 - Achenbach, R. A1 - Angst, U. A1 - Dauberschmidt, C. A1 - Eichler, T. A1 - Hariri, K. A1 - Harnisch, J. A1 - Keßler, S. A1 - Kosalla, M. A1 - Mayer, T.F. A1 - Mietz, Jürgen A1 - Pruckner, F. A1 - Sodeikat, C. T1 - Specification B 12 - Corrosion monitoring in reinforced and prestressed concrete structures N2 - This specification describes how corrosion monitoring is used to check the condition of reinforced and prestressed concrete members. In this specification, the term "corrosion monitoring" covers all methods in which it is possible to continuously track corrosion-relevant variables in the area of stationary, built-in sensors. This specification does not cover other possible methods, such as potential field measurements, involving the use of mobile, portable sensors that are placed temporarily on the membersurface to take measurements. KW - Korrosion KW - Corrosion KW - Monitoring PY - 2021 SN - 978-3-947971-14-5 SP - 1 EP - 55 PB - DGZfP CY - Berlin AN - OPUS4-53092 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino A1 - Burkert, Andreas A1 - Mietz, Jürgen T1 - Corrosion behavior of galvanized reinforcement in chloride containing mortar and carbonated mortar T2 - Intergalva 2018 N2 - Korrosionseigenschaften von feuerverzinktem Betonstahl unterscheiden sich grundlegend von herkömmlichen Betonstahl. In diesem Vortrag sind Beispiele für das Korrosionsverhalten in chloridhaltigen und carbonatisierten Mörteln dargestellt T2 - Intergalva 2018 - 25th International Galvanizing Conference CY - Berlin, Germany DA - 17.06.2018 KW - Corrosion KW - Korrosion KW - Verzinkt KW - Betonstahl PY - 2018 SP - 301 EP - 309 AN - OPUS4-45240 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ebell, Gino A1 - Burkert, Andreas A1 - Mietz, Jürgen T1 - Detection of reinforcement corrosion in reinforced concrete structures by potential mapping: Theory and practice JF - International Journal of Corrosion N2 - Electrochemical potential mapping according to guideline B3 of DGZfP (German Society for Nondestructive Testing) is a recognized technique for the localization of corroding reinforcing steels. In reinforced concrete structures the measured potentials are not necessarily directly linked to the corrosion likelihood of the reinforcing steel. The measured values may be significantly affected, different from, e.g., stress measurement, by different influences on the potential formation at the phase boundary metal/concrete itself as well as the acquisition procedure. Due to the complexity of influencing factors there is a risk that the results are misinterpreted. Therefore, in a training concept firstly the theoretical basics of the test method should be imparted. Then, frequently occurring practical situations of various influencing factors will be made accessible to the participants by a model object specially designed for this purpose. The aim is to impart profound knowledge concerning the characteristics of potential mapping for detecting corrosion of reinforcing steel in order to apply this technique in practice as reliable and economical test method. KW - Corrosion KW - Potential mapping KW - Korrosion KW - Potentialfeldmessung PY - 2018 DO - https://doi.org/10.1155/2018/3027825 SN - 1687-9333 SN - 1687-9325 VL - 2018 SP - Article 3027825, 1 EP - 6 PB - Hindawi AN - OPUS4-46206 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gluth, Gregor A1 - Ebell, Gino A1 - Hlavacek, Petr A1 - Mietz, Jürgen T1 - Chloride‐induced steel corrosion in alkali‐activated fly ash mortar: Increased propensity for corrosion initiation at defects JF - Materials and Corrosion N2 - Chloride contents at the steel–mortar interface that initiate steel corrosion were determined for carbon steel in alkali‐activated fly ash mortar for three different exposure conditions: exposure to 1 M NaCl solution; leaching in deionized water and then exposure to 1 M NaCl solution; and leaching in deionized water, aging in air at 20°C and natural CO2 concentration, and then exposure to 1 M NaCl solution. For comparison, a Portland cement mortar, exposed to 1 M NaCl solution, was studied. The median values of the corrosion‐initiating chloride contents (average over the full length of the rebar) in the alkali‐activated fly ash mortar varied between 0.35 and 1.05 wt% Cl with respect to binder, consistently lower than what was obtained for the Portland cement mortar, but with no clear trend regarding the exposure conditions. For most of the alkali‐activated fly ash mortar specimens, preferential corrosion at the connection between the working electrode and the external measurement setup was observed, while preferential corrosion did not occur for the Portland cement mortar. Scanning electron microscopy and auxiliary experiments in synthetic solutions indicated that this behavior was caused by inhomogeneities at the steel–mortar interface in the alkali‐activated mortar, likely due to its peculiar rheological properties in the fresh state. KW - Alkali-activated materials KW - Steel corrosion KW - Critical chloride content KW - Steel-concrete interface PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-507268 DO - https://doi.org/10.1002/maco.202011541 VL - 71 IS - 5 SP - 749 EP - 758 PB - Wiley-VCH AN - OPUS4-50726 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gluth, Gregor A1 - Hlavacek, Petr A1 - Reinemann, Steffi A1 - Ebell, Gino A1 - Mietz, Jürgen ED - Alexander, M.G. ED - Beushausen, H. ED - Dehn, F. ED - Moyo, P. T1 - Leaching, carbonation and chloride ingress in reinforced alkali-activated fly ash mortars T2 - International Conference on Concrete Repair, Rehabilitation and Retrofitting (ICCRRR 2018) N2 - Alkali-activated fly ash mortars were studied with regard to durability-relevant transport coefficients and the electrochemical behaviour of embedded carbon steel bars on exposure of the mortars to leaching, carbonation and chloride penetration environments. The transport coefficients differed considerably between different formulations, being lowest for a mortar with BFS addition, but still acceptable for one of the purely fly ash-based mortars. Leaching over a period of ~300 days in de-ionized water did not lead to observable corrosion of the embedded steel, as shown by the electrochemical data and visual inspection of the steel. Exposure to 100 % CO2 atmosphere caused steel depassivation within approx. two weeks; in addition, indications of a deterioration of the mortar were observed. The results are discussed in the context of the different reaction products expected in high- and low-Ca alkali-activated binders, and the alterations caused by leaching and carbonation. T2 - International Conference on Concrete Repair, Rehabilitation and Retrofitting (ICCRRR 2018) CY - Cape Town, South Africa DA - 19.11.2018 KW - Alkali-activated materials KW - Steel corrosion KW - Leaching KW - Carbonation PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-464381 DO - https://doi.org/10.1051/matecconf/201819902025 VL - 199 SP - Article Number 02025 PB - EDP Sciences AN - OPUS4-46438 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Hlavacek, Petr A1 - Ebell, Gino A1 - Gluth, Gregor A1 - Reinemann, Stefi A1 - Mietz, Jürgen A1 - Kühne, Hans-Carsten T1 - Betonstahlkorrosion in Geopolymerbetonen bei Angriff von Kohlenstoffdioxid und Chlorid N2 - Der kritische, Korrosion auslösende Chloridgehalt für die Beurteilung der Korrosions-beständigkeit von Betonstahl in Geopolymerbetonen ist von großer Bedeutung für die Dauerhaftigkeitsprognose für bewehrte Elemente aus solchen Materialien. Es sind kaum experimentelle Daten in der Fachliteratur vorhanden und die vorliegenden Werte unterscheiden sich zwischen den Studien erheblich. In diesem Projekt wurde der kritische, Korrosion auslösende Chloridgehalt für Betonstahl (BSt 500) in flugaschebasierten (Ca-armen) Geopolymermörtel für verschiedene Beaufschlagungskombinationen bestimmt: Chloridbeaufschlagung mit 1 M NaCl-Lösung; Auslaugen in entionisiertem Wasser und anschließende Chloridbeaufschlagung im 1 M NaCl-Lösung; Auslaugen in entionisiertem Wasser, Carbonatisierung in Luft bei 20 °C und natürlicher CO2 Konzentration und anschließende Chloridbeaufschlagung mit 1 M NaCl-Lösung. Für Referenz-Zwecke wurde zusätzlich der Korrosion auslösende Chloridgehalt für eine Portland-Zement Mischung bei Auslagerung in 1 M NaCl-Lösung bestimmt. KW - Korrosion KW - Geopolymer PY - 2019 SP - 1 EP - 83 AN - OPUS4-49752 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hlavacek, Petr A1 - Reinemann, Steffi A1 - Gluth, Gregor A1 - Ebell, Gino A1 - Mietz, Jürgen ED - Serdar, M. ED - Stirmer, N. ED - Provis, J. T1 - Behaviour of reinforced alkali-activated fly ash mortars under leaching conditions T2 - Proceedings of the International Conference on Sustainable Materials, Systems and Structures (SMSS2019), Vol. 1: New Generation of Construction Materials N2 - Corrosion of steel reinforcement in concrete is one of the major deterioration mechanisms limiting the service life of reinforced concrete structures. While for conventional (Portland cement-based) concretes a great amount of experience exists in this regard, the factors that determine the onset of reinforcement corrosion in alkali-activated materials are incompletely understood yet. One aspect of corrosion protection is leaching and the accompanying changes of the concrete pore solution. In the present study, alkali-activated fly ash mortars with embedded carbon steel rebars were exposed to de-ionised water for periods up to 330 days, and the electrochemical response of the steel (free corrosion potential, polarisation resistance), the alteration of the mortar (ohmic resistance, mechanical strength, pore size distribution) as well as the pore solution composition were monitored. Although substantial alkali leaching was observed, the pH of the pore solution remained at values sufficient to protect the embedded steel from depassivation. The mortar did not exhibit indications of significant deterioration. Thus, the present results suggest that leaching is not critical for protection of steel reinforcement in alkali-activated fly ash mortars and concretes. T2 - International Conference on Sustainable Materials, Systems and Structures (SMSS 2019) CY - Rovinj, Croatia DA - 20.03.2019 KW - Alkali-activated materials KW - Steel corrosion KW - Leaching PY - 2019 SN - 978-2-35158-223-7 VL - 1 SP - 118 EP - 124 PB - RILEM Publications CY - Paris AN - OPUS4-47585 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mayer, T. F. A1 - Dauberschmidt, C. A1 - Bruns, M. A1 - Eichler, T. A1 - Wiens, U. A1 - Mietz, Jürgen A1 - Gehlen, C. A1 - Ebell, Gino A1 - Gerhard, G. A1 - Osterminski, K. T1 - Das Instandsetzungsprinzip W-Cl JF - BAutechnik N2 - Während das Instandsetzungsprinzip W bei carbonatisierungsinduzierter Korrosion seit vielen Jahren als Standardverfahren etabliert ist, wird seine Anwendbarkeit bei chloridinduzierter Korrosion (W-Cl) in der Fachwelt bis heute kontrovers diskutiert. Zwar ergeben sich aus seiner Anwendung gegenüber anderen Instandsetzungsverfahren auf den ersten Blick u. U. deutliche wirtschaftliche Vorteile, allerdings besteht bei diesem Verfahren ein deutlich höheres Risiko, dass das Instandsetzungsziel nicht erreicht wird. Im vorliegenden Beitrag werden die technischen Grundlagen des Instandsetzungsprinzips W-Cl sowie der aktuelle Kenntnisstand - sowohl für den gerissenen als auch für den ungerissenen Beton - dargestellt und baurechtliche Konsequenzen, die sich aus dem erhöhten Ausführungsrisiko ergeben, diskutiert. Korrosionsmonitoring als Element zum Nachweis des Instandsetzungserfolgs bei Anwendung des Prinzips W-Cl wird vorgestellt. Anhand von Anwendungsbeispielen werden sowohl die Risiken, die mit dem Verfahren verbunden sind, als auch das Potenzial bei erfolgreicher Anwendung veranschaulicht. KW - Korrosion KW - Instandsetzung KW - W-Cl KW - Risse PY - 2020 DO - https://doi.org/10.1002/bate.201900083 SN - 0932-8351 VL - 97 IS - 1 SP - 2 EP - 10 PB - Ernst & Sohn CY - Berlin AN - OPUS4-50246 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -